• Refine Query
  • Source
  • Publication year
  • to
  • Language
  • 106
  • Tagged with
  • 106
  • 106
  • 56
  • 49
  • 18
  • 16
  • 16
  • 14
  • 14
  • 13
  • 12
  • 12
  • 11
  • 11
  • 11
  • About
  • The Global ETD Search service is a free service for researchers to find electronic theses and dissertations. This service is provided by the Networked Digital Library of Theses and Dissertations.
    Our metadata is collected from universities around the world. If you manage a university/consortium/country archive and want to be added, details can be found on the NDLTD website.
51

Nitretação a plasma de um aço inoxidável duplex 2205. / Pasma nitriding of a dupllex stainless steel 2005.

Zimmermann, Margarita Rosa Bobadilla 19 November 2014 (has links)
Os aços inoxidáveis duplex se caracterizam por terem boas propriedades mecânicas e de resistência a corrosão, no entanto as suas propriedades de resistência ao desgaste são baixas. Para melhorar as propriedades superficiais desses materiais são utilizados tratamentos termoquímicos como a nitretação a plasma. Este tratamento é feito em temperaturas baixas para evitar a formação de nitretos de cromo, os quais quando são formados empobrecem o teor de cromo da matriz metálica, evitando que se forme a camada passiva, que confere resistência a corrosão a este tipo de material. Também, a nitretação a plasma permite que a dureza superficial atinja até dez vezes o valor da dureza inicial do material, o que melhora notavelmente as propriedades de resistência ao desgaste destes aços. Este estudo tem por objetivo avaliar camadas nitretadas formadas por nitretação a plasma em um aço inoxidável duplex AISI 2205. Para isto foram feitas várias experiências onde se estudou o efeito das variáveis do processo na formação da camada nitretada. Foram feitos tratamentos na temperatura de 400ºC sob pressões de 1,8 e 3,6 Torr por 720 min. Outra série de experimentos foi feita entre 350 e 500º por 240 min, para avaliar o efeito da temperatura nesse tratamento. Além disso, foi estudado o efeito de diferentes porcentagens de ferrita (40 e 64%) incialmente presente na microestrutura do material. Para isto foi feito um tratamento térmico de solubilização com têmpera em água a partir de 1200°C por uma hora, no material como recebido. A caracterização das camadas formadas foi feita por microscopia eletrônica de varredura, microscopia de força atômica, difração de raios x com radiação Cu K e difração de raios x de ângulo rasante a 5º. 7 Obtiveram-se camadas nitretadas com espessuras entre 3 µm e 18 µm. As espessuras das camadas sugerem que as variáveis: temperatura, tempo e pressão se relacionam com a espessura de forma direta, à medida que aumentam cada uma dessas variáveis, há um aumento da espessura da camada. As imagens obtidas por AFM sugerem que a nitretação a plasma induz mudanças na topografia da superfície, mudando com isto os valores de rugosidade. Também, foi observado que a espessura da camada nitretada é maior na amostra com menor percentagem de ferrita (40%). Nos difratogramas foi possível identificar a formação de austenita expandida e nitretos de cromo CrN. / The duplex stainless steels are characterized by their good mechanical properties and corrosion resistance, but their wear resistance is low. To improve the surface properties of these materials plasma nitriding thermochemical treatments are used. This treatment is done at low temperatures to avoid chromium nitrides precipitation. CrN precipitation promotes the depletion of chromium of the metallic matrix preventing the formation of the chromium oxide layer that passivates these kind of materials. In addition, the plasma nitriding treatment allows reaching hardness values up to ten times greater the characteristic values of the untreated material, greatly improving the wear resistance of these steels. The aim of this work is to study nitrided layers formed by plasma nitriding in an AISI 2205 duplex stainless steel. For this, there were made several experiments where it was studied the effect of process variables on the nitrided layer formation. Treatments were performed at temperature of 400 °C under 1.8 and 3.6 Torr pressures during 720 min. Another series of experiments was tested between 350 °C and 500 °C during 240 min, to study the temperature effect. In addition, the effect of different ferrite percentages (40 and 64%) in the microstructure was studied. The ferrite percentage variation was obtained by a heat treatment of quenching in water at 1200 °C for one hour in the material as received. Samples characterization was done by scanning electron microscopy, atomic force microscopy and x-ray diffraction Cu K, glancing angle x-ray diffraction with an incident angle of 5º. There were obtained nitrided layer with a thickness between 3m and 18m. Layer thicknesses suggest that the variables: temperature, pressure and time are related to the thickness directly. AFM images obtained suggest that the plasma nitriding induces changes in surface topography, changing the values of roughness of the surface. In addition, it was observed that the layer thickness is bigger in the sample with less ferrite percentage (40%). X-ray patterns show the presence of expanded austenite and CrN.
52

