Includes bibliographical references (leaves [1-20]). / xxi, 168, [20] leaves : ill. (some col.) ; 30 cm. / Title page, contents and abstract only. The complete thesis in print form is available from the University Library. / A systematic analysis of wear involving the in vitro analysis of the wear of standard composite resin and glass ionomer cements restorations under controlled conditions; and, the qualitative and quantitative investigation of wear over a range of pH's and loads which might be encountered clinically in order to develop a "wear map" of the micromorphology of wearing teeth and restorations and a systematic modeling of wear rates. / Thesis (Ph.D.)--University of Adelaide, Dept. of Dentistry, 2001

Submitted by CAMILA AUGUSTO SILVEIRA null (mila_rock_bull@hotmail.com) on 2016-01-25T17:55:14Z No. of bitstreams: 1 tese Camila 25.01.2016 final pdf.pdf: 1354976 bytes, checksum: 4ab9699639ad08683e783abe0d66648c (MD5) / Approved for entry into archive by Sandra Manzano de Almeida (smanzano@marilia.unesp.br) on 2016-01-26T12:07:14Z (GMT) No. of bitstreams: 2 silveira_ca_me_sjc_int.pdf: 1354976 bytes, checksum: 4ab9699639ad08683e783abe0d66648c (MD5) silveira_ca_me_sjc_par.pdf: 411993 bytes, checksum: b5c5a046719cd7dd1155e259de7e081c (MD5) / Made available in DSpace on 2016-01-26T12:07:14Z (GMT). No. of bitstreams: 2 silveira_ca_me_sjc_int.pdf: 1354976 bytes, checksum: 4ab9699639ad08683e783abe0d66648c (MD5) silveira_ca_me_sjc_par.pdf: 411993 bytes, checksum: b5c5a046719cd7dd1155e259de7e081c (MD5) Previous issue date: 2016-01-08 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo do presente estudo foi avaliar um novo protocolo multidisciplinar por meio de um estudo clínico randomizado para o tratamento de recessões gengivais associadas à lesão cervical não-cariosa. Foram selecionados 40 pacientes alocados aleatoriamente em dois grupos: Grupo Teste (n=20), restauração parcial da lesão cervical e cirurgia para recobrimento radicular com enxerto de tecido conjuntivo (CTG+RP) e Grupo Controle (n=20), aplainamento da lesão cervical e cirurgia para recobrimento radicular com enxerto de tecido conjuntivo (CTG). Os grupos foram comparados quanto ao sangramento à sondagem (SS), índice de placa (IP), recessão gengival relativa (RGR), nível clínico de inserção (NIC), altura e largura das papilas (AL, LP),altura e espessura do tecido queratinizado (ATQ e ETQ), profundidade da lesão cervical (PLC), hipersensibilidade dentinária (HD) e na avaliação estética (MRES) durante um período de 6 meses. Após 6 meses, as porcentagens médias de recobrimento da altura da lesão cervical não-cariosa foram de 72,34±25,2 para o grupo teste e 74,85±33,1 para o grupo controle, sem diferença estatística entre eles. Foi notada diferença estatisticamente significante quando a hipersensibilidade cervical foi analisada. O grupo teste mostrou-se mais eficaz em 6 meses de acompanhamento na resolução desse sintoma (p=0,034). Na análise individual dos parâmetros da escala MRES, o grupo teste mostrou um melhor contorno gengival com diferença significante em relação ao grupo controle. Nos demais parâmetros, não houve diferenças significantes. Dentro dos limites do presente estudo, pode-se concluir que ambos os tratamentos foram efetivos e que a presença da restauração parcial de resina composta não interfere na taxa de recobrimento quando o retalho posicionado coronariamente associado ao enxerto de tecido conjuntivo é utilizado para o tratamento de recessões gengivais associadas à lesão cervical não-cariosa, além de proporcionar um melhor controle da hipersensibilidade dentinária e resultado estético mais harmonioso. / The aim of this study was to evaluate a new multidisciplinary protocol by means of a randomized controlled clinical trial for the treatment of gingival recession associated with cervical lesion non-carious. Were selected 40 patients randomly allocated to one of the following groups: Test group (n = 20), partial restoration of cervical lesion and surgery for root coverage with connective tissue graft (CTG + PR) and control group (n = 20), planning of non-carious cervical lesion and surgery for root coverage with connective tissue graft (CTG + RT). The groups were compared as to bleeding on probing (BOP), biofilm accumulation (IP), relative gingival recession (RGR), clinical attachment level (CAL), height and width of papillae (PH, PW), height and thickness of keratinized tissue (KTH and KTT), depth of the cervical lesion (CLD), dentin hypersensitivity (DH) and aesthetic evaluation (AE) for a period of 6 months. Average percentage rates of root coverage for test and control group were 72.34% and 74.85%, respectively. No significant statistical difference between test and control was observed regarding root coverage. A significant difference (p=0.034) was found for dentin sensitivity when control and test were compared. The test group showed better results regarding this parameter. The individual aesthetic analysis of MRES parameters, the test group showed a better gingival contour with a significant difference compared to the control group. When the other parameters were compared between the two groups, no difference was found. Within the limits of this study it can be concluded that both treatments were effective and that the presence of the partial restoration composite resin does not affect the root coverage when the coronally advanced flap associated with connective tissue graft is used for the treatment of gingival recession associated with non-carious cervical lesion, and provide better control of dentin hypersensitivity and harmonious aesthetic results.

