Submitted by JOSIANE SANTOS DE OLIVEIRA (josianeso) on 2019-03-25T12:12:43Z No. of bitstreams: 1 Suellen Brasil Schröpfer_.pdf: 1391520 bytes, checksum: 0844b5c8e4465d26543bb978bfd9d940 (MD5) / Made available in DSpace on 2019-03-25T12:12:43Z (GMT). No. of bitstreams: 1 Suellen Brasil Schröpfer_.pdf: 1391520 bytes, checksum: 0844b5c8e4465d26543bb978bfd9d940 (MD5) Previous issue date: 2018-12-14 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / A Organização das Nações Unidas (ONU) afirma que até 2050 a população mundial atingirá o número de 9,7 bilhões de pessoas, o que aumentará a demanda de energia e a necessidade de ampliação da produção agrícola. Para tanto, será necessário manter um equilíbrio entre as plantações, a fim de que o setor agrícola possa suprir tanto a indústria de combustíveis alternativos, como o ramo alimentício. O arroz é uma das principais culturas plantadas no Brasil e, gera de 20 a 30% do seu peso em casca de arroz, um resíduo sólido agroindustrial com potencial de aplicabilidade na indústria e uma importante fonte de produção de calor. A casca de arroz pode ser convertida em fonte energética por meio de técnicas de decomposição termoquímica, sendo a pirólise à vácuo um destes métodos. Durante a conversão energética da biomassa são produzidos bio-óleo, gás não-condensável e biocarvão. Este último é um material sólido com alto teor de carbono, que pode ser utilizado como combustível, insumo para produção de produtos químicos, agente condicionador de solo e para diversas outras aplicações. Esta pesquisa teve como objetivo estudar a influência dos parâmetros de operação da pirólise à vácuo na produção de biocarvão a partir da casca de arroz (BCA). Os parâmetros avaliados foram: temperatura máxima de operação (400, 550 e 700 °C), taxa de aquecimento (5 e 20 °C min-1) e tempo de residência da biomassa no reator (5 e 30 minutos). O rendimento médio obtido de BCA foi de 60%, sendo que a temperatura máxima foi o parâmetro de operação que causou maior efeito na produção de biocarvão. A média dos teores de cinzas, carbono fixo e matéria volátil presentes nos biocarvões foram de 51, 22 e 19 %, respectivamente. Em geral, os BCAs apresentaram um comportamento próximo à neutralidade (6,0 - 7,5) com uma condutividade elétrica variando de 21 a 44 S/com. / The United Nations (UN) says that by 2050 the world population will reach 9.7 billion people, which will increase energy demand and the need to expand agricultural production. Therefore, it will be necessary to maintain a balance in agricultural production, in order that the sector can supply both the alternative fuels and the food industries. Rice is one of the main crops planted in Brazil and generates from 20 to 30% of its weight in rice husks. The rice husk is an agro-industrial residue with potential of applicability in the industry and an important source of heat production. Rice husk can be converted into an energy source by means of thermochemical decomposition techniques, with vacuum pyrolysis being one of these methods. When converted to an energy source through vacuum pyrolysis, it generates biochar, non-condensable gases and biooil. Biochar is a solid material with high carbon content, which can be used as fuel, input for producing chemicals, soil conditioning agent and other industrial applications. This research aimed to study the influence of vacuum pyrolysis operation parameters on the production of rice husk biochar (RHB). The parameters evaluated were: maximum operating temperature (400, 550 and 700 °C), heating rate (5 and 20 °C/min) and residence time of biomass into reactor (5 and 30 minutes). The average yield obtained from RHB was 60%, and the maximum operation temperature was the variable that most influenced the results. The average mass fractions of ash, fixed carbon and volatile matter present in the biochars were 51%, 22% and 19%, respectively. In general, the RHBs presented a close to neutrality (6.0-7.5) behavior and a conductivity ranging from 21 to 44 µS/com.

