Submitted by Mario BC (mario@bc.ufrpe.br) on 2016-09-20T11:57:07Z No. of bitstreams: 1 Lamonier Chaves Ramos.pdf: 550825 bytes, checksum: b8839328e2d38c2e95c580ba9f82fa5a (MD5) / Made available in DSpace on 2016-09-20T11:57:07Z (GMT). No. of bitstreams: 1 Lamonier Chaves Ramos.pdf: 550825 bytes, checksum: b8839328e2d38c2e95c580ba9f82fa5a (MD5) Previous issue date: 2014-08-14 / Conselho Nacional de Pesquisa e Desenvolvimento Científico e Tecnológico - CNPq / The genus Agave L. is extensively cultivated in many countries for present utilities in various sectors of the economy. The species Agave sisalana Perrine and the hybrid 11648 are the most important economically genotypes for Brazil, which is the largest producer and exporter of the extracted fiber from its leaves, known as “sisal”. Studies of their karyotypes have been limited so far the conventional staining techniques, which have been presented as insufficient, which have proven insufficient due to the small size and similarity of their chromosomes, so there is a need for more detailed analysis. This study aimed to analyze the karyotypes of the species Agave sisalana and hybrid 11648, by means of conventional staining techniques, the double staining CMA / DAPI and fluorescent in situ hybridization (FISH), in order to provide information that might be useful in breeding programs. The research was conducted at the Laboratório de Citogenética Vegetal, on the Universidade Federal Rural de Pernambuco (Botany Departament, UFRPE). The data of the conventional staining revealed that the hybrid 11648 is a diploid with 2n = 60, with a bimodal karyotype composed by five large chromosomes pairs and 25 small pairs. On the other hand, the species A. sisalana presented a pentaploid karyotype with 5n = 147 chromosomes, of which 25 were large and 122 were small. The pattern of CMA + band observed revealed that there is presence of constitutive heterochromatin rich in CG and that probably it remains conserved in both genotypes, with four bands observed in the hybrid and eight in the A. sisalana. In the hybrid sisal, FISH revealed two sites of 5S rDNA in a small chromosomes pair and two sites of 45S rDNA in a large chromosomes pair. In the species A. sisalana, 45S rDNA probes revealed five NOR, two of which are fully distended, forming secondary constrictions and the other three remain condensed and inactive throughout the cell cycle. This study provides new insights on the sisal karyotype, which can be useful for purposes of characterization and conservation of hits on germplasm banks as well as for use in breeding programs. / O gênero Agave L. representa uma cultura extensivamente cultivada em vários países por apresentar utilidades em diversos setores da economia. A espécie Agave sisalana Perrine e o híbrido 11648 são os genótipos de maior importância econômica para o Brasil, que é o maior produtor e exportador da fibra extraída de suas folhas, conhecida como sisal. Os estudos de seus cariótipos têm sido limitados, até então, as técnicas de coloração convencional, que têm se mostrado insuficientes devido ao pequeno tamanho e similaridade dos seus cromossomos, havendo assim a necessidade de análises mais detalhadas. O presente trabalho objetivou analisar os cariótipos da espécie Agave sisalana e do híbrido 11648, por meio das técnicas de coloração convencional, da dupla coloração CMA/DAPI e da hibridização in situ fluorescente (FISH), com a finalidade de fornecer informações que possam ser úteis em programas de melhoramento. A pesquisa foi conduzida no Laboratório de Citogenética Vegetal, da Universidade Federal Rural de Pernambuco (Departamento de Botânica, UFRPE). Os dados da coloração convencional revelaram que o híbrido 11648 é um diplóide com 2n = 60, com um cariótipo bimodal, composto de cinco pares cromossômicos grandes e 25 pares pequenos. Já a espécie A. sisalana apresentou um cariótipo pentaplóide com 5n = 147 cromossomos, dos quais 25 foram grandes e 122 foram pequenos. O padrão de banda CMA+ observado revelou que há presença de heterocromatina constitutiva rica em CG e que, provavelmente, esta se mantém conservada em ambos os genótipos, sendo observadas quatro bandas no híbrido e oito na A. sisalana. No sisal híbrido, a FISH revelou dois sítios de DNAr 5S em um par de cromossomos pequenos e dois sítios de DNAr 45S em um par de cromossomos grandes. Na espécie A. sisalana, as sondas de DNAr 45S revelaram cinco RONs, sendo que duas delas são completamente distendidas, formando constrições secundárias, e as outras três se mantêm condensadas e inativas ao longo do ciclo celular. O presente estudo traz novas contribuições sobre o cariótipo de sisal que podem ser úteis para fins de caracterização e conservação de acessos em bancos de germoplasma bem como para uso em programas de melhoramento genético.