Made available in DSpace on 2015-01-26T13:21:31Z (GMT). No. of bitstreams: 0 Previous issue date: 2000-03-06Bitstream added on 2015-01-26T13:30:17Z : No. of bitstreams: 1 000134871.pdf: 7061870 bytes, checksum: 73e133b2649ba2fd2f69348825cc9651 (MD5) / O objetivo desse trabalho foi avaliar in vitro a microinfiltração marginal de cavidades de classe V preparadas com turbina de alta rotação (AR), jato abrasivo (AB), ultra-som (US) e laser de Er:YAG (LA) e restauradas com um sistema adesivo multi-passos e um auto-condicionante. Foram selecionados 160 incisivos bovinos para prepare das cavidades na face vestibular, com margem gengival localizada na junção esmalte-cemento e margem oclusal em esmalte. Os materiais utilizados foram Scotchbond Multi-uso Plus/3M (SBMUP), Etch&Prime 3.0/Degussa (EP) e a resina composta Z1 00/3M. Os dentes foram divididos em oito grupos de vinte, de acordo com equipamento e sistema adesivo empregado: a) AR + SBMUP; b) AR + EP; c) AB + SBMUP; d) AB + EP; e) US+ SBMUP; f) US+ EP; g) LA+ SBMUP; e h) LA+ EP. Os dentes restaurados foram armazenados a 37°C par 6 dias, termociclados (500: 5-55°C) e colocados em solução de Rodamina B a 2% por 24 horas. Em seguida foram seccionados e avaliados em lupa estereomicroscópica para determinar o grau de microinfiltração segundo uma escala de 0 a 4. Os dados foram submetidos aos testes estatísticos de Sinais de pastas de Wilcoxon, Kruskai-Wallis e Tukey. Houve diferença estatisticamente significante entre as margens, com maior microinfiltração na cervical; o melhor selamento marginal foi obtido no grupo US/SBMUP; não houve diferença estatisticamente significante entre os preparos cavitários realizados com laser de Er: YAG e alta-rotação e alta-rotação e abrasão a ar; os maiores valores de microinfiltração foram obtidos no grupo AB/EP / The aim of this study was to evaluate in vitro the marginal microleakage of class V prepared with high-speed (HS}, air abrasion (AA), ultrasound (US) and Er:YAG /aser(LA), and restored with multi-step or self-etching adhesives systems. One-hundred-sixty incisives bovine teeth were selected for the cavity preparation on the buccal surface with the gingival margin at the enamel-cement junction and occlusal margin in enamel. The materials Scotchbond Multi Purpose/3M (SBMUP) and Etch&Prime 3.0/Degussa (EP) and Z10013M composite resin were used in this study. The teeth were divided in eigth groups with 20 teeth in each froup according to the equipment and to the adhesive system used: HS + SBMUP; HS +EP; AA +SBMUP; AA + EP; US+ SBMUP; US+ EP; LA+ SBMUP; LA + EP. The restored teeth were stored at 37CC for 6 days, thermocycled (500: 5-55 C) and kept in a 2% Rodamine B solution tor 24 hours. After this they were seccioned and evaluated through stereomicroscope in order to determine the micro/eakage degree according to 0-4 score. The data were submitted to the Wilkoxon, KruskaiWal/ is and tukey statistical tests. There was significant statistical difference among the margins with the highest microleakage degrees in the cervical area; the best marginal sealing was with the US + SBMUP group. There was no significant statistical difference among the cavity preparations made with the Er:YAG laser and high-speed and high-speed and air abrasion. The highest microleakage values were found in the AA +EP group

The issue of skin friction related injuries has been one of the problems challenging the artificial sports turf industry. It has been identified by users as a major factor impeding acceptance of artificial turf at the professional level. However, information explaining the mechanisms for skin-turf abrasion is limited and little progress has been made, it appears, to derive an appropriate testing method for product approval or in evidence of improvement of the skin-friendliness of these products in sport surface surfaces. This research project focused on exploring the potential for improving the skin-friendliness of artificial turfs through a multi-faceted approach: identifying the contribution of the abrasive-components in modern artificial turf surfaces through mechanical testing; while critically evaluating currently available skin friction standards , evaluating strategies for polymer material modifications to reduce the skin-surface friction; and the designing of an appropriate bench-top set-up for the lab-based assessment of material skin-friendliness. The lack of understanding of skin-turf interaction was addressed by identifying the turf-component that has the greatest influence on the skin-turf friction with the mechanical device used in the current industry standard. The skin -turf frictional profiles of a series of third generation (3G) turf surfaces were examined, in combination with independent measurements of the silicone skin surface roughness pre- and post-friction testing. Results indicated that turf carpets without any infill material exhibited the highest frictional values while surfaces completely filled with either sand or rubber displayed similarly low frictional values, independent of infill type. Morphological measurements also showed the largest decrease in surface roughness