Made available in DSpace on 2014-06-11T19:24:07Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-07-05Bitstream added on 2014-06-13T19:51:19Z : No. of bitstreams: 1 silva_prp_me_sjc.pdf: 750069 bytes, checksum: 94263aef7c378118e8087ea9d933ad86 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo desta pesquisa foi avaliar a influência do laser Nd:YAG nas propriedades mecânicas (dureza e módulo de elasticidade) da interface adesiva, utilizando a técnica da nanoindentação, empregando-se sistema adesivo convencional Adper Single Bond 2 – 3M ESPE (SB) ou autocondicionante Clearfil SE Bond – Kuraray (CSE). Doze terceiros molares humanos tiveram suas superfícies oclusais desgastadas até a exposição da dentina superficial. Uma cavidade circular padronizada com fresa 3053 foi realizada na superfície oclusal proporcionando 2 mm de dentina remanescente. Os espécimes foram embutidos em resina acrílica, e seccionados no sentido mésio-distal, sendo as 24 hemi-coroas obtidas divididas em quatro grupos: Grupo controle (SBC) - aplicação do sistema SB de acordo com as recomendações do fabricante; Grupo laser (SBL) - aplicação do sistema adesivo SB e tratamento com laser Nd:YAG (140mJ/cm2/60s/não contato); Grupo controle (CSEC) - aplicação do sistema adesivo autocondicionante CSE de acordo com as recomendações do fabricante; Grupo laser (CSEL)- aplicação do sistema adesivo autocondicionante CSE e tratamento com laser Nd:YAG (140mJ/cm2/60s/não contato). Após a polimerização dos sistemas adesivos, foram aplicados dois incrementos da resina composta Filtek Z 350 (3M ESPE). Os corpos-de-prova foram imersos em água destilada e armazenados por 24h em estufa 37ºC e submetidos à nanoidentação em aparelho Nano Indenter® XP (MTS®, MN, EUA).. Os resultados foram submetidos aos testes estatísticos de Análise de Variância (ANOVA), Tukey e t-Student (p<0,05). Concluiu-se que a aplicação do laser Nd:YAG em ambos os sistemas adesivos não alterou o nível de dureza da interface adesiva, no entanto alterou o módulo de elasticidade / The aim of this study was to evaluate the influence of Nd: YAG laser on the mechanical properties (hardness and modulus of elasticity) of the adhesive interface, using the technique of nanoindentation, employing conventional adhesive system Single Bond 2 3M ESPE (SB) or selfetching adhesive system Clearfil SE Bond - Kuraray (CSE). On 12 human molars, a flat superficial dentin surface was exposed by abrasion. A standardized circular cavity with bur 3053 was performed on the occlusal surface and dentin thickness was standardized in 2 mm. The specimens were embedded in resin acrylic and sectioned mesio-distally through their long axes, and the 24 hemi-crowns obtained divided into four groups: Control Group (SBC) – the application of SB system according to the manufacturer's recommendations; Laser Group (SBL) – SB adhesive system and treatment with Nd: YAG laser (140mJ/cm2/60s/no contact) Control Group (CSEC) – application of CSE self-etching adhesive system according to the manufacturer's recommendations; Laser Group (CSEL) – application of CSE self-etching adhesive system and treatment with Nd: YAG laser (140mJ/cm2/60s/no contact). After polymerization of the adhesives, were applied two increments of composite resin Filtek Supreme and specimens were immersed in distilled water and stored for 24 hours at 37 ºC and submitted to nanoidentation in Nano Indenter ® XP (MTS ®, MN, USA. Nanoindentation were made on composite resin, adhesive system, hybrid layer and dentin. The results were analyzed by a tree-way ANOVA, Tukey and e t-Students (p<0,05). It was concluded that the application of Nd:YAG laser in both adhesive systems did not change hardness level of hybrid layer, however chanded the elastic modulus

Submitted by DAIR FERREIRA SALGADO JUNIOR null (dairsalgado@gmail.com) on 2017-01-05T17:54:35Z No. of bitstreams: 1 Dissertação.pdf: 5078960 bytes, checksum: f66841a9969c704bd527a1761f8e7e3b (MD5) / Approved for entry into archive by Juliano Benedito Ferreira (julianoferreira@reitoria.unesp.br) on 2017-01-10T17:08:35Z (GMT) No. of bitstreams: 1 salgadojunior_df_me_ilha.pdf: 5078960 bytes, checksum: f66841a9969c704bd527a1761f8e7e3b (MD5) / Made available in DSpace on 2017-01-10T17:08:35Z (GMT). No. of bitstreams: 1 salgadojunior_df_me_ilha.pdf: 5078960 bytes, checksum: f66841a9969c704bd527a1761f8e7e3b (MD5) Previous issue date: 2016-12-12 / A evolução do processo de furação nos trouxe ao desenvolvimento do método de furação por laser pulsado, mas não temos definido o que a variação de cada parâmetro produz nos microfuros em relação à qualidade dos mesmos medidos com base em seu formato em aço inoxidável austenítico AISI 316L. O presente estudo analisou como variações na potência de pico, largura temporal do pulso e existência ou não de atmosfera protetora podem mudar os tamanhos, formatos e profundidades em microfuros. Produziram-se combinações dos parâmetros que foram usadas para obter furos em chapas de aço AISI 316L com 1 mm de espessura com o uso de uma fonte de laser pulsado Nd:YAG e analisar as propriedades em cada combinação, tais como diâmetros de entrada e de saída, profundidades e formatos observados em estereoscópio.