Orientador: Jorge Luís Akasaki / Banca: Marco Antonio Morais Alcantara / Banca: Antonio Ludovico Beraldo / Resumo: A presente pesquisa contribui para a utilização de cinza de casca de arroz (CCA) na construção civil abordando dois aspectos importantes ainda em discussão na literatura. O primeiro aspecto compreende uma análise da influência que a forma de plantio, clima, solo, cultivares e fonte/quantidade de fertilizantes à base de nitrogênio, utilizados na cultura do arroz, exercem na composição química e nas propriedades cristalográficas da CCA. O segundo aspecto foi aplicar em pastas, argamassas e concretos de alto desempenho uma CCA com baixo teor de carbono, de elevado caráter pozolânico, na condição natural (sem moagem), produzida de uma maneira simples e sem controle de temperatura. De acordo com os resultados obtidos neste trabalho, verifica-se a importância de efetuar ensaios rotineiros de análises químicas e de Difração de Raio-X para manter o controle de qualidade das CCAs produzidas, pois em situação de produção de CCA em larga escala, poderiam ser utilizadas cascas de diferentes origens. Neste trabalho, também ficou comprovada a viabilidade técnica e científica do método de produção de CCA utilizado. O método produz CCA que, dependendo da forma de amassamento dos compósitos, pode dispensar o emprego de moinhos para aumentar a finura e/ou reatividade de CCAs. / Abstract: This research contributes to the use of rice husk ash (RHA) in the civil building covering two important aspects that still under discussion in the literature. The first one includes an analysis of the influence that the form of planting, climate, soil, rice and source/amount of nitrogen-based fertilizers used in rice cultivation in performing crystallographic properties and chemical composition of the rice husk ash. The second one was to aplicate to the pastes, mortar and concrete of high performance a RHA with low carbon, high pozzolanic character, in the natural physical state (without grinding), produced in a simple way and without control of temperature. According to the results obtained in this research, it is important to do routine testing of chemical analysis and X-ray Diffraction to keep quality control of RHAs produced, because at industrial production in large scale it can be used husks of different origins. This research was also demonstrated the feasibility technical and scientific method of production of RHA used. The method produces RHA that depending on the form of production of the composite may eliminate the use of grinders to increase the fineness and/or reactivity of RHAs. / Mestre

The Mae Tao watershed, northwestern Thailand, has become contaminated with cadmium (Cd) from the zinc mining activities area in the nearby Thanon-Thongchai mountains. Consumption of Cd-contaminated rice has led to documented human health impacts. The aim of this study was to clarify transfer pathways from creek and canal waters to the paddy field soils near Baan Mae Tao Mai village and to determine the relationship between Cd forms in the soil and uptake by rice plants. Soils, irrigation canal sediments and water samples were collected during the dry season and at the onset of the rainy season. Rice samples were collected at harvesting time and samples of soil fertiliser were also obtained. Water samples were filtered, ultrafiltered and analysed by ICP-MS whilst sub-samples of dried, ground soils and sediments were first subjected to micro-wave assisted acid digestion (modified US EPA method 3052). XPRD and SEM-EDX methods were used for mineralogical characterisation and selective chemical extractions have assisted in the characterisation of solid phase Cd associations. Transfer mainly occurred in association with particulate matter during flooding and channel dredging and, in contrast with many other studies, most of the soil Cd was associated with exchangeable and carbonate-bound fractions. Moreover, there was a significant positive relationship between soil total Cd and rice grain Cd (R2=0.715), but a stronger relationship between both the Tessier-exchangeable soil Cd and the BCR-exchangeable soil Cd and rice grain Cd (R2=0.895 and 0.861, respectively). Stable Isotope Exchange (gives isotopically exchangeable Cd - E value) is generally considered to provide a better measure of bioavailability. The results of this study showed that SIE gave values which significantly positive correlated with the Tessier exchangeable fraction. Biochar has a porous structure and acidic functional groups on its surface which give it a high capacity to affect heavy metal adsorption when added to soils. Biochar samples were produced from rice husk (RHC) and miscanthus (MC) since these are cheap and readily available materials in Thailand. Indeed rice husk char is already used for rice seed germination by local farmers. Evaluation of the chemical and physical properties of the chars showed that the lower temperature (350°C) chars had greater proportions of oxygen-containing functional groups than those produced at 700°C. Moreover the low temperature RHC had the greater cation exchange capacity than the MC produced at the same temperature. In abiotic feasibility tests, it was shown that RHC was more effective than MC at lowering soil available Cd. The former reduced the E values for the medium-Cd soils by 4.7% and 16.0% when 1% and 5% RHC, was added, respectively. From pot experiments, in medium-Cd soils, 1% and 5% RHC amendment showed the potential to decrease Cd uptake by rice roots. However, further work involving addition of a greater proportion of biochar with a higher number of replicates is needed to reach more robust conclusions.

