BORGES, D. da S. Um estudo sobre a injeção de fios magnéticos em cavidades. 2016. 56 f. Dissertação (Mestrado em Física) - Centro de Ciências, Universidade Federal do Ceará, Fortaleza, 2016. / Submitted by Giordana Silva (giordana.nascimento@gmail.com) on 2016-09-27T19:04:46Z No. of bitstreams: 1 2016_dis_ddsborges.pdf: 25114843 bytes, checksum: 5f9b742c03f819714ebb1a2b99cdbe18 (MD5) / Approved for entry into archive by Giordana Silva (giordana.nascimento@gmail.com) on 2016-09-27T19:05:07Z (GMT) No. of bitstreams: 1 2016_dis_ddsborges.pdf: 25114843 bytes, checksum: 5f9b742c03f819714ebb1a2b99cdbe18 (MD5) / Made available in DSpace on 2016-09-27T19:05:07Z (GMT). No. of bitstreams: 1 2016_dis_ddsborges.pdf: 25114843 bytes, checksum: 5f9b742c03f819714ebb1a2b99cdbe18 (MD5) Previous issue date: 2016 / In this work we created some experiments concerning about injection process of magnetic wire into a rigid circular cavity in order to get a better understanding about characteristics of the morphologies generate under certain initial conditions. Our results implies the possibility of formation of two morphologies that have different characteristics. When the two wires injected diametrically opposite, but have magnetic dipoles in opposite direction we achieve spiral morphology. In the case of the two wires injected diametrically opposite, but have magnetic dipoles in same direction we achieve loop morphology. So we make a series of statistical analysis based on the image structures, form during the injection of the wire in the cavity. As a result these analyzes we found that the loop morphology showed a size ties distribution like power law in function of the packing fraction φ, behaving as Nl / φα. The exponent α rules the behavior of a power law is quite different from those found in other works about packing wires. We believe the difference comes from to the presence of long-range forces present in magnetic systems. / No presente trabalho realizamos uma série de experimentos acerca do processo de injeção de um fio magético no interior de uma cavidade circular rı́gida com o objetivo de obter uma melhor compreensão sobre as caracterı́sticas das morfologias geradas dependendo das condições iniciais. Nossos resultados indicam a possibilidade de formação de duas morfologias que apresentam caracterı́sticas bastante distintas. Quando os dois fios injetados em posições diametralmente opostos na cavidade apresentam dipolos magnéticos que apontam na mesma direção, porém em sentidos opostos, observamos a formação do padrão tipo Espiral. Já no caso dos dois fios apre- sentarem dipolos que apontam na mesma direção e sentido, os padrões de empacotamentos são do tipo Loop. Em seguida, realizamos uma série de análises estatı́sticas com bases nas imagens das estruturas formadas durante a injeção do fio na cavidade. Como resultados destas análises observamos que a morfologia da estrutura no caso do empacotamento tipo Loop apresentava uma distribuição de tamanhos de laços que exibe um comportamento em lei de potência quanto a quantidade de laços formados em função da fração de ocupação da cavidade φ do tipo N l ∝ φ α . O expoente α que governa o comportamento em lei de potência é bastante diferente dos expoen- tes encontrados para o caso de empacotamento de fios. Acreditamos que esta diferença se deve a presença de forças de longo alcance que estão presentes em sistemas magnéticos.