Orientador: Lucia Helena Innocentini Mei / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-08-11T05:07:51Z (GMT). No. of bitstreams: 1 Jesus_RodolfoCardosode_M.pdf: 2937094 bytes, checksum: 406428b06b411d967d625ec5cff8fa13 (MD5) Previous issue date: 2008 / Resumo: O problema do acúmulo de lixo urbano tem aumentado nas últimas décadas e o grande consumo de plásticos é um dos responsáveis por esta situação. Estes materiais possuem a capacidade de permanecer no ambiente por muitos anos o que dificulta ainda mais a sua destinação correta. Este problema foi a principal motivação do trabalho aqui apresentado. O PHB é um material termoplástico biodegradável produzido por bactérias que se alimentam de sacarose, tais microorganismo convertem a sacarose em PHB. O Brasil é hoje um dos maiores produtores de PHB, entretanto este material possui baixas propriedades mecânicas quando comparados' a plásticos mais usados industrialmente. Algumas propriedades mecânicas foram melhoradas com a adição de triacetina como agente de plastificação, mas a resistência ao impacto diminui com este aditivo. Fibras são materiais utilizados em compósitos de matriz plástica para conferir resistência e flexibilidade a estes materiais. Fibras naturais têm sido empregadas com sucesso na tentativa de diminuir custos de compósitos e gerar reforço estrutural, além de diminuir o impacto ambiental dos plásticos. Neste trabalho foram obtidos compósitós de PHB, Triacetina e Fibras de Coco ou de Sisal, acetiladas e não-acetiladas, através de processos de extrusão e injeção. Os compósitos foram caracterizados por Análises Térmicas, Mecânicas, Espectroscópicas, Microscópicas e de Biodegradação. Os compósitos obtidos apresentaram vantagem em relação a matriz de PHB nos desempenhos mecânicos e de biodegradação devido a adição das fibras naturais e da triacetina. A reação de acetilação aparentemente melhorou a interação entre a superficie fibra-matriz e aparentemente foi mais bem sucedida na fibra de sisal / Abstract: The problem of urban waste accumulation has increased in recent decades and the large consumption of plastics is one of those responsible for this situation. These materiaIs have the ability to remain in the environment for many years making it difficult further to provide its correct destination. This problem was the main motivation of the work presented here. The PHB is a biodegradable thermoplastic material produced by bacteria feeding on sucrose, such microorganisms convert the sucrose in PHB. Brazil is today one of the largest producers of PHB, however this material has low mechanical properties compared to most plastics used industrially. Some mechanical propérties were improved with the addition of triacetin as agent for plasticization, but the resistance to the impact decreases with this additive. Fibers are used materiaIs in plastic matrix composite to give strength and flexibility to these materiaIs. Natural fibers have been used successfully in the attempt to reduce costs, and generate structural reinforcement composites, in addition to reducing the environmental impact of plastics. In this study were obtained from composites PHB, triacetate and Fibers of Coconut or Sisal, acetylated and non-acetylated through extrusion ~d injection, processes. The composites were characterized by Thermal Analysis, Mechanical, Spectroscopics, Microscopics and biodegradation. The composites obtained showed advantage over the array of PHB in the mechanical and performance degradation due to the addition of natural fibers and triacetate. The acetylation reaction apparently improved the interaction between the surface fiber-matrix and apparently was more successful in the sisal fiber / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química