"Influência da nitretação a plasma no comportamento em fadiga dos aços inoxidáveis austeníticos AISI-SAE 304 e 316" / Plasma nitriding influence in the fatigue behaviour of austenitic stainless steels AlSl 304 and 316

Manfrinato, Marcos Dorigão 31 August 2006 (has links)
Os aços inoxidáveis austeníticos são materiais atrativos para serem utilizados em vários setores industriais que operam sob meios corrosivos, como por exemplo: indústria química, alcooleira, petroquímica, de papel e celulose, na prospecção de petróleo e nas indústrias têxtil e farmacêutica. Contudo, apresentam propriedades tribológicas pobres. No sentido de melhorar essas propriedades, como aumentar a dureza superficial, a resistência ao desgaste e a resistência à fadiga, vários métodos de tratamentos superficiais vêm sendo utilizados. Dentre eles, o mais eficiente é a nitretação por plasma. Este processo é realizado em uma câmara de vácuo sob uma mistura gasosa de hidrogênio e nitrogênio. É aplicada uma diferença de potencial entre o cátodo (porta amostras) e o ânodo (paredes da câmara), acelerando os íons contra a superfície da peça, aquecendo-a e arrancando elétrons de sua superfície. Os íons reagem com espécies da superfície do plasma formando compostos instáveis do tipo FeN que se recombinam para formarem nitretos estáveis. O sucesso deste tratamento se deve à baixa temperatura de operação, ao menor tempo efetivo de tratamento e ao controle da uniformidade da espessura da camada. A camada de nitretos formada durante o tratamento possui uma influência positiva na vida em fadiga de um componente, graças a dois motivos principais. O primeiro é o atraso na nucleação da trinca devido ao aumento da resistência mecânica superficial. O segundo motivo está relacionado com a introdução de tensões residuais compressivas durante o processo de endurecimento da superfície, que retarda a iniciação da trinca e diminui o fator de intensidade de tensão. Os corpos de prova foram nitretados a 400ºC durante 6 horas, com uma pressão de 4,5 mbar e utilizando uma mistura gasosa de 80% vol.H2 e 20%vol.N2. Ocorreu um aumento da resistência mecânica próxima á superfície, devido à camada de nitretos, o que ficou evidente com o sensível aumento no valor do limite de fadiga do material nitretado em relação ao não nitretado. O limite de fadiga do aço AISI 316 não tratado foi de 400MPa e do nitretado foi de 510MPa, enquanto que, para o aço AISI 304, o limite de fadiga do material não tratado foi de 380MPa e o limite para material submetido ao tratamento de nitretação foi de 560MPa. / The austenitic stainless steels are attractive materials to many industrial sectors which work on corrosive environments, as chemical industry alcohol, petrochemical, cellulose industries, in the petroleum prospection and pharmaceutical and textiles industries. However, they present poor tribological properties. In order to improve these properties, like increasing superficial hardness, wear and fatigue resistance superficial heat treatment methods have being used. The most efficient is the plasma nitriding process which occurs in a vacuum container under hydrogen and nitrogen gas mixture. A potential difference is applied between the cathode (samples receptor) and the anode (container walls), accelerating the ions against the piece, heating it and removing electron from the surface of material. These atoms react with the surface plasma species, producing unstable compounds like FeN, which recombine producing stable nitrides. The success of this treatment is due to the low temperature operation, the short effective time of treatment and to the uniformity control of the layer’s thickness. The nitrides layer produced during the treatment have a positive influence in the fatigue life of a component, thanks to two main reasons. The first is the retardation in crack nucleation due to increasing of superficial mechanical strength. The second reason is due to introduction of compressive residual stress during the surface hardening process, which retards de crack initiation process. The specimens were nitriding at 400°C during 6 hours, at a 4,5mbar pressure and using a gas mixture of 80% vol. H2 and 20% vol. N2. The surface mechanical strength increased, due to the nitrides layer, which was evident with the sensitive increase in the fatigue limit of the nitriding specimens, comparing to the untreated ones. The fatigue limit of the AlSl 316 steel in untreated condition was 400 MPa and in nitriding condition was 510 MPa, whereas AlSl 304 steel, the fatigue limit of the untreated condition was 480 MPa and the fatigue limit for the nitrided condition was 560 MPa.
53