Submitted by CAROLINA DE OLIVEIRA SILVA null (caroli_oliveira@hotmail.com) on 2017-04-18T05:45:14Z No. of bitstreams: 1 trabalho revisado - Carol corrigida 18-04.pdf: 4289233 bytes, checksum: 352f0db50ce2a9d93581a7a0dd27df20 (MD5) / Approved for entry into archive by Luiz Galeffi (luizgaleffi@gmail.com) on 2017-04-18T18:52:43Z (GMT) No. of bitstreams: 1 silva_co_me_ilha.pdf: 4289233 bytes, checksum: 352f0db50ce2a9d93581a7a0dd27df20 (MD5) / Made available in DSpace on 2017-04-18T18:52:43Z (GMT). No. of bitstreams: 1 silva_co_me_ilha.pdf: 4289233 bytes, checksum: 352f0db50ce2a9d93581a7a0dd27df20 (MD5) Previous issue date: 2017-02-17 / O aço inoxidável austenítico 316L é um material empregado nas indústrias que requerem resistência à corrosão e mecânica como a indústria de petróleo, gás natural e papel e celulose. O uso do laser vem se tornando uma ferramenta atrativa em relação as soldagens convencionais, devido aos seus benefícios que vão desde processo sem contato, controle de energia do feixe e fácil automatização do sistema. Nesse trabalho o objetivo foi analisar a influência do processo de soldagem laser pulsado Nd: YAG nas características mecânicas e microestruturais da junta soldada de chapas de aço inoxidável austenítico AISI 316L com 1,0 mm de espessura, averiguando o efeito da energia de soldagem nas características do cordão de solda desenvolvidas no Laboratório de Soldagem Laser, do Departamento de Engenharia Mecânica da FEIS UNESP. Foram realizadas soldagens de juntas de chapas aço inoxidável austenítico com valores fixos de energias de soldagem em 8 Joules, largura temporal em 4 ms, velocidade de soldagem em 1 mm/s, variando apenas a frequência entre 2 e 10 Hz, com isso obteve-se diferentes taxas de sobreposição, com proteção gasosa de argônio. Com as diferentes condições obtidas foram realizadas análises macrográficas das juntas soldadas, através de secções transversais das mesmas e, ensaios de microdureza Vickers e ensaios de tração. Os resultados obtidos mostraram que o cordão de solda se comportou de forma frágil, rompendo-se todos no cordão, a fractografia da seção transversal aparentemente apresentou muitos vazios, a ZTA mostrou-se muito pequena e aparentemente não houve crescimento do grão, o aumento da sobreposição da junta soldada tem influencia direta com a dureza do material. / 316L austenitic stainless steel is a material used in industries which require mechanical and corrosion resistance like the petroleum industry, natural gas and paper/cellulose industry. The usage of laser has become an attractive tool compared to conventional welding, due to its benefits ranging from contactless process, beam power control and easy system automation. In this work the objective was to analyze the influence of the Nd: YAG pulsed laser welding process on the mechanical and microstructural characteristics of the welded joint of AISI 316L austenitic stainless steel sheets with 1.0 mm thickness, investigating the effect of the welding energy on the characteristics Of the weld bead developed at the Laser Welding Laboratory of the Mechanical Engineering Department of FEIS UNESP. Sheet joints of austenitic stainless steel were welded with fixed values of welding energies in 8 Joules, temporal width in 4 ms, welding speed in 1 mm / s, only varying the frequency between 2 to 10 Hz. With this, different rates of overlap, with argon gas protection. With the different conditions obtained, macroscopic analysis of the welded joints were carried out through cross sections of the welds and Vickers microhardness tests and tensile tests. The results showed that the weld bead behaved in a fragile manner, breaking all in the cord, the fracture of the cross section apparently presented many voids, the ZTA showed to be very small and apparently there was no growth in the grain, the increase of the overlap of the welded joint has a direct influence on the hardness of the material.