for skin samples tested on carpet-only surfaces, indicating a smoothening effect via abrasion. This abrading effect is alleviated with the addition of infill to the surface, with fully-filled surfaces having the least damage to the skin s. This unprecedented study suggests that the carpet may have the largest influence on the overall frictional behaviour of an artificial turf surface narrowing down the turf component to be targeted when applying product improvements to address skin-friendly properties. The strategy of material surface modification was then employed, to study the effect of polyzwitterionic brushes on improving the skin-friendliness of the identified polypropylene substrate. To address the intended application for artificial turfs, a bench-top test was developed to investigate the frictional properties of the hydrated samples outside of commonly used aqueous environments, where an excess of lubricating water molecules is absent. Photo-grafted poly(sulfobetaine methacrylate) (pSBMA) brushes of various irradiation durations were prepared and the improvement in frictional properties was studied. Frictional measurements using silicone skin tips, under both dry and hydrated surface conditions, showed that the applied modification was capable of forming a stable lubrication layer in the absence of excess water, significantly reducing the coefficient of friction by up to 78.8 %. The pSBMA brushes also provided the additional advantage of antifouling exhibiting resistance towards pathogenic Staphylococcus aureus with almost zero surface colonization for well-grafted samples. The low skin -sample friction under ambient conditions and desirable fouling-resistance highlights the potential of pSBMA brushes as a modification strategy for achieving skin-friendly surfaces targeted at reducing the risk of skin abrasions. The tribological implications of counter-surface selection were investigated. Frictional assessments of the pSBMA-modified samples were carried out using standard steel tribo-tips, in addition to the skin tips used. Measurements with the skin tips showed that the hydrated pSBMA brushes were successful in reducing initial skin -sample friction though the effect diminishes with extended testing, attributed to the drying of the interfacial water. The standard steel tribo-tips were unable to reciprocate these results, returning consistently low frictional values regardless of extent of surface modification or hydration. These observations draw attention to the importance of counter-surface selection in frictional assessments, highlighting how appropriate test materials can identify characteristic surface properties while providing an interaction that simulates that of the intended application. The simple experimental set-up used may potentially be enhanced as an intermediate product qualification method in the manufacturing of skin-friendly artificial turf yarns.

Submitted by Samira Branco Martins (samirabmartins@foar.unesp.br) on 2018-08-30T19:44:38Z No. of bitstreams: 1 TESE DOUTORADO SAMIRA .pdf: 933881 bytes, checksum: 1ebe4097c1b2d6665a4be82cc94f2dfa (MD5) / Rejected by Marley Cristina Chiusoli Montagnoli (marley@foar.unesp.br), reason: Por favor, fazer as seguintes correções: - inserir a ficha catalográfica no arquivo de sua tese; - quando for preencher metadados, preencher o campo Agência de fomento. on 2018-09-04T12:52:59Z (GMT) / Submitted by Samira Branco Martins (samirabmartins@foar.unesp.br) on 2018-09-06T18:29:33Z No. of bitstreams: 1 TESE DOUTORADO SAMIRA .pdf: 1082516 bytes, checksum: 012f9fe0b3e970650b71802c977af92d (MD5) / Rejected by Marley Cristina Chiusoli Montagnoli (marley@foar.unesp.br), reason: A ficha catalográfica está fora do padrão. Quando for inserir no seu arquivo observar em opções de colagem e escolher a opção que não desconfigure a sua ficha. Qualquer dúvida procure a Biblioteca de sua unidade. on 2018-09-06T19:06:06Z (GMT) / Submitted by Samira Branco Martins (samirabmartins@foar.unesp.br) on 2018-09-06T20:03:50Z No. of bitstreams: 1 TESE DOUTORADO SAMIRA.pdf: 939079 bytes, checksum: 5d37e78b11c143842a751fbaf6498aa2 (MD5) / Approved for entry into archive by Marley Cristina Chiusoli Montagnoli (marley@foar.unesp.br) on 2018-09-10T17:35:24Z (GMT) No. of bitstreams: 1 martins_sb_dr_arafor.int.pdf: 879795 bytes, checksum: 35bf73c7fbec804a07b0b28fe05ae668 (MD5) / Made available in DSpace on 2018-09-10T17:35:24Z (GMT). No. of bitstreams: 1 martins_sb_dr_arafor.int.pdf: 879795 bytes, checksum: 35bf73c7fbec804a07b0b28fe05ae668 (MD5) Previous issue date: 2018-08-03 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Pouco se sabe sobre o efeito do jateamento pré-sinterização da zircônia na sua resistência mecânica, sob condições de envelhecimento. Este estudo avaliou a influência do tamanho da partícula, do momento do jateamento e do envelhecimento na resistência mecânica de uma zircônia estabilizada por ítria. Quatrocentos discos de uma zircônia estabilizada por ítria pré-sinterizados foram alocados como segue: sem jateamento; jateamento com partículas de óxido de alumínio (Al2O3) de 50 µm ou 120 µm antes (50/PRÉ ou 120/PRÉ) ou