Análise do desgaste na interface do aço rápido AISI M2 nitretado a plasma formando pares tribológicos com materiais metálicos

Travi, Lucas January 2016 (has links)
acarretar em uma série de fenômenos que irão desgastar ambas. O emprego de conceitos tribológicos de forma a reduzir a taxa de desgaste nas superfícies de ferramentas e melhorar o acabamento superfícial de peças produzidas fez com que tratamentos superficiais e revestimentos. Entre os tratamentos superficiais, um dos mais aplicados é a nitretação a plasma, que consiste em criar uma camada de nitretos, aumentando a dureza e resistência ao desgaste do material, podendo ele ser feito com corrente direta (método convencional) e gaiola catódica, um método deenvolvido para reduzir as heterogeneidades. Dureza e resistência ao desgaste são conceitos normalmente confundidos, mas há uma série de outros parâmetros que devem ser considerados, como o aspecto topográfico da superfície. Alguns pesquisadores concluíram que a superfície nitretada com gaiola catódica possuía um aspecto lisoe não atacada por bombardeamento iônico como a nitretada via processo convencional. Este trabalho comparou diferentes parâmetros de nitretação a plasma, caracterizando não só a superfície através de medições de microdureza Vickers e rugosidade superficial média, como também o desgaste através da formação de diferentes pares tribológicos com materiais metálicos (alumínio, aço inoxidável e aço baixo carbono), através de técnicas de microscopia óptica e microscopia eletrônica de varredura. Foi possível concluir que camadas nitretadas com menor rugosidade superficial pós-tratamento associadas a um incremento de dureza superficial reduziram o coeficiente de atrito do sistema tribológico, além disso, foi evidente a redução de material aderido na superficie nitretada com gaiola catódica para as esferas de aço inoxidável e alumínio. / The mechanical contact between two surfaces and its relative movement promotes a range of phenomena that will causes wear in both materials. The use of tribological concepts to reduce wear rate on tool surfaces and improve the surface finish of pieces produced brought the development of surface treatments and coatings. Between the surface treatments, plasma nitriding is one of the most applied, which consists in the creation of a nitrided layer that improves surface hardness and wear resistance, it may be carried out by direct current (conventional) or cathodic cage, a method developed to reduce heterogeneities. Hardness and wear resistance are concepts often related, but there are other parameters to be considered, as the surface topography. Some researchers showed that the cathodic cage plasma nitrided surface is smooth and non-attacked by sputtering as the direct current plasma nitrided surface. This work compared different plasma nitriding parameters of the AISI M2 tool steel, characterizing the surface by Vickers microhardness and average roughness and the wear by the creation of different tribopairs with metallic materials (aluminum, stainless steel and low carbon steel) using optical microscopy and scanning electron microscopy techniques. The plasma nitrided surfaces with smaller surface roughness obtained lower friction coefficient for its tribological systems, besides that, it was evident the smaller material adhesion on the cathodic cage plasma nitrided surface for the tribopairs created with the aluminum and stainless steel.
54

Desenvolvimento de um sistema de nitretação a plasma e investigação da influência da temperatura e composição da atmosfera na nitretação da liga Ti-6Al-4V

