Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Recently, a new category of adhesive systems has been proposed to perform restorative procedures. These adhesives, named as universal have been released in the market with the purpose to decrease the technique sensitivity, likewise they offer a great versatility in the procedure as can be applied to tooth structures in both application modes. The objective of this dissertation is to present two papers. The first article aimed to compare the bond strength of a universal adhesive (Scotchbond Universal Adhesive) applied in both application modes to its controls, Adper Single Bond 2 and Clearfil SE Bond, when bonded to caries-affected primary and permanent dentin. The second article compared the bond strength of the Scotchbond Universal Adhesive in both application modes to the same controls aforementioned to caries-affected and sound permanent dentin. Forty-eight permanent teeth and twenty-four primary teeth were selected to perform the experiments in both papers. All teeth had their mid-coronal dentin surfaces exposed by removing the occlusal third. The dentin surfaces, which represent caries-affected dentin substrate, were submitted to pHcycling. The other teeth, sound dentin, remained intact until the bonding procedure. Specimens were randomly allocated (n=6) according to the adhesives tested and conditions of the dentin. After bonding procedures, a composite core was build-up to a height of 4-5mm and then was sectioned perpendicular to the adhesive interface in order to obtain rectangular sticks (0.8 mm2) that were submitted to microtensile tests (1mm/min). Two-way Analysis of Variance and post-hoc Tukey´s test (α = 0.05) were performed as statistical analysis. In the first paper, the universal adhesive, Scotchbond Universal Adhesive, presented statistically similar bond strength values to its controls in both dentin substrates, likewise the different substrates did not differ in bond strength values. In the second paper, adhesives bonded to sound dentin presented higher bond strength values compared with caries-affected dentin, but none of the adhesives tested presented statistically significant differences. The new universal adhesive, Scotchbond Universal Adhesive, can be applied in both application modes without the concern of compromise the bonding performance on resin composite restorations. / Recentemente, uma nova categoria de sistemas adesivos foi proposta para a realização de procedimentos restauradores. Estes sistemas adesivos, intitulados universais , se propõem a diminuir a sensibilidade da técnica operatória, assim como aumentar a versatilidade na escolha do modo de aplicação a ser empregado sobre as estruturas dentárias. O objetivo deste trabalho foi apresentar dois artigos para avaliar o comportamento destes sistemas adesivos universais. O primeiro artigo se propõe a avaliar o sistema adesivo universal (Single Bond Universal) aplicado nas duas estratégias de condicionamento à dentina desmineralizada de dentes decíduos e permanentes, em termos de resistência de união e comparar a dois sistemas de referência, Adper Single Bond 2 e Clearfil SE Bond. O segundo artigo comparou a resistência de união do Single Bond Universal em ambas estratégias de condicionamento aos mesmos sistemas adesivos de controle, porém à dentina desmineralizada e hígida de dentes permanentes. Quarenta e oito dentes permanentes e vinte e quatro dentes decíduos foram selecionados para realização de ambos estudos. Todos os dentes tiveram suas porções coronárias seccionadas para obtenção de superfícies planas em dentina (corpos de prova). A superfície dentinária dos dentes os quais representavam o substrato desmineralizado foram submetidas ao desenvolvimento de lesão de cárie por ciclagem de pH. Os demais dentes que representavam o substrato hígido foram mantidos intactos até os procedimentos adesivos. Os corpos de prova, de acordo com o tipo de dente, foram alocados aleatoriamente em grupos (n=6) de acordo com o sistema adesivo/ estratégia de condicionamento. Após os procedimentos adesivos, blocos de resina composta foram confeccionados e os corpos de prova seccionados perpendicularmente a interface adesiva para obtenção de espécimes com área de seção de aproximadamente 0,8mm2. Os espécimes foram submetidos ao ensaio de microtração (1mm/min). Os valores de resistência de união foram submetidos à análise de variância de dois-fatores (tipo de dente e sistema adesivo/ estratégia) (α = 0,05). No primeiro artigo, o sistema adesivo Single Bond Universal, em ambas estratégias de condicionamento, apresentou valores de resistência de união similares aos controles em ambos os substratos dentinários, assim como os diferentes substratos não apresentaram diferenças entre si. No segundo artigo, os valores de resistência de união à dentina hígida foram maiores comparados a dentina desmineralizada, porém nenhum sistema adesivo apresentou diferenças entre si. O sistema adesivo Single Bond Universal pode ser utilizado em ambas estratégias de condicionamento sem comprometer os procedimentos adesivos.

As lesões cervicais não cariosas (LCNCs) são definidas pela perda de estrutura dental na junção cemento/esmalte que envolve três mecanismos de estresse mecânico (tensão), atrito (fricção) e erosão (degradação química).. Existem tratamentos preventivos e dessensibilizantes para o principal sintoma das LCNCs, a hipersensibilidade dentinária cervical (HDC), porém, em casos que há perda de estrutura dental maior que 1mm é necessário realizar uma intervenção restauradora. Dessa forma, o objetivo deste estudo foi avaliar a resistência de união da dentina erodida e abrasionada modificada com diferentes pré-tratamentos e posteriormente restauradas com resina composta, através do teste de microtração. Para tanto, foram selecionados 40 molares humanos íntegros, que tiveram as porções oclusais seccionadas até exposição da dentina. Os espécimes passaram por desafio erosivo e abrasivo em uma ciclagem de 5 dias. Após os desafios, os espécimes receberam os tratamentos de superfície (n=10): G1: controle sem tratamento; G2: tratamento de superfície com ponta diamantada; G3: jateamento com óxido de alumínio, G4: ciclagem com enxaguatório fluoretado Elmex Erosion. Feito isso os espécimes foram restaurados, seccionados em palitos e submetidos ao teste de microtração em uma máquina universal de ensaios a 0,5mm/min. Para a analise estatística, foi utilizado o teste paramétrico de análise de variância (ANOVA) um fator e o teste auxiliar de Tukey. Foi observado que não houve diferença entre os tratamentos com ponta diamantada, óxido de alumínio e enxaguatório fluoretado. O único grupo a se diferenciar dos demais foi o grupo controle que apresentou valores de resistência de união inferiores. Dentro das limitações de um trabalho in vitro, conclui-se que os tratamentos de superfície estudados são procedimentos indicados para melhorar a adesão dental frente à necessidade de restaurar uma LCNC. / Non-carious cervical lesions (NCCLs) are defined by loss of dental structure at the cement/enamel junction involving three mechanisms of mechanical stress (tension), friction and erosion (chemical degradation). There are preventive and desensitizing treatments for the the main symptom of NCCLs, cervical dentin hypersensitivity (CDH), but in cases where there is loss of tooth structure greater than 1mm, a restorative intervention is necessary. Thus, the objective of this study was to evaluate the bond strength of the eroded and abraded dentin modified with different pre-treatments and later restored with composite resin, through the microtensile test. For this, 40 sound human molars were selected, which had the occlusal portions sectioned until exposure of the dentin. The specimens underwent erosive and abrasive challenge in a 5-day cycling. After the challenges, the specimens received the surface treatments (n = 10): G1: control without treatment; G2: surface treatment with diamond tip; G3: sandblasting with aluminum oxide, G4: cycling with fluoridated rinse Elmex Erosion. After this, the specimens were restored, sectioned on sticks and subjected to the microtensile test in a universal test machine at 0.5mm/min. For statistical analysis, the parametric analysis of variance (ANOVA) one factor and the Tukey auxiliary test were used. It was observed that there was no difference between treatments with diamond tip, aluminum oxide and fluoride. The only group to differentiate from the others was the control group that presented inferior bond strength values. Within the limitations of an in vitro work, it is concluded that the surface treatments studied are procedures indicated to improve dental adhesion in view of the need to restore NCCL.