Dissertação (mestrado)—Universidade de Brasília, Programa de Pós-Graduação em Física, Instituto de Física, 2013. / Submitted by Elna Araújo (elna@bce.unb.br) on 2013-11-21T20:28:39Z No. of bitstreams: 1 2013_ValdeirAntonioDaSilva.pdf: 251047516 bytes, checksum: afbd10cdbcf21b5980832021ef1869d6 (MD5) / Rejected by Patrícia Nunes da Silva(patricia@bce.unb.br), reason: oi on 2013-11-21T20:30:08Z (GMT) / Submitted by Elna Araújo (elna@bce.unb.br) on 2013-11-21T20:36:01Z No. of bitstreams: 1 2013_ValdeirAntonioDaSilva.pdf: 251047516 bytes, checksum: afbd10cdbcf21b5980832021ef1869d6 (MD5) / Approved for entry into archive by Patrícia Nunes da Silva(patricia@bce.unb.br) on 2013-11-26T19:12:11Z (GMT) No. of bitstreams: 1 2013_ValdeirAntonioDaSilva.pdf: 251047516 bytes, checksum: afbd10cdbcf21b5980832021ef1869d6 (MD5) / Made available in DSpace on 2013-11-26T19:12:11Z (GMT). No. of bitstreams: 1 2013_ValdeirAntonioDaSilva.pdf: 251047516 bytes, checksum: afbd10cdbcf21b5980832021ef1869d6 (MD5) / Uma nova matriz vítrea com composição química nominal, LBA: 50Li2O . 45B2O3 . 5Al2O3 (mol%), sem dopantes intencionais e dopada com TiO2 e/ou Nd3+, foi sintetizada pelo tradicional método de fusão e suas propriedades físicas foram investigadas pelas técnicas de Análise Térmica Diferencial (DTA), Absorção Óptica (AO), Fotoluminescência (PL), Espectroscopia Raman (ER), Microscopia de Força Atômica (AFM), Difração de Raios-X (DRX) e por cálculos realizados com base na teórica JMAYK e na Teoria de Judd-Ofelt (JO). Foi investigado a cinética de cristalização da matriz LBA, não dopada, bem como as fases cristalinas formadas (LiBO2 e Li3AlB2O6) durante o processo de tratamento térmico a 450°C, por intervalos de tempo crescentes, na faixa de 1h a 7h. Cálculos JMAYK, conjuntamente com Medidas de AFM, revelaram que a cristalização inicia-se preferencialmente na superfície e evolui para o volume em função do tempo de tratamento. Os parâmetros térmicos e a energia de ativação do sistema vítreo LBA foram obtidos pelo Método Não Isotérmico de análise de reações térmicas. Também foi investigada a cinética de cristalização da matriz LBA, não dopada e dopada com concentrações crescentes de xTiO2 (x = 0; 0,5; 1,0; 1,5; ...; 5,0)(wt%) , bem como as fases cristalinas formadas (LiBO2, LiAlO2 e LiTiO2), durante o processo de tratamento térmico na primeira e na segunda temperatura de máximo da cristalização, TC1 e TC2, por intervalos de tempo crescentes. Análises térmicas e estruturais evidenciaram uma competição entre fases cristalinas, LiAlO2 - LiTiO2, devido à co-dopagem com TiO2. A matriz vítrea LBA proposta neste trabalho, foi sugerida como meio hospedeiro para íons de neodímio, a fim de investigar a influência da variação do campo cristalino nos parâmetros espectroscópicos deste sistema. Para obter tais parâmetros, utilizou-se a Teoria de Judd-Ofelt. Foram calculados os parâmetros de intensidade, Ω9; probabilidade de emissão espontânea, (( "#/ , %)´); a taxa de ramificação, ( "#/ , %)´); a seção eficaz de emissão +(,, ,´); eficiência quântica (,); o tempo de vida radiativo 056 e a qualidade espectroscópica, 7. A codopagem com TiO2 modificou o ambiente químico e promoveu variação significativa da qualidade espectroscópica. Além disso, diminui a intensidade de absorção da “banda água” (OH). Está é uma importante fonte de supressão de luminescência (quenching). Foi investigado a devitrificação da matriz LBA, um importante passo na elucidação da estrutura vítrea, bem como, sugerimos a aplicação em sistemas fotônicos, quando dopada com Nd3+ e/ou codopada com TiO2. Por fim, nós esperamos que estes resultados possam incentivar novas pesquisas sobre esta matriz vítrea utilizando outras técnicas de caracterização. _________________________________________________________________________ ABSTRACT / A new glass matrix with chemical nominal composition, LBA: 50Li2O . 45B2O3 . 