Lima, Saulo Cordeiro January 2010 (has links)
A nitretação a plasma é um processo de tratamento superficial extensivamente usado para promover melhoria de propriedades física e mecânica de metais, tais como sua dureza, resistência ao desgaste e à corrosão, que são necessárias em determinadas condições de uso mais severo. Neste trabalho foi inicialmente desenvolvido um sistema de nitretação funcional, com possibilidade de ajuste de diversos parâmetros influentes do processo, como temperatura, pressão, composição e fluxo da atmosfera nitretante e parâmetros elétricos. Utilizou-se esse sistema para nitretar amostras de Ti-6Al-4V em três temperaturas (500, 600 e 700 ºC) e cinco misturas (80, 60, 50, 40, 20 Vol%N2 com balanço de N2). Empregando as técnicas de reação nuclear e difração de raios X em ângulo rasante, obtivemos informações sobre a influência da temperatura e composição da mistura na formação das fases bem como suas estequiometrias e as espessuras dos filmes. Adicionalmente, foram adquiridos espectros Raman das amostras e então comparada às intensidades relativas entre os picos ópticos e acústicos com a composição obtida por NRA. Procedimento semelhante foi realizado tomando em conta a largura dos picos, resultando numa proposta de análise semi- quantitativa da estequiometria da fase δ-TiNx via espectro Raman. / Plasma nitriding is a surface treatment widely used to improve physical and mechanical properties of metals, such as hardness, wear resistance, and corrosion resistance that are necessary under conditions of severe use. In this work a nitriding system was built that allowed the setting of various process-parameters, such as voltage, current, temperature, pressure, flow and composition of the nitriding atmosphere. Ti-6Al-4V samples were nitrided in different treatment conditions and characterized with several analytical techniques. . Nuclear Reaction Analysis (NRA) and Grazing Incidence X-Ray Diffraction (GIXRD) gave information about the influence of deposition parameters on the formation of phases, their stoichiometry, and film thickness. In addition, Raman spectra of the samples were acquired and the intensity ratio between the optical and acoustic peaks was compared with the composition obtained by NRA. Also the width of the peaks was compared with the deviation from stoichiometry, resulting in a proposal for semi-quantitative analysis of the δ-TiNx phase via width of Raman spectrum peaks.
55

Estudo da nitretação a plasma com tela ativa e potencial flutuante para o aço rápido ASTM M2 / Investigation on active screen plasma nitriding with floating electrical potential for ASTM M2 high speed tool steel

Oliveira, Leonardo Fonseca January 2017 (has links)
No presente trabalho foi investigada a nitretação a plasma do aço rápido ASTM M2 utilizando diferentes configurações, envolvendo as técnicas convencional e com tela ativa. Na técnica convencional, o material a ser nitretado atua como o cátodo do sistema, sendo coberto diretamente pela bainha da descarga luminescente. Nos tratamentos conduzidos com a técnica de tela ativa, uma estrutura de tela em formato cilíndrico atua como cátodo e o material a ser nitretado é posicionado no seu interior. Neste novo processo, como não há potencial elétrico externo aplicado aos substratos, a descarga luminescente se desenvolve apenas na estrutura da tela, evitando problemas intrínsecos do método convencional de nitretação a plasma. Todos os tratamentos investigados foram executados com os seguintes parâmetros: Temperatura de 500 °C, mistura gasosa composta 76% de volume de gás nitrogênio e 24% de volume de gás hidrogênio e pressão de 3 milibar. Para os tratamentos com tela ativa, os substratos foram mantidos eletricamente isolados. Os resultados foram comparados observando a diferença de método de nitretação (com e sem o uso de tela ativa) e a influência do tempo de tratamento (variando sua duração em 1, 4 e 8 horas) Todos os experimentos foram realizados utilizando uma fonte de potência de tensão retificada aplicada na tela ou nas amostras, dependendo da configuração. Adicionalmente, para o tempo de nitretação de 4 horas uma fonte de potência com tensão pulsada também foi aplicada. As amostras nitretadas foram caracterizadas por ensaios de rugosidade, ensaios de dureza e microdureza, microscopia ótica, microscopia eletrônica de varredura e difração de raios-X. Ensaios tribológicos para avaliação da resistência ao desgaste das diferentes condições de tratamento foram conduzidos. Dentre os principais resultados foi observada uma clara diferença na profundidade de camada nitretada, que foi sempre mais profunda nos tratamentos convencionais. Apesar de formadas camadas menos profundas, as amostras nitretadas oriundas dos tratamentos com tela ativa demonstraram melhor desempenho nos ensaios tribológicos, resultando em taxas de desgaste até sete vezes inferior do que as amostras do nitretadas convencionalmente, este resultado foi atribuído a não formação da zona de compostos nas amostras nitretadas com tela ativa. / In the present work an investigation on the plasma nitriding of ASTM M2 High-Speed Steel using different configurations was carried out, involving traditional and active screen techniques. In the traditional technique, the material to be nitrided act as the system cathode, being directly covered by the glow discharge sheath. In the active screen treatments, a cylindrical mesh structure (screen) plays the role of the cathode and the material to be nitrided is positioned in its interior. In this new process, as there is no external electric potential applied to the specimens, the glow discharge develops only in the screen structure, avoiding intrinsic problems from the conventional plasma nitriding method. All the studied treatments were carried out with the following parameters: temperature of 500 °C, gas mixture of 76 vol.-% N2 and 24 vol.-% H2 and pressure of 3 millibar. For the active screen treatments, the samples were kept electrically insulated. The results were compared observing the differences in the nitriding method (with and without the use of active screen) and the nitriding time influence (varying its duration in 1, 4 and 8 hours) All experiments were carried using a rectified voltage power supply applied to the screen or to the samples, depending on the configuration. Additionally, for the nitriding time of 4 hours a pulsed voltage power supply was also employed. The nitrided samples were characterized by roughness tests, hardness and microhardness tests, optical microscopy and scanning electron microscopy, X-ray diffraction. Tribological tests to evaluate the wear resistance of the different treatment conditions were also carried out. Among the main results a clear difference in the case layer depth was noticed, which was always deeper in the conventional treatments. Although forming shallower case depths, the active screen nitrided specimens presented better performance in the tribological tests, resulting in wear rates up to seven times lower than the wear rate for conventionally plasma nitrided samples, this result was assigned due to the non-formation of compound layer in the active screen plasma nitrided samples.
56

