Made available in DSpace on 2014-06-11T19:35:01Z (GMT). No. of bitstreams: 0 Previous issue date: 2009-07-03Bitstream added on 2014-06-13T19:44:47Z : No. of bitstreams: 1 reis_jmsn_dr_arafo.pdf: 1310753 bytes, checksum: 17bd719b0c46c00b10cbd2db022db42a (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Este estudo avaliou o comportamento exotérmico de 5 resinas rígidas para reembasamento imediato, duas experimentais (E1 e E2) à base de agentes de ligação cruzada (etileno glicol dimetacrilato e 1,4-butanediol dimetacrilato) e três comerciais (Kooliner-K, New Truliner-NT, Tokuyama Rebase II-TR II), bem como o grau de conversão (GC), a sorção (Sor) e a solubilidade (Sol) em água, a contração linear de polimerização (CLP), as propriedades viscoelásticas e a resistência à flexão desses materiais e de uma resina para base de prótese (Lucitone 550-L). Foi avaliada, ainda, a resistência de união (RU) entre os reembasadores e a resina de base. O comportamento exotérmico foi avaliado (n=4) com termopar tipo K inserido no interior das resinas, em matriz circular (60 x 2,0 mm), e mantido até a polimerização. O GC (%) foi avaliado (n=5) por espectroscopia de infravermelho por transformadas de Fourier (32 leituras; resolução 4,0 cm-1). A Sor e a Sol (μg/mm3) foram mensuradas (n=5) seguindo as recomendações da ISO 1567. A CLP (%) foi avaliada (n=10), em projetor de perfil (Nikon 6C), em corpos-de-prova circulares (50 x 0,5 mm). Para avaliar as propriedades viscoelásticas, corpos-de-prova (40 x 10 x 3,3 mm) foram submetidos (n=2) à análise térmica dinâmico-mecânica (DMTA) em diferentes intervalos de temperatura (ciclos). O módulo de armazenamento (E’) e o amortecimento mecânico (tan δ) a 37ºC foram registrados durante o primeiro e último ciclo da DMTA. A temperatura de transição vítrea (Tg) foi mensurada somente no último ciclo da DMTA. Os ensaios mecânicos de flexão (0,5 mm/min) foram realizados (n=10) em corpos-de-prova (64 x 10 x 3,3 mm) intactos ou reembasados e a resistência (MPa) calculada na tensão máxima (RFM) e no limite de proporcionalidade (RFLP). Para avaliar a RU (MPa) entre os materiais, 60 cilindros (20 x 20 mm) da resina L foram processados... / This study evaluated the exothermic behavior, degree of conversion (DC), water sorption (WSor), water solubility (WSol), linear polymerization shrinkage (LPS), viscoelastic properties and flexural strength of 5 hard chairside reline resins, two experimental (E1 and E2) based on crosslinking agents (ethylene glycol dimethacrylate and 1,4-butanediol dimethacrylate) and three commercially available (Kooliner-K, New Truliner-NT and Tokuyama Rebase II-TR II), and one heat-polymerized denture base resin (Lucitone 550-L). The shear bond strength (SBS) between the denture base resin and the reline materials was also evaluated. The exothermic behavior of circular specimens (60 x 2.0 mm) during polymerization was assessed (n=4) using a type K thermocouple. The DC (%) was measured (n=5) by Fourier Transformed infrared-attenuated total reflectance (FTIR-ATR) spectroscopy (32 scans; resolution of 4.0 cm-1). WSor and Wsol (μg/mm3) were determined (n=5) according to the recommendation stated in ISO 1567. The LPS (%) was measured (n=10) in circular specimens (50 x 0.5 mm) using a perfilometer (Nikon 6C). The viscoelastic properties of the specimens (40 x 10 x 3.3 mm) were evaluated (n=2) by dynamical-mechanical thermal analysis (DMTA) under different temperature ranges (runs). Values of storage modulus (E’) and loss tangent (tan δ) at 37ºC were obtained from the first and last runs. The glass transition temperature (Tg) was only measured from the last run. Ultimate flexural strength (UFS - MPa) and flexural strength at the proportional limit (FSPL - MPa) were determined (n=10) by three-point test (0.5 mm/min) using intact and relined specimens (64 x 10 x 3.3 mm). To evaluate the SBS between the materials, 60 cylinders (20 x 20 mm) of the denture base resin L were processed, relined (3.5 x 5.0 mm) and submitted to shear testing (0.5 mm/min). Data were analyzed by ANOVA and Tukey... (Complete abstract click electronic access below)

Este estudo investigou a resistência à tração (ou limite de resistência à tração- LRT) e a porosidade de reembasadores resilientes temporários modificados por concentrações inibitórias mínimas (CIMs) de agentes antifúngicos para o biofilme Candida albicans (SC5314). Para os testes de LRT, corpos de prova em forma de halteres (n=7) com uma área transversal de 33 mm x 6 mm x 3 mm foram produzidos para os materiais resilientes (Trusoft e Softone) sem (controle) ou com incorporação de cinco fármacos em suas CIMs: nistatina- 0,032 g; diacetato de clorexidina- 0,064; cetoconazol- 0,128 g; miconazol- 0,256 g; itraconazol-0,256 g (grama de fármaco por grama de pó de material resiliente). Após a plastificação, as amostras foram imersas em água destilada a 37°C durante 24 h, 7 e 14 dias e, então, testadas em tensão em uma máquina universal de ensaios (EMIC DL-500 MF) a 40 mm/min. A porosidade foi mensurada por absorção de água, com base na exclusão do efeito plastificante. Inicialmente, determinou-se por isotermas de sorção, que a solução de armazenagem adequada para os corpos de prova (65 mm x 10 mm x 3,3 mm) de ambos os materiais foi o cloreto de cálcio anidro a 50% (S50). Assim, o fator de porosidade (FP) foi calculado para os grupos de estudo (n=10) formados por espécimes sem (controle) ou com incorporação de fármaco em suas