Hydrogen is an efficient, carbon-free and safe energy carrier. However, its compact and weight-efficient storage is an ongoing subject for research and development. Among the intensively investigated hydrogen storage materials, lithium aluminum hydride (LiAlH4) is an attractive candidate because of its high theoretical hydrogen density (volumetric: 96.7g H2/l material; gravimetric: 10.6 wt.%-H2) in combination with rather low decomposition temperatures (onset temperature <100°C after doping). Although the reversible dehydrogenation of LiAlH4 must be carried out with the help of organic solvent, LiAlH4 can serve as single-use hydrogen storage material for various special applications, for example, hydrogen fuel cell systems. This thesis deals with transition metal (TM)-doped LiAlH4 aiming at tailored dehydrogenation properties. The crystal structure and morphology of TM-doped LiAlH4 is characterized by XRD and SEM respectively. The positive effects of four dopants (NiCl2, TiCl3, ZrCl4 and TiCl4) on promoting the dehydrogenation kinetics of LiAlH4 are systematically studied by thermal analysis. Based on the state of each TM chloride (solid or liquid), three low-energy-input doping methods (1. ball-milling at low rotation speed; 2. manual grinding or magnetic stirring; 3. magnetic stirring in ethyl ether) are compared in order to prepare LiAlH4 with the maximum amount of hydrogen release in combination with fast dehydrogenation kinetics. The dehydrogenation properties of the TM-doped LiAlH4 powders are measured under isothermal conditions at 80°C at a H2 pressure of 1 bar, which is within the operating temperature range of proton exchange membrane (PEM) fuel cells, aiming at applications where the exhaust heat of the fuel cell is used to trigger the dehydrogenation of the hydrogen storage material. Furthermore, the mid-term dehydrogenation behavior of TM-doped LiAlH4 was monitored up to a few months in order to test its mid-term storability. In addition, the pelletization of TM-doped LiAlH4 is investigated aiming at a higher volumetric hydrogen storage capacity. The effects of compaction pressure, temperature and the H2 back-pressure on the dehydrogenation properties of TM-doped LiAlH4 pellets are systematically studied. Moreover, the volume change through dehydrogenation and the short-term storage of the TM-doped LiAlH4 pellets are discussed in view of practical applications for PEM fuel cell systems. / Wasserstoff ist ein effizienter, kohlenstofffreier und sicherer Energieträger. Jedoch die kompakte und gewichtseffiziente Speicherung ist ein permanentes Forschungs- und Entwicklungsthema. Unter den intensiv untersuchten Materialien für die Wasserstoffspeicherung ist aufgrund der hohen theoretischen Speicherdichte (volumetrisch: 96,7 g H2/L, gravimetrisch: 10.6 Gew.%-H2) in Kombination mit sehr niedrigen Zersetzungstemperaturen (Anfangstemperatur < 100°C nach Dotierung) Lithium Aluminiumhydrid (LiAlH4) ein vielversprechender Kandidat. Obwohl die reversible Dehydrierung von LiAlH4 mit Hilfe von organischen Lösungsmitteln durchgeführt werden muss, kann LiAlH4-Pulver als Einweg-Speichermaterial für verschiedene Anwendungen dienen, beispielsweise für Wasserstoff/Brennstoffzellensysteme. Diese Doktorarbeit beschäftigt sich mit LiAlH4 dotiert mit Übergangsmetall, mit dem Ziel maßgeschneiderte Dehydrierungseigenschaften zu erreichen. Die Kristallstruktur und die Morphologie der mit Übergangsmetallen dotierten LiAlH4-Pulver wurden mit Röntgenbeugung (XRD) und Rasterelektronenmikroskopie (REM) charakterisiert. Weiterhin wurde der positive Effekt der Dotanden auf die reaktionsfördernde Dehydrierung von LiAlH4 systematisch mit Hilfe thermoanalytischer Methoden untersucht. Für jedes Übergangsmetall, welches in Form von Übergangsmetallchloriden vorlag, wurden drei Dotierungsmethoden mit niedrigem Energieeintrag (Kugelmahlen mit geringer Rotations-geschwindigkeit, manuelles Schleifen/Magnetrühren, Magnetrühren mit Ethylether) verglichen, um LiAlH4-Pulver mit einer maximalen Wasserstofffreisetzungsmenge in Kombination mit einer schnellen Dehydrierungskinetik zu erzielen. Die Dehydrierung des dotierten LiAlH4-Pulvers wurde unter isothermen Bedingungen bei 80°C und einem H2-Druck von 1 bar gemessen, was im Bereich der Betriebstemperatur von PEM-Brennstoffzellen (Proton Exchange Membran) liegt. Dadurch sollen Anwendungen anvisiert werden, bei denen die entstehende Abwärme der Brennstoffzelle genutzt wird, um die Dehydrierung des Wasserstoffspeichermaterials auszulösen. Zudem wurde das Dehydrierungsverhalten des dotierten LiAlH4 bis zu einigen Monaten kontrolliert, um die mittelfristige Haltbarkeit zu testen. Weiterhin wurde die Pelletierung des mit Übergangsmetallen dotierten LiAlH4 mit dem Ziel untersucht, eine hohe volumetrische Speicherkapazität zu erreichen. Der Einfluss des Pressdrucks, der Dehydrierungstemperatur und des H2-Gegendrucks auf die Dehydrierungseigenschaften der mit Übergangsmetallen dotierten LiAlH4-Presslinge wurde systematisch analysiert. Außerdem wird die Volumenveränderung durch die Dehydrierung und die Kurzzeitspeicherung der mit Übergangsmetallen dotierten LiAlH4-Presslinge im Hinblick auf praktische Anwendungen unter Nutzung der Brennstoffzelle diskutiert.