Estudo do fenômeno da fluência na liga Ti-6AI-4V submetida a tratamentos de nitretação e carbonetação por plasma / Study of the Creep Phenomenon on Ti-6Al-4V Alloy Subjected to Treatments of Plasma Nitriding and Carburizing

Oliveira, Verônica Mara Cortez Alves de 06 July 2010 (has links)
O presente trabalho tem como objetivo principal avaliar o efeito da nitretação e da carbonetação por plasma na liga Ti-6Al-4V sob condições de fluência na faixa de 500 a 600°C. Os resultados permitiram concluir que a microestrutura da liga Ti-6Al-4V é constituída pela configuração de Widmanstätten, com uma dureza média de 300 ± 17 HV para a condição como recebida e 334±18 HV para a amostra tratada termicamente. Após os tratamentos termoquímicos por plasma observou-se para a nitretação a plasma a formação de uma camada nitretada de espessura média de 4?m e dureza de 1539 ± 157 HV. A dureza está relacionada com a espessura e a presença das fases Ti2N e TiN identificadas por difratometria de raios X. Para a carbonetação a plasma verificou-se a formação de uma camada constituída pelo carboneto TiC0,66, de espessura média igual a 1,5 ?m e dureza de 809 ± 79 HV. A nitretação a plasma reduziu os valores de rugosidade média de 1,29?m do material como recebido para 1,18?m e a carbonetação aumentou esse valor de 1,28 ?m da amostra tratada termicamente para 2,02 ?m. Os testes demonstraram que a nitretação reduziu a taxa de fluência e aumentou a vida em fluência a 600 °C. A carbonetação contribuiu para reduzir a taxa estacionária. Com base nos valores de energia de ativação na faixa de 272 a 309 kJ/mol e nos valores do expoente de tensão de 4,82 a 7,28, estima-se que o mecanismo dominante de deformação por fluência está associado à escalagem de discordâncias para todas as condições experimentais. A análise fractográfica revelou que os mecanismos de fratura estão associados principalmente à nucleação e coalescência de microcavidades e decoesão intergranular. / This work aims to evaluate the effect of plasma nitriding and carburizing on the Ti-6Al-4V alloy subjected to creep in the range 500-600 °C. The results showed that the microstructure of Ti-6Al-4V consists of Widmanstätten morphologie, with a hardness of 300 ± 17 HV for the as received condition and 334 ± 18 HV for the sample heat-treated. After treatments thermochemical by plasma was observed for plasma nitriding the formation of a nitrided layer of hardness of 1539 ± 157 HV and of average thickness of 4 ?m. The hardness is due to the thickness and the presence of Ti2N and TiN phases identified by X-ray diffraction. For plasma carburizing was observed the formation of a carbide layer composed of TiC0,66, of average thickness equal to 1.5 ?m and hardness of 809 ± 79 HV. The treatment of plasma nitriding reduced the values of average roughness of 1.29 ?m of the as received condition to 1.18 ?m and the plasma carburizing increased this value of 1.28 ?m of the sample heat-treated to 2.02 ?m. The tests showed that the plasma nitriding reduced the rate of creep and increased the creep life at 600 °C. Based on the values of activation energy in the range 272-309 kJ / mol and the values of stress exponent from 4.82 to 7.28, it was estimated that the dominant mechanism of creep deformation is associated with the climb of dislocations for all experimental conditions. The fractographic analysis revealed that the fracture mechanisms are mainly associated with the nucleation and coalescence of microvoids and decoehasion intergranular.
57