A contaminação por metais pesados em corpos hídricos tem sido extensivamente tratada com motivo de grande preocupação sobretudo nos aspectos ambientais e efeitos para a saúde humana. Metais pesados apresentam respostas deletérias ao homem, sendo causa de intoxicações agudas e crônicas, além do desenvolvimento de doenças, para o meio ambiente a bioacumulação e os efeitos adversos as espécies podem criar o desequilíbrio ambiental de ecossistemas. As fontes de metais pesados em corpos d’águas, muita das vezes advém de esgotos domésticos e industriais, tratados ou não, de forma que os sistemas convencionais de tratamento de esgotos não são aptos a removerem os metais pesados de seus sistemas, assim sendo necessário outras tecnologias para sua remoção. São tecnologias utilizadas para a extração de metais pesados de efluentes os sistemas de adsorção, troca-iônica, filtração por membranas, extração líquido-líquido, e outros. A adsorção por carvão ativado é uma técnica eficiente de remoção de contaminantes orgânico e inorgânicos. Tendo em vista que a casca de arroz é um resíduo abundante é com amplo potencial de aplicação em diversos processos esta tem sido aplicado na produção de carvões ativados. Dessa forma, este trabalho investigou a eficiência da remoção de cobre em meio aquoso utilizando carvões ativados da casca de arroz. O processo de ativação por impregnação ácido e básica produziu carvões ativados com diferentes características químicas e respostas na extração de cobre em meio aquoso. Os ensaios para avaliação das variáveis independentes utilizaram do planejamento experimental por modelo fatorial. O carvão da casca de arroz ativado por hidróxido de potássio (CA-KOH) é um bom adsorvente de íons de cobre em solução com eficiências de remoção superiores a 96%. Enquanto a melhor condição para aplicação do carvão ativado por ácido fosfórico de casca de arroz (CA-H3PO4) ocorreu em pH de 7,3 por 65 minutos de tempo de contato com a remoção de 92,9% de cobre em solução. Foram estimados a partir do planejamento experimental os modelos de regressão para predição de extração de cobre, bem como suas superfícies de resposta. O CA-KOH apresentou alto potencial para aplicação em sistemas de tratamento de efluentes, sendo que a aplicação deste para atingir valores ótimos de extração deverá ocorrer em pH entre os intervalos inferior a 4 e superior 7 com o emprego de uma dosagem de 15-20 g de carvão/L de efluente. / The contamination by heavy metals in water bodies has been extensively treated because of great concern mainly on environmental aspects and effects on human health. Heavy metals present deleterious responses to humans, causing acute and chronic intoxications, besides the development of diseases, to the environment bioaccumulation and adverse effects species can create the environmental imbalance of ecosystems. Sources of heavy metals in bodies of water often come from domestic and industrial sewage, treated or untreated, so that conventional sewage treatment systems are not able to remove heavy metals from their systems, so it is necessary other technologies for its removal. The adsorption, ion exchange, membrane filtration, liquid-liquid extraction, and other technologies are used for the extraction of heavy metals from effluents. Activated carbon for adsorption is an efficient technique for removal of organic and inorganic contaminants. Considering that the rice husk is an abundant residue, it has a wide potential of application in several processes, this has been applied in the production of activated carbons. Thus, this work investigated the efficiency of the removal of copper in aqueous media using activated carbons of rice husk. The activation process by acid and basic impregnation produced activated carbons with different chemical characteristics and responses in copper extraction in aqueous medium. The trials for evaluation of the independent variables used experimental planning by factorial model. Potassium hydroxide-activated rice husk charcoal (CA-KOH) is a good solution of copper ions adsorbent with removal efficiencies greater than 96%. While the best condition for the application of activated carbon by phosphoric acid rice husk (CA-H3PO4) occurred in pH of 7.3 for 65 minutes of contact time with the removal of 92.9% copper solution. The regression models for copper extraction prediction, as well as their response surfaces, were estimated from the experimental design. The CA-KOH presented high potential for application in effluent treatment systems, and it is recommended to apply this in pH between the intervals below 4 and higher 7 using a dosage of 15-20 g of coal / L of effluent.

