Abstract : Natural materials have received a full attention in many applications because they are degradable and derived directly from earth. In addition to these benefits, natural materials can be obtained from renewable resources such as plants (i.e. cellulosic fibers like flax, hemp, jute, and etc). Being cheap and light in weight, the cellulosic natural fiber is a good candidate for reinforcing bio-based polymer composites. However, the hydrophilic nature -resulted from the presence of hydroxyl groups in the structure of these fibers- restricts the application of these fibers in the polymeric matrices. This is because of weak interfacial adhesion, and difficulties in mixing due to poor wettability of the fibers within the matrices. Many attempts have been done to modify surface properties of natural fibers including physical, chemical, and physico-chemical treatments but on the one hand, these treatments are unable to cure the intrinsic defects of the surface of the fibers and on the other hand they cannot improve moisture, and alkali resistance of the fibers. However, the creation of a thin film on the fibers would achieve the mentioned objectives. This study aims firstly to functionalize the flax fibers by using selective oxidation of hydroxyl groups existed in cellulose structure to pave the way for better adhesion of subsequent amphiphilic TiO[subscript 2] thin films created by Sol-Gel technique. This method is capable of creating a very thin layer of metallic oxide on a substrate. In the next step, the effect of oxidation on the interfacial adhesion between the TiO[subscript 2] film and the fiber and thus on the physical and mechanical properties of the fiber was characterized. Eventually, the TiO[subscript 2] grafted fibers with and without oxidation were used to reinforce poly lactic acid (PLA). Tensile, impact, and short beam shear tests were performed to characterize the mechanical properties while Thermogravimetric analysis (TGA), Differential Scanning Calorimetry (DSC), Dynamic mechanical analysis (DMA), and moisture absorption were used to show the physical properties of the composites. Results showed a significant increase in physical and mechanical properties of flax fibers when the fibers were oxidized prior to TiO[subscript 2] grafting. Moreover, the TiO[subscript 2] grafted oxidized fiber caused significant changes when they were used as reinforcements in PLA. A higher interfacial strength and less amount of water absorption were obtained in comparison with the reference samples. / Résumé : Les matériaux naturels retiennent actuellement toute l’attention dans de nombreuses applications et ceci, car ils sont biodégradables et proviennent de ressources renouvelables telles que les plantes (le lin, le chanvre, le jute, etc.). De plus, du fait de leur faible coût et de leur faible densité, les fibres naturelles cellulosiques sont d’excellents candidats pour le renforcement des composites polymères bio-sourcés. Cependant, malgré leurs nombreux avantages, leur caractère hydrophile - résultant de la présence de fonctions hydroxyle dans leur structure - limite leur application dans les matrices polymères. Ceci est dû à la faible mouillabilité existant entre les fibres cellulosiques et les matrices polymériques (généralement hydrophobes) causant une faible adhésion et une mauvaise dispersion des fibres dans la matrice. De nombreuses tentatives de modification des propriétés de surface des fibres naturelles par des traitements physiques, chimiques, ainsi que physico-chimiques ont été effectuées. Cependant, ces traitements se sont révélés incapables de guérir les défauts intrinsèques présents à la surface des fibres et d’améliorer leur résistance à l'humidité et aux alcalis. Une solution permettant d’atteindre les objectifs mentionnés serait la création d’un film mince à la surface des fibres. Cette étude vise tout d'abord à fonctionnaliser les fibres de lin par une oxydation sélective des fonctions hydroxyle présentes sur la cellulose. Cette oxydation permet la création d’une meilleure adhésion entre la surface des fibres et les couches minces amphiphiles de TiO[indice inférieur 2] créées par la technique sol-gel. En effet, le procédé sol-gel est une méthode dite douce capable de créer une fine couche d'oxydes métalliques à la surface d’un substrat. Dans l'étape suivante, l'effet de l'oxydation sur l'adhésion interfaciale entre la couche de TiO[indice inférieur 2] et la fibre, et donc sur les propriétés physiques et mécaniques de la fibre, a été caractérisé. Enfin, les fibres recouvertes de TiO[indice inférieur 2] avec et sans oxydation préalable ont été utilisées pour renforcer l’acide polylactique (PLA). Des tests de traction, d’impact et de cisaillement ont été réalisés afin de caractériser les propriétés mécaniques des composites. De plus, de la calorimétrie différentielle à balayage (DSC), des mesures d'absorption d'humidité ainsi que des analyses thermogravimétrique (ATG) et mécanique dynamique (DMA) ont été effectuées dans le but de déterminer les propriétés physiques des composites. Les résultats ont montré une augmentation significative des propriétés physiques et mécaniques des fibres de lin recouvertes de TiO[indice inférieur 2], en particulier lorsque les fibres ont été préalablement oxydées. De plus, ces fibres à la fois oxydées et greffées de TiO[indice inférieur 2] ont causé de grands changements lorsque utilisées dans le renforcement du PLA. En effet, une meilleure résistance au cisaillement interlaminaire et une diminution de la quantité d’eau absorbée est obtenue en comparaison avec les échantillons de référence.