5Al2O3 (mol%) without intentional doping and doped with TiO2 and/or Nd3+ was synthesized by the traditional fusion method and their physical properties were investigated by the Differential Thermal Analysis, Optical Absorption, Photoluminescence, Micro Spectroscopy Raman, Atomic Microscopy Force and X-ray Diffraction techniques, and by the calculation performed on the basis of JMAYK and Judd-Ofelt (JO) theories. Were investigated crystallization kinetic of undoped LBA matrix, as well as, crystalline phase formed (LiBO2 e Li3AlB2O6) during heat treatment process at 450°C, by increasing time intervals in the range of 1 to 7 hour. Calculations JMAYK together with AFM measurements revealed that the crystallization starts and progresses preferentially at the surface for volume as a function of treatment time. Thermal parameters and the activation energy of the glass system LBA were obtained by Non-Isothermal analysis method of thermal reactions. Was also investigated the crystallization kinetics of the matrix LBA, doped and undoped, with increasing concentrations of xTiO2 (x = 0; 0,5; 1,0; ...; 5,0)(wt%), as well as, the crystalline phases formed (LiBO2, LiAlO2 e LiTiO2) during the heat treatment process on the first and second maximum temperature of crystallization, TC1 and TC2, for increasing time intervals. Thermal and structural analysis revealed a competition between crystalline phases, LiAlO2 - LiTiO2 due to presence with TiO2. The glassy matrix LBA proposed in this work was tested as a host medium, for neodymium ions in order to investigate the influence of the XI variation in the crystal field on the spectroscopic parameters of this system. For these, we used the Judd-Ofelt theory. They were calculated the intensity parameters, Ω9; the spontaneous emission probability, (( "#/ , %)´); the branching rate, ( "#/ , %)´); the effective emission section, +(,, ,´); the quantum efficiency, (,); the radiative life time, 056; and spectroscopic quality, 7. The presence of TiO2 modifies the environment and promotes significant variation of spectroscopic quality. It also decreases the absorption intensity of the “water” band (OH). This is an important source of suppression of luminescence (quenching). Was investigated the devitrification of LBA matrix, an important step in the elucidation of the glassy structure, as well as, we suggest the application in photonic systems, when doped with Nd3+ and/or doped with TiO2. Finally, we hope that these results will encourage further research on this glass matrix using other characterization techniques.

Embora cristais boratos dopados com ions de terras raras sejam amplamente investigados, vidros boratos desses sistemas vêm sendo pouco estudados. O cristal NdAl3(BO3)4(NAB) cujas propriedades laser e de geração de segundo harmônico (GSH) são conhecidas e continuamente relatadas na literatura, vem sendo recentemente considerado como um forte candidato para dispositivo \"microchip laser\". Alem disso, cristais dopados com íons de neodímio têm demonstrado ser excelentes para o bombeio com laseres de diodo, devido ao intenso pico de absorção próximo a 800 nm. Entretanto, existe na literatura um número muito limitado de estudos relatando as propriedades de vidros do sistema Nd2O3-Al2-O3-B2O3. Partindo dessa premissa, o objetivo principal deste trabalho foi obter vidros neste sistema, para elevadas concentrações de Nd2O3 (5-20 mol%), por meio das técnicas de fusão/moldagem convencional e fusão a laser. Dentre os materiais preparados foram obtidos três vidros transparentes, um material com separação de fases e, onde ocorreu cristalização. Os vidros obtidos, NAB136, NAB152560 e NAB226 foram caracterizados através das técnicas de análise térmica diferencial (ATD), difratometria de raios X (DRX), absorção óptica (AO) e ICP-OES (análise de composição). De acordo como os resultados de ATD, os vidros não apresentaram uma variação significativa na temperatura de transição vítrea (Tg) com o aumento da concentração de Nd2O3. O vidro NAB136, obtido com composição próxima a do cristal NdAl3(BO3)4(NAB), foi submetido a um tratamento térmico de cristalização a uma temperatura de 820°C por 2 horas. Os resultados de DRY indicaram a presença das fases cristalinas majoritárias Al4B2O9 e NAB. Medidas de absorção Óptica (AO) dos vidros no intervalo espectral de 300-1000 nm indicaram intensa absorção nos comprimentos de onda 500 nm e 800 nm. As análises de ICP-OES indicaram alta pureza dos vidros e composições próximas das composições nominais / Although borate crystals doped with rare earth ions have already been extensively investigated, borate glasses of these systems were not widely studied. The NdAl3(BO3)4(NAB) crystal, which laser and second harmonic generation (SGH) properties are well know and continuously mentioned in literature, has been recently considered as a strong candidate for microchip laser devices. Moreover, neodymium doped crystals are known for their excellent performance when pumped with diode lasers