CIMs (nistatina, clorexidina ou cetoconazol) após a armazenagem em água destilada ou S50 por 24 h, 7 e 14 dias. Os dados de resistência à tração (MPa) e percentagem de alongamento (%) foram submetidos à ANOVA de 3 fatores seguida pelo teste de Tukey (=0,05). Os dados de porosidade foram analisados estatisticamente por ANOVA de medidas repetidas para 4 fatores e teste de Tukey (=0,05). Ao final de 14 dias, a resistência à tração para ambos os materiais foi significativamente menor nos grupos modificados pelo miconazol e itraconazol em relação aos outros grupos (P<0,0001), que não mostraram diferenças significativas entre si (P>0,05). Após 7 e 14 dias em água, o miconazol e itraconazol adicionados a ambos os materiais resultaram em percentagens significativamente menores de alongamento em comparação com os outros fármacos e ao controle (P<0,0001), que foram semelhantes entre si (P>0,05). O cetoconazol não resultou em alterações significativas no FP para ambos os materiais resilientes em água ao longo de 14 dias (P>0,05). Em comparação aos controles, houve aumento dos FPs do Softone e Trusoft aos 14 dias de imersão em água somente após a adição de nistatina e clorexidina e de clorexidina, respectivamente (P<0,05). Ambos os materiais não apresentaram alterações significativas no FP em até 14 dias de imersão na S50, em comparação aos controles (P>0,05). Em todas as condições experimentais, os FPs do Softone e Trusoft foram significativamente menores quando imersos em S50 em comparação com a água destilada (P<0,05). Concluiu-se que a adição de nistatina, clorexidina e cetoconazol nas CIMs para o biofilme de C. albicans não resultou em efeitos deletérios na resistência à tração e na percentagem de alongamento dos materiais resilientes temporários para base de prótese até o período de 14 dias. A adição de antifúngicos nas CIMs não resultou em efeitos adversos à porosidade de ambos os materiais resilientes temporários em diferentes períodos de imersão em água, com exceção da clorexidina e nistatina no Softone e clorexidina no Trusoft aos 14 dias. Não foram observados efeitos deletérios para a porosidade de ambos os materiais resilientes modificados com as CIMs dos fármacos durante os 14 dias de imersão na S50. / This study investigated the tensile strength (ultimate tensile strength- UTS) and porosity of temporary soft denture liners modified by minimum inhibitory concentrations (MICs) of antifungal agents for Candida albicans biofilm (SC5314). For UTS tests, dumbbell-shaped specimens (n=7) with a central cross-sectional area of 33 mm x 6 mm x 3 mm were produced by resilient materials (Trusoft and Softone) without (control) or with incorporation of five drugs at MICs: nystatin- 0.032 g; chlorhexidine diacetate-0.064 g; ketoconazole- 0.128 g; miconazole- 0.256 g; itraconazole- 0.256 g (each per gram of soft liner powder). After plasticization, specimens were immersed in distilled water at 37°C for 24 h, 7 and 14 days, and then tested in tension in a universal testing machine (EMIC DL-500 MF) at 40 mm/min. The porosity was measured by water absorption, based on exclusion of the plasticizer effect. Initially, it was determined by sorption isotherms that the adequate storage solution for specimens (65 mm x 10 mm x 3.3 mm) of both materials was 50% anhydrous calcium chloride (S50). Then, the porosity factor (PF) was calculated for the study groups (n=10) formed by specimens without (control) or with drug incorporation at MICs (nystatin, chlorhexidine or ketoconazole) after storage in distilled water or S50 for 24 h, 7 and 14 days. Data of tensile strength (MPa) and elongation percentage (%) were submitted to 3-way ANOVA followed by Tukey\'s test (=0.05). Data of porosity were statistically analyzed by 4-way repeated measures ANOVA and Tukeys test (=0.05). At the end of 14 days, the tensile strength for both materials was significantly lower in the groups modified by miconazole and itraconazole compared to the other groups (P<0.0001), which showed no significant difference between them (P>0.05). After 7 and 14 days in water, miconazole and itraconazole added into both materials result in significant lower elongation percentages compared to the other drugs and control (P<.0001), which were similar to each other (P>0.05). Ketoconazole resulted in no significant changes in PF for both liners in water over 14 days (P>0.05). Compared to the controls, Softone and Trusoft PFs were increased at 14-day water immersion only after addition of nystatin and chlorhexidine, and chlorhexidine, respectively (P<0.05). Both materials showed no significant changes in PF in up to 14 days of S50 immersion, compared to the controls (P>0.05). In all experimental conditions, Softone and Trusoft PFs were significantly lower when immersed in S50 compared to distilled water (P<0.05). It was concluded that the addition of the nystatin, chlorhexidine and ketoconazole at MICs for C. albicans biofilm resulted in no harmful effects on the ultimate tensile strength and elongation percentage of the temporary soft denture liners up to 14-day period. The addition of antifungals at MICs resulted in no detrimental effects for the porosity of both temporary soft liners in different periods of water immersion, except for chlorhexidine and nystatin in Softone and chlorhexidine in Trusoft at 14 days. No deleterious effect was observed for the porosity of both soft liners modified by the drugs at MICs over 14 days of S50 immersion.

