No description available.

No description available.

In marine environments and where de-icing salts are applied, the degradation of reinforced concrete structures due to chloride induced corrosion of the reinforcement is a major problem. The expansive nature of the corrosion process results in cracking of the concrete and eventually spalling. In order to select suitable remedial measures it is necessary to make an assessment of the residual strength and the residual life. In order to investigate the effect of corrosion on bond strength of the reinforcement, specimens comprising square prismatic sections containing steel reinforcement in the four corners have been subjected to a wet-dry cycle and corrosion has been accelerated by polarising the bars. The research has studied the change of bond strength with level of corrosion for 12 mm and 16 mm bars with concrete cover of 1 and 3 times the bar size. The bond strength is assessed by means of pull out tests and the corresponding extent of corrosion has been assessed in terms of the mass loss. Observations and measurements of the form of the corrosion (pit dimensions and loss of bar diameter) are also presented. The relationship between bond strength and surface crack width has been investigated. Results show that the surface crack width may be a good indicator of residual bond strength. In addition, the influence on bond strength of concrete compressive strength, reinforcement cover, bar position and bar size on the change of bond strength has been explored. It should be noted that all conclusions drawn in this project are based on tests on specimens without shear reinforcement (unconfined) and that accelerated corrosion (by impressed current) has been adopted. Consequently, care should be exercised in applying these results directly to structures in the field. Additional research is needed to assess the influence of impressed current on crack patterns and the effect of shear reinforcement.

No description available.

No description available.

<p>Bridge deck deterioration due to chloride-induced pitting corrosion of steel reinforcement is a common occurrence. Because rust decreases the cross-sectional area of reinforcing bars, corrosion of bridge deck reinforcement directly reduces the structural capacity of the bridge deck. A typical NDT method for assessing the possibility of corrosion at the top reinforcement level is ground-penetrating radar (GPR). The goal of the study is to investigate the effect of reducing the cross-sectional area of the reinforcing bar on deck strength due to corrosion. Flexural and shear failure were considered in the analysis. In conclusion, typical corrosion of reinforcement was not found to cause a bridge deck to collapse after testing the flexure with the yield line method, the one-way and two-way shears with AASHTO LRFD Bridge Design Specifications (2020), and the one-way shear with ACI 318 (2019). </p>

This thesis reports on the research outcome of corrosion mechanism and corrosion rate of mild steel in different environments (saline, alkaline solutions and concrete media) using potentiodynamic polarization technique. The study also included the effect of corrosion on bond strength between reinforcing steel and concrete using pull-out test. Corrosion of mild steel and 316L stainless steel with different surface conditions in 1, 3 and 5% saline (NaCl + Distilled water) was investigated. Specimens ground with 200 and 600 grit silicon carbide grinding paper as well as 1μm surface finish (polished with 1μm diamond paste) were tested. In case of mild steel specimens, reduction in surface roughness caused increase in corrosion rate, while in 316L stainless steel corrosion rate decreased as the surface roughness improved. Metallographic examination of corroded specimens confirmed breakdown of passive region due to pitting corrosion. Corrosion of mild steel was also investigated in alkaline solution (saturated calcium hydroxide, pH =12.5) contaminated with 1, 3 and 5% saline. A series of corrosion experiments were also conducted to examine the efficiency of various concentrations of calcium nitrite (CN) on corrosion behaviour of both as-received and polished mild steel in alkaline solution containing 3% saline after 1 hour and 28 days of exposure. Corrosion rate was higher for the as-received than polished mild steel surface under the same testing conditions in NaCl alkaline solution with and without nitrites due to the effect of surface roughness. Morphology investigation of mild steel specimens in alkaline solution ii containing chlorides and nitrites showed localized pits even at nitrite concentration equal to chloride concentration. Corrosion of steel bars embedded in concrete having compressive strengths of 20, 30 and 46MPa was also investigated. The effect of 2 and 4% CN by weight of cement on corrosion behaviour of steel bar in low and high concrete strengths specimens were also studied. All reinforced concrete specimens were immersed in 3% saline solution for three different periods of 1, 7 and 15 days. In order to accelerate the chemical reactions, an external current of 0.4A was applied. Corrosion rate was measured by retrieving electrochemical information from polarization tests. Pull-out tests of reinforced concrete specimens were then conducted to assess the corroded steel/concrete bond characteristics. Experimental results showed that corrosion rate of steel bars and bond strength were dependent on concrete strength, amount of CN and acceleration corrosion period. As concrete strength increased from 20 to 46MPa, corrosion rate of embedded steel decreased. First day of corrosion acceleration showed a slight increase in steel/concrete bond strength, whereas severe corrosion due to 7 and 15 days corrosion acceleration significantly reduced steel/concrete bond strength. Addition of only 2% CN did not give corrosion protection for steel reinforcement in concrete with 20MPa strength at long time of exposure. However, the combination of good quality concrete and addition of CN appear to be a desirable approach to reduce the effect of chloride induced corrosion of steel reinforcement. At less time of exposure, specimens without CN showed higher bond strength in both concrete mixes than those with CN. After 7 days of corrosion acceleration, the higher concentration of CN gave higher bond strength in both concrete mixes. The same trend was observed at 15 days of corrosion acceleration except for the specimen with 20MPa compressive strength and 2% CN which recorded the highest deterioration in bond strength.