due to its intense absorption peak near to 800 nm. However, a limited number of papers have been published referring to the properties of glasses in the system Nd2O3-Al2-O3-B2O3. Based on this premise, the main purpose of this work was to prepare glasses in this system for Nd2O3 elevate concentrations (5-20 mol%) by the conventional melting/molding and laser heated methods. Among the prepared materials it was obtained three clear glasses, a material with phase separation and another one, which has crystallized. The obtained glasses, NAB136, NAB152560 and NAB226, where characterized by differential thermal analysis (DTA), X-ray diffractometry (XRD), optical absorption (OA) and ICP-OES (compositional analysis). According to the DTA results, the glasses have not presenteá a rneaningfut change in the glass transition temperature (Tg) with the increase of Nd2O3 content. The NAB136 glass, with the closest composition to the crystal NdAl3(BO3)4(NAB), was submitted to a crystallization thermal treatment at 820°C for 2 hours. XRD results showed the existence of the main crystalline phases and NAB. Optical absorption (OA) measurements of the glasses in the spectral range 300-1000 nm indicated intense absorpâion in the 500 nm and 800 nm wavelengths. ICP-OES analysis showed that the glasses posses high purity stoichiometry, close to the nominal ones

Amostras de vidros aluminoboratos de bário contendo impureza de cromo, apresentando proporções de íons Cr POT. 3+, Cr POT 5+ e Cr POT. 6+, determinadas pelas condições oxidantes ou redutoras de fusão, foram preparadas e caracterizadas pelas técnicas de absorção óptica (AO), fluorescência e de ressonância paramagnética eletrônica (RPE). As condições redutoras necessárias para favorecer a obtenção de vidros contendo majoritariamente íons de Cr POT. 3+ foram satisfeitas com a adição de 0,6% em peso de Sb IND. 2 O IND. 3. Nos vidros contendo antimônio, a banda 4 ANTIPOT. T IND. 2 do Cr POT. 3+ aparece ligeiramente deslocada para comprimentos de onda maiores e mais alargada, em relação ao vidro contendo apenas cromo como impureza adicional. O parâmetro de Racah B e a intensidade de campo ligante Ll foram determinados, obtendo-se os valores B = 759 cm-1 e = 15800 cm-1 para o vidro com cromo e antimônio e B = 736 cm-1 e = 16150 cm-1 para o vidro contendo apenas a adição de cromo. Foram observadas antirressonâncias de Fano nos espectros de AO, mais definidas nas amostras sem antimônio. Os espectros de RPE indicam que os íons Cr POT. 3+ isolados estão preferencialmente localizados em sítios distorcidos de simetria octaédrica, apresentando uma linha de absorção em g = 5,15, notando-se também a presença de pares de Cr POT 3+ caracterizados por uma componente da linha em g = 2,0. Com a adição de neodímio, os espectros de AO e de RPE do Cr POT. 3- não sofreram alterações, mas o espectro de fluorescência, com o máximo localizado em 776 nm, foi bastante modificado, mostrando uma diminuição da intensidade em regiões do espectro características da absorção do Nd POT. 3+, indicando a ocorrência de um processo de transferência de energia dos íons Cr POT. 3+ para os íons Nd POT. 3+ nos vidros aluminoboratos de bário, à temperatura ambiente. Os espectros de fluorescência e excitação dos vidros duplamente dopados com cromo e neodímio mostraram o efeito de antiressonâncias de Fano, com o deslocamento de Lamb dos vales associados ao neodímio sobre do Cr POT. 3+. / Barium aluminoborate glass samples containing chromium impurities, presenting Cr3- , Cr5- e Cr6+ íon amounts determined by the oxidizing or reducing melting conditions, have been prepared and characterized by Optical Absorption (OA), fluorescence and Electron Paramagnetic Resonance (EPR) techniques. The reducing conditions necessary to obtain glasses having mainly Cr3+ íons were satisfied with the addition of 0.6 wt% of Sb2 O3 to the batch. In glasses containing antimony, the 4T2 band is wider and shifted towards the higher wavelengths in relation to glass containing only chromium as additional impurity. The Racah parameter B and the ligand field intensity L1 were determined, yielding B = 759 cm-1 and L1 = 15800 cm-1 for the chromium- and antimony-doped glass, and B = 736 cm-1 and L1 = 16150 cm-1 for glass containing only chromium impurity. Fano antiresonances were observed in the OA spectra, better defined in the samples without antimony. The RPE spectra show that the Cr3- ions are preferentially located at distorted octahedral sites. An absorption line was observed at g = 5. 