Made available in DSpace on 2014-06-11T19:27:48Z (GMT). No. of bitstreams: 0 Previous issue date: 2008-07-30Bitstream added on 2014-06-13T20:36:16Z : No. of bitstreams: 1 oliveira_albm_me_arafo.pdf: 438115 bytes, checksum: dead0bfc4e29a4fcc0bc6644a0ce506c (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo deste estudo foi avaliar o efeito do acabamento e polimento na estabilidade de cor e na rugosidade superficial da resina composta Filtek Supreme XT em função de diferentes soluções fluoretadas. Para isso foram confeccionados corpos-de-prova (n= 140) por meio de uma matriz de aço inoxidável hemiseccionada com quatro orifícios circulares de 10 mm de diâmetro e 2 mm de espessura. A resina composta foi inserida na matriz num único incremento e fotoativada pelo aparelho de luz halógena Curing Light XL 3000 (3M/ESPE) por 40 segundos. Metade da amostra foi submetida a procedimentos de acabamento e polimento com discos de lixa Super-Snap® em ordem decrescente de granulação. Os grupos experimentais foram divididos de acordo com a presença ou ausência de acabamento e polimento e diferentes meios de imersão (saliva artificial, solução de fluoreto de sódio a 0,05%- manipulado, Fluordent Reach, Oral B, Fluorgard). Os espécimes permaneceram imersos em saliva artificial por 24 horas e foram submetidos à análise da cor no espectrofotômetro de colorimetria (Color guide 45/0, PCB 6807 BYK-Gardner GmbH Gerestsried, Alemanha) pelo sistema CIELab e à avaliação da rugosidade superficial (Ra) pelo rugosímetro portátil (Mitutoyo surftest SJ-401, Mitutoyo Corporation, Japão). A partir deste período, foram imersos nas diferentes soluções por 1 minuto ao dia durante 60 dias. Nos intervalos entre as imersões foram mantidos em saliva artificial a 37 _ 1 0C. As leituras da alteração de cor foram realizadas após 24 e 48 horas, 7, 14, 21, 30 e 60 dias do início da imersão e a da rugosidade superficial após 60 dias. Atendidos os pressupostos de normalidade e homocedasticidade, realizou-se Análise de Variância a dois fatores e teste de Tukey para comparações múltiplas, ambos com nível de significância de 5%. Para comparação das médias de rugosidade... / The aim of this study was to evaluate the effect of finishing and polishing procedures on the color stability and roughness of the Filtek Supreme XT resin composite surface submitted to different fluoride solutions. Samples were made (n= 140) in a hemi sectioned stainless steel mold with four 10-mm diameter and 2mm thick circular orifices. The composite resin was inserted in a single increment and light-cured with a halogen light curing unit (Curing Light XL 3000, 3M/ESPE) for 40 seconds. Half of each sample was submitted to finishing and polishing procedures with Super-Snap® grit disks in a decreasing order of granulation. Experimental groups were divided according to the presence or absence of finishing and polishing procedure and also to the different immersion media they were submitted to (artificial saliva, a manipulated 0, 05% sodium fluoride solution, Fluordent Reach, Oral B, Fluorgard). Specimens were kept in artificial saliva for 24 hours and submitted to color analysis in a colorimetric spectrophotometer (Color guide 45/0, PCB 6807 BYK-Gardner GmbH Gerestsried, Germany) by the CIELab system and to superficial roughness (Ra) evaluation by a portable rugosimeter (Mitutoyo surftest SJ-401, Mitutoyo Corporation, Japan). From this period, specimens were immersed in the different solutions for 1 minute per day, during 60 days. In periods between immersions, they were kept in artificial saliva at 37 _ 1 0C. Color alteration evaluations were performed after 24 and 48 hours, 7, 14, 21, 30 e 60 days and superficial roughness after 60 days from the beginning of immersions. After normality and homoscedasticity presumption had been confirmed, the two-way Analysis of Variance and Tukey`s test for multiple comparisons were realized, both with a 5% significance level. For comparison of roughness means in baseline and in the 60 days... (Complete abstract click electronic access below)

Made available in DSpace on 2014-06-11T19:28:03Z (GMT). No. of bitstreams: 0 Previous issue date: 2006Bitstream added on 2014-06-13T18:57:07Z : No. of bitstreams: 1 sartori_r_me_arafo.pdf: 1051874 bytes, checksum: cefcb24c1a056b34cdd58078fbe9390f (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Universidade Estadual Paulista (UNESP) / Atualmente o titânio é empregado como biomaterial devido sua biocompatibilidade e resistência à corrosão, entretanto os íons fluoretos são efetivos no processo de corrosão. O objetivo deste estudo foi analisar a influência de um meio fluoretado com diferentes pH nas propriedades mecânicas e na resistência à corrosão dos conjuntos implantes/componentes protéticos à base de Ti c.p., a partir dos testes de ciclagem mecânica, microscopia eletrônica de varredura (MEV) e dureza. Foram simulados cinco anos de uso regular de meios de higiene oral com conteúdo de 1500 ppm de NaF, com dois diferentes pH, mediante imersão das amostras nesse meio durante 184 horas. As amostras foram testadas num durômetro Micromet 2001. Os dados dos testes de dureza foram analisados pelo teste de Wilcoxon, demonstrando que as amostras sofreram influência negativa na dureza após a ação dos íons fluoreto. Entretanto, essa influência não ocorreu nos testes de ciclagem mecânica realizados em uma máquina de ensaios universais MTS-810, fixada a 100.000 ciclos, 15Hz e programada com força de fadiga a 150 N. Pela