Submitted by Leonardo Freitas (leonardo.hfreitas@ufpe.br) on 2015-04-14T14:35:17Z No. of bitstreams: 2 license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5) Dissertação Patricia Fernandes Cassimiro.pdf: 1701117 bytes, checksum: d5a72b1cd9462cd35a6de464d1725fac (MD5) / Made available in DSpace on 2015-04-14T14:35:17Z (GMT). No. of bitstreams: 2 license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5) Dissertação Patricia Fernandes Cassimiro.pdf: 1701117 bytes, checksum: d5a72b1cd9462cd35a6de464d1725fac (MD5) Previous issue date: 2013-01-31 / CAPES / O objetivo deste estudo foi avaliar o efeito preventivo do laser Nd:YAG utilizado juntamente com um verniz fluoretado na erosão e a efetividade da sua associação ao uso de um creme dental a base de fluoreto de sódio (NaF), além de avaliar o efeito inibidor de diferentes cremes dentais a base de NaF, fluoreto de estanho (SnF2) e nano complexo caseína fosfopeptídea e fosfato de cálcio amorfo (CPPACP) frente ao processo erosivo. Junto a isso, verificar se a tomografia por coerência óptica (TCO) pode ser um método quantitativo a ser utilizado para avaliação de erosão do esmalte. Superfícies de esmalte bovino foram distribuídos aleatoriamente em 6 grupos (n=7): NC – controle negativo (sem tratamento); LV – Laser Nd:YAG + verniz de NaF; LV/NaF – Laser Nd:YAG + verniz de NaF + Proesmalte (NaF); NaF – Pro-esmalte; SnF2/NaF – Pro-Saúde; CPP-ACP/NaF – MI Paste Plus. Os grupos LV e LV/NaF foram irradiados a laser Nd:YAG (10 Hz, 1W, 141,5 J/cm2) durante 30 segundos e em seguida foi aplicado verniz fluoretado (NaF) por 4 horas. A ciclagem erosiva foi realizada em solução de ácido cítrico 0,5% (pH 2,6) 5 x 3 minutos ao dia, seguido pela exposição aos cremes dentais por 2 minutos após a primeira e última ciclagem de cada dia em todos os grupos, com exceção dos grupos NC e LV. No grupo NC nenhum tratamento foi realizado. A análise quantitativa foi realizada através de perfilometria por contato e tomografia por coerência óptica, complementada pela análise qualitativa da microscopia eletrônica de varredura. Entre os métodos testados, a associação laser/verniz/pro-esmalte mostrou-se uma boa estratégia preventiva, com maior efeito redutor de perda mineral. Entre os cremes dentais, em ambos os métodos quantitativos de avaliação, o CPP-ACP/NaF foi o que apresentou o menor efeito redutor da erosão, no entanto Click to buy NOW! PDF-XChange Viewer www.docu-track.com Click to buy NOW! PDF-XChange Viewer www.docu-track.com o creme dental a base de SnF2/NaF apresentou bons resultados. Ambos os métodos de avaliação foram efetivos, não apresentando diferenças estatísticas.

O estudo teve o objetivo de avaliar a resistência adesiva e a degradação da interface entre uma cerâmica tratada com laser e cimentos resinosos. Sessenta e quatro blocos cerâmicos foram distribuídos em 16 grupos distribuídos de acordo com os fatores em estudo: tratamento da superfície interna da cerâmica: Oxido de Alumínio (Ox), Rocatec (R), Laser de Nd:YAG 141,54 J/cm2 (Nd) e Laser de Nd:YAG + Rocatec (NdR); cimentos resinosos: Panavia F (Kuraray) e Relyx Unicem (3M ESPE); e método de envelhecimento: água destilada (W) e hipoclorito de sódio 10% (H). Após os procedimentos de cimentação e corte dos blocos, metade dos palitos foi armazenada em solução de hipoclorito de sódio 10% para simular envelhecimento in vitro. A resistência de união foi avaliada através do ensaio de microtração (0,5 mm/min) e os padrões de fratura foram classificados em adesivo, coesivo ou misto. Blocos cerâmicos adionciais foram confeccionados e analisados em Microscopia Eletrônica de Varredura e em Microscópio de Força Atômica para verificação dos padrões gerados pelos tratamentos. Os grupos tratados com laser de Nd:YAG apresentaram os maiores valores de resistência de união. Para os grupos cimentados com Panavia F, os valores de resistência de união foram: OxW: 27,71±6,3; RW: 35,67±5,13; NdW: 42,49±6,8; NdRW: 37,41±4,76; OxH: 22,27±6,05; RH: 27,49±8,83; NdH: 32,24±6,94; NdRH: 31,75±7,77. Para os grupos com RelyX Unicem: OxW: 26,74±6,34; RW: 35,07±6,02; NdW: 41,05±7,71; NdRW: 33,85±6,03; OxH: 22,77±7,37; RH: 27,84±6,26; NdH: 36,42±5,08; NdRH: 27,6±5,8. Pode-se concluir que o laser de Nd:YAG foi o tratamento mais efetivo, seguido da associação entre o laser de Nd:YAG+Rocatec, Rocatec e jateamento com Al2O3. Os cimentos testados apresentam comportamentos similares. O envelhecimento in vitro com hipoclorito de sódio diminuiu os valores de resistência de união. / The aim of this study was to evaluate the influence of different surface treatments on resistance to degradation between In-Ceram Alumina and two resin-based cements. Sixteen experimental groups were formed according to ceramic treatment: Sandblasting (S), Rocatec System (R), Nd:YAG Laser (Nd), Nd:YAG Laser plus Rocatec System (NR); luting cement: Panavia F (Kuraray) or Relyx Unicem (3M ESPE); and aging method: water (W) or sodium hypochlorite (H). Sixty four In-Ceram Alumina blocks (10x10x6mm) received four surface treatments: Al2O3 sandblasting; Al2O3 sandblasting + Rocatec Plus; Al2O3 sandblasting + Nd:YAG Lase; Al2O3 sandblasting + Nd:YAG Laser + Rocatec Plus. Each conditioned ceramic block was bonded to a composite block using a resin cement system. After 24h storage time, the blocks were sectioned to obtain sticks with cross-sectional area of 1.0mm2. The specimens were loaded to failure in a universal testing machine at a crosshead speed of 0.5mm/min. The fractured surface morphology of the debonded specimens was observed (40X) to evaluate the fracture pattern. Failure modes were classified as adhesive, cohesive in ceramic, cohesive in resin cement and mixed. The ceramic treatment and the aging method significantly affected the microtensile bond strength. Nd:YAG surface treatment resulted in the best bond strength values. To groups luted with Panavia F cement the microtensile bond strength values were: SW: 27,71±6,3; RW: 35,67±5,13; NdW: 42,49±6,8; NdRW: 37,41±4,76; SH: 22,27±6,05; RH: 27,49±8,83; NdH: 32,24±6,94; NdRH: 31,75±7,77. To groups luted with RelyX cement: SW: 26,74±6,34; RW: 35,07±6,02; NdW: 41,05±7,71; NdRW: 33,85±6,03; SH: 22,77±7,37; RH: 27,84±6,26; NdH: 36,42±5,08; NdRH: 27,6±5,8. Nd:YAG laser was the most effective surface treatment, followed by Nd:YAG+Rocatec, Rocatec and Al2O3 sandblasting. Resin cements presented similar behaviors in spite of aging. NaOCl 12h-immersion decreased Bond strength values.

