Electronic textiles, or smart textiles, is a field that is growing due to the opportunities it provides. Textile integrated electronics enables soft, flexible, lightweight electronic devices that enable long term monitoring within the medical field. Pressure sensors is one device within this field that has been researched. A textile integrated pressure sensor enables monitoring of heart rate, muscle activity, posture, gait phases and finger movements. In this project a resistive pressure sensor has been produced using embroidery with the purpose of investigating how construction and design parameters influence the resistance-pressure relationship. The study consisted in different phases where in Phase I parameters such as fabric substrate, stitch length and yarn type was examined. Phase II investigated design parameters like electrode pattern design, sensor shape, trace distance and size. In the design phase a new electrode pattern and sensor shape was tested. Finally in Phase III a sensor matix and sensor chain was constructed in order to evaluate the possibility of obtaining touch location. The findings in this study showed that the shape, size and yarn type had the most distinct influence on the sensor performance in regards to the resistance-pressure relationship. In an additional recovery test the results indicated that both textile substrate and stitch length could influence the ability to recover to its original shape after applying cyclic pressure. It was also found that the new pattern design performed equally to the conventional pattern designs and at the same time reduced material consumption as well as the embroidery time. The sensor matrix and sensor chain could display a change in resistance when applying a weight at each sensing element, implying that touch location could be detected, but would need further development in construction before potential implementation.

No description available.

Tato diplomová práce se zabývá technologií tlustých vrstev a jejím možným použitím pro nekonvenční aplikace. První část práce je rešeršní a zaměřuje se především na aplikace tlustovrstvé technologie v různých oblastech použití. V teoretické části práce je dále popsána technologie LTCC, včetně technologických postupů výroby. V praktické části jsou řešeny dvě aplikace v tlustovrstvé technologii. Jedná se návrh a výrobu vysokofrekvenčního filtru a optického senzoru tlaku technologií LTCC. V závěru práce jsou provedena měření a jsou zhodnoceny dosažené výsledky.

This diploma thesis describes design and development of creating field instrument demonstration kit. Kit is capable of measuring multiple sensors such as thermocouples, RTDs, or pressure sensors, analogue sensor simulation is also provided. Sensor’s side is isolated from output, which is composed of 4 - 20 mA current loop and HART interface. Current loop also provides power supply and kit can communicate via HART also when alarm current (3,2 mA) is set. Basic safety features like open wire detection, over and undervoltage protection are also implemented.

This paper deals with the estimation of altitude of the drone for which the sensors like ultrasonic, barometric pressure sensors and their characteristics plays a major role. To  estimate the altitude of the drone, we used the matlab software with Simulink. apart from the software and hardware description, we discuss several issues regarding the equipment,abilities and performance of the drone.