análise de MEV e EDS não foi contatado evidências de corrosão na superfície das amostras após ação de íons fluoretos, nem incorporação de íons fluoretos sobre a superfície dos conjuntos. Concluiu-se que a concentração de flúor e o pH das soluções não exerceram influência nas propriedades mecânicas e na resistência à corrosão. / Titanium has been widely used as biomaterial owing to its excellent corrosion resistance, mechanical properties and biocompatibility. However, it has been reported that fluoride-containing environments can attack titanium. The aim of this study was evaluated fluoride environments influence with different pH values in the implant/abutment sets. The implants were separated into 3 groups containing 7 implants/brand: one was submerged in acid fluoride environment (NaF 1500ppm 184h pH 5.3), one in neutral fluoride environment (NaF 1500ppm 184h pH 7.4), and other group in distillated water, simulating five years of dental hygiene. Hardness and surface texture were evaluated before and after fluoride exposition by Vickers method (500gf 30s) and scanning electron microscopy (SEM), respectively. The fatigue test was performed with 100.000 load cycles, 15 Hz and 150 N. There was decrease in hardness in implants submitted to the fluoride environment. SEM and EDS evaluation showed dark stains in all implants, irrespective of fluoride pH, resulting from pitting corrosion process. All sets supported the fatigue test until 100.000 load cycles. The results demonstrated that fluoride environment there was no influence in mechanical properties and corrosion resistence of the implant/abutment sets.

Orientador: Daniela Micheline dos Santos / Banca: Marcelo Coelho Goiato / Banca: Valentim Adelino Ricardo Barão / Resumo: A degradação de cerâmicas odontológicas acontece na cavidade oral e em contato com soluções erosivas. Duzentos e vinte discos de cerâmica de dissilicato de lítio foram divididos em 4 grupos. As amostras do Grupo Controle (Co) foram imersas em diferentes bebidas ácidas ou em saliva artificial. Os grupos que foram expostos em fluoreto de sódio 0,05% (NaF 0,05%) e 0,2% (NaF 0,2%) ou em gel de fluoreto fosfatado acidulado a 1,23% (FFA 1,23%), foram imersos em uma dessas soluções, para em seguida serem imersos nas bebidas ácidas testadas. As amostras foram imersas nas bebidas ácidas de uso comum durante 4 horas/dia, seguido da imersão em saliva artificial, durante 21 dias. De forma contínua, as amostras dos grupos NaF 0,05%, NaF 0,2%, FFA 1,23% foram imersas nas respectivas soluções a base de flúor durante 12, 73 e 48 horas, respectivamente. A superfície das amostras foi analisada por meio da microdureza Vicker's, rugosidade, microscopia eletrônica de varredura associada à espectroscopia de energia dispersiva (MEV/EDS) e microscopia de força atômica (AFM). Os dados de microdureza e rugosidade superficial foram submetidos à nested-ANOVA e Tukey (α = 0,05). As análises de MEV/EDS e AFM foram comparadas visualmente entre os grupos. Como resultados, pode-se observar que a imersão nas bebidas ácidas de uso comum (Grupo Co) diminuiu os valores de microdureza e aumentou os de rugosidade. A solução de fluoreto de sódio a 0,2% foi capaz de produzir reduções estatisticamente significativas nos valores de microdureza. Além disso, quando as amostras foram imersas posteriormente nas bebidas ácidas de uso comum tanto o Grupo NaF 0,05% quanto o Grupo NaF 0,2% apresentaram reduções significativas na microdureza. Não foi possível realizar leituras de microdureza na superfície das amostras do Grupo FFA 1,23% devido... / Abstract: The degradation of dental ceramics occurs in oral cavity and in contact with erosive solutions. Two hundred lithium disilicate ceramic disks were divided on 4 groups. The disks of Control Group (Co) were immersed in common acid beverages or in artificial saliva. The groups that were exposed to sodium fluoride 0.05% (NaF 0.05%) and 0.2% (NaF 0.2%) or in acidulated phosphate fluoride gel 1.23% were immersed in one of these solutions followed by the immersion in common acid beverages. Specimens were immersed in the common acid beverages for 4 h day-1 followed by the immersion in artificial saliva for the remaining 20 h for 21 days. Continuously, the disks of the Groups NaF 0.05%, NaF 0.2% and APF 1.23% were immersed in each fluoride solutions for 12, 73 and 48 hours, respectively. The surface of the disks was analyzed by Vicker's microhardness (HV), surface roughness (μm), scanning electronic microscopy associated with X-ray dispersive spectroscopy (SEM)-EDS and atomic force microscopy (AFM). Quantitative data were analyzed by ANOVA and Tukey's test (α = 0.05). SEM and AFM images were visually compared among groups. The immersion of the disks in test common acid beverages (Co Group) affected hardness and surface roughness results. Sodium fluoride 0.2% promoted a significant decrease in hardness results. NaF 0.05% and NaF 0.2% Groups showed significant reductions in hardness results after immersion in the common acid beverages. SEM and AFM images revealed dramatic changes in the disks of APF Group which enable the hardness test. Regardless of the solution, the disks of Co Group showed a significant increase in surface roughness when comparing them with the initial results. Superior significant results of surface roughness were observed in NaF 0.2% and APF 1.23 Groups corroborated by MEV and AFM... / Mestre