Buscou-se minimizar ou prevenir a degradação das fibrilas colágenas, tanto no controle da progressão do desgaste erosivo em dentina, quanto na preservação das interfaces adesivas aí estabelecidas, por meio do uso de agentes antiproteolíticos (clorexidina/CHX e epigalocatequina-3-galato/EGCG) ou, ao mesmo tempo, promotores de ligações cruzadas entre elas (proantocianidina/PAC). O papel de algumas dessas estratégias no estabelecimento, e conservação, de interfaces adesivas em dentina erodida, substrato adverso à interação com materiais adesivos, tem sido, porém, pouquíssimas vezes reportado. Este estudo in vitro propôs-se a avaliar, pois, o efeito de tais agentes, usados como estratégias para prevenção/controle do desgaste, na resistência de união (RU) do conjunto sistema adesivo condicione e lave simplificado-resina composta à dentina erodida, comparada à normal. A dentina superficial oclusal de terceiros molares foi apenas submetida à ação de uma lixa de SiC (granulação 600; 1 min; N: substrato normal) ou sequencialmente a desafio erosivo inicial (Coca-Cola®; 5 min). Recebeu, então, ou não (C: controle/sem aplicação), a aplicação de um dos géis com os seguintes princípios ativos - P: placebo/sem princípio ativo; CHX: digluconato de clorexidina a 0,12%; EGCG: epigalocatequina-3-galato a 400 ?m; PAC: proantocianidina a 10%. Aquela de início desmineralizada ainda foi submetida a ciclagem de pH (Coca-Cola®; imersões de 5 min, 3x/dia, 5 dias; E: substrato erodido). Após condicionamento (H3PO4 a 37%; 15 s; lavagem 30 s; secagem com papel absorvente), o adesivo AdperTM Single Bond 2® foi aplicado em todos os espécimes e a porção coronária, reconstruída com a resina FiltekTM Z350®. Transcorridas 24 h (água destilada/37?C), os espécimes foram seccionados em palitos e testados (?TBS; 0,5 mm/min). As superfícies fraturadas de cada palito foram avaliadas utilizando-se um microscópio digital (50x de aumento). Os valores de RU obtidos foram organizados considerando- se cada dente como unidade experimental e os testes de Análise de Variância a 2 critérios e de Tukey aplicados (?=0,05). Um dente extra para cada grupo foi tratado exatamente como os outros, mas o corante fluorescente rodamina B foi previamente adicionado (0,16 mg/mL) ao sistema adesivo para permitir a avaliação qualitativa da interface adesiva por meio de Microscopia Confocal de Varredura a Laser. Analisando-se os dados obtidos pôde-se observar que, diferentemente da variável aplicação de géis para prevenção/controle do desgaste erosivo (p=0,076), a variável condição do substrato dentinário exerceu influência significante sobre os resultados (p<0,001). Ademais, não houve interação entre elas (p=0,979). Os valores imediatos de RU ao substrato erodido foram, pois, sempre inferiores que aqueles ao substrato normal, independentemente da aplicação, ou não, de qualquer um dos géis para prevenção/controle do desgaste erosivo. Quanto ao padrão de fratura dos palitos testados, as falhas adesivas e mistas foram predominantes em relação às coesivas, independentemente se em dentina ou em resina. Menores porcentagens de falhas coesivas ainda puderam ser verificadas para o substrato erodido, com relação ao normal. No que se refere à análise qualitativa, observou-se, para o erodido, comparado ao normal, independetemente do tratamento para controle do desgaste, camada escura subjacente à de adesivo propriamente, representação da menor concentração de material marcado por rodamina B, bem como tags resinosos com maior comprimento e em maior quantidade. Assim sendo, conclui-se, por ora, que as estratégias estudadas não foram capazes de favorecer, tampouco de prejudicar, o estabelecimento de interface adesiva em dentina erodida. / In order to minimize the degradation of collagen fibrils, both to control the progression of the dentin erosive wear and to preserve adhesive interfaces established there, antiproteolytic (chlorhexidine/CHX and epigallocatechin-3-gallate/EGCG) or, at the same time, collagen cross-linking agents (grape seed proanthocyanidin extract/PAC) started to be successfully used. Some of these strategies in the establishment and preservation of adhesive interfaces on eroded dentin, a substrate adverse to the interaction with adhesive materials, has been seldom reported yet. This in vitro study aimed to evaluate, thus, the effect of such agents, used as strategies for wear preventing/controlling, on bond strength (BS) of a simplified etch-and-rinse adhesive system adhesive plus a resin composite to eroded, and normal (parameter for comparisons) dentin. Superficial occlusal dentin of third molars was only ground with a SiC paper (600-grit; 1 min; N: normal substrate), or subsequently submitted to an initial erosive challenge (Coca-Cola®; 5 min). It, then, received or not (C: control/without application), application of one of the gels with the following active principles - P: placebo/without active principle; CHX: 0.012% chlorhexidine digluconate; EGCG: epigallocatechin-3-gallate at 400 ?m; PAC: 10% proanthocyanidin. Initial demineralized dentin was still submitted to a pH cycling (Coca-Cola®, 5 min immersions, 3x/day, 5 days, E: eroded substrate). After acid-etched (37% H3PO4; 15 sec; 30 sec washing; drying with absorbent paper), the adhesive Adper(TM) Single Bond 2® was applied in all specimens and resin composite buildups were constructed with Filtek(TM)Z350®. After 24 h (distilled water/37?C), specimens were sectioned in beams and tested (?TBS; 0.5 mm/min). Obtained BS values were organized considering each tooth as an experimental unit and two-way ANOVA and Tukey tests were applied (?=0.05). An extra tooth for each group was treated just like the others, but the adhesive system was marked by the addition of rhodamine B (0.16 mg/mL) to allow qualitative evaluation of the adhesive interface by means of Confocal Laser Scanning Microscopy. As opposed to the variable application of gels for wear preventing/controlling (p=0.076), the condition of the dentin substrate had a significant influence on the results (p<0.001). In addition, there was no interaction between them (p=0.979). Immediate BS values to the eroded substrate were always lower than that to the normal substrate, regardless of the application or not of any of the gels for wear preventing/controlling. As for the fracture pattern of the tested beams, adhesive and mixed failures were predominant in relation to the cohesive failures, regardless of whether in dentin or in resin. Lower percentages of cohesive failures could still be verified for the eroded substrate, relative to the normal one. Concerning the qualitative analysis, it was observed, for the eroded substrate, compared to the normal, independently of the treatment for wear preventing/controlling, a dark layer underlying that of the adhesive itself, which represents a lower concentration of rhodamine B-labeled material, as well as resinous tags with greater length and in greater quantity. Therefore, studied strategies were not able either to improve, neither to impair, the establishment of adhesive interface on eroded dentin.