Main goal of this thesis is evaluation of the available SON and sacrificial layer technologies from the perspective of temperature sensor design. Based on the findings, a series of detector architectures is proposed. The work is subdivided into two major parts, with the first one targeting the process characterization. Good command of the selected technology, awareness of its dependencies and limitations, is essential and has to be examined prior to any MEMS design. Pressure related topics are of particular interest, since this criterion, among others, highly influences the performance of thermal systems. Knowledge of the critical parameters is applied in the second half, where the actual IR sensor design is considered. Process characterization, required for thermal insulation estimations, is not the only link between the two physics fields. Discussed IR detectors are highly inspired by the developed pressure sensing solutions. This resulted in either similar operation principles being applied, or even the same fabricated structures being adapted for new use.:List of abbreviations List of Figures List of Tables Acknowledgements 1 Introduction 1.1 Motivation and organization of the work 1.2 Microstructure fabrication methods 1.2.1 Surface micromachining 1.2.2 Bulk micromachining 1.2.3 SOI and SON structuring 2 Pressure sensor for process characterization applications 2.1 Motivation 2.2 Pirani gauge approach 2.2.1 Principles of operation and state of the art 2.2.2 Modelling 2.2.2.1 Setup 2.2.2.2 Results 2.2.3 Processing 2.2.4 Measurement 2.2.4.1 Setup 2.2.4.2 Results 2.2.5 Application 2.2.5.1 Outgassing characterization 2.2.5.2 Reliability investigation 2.2.5.3 Thermal emitter for IR spectroscopy 2.2.5.4 Active pressure sensor 2.3 Capacitive sensor approach 2.3.1 Principles of operation and state of the art 2.3.2 Surface channel approach 2.3.3 SON channel approach 2.3.4 Application 2.3.4.1 MEMS dynamic characterization 2.3.4.2 Differential capacitive pressure sensor 2.4 Summary and overview of results 3 Temperature sensor for IR applications 3.1 Motivation 3.2 Resistive sensor approach 3.2.1 Principles of operation 3.2.2 Modelling 3.2.3 Measurement 3.3 Capacitive sensor approach 3.3.1 Principles of operation 3.3.2 Modelling 3.3.2.1 Setup 3.3.2.2 Results 3.3.3 Processing 3.4 Junction - based approach 3.4.1 State of the art 3.4.2 Thermal insulation design 3.4.2.1 Overview 3.4.2.2 Processing 3.4.2.3 Thermal performance 3.4.3 Detector design 3.4.3.1 Diode sensing solution 3.4.3.2 Bipolar Junction Transistor sensing solution 3.4.3.3 Junction Field Effect Transistor sensing solution 3.5 Summary and overview of results 4 Conclusion Bibliography

No description available.

O objetivo deste estudo foi o desenvolvimento de compósitos poliméricos flexíveis e altamente condutores elétricos preparados por moldagem por compressão e por fabricação de filamentos fundidos (FFF) para possíveis aplicações como materiais piezoresistivos ou piezoelétricos para sensores de compressão. Compósitos baseados em misturas de poli(fluoreto de vinilideno)/poliuretano termoplástico (PVDF/TPU) como matriz e contendo várias frações de negro de fumo-polipirrol (CB-PPy) como aditivo condutor foram preparados. Diversas técnicas de caracterização foram realizadas para avaliar as propriedades mecânicas, térmicas, químicas e elétricas, morfologia e printabilidade dos materiais investigados. Primeiro, blendas de PVDF/TPU com diferentes composições foram produzidas por mistura por fusão seguida de moldagem por compressão. Os resultados mostraram que a flexibilidade desejada para os materiais foi melhorada com a adição de TPU aos compósitos de PVDF. As imagens SEM evidenciaram a obtenção de uma blenda co-contínua com 50/50 vol% de PVDF/TPU. As blendas compostas de PVDF/TPU 38/62 vol% e a blenda co-contínua de PVDF/TPU 50/50 vol% foram selecionadas como matrizes para a preparação de compósitos moldados por compressão e impressos em 3D a fim de alcançar uma ótima combinação entre condutividade, propriedades mecânicas e printabilidade. Várias quantidades de negro de fumo-polipirrol, de 0 a 15%, foram adicionadas às blendas selecionadas para aumentar a condutividade elétrica dos compósitos e possivelmente atuar como agente nucleante para a fase cristalina do PVDF a fim de aumentar sua resposta piezoelétrica. A adição de CB-PPy