Deterioration of concrete structures due to the corrosion of embedded steel is a well-known universal problem. Norway with its numerous bridges, ports, offshore and floating structures along its coastline, is also encountered with corrosion degradation. The harsh environment of the Norwegian Sea regarding its low temperature, wind, and waves, makes the design and construction of marine structures more demanding. In recent years, usage of sustainable composite materials in the field of structural engineering has been rising. The usage of natural fibre reinforced polymer materials in the form of reinforcement bars or macro fibres with a low density, high strength, and excellent corrosion resistance, gives us better choices for the design and construction of marine structures. Our knowledge about the fibre reinforced self-compacting concrete has increased as a result of introducing it as a building material some decades ago. However, more research is still needed when it comes to the application of new types of fibres. This thesis is a result of this need, whereby the author has done two series of experimental programmes regarding the subject. In the first series, the flow characteristics of fresh state, conventional and self-compacting macro basalt fibre concrete were studied. In the second series, mechanical properties of high performance and medium strength macro basalt fibre concrete including the post-cracking behaviour, compressive strength and electrical resistivity were in focus. The findings were presented in three appended papers and the extended summary composing this thesis. Additionally, the thesis presents an overview of the design procedure of floating concrete structures and the possibility of using macro basalt fibre concrete via a case study. The author’s literature review shows that basalt fibres have an adequate resistance against alkali environment of the concrete matrix and corrosive environment of seawater. / <p>QC 20160607</p>

The purpose of this study was to extract galvanized steel wire reinforcement coupons from mechanically stabilized earth (MSE) walls along I-15 and determine the rate of corrosion that has taken place since Phase I, which was conducted by Gerber and Billings (2010). The galvanized steel reinforcement analyzed in this study has been in place for 19 to 20 years at the time of extraction. A total of 85 coupons were extracted and laboratory analysis was performed to determine the thickness of remaining zinc galvanization on each coupon. Soil samples were obtained from each one-stage wall extraction location to determine moisture content for correlation with corrosion. After laboratory testing was performed, the measured zinc coating thickness was compared to that determined in Phase I. An average corrosion rate of approximately 0.032 oz/ft²/year has occurred since Phase I. According to the AASHTO (2017) design corrosion rate of 0.35 oz/ft²/year for the first two years and 0.09 oz/ft²/year until the depletion of the zinc, the zinc coating would have been completely depleted after 16 years. Based on the results of laboratory testing, the initial galvanization coating was likely greater than the specified thickness of 2.0 oz/ft² (86 μm). The zinc galvanization is corroding at a slower rate than the AASHTO design rate. The AASHTO design rate for depletion of zinc coating and subsequent corrosion of the steel reinforcement is conservative for the corrosion conditions present in the MSE wall reinforcement coupons tested. The integrity of the steel reinforcement that is currently in place is not likely to be compromised by corrosion.

This thesis reports on the research outcome of corrosion mechanism and corrosion rate of mild steel in different environments (saline, alkaline solutions and concrete media) using potentiodynamic polarization technique. The study also included the effect of corrosion on bond strength between reinforcing steel and concrete using pull-out test. Corrosion of mild steel and 316L stainless steel with different surface conditions in 1, 3 and 5% saline (NaCl + Distilled water) was investigated. Specimens ground with 200 and 600 grit silicon carbide grinding paper as well as 1¿m surface finish (polished with 1¿m diamond paste) were tested. In case of mild steel specimens, reduction in surface roughness caused increase in corrosion rate, while in 316L stainless steel corrosion rate decreased as the surface roughness improved. Metallographic examination of corroded specimens confirmed breakdown of passive region due to pitting corrosion. Corrosion of mild steel was also investigated in alkaline solution (saturated calcium hydroxide, pH =12.5) contaminated with 1, 3 and 5% saline. A series of corrosion experiments were also conducted to examine the efficiency of various concentrations of calcium nitrite (CN) on corrosion behaviour of both as-received and polished mild steel in alkaline solution containing 3% saline after 1 hour and 28 days of exposure. Corrosion rate was higher for the as-received than polished mild steel surface under the same testing conditions in NaCl alkaline solution with and without nitrites due to the effect of surface roughness. Morphology investigation of mild steel specimens in alkaline solution ii containing chlorides and nitrites showed localized pits even at nitrite concentration equal to chloride concentration. Corrosion of steel bars embedded in concrete having compressive strengths of 20, 30 and 46MPa was also investigated. The effect of 2 and 4% CN by weight of cement on corrosion behaviour of steel bar in low and high concrete strengths specimens were also studied. All reinforced concrete specimens were immersed in 3% saline solution for three different periods of 1, 7 and 15 days. In order to accelerate the chemical reactions, an external current of 0.4A was applied. Corrosion rate was measured by retrieving electrochemical information from polarization tests. Pull-out tests of reinforced concrete specimens were then conducted to assess the corroded steel/concrete bond characteristics. Experimental results showed that corrosion rate of steel bars and bond strength were dependent on concrete strength, amount of CN and acceleration corrosion period. As concrete strength increased from 20 to 46MPa, corrosion rate of embedded steel decreased. First day of corrosion acceleration showed a slight increase in steel/concrete bond strength, whereas severe corrosion due to 7 and 15 days corrosion acceleration significantly reduced steel/concrete bond strength. Addition of only 2% CN did not give corrosion protection for steel reinforcement in concrete with 20MPa strength at long time of exposure. However, the combination of good quality concrete and addition of CN appear to be a desirable approach to reduce the effect of chloride induced corrosion of steel reinforcement. At less time of exposure, specimens without CN showed higher bond strength in both concrete mixes than those with CN. After 7 days of corrosion acceleration, the higher concentration of CN gave higher bond strength in both concrete mixes. The same trend was observed at 15 days of corrosion acceleration except for the specimen with 20MPa compressive strength and 2% CN which recorded the highest deterioration in bond strength.