Hydrogen is an efficient, carbon-free and safe energy carrier. However, its compact and weight-efficient storage is an ongoing subject for research and development. Among the intensively investigated hydrogen storage materials, lithium aluminum hydride (LiAlH4) is an attractive candidate because of its high theoretical hydrogen density (volumetric: 96.7g H2/l material; gravimetric: 10.6 wt.%-H2) in combination with rather low decomposition temperatures (onset temperature <100°C after doping). Although the reversible dehydrogenation of LiAlH4 must be carried out with the help of organic solvent, LiAlH4 can serve as single-use hydrogen storage material for various special applications, for example, hydrogen fuel cell systems. This thesis deals with transition metal (TM)-doped LiAlH4 aiming at tailored dehydrogenation properties. The crystal structure and morphology of TM-doped LiAlH4 is characterized by XRD and SEM respectively. The positive effects of four dopants (NiCl2, TiCl3, ZrCl4 and TiCl4) on promoting the dehydrogenation kinetics of LiAlH4 are systematically studied by thermal analysis. Based on the state of each TM chloride (solid or liquid), three low-energy-input doping methods (1. ball-milling at low rotation speed; 2. manual grinding or magnetic stirring; 3. magnetic stirring in ethyl ether) are compared in order to prepare LiAlH4 with the maximum amount of hydrogen release in combination with fast dehydrogenation kinetics. The dehydrogenation properties of the TM-doped LiAlH4 powders are measured under isothermal conditions at 80°C at a H2 pressure of 1 bar, which is within the operating temperature range of proton exchange membrane (PEM) fuel cells, aiming at applications where the exhaust heat of the fuel cell is used to trigger the dehydrogenation of the hydrogen storage material. Furthermore, the mid-term dehydrogenation behavior of TM-doped LiAlH4 was monitored up to a few months in order to test its mid-term storability. In addition, the pelletization of TM-doped LiAlH4 is investigated aiming at a higher volumetric hydrogen storage capacity. The effects of compaction pressure, temperature and the H2 back-pressure on the dehydrogenation properties of TM-doped LiAlH4 pellets are systematically studied. Moreover, the volume change through dehydrogenation and the short-term storage of the TM-doped LiAlH4 pellets are discussed in view of practical applications for PEM fuel cell systems. / Wasserstoff ist ein effizienter, kohlenstofffreier und sicherer Energieträger. Jedoch die kompakte und gewichtseffiziente Speicherung ist ein permanentes Forschungs- und Entwicklungsthema. Unter den intensiv untersuchten Materialien für die Wasserstoffspeicherung ist aufgrund der hohen theoretischen Speicherdichte (volumetrisch: 96,7 g H2/L, gravimetrisch: 10.6 Gew.%-H2) in Kombination mit sehr niedrigen Zersetzungstemperaturen (Anfangstemperatur < 100°C nach Dotierung) Lithium Aluminiumhydrid (LiAlH4) ein vielversprechender Kandidat. Obwohl die reversible Dehydrierung von LiAlH4 mit Hilfe von organischen Lösungsmitteln durchgeführt werden muss, kann LiAlH4-Pulver als Einweg-Speichermaterial für verschiedene Anwendungen dienen, beispielsweise für Wasserstoff/Brennstoffzellensysteme. Diese Doktorarbeit beschäftigt sich mit LiAlH4 dotiert mit Übergangsmetall, mit dem Ziel maßgeschneiderte Dehydrierungseigenschaften zu erreichen. Die Kristallstruktur und die Morphologie der mit Übergangsmetallen dotierten LiAlH4-Pulver wurden mit Röntgenbeugung (XRD) und Rasterelektronenmikroskopie (REM) charakterisiert. Weiterhin wurde der positive Effekt der Dotanden auf die reaktionsfördernde Dehydrierung von LiAlH4 systematisch mit Hilfe thermoanalytischer Methoden untersucht. Für jedes Übergangsmetall, welches in Form von Übergangsmetallchloriden vorlag, wurden drei Dotierungsmethoden mit niedrigem Energieeintrag (Kugelmahlen mit geringer Rotations-geschwindigkeit, manuelles Schleifen/Magnetrühren, Magnetrühren mit Ethylether) verglichen, um LiAlH4-Pulver mit einer maximalen Wasserstofffreisetzungsmenge in Kombination mit einer schnellen Dehydrierungskinetik zu erzielen. Die Dehydrierung des dotierten LiAlH4-Pulvers wurde unter isothermen