O objetivo desse estudo foi avaliar in vitro e in situ a efetividade de irradiação dos lasers Er:YAG, Nd:YAG e CO2 no aumento da resistência ácida do esmalte em regiões de sulcos e fissuras. Para o estudo in vitro foram utilizados molares humanos em fragmentos da porção oclusal de 8mmx4mm divididos em 3 grupos de acordo com o tipo de tratamento : Grupo 1 - Er:YAG; Grupo 2 - Nd:YAG; Grupo 3 - CO2 (n=15). O tratamento de superfície foi feito apenas em metade da área do fragmento, sendo que a outra metade foi considerada controle. As áreas expostas ao desafio cariogênico (14mm2) foram submetidas a ciclagens de pH. Para o testede microdureza os espécimes foram seccionados ao meio e a parede da secção é que sofreu o teste, a outra metade foi utilizada para análise em microscopia de luz polarizada para a medição da área da lesão de desmineralização e análise em MEV para verificar as alterações na morfologia do tecido dentário. As análises dos dados de microdureza (HKN) e área das lesões (mm2) foram feitas com o teste de Wilcoxon para a comparação interna de cada grupo com o seu controle e a comparação entre os grupos utilizou ANOVA para as áreas das lesões e Kruskal Wallis para a microdureza (&alpha; = 5%). Foi observada apenas diferença estatística significante para as amostras do grupo irradiado com laser CO2 entre as partes controle e experimental. Os demais grupos não apresentaram diferença estatisticamente significante com sua área controle. Na análise das medidas de lesão foram observadas diferença estatística significante para as amostras do grupo irradiado com os lasers CO2 e Nd:YAG com suas partes controles, sendo as medidas de área de lesão apresentadas pela área irradiada inferiores a área controle. Na análise em MEV o grupo irradiado com laser CO2 mostrou ausência de exposição dos prismas de esmalte e modificação de superfície na área irradiada. Para o estudo in situ foram utilizados molares humanos em fragmentos da porção oclusal de 4mmx4mm tratados com os 3 diferentes tipos de laser: Grupo 1 - controle (sem tratamento); Grupo 2 - Er:YAG; Grupo 3 - Nd:YAG; Grupo 4 - CO2 (n=15). Os espécimes foram adaptados a um dispositivo intrabucal que foi utilizado pelos voluntários durante 14 dias. Para o desafio cariogênico gotejou-se solução de sacarose 20% sobre os espécimes. Assim como no estudo in vitro, foram realizados o teste de microdureza, análise em microscópio de luz polarizada e análise em MEV. Para a análise dos dados de microdureza (HKN) foi utilizada ANOVA e teste de Fisher LSD (&alpha;= 5%). Foi observada diferença estatística significante para as amostras do grupo irradiado com laser CO2 e Nd:YAG, que apresentaram maiores valores de microdureza do que o grupo controle e não foram diferentes estatisticamente entre si. Os valores de microdureza observados em profundidade foram maiores proporcionalmente a distância da superfície, ou seja, 20&micro;m <30&micro;m <40&micro;m <50&micro;m. Na análise em microscopia de luz polarizada a análise foi feita com teste de Wilcoxon e todos os grupos apresentaram semelhança estatística. Considerando os resultados obtidos nos dois estudo pode-se concluir que os lasers CO2 e Nd:YAG foram capazes de promover aumento de resistência ácida no esmalte dental localizado nas superfície de sulcos e fissuras. / The aim of this study was to assess in vitro and in situ the lasers Er:YAG, Nd:YAG e CO2 in preventing enamel demineralization on the pits and fissures surface. For the in vitro study 45 occlusal enamel blocks were randomly divided into 3 groups in according with the treatment: G1 - Er:YAG; G2 - Nd:YAG; G3 - CO2. Treatments were made only on a half of the specimen and the remaining part was considered as a control. The samples were submitted to an in vitro pH cycles. For the microhardness test the specimens were seccioned in the middle and the seccioned wall received the test. The other halves were analyzed using polarized light microscopy for the measurement of the caries-lesion areas and morphological SEM analyses. Wilcoxon test were performed for the statistical analysis of the data obtained from the microhardness test (KHN) and caries-lesion area measurements (mm2) (&alpha;= 5%) when each groups was compared with its control. Variance analysis were performed for the difference in means of microhardness data and Kruskal Wallis test were performed for the difference in means of caries-lesion area measurements (&alpha;= 5%). For the microhardness data the G3 was statically different from its control area and the others groups presented statistical similarity among the experimental and control areas. For the caries-lesion area measurements statistical difference was observed for the groups G2 and G3 presenting smaller caries-lesion area when compared with their respective control areas. In the SEM analysis the G3 showed uniform surface without enamel-prism exposure. For the in situ study 60 occlusal enamel blocks were randomly divided into 4 groups in according with the treatment: G1 - Control (no treatment); G2 - Er:YAG; G3 - Nd:YAG; G4 - CO2 (n=15). The specimens