aumentou a condutividade elétrica de todos os compósitos. No entanto, a condutividade elétrica dos compósitos baseados em blendas co-contínuas PVDF/TPU 50/50 vol% foi maior do que as encontradas para os compósitos de PVDF/TPU 38/62 vol% com mesma concentração de aditivo. De fato, o limiar de percolação elétrico dos compósitos com blenda co-contínua foi de 2%, enquanto o limiar de percolação elétrico dos compósitos compostos da blenda não contínua foi de 5%. Com relação às propriedades mecânicas, a incorporação do aditivo condutor nas blendas resultou em materiais mais rígidos com maior módulo de elasticidade, menor alongamento na ruptura e maior módulo de armazenamento. O módulo de armazenamento (G') e a viscosidade complexa (η*) dos compósitos aumentaram com a adição de CB-PPy. O limiar de percolação reológico foi de 3% para PVDF/TPU/CB-PPy 38/62 vol% e 1% para PVDF/TPU/CB-PPy 50/50 vol%, indicando que uma quantidade maior de carga poderia comprometer a processabilidade dos compósitos. A adição de CB-PPy também resultou na redução dos valores de Tg e Tm dos compósitos devido à redução da mobilidade das cadeias poliméricas. Com base na condutividade elétrica e no comportamento mecânico dos compósitos, três composições diferentes foram selecionadas para a extrusão de filamentos para serem posteriormente utilizados no processo de impressão 3D. No geral, as peças impressas em 3D apresentaram propriedades mecânicas e elétricas inferiores devido à presença de vazios, defeitos e camadas sobrepostas que podem dificultar o fluxo de elétrons. Os valores de condutividade elétrica dos compósitos impressos em 3D de PVDF/TPU/CB-PPy 38/62 vol% contendo 5% e 6% de CB-PPy são de uma a sete ordens de grandeza menores do que os encontrados para os compósitos com a mesma composição moldados por compressão. Mesmo que o valor da condutividade elétrica para o compósito PVDF/TPU 38/62 vol% com 6% de CB-PPy moldado por compressão foi de 1,94x10-1 S•m-1, o compósito impresso em 3D com a mesma composição mostrou um valor muito baixo de condutividade elétrica de 6,01x10-8 S•m-1. Por outro lado, o compósito co-contínuo de PVDF/TPU 50/50 vol% com 10% de aditivo impresso em 3D apresentou um alto valor de condutividade elétrica de 4,14×100 S•m-1 mesmo após o processo de impressão. Além disso, as respostas piezoresistivas dos compósitos foram investigadas. Para os compósitos PVDF/TPU/CB-PPy 38/62 vol%, as amostras moldadas por compressão e impressas em 3D com 5% e 6% de CB-PPy exibiram boa resposta piezoresistiva. No entanto, apenas os compósitos com 6% de aditivo apresentaram valores elevados de sensibilidade e gauge factor, atuação em ampla faixa de pressão e respostas piezoresistivas reprodutíveis durante a aplicação de 100 ciclos de compressão/descompressão para ambos os métodos de fabricação. Por outro lado, para os compósitos co-contínuos de PVDF/TPU/CB-PPy apenas a amostra moldada por compressão com 5% de CB-PPy apresentou respostas piezorresistivas boas e reprodutíveis. A cristalinidade e o teor de fase β do PVDF foram investigados para os compósitos. Embora o grau de cristalinidade das amostras tenha diminuído com a adição de CB-PPy, a porcentagem de fase β no PVDF aumentou. O coeficiente piezoelétrico d33 das amostras aumentou com a porcentagem de fase β. A adição de 6% ou mais de CB-PPy foi necessária para aumentar significativamente o coeficiente piezoelétrico (d33) dos compósitos. O conteúdo de fase β e as respostas piezoelétricas do PVDF foram menores para as amostras preparadas por FFF. Por fim, como pesquisa colateral, a eficiência de blindagem contra interferência eletromagnética (EMI-SE) foi medida para todos os compósitos. Compósitos com maior condutividade elétrica apresentaram melhor blindagem da radiação eletromagnética. Além disso, os compósitos baseados na blenda co-contínua apresentaram maior eficiência de blindagem contra EMI do que os compósitos de