Submitted by Cátia Araújo (catia.araujo@unipampa.edu.br) on 2017-09-29T12:26:35Z No. of bitstreams: 1 Alessandro da Silva Nunes - 2017.pdf: 6741171 bytes, checksum: d73d33e3d451f8c04927bd5a122638d5 (MD5) / Approved for entry into archive by Marlucy Farias Medeiros (marlucy.farias@unipampa.edu.br) on 2017-09-29T16:24:11Z (GMT) No. of bitstreams: 1 Alessandro da Silva Nunes - 2017.pdf: 6741171 bytes, checksum: d73d33e3d451f8c04927bd5a122638d5 (MD5) / Made available in DSpace on 2017-09-29T16:24:11Z (GMT). No. of bitstreams: 1 Alessandro da Silva Nunes - 2017.pdf: 6741171 bytes, checksum: d73d33e3d451f8c04927bd5a122638d5 (MD5) Previous issue date: 2017-04-25 / O presente trabalho tem o objetivo de desenvolver novos materiais cerâmicos refratários, através do aproveitamento de resíduos derivados da geração de energia elétrica a partir da queima da casca de arroz. Microfibras cerâmicas foram introduzidas com o intuito de melhorar a resistência ao choque térmico. Os corpos de prova foram produzidos pelo método de prensagem uniaxial (20MPa), com substituição da argila refratária por sílica da casca de arroz (20%), e microfibras cerâmicas (20%) ou fibras de aço (1,9%, 3,8% e 5,6%). A sinterização ocorreu na temperatura de 1300º C. As propriedades físicas foram avaliadas através dos ensaios de porosidade aparente, absorção de água, densidade de massa, retração linear de queima, variação de massa e condutividade térmica. As propriedades mecânicas foram avaliadas pelos ensaios de resistência à compressão e resistência à flexão em três pontos. As propriedades térmicas foram avaliadas pelo ensaio de resistência ao choque térmico. As análises de XRD mostraram que houve transformação de parte da sílica presente na mistura em mulita e o restante permaneceu como quartzo. Além disso, a adição de sílica de casca de arroz resultou em uma microestrutura com baixa porosidade, alta retração de queima e elevada resistência mecânica. As cerâmicas com fibras apresentaram porosidade elevada, menor retração de queima e menor condutividade térmica do que a cerâmica de referência. Relativamente à resistência ao choque térmico, as cerâmicas com fibras de aço apresentaram desempenho significativamente superior em relação às cerâmicas sem fibras. / This study aims to develop new refractory ceramic materials, through the use of waste resulting from the electricity generation from rice husk burning. Ceramic microfibers were introduced with the aim of improving the resistance to thermal shock. The samples are produced by uniaxial pressing method (20MPa), by replacing refractory clay for ashes of rice husks (20%), ceramic microfibers (20%), and steel fiber (1,8%, 3,8% and 5,6%). The sintered occurred at temperature of 1300º C. Samples physical properties will be evaluated through the apparent mass density tests, apparent porosity, water absorption, linear shrinkage after burning, mass variation and thermal conductivity. The mechanical properties are evaluated by the compressive strength test and three points flexural test. The thermal properties will be evaluated by the thermal shock resistance test. XRD analyzes showed that some silica was present in the mullite mixture and the rest remained as quartz. The results show that the addition of SCA resulted in a microstructure with low porosity and with high firing shrinkage. The ceramics with fibers presented high porosity and low firing shrinkage and thermal conductivity, even, lower than the reference ceramic. The ceramics with SCA presented high mechanical resistance, while the ceramics with steel fibers had more ductile behavior. Regarding the thermal shock resistance, the ceramics with steel fibers presented a significantly superior performance in relation to the ceramics without fibers.