were fixed in intra oral appliances and worn by the volunteers for 14d. Sucrose solution (20%) was applied to each specimen 6 times/d. As the in vitro study the samples were removed, sectioned and examined for microhardness, caries-lesion area measurements on the polarized light microcopy and morphological analyses on SEM. Variance analysis and the Fisher test were performed for the statistical analysis of the data obtained from the microhardness test (KHN) (&alpha;= 5%). The control group was statically different from G3 and G4, which present higher microhardness values and were statistical similar between them. The data of microhardness from the depth of surface were greater in proportion of distance from the surface, as 20&micro;m <30&micro;m <40&micro;m <50&micro;m. Wilcoxon test were performed for the statistical analysis of the data obtained from the caries-lesion area measurements (mm2) (= 5%) and all the groups were statically similar. Considering the results obtained from the both of studies can be concluded that the laser CO2 and Nd:YAG were able to increase the enamel acid resistance on the surface of pits and fissures.

O objetivo do presente estudo foi avaliar in situ o efeito da associação do verniz fluoretado ao laser de Er:YAG e ao laser Nd:YAG na permeabilidade da dentina radicular erodida. Quarenta e oito fragmentos de dentina radicular bovina, com dimensões 2x2x2 mm, foram submetidos a um desafio erosivo inicial com ácido cítrico (0,3%, pH 3,2), por duas horas, sob agitação e armazenados em saliva artificial por vinte e quatro horas. Posteriormente, os espécimes foram divididos em relação aos tratamentos: verniz fluoretado e não fluoretado e subdivididos conforme a irradiação: laser de Er:YAG (100mJ, 3Hz), laser de Nd:YAG (70mJ, 15 Hz) e não irradiado. Após um período de lead in (2 dias), os voluntários (n=8) utilizaram dispositivos palatinos contendo três espécimes que foram submetidos a desafios erosivos ex vivo, quatro vezes ao dia, com ácido cítrico (0,3%, pH 3,2), durante 90s, por cinco dias. Na primeira fase do experimento, metade dos voluntários utilizou dispositivos contendo fragmentos tratados com verniz fluoretado, verniz fluoretado + laser de Er:YAG e verniz fluoretado + laser de Nd:YAG. A outra metade utilizou verniz não fluoretado, verniz não fluoretado + laser de Er:YAG e verniz não fluoretado + laser de Nd:YAG. Depois de um período de wash-out (15 dias), os voluntários foram cruzados quanto aos tratamentos, caracterizando um experimento cross-over 2x2. Ao final de cada fase experimental, a permeabilidade dentinária foi avaliada. A ANOVA dois critérios e o teste complementar de Duncan revelaram uma diferença significativa entre os espécimes tratados com o verniz fluoretado (p=0,005), verniz fluoretado + laser de Er:YAG (p=0,014) e verniz fluoretado + laser de Nd:YAG (p=0,025), em comparação aos tratados com verniz não fluoretado. Observou-se que, independentemente da associação aos lasers (Er:YAG ou Nd:YAG), o verniz fluoretado foi capaz de promover a redução da permeabilidade da dentina radicular erodida. Não se observou efeito adicional com a associação dos tratamentos. / The present study aimed to evaluate in situ the effect of associating the fluoride varnish to Er:YAG or Nd:YAG laser at permeability of eroded root dentin. Forty-eight specimens of bovine root dentin (2x2x2mm) were subjected to initial erosive challenge with citric acid (0.3%, pH 3.2), for 2 hours under agitation and stored at artificial saliva, at 37&deg C, for 24 hours, followed by a remineralization period in artificial saliva. After that, specimens were divided according to the treatment: fluoride varnish and non-flouride varnish, and subdivided according to the irradiation: Er:YAG laser (100mJ, 3Hz), Nd:YAG laser (70mJ, 15Hz) and non-irradiated. After a lead-in period (2 days), 8 volunteers (n=8) wore a palatal device containing 3 specimens that was subjected to erosive challenges ex vivo, four times a day with citric acid (0.3%, pH3.2), for 90s, during 5 days. At the first experimental phase, half of volunteers wore devices containing specimens treated with fluoride varnish, fluoride varnish + Er:YAG laser and fluoride varnish + Nd:YAG laser, and the other half wore the specimens treated with non-fluoride varnish, non-fluoride varnish + Er:YAG laser and non-flouride varnish + Nd:YAG laser. After a wash-out period (15 days), volunteers were crossed to different treatment, characterizing a 2x2 cross-over experiment. At the end of each experimental phase, the dentinal permeability was evaluated. Two-way ANOVA and Duncans test revealed a significant difference between specimens treated with fluoride varnish (p=0,005), fluoride varnish + Er:YAG laser (p=0,014) and fluoride varnish + Nd:YAG (p=0,025) compared to specimens treated with no-fluoride varnish. It was observed that regardless of association to laser (Er:YAG or Nd:YAG), fluoride varnish was able to promote, in situ, the reduction of permeability of eroded root dentin, but no additional effect was observed when the treatments were associated.