Efeito da nitretação por plasma no comportamento em fadiga da liga Ti-6Al-4V / Nitriding plasma effect on Ti-6Al-4V fatigue behavior

Castro, Michele Cristina Biondo de 03 December 2018 (has links)
A liga Ti-6Al-4V apresenta excelentes propriedades mecânicas, baixa densidade, alta dureza e resistência à corrosão. Entretanto, tratamentos superficiais como a nitretação por plasma são amplamente utilizadas para melhorar a resistência a fadiga desta liga. O objetivo deste trabalho foi tratar termoquimicamente a liga Ti-6Al-4V por meio da nitretação por plasma a fim de verificar a sua influência nas propriedades de fadiga e comparar os resultados obtidos com as não nitretadas. Este tratamento superficial foi realizado com o objetivo de retardar a etapa de nucleação da trinca. A nitretação por plasma foi realizada em temperaturas em torno de 720°C por 4 horas, numa atmosfera de N2, Ar e H2 (5:5:1). Foi realizado um tratamento térmico nas amostras para se obter a microestrutura de Widmanstätten. A temperatura usada foi de 1050°C por 30 minutos. A caracterização microestrutural das amostras nitretadas e não nitretadas foi realizada usando difração de raios X (DRX), microscopia óptica (MO), e microscopia eletrônica de varredura (MEV). Os resultados da difração de raios X das amostras nitretadas mostram a presença de fases: α, β, ε-Ti2N, e δ-TiN e nas amostras não nitretadas as fases α e β. Essas análises revelaram a presença de uma superfície rica em nitretos seguida de uma zona de difusão com nitrogênio na matriz. A rugosidade superficial foi estudada, e foi observada um aumento na rugosidade de 61% após a nitretação. Os testes de fadiga foram realizados em uma máquina de ensaios flexo rotativa, com uma razão de carregamento R=-1 . Os resultados obtidos mostraram que as propriedades de fadiga foram melhoradas após a nitretação por plasma, retardando a etapa de nucleação de trinca. / The Ti-6Al-4V alloy presents excellent mechanical properties, low density, high toughness and corrosion resistance. However, surface treatments like plasma nitriding are widely used to improve the fatigue resistance of this alloy. Therefore, the aim of this work was to treat thermochemically Ti-6Al-4V alloy by means of plasma nitriding to verify its influence in fatigue properties and compare the results with the untreated ones. This surface treatment was performed with the purpose of retards the crack initiation. The plasma nitriding was performed in temperatures around 720°C for 4 hours, with a gas atmosphere N2, Ar and H2 (5:5:1). A heat treatment was made in the samples to obtain a Widmanstätten microstructure. The temperature used was 1050°C for 30 minutes. Microstructural characterizations of nitrided and non-nitrided samples were carried out using X-ray diffraction (XRD), optical microscopy (OM) and scanning electron microscopy (SEM). The XRD results of the nitrided sample showed the presence of the α, β, ε-Ti2N, and δ-TiN phases. These analyses revealed a surface layer rich in nitrides on the surface, followed by a diffusion layer of nitrogen in the matrix. The surface roughness was compared between the nitrided and non-nitrided layer, and it was observed that the roughness increased 61% after the plasma nitriding. Fatigue tests were performed in a rotating bending testing machine with a stress ratio (R=-1). The results obtained in fatigue tests showed that the fatigue properties were improved after plasma nitriding, retarding the crack initiation.
58

Caracterização e avaliação do comportamento tribológico do aço DIN X100CrMoV8-1-1 com tratamento dúplex