A questão central deste trabalho é demonstrar a viabilidade técnica e econômica da estabilização de solos com os cimentos pozolânicos de cinza de casca de arroz e de resíduo cerâmico. Para alcançar este objetivo o trabalho foi desenvolvido em duas etapas: a primeira referente ao desenvolvimento dos cimentos pozolânicos e a segunda referente à estabilização do solo propriamente dita. Em ambas as etapas adotou-se o critério da simplicidade e da possibilidade de utilização de equipamentos leves e de absorção de mão-de-obra não especializada. Os resultados técnicos e econômicos referentes ao cimento pozolânico de cinza de casca de arroz foram animadores; porém o mesmo não ocorreu com o cimento pozolânico de resíduo cerâmico que apresentou um desempenho em um patamar inferior. Quanto à estabilização de solos, os experimentos e a avaliação econômica efetuada mostram que a eficácia dos cimentos pozolânicos utilizados é limitada sendo difícil a obtenção de resultados comparáveis com o atualmente obtido com o cimento Portland. / The main scope of this work is to demonstrate the technical and economical viability of the soil stabilization with pozzolanic cements made from rice husk ash and waste bricks and tiles. In order to reach this objective the work has been developed in two stages: the first referes to the development of the pozzolanic cement and the second one referes to the soil stabilization. In both these stages the criteria that has been adopted was of the simplicity, of the use of light equipments and of non skilled labour. The technical and economical results referring to the rice husk ash pozzolanic cement were encouraging; but the same was not the case with the waste bricks and tiles pozzolanic cement that had an inferior performance. As regards the soil stabilization, the tests and the economical evaluation show that the efficiency of the pozzolanic cement is limited thus the results achieved are not as good as of the Portland cement.

Esta tese apresenta a obtenção de sílica xerogel a partir de carvão de cascas de arroz e a modificação da sua superfície com um ligante orgânico tipo base de Schiff. O objetivo da utilização deste resíduo agroindustrial é a obtenção de um adsorvente capaz de atuar no tratamento de águas contaminadas contendo íons cádmio II, em uma concepção de valorização de resíduos. A sílica contida na biomassa foi obtida na forma de silicato de sódio através de extração química com solução de hidróxido de sódio, seguida de hidrólise e condensação do monômero através do processo solgel. A modificação da superfície da sílica com o ligante salen foi realizada utilizando o 1,2-dicloroetano como espaçador bifuncional. A sílica xerogel modificada foi avaliada através de análises de isotermas de adsorção e dessorção de nitrogênio (BET/BJH), difração de raios-X (DRX), análise química elementar (CHN), espectroscopia de infravermelho com transformada de Fourier (FTIR), microscopia eletrônica de varredura (MEV) e termogravimetria (TG/DTG). A análise elementar indicou que 0,341 mmol/g de 1,2-dicloroetano e 0,095 mmol/g de salen foi ancorado na superfície da sílica, que apresentou estabilidade térmica até 209°C e área de superfície específica de 106,4 m²/g. Foi realizado um estudo sobre a capacidade de adsorção de íons cádmio (II) pela sílica modificada e não modificada. Os resultados indicam a superior capacidade de adsorção de cádmio pela sílica modificada, em soluções com baixa concentração do íon. / This thesis presents the obtainment of silica xerogel by rice husk charcoal and its surface modification using an organic ligand type Schiff-base. The purpose of this agro-industrial residue utilization is the production of an adsorbent capable to remove heavy metals present in contaminated waters. The silica contained in the biomass was obtained by alkaline extraction in sodium silicate with hydrolysis through sol-gel process, and modified with salen, using 1,2-dichloroethane as bi-functional spacer. The modified xerogel silica was evaluated through analysis of nitrogen adsorption/desorption isotherms (BET/BJH), X-ray diffraction (XRD), chemical elementary analysis (CHN), Fourier transform infrared spectroscopy (FTIR), scanning electronic microscopy (SEM) and thermogravimetric analysis (TG/DTG). The elementary analysis pointed that 0,341mmol/g of the 1,2-dichloroethane and 0,095mmol/g of the salen was anchored to the silica surface, that presented thermal stability until 209°C and specific surface area of 106,4 m²/g. An evaluation about the ion cadmium II adsorption capacity of the silica modified and unmodified was performed. The results pointed to the superior cadmium adsorption capacity for the modified silica if low ion concentration solutions.