15 and it has been noted also the presence of Cr3+ pairs characterized by a line component at g = 2.0. With the addition of neodymium, the OA and EPR spectra of Cr3+ did not change, but the fluorescence spectrum observed at 776 nm was considerably modified, indicating the occurrence of an energy transfer process from Cr3+ to Nd3- íons in barium aluminoborate glasses at room temperature. The fluorescence and excitation spectra of glasses doped with chromium and neodymium have shown the Fano antiresonance effect, with the Lamb shift of the valleys associated to neodymium over the emission bands ofCr3+.

Amostras de vidros aluminoboratos de bário contendo impureza de cromo, apresentando proporções de íons Cr POT. 3+, Cr POT 5+ e Cr POT. 6+, determinadas pelas condições oxidantes ou redutoras de fusão, foram preparadas e caracterizadas pelas técnicas de absorção óptica (AO), fluorescência e de ressonância paramagnética eletrônica (RPE). As condições redutoras necessárias para favorecer a obtenção de vidros contendo majoritariamente íons de Cr POT. 3+ foram satisfeitas com a adição de 0,6% em peso de Sb IND. 2 O IND. 3. Nos vidros contendo antimônio, a banda 4 ANTIPOT. T IND. 2 do Cr POT. 3+ aparece ligeiramente deslocada para comprimentos de onda maiores e mais alargada, em relação ao vidro contendo apenas cromo como impureza adicional. O parâmetro de Racah B e a intensidade de campo ligante Ll foram determinados, obtendo-se os valores B = 759 cm-1 e = 15800 cm-1 para o vidro com cromo e antimônio e B = 736 cm-1 e = 16150 cm-1 para o vidro contendo apenas a adição de cromo. Foram observadas antirressonâncias de Fano nos espectros de AO, mais definidas nas amostras sem antimônio. Os espectros de RPE indicam que os íons Cr POT. 3+ isolados estão preferencialmente localizados em sítios distorcidos de simetria octaédrica, apresentando uma linha de absorção em g = 5,15, notando-se também a presença de pares de Cr POT 3+ caracterizados por uma componente da linha em g = 2,0. Com a adição de neodímio, os espectros de AO e de RPE do Cr POT. 3- não sofreram alterações, mas o espectro de fluorescência, com o máximo localizado em 776 nm, foi bastante modificado, mostrando uma diminuição da intensidade em regiões do espectro características da absorção do Nd POT. 3+, indicando a ocorrência de um processo de transferência de energia dos íons Cr POT. 3+ para os íons Nd POT. 3+ nos vidros aluminoboratos de bário, à temperatura ambiente. Os espectros de fluorescência e excitação dos vidros duplamente dopados com cromo e neodímio mostraram o efeito de antiressonâncias de Fano, com o deslocamento de Lamb dos vales associados ao neodímio sobre do Cr POT. 3+. / Barium aluminoborate glass samples containing chromium impurities, presenting Cr3- , Cr5- e Cr6+ íon amounts determined by the oxidizing or reducing melting conditions, have been prepared and characterized by Optical Absorption (OA), fluorescence and Electron Paramagnetic Resonance (EPR) techniques. The reducing conditions necessary to obtain glasses having mainly Cr3+ íons were satisfied with the addition of 0.6 wt% of Sb2 O3 to the batch. In glasses containing antimony, the 4T2 band is wider and shifted towards the higher wavelengths in relation to glass containing only chromium as additional impurity. The Racah parameter B and the ligand field intensity L1 were determined, yielding B = 759 cm-1 and L1 = 15800 cm-1 for the chromium- and antimony-doped glass, and B = 736 cm-1 and L1 = 16150 cm-1 for glass containing only chromium impurity. Fano antiresonances were observed in the OA spectra, better defined in the samples without antimony. The RPE spectra show that the Cr3- ions are preferentially located at distorted octahedral sites. An absorption line was observed at g = 5. 15 and it has been noted also the presence of Cr3+ pairs characterized by a line component at g = 2.0. With the addition of neodymium, the OA and EPR spectra of Cr3+ did not change, but the fluorescence spectrum observed at 776 nm was considerably modified, indicating the occurrence of an energy transfer process from Cr3+ to Nd3- íons in barium aluminoborate glasses at room temperature. The fluorescence and excitation spectra of glasses doped with chromium and neodymium have shown the Fano antiresonance effect, with the Lamb shift of the valleys associated to neodymium over the emission bands ofCr3+.