Cette thèse de doctorat a été réalisée dans le cadre du projet Fiabilin, qui regroupe 15 partenaires industriels et académiques, et vise à structurer une filière industrielle de production de biocomposites polyamide-11/fibres de lin. Ces travaux ont pour objectif de déterminer des performances multi-échelles de ce composite 100% biosourcé, afin d’envisager son usage en substitution de composites pétrosourcés. Nous avons tout d’abord mis en évidence la sensibilité des fibres de lin aux cycles temps-température des procédés de mise en œuvre, tant du point de vue de leurs propriétés mécaniques que de leur structure biochimique. Ensuite, nous avons montré les capacités du système PA11-lin à produire des performances mécaniques en traction compétitives vis-à-vis d’autres composites pétrosourcés. La qualité de l’interface fibre/matrice du biocomposite a également été étudiée à différentes échelles, montrant une compatibilité supérieure à celles de systèmes lin-résines thermodurcissables. La fin de vie du composite PA11-lin a été envisagée à travers le recyclage par broyages et injections successives. Les propriétés mécaniques du biocomposite à fibres courtes ainsi obtenu sont semblables au composite PPgMA-lin, avec une déformation à rupture accrue et qui augmente significativement avec le nombre de recyclages. Une analyse des cycles de production de plusieurs composites révèle les plus faibles impacts environnementaux du PA11-lin lors d’un dimensionnement des pièces en rigidité équivalentes. / This thesis has been carried out as part of the project Fiabilin, which includes 15 different academic and industrial partners, with an aim to develop industrial production of polyamide-11/flax biocomposite. The purpose of this work is to determine multi-scale performances of 100% biosourced composite, in order to substitute composite materials containing glass fibers and/or matrix derived from petroleum. First, we highlighted the flax fiber sensibility toward processing cycles (time and temperature), from mechanical and biochemical structure aspects. Then, we revealed the capacity of PA11-flax association to produce competitive mechanical properties compared to others usual composites. Fiber-matrix interface of the biocomposite was studied at micro and macro scales, showing a higher compatibility than some flax-thermoset resin systems. The end-of-life of the biocomposite was considered by recycling with successive grinding and injections. Then stiffness and strength at break of short fiber biocomposites thus obtained are similar to PPgMA-flax composites, whereas a strong increase of the strain at break according to the number of injection cycles was observed. A life cycle analysis of some composites production steps shows lower environmental impacts of PA11-flax when sizing was made through equivalent material stiffness.