Bedingungen bei 80°C und einem H2-Druck von 1 bar gemessen, was im Bereich der Betriebstemperatur von PEM-Brennstoffzellen (Proton Exchange Membran) liegt. Dadurch sollen Anwendungen anvisiert werden, bei denen die entstehende Abwärme der Brennstoffzelle genutzt wird, um die Dehydrierung des Wasserstoffspeichermaterials auszulösen. Zudem wurde das Dehydrierungsverhalten des dotierten LiAlH4 bis zu einigen Monaten kontrolliert, um die mittelfristige Haltbarkeit zu testen. Weiterhin wurde die Pelletierung des mit Übergangsmetallen dotierten LiAlH4 mit dem Ziel untersucht, eine hohe volumetrische Speicherkapazität zu erreichen. Der Einfluss des Pressdrucks, der Dehydrierungstemperatur und des H2-Gegendrucks auf die Dehydrierungseigenschaften der mit Übergangsmetallen dotierten LiAlH4-Presslinge wurde systematisch analysiert. Außerdem wird die Volumenveränderung durch die Dehydrierung und die Kurzzeitspeicherung der mit Übergangsmetallen dotierten LiAlH4-Presslinge im Hinblick auf praktische Anwendungen unter Nutzung der Brennstoffzelle diskutiert.

Les phosphines sulfonées sont les ligands hydrosolubles les plus utilisés en catalyse organométallique aqueuse. La méthode la plus courante d’introduction des groupements sulfonate sur une arylphosphine consiste en la réaction de celle-ci avec l’oléum sulfurique. Dans ce contexte, la première partie de cette thèse a été consacrée à la synthèse de nouvelles triarylphosphines sulfonées encombrées possédant des groupements naphtyle. Plus précisément, les phosphines sulfonées synthétisées ont été du type [(1 ou 2-naphtyl)x(phényl)3-x]phosphine (x = 1, 2, 3) avec en moyenne, deux groupes sodium sulfonate par molécule. Dans la seconde partie de cette thèse, le développement d’une nouvelle voie d’accès à des phosphines du type R-diphénylphosphines disulfonées, où R est un groupement sensible aux conditions drastiques de sulfonation a été mis en œuvre. Ce protocole met en jeu deux étapes : la première étape implique l’alkylation de la benzyldiphénylphosphine trisulfonée (BDPPTS) ou du 1,2-bis(diphénylphosphino)éthane tétrasulfoné (DPPETS) par un dérivé halogéné (RX) apportant le groupement R sensible. La seconde étape consiste en le clivage réducteur par l’aluminohydrure de lithium (LiAlH4) des sels de phosphonium ou de bis-phosphonium ainsi obtenus et conduit à la R-diphénylphosphine disulfonée. Les phosphines qui ont été synthétisées par cette méthode sont les n-octyl-, n-dodécyl-, n-hexadécyl-, phénéthyl- et but-3-ényl-diphénylphosphines disulfonées. Les phosphines sulfonées synthétisées dans le cadre de cette thèse ont été valorisées en tant que ligands dans la réaction d’hydroformylation du déc-1-ène catalysée au rhodium et assistée ou non par des cyclodextrines. / Sulfonated arylphosphanes are the most applied water-soluble ligands in aqueous organometalliccatalysis. Sodium sulfonate groups are commonly introduced on an arylphosphane by using sulfuric oleum(SO3/H2SO4) followed by neutralization with aqueous sodium hydroxide. In this context, the first part of thiswork was focused on the synthesis of new bulky sulfonated triarylphosphanes with naphtyl groups. Moreprecisely, sulfonated [(1 or 2-naphtyl)x(phenyl)3-x]phosphane (x = 1, 2, 3) with an average sulfonation degreearound two have been prepared. In the second part, a new and convenient synthesis pathway to disulfonatedR-diphenylphosphanes with R an oleum-sensitive group was developed. This route involves two steps: thefirst step is the alkylation of trisulfonated benzyldiphenylphosphane (BDPPTS) or tetrasulfonated 1,2-bis(diphenylphosphanyl)ethane (DPPETS) with an halide compound (RX) bearing the sensitive group R. Inthe second step, the synthetized trisulfonated phosphonium or tetrasulfonated bis-phosphonium salt aresubsequently cleaved by lithium aluminium hydride (LiAlH4) to give the corresponding disulfonated Rdiphenylphosphanes.The phosphanes obtained by this new methodology are the disulfonated n-octyl-, ndodecyl-,n-hexadecyl-, phenethyl-, and but-3-enyl-diphenylphosphanes. Most of the synthetized phosphanesin this work have then been tested as ligand in the rhodium catalyzed dec-1-ene hydroformylation assisted ornot by cyclodextrins.