Orientador: Marcelo Ferraz Mesquita / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-12T19:45:53Z (GMT). No. of bitstreams: 1 Takahashi_JessicaMieFerreiraKoyama_M.pdf: 3156848 bytes, checksum: e45be536e6455880f4523ac84c0d2894 (MD5) Previous issue date: 2009 / Resumo: O objetivo neste estudo foi avaliar o efeito de diferentes tempos de envelhecimento acelerado realizado por meio da simulação do intemperismo natural, sobre as propriedades de deformação permanente e resistência à tração da união de dois materiais resilientes usados como forradores de base de prótese, sendo um à base de resina acrílica e outro à base de silicone. Para o ensaio de resistência à tração da união, os materiais reembasadores foram unidos a dois blocos de resina acrílica (9 X 9 X 40 mm) utilizada para a confecção de bases de próteses totais. Para o ensaio de deformação permanente, os corpos-de-prova de reembasador resiliente apresentaram 19 mm de altura e 12,7 mm de diâmetro. Os corpos-de-prova (n=10) foram submetidos ao envelhecimento acelerado nos tempos 2, 4, 8, 16, 32 e 64 ciclos por meio da simulação do intemperismo natural. O ensaio de resistência à tração da união foi realizado em máquina de ensaios EMIC DL-500 MF com velocidade média de 5 mm/min, sendo avaliado também o tipo de falha de união (adesiva, coesiva ou mista). Para o ensaio de deformação permanente foi utilizado aparelho mecânico descrito na especificação no 18 da A.D.A., com carga compressiva de 750 gf. Foi realizada análise estatística utilizando o teste Kruskall-Wallis associado ao método de Dunn, para comparação entre os materiais no mesmo intervalo de envelhecimento, e o teste Mann-Whitney para comparação do efeito dos tempos de envelhecimento em cada material. Avaliando os resultados obtidos após a análise estatística, pôde-se observar que o reembasador à base de silicone apresentou menor porcentagem de deformação permanente (p<0,0001) e maior resistência à tração (p<0,0001) que o reembasador à base de resina acrílica em todos os intervalos de envelhecimento. E que a simulação do intemperismo natural não afetou a deformação permanente (p=0,90) e a resistência à tração (p=0,15) do reembasador à base de silicone, mas reduziu a porcentagem de deformação permanente e aumentou a resistência à tração do material à base de resina acrílica (p<0,05). Os resultados demonstraram que o reembasador resiliente à base de silicone é menos susceptível à cargas compressivas, pois apresentou melhor recuperação elástica, menor deformação permanente e maior resistência à tração que o à base de resina acrílica. E que o envelhecimento acelerado, afeta as propriedades de deformação permanente e resistência à tração do material reembasador à base de resina acrílica. / Abstract: This study aimed to evaluate the effect of different times of accelerated ageing over the properties of permanent deformation and tensile bond strength of two soft liners used on prostheses relining. The soft liners studied were auto-polymerizing and acrylic resin and silicone based. The materials were processed according the manufacturers' instructions. The resilient liner specimens (9 X 9 X 3 mm) for tensile bond strength were processed between 2 acrylic resin blocks (9 X 9 X 40 mm). The resilient liner specimens for permanent deformation test were 19 mm height and 12.7 mm diameter. The specimens (n=10) were submitted to accelerated ageing process during 2, 4, 8, 16, 32 and 64 cycles. Tensile bond strength was performed with crosshead speed of 5 mm/min using a testing machine EMIC DL-500 MF. Permanent deformation was performed with an apparatus described on specification no 18 of A.D.A., with compressive load of 750 gf. Statistical analysis was performed using Kruskall-Wallis and Dunn tests to compare materials on the same ageing period and Mann-Whitney test to compare the effect of different ageing periods on each material. The results obtained after statistical analysis demonstrated that the silicone based reliner presented lower percentage of permanent deformation (p<0.0001) and higher tensile bond strength (p<0.0001) than the acrylic resin based reliner in all the ageing intervals. And that the accelerated ageing process did not affect the permanent deformation (p=0.90) and tensile bond strength (p=0.15) of the silicone based reliner, but reduced the percentage of permanent deformation and increased tensile bond strength of the acrylic resin based reliner (p<0.05). Results demonstrated that silicone based reliner is less susceptible to compressive loads, presenting better elastic recovery, lower permanent deformation and higher tensile bond strength. And that accelerated ageing affected only acrylic resin based reliners. / Mestrado / Protese Dental / Mestre em Clínica Odontológica

A proposta desse trabalho foi verificar através de microscopia confocal de varredura a laser, se a utilização de uma resina fotopolimerizável de baixa viscosidade (Biscover®) e do etil-cianoacrilato (Super Bonder®) seriam eficientes em prevenir ou reduzir a formação de biofilme de Candida albicans. Cinqüenta e seis corpos de prova em resina acrílica para reembasamento (New Truliner) foram divididos aleatoriamente em 7 grupos: G1 (C)- Controle; G2 (SBAE)- Recebeu uma camada de Super Bonder® em sua superfície antes de esterilizar; G3 (SBDE)- Recebeu uma camada de Super Bonder® em sua superfície depois de esterilizar; G4 (SB3G)- 3 gotas de Super Bonder® incorporadas na resina; G5 (SB4G)- 4 gotas de Super Bonder® incorporadas na resina; G6 (BCDE)- Recebeu uma camada de Biscover® em sua superfície depois de esterilizar e G7 (BCAE) Recebeu uma camada de Biscover® em sua superfície antes de esterilizar. Todos os corpos de prova foram inoculados com Candida albicans para formação de biofilme. Os biofilmes remanescentes sobre os corpos de prova foram corados através dos fluorocromos SYTO-9 e iodeto de propídeo para análise no microscópio confocal. Os dados foram analisados através dos testes estatísticos de Kruskal-Wallis e Dunn, a um nível de significância de 5%. Os resultados obtidos pelo microscópio confocal mostraram que, de todos os corpos de prova modificados, os que receberam a Super Bonder® em sua superfície, G2(SBAE) e G3(SBDE) foram os únicos que significativamente reduziram a formação de biofilme de Candida albicans. Através da análise das imagens geradas pelo microscópio confocal, pôde-se observar que nos grupos G2(SBAE) e G3(SBDE) os campos apresentaram um reduzido número de células fúngicas e a maioria se encontrava na forma de levedura (inócua), enquanto que, para os demais grupos, além de observado um elevado número de células, a maioria destas se apresentava em forma de hifa (patogênica). Desse modo, a partir das condições experimentais desse estudo pôde-se concluir que as modificações do material testado com a Super Bonder® aplicada em sua superfície podem ser uma abordagem potencialmente útil para reduzir ou controlar a formação do biofilme em resinas acrílicas. / The purpose of this study was to verify, using the confocal laser scanning microscopy (CLSM), if the use of a photoactivated resin of low viscosity (Biscover®) and a ethyl-cyanoacrylate (Super Bonder®) could be efficient in the prevention or reduction of Candida albicans biofilms. Fifty six reline resin specimens (New Truliner) were fabricated and randomly divided into 7 groups: G1 (C)- Control; G2 (SBAE)- a Super Bonder® layer was applied on the surface before sterilization; G3 (SBDE)- the surface received a Super Bonder® layer after sterilization; G4 (SB3G)- 3 drops of Super Bonder® were incorporated in the structure of the resin; G5 (SB4G)- 4 drops of Super Bonder® were incorporated in the structure of the resin; G6 (BCDE)- a Biscover® layer was applied on the surface after sterilization; G7 (BCAE) the surface received a Biscover® layer before sterilization. All the specimens were inoculated with Candida albicans for biofilm dvelopment. The remaining biofilms on the specimens were stained with fluorochromes SYTO-9 and propidium iodide to be analyzed by CLSM. The data were statistically analyzed using the Kruskal-Wallis and Dunn test, considering a significance level of 5%. The data obtained by CLSM revealed that of all specimens modified, those that received a Super Bonder® layer on their surface, G2(SBAE) e G3(SBDE), presented the better results, reducing Candida albicans biofilm formation. Analyzing the images produced by CLSM it was possible to see that groups G2(SBAE) e G3(SBDE) showed a reduced number of cells, and they were in a less phatogenetic form (Yeast), while the other groups showed a high number of cells in a more pathogenetic form (Hyphae). Considering the experimental conditions of this study we can conclude that the material modifications done with Super Bonder® on the surface could be an interesting way to prevent or control biofilm formation on acrylic resin.