Avec les préoccupations environnementales actuelles, la recherche se tourne vers des solutions alternatives à l’utilisation de fibres synthétiques. Les fibres végétales apparaissent comme de bonnes candidates, avec de bonnes propriétés spécifiques. Cependant, leur faible durabilité constitue une problématique majeure, notamment lorsque les composites sont soumis à des sollicitations hygro(hygro)thermiques.L’objectif de cette thèse est donc d’analyser et de comprendre les mécanismes de dégradation au cours de sollicitations hydro-thermo-mécaniques, afin de réaliser un modèle prédictif de la durabilité de ces composites.Pour cela, le procédé de fabrication a été étudié et optimisé afin d’obtenir des composites robustes et répétables. Deux matériaux ont ainsi été fabriqués, différenciés par leurs taux volumiques de fibres, de 37.7 % et 51.1 %.Des campagnes expérimentales avaient pour but la caractérisation du comportement mécanique des matériaux sous différentes sollicitations. Un vieillissement hydrothermique a été étudié via des essais sous chargement monotone et des essais sous chargement cyclique (fatigue) en immersion in situ. Aussi, un vieillissement hygrothermique cyclique a été étudié afin de se rapprocher des conditions de service visées.Ces différentes campagnes expérimentales ont mis en évidence le fait que les composites étudiés présentent une forte chute de propriétés mécaniques en fonction du vieillissement, avec une influence finalement peu significative du taux volumique de fibres sur les propriétés après vieillissement, ce qui permet de questionner l’utilité industrielle d’atteindre ces taux volumiques de fibres.Les propriétés mécaniques élastiques sous chargement monotone après des cycles de sollicitations hygrothermiques sont stables après le premier cycle, ce qui peut être rassurant pour une utilisation de ces matériaux. En revanche, des endommagements semblent s’accumuler jusqu’à environ 4 cycles avant de se stabiliser.Les résultats en fatigue montrent également que la saturation peut améliorer la résistance en fatigue en dessous d’une certaine contrainte maximale appliquée, ce qui est particulièrement intéressant pour l’utilisation industrielle visée.Un modèle a pu être implémenté, intégrant l’évolution des propriétés mécaniques au cours de la diffusion, étudiée sur une surface. Ce modèle a permis non seulement de montrer que le matériau est globalement en compression, ce qui est cohérent avec le gonflement contraint des fibres dans la résine, notamment, mais également de mettre en évidence des développements qui seraient nécessaires afin d’aboutir à un modèle prédictif robuste, dont notamment des couplages forts en intégrant une modification de la diffusion en fonction de l’état de contraintes et de déformations des constituants.De nombreuses perspectives ont été discutées, notamment sur des campagnes expérimentales lors de sollicitations mécaniques multiaxiales ou avec des modes de rupture différents (choc, fluage). De plus, le modèle prédictif n’est pas encore atteint et des développements nécessaires ont été identifiés. / With the current environmental concerns, research turns to alternative solutions to synthetic fibres. Vegetal fibers appears as good candidates, with good mechanical properties. However, their low durability is a major issue, especially when the composites are exposed to hydro(hygro)thermal loadings.The purpore of this thesis is to analyse and understand the degradation mechanisms when hydro-thermo-mechanical loadings are applied, in order to implement a predictive modelisation of the composite durability.The manufacturing process wasstudied and optimised to produce reproducible and strong composites. Two materials were produced. Their only difference is their volumetric fiber contents (37.7 % and 51.1 %).Experimental campaigns were led to characterize the composite mechanical behavior under different loadings. A hydrothermal ageing was studied through monotonic mechanical testing and cyclic mechanical testing (fatigue) with in situ immersion. A hydrothermal ageing was also studied in order to be closer to the aimed service conditions.These differents test campaigns showed an important loss of mechanical properties with the ageing processes. The volumetric fiber contents also showed almost no difference after the hydrothermal ageing. The industrial use of a high fiber content can then be questionned.After the first hygrothermal cycle, the composite mechanical elastic properties were found constant, which is reassuring for an industrial use. However, damages accumulated throughout the first 4 cycles before stabilizing.Fatigue results showed that the saturation can enhance the fatigue resistance below a certain maximal loading, which is very interesting for the aimed industrial use.A surfacic numeric modelisation was implemented with the evolution of the mechanical properties thoughout the diffusion process. This modelisation showed that the composite is mostly in compression, which is expected from the constrained swelling of the fibers within the resin, but also showed some developpement ideas which would be necessary to achieve an accurate predictive modelisation. Among these ideas, strong coupling between the diffusion process and the internal strains/stresses of the components.Numerous perspectives were discussed. Multiaxial loadings or breakage mode with impact or creep tests were mentionned. Moreover, the predictive modelisation that was aimed was not achieved yet, but amelioration axes were identified.