O estabelecimento de interfaces adesivas no substrato dentinário artificialmente erodido, conceitualmente pobre em minerais, revestido por matriz orgânica exposta, é pouco promissor. Por ora, tornam-no similar àquele verificado para a dentina normal/hígida apenas a asperização ou, quando do uso de adesivos universais, a desproteinização com hipoclorito de sódio. Manter a camada de fibrilas colágenas, por meio do uso de inibidores de proteinases, talvez mesmo que compactada por abrasão, pode, porém, ser conveniente, já que desempenha importante papel nos processos de des e remineralização, inclusive contendo a progressão do desgaste erosivo e erosivo-abrasivo, e no estabelecimento de uma camada híbrida propriamente dita. Avaliou-se, pois, de imediato, a resistência de união do conjunto sistema adesivo condicione e lave simplificado-resina composta à dentina, considerando-se como fatores experimentais a condição desse substrato, em três níveis (N: normal; E: erodido; EA: erodido-abrasionado), e a aplicação de um gel para prevenção/controle do desgaste erosivo em três níveis (C: controle/sem aplicação; P: placebo/sem princípio ativo; CHX: digluconato de clorexidina a 0,12%). Para determinação do substrato normal, a dentina superficial oclusal de terceiros molares foi apenas submetida à ação de uma lixa de SiC (#600; 1 min; N); para a do erodido e do erodidoabrasionado, sequencialmente, de pronto, a desafio erosivo inicial (Coca-Cola®; 5 min). Aplicou-se sobre ela, então, ou não (controle/sem aplicação), um dos géis: placebo/sem princípio ativo; ou à base de CHX a 0,12%. Aquela de início desmineralizada ainda foi submetida à ciclagem de pH (Coca-Cola®; imersões de 5 min, 3x/dia, 5 dias), determinando-se, fatidicamente, o substrato erodido (E), ou a ciclagem de pH associada a escovação (escova elétrica/dentifrício com flúor diluído em água, 2,5 N, 30 s, 2x/dia, após 1º e último desafios ácidos), determinando-se o substrato erodido-abrasionado (EA). Após condicionamento (H3PO4 a 37%; 15 s; lavagem 30 s; secagem com papel absorvente), o adesivo AdperTM Single Bond 2® foi aplicado em todos os espécimes e a porção coronária, reconstruída com a resina FiltekTM Z350®. Transcorridas 24 h (água destilada / 37?C), os espécimes foram seccionados em palitos e testados (?TBS; 0,5 mm/min). Os valores de RU obtidos foram organizados considerando-se cada dente como unidade experimental e os testes de Análise de Variância a 2 critérios e de Tukey, aplicados (?=0,05). Um dente extra para cada grupo foi tratado exatamente como os outros, mas o corante fluorescente rodamina B foi previamente adicionado (0,16 mg/mL) ao sistema adesivo para permitir a avaliação qualitativa da interface adesiva por meio de Microscopia Confocal de Varredura a Laser. Diferentemente da variável aplicação de géis para prevenção/controle do desgaste erosivo (p=0,359), a variável condição do substrato dentinário exerceu influência significante sobre os resultados (p<0,001). Ademais, não houve interação entre elas (p=0,856). Os valores imediatos de RU ao substrato erodido e ao erodido-abrasionado, equivalentes entre si, foram sempre inferiores àqueles ao substrato normal, independentemente da aplicação, ou não, do gel de CHX, ou placebo, para prevenção/controle do desgaste erosivo. No tocante ao padrão de fratura dos palitos testados, as falhas adesivas e mistas foram predominantes em relação às coesivas, independentemente se em dentina ou em resina. Quanto à análise qualitativa, nota-se que tags resinosos se manifestam em maior número e comprimento nos substratos submetidos a desafio erosivo inicial, ou seja, o erodido e o erodido-abrasionado, independentemente da aplicação de qualquer estratégia para controle da progressão do desgaste. Dentre eles, para o substrato erodido, há uma identificável camada escura subjacente à de adesivo propriamente dito, entre os tags resinosos, representação da menor concentração de material marcado por rodamina B. Para o substrato erodido-abrasionado, verifica-se camada híbrida devidamente expressa por anuviado vermelho subjacente à camada de adesivo, mais e menos espessa, respectivamente, que a estabelecida no substrato normal e erodido. Destarte, conclui-se que o gel de CHX não foi capaz de determinar, por meio da preservação/controle do desgaste erosivo, ou erosivo-abrasivo, substrato tão favorável à adesão com os materiais resinosos quanto o normal, mesmo que não o tenha desajudado ainda mais. / The establishment of adhesive interfaces on artificially eroded dentin substrate, conceptually poor in minerals, coated with an exposed organic matrix, is little promising. For the time being, only diamond bur surface roughening and deproteinization with sodium hypochlorite, when universal adhesives are used, make it similar to the obtained for normal/sound dentin. Maintaining the layer of collagen fibrils, using protease inhibitors, perhaps even when compressed by abrasion, may, however, be convenient, since it plays an important role in the demineralization and remineralization processes, including the erosive and erosive-abrasive wear progression, and in establishing a hybrid layer itself. The aim of this study was to evaluate, immediately, bond strength (BS) of an etch-and-rinse adhesive system plus a composite to dentin, considering the condition of its substrate in three levels (N: normal; E: eroded; EA: eroded-abraded), and the application of a gel for the prevention/control of the erosive wear in three levels (C: control / without application, P: placebo / without an active principle, and CHX: 0.12% chlorhexidine digluconate). To determine the normal substrate, occlusal dentin from third molars was subjected solely to the action of a SiC sandpaper (# 600; 1 min; N); to determine the eroded and eroded-abraded, it was sequentially, and readily, subjected to an initial erosive challenge (Coca-Cola®, 5 min). One of the gels were applied, or not (control / without application), on it: placebo / without active principle; or containing 0.12% CHX. The initial demineralized one was still submitted to a pH cycling (Coca-Cola®, immersions of 5 min, 3x /day, 5 days), determining the eroded substrate (E), or to the pH cycling associated to brushing (electric toothbrush/fluoride toothpaste diluted in water, 2.5 N, 30 s, 2x/day, after 1st and last acid challenges), determining the eroded-abraded substrate (EA). After acid-etching (37% H3PO4, 15 sec, 30 sec washing, drying with absorbent paper), Adper(TM) Single Bond 2® adhesive was applied to all specimens and resin composite buildups constructed with Filtek(TM)Z350®. After 24 h (distilled water / 37?C), specimens were sectioned in beams and tested (?TBS, 0.5 mm/min). BS values obtained were organized considering each tooth as an experimental unit and a twoway ANOVA and Tukey test, applied (?