No presente estudo, a proposta foi avaliar a ação antimicrobiana sobre o biofilme de Candida albicans (SC 5314) e determinar a mínima concentração inibitória (MCI) de cinco fármacos utilizados no tratamento de estomatite protética (nistatina, miconazol, cetoconazol, itraconazol e diacetato de clorexidina), quando incorporados em reembasadores resilientes temporários à base de resina acrílica (Trusoft e Softone) bem como o efeito dessa modificação sobre as propriedades de dureza Shore A e rugosidade superficial dos materiais. Para determinação das MCIs, o biofilme fúngico foi formado sobre corpos de prova circulares (10 mm x 1 mm) dos materiais (n = 6) modificados (experimentais) ou não (controle) pela adição dos fármacos. Diferentes concentrações dos antimicrobianos foram testadas e a viabilidade celular determinada espectrofotometricamente pelo ensaio de redução de sais de tetrazólio- XTT, nos períodos de 24 h, 48 h, 7 e 14 dias. As medidas espectrofotométricas foram convertidas em porcentagens de redução fúngica e as MCIs determinadas como aquelas suficientes para inibir 90% ou mais do crescimento de C. albicans. Para os ensaios de dureza e rugosidade, corpos de prova retangulares (36 mm x 7 mm x 6 mm) dos materiais resilientes (n= 8) foram confeccionados sem (controle) ou com incorporação dos fármacos nas MCIs previamente definidas. Após armazenamento em água destilada a 37°C por 24 h, 7 e 14 dias, foram realizados os testes de dureza em durômetro Shore A (Woltest, GSD-709A) e de rugosidade superficial em rugosímetro (Surftest SJ-301). Os resultados foram analisados estatisticamente por ANOVA 3 fatores, seguida pelo teste de Tukey (=0,05). De acordo com os resultados, as MCIs determinadas para fármacos incorporados aos materiais resilientes foram: 0,032, 0,256, 0,128, 0,256 e 0,064 g/mL para nistatina, miconazol, cetoconazol, itraconazol e clorexidina, respectivamente. A adição dos antimicrobianos em ambos os materiais não alterou os valores de dureza, ou resultou na sua diminuição em relação ao controle, exceto para a incorporação de miconazol ao Softone, que demonstrou maiores médias após 14 dias (P=0,0035). A incorporação de nistatina aos dois materiais, de clorexidina ao Trusoft e de cetoconazol ao Softone não alterou os valores de rugosidade em relação ao controle após 7 e 14 dias (P>0,05). Nesses períodos, o itraconazol aumentou a rugosidade dos materiais (P<0,0001). Em relação às 24 h iniciais, o período de 14 dias mostrou que a rugosidade com a adição de nistatina, miconazol e cetoconazol foi reduzida para o Trusoft (P<0,05) e não apresentou alteração para o Softone (P>0,05). Foi possível concluir que a incorporação dos antimicrobianos testados inibiu o crescimento de C. albicans nos materiais ao longo de 14 dias de avaliação. A adição de todos os fármacos testados, exceto o miconazol no Softone, não causou alterações deletérias à dureza dos materiais resilientes no período avaliado. No período final, a adição de nistatina, miconazol e cetoconazol em ambos os reembasadores e de clorexidina no Trusoft não resultou em efeitos adversos na rugosidade. / The purpose of this study was to evaluate the antimicrobial action on Candida albicans biofilm (SC5314) and determine the minimum inhibitory concentration (MIC) of five drugs for denture stomatitis\' treatment (nystatin, miconazole, ketoconazole, itraconazole, and chlorhexidine diacetate) incorporated into temporary denture relines (Trusoft e Softone) as well the effect of this addition on the Shore A hardness and surface roughness of the materials. For MIC determination, the fungal biofilm was formed on disc specimens (10mm x 1 mm) of the materials (n= 6) modified (experimental) or not (control) by the addition of drugs. Different dosages of the antimicrobials were tested and cellular viability was determined by spectrophotometric tetrazolium salt XTT reduction assay at 24 h, 48 h, 7 and 14 days of incubation. The spectrophotometric measurements were converted to percentage reduction in candidal growth and the MICs were determined as the concentrations necessary to inhibit 90% or more of fungal viability. For hardness and surface tests, rectangular specimens (36 mm X 7 mm X 6 mm) of the resilient materials (n= 8) were made without (control) or with incorporation of the MIC drugs. After storage in distilled water at 37°C for 24h, 7 and 14 days, the hardness tests were performed using a Shore A hardness tester (Woltest, GSD-709A) and the roughness assay was conducted in a surface roughness tester (Surftest SJ-301). Data were statistically analyzed by 3-way ANOVA followed by Tukeys test (=.05). According to the results, MICs of the drugs incorporated into the material were: 0.032, 0.256, 0.128, 0.256 e 0.064 g/mL for nystatin, miconazole, ketoconazole, itraconazole and chlorhexidine, respectively. The addition of the tested antimicrobial agents in both materials demonstrated no evident hardness change or resulted in its decrease compared to the control, except for miconazole incorporation into Softone, which increased the hardness values after 14 days (P = .0035). The addition of nystatin into the two materials, chlorhexidine into Trusoft and ketoconazole into Softone resulted in no significant changes of roughness values compared to the control after 7 and 14 days (P>.05). In these periods, itraconazole promoted increase of the roughness for both materials (P<.0001). Compare to the 24- h period, the roughness at 14- day time with the addition of nystatin, miconazole and ketoconazole was reduced for Trusoft (P<.05) and remained unaffected for Softone (P> .05). It can be concluded that the incorporation of antimicrobial agents inhibited the C. albicans growth on the materials up to 14 days. The addition of all tested drugs, except for the miconazole into Softone, resulted in no deleterious effects on hardness of the resilient materials over the evaluation time. At the end period, the incorporation of nystatin, miconazole and ketoconazole into both denture relines and chlorhexidine into Trusoft resulted in no detrimental changes on the roughness.