Dans ce travail de thèse on a examiné expérimentalement l’efficacité épuratoire d’un dispositif de filtration, constitué de sable concassé et de nappes de géotextile en fibre de lin, à l’échelle de laboratoire afin d’installer en conditions locales (Agglomération Havraise) un site expérimental en vraie grandeur. Deux types d’essais ont été utilisés : (1) Des essais batch pour quantifier le potentiel de sorption des ions plomb, cuivre et zinc par les étoupes de fibres de lin à partir d'une solution aqueuse. (2) Des essais de filtration de longue durée dans des colonnes en laboratoire remplie de sable concassé avec et sans strates de géotextile en fibres de lin pour étudier l'influence de la présence de géotextiles sur le transfert et la rétention (i) des particules en suspension non polluées (particules de kaolinite) (ii) des métaux lourds solubles dans l'eau (iii) des métaux lourds sous forme particulaire (ions métalliques adsorbés sur les particules de kaolinite en suspension) et métaux lourds et solubles dans l'eau. Les essais de sorption ont montré que l'adsorption des ions métalliques par les fibres de lin est favorable avec une capacité d'adsorption maximale de 9,9 ; 10,7 et 8,4 mg g-1 respectivement pour le cuivre, le plomb et le zinc. Les essais de filtration ont montré que la présence des géotextiles dans le sable influence le transfert des métaux lourds, sous les deux formes soluble et particulaire. La rétention des métaux dans le sable est favorisée et les profils de rétention sont modifiés. De plus, et contrairement aux géotextiles synthétiques, les géotextiles en fibres de lin contribuent eux-mêmes à la rétention d’une fraction non négligeable de polluants métalliques sous forme soluble et particulaire dans leur propre structure. L’efficacité globale de rétention des métaux par le dispositif de filtration est améliorée. Ces résultats sont de bons indicateurs pour envisager l'utilisation de matériaux à base de fibre de lin dans la conception de systèmes de traitement local des eaux de ruissellement et l'élimination de polluants métalliques. / In this thesis work, the purification efficiency of a filtration device, consisting of crushed sand and flax fiber geotextile layers, was investigated experimentally at the laboratory scale in order to install in local conditions (Havre agglomeration) an experimental site in full size. Two types of tests were used: (1) Batch tests to quantify the sorption potential of lead, copper and zinc ions by flax fiber tows from an aqueous solution , (2) Long-term filtration tests in laboratory columns filled with crushed sand with and without flax fiber geotextile layers to study the influence of the presence of geotextiles on the transfer and retention of (i) particles in unpolluted suspension (kaolinite particles) (ii) water-soluble heavy metals (iii) heavy metals in particulate form (metal ions adsorbed on suspended kaolinite particles) and heavy and water-soluble metals. Sorption tests have shown that the adsorption of metal ions by flax fibers is favorable with a maximum adsorption capacity of 9.9; 10.7 and 8.4 mg g-1 respectively for copper, lead and zinc. Filtration tests have shown that the presence of geotextiles in sand influences the transfer of heavy metals, in both soluble and particulate forms. The retention of metals in the sand is favored and the retention profiles are modified. In addition, and unlike synthetic geotextiles, flax fiber geotextiles themselves contribute to the retention of a significant fraction of metal pollutants in soluble and particulate form in their own structure. The overall metal retention efficiency of the filtration device is improved. These results are good indicators for considering the use of flax fiber materials in the design of local stormwater treatment systems and the removal of metal pollutants.