=0.05). An extra tooth for each group was treated exactly like the others, but rhodamine B fluorescent dye was previously added (0.16 mg / mL) to the adhesive system to allow qualitative evaluation of the adhesive interface by means of Confocal Laser Scanning Microscopy. Differently from the variable application of gels for prevention/control of erosive wear (p=0.359), the condition of the dentin substrate had a significant influence on the results (p<0.001). In addition, there was no interaction between them (p=0.856). Immediate BS values to eroded and eroded-abraded substrates, equivalent to each other, were always lower than that to the sound substrate, regardless of the application, or not, of the CHX or the placebo gel for prevention/control of erosive wear. Concerning the fracture pattern of the tested beams, adhesive and mixed failures were predominant in relation to the cohesive, regardless of whether in dentin or in resin composite. As for the qualitative analysis, it is noticed that resinous tags are manifested in greater number and length in the substrates submitted to erosive initial challenge, that is, eroded and erodedabraded substrates, regardless of the application of any strategy to control progression of wear. Among them, for the eroded substrate, there is an identifiable dark layer underlying that of the adhesive itself, among the resin tags, representing the lowest concentration of material marked by rhodamine B. For the eroded-abraded substrate, hybrid layer is duly expressed by a red blur underlying the layer of adhesive, more and less thick than that established in the normal and eroded substrates, respectively. Therefore, it is concluded that the CHX gel was not able to determine, while preserving/controlling the erosive or erosive-abrasive wear, a substrate as favorable to bonding with resinous materials as a sound one, even if it has not impaired it even more.

Este estudo longitudinal investigou a influência de tratamentos de superfície com o laser de Er:YAG com 50?s de largura de pulso sobre a adesão de dois sistemas adesivos autocondicionantes (SA) em dentina hígida (DH) e dentina afetada por cárie (DAC) através dos teste de resistência de união (RU) de microcisalhamento (?SBS), teste de ultramicrodureza da camada de adesivo (NdA) e da camada híbrida (NdCH), além de análise da interface adesiva com microscopia eletrônica de varredura (MEV). A análise qualitativa dos tratamentos de superfície realizados foi executada através de MEV e microscopia eletrônica de transmissão (MET). A dentina oclusal planificada de 215 molares humanos foi protegida com verniz ácido resistente, exceto em janela de 4x5mm para produção de DAC artificial após 7 dias de desafio cariogênico com biofilme de S. mutans, permitindo dados pareados por substrato. Os espécimes foram divididos nos grupos experimentais de acordo com: tratamento de superfície [controle-sem tratamento-(G1); Laser 80-80mJ, 2 Hz, 12.58J/cm2-(G2); Laser 50-50mJ, 10 Hz, 9.4J/cm2-(G3)]; sistema adesivo [Clearfil SE Bond(CF) e Single Bond Universal(SB)]; substrato [DH(h) ou DAC(a)] e tempo de armazenamento em saliva artificial [24 horas (24) ou 1 ano (1)], compondo 24 grupos experimentais: CFG1h24; CFG1h1; CFG1a24; CFG1a1; CFG2h24; CFG2h1; CFG2a24; CFG2a1; CFG3h24; CFG3h1; CFG3a24; CFG3a1; SBG1h24; SBG1h1; SBG1a24; SBG1a1; SBG2h24; SBG2h1; SBG2a24; SBG2a1; SBG3h24; SBG3h1; SBG3a24; SBG3a1. Nos grupos tratados com laser a largura temporal de pulso foi ajustada em 50?s. A resina composta Z350XT foi utilizada para a confecção dos corpos de prova. Os sistemas adesivos foram aplicados de acordo com as instruções do fabricante. As análises de MEV e MET de superfície avaliaram somente o efeito dos tratamentos em ambos os substratos testados. Os valores de RU e de nanodureza foram analisados através do teste de ANOVA (três fatores) e do teste de comparações múltiplas de Tukey (?=0,05). Para o teste de ?SBS, para ambos os SA, e todos tratamentos de superfície, a DAC apresentou valores de RU menores comparados à DH; a influência do armazenamento em saliva artificial foi substrato dependente: corpos de prova obtidos com DAC apresentaram queda nos valores de RU após 1 ano de armazenamento, enquanto nenhuma diferença entre os grupos experimentais foi observada em dentina hígida. NdA revelou que apenas os corpos de prova construídos com CF apresentaram redução dos valores após 1 ano. A NdCH obtida com CF e SB, resultou em menores valores em DAC comparada à DH, após 1 ano de armazenamento ambos os substratos apresentaram redução da NdCH, para todos tratamentos de superfície. A MEV revelou que todas as interfaces adesivas, especialmente aquelas obtidas em DAC, sofreram degradação intensa após 1 ano. Os tratamentos com Laser 80 e Laser 50 promovem alteração superficial característica de ablação em DAC e DH, conforme observado em MEV de superfície, e alterações de fibrilas colágenas observadas em MET. Independentemente dos SA, a adesão e nanodureza em DAC é menor que em DH. Todas as interfaces adesivas obtidas foram sensíveis ao armazenamento em saliva artificial por 1 ano. A adesão não foi influenciada pelo tratamento com o laser Er:YAG com 50?s de largura de pulso. / This longitudinal study investigated the influence of super short pulse Er:YAG laser treatment on microshear bond strength (?SBS), adhesive and hybrid layer nanohardness test and qualitative interface scanning electron microscopy (SEM) of two self-etch adhesive systems to sound (SD) and caries-affected like dentin (CAD). Additionally, qualitative investigation of surface treatments by SEM and transmission electron microscopy (TEM) were performed. CAD lesions (4x5mm) were produced by 7 days S. mutans biofilm cariogenic challenge in 215 human ground flat human dentin specimens, enabling