Resumo: Atualmente o titânio é empregado como biomaterial devido sua biocompatibilidade e resistência à corrosão, entretanto os íons fluoretos são efetivos no processo de corrosão. O objetivo deste estudo foi analisar a influência de um meio fluoretado com diferentes pH nas propriedades mecânicas e na resistência à corrosão dos conjuntos implantes/componentes protéticos à base de Ti c.p., a partir dos testes de ciclagem mecânica, microscopia eletrônica de varredura (MEV) e dureza. Foram simulados cinco anos de uso regular de meios de higiene oral com conteúdo de 1500 ppm de NaF, com dois diferentes pH, mediante imersão das amostras nesse meio durante 184 horas. As amostras foram testadas num durômetro Micromet 2001. Os dados dos testes de dureza foram analisados pelo teste de Wilcoxon, demonstrando que as amostras sofreram influência negativa na dureza após a ação dos íons fluoreto. Entretanto, essa influência não ocorreu nos testes de ciclagem mecânica realizados em uma máquina de ensaios universais MTS-810, fixada a 100.000 ciclos, 15Hz e programada com força de fadiga a 150 N. Pela análise de MEV e EDS não foi contatado evidências de corrosão na superfície das amostras após ação de íons fluoretos, nem incorporação de íons fluoretos sobre a superfície dos conjuntos. Concluiu-se que a concentração de flúor e o pH das soluções não exerceram influência nas propriedades mecânicas e na resistência à corrosão. / Abstract: Titanium has been widely used as biomaterial owing to its excellent corrosion resistance, mechanical properties and biocompatibility. However, it has been reported that fluoride-containing environments can attack titanium. The aim of this study was evaluated fluoride environments influence with different pH values in the implant/abutment sets. The implants were separated into 3 groups containing 7 implants/brand: one was submerged in acid fluoride environment (NaF 1500ppm 184h pH 5.3), one in neutral fluoride environment (NaF 1500ppm 184h pH 7.4), and other group in distillated water, simulating five years of dental hygiene. Hardness and surface texture were evaluated before and after fluoride exposition by Vickers method (500gf 30s) and scanning electron microscopy (SEM), respectively. The fatigue test was performed with 100.000 load cycles, 15 Hz and 150 N. There was decrease in hardness in implants submitted to the fluoride environment. SEM and EDS evaluation showed dark stains in all implants, irrespective of fluoride pH, resulting from pitting corrosion process. All sets supported the fatigue test until 100.000 load cycles. The results demonstrated that fluoride environment there was no influence in mechanical properties and corrosion resistence of the implant/abutment sets. / Orientador: Luis Geraldo Vaz / Coorientador: Elcio Marcantonio Junior / Banca: Valfrido Antonio Pereira Filho / Banca: Gibson Luiz Pilatti / Mestre

Orientador: Patrícia Petromilli Nordi Sasso Garcia / Banca: Maria Cristina Borsatto / Banca: Welingtom Dinelli / Resumo: O objetivo deste estudo foi avaliar o efeito do acabamento e polimento na estabilidade de cor e na rugosidade superficial da resina composta Filtek Supreme XT em função de diferentes soluções fluoretadas. Para isso foram confeccionados corpos-de-prova (n= 140) por meio de uma matriz de aço inoxidável hemiseccionada com quatro orifícios circulares de 10 mm de diâmetro e 2 mm de espessura. A resina composta foi inserida na matriz num único incremento e fotoativada pelo aparelho de luz halógena Curing Light XL 3000 (3M/ESPE) por 40 segundos. Metade da amostra foi submetida a procedimentos de acabamento e polimento com discos de lixa Super-Snap® em ordem decrescente de granulação. Os grupos experimentais foram divididos de acordo com a presença ou ausência de acabamento e polimento e diferentes meios de imersão (saliva artificial, solução de fluoreto de sódio a 0,05%- manipulado, Fluordent Reach, Oral B, Fluorgard). Os espécimes permaneceram imersos em saliva artificial por 24 horas e foram submetidos à análise da cor no espectrofotômetro de colorimetria (Color guide 45/0, PCB 6807 BYK-Gardner GmbH Gerestsried, Alemanha) pelo sistema CIELab e à avaliação da rugosidade superficial (Ra) pelo rugosímetro portátil (Mitutoyo surftest SJ-401, Mitutoyo Corporation, Japão). A partir deste período, foram imersos nas diferentes soluções por 1 minuto ao dia durante 60 dias. Nos intervalos entre as imersões foram mantidos em saliva artificial a 37 _ 1 0C. As leituras da alteração de cor foram realizadas após 24 e 48 horas, 7, 14, 21, 30 e 60 dias do início da imersão e a da rugosidade superficial após 60 dias. Atendidos os pressupostos de normalidade e homocedasticidade, realizou-se Análise de Variância a dois fatores e teste de Tukey para comparações múltiplas, ambos com nível de significância de 5%. Para comparação das médias de rugosidade... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of this study was to evaluate the effect of finishing and polishing procedures on the color stability and roughness of the Filtek Supreme XT resin composite surface submitted to different fluoride solutions. Samples were made (n= 140) in a hemi sectioned stainless steel mold with four 10-mm diameter and 2mm thick circular orifices. The composite resin was inserted in a single increment and light-cured with a halogen light curing unit (Curing Light XL 3000, 3M/ESPE) for 40 seconds. Half of each sample was submitted to finishing and polishing procedures with Super-Snap® grit disks in a decreasing order of granulation. Experimental groups were divided according to the presence or absence of finishing and polishing procedure and also to the different immersion media they were submitted to (artificial saliva, a manipulated 0, 05% sodium fluoride solution, Fluordent Reach, Oral B, Fluorgard). Specimens were kept in artificial saliva for 24 hours and submitted to color analysis in a colorimetric spectrophotometer (Color guide 45/0, PCB 6807 BYK-Gardner GmbH Gerestsried, Germany) by the CIELab system and to superficial roughness (Ra) evaluation by a portable rugosimeter (Mitutoyo surftest SJ-401, Mitutoyo Corporation, Japan). From this period, specimens were immersed in the different solutions for 1 minute per day, during 60 days. In periods between immersions, they were kept in artificial saliva at 37 _ 1 0C. Color alteration evaluations were performed after 24 and 48 hours, 7, 14, 21, 30 e 60 days and superficial roughness after 60 days from the beginning of immersions. After normality and homoscedasticity presumption had been confirmed, the two-way Analysis of Variance and Tukey's test for multiple comparisons were realized, both with a 5% significance level. For comparison of roughness means in baseline and in the 60 days... (Complete abstract click electronic access below) / Mestre

O objetivo deste estudo in vitro foi analisar o comportamento superficial do titânio comercialmente puro (grau 2 ASTM) usinado e obtido pelo processamento de metalurgia do pó sob a ação de diferentes soluções fluoretadas, através da análise do grau de corrosão em microscopia óptica (MO) e da rugosidade superficial. Além disso, o estudo se propôs a comparar essas análises com os resultados obtidos com o titânio fundido da dissertação de mestrado de Barros (2004). Todas as amostras receberam procedimento metalográfico padrão e foram divididas em grupos: Gr.1- saliva artificial com pH 7.0 (controle), Gr.2- gel de flúor fosfato acidulado a 1,23% com pH 3.5, Gr.3- gel de NaF a 2% com pH 6.5, Gr.4- solução de NaF a 0,05% com pH 4.0 e Gr.5- solução de NaF a 0,05% com pH 7.5. As amostras foram expostas a estas soluções por 1, 4, 8 e 16 min, intercaladas com imersão em saliva artificial por 24 h, e depois foram observadas em MO e MEV, a cada intervalo de tempo. As imagens em MO, 100x, foram classificadas através de escores de 0 a 4, conforme o grau de corrosão. A rugosidade foi analisada utilizando o parâmetro Ra. Os resultados da análise de MO foram tratados estatisticamente pelo teste qui-quadrado e da rugosidade pelo teste F de Snedecor e de Bonferroni (p<0,05). Nos três tipos de amostras, o Gr2 apresentou a corrosão mais severa, e os Gr.4 e 5 apresentaram os menores graus de corrosão. Entretanto, nas amostras usinadas o Gr5 apresentou uma corrosão menos acentuada em relação ao Gr4. No Gr3 houve um aumento da corrosão em função do tempo, sendo que as amostras fundidas mostraram este aumento mais rapidamente. Houve um aumento significativo na rugosidade superficial no Gr.2 nos três tipos de amostras. Nos diversos grupos, os valores de rugosidade superficial das amostras fundidas foram significantemente maiores que os das usinadas e as de metalurgia do pó. Os autores concluíram que as soluções fluoretadas de uso odontológico são danosas às superfícies do titânio fundido, usinado e metalurgia do pó, principalmente as soluções com alta concentração de fluoreto. / The purpose of this in vitro study was to analyze the superficial behavior of commercially pure titanium (grade 2, ASTM), obtained by milling or powder metallurgical process, under the action of different fluoride solutions through the analysis of corrosion grade under an optical microscope (OM) and superficial roughness. Furthermore the results obtained from such analyses were compared with the ones of cast titanium from Barross masters degree dissertation (2004). All specimens received the standard metallography procedure for titanium, and were divided into the following groups, according to the attack solution received: Gr.1- synthetic saliva with pH 7.0 (control), Gr.2- 1.23% acidulated phosphate fluoride gel with pH 3.5, Gr.3- 2% NaF gel with pH 6.5, Gr.4- 0.05% NaF solution with pH 4.0, and Gr.5- 0.05% NaF solution with pH 7.5. The specimens were exposed to these solutions for 1, 4, 8, and 16 minutes, and between each of these times they were immersed in synthetic saliva for 24 h. The surfaces of samples were observed under OM and SEM at each interval time. The images of 100x in OM were classified by means of scores which ranged from 0 to 4, according to corrosion grade. The rugosity was analyzed using Ra parameter. The results of OM analysis were statistically treated by means of Chi-square test and of rugosity through Snededor F test and Bonferroni test (p<0,05). In the three different types of samples, the Gr2 presented the most severe corrosion, and the Gr.4 and 5 showed the smallest corrosion grade. However in the milled samples Gr5 showed a less Sharp corrosion than Gr4. The corrosion grade of Gr3 increased according to time, but the cast specimens showed this increase more quickly. There was a significant increase in the superficial rugosity in the Gr.2 in the three types of samples. In the several groups the values of the superficial rugosity of the cast samples were significantly greater than the milled and powder metallurgical ones. The authors concluded that the fluoride solutions used in dentistry are harmful to the surfaces of cast, milled and powder metallurgical titanium, mainly the solutions with high fluoride concentration.