Embora cristais boratos dopados com ions de terras raras sejam amplamente investigados, vidros boratos desses sistemas vêm sendo pouco estudados. O cristal NdAl3(BO3)4(NAB) cujas propriedades laser e de geração de segundo harmônico (GSH) são conhecidas e continuamente relatadas na literatura, vem sendo recentemente considerado como um forte candidato para dispositivo \"microchip laser\". Alem disso, cristais dopados com íons de neodímio têm demonstrado ser excelentes para o bombeio com laseres de diodo, devido ao intenso pico de absorção próximo a 800 nm. Entretanto, existe na literatura um número muito limitado de estudos relatando as propriedades de vidros do sistema Nd2O3-Al2-O3-B2O3. Partindo dessa premissa, o objetivo principal deste trabalho foi obter vidros neste sistema, para elevadas concentrações de Nd2O3 (5-20 mol%), por meio das técnicas de fusão/moldagem convencional e fusão a laser. Dentre os materiais preparados foram obtidos três vidros transparentes, um material com separação de fases e, onde ocorreu cristalização. Os vidros obtidos, NAB136, NAB152560 e NAB226 foram caracterizados através das técnicas de análise térmica diferencial (ATD), difratometria de raios X (DRX), absorção óptica (AO) e ICP-OES (análise de composição). De acordo como os resultados de ATD, os vidros não apresentaram uma variação significativa na temperatura de transição vítrea (Tg) com o aumento da concentração de Nd2O3. O vidro NAB136, obtido com composição próxima a do cristal NdAl3(BO3)4(NAB), foi submetido a um tratamento térmico de cristalização a uma temperatura de 820°C por 2 horas. Os resultados de DRY indicaram a presença das fases cristalinas majoritárias Al4B2O9 e NAB. Medidas de absorção Óptica (AO) dos vidros no intervalo espectral de 300-1000 nm indicaram intensa absorção nos comprimentos de onda 500 nm e 800 nm. As análises de ICP-OES indicaram alta pureza dos vidros e composições próximas das composições nominais / Although borate crystals doped with rare earth ions have already been extensively investigated, borate glasses of these systems were not widely studied. The NdAl3(BO3)4(NAB) crystal, which laser and second harmonic generation (SGH) properties are well know and continuously mentioned in literature, has been recently considered as a strong candidate for microchip laser devices. Moreover, neodymium doped crystals are known for their excellent performance when pumped with diode lasers due to its intense absorption peak near to 800 nm. However, a limited number of papers have been published referring to the properties of glasses in the system Nd2O3-Al2-O3-B2O3. Based on this premise, the main purpose of this work was to prepare glasses in this system for Nd2O3 elevate concentrations (5-20 mol%) by the conventional melting/molding and laser heated methods. Among the prepared materials it was obtained three clear glasses, a material with phase separation and another one, which has crystallized. The obtained glasses, NAB136, NAB152560 and NAB226, where characterized by differential thermal analysis (DTA), X-ray diffractometry (XRD), optical absorption (OA) and ICP-OES (compositional analysis). According to the DTA results, the glasses have not presenteá a rneaningfut change in the glass transition temperature (Tg) with the increase of Nd2O3 content. The NAB136 glass, with the closest composition to the crystal NdAl3(BO3)4(NAB), was submitted to a crystallization thermal treatment at 820°C for 2 hours. XRD results showed the existence of the main crystalline phases and NAB. Optical absorption (OA) measurements of the glasses in the spectral range 300-1000 nm indicated intense absorpâion in the 500 nm and 800 nm wavelengths. ICP-OES analysis showed that the glasses posses high purity stoichiometry, close to the nominal ones