Cette thèse s’intéresse au tissage et au préformage de renforts fibreux à base de fibres de lin. Avant d’être utilisés, ces fibres sont disposées en faisceaux de faible longueur (~ 30 mm en moyenne) et ont besoin d’être assemblées pour constituer un renfort linéaire continu. L’utilisation de rubans ou de rovings sans torsion est recommandée pour des applications composites. Dans un premier temps, cette étude se concentre sur l’élaboration et l’utilisation de rovings traités par un agent d’encollage et sans torsion ainsi que sur l’influence des paramètres du procédé de tissage sur les propriétés mécaniques et les caractéristiques textiles des renforts tissés. Pour éviter l’endommagement de ces rovings durant le tissage, des solutions sont proposées. Dans un second temps cette thèse s’intéresse à la mise en forme de ces renforts sur une géométrie complexe. Ce travail se concentre alors sur l’étape de préformage du procédé RTM. Une approche expérimentale est abordée pour identifier et quantifier les défauts apparaissant durant l’emboutissage sur une géométrie complexe comme le tétraèdre. Cette analyse se concentre en particulier sur le défaut de bouclage causé par un fléchissement des mèches. Des solutions comme l’optimisation de l’architecture des renforts sont observées pour obtenir cette géométrie complexe sans défaut avec des renforts à base de fibres de lin. La forme, le positionnement ainsi que la pression appliquée sur les serre-flans maintenant le renfort au cours du passage du poinçon influent également sur la génération des défauts. L’optimisation du procédé d’emboutissage pour empêcher l’apparition de boucles sur les préformes conclut ce travail. / This work focuses on the weaving and forming of flax based reinforcements. Before being woven, naturalfibres on the form of finite length bundles (~ 30 mm in average for flax) need to be assembled together in a1D continuous product. The use of roving or slivers without twist is rather recommended for compositeapplications. In a first part, this study focuses on the manufacturing and the use of untwisted rovings treatedwith a bonding agent as well as on the weaving process parameters that may influence the mechanicalproperties and the textile characteristics of the woven fabric. Solutions to prevent roving defects duringweaving are proposed. In a second part, this study investigates the ability to develop composite parts with complex geometrieswithout defect. It focuses on the first step of RTM process which consists in forming dry fibrousreinforcements. An experimental approach is used to identify and quantify the defects. The buckling defectcaused by the bending of tows during the preforming step is particularly investigated. Solutions to realize acomplex shape such as a tetrahedron without any defect from flax based woven reinforcements areproposed. With optimized reinforcement architecture, buckling can be prevented. Another solutionconsisting in optimising the process parameters such as the blank holder geometry or the blank holderpressure to prevent the appearance of buckles from commercial fabrics was also investigated with success.

No description available.

Les composites bio-sourcés et notamment à base de fibres de lin connaissent depuis quelques années un regain d’intérêt, particulièrement dans les domaines des transports, de la mobilité et des loisirs. En effet, le faible coût énergétique et environnemental de la fibre de lin lui confère un avantage face à la fibre de verre, tout en la concurrençant en termes de propriétés mécaniques spécifiques. Cependant le comportement à long terme en environnement humide des composites à base de fibres de lin reste méconnu et constitue un frein à leur utilisation à plus grande échelle. Les objectifs de ces travaux sont de donner des clés pour produire un composite lin/époxy de haute qualité et de contribuer à l’amélioration de la connaissance de la durabilité de ces matériaux. Tout d’abord, l’influence de nombreux paramètres de mise en œuvre [(i) le pré conditionnement des renforts, (ii) la température de cuisson, (iii) la pression appliquée lors de la cuisson, (iv) la vitesse de refroidissement, (v) la température de sortie de la plaque, (vi) la température de post-cuisson et (vii) la durée de post-cuisson] sur les propriétés mécaniques des composites a été étudiée afin d’obtenir des matériaux de haute qualité. Une méthode de vieillissement « réaliste » a ensuite été développée afin d’étudier la durabilité de ce type de composites en présence d’eau. Des cycles de vieillissements hygrothermiques ont ainsi été menés en laboratoire sur des éprouvettes de composite, de résine et des faisceaux de fibres. Puis des analyses multi-échelles basées sur des caractérisations physico-chimiques, microstructurales et morphologiques du composite lin/époxy au cours de ce vieillissement ont permis de mieux comprendre les mécanismes responsables de