O objetivo deste estudo preliminar foi obter padrões metodológicos para viabilizar a utilização de um dispositivo acrílico intra-oral adaptável à mucosa palatina de ratos e passível de reembasamento com material resiliente temporário (Trusoft) modificado com antimicrobianos em suas mínimas concentrações inibitórias (MCIs) para biofilme de Candida albicans. Para delinear essa adequação, foram determinados parâmetros em relação à dieta e alojamento dos animais enquanto usuários desses dispositivos. A amostra total dos ratos (n=115) foi dividida em seis grupos: Controle Negativo (CN): sem dispositivo acrílico intra-oral; Controle Geral (CG): dispositivo acrílico sem reembasamento; Controle Positivo (CP): dispositivo reembasado com Trusoft sem fármaco; Diacetato de Clorexidina (CLO): dispositivo reembasado com Trusoft contendo clorexidina (0,064 g/mL); Cetoconazol (CET): dispositivo reembasado com Trusoft contendo cetoconazol (0,128 g/mL) e Nistatina (NIS): dispositivo reembasado com Trusoft contendo nistatina (0,032 g/mL). Os animais foram eutanasiados após 7 ou 14 dias da instalação dos dispositivos intraorais. As adaptações para a obtenção dos dispositivos incluíram a técnica de moldagem, método de reembasamento e formas de retenção à mucosa palatina dos animais. Para proporcionar a análise histopatológica descritiva padronizada, foram estabelecidos critérios em relação à obtenção das amostras histológicas, à seleção da região de interesse (RI) da análise e aos determinantes utilizados na descrição. Foi observado que a dieta pastosa e o alojamento em gaiolas com piso aramado sobre base de maravalha e papel craft possibilitaram melhores condições de sobrevivência aos animais. Os dispositivos intra-orais confeccionados individualmente e retidos via amarrilhos com fios ortodônticos nos incisivos e molares se mantiveram satisfatoriamente em posição durante todo o experimento para a maioria dos animais (72,6%), sobretudo no período inicial de 7 dias. O procedimento para o reembasamento dos dispositivos foi considerado apropriado em ambos os períodos testados. Houve perda de alguns animais por desnutrição (9,5%) ou durante a anestesia (4,1%). As amostras histológicas obtidas da mucosa palatina (tecido mole) foram descartadas por serem adequadas para a determinação da RI, sendo utilizadas apenas aquelas provenientes de tecidos mole e duro (n=12). A RI mais satisfatória para análise histopatológica correspondeu à área entre os primeiros molares, de um feixe neurovascular ao outro. A simples comparação visual das fotomicrografias obtidas na análise histopatológica descritiva sugeriu a ausência de infiltrado inflamatório em todos os grupos testados para ambos os períodos de avaliação. Após 7 dias, a espessura da camada córnea, estratificação das camadas do epitélio e disposição das fibras colágenas, dos vasos e das células da lâmina própria dos grupos de estudo se apresentaram similares ao observado para o grupo CN, havendo sinais de reabsorção óssea palatina apenas no grupo CG. Aos 14 dias, foi observado aumento da espessura de ortoqueratina e compressão das células epiteliais e do tecido conjuntivo da lâmina própria de todos os grupos em relação ao CN. Neste período, a reabsorção óssea palatina foi presente em todos os grupos, exceto CN e CP, com maior intensidade no grupo CG. Foi possível sugerir que os dispositivos acrílicos intra-orais podem ser considerados funcionais e viáveis para os testes de materiais para base de próteses e avaliação de tratamento para estomatite protética em ratos, sobretudo em períodos de até 7 dias. / The purpose of this study was to produce preliminary methodological standards to allow the use of an intraoral acrylic device adjusted to the palatal mucosa of rats and capable of relining with temporary resilient material (Trusoft) modified with antimicrobial agents in the minimum inhibitory concentrations (MICs) for Candida albicans biofilm. To design this adjustment, parameters were determined in relation to the diet and housing of animals as users of these devices. The total sample (n=115) was divided into six groups: Negative control (NC): without an acrylic intraoral device; Overall Control (OC): device without relining; Positive Control (PC): device relined with Trusoft without the addition of drugs; Chlorhexidine diacetate (CHL): device relined with Trusoft containing chlorhexidine diacetate (0.064 g/mL); Ketoconazole (KET): device relined with Trusoft containing ketoconazole (0.128g/mL); and Nystatin (NYT): acrylic device relined with Trusoft containing nystatin (0.032 g/mL). The animals were sacrificed after 7 or 14 days from the installation ofthe intra-oral devices. The adaptations for obtaining the devices included the impression technique, the reline method and the means of retaining in the palatal mucosa of animals. To obtain the standard descriptive histopathological analysis, criteria had been established in relation to obtaining the histological samples,selecting the region of interest (RI) of analysis and the criteria utilized in the description. It was observed that a paste diet and housing in cages with a wired fence floor with an additional base of wood shavings and craft paper enabled the best possible survival conditions for the animals. The individually made intra-oral devices retained with stainless steel wires at the incisors and molars remained satisfactorily in position throughout the experiment for most animals (72.6%), mainly in the initial period of 7 days. The procedure for the relining of the devices was deemed appropriate for both test periods. Some animals were lost from malnutrition (9.5%) or failure to recover from the anaesthetic (4.1%). The obtained histological samples of the palatine mucosa (soft tissue) were discarded as inappropriate for the determination of the RI, having utilized only those derived from hard and soft tissues (n = 12). The RI most satisfactory for the histopathological analysis corresponded to the area between the first molars from a palatal neurovascular bundle. A simple visual comparison of the photomicrographs obtained from the descriptive histopathological analysis suggested the absence of an inflammatory infiltrate in all the groups tested for both periods. After 7 days, the thickness of the keratin, the layers of the stratified epithelium and arrangement of the collagen fibers, cells and vessels of the lamina from the mucosa of the study groups presented similar findings to those observed for the NC group, having signals of palatine bone resorption only in the OC group. At 14 days, there was an increasing thickness of the keratin and compression of the epithelial cells and connective tissue of the lamina from the mucosa of all groups in relation to the NC group. In this period, the palatal bone resorption was present in all groups except the NC and PC groups, with a greater intensity in the OC group. It was possible to suggest that the intraoral acrylic devices may be considered as functional and viable for the testing of denture base materials and the evaluation of treatment for denture stomatitis in rats, especially in periods of up to 7 days.