O objetivo do presente estudo foi avaliar in situ o efeito da associação do verniz fluoretado ao laser de Er:YAG e ao laser Nd:YAG na permeabilidade da dentina radicular erodida. Quarenta e oito fragmentos de dentina radicular bovina, com dimensões 2x2x2 mm, foram submetidos a um desafio erosivo inicial com ácido cítrico (0,3%, pH 3,2), por duas horas, sob agitação e armazenados em saliva artificial por vinte e quatro horas. Posteriormente, os espécimes foram divididos em relação aos tratamentos: verniz fluoretado e não fluoretado e subdivididos conforme a irradiação: laser de Er:YAG (100mJ, 3Hz), laser de Nd:YAG (70mJ, 15 Hz) e não irradiado. Após um período de lead in (2 dias), os voluntários (n=8) utilizaram dispositivos palatinos contendo três espécimes que foram submetidos a desafios erosivos ex vivo, quatro vezes ao dia, com ácido cítrico (0,3%, pH 3,2), durante 90s, por cinco dias. Na primeira fase do experimento, metade dos voluntários utilizou dispositivos contendo fragmentos tratados com verniz fluoretado, verniz fluoretado + laser de Er:YAG e verniz fluoretado + laser de Nd:YAG. A outra metade utilizou verniz não fluoretado, verniz não fluoretado + laser de Er:YAG e verniz não fluoretado + laser de Nd:YAG. Depois de um período de wash-out (15 dias), os voluntários foram cruzados quanto aos tratamentos, caracterizando um experimento cross-over 2x2. Ao final de cada fase experimental, a permeabilidade dentinária foi avaliada. A ANOVA dois critérios e o teste complementar de Duncan revelaram uma diferença significativa entre os espécimes tratados com o verniz fluoretado (p=0,005), verniz fluoretado + laser de Er:YAG (p=0,014) e verniz fluoretado + laser de Nd:YAG (p=0,025), em comparação aos tratados com verniz não fluoretado. Observou-se que, independentemente da associação aos lasers (Er:YAG ou Nd:YAG), o verniz fluoretado foi capaz de promover a redução da permeabilidade da dentina radicular erodida. Não se observou efeito adicional com a associação dos tratamentos. / The present study aimed to evaluate in situ the effect of associating the fluoride varnish to Er:YAG or Nd:YAG laser at permeability of eroded root dentin. Forty-eight specimens of bovine root dentin (2x2x2mm) were subjected to initial erosive challenge with citric acid (0.3%, pH 3.2), for 2 hours under agitation and stored at artificial saliva, at 37&deg C, for 24 hours, followed by a remineralization period in artificial saliva. After that, specimens were divided according to the treatment: fluoride varnish and non-flouride varnish, and subdivided according to the irradiation: Er:YAG laser (100mJ, 3Hz), Nd:YAG laser (70mJ, 15Hz) and non-irradiated. After a lead-in period (2 days), 8 volunteers (n=8) wore a palatal device containing 3 specimens that was subjected to erosive challenges ex vivo, four times a day with citric acid (0.3%, pH3.2), for 90s, during 5 days. At the first experimental phase, half of volunteers wore devices containing specimens treated with fluoride varnish, fluoride varnish + Er:YAG laser and fluoride varnish + Nd:YAG laser, and the other half wore the specimens treated with non-fluoride varnish, non-fluoride varnish + Er:YAG laser and non-flouride varnish + Nd:YAG laser. After a wash-out period (15 days), volunteers were crossed to different treatment, characterizing a 2x2 cross-over experiment. At the end of each experimental phase, the dentinal permeability was evaluated. Two-way ANOVA and Duncans test revealed a significant difference between specimens treated with fluoride varnish (p=0,005), fluoride varnish + Er:YAG laser (p=0,014) and fluoride varnish + Nd:YAG (p=0,025) compared to specimens treated with no-fluoride varnish. It was observed that regardless of association to laser (Er:YAG or Nd:YAG), fluoride varnish was able to promote, in situ, the reduction of permeability of eroded root dentin, but no additional effect was observed when the treatments were associated.