leurs évolutions de propriétés mécaniques longitudinales et transverses au cours du temps. / In recent years there is renewed interest for bio-sourced composites, including those based on flax fibers, and especially in the field of transport, mobility and leisure. In fact, the lower energy cost and environmental impact of flax fiber give it an advantage over glass fiber, while competing with its specific mechanical properties. However, flax fibers based composites long-term behavior remains poorly known in damp environments and constitutes an obstacle to a wider use. This work aims to provide adapted parameters to produce a high-grade flax/epoxy composite and to contribute to improve the durability knowledge of these materials. First, the influence of many processing parameters [(i) conditioning of the reinforcements, (ii) curing temperature, (iii) curing pressure, (iv) cooling speed, (v) exit temperature, (vi) post curing temperature and (vii) post curing duration] on the composites’ mechanical properties have been studied in order to manufacture high-grade materials. Then a “realistic” ageing method has been developed to study the durability of this kind of composites when exposed to water. Thus cyclic hygrothermal ageing has been applied to composite, resin and fiber bundles in the laboratory. Then multi-scale analyzes based on physicochemical, microstructural and morphological characterizations of the flax/epoxy composites helped to better understand the mechanisms responsible for the longitudinal and transverse mechanical properties’ evolutions over time.

Les éco-composites s'imposent progressivement comme une alternative à certains matériaux classiques. L'utilisation de fibres végétales en guise de renfort permet en effet d'améliorer les performances environnementales de ces matériaux ainsi que leurs propriétés spécifiques élevées. Dans ce contexte, cette étude propose d'élaborer un éco-composite sandwich dont les peaux sont constituées d'une résine thermoplastique innovante associée à des fibres de lin et à une âme en balsa. Tout d'abord, les comportements statiques de la résine et de l'âme sont analysés. Par la suite, le composite renforcé de fibres de lin constituant les peaux du sandwich est étudié. Les caractéristiques élastiques principales du pli UD en contraintes planes sont déterminées. De plus, une analyse des mécanismes d'endommagement est effectuée au moyen de la technique d'émission acoustique. Le comportement des poutres sandwiches sollicitées en flexion est ensuite étudié. Une attention particulière est portée à la compréhension des modes de rupture et à l'influence des variations locales des propriétés mécaniques de l'âme. Par ailleurs, certaines propriétés dynamiques de cette structure sont explorées, notamment son comportement en fatigue et sa réponse à l'impact afin de discuter de sa durabilité. Enfin, une étude expérimentale du comportement vibratoire des poutres composites et sandwiches est réalisée. Le rôle des différents constituants dans l'amortissement global des vibrations est discuté au moyen d'une modélisation par élément finis. L'ensemble des propriétés déterminées sont comparées à celles des matériaux non bio-sourcés, afin de situer ses performances. / Bio-based composites appear to be very promising alternatives to traditional composites. The use of natural fibres as reinforcement reduces the environmental impact of these materials and their specific properties are significantly increased. In this context, this work focuses on the manufacturing and the mechanical characterization of a bio-based sandwich structure. The skins are made of an innovative thermoplastic resin associated with flax fibres. The core is made of balsa wood. First, quasi-static analyses are performed on the different components. Then, the tensile properties of the composite skins are studied. Moreover, the main damage mechanisms are identified and described by means of the acoustic emission technique. Next, the flexural behavior of the whole sandwich structure is studied. Particular attention is paid to the detection and prediction of the main fracture modes. Moreover, the statistical spreads of the material properties of the balsa core are taken into account. In addition, cyclic fatigue and impact tests are performed to investigate the behavior of this structure under dynamic loads, and to discuss whether or not this material could be suitable for potential semi-structural applications. Finally, experimental analyses of the vibration behavior of composite and sandwich beams are performed. The contributions of the different components to the global damping properties of the sandwich structure are analyzed by means of a finite elements model. This work also compares the properties of this bio-based sandwich to those of traditional materials, in order to benchmark its mechanical performances with a view to further industrial usage.