paired data by substrate. Specimen were divided in groups according to surface treatment [control-no treatment-(G1); Laser 80-80mJ, 2Hz, 12.58J/cm2-(G2); Laser 50-50mJ, 10Hz, 9.4J/cm2-(G3)]; self-etching adhesive system [Clearfil SE Bond(CF) and Single Bond Universal(SB)]; substrate [SD(h) or CAD(a)] and artificial saliva storage [24 hours(24) or 1 year(1)]: CFG1h24; CFG1h1; CFG1a24; CFG1a1; CFG2h24; CFG2h1; CFG2a24; CFG2a1; CFG3h24; CFG3h1; CFG3a24; CFG3a1; SBG1h24; SBG1h1; SBG1a24; SBG1a1; SBG2h24; SBG2h1; SBG2a24; SBG2a1; SBG3h24; SBG3h1; SBG3a24; SBG3a1. Pulse duration was set in 50?s for laser groups. ?SBS, nanohardness and interface SEM specimen preparation was constructed with Z350XT composite resin. Adhesive systems were applied according to manufacturer\'s instructions. Surface SEM and TEM specimen only evaluated treatment effects on distinct substrates. The ?SBS and nanohardness means were analysed using three-way ANOVA and Tukey´s multiples comparisons test (?=0.05). For ?SBS test, for both adhesive systems, and all surface treatments, CAD revealed lower ?SBS values compared to SD; the influence of artificial saliva storage was substrate dependent. CAD specimens resulted in lower ?SBS values after 1 year, while no difference among experimental groups was observed in SD. The adhesive layer (AL) nanohardness statistical evaluation revealed that only CF specimens decreased the AL nanohardness after 1 year of storage. The hybrid layer (HL) produced with CF and SB, resulted in lower nanohardness values for CAD than SD, which reduces after 1 year storage, for all surface treatments. Interface SEM analysis revealed that all adhesive interfaces, especially those in CAD, have experienced degradation after 1 year of storage. Laser 80 and Laser 50 promotes surface ablation characteristics in CAD and SD, as noted in surface SEM and collagen fibrils alterations observed in TEM. Despite of adhesive systems, bonding and nanohardness to CAD is lower than to SD. All tested adhesive interfaces were sensitive to saliva storage. Surface treatment with 50?s Er:YAG laser did not influence on bonding.

Avanços na tecnologia introduziram o laser como um grande aliado na remoção seletiva do tecido cariado. Entretanto, o efeito dos lasers e seus diferentes parâmetros nos tecidos duros dentais e fibrilas colágenas não foi completamente estudado. O objetivo deste estudo foi avaliar os efeitos da irradiação com os lasers de Er:YAG e Er,Cr:YSGG na morfologia e na resistência de união da dentina irradiada à resina composta. Sessenta e quatro hemi-discos de dentina obtidos de terceiros molares humanos foram aleatoriamente divididos em 9 grupos (n=7): G1 Controle (não irradiado); G2 Laser de Er:YAG 250 mJ, 4 Hz; G3 Laser de Er:YAG 200 mJ, 4 Hz; G4 Laser de Er:YAG 180 mJ, 10 Hz; G5 Laser de Er:YAG 160 mJ, 10 Hz; G6 - Laser de Er,Cr:YSGG 2W, 20 Hz; G7 - Laser de Er,Cr:YSGG 2,5W, 20 Hz; G8 - Laser de Er,Cr:YSGG 3W, 20 Hz; G9 - Laser de Er,Cr:YSGG 4W, 20 Hz. Destes, vinte e sete amostras (n=3) foram processadas e destinadas à avaliação em Microscopia Eletrônica de Varredura (MEV) para análise morfológica de superfície e em corte transversal da dentina irradiada. Nove fragmentos (n=1) foram submetidos à Microscopia Eletrônica de Transmissão (MET) e vinte e sete (n=3) foram restaurados para análise da interface adesiva. Para o teste de resistência de união, 45 superfícies dentinárias planificadas foram restauradas e, após 24 horas de armazenamento em água, foram submetidas ao teste de microtração. O teste de ANOVA (=5%) foi realizado e verificou-se que o G1 apresentou os maiores valores de resistência de união quando comparado aos demais grupos experimentais. Não houve diferença estatisticamente significativa entre os grupos irradiados, e a análise morfológica revelou para estes grupos uma superfície irregular, com aparência escamosa, sem smear layer e com os túbulos dentinários abertos. Nos cortes transversais foi possível observar que esses efeitos se estendem à subsuperfície dentinária e resultam na formação de um padrão modificado dos tags durante o processo de hibridização. Os resultados deste estudo in vitro sugerem que a irradiação com os lasers de Er:YAG e Er,Cr:YSGG promovem um padrão morfológico específico da superfície dentinária, os quais podem interferir negativamente nos valores de resistência de união à resina composta. / Improvements on technology have introduced the laser as a great ally in the selected removal of dental caries. However, the different laser parameters and their effects on dental hard tissues and collagen fibrils have not yet been completely studied. The aim of the present study was to evaluate the effect of Er:YAG and Er,Cr:YSGG laser irradiation on dentin morphology and on microtensile bond strength of resin composite to the irradiated dentin. Sixty-four dentin hemi-disks obtained from sound human third molars were randomly divided into 9 groups (n=7): G1 Control, G2 Er:YAG Laser 250 mJ, 4 Hz; G3 Er:YAG Laser 200 mJ, 4 Hz; G4 Er:YAG Laser 180 mJ, 10 Hz; G5 Er:YAG Laser 160 mJ, 10 Hz; G6 - Er,Cr:YSGG Laser 2W, 20 Hz; G7 - Er,Cr:YSGG Laser 2,5W, 20 Hz; G8 - Er,Cr:YSGG Laser 3W, 20 Hz; G9 - Er,Cr:YSGG Laser 4W, 20 Hz. Twenty seven specimens (n=3) were processed for Scanning Electron Microscopy (SEM) for surface and cross-sectional morphological analysis. Nine specimens (n=1) were processed for Transmission Electron Microscopy (TEM) and twenty seven (n=3) were restored to evaluate the adhesive interface. For the microtensile bond strength (^TBS) test, 45 flat occlusal dentin surfaces were restored and after storage in water for 24h, were submitted to ^TBS test. ANOVA (=5%) showed that G1 (control group) presented the highest ^TBS values when compared with the irradiated groups, which did not differ from each other. SEM analysis showed an irregular scaly surface, free of smear layer and with open dentinal tubules. The cross-sectional dentin micrographs showed that the effects of laser extended to the dentin subsurface resulting in a pattern of tags modified in the hibridization process. The findings of this in vitro study showed that both Er:YAG and Er,Cr:YSGG laser irradiation resulted in a specific morphological pattern of dentin that negatively affects the bond strength to resin composite to such dentin.