Nesta trabalho estudamos o efeito de refração não linear em cristais fluoretos dopados com Cr+3 e polímeros. Tais cristais fluoretos têm recebido bastante atenção dos pesquisadores por apresentarem um espectro de emissão de banda larga e ação laser sintonizável na região de aproximadamente 780-1010 nm. Aplicando a técnica de lente Térmica (LT), realizamos um estudo quantitativo do comportamento da eficiência quântica de emissão, na presença dos processos de supressão térmica da fluorescência e conversão ascendente. Apresentamos um novo método de aplicação da técnica de LT, que possibilita a determinação da eficiência quântica em função do parâmetro de saturação S (S= IM/Is, em que IM é a intensidade média incidente no material e Is a intensidade de saturação). A partir desses resultados é possível determinar o parâmetro de conversão ascendente Auger (&#947;), desde que se conheça a população total do Cr+3 ( N0) e o tempo de vida de emissão &#964;(&#964;-1=&#964;R-1+&#964;NR-1) do material investigado. Este método é apresentado para LiSAF dopados com 1% e 7% de Cr+3 , e LiSGaF 4.7% de dopagem de Cr+3, excitados em regime cw sob 15°C. No caso dos polímeros, estudamos a caracterização das propriedades não lineares (eletrônica e térmica) das amostras de polianilina (PANI) dopadas e não-dopadas com H2SO4 na forma plastificada e dissolvida em dimetil sulfóxido (DMSO). Utilizamos para isso as técnicas de LT (cw) e Z-scan (cw e pulso de 70 ps). As medidas foram realizadas em função da concentração de PANI e temperatura. Utilizando um laser de Nd:YAG com um trem de pulsos, realizamos um estudo dinâmico da não linearidade em função da concentração da PANI. Dessa forma pudemos discriminar o efeito eletrônico do efeito térmico, determinando o índice de refração não linear (n2f) um índice térmico (n2cth) que está relacionado ao parâmetro térmico dn/dT (variação do coeficiente óptico com a temperatura). / In this work we studied the effect of nonlinear refraction in Cr+3 doped fluoride host crystals and polymers. The fluoride crystals have been attractive due a broad emission bandwidth and a tunable solid-state lasing in the range of approximately 780-1010 nm. Applying the Thermal Lens (TL) technique, we accomplished a quantitative study of the behavior of the quantum efficiency, in the presence of the processes of the fluorescence thermal quenching and upconversion processes. We introduced a new method of application of the TL technique, which makes possible the determination of the quantum efficiency as a function of the saturation parameter S (S= IM/Is, where IM is the medium intensity in the material and Is, the saturation intensity). Based on those results it is possible to determine the Auger upconversion parameter (&#947;), it one knows the total population of Cr+3 (N0) and the emission lifetime &#964;(&#964;-1=&#964;R-1+&#964;NR-1) of the investigated material. This method is presented for 1% and 7% Cr+3 doped LiSAF, and 4.7% of Cr+3 doped LiSGaF, upon excitation in the cw regime at 15°C. In the case of the polymers, we studied the nonlinear properties (electronics and thermal nonlinearities) of the polyaniline samples (PANI) doped and nondoped with H2SO4 in the film form and dissolved in dimethylsulfoxide. We used the LT (cw) and Z-scan (cw and pulse of 70 ps) techniques. The measurements were accomplished as a function of the concentration of PANI and temperature. Using a laser of Nd:YAG with pulse trains, we accomplished the dynamic behavior of the optical nonlinearity as a function of the PANI concentration. By this method we were able to discriminate between electronic and thermal lensing nonlinearities, and allows the determination of the nonlinear refractive index (n2f) and thermal index (n2cth) that is related to the thermal parameter dn/dT (temperature coefficient of refractive index).