Reembasadores resilientes temporários contendo fármacos antifúngicos foram sugeridos como um tratamento adjunto para estomatite protética. No entanto, antes de utilizar clinicamente estes reembasadores modificados em humanos, é importante avaliar a sua biocompatibilidade em modelos animais. Este estudo avaliou a biocompatibilidade in vivo de um reembasador resiliente temporário para base de prótese (Trusoft) modificado por agentes antimicrobianos em suas mínimas concentrações inibitórias (MCIs) para biofilme de Candida albicans. Dispositivos acrílicos intra-orais (DIOs) foram confeccionados individualmente para 60 ratos Wistar. Os ratos foram divididos em 6 grupos (n=5): 3 grupos controle (Negativo: sem DIO; Geral: DIO sem reembasamento; Positivo: DIO reembasado com Trusoft sem fármacos) e 3 grupos experimentais (DIOs reembasados com Trusoft modificados por fármacos em suas respectivas MCIs: 0,032 g de nistatina, 0,064 g de diacetato de clorexidina e 0,128 g de cetoconazol). Os ratos com ou sem os DIOs foram eutanasiados após 7 e 14 dias de avaliação. A análise histopatológica qualitativa foi realizada comparando-se fotomicrografias de secções histológicas, que foram obtidas utilizando um microscópio óptico que abrangeu transversalmente a região intermolares. As alterações morfológicas no epitélio e queratina foram analisadas quantitativamente através da realização de planimetria computadorizada. Os dados quantitativos foram analisados utilizando ANOVA 2-fatores e teste de Tukey (=0,05). A análise quantitativa mostrou que apenas o grupo com DIO contendo cetoconazol diminuiu significativamente a espessura e a área do estrato córneo em comparação com os outros grupos (p<0,05), que não apresentaram diferenças significativas entre si (p>0,05). Estes resultados estiveram de acordo com os obtidos para análise qualitativa. A incorporação de MCIs de nistatina e diacetato de clorexidina no Trusoft não induziram alterações histopatológicas na mucosa palatina de ratos, sugerindo a biocompatibilidade in vivo deste protocolo para o tratamento de estomatite protética. / Temporary resilient denture liners containing antifungal drugs have been suggested as an adjunct treatment for denture stomatitis. However, before clinically using these modified liners in humans, it is important to assess their biocompatibility in animal models. This study evaluated the in vivo biocompatibility of a temporary soft denture liner (Trusoft) modified by antimicrobial agents at their minimum inhibitory concentrations (MICs) for biofilm formation by Candida albicans. Methods: Acrylic intraoral devices (IODs) were individually made for 60 Wistar rats. The rats were divided into the following 6 groups (n=5): 3 control groups (Negative: without IOD; General: IOD without relining; Positive: IOD relined with Trusoft without drugs) and 3 experimental groups (IOD relined with Trusoft modified by drugs at MICs: 0.032 g for nystatin, 0.064 g for chlorhexidine diacetate, and 0.128 g for ketoconazole). The rats with or without the IODs were sacrificed after 7 or 14 days of evaluation. Histopathological qualitative analysis was performed by comparing photomicrographs of histological sections, which were obtained using an optical microscope that transversely covered the inter-molar region. Morphological changes in the epithelium and keratin were quantitatively analyzed by performing computerized planimetry. Quantitative data were analyzed using 2-way ANOVA and Tukey\'s test (=0.05). Quantitative analysis showed that only the group with IOD containing ketoconazole significantly decreased the thickness and area of the stratum corneum compared with the other groups (p<0.05), which showed no significant differences between each other (p>0.05). These results were in accordance with those obtained for qualitative analysis. Incorporation of MICs of nystatin and chlorhexidine diacetate in Trusoft did not induce histopathological changes in the palatal mucosa of rats, suggesting the in vivo biocompatibility of this protocol for treating denture stomatitis.