PVDF/TPU 38/62 vol%. O principal mecanismo de blindagem foi a absorção para todos os compósitos. As amostras preparadas por FFF apresentaram respostas de EMI-SE menores quando comparadas às amostras moldadas por compressão. / The aim of this study was the development of flexible and highly electrically conductive polymer composites via compression molding and fused filament fabrication for possible applications as piezoresistive or piezoelectric materials for pressure sensors. Composites based on blends of poly(vinylidene fluoride)/thermoplastic polyurethane (PVDF/TPU) as matrix and containing various fractions of carbon black-polypyrrole (CB-PPy) as conductive filler were prepared. Several characterization techniques were performed in order to evaluate the mechanical, thermal, chemical and electrical properties, morphology and printability of the investigated materials. First, PVDF/TPU blends with different compositions were prepared by melt compounding followed by compression molding. The results showed that the flexibility aimed for the final materials was improved with the addition of TPU to PVDF composites. SEM images evidenced the achievement of a co-continuous blend comprising 50/50 vol% of PVDF/TPU. The blends composed of PVDF/TPU 38/62 vol% and the co-continuous blend of PVDF/TPU 50/50 vol% were selected as matrices for the preparation of compression molded and 3D printed composites in order to achieve an optimal compromise between electrical conductivity, mechanical properties and printability. Various amounts of carbon black-polypyrrole, from 0 up to 15%, were added to the selected blends in order to rise the electrical conductivity of the composites and to possible act as nucleating filler for the β crystalline phase of PVDF in order to increase its piezoelectric response. The addition of CB-PPy increased the electrical conductivity of all composites. However, the electrical conductivity of composites based on PVDF/TPU 50/50 vol% co-continuous blends was higher than those found for PVDF/TPU 38/62 vol% composites at the same filler content. Indeed, the electrical percolation threshold of the conductive co-continuous composite blends was 2%, while the electrical percolation threshold of the composites with the nonco-continuous composite blends was 5%. With respect to the mechanical properties, the incorporation of the filler into the blends leaded to more rigid materials with higher elastic modulus, lower elongation at break and higher storage modulus. The storage modulus (G’) and complex viscosity (η*) of the composites increased with the addition of CB-PPy. The rheological percolation threshold was found to be 3% for PVDF/TPU/CB-PPy 38/62 vol% and 1% for PVDF/TPU/CB-PPy 50/50 vol%, indicating that higher amount of filler could compromise the processability of the composites. The addition of CB-PPy also resulted in a reduction on the Tg and Tm values of the composites due to the reduction of the mobility of the polymeric chains. Based on the electrical conductivity and mechanical behavior of the composites, three different compositions were selected for the extrusion of filaments to be used in a 3D printing process. Overall, the 3D printed parts presented lower mechanical and electrical properties because of the presence of voids, defects and overlapping layers that can hinder the flow of electrons. The electrical conductivity values of PVDF/TPU/CB-PPy 38/62 vol% composites containing 5% and 6 wt% of CB-PPy 3D printed samples are one to seven orders of magnitude lower than those found for compression molded composites with the same composition. Even if the electrical conductivity value for PVDF/TPU 38/62 vol% compression molded composite with 6% of CB-PPy was as high as 1.94x10-1 S•m-1, the 3D printed composite with same composition showed a very low electrical conductivity of 6.01x10-8 S•m-1. On the other hand, the 3D printed co-continuous