O estudo teve o objetivo de avaliar a resistência adesiva e a degradação da interface entre uma cerâmica tratada com laser e cimentos resinosos. Sessenta e quatro blocos cerâmicos foram distribuídos em 16 grupos distribuídos de acordo com os fatores em estudo: tratamento da superfície interna da cerâmica: Oxido de Alumínio (Ox), Rocatec (R), Laser de Nd:YAG 141,54 J/cm2 (Nd) e Laser de Nd:YAG + Rocatec (NdR); cimentos resinosos: Panavia F (Kuraray) e Relyx Unicem (3M ESPE); e método de envelhecimento: água destilada (W) e hipoclorito de sódio 10% (H). Após os procedimentos de cimentação e corte dos blocos, metade dos palitos foi armazenada em solução de hipoclorito de sódio 10% para simular envelhecimento in vitro. A resistência de união foi avaliada através do ensaio de microtração (0,5 mm/min) e os padrões de fratura foram classificados em adesivo, coesivo ou misto. Blocos cerâmicos adionciais foram confeccionados e analisados em Microscopia Eletrônica de Varredura e em Microscópio de Força Atômica para verificação dos padrões gerados pelos tratamentos. Os grupos tratados com laser de Nd:YAG apresentaram os maiores valores de resistência de união. Para os grupos cimentados com Panavia F, os valores de resistência de união foram: OxW: 27,71±6,3; RW: 35,67±5,13; NdW: 42,49±6,8; NdRW: 37,41±4,76; OxH: 22,27±6,05; RH: 27,49±8,83; NdH: 32,24±6,94; NdRH: 31,75±7,77. Para os grupos com RelyX Unicem: OxW: 26,74±6,34; RW: 35,07±6,02; NdW: 41,05±7,71; NdRW: 33,85±6,03; OxH: 22,77±7,37; RH: 27,84±6,26; NdH: 36,42±5,08; NdRH: 27,6±5,8. Pode-se concluir que o laser de Nd:YAG foi o tratamento mais efetivo, seguido da associação entre o laser de Nd:YAG+Rocatec, Rocatec e jateamento com Al2O3. Os cimentos testados apresentam comportamentos similares. O envelhecimento in vitro com hipoclorito de sódio diminuiu os valores de resistência de união. / The aim of this study was to evaluate the influence of different surface treatments on resistance to degradation between In-Ceram Alumina and two resin-based cements. Sixteen experimental groups were formed according to ceramic treatment: Sandblasting (S), Rocatec System (R), Nd:YAG Laser (Nd), Nd:YAG Laser plus Rocatec System (NR); luting cement: Panavia F (Kuraray) or Relyx Unicem (3M ESPE); and aging method: water (W) or sodium hypochlorite (H). Sixty four In-Ceram Alumina blocks (10x10x6mm) received four surface treatments: Al2O3 sandblasting; Al2O3 sandblasting + Rocatec Plus; Al2O3 sandblasting + Nd:YAG Lase; Al2O3 sandblasting + Nd:YAG Laser + Rocatec Plus. Each conditioned ceramic block was bonded to a composite block using a resin cement system. After 24h storage time, the blocks were sectioned to obtain sticks with cross-sectional area of 1.0mm2. The specimens were loaded to failure in a universal testing machine at a crosshead speed of 0.5mm/min. The fractured surface morphology of the debonded specimens was observed (40X) to evaluate the fracture pattern. Failure modes were classified as adhesive, cohesive in ceramic, cohesive in resin cement and mixed. The ceramic treatment and the aging method significantly affected the microtensile bond strength. Nd:YAG surface treatment resulted in the best bond strength values. To groups luted with Panavia F cement the microtensile bond strength values were: SW: 27,71±6,3; RW: 35,67±5,13; NdW: 42,49±6,8; NdRW: 37,41±4,76; SH: 22,27±6,05; RH: 27,49±8,83; NdH: 32,24±6,94; NdRH: 31,75±7,77. To groups luted with RelyX cement: SW: 26,74±6,34; RW: 35,07±6,02; NdW: 41,05±7,71; NdRW: 33,85±6,03; SH: 22,77±7,37; RH: 27,84±6,26; NdH: 36,42±5,08; NdRH: 27,6±5,8. Nd:YAG laser was the most effective surface treatment, followed by Nd:YAG+Rocatec, Rocatec and Al2O3 sandblasting. Resin cements presented similar behaviors in spite of aging. NaOCl 12h-immersion decreased Bond strength values.