Avaliou-se o selamento apical, os aspectos micromorfológicos da interface adesiva, as características físicas e a resistência de união à dentina de cimentos resinosos endodônticos. Setenta e dois pré-molares humanos unirradiculares foram preparados endodonticamente. Trinta e três dentes foram divididos aleatoriamente em 3 grupos, impermeabilizados externamente e obturados pela técnica da condensação lateral acorde as seguintes condições: AH Plus (AH Plus/Gutapercha); AH Primer (Epiphany primer/AH Plus/Gutapercha) e Epiphany (sistema Epiphany). Foram mantidos a 37oC e 100% de umidade por 72 h e, em seguida, imersos em solução aquosa de nitrato de prata a 50% por 24 h. Após secção longitudinal dos dentes, foram realizadas réplicas em resina epóxica. Réplicas e espécimes foram preparados para MEV. Nas réplicas, observou-se a freqüência de fendas apicais na interface dentina/cimento. Nos espécimes, detectou-se e confirmou-se com EDS (Energy Dispersive Spectroscopy) a microinfiltração apical. A interface dentina/cimento foi observada em seis espécimes de cada grupo, selecionados aleatoriamente. A microinfiltração foi similar entre os grupos (p>0,05), sendo influenciada pela freqüência de fendas (p<0,05). Foram observadas tanto regiões com fendas quanto com camada híbrida e longos tags para o grupo Epiphany. Para os grupos AH Primer e AH Plus foi verificada boa adaptação marginal com longos tags vazios e pequenos plugs, respectivamente, embora tenha ocorrido a formação de fendas em ambos. Os outros dentes foram utilizados para as avaliações adicionais: seis, para complementar o estudo micromorfológico da interface adesiva; três, para o ensaio de microdureza Knoop; e, trinta, para o teste de resistência de união. O cimento Epiphany mostrou maior escoamento (p<0,001) e tensão de polimerização (p<0,05), e a menor resistência de união (p<0,001). Os valores de microdureza Knoop decresceram acentuadamente de cervical para apical (p<0,001). Concluiu-se que a total impermeabilização do sistema de canais radiculares não foi obtida com nenhum dos cimentos testados, e que o sistema Epiphany formou mais fendas no ápice. / Resin-based root canal sealers had their apical sealing, micromorphological aspects, physical characteristics and bond strength to dentin evaluated in this study. For this purpose, seventy-two single-rooted human premolars were endodontically treated. Thirty-three teeth were randomly divided into three groups, externally coated with nail varnish and obturated by lateral condensation technique according to such conditions: AH Plus (AH Plus/Gutta-percha); AH Primer (Epiphany primer/AH Plus/ Gutta-percha) and Epiphany (Epiphany system). They were kept in 100% humidity at 37oC for 72 h, and then the specimens were immersed in 50% aqueous silver nitrate tracer solution for 24 h. The teeth were longitudinally sectioned and their epoxy resin replicas were obtained. Both the specimens and their corresponding replicas were prepared for SEM. In the replicas, the frequency of apical gaps at the dentin/cement interface was observed. In the specimens, the apical microleakage was detected and confirmed by EDS (Energy Dispersive Spectroscopy). The dentin/cement interface was observed in six specimens of each group randomly selected. The microleakage was similar among the groups (p>0,05) being influenced by gaps frequency (p<0,05). The Epiphany group presented gap-containing regions, hybrid layer formation and long tags. For AH Primer and AH Plus groups, good marginal adaptation with long empty tags and small plugs, respectively, although gaps formation was found in both groups. The remaining teeth were used for other evaluations: six, to finish micromorphological study at the adhesive interface; three, for Knoop microhardness; and thirty, for bond strength test. The Epiphany resin sealer has showed the highest flow (p<0.001) and polymerization stress (p<0.05), and the lowest bond strength values (p<0.001). The Knoop microhardness values have decreased excessively from the cervical to the apical third (p<0.001). It was concluded that none of the sealers tested achieved a complete sealing of the root canals system, and the Epiphany system has developed more gaps to the apex.

Made available in DSpace on 2017-07-24T19:22:00Z (GMT). No. of bitstreams: 1 Andres Felipe M Cardenas.pdf: 5280325 bytes, checksum: 04a1911a6a06b35dcfc2a254330c8113 (MD5) Previous issue date: 2016-05-25 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / This study evaluated the effect of application the different pHs (0.5, 1 and 2) of meta-phosphoric acid 40% (MPA) with ortho-phosphoric acid 37% (OPA) in different application times with three laboratory studies in vitro. For all experiments, the teeth were distributed into 12 experimental conditions according to the combination of independent variables: acid [37% orthophosphoric acid (OPA), 40% metaphosphoric acid (MPA) pH - 0.5, 1 and 2] and application time [7, 15 and 30 seconds]. For experiment 1, the acids were applied on 72 human molars for microtensile bond strength (μTBS), and nanoleakage (NL). After acid conditioning the adhesive system was applied (Ambar) and restoration in composite resin was performed. Then, the teeth were sectioned to obtain specimens and tested immediately. The Etching Pattern (PC) was evaluated after acid application in dentin. For experiment 2, 93 human molars were used. After acid application in dentin, the adhesive system was applied and composite resin restoration was made. They were then sectioned, half sticks were tested immediately and the other half after 6 months of storage in water for μTBS and NL analysis. The analysis of chemical composition was performed by micro-Raman spectrometry. For experiment 3, 60 human molars were distributed according to the similar independent variables as the experiment 1 and 2. The enamel surfaces were stored in water (37 °C / 24 h) and tested for (μSBS). The PC and qualitative analysis composition of chemical enamel by micro-Raman test was evaluated. For the experiment 1 and 3, acid vs time of application the μTBS and NL data were submitted to 2-way ANOVA and Tukey's test (α = 0.05). For the experiment 2, acid vs application time vs storage time the μTBS data and NL were submitted to 3-way ANOVA and Tukey's test (α = 0.05). For experiment 1, MPA pH 0.5 showed μTBS similar to OPA, independent of the application time (p> 0.05) and statistically higher NL was observed for OPA compared with MPA (p <0, 03). For experiment 2, a significant decrease μTBS value was observed only OPA after 6 months (p = 0.001) and higher values of NL were found when compared to MPA (p = 0.003). For the experiment 3, OPA and MPA pH 0.5 produced statistically higher μSBS when compared to MPA pH 1 and 2 independent of the application times (p <0.001). The MPA acid is an alternative agent for the simultaneous conditioning of enamel and dentin, increasing the μTBS, reducing the NL immediate and after 6 months of storage when compared to the conventional ortho-phosphoric acid. The sum of the properties evaluated, MPA pH 0.5 showed high μSBS, showing be promissory. / O objetivo desse trabalho foi avaliar o efeito de diferentes pHs (0,5, 1 e 2) do ácido metafosfórico 40% (AMF) com o ácido ortofosfórico 37% (AOF) sob diferentes tempos de aplicação por meio de três estudos laboratoriais in vitro. Em cada estudo, os dentes foram distribuídos aleatoriamente em 12 condições de acordo com a combinação das variáveis independentes: Ácido [ácido ortofosfórico a 37% (AOF), ácido metafosfórico a 40% (AMF) pH - 0,5, 1 e 2] e tempos de aplicação [7, 15 e 30 s]. Para o experimento 1, os ácidos foram