Conselho Nacional de Desenvolvimento CientÃfico e TecnolÃgico / CoordenaÃÃo de AperfeiÃoamento de Pessoal de NÃvel Superior / A aplicaÃÃo da nanotecnologia na Odontologia pode promover a otimizaÃÃo de caracterÃsticas estÃticas e mecÃnicas de materiais odontolÃgicos bem como propiciar uma aÃÃo anticÃrie pelo menor acÃmulo de biofilme oral sobre estes materiais e liberaÃÃo de compostos antimicrobianos ou remineralizantes. Os objetivos de cada capÃtulo sÃo: 1) revisar a literatura concernente ao uso de nanopartÃculas em materiais odontolÃgicos com implicaÃÃes diretas ou indiretas no controle de lesÃes de cÃrie (capÃtulo 1); 2) investigar in vitro a liberaÃÃo de flÃor e o potencial inibitÃrio de cimento ortodÃntico nanoparticulado fluoretado na desmineralizaÃÃo do esmalte (capÃtulo 2); 3) estudar o efeito in situ de resina composta fluoretada contendo nanopartÃculas na liberaÃÃo de flÃor e na capacidade inibitÃria da desmineralizaÃÃo em esmalte (capÃtulo 3); 4) avaliar o efeito da incorporaÃÃo de nanopartÃculas de prata (NAg) e fosfato de cÃlcio amorfo (NACP) em sistema adesivo comercial (capÃtulo 4); 5) avaliar o efeito da incorporaÃÃo de monÃmero associado a quaternÃrio de amÃnio (QADM), NAg e NACP em sistema adesivo experimental (capÃtulo 5) e 6) estudar o efeito in situ de resina composta contendo NACP no biofilme oral e em lesÃes de cÃries em esmalte (capÃtulo 6). Como abordagens metodolÃgicas foram realizadas: uma revisÃo de literatura, 3 estudos in vitro com induÃÃo de cÃrie por modelo microbiolÃgico e 2 estudos in situ relacionados aos objetivos citados. Como resultados, o desenvolvimento de materiais nanomÃtricos anticÃrie ainda necessita de um melhor conhecimento dos mecanismos de aÃÃo, seguranÃa e eficÃcia das nanopartÃculas (capÃtulo 1). A liberaÃÃo de flÃor e o potencial inibitÃrio na desmineralizaÃÃo do esmalte de cimento ortodÃntico nanoparticulado fluoretado foi inferior ao apresentado por cimento de ionÃmero de vidro modificado por resina (capÃtulo 2). Resina composta nanoparticulada apresentou pequena atividade anticÃrie in situ sem detrimento de sua lisura de superfÃcie (capÃtulo 3). A inclusÃo de NAg e NACP em sistema adesivo apresentou significativo efeito antimicrobiano in vitro sem diminuiÃÃo da resistÃncia de uniÃo quando comparado ao controle (capÃtulo 4). A atividade metabÃlica, produÃÃo de Ãcido lÃtico e nÃmero de unidades formadoras de colÃnias foram menores em biofilmes formados sobre sistemas adesivos experimentais contendo QADM, NAg e NACP sem diminuiÃÃo da resistÃncia de uniÃo quando comparado ao controle (capÃtulo 5). CompÃsito com NACP liberou mais cÃlcio e fÃsforo em biofilme cariogÃnico formado in situ e propiciou menores lesÃes de cÃrie em esmalte ao redor das restauraÃÃes que o compÃsito controle (capÃtulo 6). Em resumo, a presenÃa de nanopartÃculas de carga na composiÃÃo bÃsica de materiais odontolÃgicos nÃo garante por si sà uma atividade anticÃrie efetiva. A incorporaÃÃo de QADM, NAg e NACP em materiais odontolÃgicos pode permitir a promoÃÃo de um efeito anticÃrie, apresentando-se como uma promissora abordagem no desenvolvimento de materiais restauradores diretos. / The application of nanotechnology in dentistry can promote the optimization of aesthetic and mechanical characteristics of dental materials as well as provide an anticaries action due to the lowest oral biofilm accumulation on these materials and release of antimicrobial or remineralizing compounds. The objectives of each chapter are: 1) to review the literature concerning the use of nanoparticles in dental materials with direct or indirect implications for the control of caries lesions (chapter 1), 2) to investigate in vitro the fluoride release and the inhibitory potential of nanoparticulated fluoridated orthodontic cement on demineralization of enamel (chapter 2), 3) to study the in situ effect of nanoparticle composite containing fluoride on fluoride release and the inhibition of enamel demineralization (chapter 3) 4) to evaluate the effect of incorporation of silver nanoparticles (NAg) and amorphous calcium phosphate (NACP) in commercial adhesive system (chapter 4), 5) to evaluate the effect of incorporation monomer associated with quaternary ammonium (QADM), NAg and NACP in experimental adhesive system (chapter 5) and 6) to study the in situ effect of composite resin containing NACP on the oral biofilm and enamel caries lesions (chapter 6). As methodology approaches a literature review, 3 in vitro studies with microbiological caries model and 2 in situ studies were performed according to the cited objectives. As results, the developing anticaries nanomaterials still need a better understanding of the action mechanisms, safety and efficacy of nanoparticles (chapter 1). Fluoride release and the enamel demineralization inhibition of the nanoparticulated fluoridated orthodontic cement were lower than that shown by resin-modified glass ionomer cement (chapter 2). Nanoparticle-containing composite showed little in situ anticaries activity without prejudice to its surface roughness (chapter 3). The inclusion of NAG and NACP in adhesive system showed significant in vitro antimicrobial effect without decreasing bond strength when compared to control (chapter 4). Metabolic activity, lactic acid production and number of colony forming units were lower in biofilms formed on experimental adhesive systems containing QADM, Nag and NACP without decreased bond strength when compared to control (chapter 5). NACP composite released more calcium and phosphorus in cariogenic biofilm formed in situ and caused shallow caries lesions on enamel around the restorations that the control composite (chapter 6). In summary, the presence of nanoparticles fillers as basic composition of dental materials does not assure effective anticaries activity. Incorporating QADM, Nag and NACP in dental materials can promote anticaries effect, and showing as a promising approach in dental materials development.