após (50/PÓS ou 120/PÓS) sua sinterização. Os discos foram não envelhecidos (24h) ou envelhecidos por: ciclagem mecânica (CM); envelhecimento hidrotérmico (EH) ou CM+EH, totalizando 20 grupos (n=20). Os espécimes foram submetidos ao teste de resistência à flexão biaxial (RFB) e, posteriormente, foram analisados fractograficamente. A análise de difração de raios-X (DRX) foi realizada em determinadas condições para caracterizar cristalograficamente o efeito do jateamento na zircônia. Os dados de RFB (MPa) foram analisados por ANOVA a 3 fatores e pós teste de Games Howell (α=0,05). Também foi realizada análise de Weibull. A RFB e a resistência característica (σ0) dos grupos 120/PÓS, envelhecidos ou não, foram significativamente maiores que as dos demais grupos jateados, e estatisticamente similares ou maiores que as dos respectivos grupos sem jateamento. Em contrapartida, o grupo 120/PRÉ/não envelhecido e todos os grupos 50/PRÉ apresentaram os menores valores. Em todos os grupos, o defeito inicial se originou na superfície submetida à tração. Nem o jateamento, nem o envelhecimento (exceto o grupo 50/PÓS/CM+EH) reduziram a confiabilidade da zircônia em relação à dos respectivos grupos controles. O jateamento promoveu um aumento do conteúdo de fase monoclínica, enquanto a sinterização zerou essa fase. O jateamento da zircônia antes da sinterização teve pior desempenho para RFB em comparação ao realizado após sua sinterização, sob os meios de envelhecimentos. A RFB e σ0 foram fortemente determinadas pelo tamanho da partícula e pelo momento do jateamento, enquanto o envelhecimento agiu apenas quando a zircônia foi jateada antes da sinterização. / Little is known about the effect of air-abrasion before zirconia sintering on its strength, under aging challenge. This study aimed to verify the influence of the air-abrasion moment (before or after zirconia sintering), particle size (50 or 120 μm) and aging on the mechanical strength of a Y-TZP ceramic. Four hundred pre-sintered zirconia discs were allocated as follows: non-air-abraded; air-abraded with 50 μm or 120 μm Al2O3 particles before (50/BS or 120/BS) or after sintering (50/AS or 120/AS). The discs were non-aged (24h) or aged by: mechanical cycling (MC); hydrothermal aging (HA) or by both methods (MC+HA), totaling 20 groups (n=20). Specimens were subjected to biaxial flexural strength test (BFS). Fractographic analysis was performed to identify the fracture origin. The X-ray diffraction analysis (XRD) was performed under certain conditions to characterize the crystallographic effect of air-abrasion on the zirconia. The BFS data (MPa) were analyzed by ANOVA and Games Howell post hoc test (α=.05). Weibull statistics was also applied. The BFS and the characteristic resistance (σ0) of the 120/AS groups, aged or not, were significantly higher than those of the other air-abraded groups, and statistically similar or higher than the respective groups without air-abrasion. In contrast, the 120/BS/non-aged group and all those 50/BS presented the lowest values. In all groups, the initial defect had its origin on the tensile stress side. Neither air-abrasion nor aging (except for 50/AS/MC+HA) reduced the zirconia reliability compared with the respective controls. Air-abrasion promotes an increase in the monoclinic phase content, while sintering zeroed this phase. Air-abrasion before zirconia sintering yields worse performance for BFS than after sintering, under aging challenges. The BFS and σ0 were strongly determined by the particle size and air-abrasion moment, while aging acted only when the zirconia was air-abraded before sintering.

Orientador: Maria Amélia Máximo de Araújo / Banca: Maria Salete Machado Candido / Banca: Marcos Augusto do Rego / Banca: Marcia Carneiro Valera / Banca: Regina Celia Santos Pinto Silva / Resumo: O objetivo desse trabalho foi avaliar in vitro a microinfiltração marginal de cavidades de classe V preparadas com turbina de alta rotação (AR), jato abrasivo (AB), ultra-som (US) e laser de Er:YAG (LA) e restauradas com um sistema adesivo multi-passos e um auto-condicionante. Foram selecionados 160 incisivos bovinos para prepare das cavidades na face vestibular, com margem gengival localizada na junção esmalte-cemento e margem oclusal em esmalte. Os materiais utilizados foram Scotchbond Multi-uso Plus/3M (SBMUP), Etch&Prime 3.0/Degussa (EP) e a resina composta Z1 00/3M. Os dentes foram divididos em oito grupos de vinte, de acordo com equipamento e sistema adesivo empregado: a) AR + SBMUP; b) AR + EP; c) AB + SBMUP; d) AB + EP; e) US+ SBMUP; f) US+ EP; g) LA+ SBMUP; e h) LA+ EP. Os dentes restaurados foram armazenados a 37°C par 6 dias, termociclados (500: 5-55°C) e colocados em solução de Rodamina B a 2% por 24 horas. Em seguida foram seccionados e avaliados em lupa estereomicroscópica para determinar o grau de microinfiltração segundo uma escala de 0 a 4. Os dados foram submetidos aos testes estatísticos de Sinais de pastas de Wilcoxon, Kruskai-Wallis e Tukey. Houve diferença estatisticamente significante entre as margens, com maior microinfiltração na cervical; o melhor selamento marginal foi obtido no grupo