Santos, Giovanni Rocha dos January 2015 (has links)
As vantagens relacionadas à utilização de revestimentos duros depositados via processos PAPVD (Plasma Assisted Physical Vapor Deposition) são bem conhecidas e dadas por suas propriedades. As principais propriedades destes filmes são a capacidade de não incrementar significativamente a rugosidade dos substratos em que são depositados, sua alta dureza conferindo alta resistência ao desgaste, baixa reatividade quando se trata de revestimentos de compostos cerâmicos e capacidade de reduzir o coeficiente de atrito de pares tribológicos inseridos em diversos meios. A nitretação a plasma de substratos antes da aplicação de um revestimento faz com que outros benefícios possam ser encontrados, dentre eles destacam-se o aumento da capacidade de sustentação de carga do substrato e a criação de uma região que propicia um gradiente de propriedades entre o substrato e o revestimento. Desta forma é caracterizado o tratamento dúplex, o qual consiste em um substrato nitretado seguido da aplicação de um revestimento. Através do processo de nitretação a plasma, camadas de difusão foram formadas em amostras de geometria cilíndrica do aço DIN X100CrMoV8-1-1, industrialmente utilizado para construção de ferramentas para operações de corte e estampagem. Duas profundidades distintas de camada de difusão foram formadas. O revestimento escolhido para este estudo foi o TiCN (carbonitreto de titânio), produzido industrialmente e disponível no mercado brasileiro. As técnicas de caracterização foram utilizadas para medir a rugosidade, a dureza, os perfis de composição química, as fases formadas, as tensões residuais e a adesão dos revestimentos. Após esta caracterização inicial, foram feitos ensaios utilizando a técnica de esfera-sobre-disco em amostras e de DST (Dobramento sob Tensão) em pinos com geometria específica com o objetivo de se avaliar o comportamento tribológico dos tratamentos dúplex desenvolvidos. / The advantages related to the utilization of hard thin films deposited on tools and components via PAPVD (Plasma Assisted Physical Vapor Deposition) are well known and given by their properties. The main properties of these coatings are their capacity to avoid significant roughness increase of the coated substrates, high hardness which provides high wear resistance, low reactivity in the case of ceramic coatings and the possibility to provide very low friction coefficient. The thin films associated with plasma nitriding (the so called duplex treatments) applied to the substrates can bring much more benefits. The coating load bearing capacity can be increased by the presence of the diffusion zone on the substrate that allows a gradient of mechanical properties from the coating to the core of the material. In this work, by plasma nitriding process, two distinct depths of diffusion layer were developed in samples and pins manufactured out of the DIN X100CrMoV8-1-1 steel. This steel grade is commonly used to manufacture tools for cutting and stamping operations. Following a previous work the chosen coating for this study was a graded TiCN (titanium carbonitride). The samples were characterized by several different techniques in order to access surface roughness, chemical composition profiles, present phases, residual stresses, hardness and adhesion of the obtained nitrided layer and coatings. After this initial characterization, tests were performed using a pin-on-disc apparatus and BUT (Bending under tension test) with the aim to evaluate the tribological behavior of the developed duplex treatment for for sheet metal forming application.
59

Caracterização e avaliação do comportamento tribológico do aço DIN X100CrMoV8-1-1 com tratamento dúplex