Entre as várias terapêuticas propostas para o tratamento da osteoporose, a administração de altas doses de fluoreto é uma alternativa que ainda apresenta controvérsia na literatura. O fluoreto se destaca por influenciar na atividade dos osteoblastos, os quais são responsáveis por mediar a síntese de moléculas que compõem o osso. No entanto, o mecanismo de ação do fluoreto em células do tecido ósseo (osteoblastos, osteócitos e osteoclastos) ainda não está bem esclarecido. Neste trabalho foram utilizados camundongos com diferentes densidades ósseas, sendo 32 da linhagem C57BL/6J (menor densidade óssea) e 32 da linhagem C3H/HeJ (maior densidade óssea) com 60 dias de vida, os quais receberam água deionizada ou água com 50 ppm de fluoreto (na forma de NaF). Realizou-se os procedimentos cirúrgicos extraindo o incisivo superior esquerdo e posteriormente os animais foram eutanasiados 7, 14, 21 e 28 dias após a extração. Imediatamente após a eutanásia, foi removida a peça com alvéolo dental esquerdo. Foram feitas análises descritiva e morfométrica das lâminas obtidas (coloração em Hematoxilina Eosina). Foi utilizada análise ANOVA a quatro critérios seguida da análise de Tukey (p<0,05). Em geral, para todos os grupos, a análise histológica mostrou neoformação óssea à partir das paredes do alvéolo e formação de ilhotas ósseas invadindo o centro dos alvéolos, substituindo o tecido conjuntivo existente. O tecido ósseo neoformado substituiu aos poucos o tecido conjuntivo ao longo dos períodos experimentais, sendo esse fenômeno ligeiramente mais evidente nos camundongos da linhagem C57BL/6J. A análise morfométrica confirmou os achados histológicos em relação à quantidade de tecido ósseo neoformado e mostrou diminuição do tecido ósseo neoformado no último período (28 dias) nos animais C3H/HeJ (grupos controle e experimental). Concluimos que o processo de reparo ósseo alveolar é semelhante nas duas linhagens estudadas, porém apresentam padrão de formação óssea diferentes entre elas. O fluoreto parece influenciar as etapas do processo de reparo alveolar nas duas linhagens, aumentando a quantidade de osso neoformado, no entanto, a linhagem de camundongos C57BL/6J é mais propensa aos efeitos do flúor. / Among the various therapeutic proposals for the osteoporosis treatment, the administration of high doses of fluoride is an alternative that still has controversies in literature. Fluoride is highlighted by influencing the activity of osteoblasts, which are responsible for mediating the synthesis of bone. But, the mechanism of action of fluoride on bone cells (osteoblasts, osteocytes and osteoclasts) is not well understood. This way, this study aims to evaluate the alveolar bone repair in rats under the effect of fluoride (NaF) administered in the water. This work were used four groups of strains C57BL/6J mice (total of 32) and C3H/HeJ (total of 32) for 60 days, which received deionized water or water with 50 ppm of fluoride. The surgical procedures were made by extracting the upper left incisor and then the animals were euthanized 7, 14, 21 and 28 days. Histological analysis (Hematoxylin Eosin staining), by light microscopy, were made. The statistical analysis were made using the statistical test one-way ANOVA complemented by Tukey\'s test (p <0.05). Generally, for all groups, the histological analysis showed a new bone formed from the alveolar walls, replacing the connective tissue. The newly formed bone tissue gradually replaces the connective tissue over time; wich was more evident in C57BL/6J mice. Morphometric analisys confirmed the histological findings of the new bone formed and showed a decrease in the new formed bone in the last period (28 days) of the C3H/HeJ animals. We concluded that the process of alveolar repair is similar when it respects to the stages of repair, however they presents different pattern of new bone formation. The fluoride influences the stages of alveolar repair in both lineages, increasing the amount of bone formed, however the mice lineage of C57BL/6J is more prone to the effects of fluoride.