composite PVDF/TPU 50/50 vol% with 10% of filler displayed a high value of electrical conductivity of 4.14×100 S•m-1 even after the printing process. Moreover, the piezoresistive responses of the composites were investigated. For PVDF/TPU/CB-PPy 38/62 vol% composites, the compression molded and 3D printed samples with 5% and 6% of CB-PPy exhibited good piezoresistive response. However, only the composites with 6% displayed high sensitivity and gauge factor values, large pressure range and reproducible piezoresistive responses under 100 cycles for both methods. On the other hand, for PVDF/TPU/CB-PPy co-continuous composites only the compression molded sample with 5% of CB-PPy presented good and reproducible piezoresistive responses. The crystallinity and β phase content of PVDF were investigated for the composites. Althought the degree of crystallinity of the samples decreased with the addition of CB-PPy, the percentage of β phase in PVDF was increased. The piezoelectric coefficient d33 of the samples increased with the percentage of β phase. The addition of 6% or more of CB-PPy was necessary to increase significatively the piezoelectric coefficient (d33) of the composites. The β phase content and piezoelectric responses of PVDF were lower for samples prepared by FFF. Finally, as a collateral research, the electromagnetic interference shielding effectiveness (EMI-SE) were measured for all composites. Composites with higher electrical conductivity showed better shielding of the electromagnetic radiation. In addition, composites based on the co-continuous blend displayed higher EMI shielding efficiency than 38/62 vol% composites. The main mechanism of shielding was absorption for all composites. Specimens prepared by FFF displayed diminished EMI-SE responses when compared to compression molded samples. / Lo scopo di questo studio è lo sviluppo di compositi polimerici flessibili e ad elevata conducibilità elettrica tramite stampaggio a compressione e manifattura additiva (fused filament fabrication) per possibili applicazioni come materiali piezoresistivi o piezoelettrici in sensori di pressione. In particolare, sono stati preparati compositi a base di miscele di poli(vinilidene fluoruro)/poliuretano termoplastico (PVDF/TPU) come matrice e contenenti varie frazioni di nerofumo-polipirrolo (CB-PPy) come riempitivo conduttivo. Sono state utilizzate diverse tecniche di caratterizzazione al fine di valutare le proprietà meccaniche, termiche, chimiche ed elettriche, la morfologia e la stampabilità dei materiali ottenuti. In primo luogo, miscele PVDF/TPU con diverse composizioni sono state preparate mediante mescolatura allo stato fuso seguita da stampaggio a compressione. I risultati hanno mostrato che la flessibilità del PVDF viene notevolemente migliorata dall’aggiunta di TPU. Le immagini SEM hanno evidenziato il raggiungimento di una miscela co-continua per una composizione 50/50% in volume di PVDF/TPU. Le miscele composte da PVDF/TPU 38/62 vol% e la miscela co-continua di PVDF/TPU 50/50 vol% sono state selezionate come matrici per la preparazione di compositi per stampaggio a compressione e manifattura additiva al fine di ottenere un compromesso ottimale tra conducibilità, proprietà meccaniche e stampabilità. Alle miscele selezionate sono state aggiunte varie quantità di nerofumo-polipirrolo, dallo 0 al 15%, per aumentare la conducibilità elettrica dei compositi ed eventualmente fungere da additivo nucleante per la fase β cristallina del PVDF al fine di aumentarne la risposta piezoelettrica. L'aggiunta di CB-PPy ha aumentato la conduttività elettrica di tutti i compositi. Tuttavia, la conduttività elettrica dei compositi basati su miscele co-continue di PVDF/TPU 50/50% in volume era superiore a quella trovata per compositi PVDF/TPU 38/62% in volume con lo stesso contenuto di riempitivo. Infatti, la soglia di percolazione elettrica delle miscele