Na primeira etapa deste trabalho foi avaliada a potencialidade do uso da cinza de casca de arroz como carga em polipropileno (PP) comparando-a com o talco que é a carga mineral mais utilizada em polímeros. Esta comparação foi feita utilizando os compósitos formados por polipropileno com 20% da cinza de casca de arroz assim como, os formados por polipropileno com 20% de talco, determinando as suas propriedades. Apesar das propriedades do compósito de PP com a carga de 20% de cinza de casca de arroz apresentarem resultados inferiores em relação àqueles quando se utilizou o talco como carga, pode-se dizer que a cinza de casca de arroz pode ser usada como carga para outros usos menos nobres do PP. Desta forma se está dando um destino para esse resíduo que hoje é descartado no meio ambiente contribuindo assim, para a preservação do mesmo, além de reduzir o custo do produto. Este trabalho também teve como objetivo estudar o efeito da radiação ionizante nas propriedades destes compósitos de PP com 20% de cinza de casca de arroz. Utilizou-se o agente de acoplagem, anidrido maleico, para verificar se houve melhora na homogeneização das amostras. Em virtude do PP ser um polímero semicristalino, quando exposto ao processo de irradiação, tem sua morfologia modificada devido aos mecanismos de cisão das cadeias poliméricas. Este fato é atribuído aos mecanismos de cisão das cadeias poliméricas, que está de acordo com a literatura. / In the first step of this work, it was evaluated the possibility of using rice husk ash as a filler in polypropylene (PP) making a comparison with talc which is the most used mineral filler in polymers. This comparison was made by using polypropylene with 20% rice husk ash as well as polypropylene with 20% talc measuring their properties. Despite the properties of the PP with 20% rice husk ash decreased compared with the composite of polypropylene with 20% talc it can be said that the rice husk ash can be used as filler for or other utilization less noble of PP . This way it is being given a destination for this residue that it is disposable in the environment contributing to its preservation, moreover reducing the product cost. This work had also as an aim to study the ionizing radiation effect in the properties of these composites. It was used the coupling agent, maleic anhydride , to verify a best sample homogenization. According to the results it can be said that PP is a semicrystalline polymer, and so it has its morphology modified when exposed to the irradiation process. This fact is due to the scission mechanisms of the polymeric chains which it is in compliance to the literature.

O uso de adições minerais no concreto como substituição parcial ao cimento Portland ajuda a preservar os recursos naturais poupando a matéria-prima, reduzindo o consumo de energia necessária para a produção do cimento e reciclando rejeitos que se lançados no meio ambiente causariam problemas ambientais e de saúde pública. A adição mineral que vem tendo muito destaque devido à sua alta reatividade, considerada por vários pesquisadores como uma superpozolana, é a sílica ativa (SA), um subproduto da fabricação de silício metálico ou ligas de ferro-silício. A sílica ativa se caracteriza por uma elevada finura e alta área específica e um alto teor de sílica vítrea, estes fatores somados garantem à SA a alta reatividade com o hidróxido de cálcio, transformando-o em silicato de cálcio hidratado. A casca do arroz vem sendo pesquisada como uma fonte alternativa de sílica ativa. A sílica ativa extraída da casca de arroz contém um alto teor de SiO2 e, dependendo do processo de extração, possui propriedades adequadas para a utilização na confecção de concretos de elevado desempenho. Este trabalho visa estudar a atividade pozolânica da sílica da casca de arroz produzida no laboratório de materiais avançados à base de cimento. Para avaliar as características das sílicas, foram realizados ensaios tanto para determinação das suas propriedades físicas quanto para a determinação de sua composição química e pozolanicidade. Os ensaios realizados foram:composição química, pozolanicidade (método Chapelle modificado), área superficial B.E.T., distribuição granulométrica, distribuição do tamanho de partículas via MEV, amorficidade (por difratometria de raio X), massa específica e determinação do índice de atividade pozolânica com cimento Portland (NBR-5752). Os ensaios de caracterização demonstraram que a sílica da casca de arroz possui um alto grau de amorficidade e elevada área superficial, que garantiram uma maior reatividade nas idades iniciais, porém em idades avançadas apresentou a mesma eficiência que a sílica de ferro-silício. / The use of mineral additions in concrete in order to partially replace Portland cement helps to protect natural resources by saving raw material, reducing energy consumption in cement production and recycling industrial waste that could otherwise cause environmental and public health hazards. One mineral addition that has drawn considerable attention due to its high reactivity is silica fume (SF), a byproduct of the manufacturing process of metallic silicon or iron-silicon alloys and considered by many researchers as a superpozzolan. Silica fume is characterizated by high fineness, high specific area and high content of vitreous silica. The sum of these factors provides SF high reactivity with calcium hydroxide, which is transformed into hydrated calcium silicate. Rice husk ash has also been investigated as an alternative source of silica fume. The silica from rice husk ash contains a high percentage of SiO2 and, depending on the extraction process, has adequate properties to be employed in the manufacturing of high-performance concrete. The objective of this work is to study the pozzolanic activity of silica from rice husk ash produced at the Laboratório de Materiais Avançados à Base de Cimento. In order to evaluate the characteristics of silica samples from rice husk, assays were performed to determine their physical properties as well as their chemical composition and pozzolanicity. The assays performed were: chemical composition,pozzolanicity (modified Chapelle method), B.E.T. surface area method, granulometric distribution, particle size distribution by Scanning Electron Microscope (SEM), amorphicity by X-ray diffractometry (XRD), specific mass and pozzolanic activity index determination with Portland cement (NBR-5752). The characterization assays showed that the silica from rice husk ash has a high amorphicity level and a high surface area, which yield higher reactivity at initial ages. However, at advanced ages it pesented the same efficiency as that of silica from iron-silicon.