O balanço do fluoreto (F) dentro do corpo é modulado por sua ingestão, absorção e remoção, e os rins, responsáveis pela sua excreção do organismo, são particularmente vulneráveis à toxicidade do F. Os efeitos nefrotóxicos do F envolvem mudanças estruturais marcantes nos rins, além disso, estudos proteomicos têm mostrado grandes alterações no perfil de proteínas envolvidas em pontos chave na transdução de sinal. Estes efeitos podem influenciar negativamente no transporte iônico nos rins. A vista deste fato, o transporte iônico no canal de sódio epitelial (ENaC) é limitante para a taxa de reabsorção de sódio nos rins, sendo essencial para a manutenção do equilíbrio eletrolítico e homeostase do corpo. Assim, este trabalho objetivou investigar os efeitos do F, utilizando concentrações semelhantes às que podem ser encontradas no néfron durante a fluorose dentária, na viabilidade celular e expressão de transportadores de membrana (ENaC) em linhagem celular renal M-1. Para os ensaios de viabilidade das células da linhagem M-1 foi empregado os testes colorimétricos Cristal Violeta e MTT, utilizando as concentrações de tratamento com fluoreto de sódio (NaF) a 10, 40, 100, 200 e 400 M, durante períodos experimentais de 24, 48, 72 e 96 h. As mesmas concentrações e os mesmos tempos foram utilizados no tratamento com cloreto de sódio (NaCl), utilizado como controle na possível interferência de Na+ na modulação das células. Para a investigação da influência do F: 1) nos canais ENaC foi utilizada a técnica de imunofluorescência e 2) para a análise de expressão gênica das subunidades que formam o ENaC, foi utilizada a técnica RT-PCR. Em nossos resultados pudemos observar que as maiores concentrações tanto de NaF quanto de NaCl provocaram a diminuição da viabilidade celular para ambos os ensaios de viabilidade, no entanto, foi possível observar algumas diferenças na resposta do tratamento com NaF em comparação com NaCl, por meio do ensaio Cristal Violeta. Não foi observado diferenças nas imagens de imunofluorescêcia, mas outros aspectos morfológicos foram vistos nessas imagens, como o aparecimento de domes celular, sugerindo que até mesmo a maior concentração de F não foi capaz de inibir a proliferação celular. Nosso resultado mais significativo foi em relação à expressão das subunidades dos canais de ENaC, onde a concentração de 400 M foi capaz de diminuir bruscamente a expressão das três subunidades do ENaC, enquanto as concentrações de 100 e 200 M mostraram apresentar expressão igual e em alguns casos até maior que o grupo controle. Pudemos concluir que doses de F na ordem de micromolares podem modular a expressão das subunidades formadoras do ENaC, positivamente quando em baixas concentrações e negativamente quando em concentrações elevadas. / The balance of fluoride (F) within the body is modulated by its ingestion, absorption and removal, and the kidneys, responsible for their excretion of the organism, are particularly vulnerable to the toxicity of F. The nephrotoxic effects of F involve marked structural changes in the kidneys , in addition, proteomic studies have shown large changes in the profile of proteins involved in key points in signal transduction. These effects may negatively influence ion transport in the kidneys. In view of this fact, the ionic transport in the epithelial sodium channel (ENaC) is limiting to the rate of sodium reabsorption in the kidneys, being essential for the maintenance of the electrolyte balance and homeostasis of the body. Thus, the objective of this work was to investigate the effects of F, using concentrations similar to those found in the nephron during dental fluorosis, cell viability and expression of membrane transporters (ENaC) in renal cell line M-1. For the M-1 cell line viability assays, the Crystal Violet and MTT colorimetric assays were used, using the 10, 40, 100, 200 and 400 M sodium fluoride (NaF) treatment concentrations during experimental periods of 24, 48, 72 and 96 h. The same concentrations and the same times were used in the treatment with sodium chloride (NaCl), used as control in the possible interference of Na + in the modulation of the cells. For the investigation of the influence of F: 1) in the ENaC channels, the immunofluorescence technique was used and 2) for the analysis of gene expression of the subunits that form the ENaC, the RT-PCR technique was used. In our results it was observed that the higher concentrations of NaF and NaCl caused a decrease in cell viability for both viability assays, however, it was possible to observe some differences in NaF treatment response in comparison to NaCl, through test Crystal Violet. No differences were observed in immunofluorescence images, but other morphological aspects were seen in these images, such as the appearance of cellular \"domes\", suggesting that even the highest F concentration was not able to inhibit cell proliferation. Our most significant result was the expression of the subunits of the ENaC channels, where the concentration of 400 M was able to decrease expression of the three subunits of the ENaC, whereas the concentrations of 100 and 200 M showed equal expression and in some cases even higher than the control group. We can conclude that doses in the order of micromolar the F can modulate the expression of the ENaC forming subunits, positively when in low concentrations and negatively when in high concentrations.