conduttive era del 2%, mentre la soglia di percolazione elettrica dei compositi con miscele composite non continue era del 5%. Per quanto riguarda le proprietà meccaniche, l'incorporazione del riempitivo nelle mescole ha portato a materiali più rigidi con modulo elastico più elevato, allungamento a rottura inferiore e modulo conservativo più elevato. Il modulo conservativo (G') e la viscosità complessa (η*) dei compositi sono aumentate con l'aggiunta di CB-PPy. La soglia di percolazione reologica è risultata essere del 3% per PVDF/TPU/CB-PPy 38/62 vol% e dell'1% per PVDF/TPU/CB-PPy 50/50 vol%, indicando che una maggiore quantità di riempitivo potrebbe compromettere la processabilità dei compositi. L'aggiunta di CB-PPy ha comportato anche una riduzione dei valori di Tg e Tm dei compositi a causa della riduzione della mobilità delle catene polimeriche. Sulla base della conduttività elettrica e del comportamento meccanico dei compositi, sono state selezionate tre diverse composizioni per l'estrusione di filamenti da utilizzare in un processo di stampa 3D. Nel complesso, le parti stampate in 3D presentavano proprietà meccaniche ed elettriche inferiori a causa della presenza di vuoti, difetti e strati sovrapposti che possono ostacolare il flusso di elettroni. I valori di conducibilità elettrica dei compositi PVDF/TPU/CB-PPy 38/62 vol% contenenti il 5% e il 6% di CB-PPy di campioni stampati in 3D sono da uno a sette ordini di grandezza inferiori a quelli trovati per i compositi stampati a compressione con la stessa composizione. Anche se il valore di conducibilità elettrica per il composito stampato a compressione PVDF/TPU 38/62 vol% con il 6% di CB-PPy era pari a 1,94x10-1 S•m-1, il composito stampato in 3D con la stessa composizione ha mostrato un valore molto basso di conducibilità elettrica, pari a 6,01x10-8 S•m-1. D'altra parte, il composito PVDF/TPU 50/50 vol% stampato in 3D con il 10% di riempitivo ha mostrato un elevato valore di conducibilità elettrica, pari a 4,14 × 100 S•m-1, anche dopo il processo di stampa. Inoltre, sono state studiate le risposte piezoresistive dei compositi. Per i compositi PVDF/TPU/CB-PPy 38/62 vol%, i campioni stampati a compressione e stampati in 3D con il 5% e il 6% di CB-PPy hanno mostrato una buona risposta piezoresistiva. Tuttavia, solo i compositi con il 6% hanno mostrato valori di sensibilità e gauge factor elevati, ampio intervallo di pressione e risposte piezoresistive riproducibili in 100 cicli per entrambi i metodi. D'altra parte, per i compositi co-continui PVDF/TPU/CB-PPy solo il campione stampato a compressione con il 5% di CB-PPy ha presentato risposte piezoresistive adeguate e riproducibili. La cristallinità e il contenuto di fase β del PVDF sono stati studiati per i compositi. Sebbene il grado di cristallinità dei campioni diminuisca con l'aggiunta di CB-PPy, la percentuale di fase β in PVDF risulta aumentata. Il coefficiente piezoelettrico d33 dei campioni aumenta anch’esso con la percentuale di fase β. L'aggiunta del 6% o più di CB-PPy è stata necessaria per aumentare significativamente il coefficiente piezoelettrico (d33) dei compositi. Il contenuto di fase β e le risposte piezoelettriche del PVDF sono inferiori per i campioni ottenuti mediante stampa 3D. Infine, come ricerca collaterale, è stata misurata l'efficacia della schermatura contro le interferenze elettromagnetiche (EMI-SE) per tutti i compositi. I compositi con una maggiore conduttività elettrica hanno mostrato una migliore schermatura della radiazione elettromagnetica. Inoltre, i compositi basati sulla miscela co-continua hanno mostrato un'efficienza di schermatura EMI maggiore rispetto ai compositi a 38/62% in volume. Per tutti i compositi, il principale meccanismo di schermatura è l'assorbimento. I campioni preparati mediante manifattura additiva hanno mostrato risposte EMI-SE inferiori rispetto ai campioni stampati a compressione.