US/SBMUP; não houve diferença estatisticamente significante entre os preparos cavitários realizados com laser de Er: YAG e alta-rotação e alta-rotação e abrasão a ar; os maiores valores de microinfiltração foram obtidos no grupo AB/EP / Abstract: The aim of this study was to evaluate in vitro the marginal microleakage of class V prepared with high-speed (HS}, air abrasion (AA), ultrasound (US) and Er:YAG /aser(LA), and restored with multi-step or self-etching adhesives systems. One-hundred-sixty incisives bovine teeth were selected for the cavity preparation on the buccal surface with the gingival margin at the enamel-cement junction and occlusal margin in enamel. The materials Scotchbond Multi Purpose/3M (SBMUP) and Etch&Prime 3.0/Degussa (EP) and Z10013M composite resin were used in this study. The teeth were divided in eigth groups with 20 teeth in each froup according to the equipment and to the adhesive system used: HS + SBMUP; HS +EP; AA +SBMUP; AA + EP; US+ SBMUP; US+ EP; LA+ SBMUP; LA + EP. The restored teeth were stored at 37CC for 6 days, thermocycled (500: 5-55 "C) and kept in a 2% Rodamine B solution tor 24 hours. After this they were seccioned and evaluated through stereomicroscope in order to determine the micro/eakage degree according to 0-4 score. The data were submitted to the Wilkoxon, KruskaiWal/ is and tukey statistical tests. There was significant statistical difference among the margins with the highest microleakage degrees in the cervical area; the best marginal sealing was with the US + SBMUP group. There was no significant statistical difference among the cavity preparations made with the Er:YAG laser and high-speed and high-speed and air abrasion. The highest microleakage values were found in the AA +EP group / Doutor

Embora haja grande exigência por restaurações estéticas livres de metal, restaurações metalocerâmicas, cujas subestruturas feitas com ligas de metais básicos, são procedimentos de rotina nos planejamentos restauradores protéticos. No entanto, a alta resistência ao desgaste destas ligas, caracterizada pela grande dificuldade de acabamento e polimento, tem sido associada à dureza, geralmente elevada. A proposta deste estudo foi avaliar resistência à abrasão e dureza de seis ligas de metais básicos (4 ligas de Ni-Cr, 1 liga de Co-Cr e 1 Ti comercialmente puro – 99,5% Ti) disponíveis comercialmente para uso com cerâmica. A resistência à abrasão foi determinada pela perda de peso dos corpos-de-prova, ao longo de 4 séries de ciclos de abrasão. A dureza Rockwell 30N também foi avaliada nos mesmos intervalos. Os dados foram analisados com o nível de significância a = 0,05. O teste de regressão e correlação da resistência à abrasão e dureza mostrou que para 3 ligas de Ni-Cr (Vera Bond, Vera Bond II e Wiron 99) a linha de regressão foi descendente, indicando que um aumento na dureza correspondeu a uma redução nos valores de perda de peso, enquanto para 1 liga de Ni-Cr (Neochrom) a linha de regressão foi ascendente, indicando um aumento nos valores de perda de peso, apesar de um aumento na dureza. Por outro lado, para a ligas de Co-Cr (New Ceram) e de titânio (Rematitan), os valores de perda de peso se mantiveram constantes. As ligas avaliadas tiveram baixos coeficientes de correlação entre resistência à abrasão e dureza. A análise metalográfica revelou particularidades que podem ter sido determinantes para as taxas de desgaste de cada material. Com exceção da liga de titânio, não houve mudanças metalográficas das ligas avaliadas, durante as séries de ciclos de abrasão. / In spite of the demand for metal free restorations, metal ceramic restorations using base metal alloys are routine in prosthodontics. Nevertheless, the high abrasion resistance of base metal alloys, characterized by difficulty in finishing and polishing, has been related to excessive hardness. The purpose of this study was to evaluate abrasion resistance and hardness of six base metal alloys (4 Ni-Cr alloys, 1 Co-Cr alloy and 1 commercially pure Ti alloy – 99.5% Ti) available commercially for use with fused porcelain. Abrasion resistance was determined by specimen weight loss along 4 series of abrasion cycles. The Rockwell 30N hardness was also determined in the same periods. Data were analyzed statistically with the level of significance set at a = 0.05. Regression and correlation analysis of abrasion resistance and hardness showed that for three Ni-Cr alloys (Vera Bond, Vera Bond II and Wiron 99) the regression lines descended indicating that an increase in hardness corresponded to a reduction in weight loss, whereas for one Ni-Cr alloy (Neochrom) the regression line ascended indicating an increase in weight loss in spite of an increase in hardness. On the other hand, for the Co-Cr alloy (New Ceram) and Ti (Rematitan), the weight loss remained constant. The alloys tested had low correlation coefficients between abrasion resistance and hardness. Microscopic analysis showed details that may have been determining for the weight loss rate of each material. With the exception of the titanium alloy, there were no metallographic changes of the alloys tested during the abrasion tests.