Made available in DSpace on 2014-06-12T18:02:45Z (GMT). No. of bitstreams: 2 arquivo2425_1.pdf: 3082700 bytes, checksum: 92455b1966dd234a3bd5c8a909cf80c9 (MD5) license.txt: 1748 bytes, checksum: 8a4605be74aa9ea9d79846c1fba20a33 (MD5) Previous issue date: 2009 / Universidade Federal de Pernambuco / Nesta dissertação são apresentados resultados experimentais que demonstram a operação de um laser aleatório constituído por um meio fortemente espalhador que contém partículas dopadas com íons de neodímio. As partículas, de formas irregulares e tamanho da ordem de 30 m, foram obtidas após pulverizarmos vidros fluoroindatos dopados com três diferentes concentrações em mol% de Nd3+: 0,5; 1,0; e 3,0. Apresentamos resultados de emissão por conversão ascendente de freqüência envolvendo Nd3+ (processo anti-Stokes). O bombeamento óptico é feito por um laser de corante centrado em 575 nm (pulsos de 10 ns; taxa de repetição de 5 Hz), em ressonância com a transição 4 I9/2 → 2 G7/2 do Nd3+. A emissão do laser aleatório ocorre em 381 nm, sendo mais eficiente na amostra que contém 3% de Nd3+. A emissão anti-Stokes ocorre devido a um processo de transferência de energia entre íons de Nd3+. Os comportamentos espectral e temporal são analisados para a caracterização do laser aleatório

Made available in DSpace on 2014-06-12T18:07:56Z (GMT). No. of bitstreams: 2 arquivo7998_1.pdf: 325094 bytes, checksum: 0addb554107bedb8490c75f5103fa527 (MD5) license.txt: 1748 bytes, checksum: 8a4605be74aa9ea9d79846c1fba20a33 (MD5) Previous issue date: 2003 / Meu maior interesse neste trabalho foi: (1) identificar mecanismos de transferência de energia entre os íons terras raras túlio (Tm3+) e neodímio (Nd3+); (2) observar conversão ascendente de energia em vidros tungstato-fluorofosfatos dopados com esses íons. A motivação para este trabalho vem do fato que os vidros tungstato-fluorofosfatos apresentam alta eficiência no que diz respeito à conversão ascendente de energia, e que alguns estados excitados do Tm3+ e Nd3+ têm aproximadamente a mesma energia, favorecendo a transferência de energia entre estes íons. Sendo assim, elaborei uma experiência onde as amostras foram bombeadas com um laser de corante operando na região 630-695nm. Inicialmente excitei as amostras com o laser de corante sintonizado em 657,7nm, pr óximo à ressonância do nível 3F2 do Tm3+ e do nível 4F9/2 do Nd3+ , e observei fluorescência em amostras contendo apenas Tm3+ ou Nd3+ . Portanto, ambos os íons absorveram a radiação incidente. Em seguida, realizei medidas adicionais na tentativa de compreender o comportamento das fluorescências encontradas nas amostras estudadas. Encontrei um processo de conversão ascendente de energia atribuído ao íon Tm3+ e resultados que indicam processos de transferência de energia (TE) entre Tm-Nd, em particular descrevi possíveis processos de TE entre estes íons

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Nesta Dissertação foi utilizado um sistema catalítico Zieger-Natta à base de neodímio para avaliar a influência do agente de halogenação e da razão molar halogênio:Nd sobre a atividade catalítica, a constante de velocidade de propagação, a conversão da polimerização, a microestrutura, a massa molecular e a polidispersão do polibutadieno 1,4-cis. O sistema utilizado era constituído por versatato de neodímio (NdV), hidreto de diisobutilalumínio (DIBAH) e um agente de halogenação. Os agentes halogenantes estudados foram: cloreto de t-butila (t-BuCl), sesquicloreto de etilalumínio (EASC) e cloreto de dietilalumínio (DEAC), em valores de razão molar Cl:Nd que variaram entre 0,5:1 e 5:1 e