utilizadas e aplicados sobre 72 molares para resistência de união (RU) e nanoinfiltração (NI). Após condicionamento ácido aplicou-se o sistema adesivo (Ambar) e realizou-se a restauração em resina composta (Opallis). Depois de 24 h foram seccionados e testados. O padrão de condicionamento (PC) foi avaliado após aplicação dos ácidos em dentina. Para o experimento 2, foram utilizados 93 molares, após aplicação dos ácidos em dentina, aplicou-se o sistema adesivo e a restauração em resina composta. Logo após, foram seccionados e metade dos palitos foram testados imediatamente e a outra metade após 6 meses de armazenamento em água para análise da RU e NI. A análise da composição química foi realizada por espectroscopia micro-Raman. Para o experimento 3, 60 molares foram utilizados e distribuídos em função das variáveis já citadas. As superfícies de esmaltes foram armazenadas em água (37 °C / 24 h) e testadas para resistência de união no esmalte por microcisalhamento. O PC e análise de composição da química qualitativa do esmalte por teste micro-Raman foram avaliados. Para o experimento 1 e 3, ácido vs tempo de aplicação os dados de RU e NI foram submetidos a ANOVA 2 fatores e teste de Tukey (α = 0,05). Para o experimento 2, ácido vs tempos de aplicação vs tempo de armazenamento os dados de RU e NI foram submetidos a ANOVA 3 fatores e teste de Tukey (α = 0,05). Para o experimento 1, o AMF pH 0,5 mostrou RU significativamente semelhante ao AOF, independentemente do tempo de aplicação (p>0,05) e uma NI estatisticamente mais elevada foi observada para AOF em comparação com AMF, (p<0,03). Para o experimento 2, diminuições significativas nos valores de RU foram observados somente para AOF após 6 meses (p = 0,001) e valores de NI mais elevados foram encontrados quando comparado com AMF (p = 0,003). Para o experimento 3, o AOF e AMF pH 0,5 produziram valores RU estatisticamente mais elevados, quando comparados com AMF pH 1 e 2 independentemente dos tempos de aplicação (p<0,001). O AMF é um ácido que pode ser utilizado simultaneamente em esmalte e dentina, demonstrando uma alta RU, diminuição da nanoinfiltração imediata e após 6 meses de armazenamento quando comparado com o AOF. No somatório das propriedades avaliadas, o pH 0,5 apresentou alta RU em esmalte em relação ao AOF, mostrando-se promissor.

Made available in DSpace on 2017-07-24T19:22:29Z (GMT). No. of bitstreams: 1 Giovana Mongruel Gomes.pdf: 3752517 bytes, checksum: 6acad02e468853d81d1d9172fd003844 (MD5) Previous issue date: 2013-09-20 / The objectives of this study were 1) to evaluate the effect of the influence of the resin cement thickness (RCT) on bond strength (BS) and gap formation (GF) between glass fiber post (FP) and root dentin and 2) to evaluate the BS and fracture resistance (FR) of restorative techniques for filling oversized root canals. In experiment 1, the roots of 24 mandibular premolars (n=8 per group) were endodontically treated. After one week, the post spaces were prepared depending on the post adaptation inside the root canal, simulating an ideal adaptation (IdAd),medium adaptation (MeAd) and inadequate adaptation (InAd). All posts were cemented with Excite® DSC and Variolink® II. After a week of cementation, the RCT and GF were measured with the Image Tool software version 3.0, and the BS by the push-out test. In experiment 2, the roots of 84 mandibular premolars were endodontically treated and, after a week, the conduits were prepared in order to simulate an oversized root canal, except for the positive control group (PC), which was cemented one prefabricated fiber post (PFP) with the diameter compatible with the conduit. In the other oversized root canals, alternative restorative techniques for filling root canals were tested: NC - negative control (PFP with a smaller diameter than of the root canal), PA - PFP + accessory posts, DAP – direct anatomical post,IAP – indirect anatomical post and RR – root reinforcement with composite resin. All posts were cemented with the same adhesive system and resin cement. After indirect composite crowns cementation, the teeth were submitted to mechanical fatigue (1.2 X 106 cycles, 40 N) before the push-out BS test (n=8) and the FR test (n=6). The data of experiments 1 and 2 were analyzed by ANOVA and paired test (α=0.05). The experiment 1 showed that the smaller RCT resulted in better fiber post adhesion, that is, higher BS and lower GF. The experiment 2 showed that the use of direct and indirect anatomical posts resulted in the best performance both in BS and FR tests,and must be the first choice for FP cementation in flared roots with oversized root canals. Therefore, we concluded that the post adaptation to root canal affected significantly its retention. The better the post adaptation, the better the laboratory results. However, in the absence of this ideal condition, the use of direct and indirect anatomic posts should be the first choice for restoring flared root canals. / Os objetivos deste estudo foram 1) avaliar o efeito da influência da espessura de cimento resinoso (ECR) na resistência de união (RU) e na formação de gaps (FG) entre pino de fibra de vidro (PFV) e dentina radicular e 2) avaliar a RU e resistência à fratura (RF) de técnicas restauradoras para preenchimento de canais radiculares excessivamente alargados. No experimento 1, as raízes de 24 pré-molares inferiores (n=8 por grupo) foram tratadas endodonticamente. Após uma semana, os condutos foram preparados em função da adaptação do pino no canal radicular, simulando uma adaptação ideal (AdId), média (AdMe) e inadequada (AdIn). Todos os pinos foram cimentados com Excite® DSC e Variolink® II. Uma semana após a cimentação, a ECR e a FG foram mensuradas com o software Image Tool versão 3.0 e a RU por meio do teste de push-out. No experimento 2, as raízes de 84 pré-molares inferiores foram tratadas endodonticamente e, após uma semana, realizou-se o preparo dos condutos, de maneira a simular um canal radicular excessivamente alargado, com exceção do grupo controle positivo (GCP), em que foi cimentado um pino préfabricado (PPF) com calibre compatível ao diâmetro do conduto. Nos outros condutos alargados, técnicas restauradoras alternativas de preenchimento dos canais radiculares foram empregadas: GCN – grupo controle negativo (PPF de diâmetro inferior ao conduto), GPA – PPF + pinos acessórios, GAD – pino anatômico direto, GAI – pino anatômico indireto e GRR – reforço radicular com resina composta + PPF. Todos os pinos foram cimentados com o mesmo sistema adesivo e cimento resinoso. Após cimentação de coroas de resina indireta, os dentes foram submetidos à fadiga mecânica (1,2 x 106 ciclos, 40 N) antes de realizar o teste de RU (n=8) e de RF (n=6). Os dados do experimento 1 e 2 foram analisados por ANOVA e teste pareado (α=0,05). O experimento 1 mostrou que quanto menor a ECR melhor a adesão dos PFV, ou seja, maior a RU e menor a FG. O experimento 2 mostrou que o uso de pinos anatômicos diretos e indiretos mostrou o melhor desempenho nos testes de RU e RF, e deve ser primeira opção para cimentação de PFV em canais radiculares alargados. Portanto, foi evidenciado que a adaptação do pino ao conduto radicular influenciou significativamente na retenção dos mesmos; quanto mais justa,melhores resultados laboratoriais. Entretanto, na ausência desta condição ideal, o uso de pinos anatômicos diretos e indiretos pode ser a primeira escolha do clínico para tratamento de canais excessivamente alargados. Palavras-chave: cimentos resinosos, dentina radicular, gap, microscopia eletrônica de varredura, pinos de fibra, raízes enfraquecidas, resistência à fratura, resistência de união.