O objetivo do presente estudo foi avaliar o efeito da adição de mínimas concentrações inibitórias (MCIs) de agentes antimicrobianos para biofilme de Candida albicans na sorção de água e solubilidade de materiais resilientes temporários (Softone e Trusoft) para reembasamento de próteses removíveis. Os grupos de estudo (n=10) foram formados por corpos de prova circulares (50 mm x 0,5 mm) dos materiais sem (controle) ou com a incorporação das MCIs de três fármacos utilizados para tratamento de estomatite protética: nistatina (Ni)-0,032g/mL; diacetato de clorexidina (Cl)- 0,064g/mL; cetoconazol (Ce)- 0,128g/mL. Para determinar a sorção de água e solubilidade, as amostras foram dessecadas, imersas em água por 24 h, 7 ou 14 dias, pesadas, dessecadas e pesadas novamente. Os dados obtidos (&#x3BC;g/mm3) foram analisados por ANOVA 3 fatores e teste de Tukey (&#x3B1;=0,05). Comparado aos respectivos controles, a sorção de água dos dois materiais avaliados aumentou com a adição de nistatina e clorexidina após 24 h e 7 dias de imersão em água (P<0,0001). Após 14 dias de avaliação, exceto pela clorexidina (P<0,0001) no Softone (483,00 ± 61,00 &#x3BC;g/mm3), a sorção dos materiais não foi afetada (P>0,05) pela adição dos fármacos (Softone: Ni- 310,72 ± 55,00 &#x3BC;g/mm3; Ce- 202,13 ± 52,28 &#x3BC;g/mm3/ Trusoft: Ni- 320,26 ± 22,89 &#x3BC;g/mm3; Ce: 300,45 ± 69,49 &#x3BC;g/mm3; Cl: 331,01 ± 48,18 &#x3BC;g/mm3) em comparação aos respectivos controles (Softone: 244,00 ± 42,00 &#x3BC;g/mm3; Trusoft: 274,85 ± 83,12 &#x3BC;g/mm3). Para todos os grupos, o tempo de imersão aumentou (P<0,0001) a solubilidade do Softone (24h: 18,82 ± 9,80 &#x3BC;g/mm3; 7d: 32,16 ± 4,48 &#x3BC;g/mm3; 14d: 58,81 ± 8,79 &#x3BC;g/mm3), mas não do Trusoft (24h: 12,46 ± 4,51 &#x3BC;g/mm3; 7d: 14,34 ± 5,20 &#x3BC;g/mm3; 14d: 15,48 ± 5,68 &#x3BC;g/mm3) (P>0,05). Em relação aos controles e para todos os períodos, a solubilidade dos dois materiais foi alterada com clorexidina e cetoconazol (P<0,0001), mas não sofreu influência da nistatina (P>0,05). Foi possível concluir após 14 dias de imersão em água, a adição das MCIs de nistatina e cetoconazol nos dois materiais resilientes e de clorexidina no Trusoft não interferiu com a sorção de água. A solubilidade dos dois materiais temporários testados não foi alterada pela nistatina em até 14 dias de avaliação. / The objective of the present study was to evaluate the addition of minimum inhibitory concentrations (MICs) of antimicrobial agents for C. albicans biofilm on the water sorption and solubility of temporary resilient materials (Softone e Trusoft) for denture base relining. Test groups (n=10) were formed by disc specimens (50 mm x 0.5 mm) of the materials without (control) or with incorporation of the MICs of three drugs for denture stomatitis\' treatment: nystatin (Nt)- 0.032g/mL; chlorhexidine diacetate (Cl)- 0.064g/mL; ketoconazole (Kt)- 0.128g/mL. To determine the water sorption and solubility, samples were dried, immersed in water for 24 h, 7 or 14 days, weighed, dried and weighed again. Data (&#x3BC;g/mm3) were analyzed by 3-way ANOVA and Tukeys test (&#x3B1;=.05). Compared to the respective controls, the water sorption of the two materials evaluated increased with the addition of nystatin and ketoconazole after 24 h and 7 days of water immersion (P<.0001). After 14 days of evaluation, except by chlorhexidine (P<.0001) in Softone (483.00 ± 61.00 &#x3BC;g/mm3), the sorption of the materials was not affected (P>.05) by the addition of the drugs (Softone: Nt- 310.72 ± 55.00 &#x3BC;g/mm3; Kt- 202.13 ± 52.28 &#x3BC;g/mm3 / Trusoft: Nt- 320.26 ± 22.89 &#x3BC;g/mm3; Kt: 300.45 ± 69.49 &#x3BC;g/mm3; Cl: 300.45 ± 69.49 &#x3BC;g/mm3) compared to the respective controls (Softone: 244.00 ± 42.00 &#x3BC;g/mm3; Trusoft: 274.85 ± 83.12 &#x3BC;g/mm3). For all groups, the immersion time increased (P<.0001) the solubility of Softone (24h: 18.82 ± 9.80 &#x3BC;g/mm3; 7d: 32.16 ± 4.48 &#x3BC;g/mm3; 14d: 58.81 ± 8.79 &#x3BC;g/mm3), but not of Trusoft (24h: 12.46 ± 4.51 &#x3BC;g/mm3; 7d: 14.34 ± 5.20 &#x3BC;g/mm3; 14d: 15.48 ± 5.68 &#x3BC;g/mm3) (P>.05). In comparison to the controls, and for all periods the solubility of the both materials was affected with chlorhexidine and ketoconazole (P<.0001), but not was influenced by nystatin (P>.05). It can be concluded that after 14 days of water immersion the addition of MICs of nystatin and ketoconazole in the both resilient materials and chlorhexidine in the Trusoft did not affect the water sorption. The solubility of the two temporary materials tested was not altered by nystatin up to 14 days.