O presente estudo, composto por 2 experimentos in situ, buscou avaliar o efeito da irradiação com laser de CO2 no controle da progressão de lesões de erosão e, posteriormente, analisar a influência da abrasão em superfícies irradiadas e erodidas. No primeiro experimento, 56 fragmentos de incisivos bovinos (5x3x2.5mm) tiveram suas superfícies de esmalte divididas em 4 áreas: 1. Hígida (área de referência); 2. Erosão inicial; 3. Tratamento (irradiado ou não com laser de CO2); 4. Após fase in situ. O desafio erosivo inicial foi realizado com ácido cítrico 1% (pH=2,3) por 5 minutos, 2x/dia, por 2 dias. Os espécimes foram divididos em 2 grupos de acordo com o tratamento da superfície: irradiados com laser de CO2 ( λ= 10,6 m; 0,5 W) e não irradiados. Após um período de lead-in de 2 dias, 14 voluntários usaram um dispositivo intraoral palatino contendo 2 espécimes (irradiado e não irradiado), em 2 fases intraorais de 5 dias cada. Seguindo um desenho cross-over, durante a primeira fase, metade dos voluntários imergiu seu dispositivo em 100mL de ácido cítrico por 5 minutos, 3x/dia, enquanto a outra metade usou água deionizada (controle). Os voluntários foram cruzados quanto aos desafios na segunda fase. O desgaste do esmalte foi determinado quantitativamente por um perfilômetro óptico e a morfologia da superfície do esmalte foi avaliada qualitativamente por microscopia eletrônica de varredura. ANOVA a três critérios para medidas repetidas mostrou que não houve interação significativa entre desafio erosivo e irradiação com laser de CO2 (p=0,419). O desafio erosivo aumentou significativamente o desgaste do esmalte (p=0,001), independente de ter sido realizada ou não a irradiação com laser de CO2. Não houve diferença no desgaste do esmalte entre os espécimes irradiados e não irradiados (p=0,513). No segundo experimento, o preparo e seleção dos espécimes de esmalte bovino, a indução das lesões de erosão iniciais e os tratamentos foram realizados como no primeiro experimento. Após um período de 2 dias de lead-in, 12 voluntários usaram um dispositivo palatino contendo dois espécimes irradiados e dois não irradiados, em duas fases intraorais de 5 dias cada. Seguindo um protocolo split-mouth, os voluntários imergiram extraoralmente, durante 5 minutos, os dispositivos em ácido cítrico 3x/dia por 5 dias. Uma hora após cada desafio erosivo, um espécime irradiado e um não irradiado foram escovados usando uma escova elétrica e slurry de dentifrício. As variáveis de resposta foram as mesmas empregadas no primeiro experimento. ANOVA a dois critérios revelou que não houve interação significativa entre desafio erosivo-abrasivo e irradiação com laser de CO2 (p=0,614). A irradiação laser não influenciou no desgaste do esmalte (p=0,742). O desgaste do esmalte dos espécimes submetidos a erosão + abrasão não foi diferente daquele verificado quando a erosão foi realizada sozinha (p=0,626), independente do laser de CO2 ter sido aplicado ou não. Pode-se concluir que, em condições intraorais, a irradiação com laser de CO2 não controlou a progressão de lesões de erosão nem de lesões de erosivo-abrasivas no esmalte. / This study, composed of 2 in situ experiments, aimed to evaluate the effect of CO2 laser irradiation to control the progression of erosive lesions and, after, analyze the influence of abrasion on irradiated and eroded surfaces. At the first experiment, 56 slabs of bovine incisors (5x3x2.5mm) had its enamel surface divided in 4 areas: 1. Sound (reference area); 2. Initial erosion; 3. Treatment (irradiated or not with CO2 laser); 4. After in situ phase. The erosive challenge was performed with 1% citric acid (pH 2.3), during 5 minutes, 2x/day, for 2 days. The specimens were divided in 2 groups according to the surface treatment: CO2 laser irradiated (λ = 10.6 m; 0.5 W) and non-irradiated. After a 2-day-lead-in period, 14 volunteers wore an intraoral palatal device containing 2 specimens (irradiated and non-irradiated), in 2 intraoral phases of 5 days each. Following a crossover design, during the first phase, half of the volunteers immersed its device on 100mL of citric acid during 5 minutes, 3x/day, while the other half immersed on deionized water (control). Volunteers were crossed on the challenges on the second phase. The enamel wear was quantitatively determined by an optical profilometer and the morphology of enamel surface was qualitatively evaluated by scanning electron microscopy. Three-way ANOVA for repeated measures showed that there was no significant interaction between erosive challenge and CO2 laser irradiation (p=0.419). The erosive challenge significantly increased the enamel wear (p=0.001), regardless of irradiated or not with CO2 laser. There was no difference on the enamel wear of irradiated and non-irradiated specimens (p=0.513). At the second experiment, preparation and selection of bovine enamel specimens, induction of initial erosive lesion and treatments were performed as already described for the first experiment. After a 2-day-lead-in period, 12 volunteers wore and intraoral palatal device containing 2 irradiated and 2 non-irradiated specimens, at two intraoral phases of 5 days each. Following a split-mouth protocol, volunteers immersed the devices extra orally, during 5 minutes, in 1% citric acid, 3x/day for 5 days. One hour after each erosive challenge, one irradiated and one non-irradiated specimen were brushed with an electrical toothbrush and dentifrice slurry. The response variables were the same studied at the first experiment. Two-way ANOVA revealed that there was no significant interaction between erosive-abrasive challenge and CO2 laser irradiation (p=0.614). The laser irradiation did not influence on the enamel wear (p=0.742). The enamel wear presented by the specimens subjected to erosion + abrasion did not differ from that verified when the erosion was performed alone. It can be concluded that, in intraoral conditions, the CO2 laser irradiation did not controlled the progression of erosive lesions or erosive-abrasive lesions on enamel