O objetivo desse estudo foi avaliar in vitro e in situ a efetividade de irradiação dos lasers Er:YAG, Nd:YAG e CO2 no aumento da resistência ácida do esmalte em regiões de sulcos e fissuras. Para o estudo in vitro foram utilizados molares humanos em fragmentos da porção oclusal de 8mmx4mm divididos em 3 grupos de acordo com o tipo de tratamento : Grupo 1 - Er:YAG; Grupo 2 - Nd:YAG; Grupo 3 - CO2 (n=15). O tratamento de superfície foi feito apenas em metade da área do fragmento, sendo que a outra metade foi considerada controle. As áreas expostas ao desafio cariogênico (14mm2) foram submetidas a ciclagens de pH. Para o testede microdureza os espécimes foram seccionados ao meio e a parede da secção é que sofreu o teste, a outra metade foi utilizada para análise em microscopia de luz polarizada para a medição da área da lesão de desmineralização e análise em MEV para verificar as alterações na morfologia do tecido dentário. As análises dos dados de microdureza (HKN) e área das lesões (mm2) foram feitas com o teste de Wilcoxon para a comparação interna de cada grupo com o seu controle e a comparação entre os grupos utilizou ANOVA para as áreas das lesões e Kruskal Wallis para a microdureza (&alpha; = 5%). Foi observada apenas diferença estatística significante para as amostras do grupo irradiado com laser CO2 entre as partes controle e experimental. Os demais grupos não apresentaram diferença estatisticamente significante com sua área controle. Na análise das medidas de lesão foram observadas diferença estatística significante para as amostras do grupo irradiado com os lasers CO2 e Nd:YAG com suas partes controles, sendo as medidas de área de lesão apresentadas pela área irradiada inferiores a área controle. Na análise em MEV o grupo irradiado com laser CO2 mostrou ausência de exposição dos prismas de esmalte e modificação de superfície na área irradiada. Para o estudo in situ foram utilizados molares humanos em fragmentos da porção oclusal de 4mmx4mm tratados com os 3 diferentes tipos de laser: Grupo 1 - controle (sem tratamento); Grupo 2 - Er:YAG; Grupo 3 - Nd:YAG; Grupo 4 - CO2 (n=15). Os espécimes foram adaptados a um dispositivo intrabucal que foi utilizado pelos voluntários durante 14 dias. Para o desafio cariogênico gotejou-se solução de sacarose 20% sobre os espécimes. Assim como no estudo in vitro, foram realizados o teste de microdureza, análise em microscópio de luz polarizada e análise em MEV. Para a análise dos dados de microdureza (HKN) foi utilizada ANOVA e teste de Fisher LSD (&alpha;= 5%). Foi observada diferença estatística significante para as amostras do grupo irradiado com laser CO2 e Nd:YAG, que apresentaram maiores valores de microdureza do que o grupo controle e não foram diferentes estatisticamente entre si. Os valores de microdureza observados em profundidade foram maiores proporcionalmente a distância da superfície, ou seja, 20&micro;m <30&micro;m <40&micro;m <50&micro;m. Na análise em microscopia de luz polarizada a análise foi feita com teste de Wilcoxon e todos os grupos apresentaram semelhança estatística. Considerando os resultados obtidos nos dois estudo pode-se concluir que os lasers CO2 e Nd:YAG foram capazes de promover aumento de resistência ácida no esmalte dental localizado nas superfície de sulcos e fissuras. / The aim of this study was to assess in vitro and in situ the lasers Er:YAG, Nd:YAG e CO2 in preventing enamel demineralization on the pits and fissures surface. For the in vitro study 45 occlusal enamel blocks were randomly divided into 3 groups in according with the treatment: G1 - Er:YAG; G2 - Nd:YAG; G3 - CO2. Treatments were made only on a half of the specimen and the remaining part was considered as a control. The samples were submitted to an in vitro pH cycles. For the microhardness test the specimens were seccioned in the middle and the seccioned wall received the test. The other halves were analyzed using polarized light microscopy for the measurement of the caries-lesion areas and morphological SEM analyses. Wilcoxon test were performed for the statistical analysis of the data obtained from the microhardness test (KHN) and caries-lesion area measurements (mm2) (&alpha;= 5%) when each groups was compared with its control. Variance analysis were performed for the difference in means of microhardness data and Kruskal Wallis test were performed for the difference in means of caries-lesion area measurements (&alpha;= 5%). For the microhardness data the G3 was statically different from its control area and the others groups presented statistical similarity among the experimental and control areas. For the caries-lesion area measurements statistical difference was observed for the groups G2 and G3 presenting smaller caries-lesion area when compared with their respective control areas. In the SEM analysis the G3 showed uniform surface without enamel-prism exposure. For the in situ study 60 occlusal enamel blocks were randomly divided into 4 groups in according with the treatment: G1 - Control (no treatment); G2 - Er:YAG; G3 - Nd:YAG; G4 - CO2 (n=15). The specimens were fixed in intra oral appliances and worn by the volunteers for 14d. Sucrose solution (20%) was applied to each specimen 6 times/d. As the in vitro study the samples were removed, sectioned and examined for microhardness, caries-lesion area measurements on the polarized light microcopy and morphological analyses on SEM. Variance analysis and the Fisher test were performed for the statistical analysis of the data obtained from the microhardness test (KHN) (&alpha;= 5%). The control group was statically different from G3 and G4, which present higher microhardness values and were statistical similar between them. The data of microhardness from the depth of surface were greater in proportion of distance from the surface, as 20&micro;m <30&micro;m <40&micro;m <50&micro;m. Wilcoxon test were performed for the statistical analysis of the data obtained from the caries-lesion area measurements (mm2) (= 5%) and all the groups were statically similar. Considering the results obtained from the both of studies can be concluded that the laser CO2 and Nd:YAG were able to increase the enamel acid resistance on the surface of pits and fissures.