Made available in DSpace on 2014-06-11T19:28:58Z (GMT). No. of bitstreams: 0 Previous issue date: 2009-04-13Bitstream added on 2014-06-13T20:18:39Z : No. of bitstreams: 1 ribeiro_pp_me_araca.pdf: 1296460 bytes, checksum: 0aa88d770aee2b3e8787125e444deac4 (MD5) / O câncer da região de cabeça e pescoço é uma doença muito prevalente no Brasil, e as principais formas de tratamento são a cirurgia acompanhada ou não da radioterapia e quimioterapia. Perdas parciais ou totais de osso maxilar podem comprometer seriamente a fisiologia bucal causando sequelas como comunicações buconasosinosal. Neste caso, podese optar como forma de tratamento pela reabilitação protética com a aplicação de implantes osseointegrados. A literatura odontológica tem mostrado inúmeros trabalhos que avaliam a distribuição de forças com a finalidade de recolher melhores subsídios para o planejamento de próteses bucomaxilofaciais, que ainda é pouquíssimo explorada. Dentre os métodos utilizados, o da fotoelasticidade tem sido aceito, especialmente por permitir uma análise fiel da distribuição de forças. Assim, a proposta deste trabalho foi verificar a tendência de distribuição de forças e estresse, através do método fotoelástico, que incidem sobre diferentes tipos de sistemas de retenção em implantes (o’ring, barra clipe e o’ring/barra clipe) associado a próteses obturadoras palatinas implantoretidas e também em próteses obturadoras mucossuportadas (sem implante), utilizandose ou não de silicone com reembasamento direto (Sofreliner). O conjunto (prótese e modelo fotoelástico) foi posicionado em polariscópio circular e recebeu aplicação de carga de 100 N a velocidade de 10 mm/s no primeiro molar de cada prótese. Após as aplicações de carga houve a formação franjas correspondentes à tensão registrada. Então, as imagens foram transferidas para um computador e analisadas no programa ADOBE Photoshop. Ao se comparar os três sistemas de retenção das próteses obturadoras palatinas implantoretidas com a prótese mucossuportada (sem implantes), podese observar que as tensões foram distribuídas de forma mais homogênea... / The head and neck cancer is a very prevalent disease in Brazil and the main treatment is the surgery with or without radiation therapy and chemotherapy. Partial or total bone maxillary defects could involve seriously oral physiology causing consequences as buconasosinosal communications. In this case could be applied other option of treatment as prosthetic rehabilitation associated with osseointegrated implants. Scientific literature demonstrated countless studies that evaluate the force distribution with the aim to provide better subsidies for the planning of bucomaxillofacial prostheses, which still have few researches. Between the methodologies, the photoelastic method has been accepted; especially by allow an accurate analysis of the force distribution. Thus, the aim of this study was to verify the tendency of force distribution and the stress on different types of retention system (o’ring, clip bar and o’ring/clip bar) associated with palatal obturator prostheses with implant retention and conventional obturator prostheses (without implants), with or without silicone soft lining(Sofreliner), by means of photoelastic method. The set (prosthesis and photoelastic model) was located in circular polariscope and was applied a load of 100 load N at 10 mm/s on the first molar of each prostheses. After the load applications was registered the tension fringes. The images was transferred to a computer and analyzed at ADOBE Photoshop software. When compared the three retention systems of the palatal obturator prostheses and mucosupported prostheses (without implants), it can be observed that the stress was distributed more homogeneous and in lesser amount that the conventional prostheses, when compared to the other prostheses that presented implants and retention systems. With relation to stress distribution in the different retention systems, the bar clip... (Complete abstract click electronic access below)

Reembasadores resilientes temporários contendo fármacos antifúngicos foram sugeridos como um tratamento adjunto para estomatite protética. No entanto, antes de utilizar clinicamente estes reembasadores modificados em humanos, é importante avaliar a sua biocompatibilidade em modelos animais. Este estudo avaliou a biocompatibilidade in vivo de um reembasador resiliente temporário para base de prótese (Trusoft) modificado por agentes antimicrobianos em suas mínimas concentrações inibitórias (MCIs) para biofilme de Candida albicans. Dispositivos acrílicos intra-orais (DIOs) foram confeccionados individualmente para 60 ratos Wistar. Os ratos foram divididos em 6 grupos (n=5): 3 grupos controle (Negativo: sem DIO; Geral: DIO sem reembasamento; Positivo: DIO reembasado com Trusoft sem fármacos) e 3 grupos experimentais (DIOs reembasados com Trusoft modificados por fármacos em suas respectivas MCIs: 0,032 g de nistatina, 0,064 g de diacetato de clorexidina e 0,128 g de cetoconazol). Os ratos com ou sem os DIOs foram eutanasiados após 7 e 14 dias de avaliação. A análise histopatológica qualitativa foi realizada comparando-se fotomicrografias de secções histológicas, que foram obtidas utilizando um microscópio óptico que abrangeu transversalmente a região intermolares. As alterações morfológicas no epitélio e queratina foram analisadas quantitativamente através da realização de planimetria computadorizada. Os dados quantitativos foram analisados utilizando ANOVA 2-fatores e teste de Tukey (=0,05). A análise quantitativa mostrou que apenas o grupo com DIO contendo cetoconazol diminuiu significativamente a espessura e a área do estrato córneo em comparação com os outros grupos (p<0,05), que não apresentaram diferenças significativas entre si (p>0,05). Estes resultados estiveram de acordo com os obtidos para análise qualitativa. A incorporação de MCIs de nistatina e diacetato de clorexidina no Trusoft não induziram alterações histopatológicas na mucosa palatina de ratos, sugerindo a biocompatibilidade in vivo deste protocolo para o tratamento de estomatite protética. / Temporary resilient denture liners containing antifungal drugs have been suggested as an adjunct treatment for denture stomatitis. However, before clinically using these modified liners in humans, it is important to assess their biocompatibility in animal models. This study evaluated the in vivo biocompatibility of a temporary soft denture liner (Trusoft) modified by antimicrobial agents at their minimum inhibitory concentrations (MICs) for biofilm formation by Candida albicans. Methods: Acrylic intraoral devices (IODs) were individually made for 60 Wistar rats. The rats were divided into the following 6 groups (n=5): 3 control groups (Negative: without IOD; General: IOD without relining; Positive: IOD relined with Trusoft without drugs) and 3 experimental groups (IOD relined with Trusoft modified by drugs at MICs: 0.032 g for nystatin, 0.064 g for chlorhexidine diacetate, and 0.128 g for ketoconazole). The rats with or without the IODs were sacrificed after 7 or 14 days of evaluation. Histopathological qualitative analysis was performed by comparing photomicrographs of histological sections, which were obtained using an optical microscope that transversely covered the inter-molar region. Morphological changes in the epithelium and keratin were quantitatively analyzed by performing computerized planimetry. Quantitative data were analyzed using 2-way ANOVA and Tukey\'s test (=0.05). Quantitative analysis showed that only the group with IOD containing ketoconazole significantly decreased the thickness and area of the stratum corneum compared with the other groups (p<0.05), which showed no significant differences between each other (p>0.05). These results were in accordance with those obtained for qualitative analysis. Incorporation of MICs of nystatin and chlorhexidine diacetate in Trusoft did not induce histopathological changes in the palatal mucosa of rats, suggesting the in vivo biocompatibility of this protocol for treating denture stomatitis.