O objetivo deste estudo é avaliar a influência da irradiação com laser de Er,Cr:YSGG no espaço protético de condutos radiculares preparados para a fixação de pinos em fibra de vidro reforçados (FRC Postec®), avaliando-se o comportamento de três diferentes técnicas adesivas (self-etching= Panavia F®; total-etching= Excite DSC® + Variolink II® e self-adhesive= RelyX Unicem Aplicap®). Observaram-se as orientações da norma ISO-TS 11405 para a preparação das raízes dentais unirradiculares humanas. As amostras foram separadas na altura da junção amelo-dentinaria, tratadas endodonticamente com instrumentação rotatória e seladas com técnica de condensação lateral. Foram utilizados dois tipos diferentes de pontas de safira para irradiação intracanal o axial (Z4, 400 m de diâmetro) e o radial ou side firing (RFT4, 415 m de diâmetro) com densidade de energia de 40 J/cm2. Esta densidade de energia foi obtida como parte deste experimento, analisando-se diversos parâmetros de energia com os resultados morfológicos e térmicos obtidos. Nesta densidade, obtive-se grande quantidade de túbulos dentinários abertos e variação de temperatura segura para uso clínico. Cada raiz foi irradiada em cinco movimentos circulares, de apical para cervical, com intervalo de 20 segundos, entre elas. Os FRC Postec foram cimentados imediatamente após a irradiação e divididos randomicamente em nove grupos (n=10). Cada raiz foi seccionada em 6 discos de 1 mm de espessura para ensaio do tipo push-out, para a obtenção da força máxima de ruptura, e posterior cálculo da resistência de união adesiva em função da área de superfície do núcleo deslocado, resultando na pressão em MPa. A resistência de união adesiva nos grupos irradiados foi estatisticamente superior do que os grupos controle. Foram avaliadas as diferenças na resistência de união adesiva em diferentes porções do núcleo (cervical, médio e apical), onde o sistema adesivo tipo self-adhesive (RelyX Unicem Aplicap) teve o melhor resultado para os grupos irradiados. Avaliou-se por técnica de FTIR as diferenças químicas ocorridas na dentina intrarradicular irradiada com laser de Er,Cr:YSGG, em diferentes porções (cervical, médio e apical) em função da orientação dos túbulos. Foram observadas nos espectros de FTIR alterações na intensidade das bandas de algumas moléculas, indicando variação na quantidade da parte orgânica (amida I e amida II) após a irradiação, nas diferentes regiões dentais em função do feixe laser sobre a orientação dos túbulos dentinários, sem causar alterações na sua composição. Essas diferenças podem interferir no resultado da resistência de união adesiva. A técnica de utilização de laser de Er,Cr: YSGG em dentina radicular pré-cimentação de núcleo protético aumenta a resistência de união adesiva, na dependência do cimento utilizado. / The aim of this study was to evaluate the influence of the Er,Cr:YSGG laser irradiation in the prosthetic post space before FRC Postec placement using three different adhesive systems (self-etching- Panavia F; total-etching- Excite DSC + Variolink II e self adhesive - RelyX Unicem Aplicap). According to ISO-TS 11405, sectioned at the CEJ, human dental single roots were endodontically treated with rotatory instruments and filled with gutta-percha points and sealer. Were used at 40 J/cm2 an axial Z4 laser tip (400 m diameter) and a radial (side firing) RFT4 laser tip (415 m diameter). This density of energy was experimentally determinated observing morphological changes in SEM images due to an increase range in the energy applied to dentinal root canal surface. At the length between 32 and 49 J/cm2 most of the intracanal dentinal tubules were open. The temperature increase was within the biological safe suggesting a feasible clinical use. Each root canal was irradiated five times with helicoidal movements from apical to cervical, with 20 seconds interval. FRC Postec were immediately cemented and randomly divided in nine groups (n=10). Each root canal was cut in six discs for push out test, were the maximum failure load was obtained and the bond strength was calculated as a function of post bonded area. The bond strength for the irradiated groups was superior among all control groups. The evaluation of bond strength among root region (cervical, middle and apical) was performed and differences were observed. The self-adhesive (RelyX Unicem Aplicap) system was noted superior among all irradiated groups and all regions. Chemical changes were analyzed by FTIR due to dental root portion and dentinal tubules orientation to laser beam direction. The FTIR spectra obtained indicated changes due to tubules orientation and root canal portion irradiated such as the proportion among the compositional ratio without causing chemical changes. These compositional ratio alterations may affect the bond strength results. The irradiation with Er,Cr:YSGG laser on dentinal walls of a prosthetic post space preparation before the post cementation, as suggested in this study, may increase the bond strength between the post and root canal dentin depending upon the luting cement that is used.