Este projeto de pesquisa apresenta o desenvolvimento de protótipos de transmissores industriais de pressão do tipo diferencial piezoresistivo com saída analógica a dois fios 4-20 mA. Os dispositivos usam um DSSP (processador digital de sinal do sensor) para realizar compensação térmica nas temperaturas de 0°C até 80°C e a calibração de pressão diferencial na faixa de 0-25 bard e de pressão de linha de 0-7 barg. Os transmissores permitem a leitura de diversas variáveis industriais: pressão diferencial, pressão relativa e pressão absoluta em fluidos. Os transmissores têm um TEB (total error band) menor que 0,15 de porcentagem de escala plena. A saída analógica dos transmissores diferenciais de pressão é caracterizada utilizando como base normas internacionais BS (British Standards). Os parâmetros avaliados nos transmissores de pressão são: a exatidão, o coeficiente térmico do offset, o coeficiente térmico do span, o total error band, e os desvios no tempo a curto e longo prazo. Esse trabalho é resultado da parceria dada entre o Laboratório de Sistemas Integráveis da Escola Politécnica da Universidade de São Paulo (LSI/EPUSP) e a empresa MEMS Microssistemas Integrados Híbridos de Pressão. / This research project presents the prototypes development of piezoresistive differential pressure transmitters with analog two-wire output of 4-20 mA. The devices use a DSSP (Digital Signal Processor Sensor) to achieve temperature compensation at temperatures from 0°C to 80°C and differential pressure calibration range from 0 bard to 25 bard and line pressure range from 0 barg to 7 barg. The transmitters measure several industrial variables: differential pressure, relative pressure and absolute pressure at fluids. The transmitters have a TEB (total error band) less than 0.15 percent of full scale. The analog output of the differential pressure transmitters is characterized using British Standards-BS. The parameters evaluated in the pressure transmitters are: the accuracy, the thermal coefficient of the offset, the thermal coefficient of the span, the total error band, the start-up drift and long-term drift. This work is the result of the academic and technological partnership between the Laboratory of Integrated Systems of the Polytechnic School of the University of São Paulo (LSI / EPUSP) and the MEMS company - Microssistemas Integrados Híbridos de Pressão Ltda.

Os objetivos do trabalho consistem em síntese e caracterização de três polímeros: poli(2,1,3-benzotiadiazol-4,7-ilenovinileno) (PBTDV), poli(2,1,3-benzotiadiazol-4,7-ilenovinileno-co-2-bromo-5-hexilóxi-p-fenilenovinileno (PBTDV-co-BHPPV) e poli(2-bromo-5-hexilóxi-p-fenilenovinileno) (BHPPV), sendo os dois primeiros inéditos; aplicação de polímeros condutores no desenvolvimento de um nariz eletrônico capaz de identificar madeiras; e aplicação de polímeros condutores em um sensor de pressão. Os polímeros foram preparados de maneira satisfatória via redução catódica de seus precursores tetra-halogenados, que forneceu produtos com rendimentos apreciáveis. Para o projeto do nariz eletrônico que pretende identificar madeiras, dois conjuntos de espécies de madeira foram estudadas: (a) mogno e cedro e (b) imbuia e canela-preta. O nariz eletrônico desenvolvido apresenta um conjunto de quatro sensores de gás, que foram construídos por meio da deposição de finos filmes de polímeros dopados sobre a superfície de eletrodos interdigitados. Esse conjunto de sensores foi desenvolvido com sucesso, sendo capaz de diferenciar as espécies de madeira com taxa de acerto de 100%. Por fim, foi desenvolvido também com sucesso um sensor de gás capaz de atuar como sensor de pressão. Esse dispositivo mostrou-se sensível à variação de pressão, do vácuo a ambiente, e os ensaios apresentaram boa reprodutibilidade. A resposta do sensor, frente à variação de pressão, é produto de interação(ões) entre a camada ativa do polímero utilizado (PHBPE, poli(4\'-hexilóxi-2,5-bifenilenoetileno)) e algum(ns) componente(s) do ar atmosférico ou da atmosfera particular do laboratório. Esse sensor é de fácil fabricação e barato (~ R$ 1,00), sendo possível sua aplicação como sensor para pressões menores do que a ambiente / The syntheses of three polymers via electrochemical reduction of their precursors are described. Two out of the three generated polymers have never been described before. An electronic nose was developed capable of identifying two pairs of wood species: (a) mahogany and cedar and (b) Brazilian walnut and black-cinnamon. The electronic nose consisted of four gas sensors, fabricated by the deposition of thin doped polymer films onto the surface of interdigitated electrodes. The device presented a rate of hits of 100% in 80 assays of identification of the above cited species. Finally, a gas sensor based on a conductive polymer and capable of acting as a pressure sensor was fabricated. The sensor was suitable for measuring air pressures in the range of 100 mmHg to 700 mmHg due to its sensibility to one or more specific compounds present in the air. The device is cheap, easy to fabricate and lasts for several months