Santos, Giovanni Rocha dos January 2015 (has links)
As vantagens relacionadas à utilização de revestimentos duros depositados via processos PAPVD (Plasma Assisted Physical Vapor Deposition) são bem conhecidas e dadas por suas propriedades. As principais propriedades destes filmes são a capacidade de não incrementar significativamente a rugosidade dos substratos em que são depositados, sua alta dureza conferindo alta resistência ao desgaste, baixa reatividade quando se trata de revestimentos de compostos cerâmicos e capacidade de reduzir o coeficiente de atrito de pares tribológicos inseridos em diversos meios. A nitretação a plasma de substratos antes da aplicação de um revestimento faz com que outros benefícios possam ser encontrados, dentre eles destacam-se o aumento da capacidade de sustentação de carga do substrato e a criação de uma região que propicia um gradiente de propriedades entre o substrato e o revestimento. Desta forma é caracterizado o tratamento dúplex, o qual consiste em um substrato nitretado seguido da aplicação de um revestimento. Através do processo de nitretação a plasma, camadas de difusão foram formadas em amostras de geometria cilíndrica do aço DIN X100CrMoV8-1-1, industrialmente utilizado para construção de ferramentas para operações de corte e estampagem. Duas profundidades distintas de camada de difusão foram formadas. O revestimento escolhido para este estudo foi o TiCN (carbonitreto de titânio), produzido industrialmente e disponível no mercado brasileiro. As técnicas de caracterização foram utilizadas para medir a rugosidade, a dureza, os perfis de composição química, as fases formadas, as tensões residuais e a adesão dos revestimentos. Após esta caracterização inicial, foram feitos ensaios utilizando a técnica de esfera-sobre-disco em amostras e de DST (Dobramento sob Tensão) em pinos com geometria específica com o objetivo de se avaliar o comportamento tribológico dos tratamentos dúplex desenvolvidos. / The advantages related to the utilization of hard thin films deposited on tools and components via PAPVD (Plasma Assisted Physical Vapor Deposition) are well known and given by their properties. The main properties of these coatings are their capacity to avoid significant roughness increase of the coated substrates, high hardness which provides high wear resistance, low reactivity in the case of ceramic coatings and the possibility to provide very low friction coefficient. The thin films associated with plasma nitriding (the so called duplex treatments) applied to the substrates can bring much more benefits. The coating load bearing capacity can be increased by the presence of the diffusion zone on the substrate that allows a gradient of mechanical properties from the coating to the core of the material. In this work, by plasma nitriding process, two distinct depths of diffusion layer were developed in samples and pins manufactured out of the DIN X100CrMoV8-1-1 steel. This steel grade is commonly used to manufacture tools for cutting and stamping operations. Following a previous work the chosen coating for this study was a graded TiCN (titanium carbonitride). The samples were characterized by several different techniques in order to access surface roughness, chemical composition profiles, present phases, residual stresses, hardness and adhesion of the obtained nitrided layer and coatings. After this initial characterization, tests were performed using a pin-on-disc apparatus and BUT (Bending under tension test) with the aim to evaluate the tribological behavior of the developed duplex treatment for for sheet metal forming application.
60

Desenvolvimento de um sistema de nitretação a plasma e investigação da influência da temperatura e composição da atmosfera na nitretação da liga Ti-6Al-4V

Lima, Saulo Cordeiro January 2010 (has links)
A nitretação a plasma é um processo de tratamento superficial extensivamente usado para promover melhoria de propriedades física e mecânica de metais, tais como sua dureza, resistência ao desgaste e à corrosão, que são necessárias em determinadas condições de uso mais severo. Neste trabalho foi inicialmente desenvolvido um sistema de nitretação funcional, com possibilidade de ajuste de diversos parâmetros influentes do processo, como temperatura, pressão, composição e fluxo da atmosfera nitretante e parâmetros elétricos. Utilizou-se esse sistema para nitretar amostras de Ti-6Al-4V em três temperaturas (500, 600 e 700 ºC) e cinco misturas (80, 60, 50, 40, 20 Vol%N2 com balanço de N2). Empregando as técnicas de reação nuclear e difração de raios X em ângulo rasante, obtivemos informações sobre a influência da temperatura e composição da mistura na formação das fases bem como suas estequiometrias e as espessuras dos filmes. Adicionalmente, foram adquiridos espectros Raman das amostras e então comparada às intensidades relativas entre os picos ópticos e acústicos com a composição obtida por NRA. Procedimento semelhante foi realizado tomando em conta a largura dos picos, resultando numa proposta de análise semi- quantitativa da estequiometria da fase δ-TiNx via espectro Raman. / Plasma nitriding is a surface treatment widely used to improve physical and mechanical properties of metals, such as hardness, wear resistance, and corrosion resistance that are necessary under conditions of severe use. In this work a nitriding system was built that allowed the setting of various process-parameters, such as voltage, current, temperature, pressure, flow and composition of the nitriding atmosphere. Ti-6Al-4V samples were nitrided in different treatment conditions and characterized with several analytical techniques. . Nuclear Reaction Analysis (NRA) and Grazing Incidence X-Ray Diffraction (GIXRD) gave information about the influence of deposition parameters on the formation of phases, their stoichiometry, and film thickness. In addition, Raman spectra of the samples were acquired and the intensity ratio between the optical and acoustic peaks was compared with the composition obtained by NRA. Also the width of the peaks was compared with the deviation from stoichiometry, resulting in a proposal for semi-quantitative analysis of the δ-TiNx phase via width of Raman spectrum peaks.