o dietil-eterato de trifluoreto de boro (BF3.Et2O), na razão molar F:Nd = 3:1. Os polímeros foram caracterizados por espectroscopia na região do infravermelho para determinação da microestrutura e por cromatografia de exclusão por tamanho para determinação das massas moleculares. O teor de unidades 1,4-cis variou de 90 a 98%, a massa molecular numérica média ( ) permaneceu na faixa entre 0,2 e 2x105, e a massa molecular ponderal média ( ) variou de 1,4 a 4x105 / In this Dissertation a catalyst system based on neodymium was employed to evaluate the influence of halogen source and the halogen:Nd molar ratio on the catalyst activity, polymerization constant rate, polymerization conversion, molecular weight characteristics and microstructure of polybutadiene. The catalyst systems were formed by diisobutylaluminium hydride (DIBAH), neodymium versatate (NdV) and a halogen source. The halogenating agents studied were t-butyl chloride (t-BuCl), ethylaluminium sesquichloride (EASC) and diethylaluminium chloride (DEAC) in a nCl:nNd molar ratio in the range from 0,5 to 5, and boron trifluoride diethyl ether (BF3.Et2O). The polymers were characterized by infrared espectroscopy for determining the microstructure and by size exclusion chromatography to obtain the molecular mass characteristics. The cis-1,4 units contents varied from 90 to 98%, the number-average molecular mass ( ) varied from 0,2 to 2x105 and the weight-average molecular mass ( ) varied from 1,4 to 4x105

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Nesta Dissertação foi utilizado um sistema catalítico Zieger-Natta à base de neodímio para avaliar a influência do agente de halogenação e da razão molar halogênio:Nd sobre a atividade catalítica, a constante de velocidade de propagação, a conversão da polimerização, a microestrutura, a massa molecular e a polidispersão do polibutadieno 1,4-cis. O sistema utilizado era constituído por versatato de neodímio (NdV), hidreto de diisobutilalumínio (DIBAH) e um agente de halogenação. Os agentes halogenantes estudados foram: cloreto de t-butila (t-BuCl), sesquicloreto de etilalumínio (EASC) e cloreto de dietilalumínio (DEAC), em valores de razão molar Cl:Nd que variaram entre 0,5:1 e 5:1 e o dietil-eterato de trifluoreto de boro (BF3.Et2O), na razão molar F:Nd = 3:1. Os polímeros foram caracterizados por espectroscopia na região do infravermelho para determinação da microestrutura e por cromatografia de exclusão por tamanho para determinação das massas moleculares. O teor de unidades 1,4-cis variou de 90 a 98%, a massa molecular numérica média ( ) permaneceu na faixa entre 0,2 e 2x105, e a massa molecular ponderal média ( ) variou de 1,4 a 4x105 / In this Dissertation a catalyst system based on neodymium was employed to evaluate the influence of halogen source and the halogen:Nd molar ratio on the catalyst activity, polymerization constant rate, polymerization conversion, molecular weight characteristics and microstructure of polybutadiene. The catalyst systems were formed by diisobutylaluminium hydride (DIBAH), neodymium versatate (NdV) and a halogen source. The halogenating agents studied were t-butyl chloride (t-BuCl), ethylaluminium sesquichloride (EASC) and diethylaluminium chloride (DEAC) in a nCl:nNd molar ratio in the range from 0,5 to 5, and boron trifluoride diethyl ether (BF3.Et2O). The polymers were characterized by infrared espectroscopy for determining the microstructure and by size exclusion chromatography to obtain the molecular mass characteristics. The cis-1,4 units contents varied from 90 to 98%, the number-average molecular mass ( ) varied from 0,2 to 2x105 and the weight-average molecular mass ( ) varied from 1,4 to 4x105