Orientador: Lourenço Correr Sobrinho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T01:39:57Z (GMT). No. of bitstreams: 1 Muzilli_Marcelo_D.pdf: 34149055 bytes, checksum: 91212ba7ea6406d835e270899c5d9256 (MD5) Previous issue date: 2009 / Resumo: O objetivo deste estudo foi avaliar o efeito do método de polimento na rugosidade e na dureza Vickers de doze cerâmicas utilizadas para cobertura, após serem submetidas ao desgaste abrasivo. Foram confeccionados quarenta discos de cada cerâmica, cor de esmalte, com 8 mm de diâmetro e 2 mm de espessura. O pó cerâmico de cada marca comercial (CERAMCO, CERCON, FINESSE, IPS D.SIGN, IPS ERIS, VINTAGE HALO, VISION, VISION ESTHETIC, VITA VM7, VITA VM9, VITA VM13 e WILL CERAM) foi aglutinado com o líquido modelador indicado e aplicado em uma matriz metálica bipartida. Após a sinterização e o esfriamento, os discos foram desgastados, simulando uma situação de ajuste oclusal, com ponta diamantada 3098 F e 3098 FF (KG Sorensen), e divididos em 4 grupos (n=10): Grupo P - polimento com abrasivos do sistema Shofu; Grupo PP - polimento com sistema Shofu + pasta diamantada (6 mm - KG SORENSEN); Grupo PG - polimento + glaze e Grupo G - glaze (Controle). Os corpos-de-prova foram levados ao rugosímetro Surf-Corder para mensuração da rugosidade de superfície, utilizando o parâmetro Ra. Foram feitas três mensurações em cada corpo-de-prova. A dureza Vickers foi efetuada no aparelho HMV-2 (Shimadzu), calibrado com carga de 9,8 N atuando por 15 segundos. Cinco penetrações foram feitas em cada corpo-de-prova e a média calculada. Os dados foram submetidos à Análise de Variância e ao teste de Tukey (5%) e mostraram que as cerâmicas Finesse, VM7, VM9, VM13 e IPS Eris não tiveram influência do método de polimento na dureza Vickers. Os menores valores de dureza Vickers foram obtidos pelas cerâmicas Vintage Halo e VM7 no grupo P; Cercon, Vintage Halo, VM9 e Ceramco no grupo PP; Cercon no grupo PG e Ceramco, Cercon, Will Ceram e Vision Esthethic no grupo G. Os métodos de polimento tiveram influência na rugosidade em todas as cerâmicas utilizadas. Os menores valores de rugosidade foram obtidas pelas cerâmicas VM9, VM13, VM7, IPS Eris, Ceramco e Vintage Halo, no grupo P; Will Ceram, VM7, VM13 e Vintage no grupo G e Will Ceram, VM7 e Vision no grupo PG. O grupo PP promoveu os menores valores de rugosidade não diferindo entre as cerâmicas utilizadas. / Abstract: The aim of this study was to evaluate the polish method influence on surface roughness and Vickers hardness number of the twelve dental ceramics, after abrasive grinding. Forty enamel ceramic disks with 8 mm in diameter and 2.0mm thickness were made. The ceramic powder for each brand (CERAMCO, CERCON, FINESSE, IPS D.SIGN, IPS ERIS, VINTAGE HALO, VISION, VISION ESTHETIC, VITA VM7, VITA VM9, VITA VM13 and WILL CERAM) was agglutinated with the appropriate modeling liquid and applied on a bipartite metallic matrix. After the sinterization and cooling, the disks were submitted to a simulation of oclusal adjustment with 3098 F and 3098 FF diamonds burs (KG SORENSEN), and divided into four groups (n=10): Group P - Shofu polishing system; Group PP - Shofu polishing system + diamond paste (6mm - KG SORENSEN); Group PG - Shofu polishing system + glaze; and, Group G - glaze (control). The roughness was measured on a Surf-Corder machine using Ra parameter. Three measurements were made for each specimen and the average calculated. The Vickers hardness number was measured with HMV 2 microhardness tester (Shimadzu), with a load of 9,8 N applied for 15 seconds. Five measurements were made for each specimen. The dates were submitted to ANOVA and Tukey's test (5%) and showed that only the ceramics FINESSE, VM7, VM9, VM13 and IPS ERIS weren't the influence of surface treatment on Vickers hardness. The lowers hardness values were obtained by Cercon, Vintage Halo and VM7, in group P; Cercon, Vintage Halo, VM9 and Ceramco in Group PP; Cercon, in Group PG; Ceramco, Cercon, Will Ceram and Vision Esthetic, in Group G. The roughness suffered the influence of the surface treatment in all the ceramics that were used. The lowers roughness values were obtained by VM9, VM13, VM7, IPS Eris, Ceramco and Vintage Halo, in Group P; Will Ceram, VM7, VM13 e Vintage in Group G and Will Ceram, VM7 e Vision in Group PG. The Group PP promoted the lowers roughness averages that didn't show any difference statistic among all the ceramics. / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários

Este projeto teve como objetivos investigar o efeito do íon ferro (Fe+2), associado ou não ao íon flúor (F-), na redução da erosão do esmalte e da dentina bovinos, bem como desenvolver e avaliar um dentifrício enriquecido com Fe+2 para a prevenção da erosão associada à abrasão. Foram realizados 4 subprojetos: (1) Determinação do efeito protetor de concentrações crescentes do Fe+2 (0 a 120 mmol/L) associadas ou não ao F- (0 a 4 g/mL), contra a dissolução do pó de esmalte bovino in vitro; (2) Avaliação, in vitro, do efeito protetor do Fe+2 a 10 mmol/L contra a dissolução mineral da superfície do esmalte bovino; (3) Desenvolvimento e avaliação, in vitro, de dentifrícios fluoretados enriquecidos com diferentes concentrações de Fe+2, visando à prevenção da perda mineral do esmalte bovino; (4) Avaliação, in situ, do efeito inibidor do dentifrício acrescido de Fe+2 e F- na desmineralização do esmalte e dentina bovinos sadios ou previamente erodidos. As variáveis de resposta utilizadas foram a quantificação da perda de fósforo (colorimetria) e o desgaste (perfilometria, m) para os subprojetos 1 e 2, e 3 e 4, respectivamente. Os dados foram submetidos à análise estatística (p<0,05). Para o Subprojeto (1), a ANOVA a 2 critérios e o teste de Bonferroni revelaram que soluções contendo Fe+2 a 1,25, 2,5, 5,0, 10, 15 e 30 mmol/L reduziram significativamente a dissolução do pó de esmalte bovino em 18, 18, 23, 35, 35 e 55%, respectivamente, em comparação ao controle (sem Fe+2). Na presença de F-, o efeito do Fe+2 na inibição da dissolução do esmalte foi reduzido, não havendo efeito sinérgico entre estes íons nas condições testadas. No Subprojeto (2), a ANOVA a 2 critérios e o teste de Bonferroni, mostraram uma redução significativa na desmineralização da superfície do esmalte bovino em torno de 30 a 40%, quando se utilizou solução de Fe+2 a 10 mmol/L. No Subprojeto (3), a ANOVA revelou diferença significativa entre os grupos (Placebo, 1100 g/mL de F-, Crest®, Fe+2 1,0 mg/g, Fe+2 2,5 mg/g, Fe+2 5,0 mg/g, F- (1100 g/mL) + Fe+2 1,0 mg/g, F- (1100 g/mL) + Fe+2 2,5 mg/g e F- (1100 g/mL) + Fe+2 5,0 mg/g) (F=4,734, p<0,0001). O menor desgaste (0,48±0,24 m) foi apresentado pelo grupo em que foi utilizado o dentifrício contendo 1100 g/mL F- e 5 mg/g Fe+2. No Subprojeto (4), para o esmalte hígido a ANOVA a 2 critérios revelou uma diferença significativa entre os dentifrícios, (F=21,72, p<0,0001), mas não entre as condições (só erosão, erosão + slurry, erosão + abrasão) (F=1,20, p=0,32) e nem para a interação entre ambos (F = 1,04, p=0,41). O teste de Bonferroni revelou que os blocos que receberam o dentifrício contendo Fe+2 e F- apresentaram valores de desgaste significativamente menores quando comparados aos blocos submetidos aos demais dentifrícios, os quais não diferiram significativamente entre si. Para a dentina hígida, o esmalte previamente erodido e a dentina previamente erodida, o mesmo padrão foi seguido, apesar destes dois últimos terem apresentado valores de desgaste maiores que aqueles observados para os blocos hígidos. / The aims of this study were to investigate the effect of iron (Fe+2) associated or not to fluoride (F-) on the reduction of bovine enamel and dentin erosion, as well as to develop and evaluate a dentifrice containing Fe+2 to prevent erosion associated to abrasion. Four subprojects were done: (1) In vitro determination of the protective effect of increasing Fe+2 concentrations (0 to 120 mmol/L) associated or not to F- (0 to 4 g/mL) against the dissolution of powdered enamel; (2) In vitro evaluation of the protective effect of 10 mol/L Fe+2 against the mineral dissolution of superficial bovine enamel; (3) Development and in vitro evaluation of fluorided dentifrices containing different Fe+2 concentrations in order to prevent the mineral loss of bovine enamel; and (4) In situ evaluation of the effect of a dentifrice containing Fe+2 and F- on the demineralization of sound or previously eroded bovine enamel and dentin. The response variables were quantification of phosphate loss (colorimetry) and tooth wear (perfilometry, m) for the subprojects 1 and 2, and 3 and 4, respectively. Data were submitted to statistical analyses (p <0.05). In subproject (1), two-way ANOVA and Bonferronis test revealed that solutions containing 1.25, 2.5, 5.0, 10.0, 15.0 and 30.0 mmol/L Fe+2 significantly reduced the dissolution of powdered enamel at 18, 18, 23, 35, 35 and 55%, respectively, in comparison to control (without Fe+2). In the presence of F-, the effect of Fe+2 on the dissolution of enamel was reduced and no synergistic effect between these ions was observed in the tested conditions. In Subproject (2), two-way ANOVA and Bonferronis test showed a significant reduction on surface demineralization of bovine enamel (around 30-40%), when the solution containing Fe+2 at 10 mmol/L was used. In Subproject (3), ANOVA revealed a significant difference among the groups (Placebo, 1,100 g/mL F, Crest®, 1.0 mg/g Fe+2, 2.5 mg/g Fe+2, 5.0 mg/g Fe+2, F- (1, 100 g/mL) + 1,0 mg/g Fe+2, F- (1100 g/mL) + 2,5 mg/g Fe+2 and F- (1,100 g/mL) + 5,0 mg/g Fe+2) (F=4,734, p<0,0001). The lowest wear (0.48±0.24 m) was observed when the dentifrice containing F + Fe was used. In Subproject (4), for sound enamel, two-way ANOVA revealed a significant difference among the dentifrices, (F=21.72, p<0.0001), but not among the conditions (erosion only, erosion + slurry, erosion + abrasion) (F=1.20, p=0.32) or for the interaction of both (F = 1.04, p=0.41). The Bonferronis test revealed that the blocks which received the dentifrice containing Fe+2 and F- presented significantly lesser wear when compared to the blocks submitted to the other dentifrices, which did not differ significantly among each other. As for sound dentin as well as for previously eroded enamel and dentin, the same pattern was obtained but the latter two presented wear values higher than those seen for the sound blocks.