A sustentabilidade das regiões de produção intensiva de suínos depende de destinos alternativos para os resíduos nelas gerados. A calcinação da cama sobreposta gera sílica vítrea que pode ser utilizada na substituição parcial de aglomerantes comerciais. A utilização de cinzas de casca de arroz como material pozolânico para a confecção de argamassas e concretos tem merecido atenção considerável, nos últimos anos, não apenas por melhorar as propriedades mecânicas de materiais cimentícios, mas, sobretudo pelos benefícios ambientais gerados, com a redução do consumo de clínquer. A falta de sustentabilidade ambiental pode limitar o crescimento econômico da suinocultura, dada a tendência do setor de crescimento concentrado em grandes empreendimentos, e, por conseqüência, do aumento da poluição provocada pelos dejetos. Com a busca de alternativas que solucionem ou minimizem tal problema, o objetivo geral deste trabalho foi o aproveitamento de resíduos agropecuários (cama sobreposta de suínos e fibra curta de sisal) para a fabricação de placas à base de compósitos cimentícios para escamoteadores com diferentes tipos de aquecimento (lâmpada incandescente e resistência elétrica). As cinzas de cama sobreposta de suínos substituíram 30% do cimento Portland. A matriz cimentícia resultante foi reforçada com fibra curta de sisal. Os resultados obtidos com a utilização da cinza da cama sobreposta de suínos valida seu uso como material de substituição parcial do cimento Portland. A temperatura ideal de calcinação é de 600 ºC, com rampa de 5 ºC/min durante 3 h. O material selecionado foi o passante na peneira ABNT No 200 (# 0,074 mm). A cinza da cama sobreposta de suínos aumentou a condutividade térmica e a fibra de sisal incorporou o ar na placa e, assim, reduziu a conducao do calor para a parte inferior. O melhor tratamento foi a utilização da placa em duas camadas com cinza de cama sobreposta e fibra de sisal, associada ao uso da lâmpada de 200 W. / The sustainability of intensive areas of swine production depends on alternative destinations for the generated residues. The calcination of swine deep bedding generates vitreous silica for partial replacement of commercial binders. The use of rice husk ashes as pozzolanic material for mortars and concretes has deserved considerable attention in the last years, not just for improving their mechanical properties, but also for the environmental benefits linked to the reduction of clinker consumption. The lack of environmental sustainability can limit the economical growth of swine production, due to the tendency for concentration in sites with intensive activity, and, as a consequence, the increase of the contamination by wastes. Aiming alternatives that can minimize or decrease such problem, the objective of this work is to test the use of agricultural waste (swine deep bedding ashes and sisal fiber) for the manufacture of piggy`s house plates with different types of heating (filament lamps and electric resistance) on based cement composite materials. The swine deep bedding ashes replaced 30% of Portland cement. The resulting cementations matrix was reinforced with sisal fiber. The results obtained with the use of swine deep bedding ashes validates the use of this material for partial replacement of Portland cement. The optimal calcination temperature is 600 °C with rate of 5 ºC/min for over 3 hours. The material selected should be as pass in ABNT sieve No 200 (# 0.074 mm). The swine deep bedding ashes increased the thermal conductivity and sisal fiber entrapped air in the plate and due to the pores incorporated there was a reduction in the heat conduction to the bottom. The best treatment was the plate with two layers of swine deep bedding ashes and sisal fiber, associated with 200 W lamp.