Ce travail vise à étudier le comportement mécanique des composites renforcées par des fibres de lin ainsi que le comportement mécanique et hydrique des composites hybrides. Un taux de porosité élevée observée chez ces matériaux conduit à une dégradation des propriétés mécaniques. Des essais de traction et de flambement avec suivi par émission acoustique ont permis d’identifier les mécanismes d’endommagements qui règnent dans ces matériaux et à mettre en évidence leur chronologie d’apparition. Des observations microscopiques des faciès de rupture ont permis de valider ces résultats. Une optimisation des propriétés mécaniques et notamment en termes de réduire le taux de porosité a été testée et ceci en insérant des fibres de carbone dans la structure. Les résultats ont montré que la position des fibres de carbone est primordiale dans l’amélioration des propriété hydrique et mécaniques. / This work aims to study the mechanical behavior of composites reinforced by flax fibers as well as the mechanical and water behavior of hybrid composites. A high porosity rate observed in these materials leads to a degradation of the mechanical properties. Tensile and buckling tests with acoustic emission monitoring have identified the mechanisms of damage that reign in these materials and highlight their chronology appearance. Microscopic observations of fracture facies validated these results. An optimization of the mechanical properties particularly in terms of reducing the porosity rate has been tested by inserting carbon fibers in the structure. The results showed that the position of carbon fibers is essential in the improvement of water and mechanical properties.

Durant les dernières décennies, les composites polymères renforcés par des fibres végétales ont reçu une attention importante de la part des scientifiques. L’utilisation de fibres végétales permet en effet d’améliorer les performances environnementales de ces matériaux tout en atteignant des propriétés spécifiques plus élevées. Néanmoins, un verrou majeur freine encore le développement de ces matériaux. En effet, leur sensibilité au vieillissement hydrique, due à leur caractère hydrophile, restreint leur utilisation. Dans ce contexte, nous proposons, dans le cadre de cette thèse, d’analyser l’effet du vieillissement hydrique sur le comportement statique et dynamique, d’identifier et suivre les mécanismes d’endommagement d’une structure sandwiche biosourcée et ses constituants. Les composites utilisés sont constitués d'une résine greenpoxy associée à des fibres de lin et à une âme en liège pour les sandwichs. Dans la première partie, nous avons étudié le comportement en statique et en dynamique de la résine, du composite, des âmes et des sandwichs. Cette étude a conduit d’une part à la détermination des caractéristiques mécaniques et à l’identification et le suivi des mécanismes d’endommagement par émission acoustique et observations microscopiques et d’autre part à la détermination des caractéristiques dynamiques. Dans la deuxième partie, nous avons analysé la cinétique de diffusion d'eau dans la résine, les peaux, les âmes et les sandwichs par identification de leurs paramètres de diffusion par le modèle de Fick. En suite, nous sommes intéressés à l’impact du vieillissement hydrique sur le comportement et les propriétés mécaniques des sandwichs et ses constituants. / In recent decades, polymer composites reinforced with plant fibers have received significant attention from scientists. The use of reinforcing vegetable fibers makes it possible to improve the environmental performance of these materials reaching higher specific properties. Nevertheless, a major lock still hinders the development of these materials. Indeed, their sensitivity to water ageing, due to their hydrophilic nature, restricts their use. In this context, we propose, as part of this thesis, to analyze the effect of water ageing on static and dynamic behavior, to identify and monitoring the damage mechanisms of a sandwich structure biobased and its constituents. The composites used consist of a greenpoxy resin associated with flax fibers and a cork core for sandwich materials. In the first part of this work, we studied the static an dynamic behavior of the resin, the composites, cores and sandwich structures. This study led on the one hand to the determination of the mechanical characteristics and to the identification and the follow-up of the mechanisms of damage by acoustic emission and microscopic observations and on the other hand to the determination of the dynamic characteristics. In the second part, we first analyzed the kinetics of water diffusion in resin, skins, cores and sandwichs by identification of their diffusion parameters by the Fick model approach. Then, we are interested in the impact of water ageing on the behavior and mechanical properties iof sandwichs and its constituents.