M.Ing. (Civil Engineering) / The purpose of this study was to determine the effectiveness of a sisal fibre natural geotextile in controlling the rate and extent of soil erosion. The effectiveness of this locally produced material was compared to other natural fibre geotextiles and other methods commonly used for the control of soil erosion. The different materials and methods were tested under the same conditions to compare the relative effectiveness of these products. The various erosion control products were subjected to laboratory tests. A rainfall simulator and an adjustable slope simulator were used to simulate the process of soil erosion. During these tests the effectiveness of the different products in controlling soil erosion was measured and conclusions were made about the effectiveness of the products. Mechanical sieve analysis tests were used to determine the erodibility of the different soil particles. Field trials that made use of the sisal fibre geotextile are also discussed.

This volume is a study based on archival sources concerning a firm based in Leipzig which acquired land in German East Africa (near the coast of what is today Tanzania) in 1907 for the purpose of growing cotton. When the cotton crop was destroyed by leaf curl, the firm turned to sisal as an alternative crop. / Dieser Band ist eine auf Archivquellen basierende Studie bezüglich einer Firma aus Leipzig, die 1907 Land in Ostafrika (nah an der Küste, im heutigen Tansania) erlangte, um Baumwolle zu pflanzen. Als die Baumwoll-Ernte durch die Kräuselkrankheit zerstört wurde, wandte sich die Firma dem Sisal als alternative Nutzpflanze zu.

The aim with this master thesis was to investigate the potential of using non-wood fibers to enhance the paper strength. Abaca, sisal and banana fibers were added to conventional bleached chemical softwood pulp. The effect of refining was investigated, both as co-refining and as separate refining. The fiber properties were determined with a Fiber Tester and the drainage resistance was determined with Schopper-Riegler. Density, tensile index, tear index and burst index were determined on paper sheets made in a Rapid-Köthen sheet former. The results showed that abaca had longer fiber length than softwood, while sisal had slightly shorter fiber length compared with softwood. Sheet density was lowered with addition of all three fiber types, while the drainage resistance was increased for the same. It was also observed that the tensile index increased with additions of abaca, while additions of sisal and banana fibers gave lower tensile indexes. The same trend was observed for the tear index and burst index. Refining gave higher values of the drainage resistance, density, tensile index and burst index. However, the tear index was affected differently depending on the fiber type and fiber blend. For sisal and banana fibers, the tear index was first increased at lower refining degrees and were thereafter decreased with further refining. When studying abaca and softwood, a declining trend was observed over the entire refining interval. The conclusion was that addition of abaca fibers increased all investigated strength properties. Sisal and banana fibers gave higher values of the tear strength, when exposed to mild refining.

El presente trabajo tuvo como objetivo general realizar una propuesta de instalación de una planta de producción de cuerda de Sisal (Agave sisalana) en la región de Lambayeque, gestionando el ingreso de este nuevo cultivo en la región porque crece en suelos arenosos con los que se cuenta actualmente, además no hay necesidad de deforestar; del mismo modo sería un impacto socioeconómico favorable, pues significa trabajo para los pobladores. En primer lugar se realizó un estudio de mercado para determinar el principal comprador que Estados Unidos y cuya demanda va en aumento, sus principales proveedores son Brasil, China y México, éste último está tomando mercado de China, por el costo y tiempos de envío, además China se está enfocando en el uso de sisal como aditivo para la elaboración de bioplástico, se tomará porcentajes que varían entre 0,114% en el 2021 y 0,2% en el 2026, al proyectar los precios y ver que éstos también van en aumento se toma la decisión de proseguir con los estudios técnicos para la instalación de la planta con el fin de rescatar áreas que actualmente se utilizan como botaderos y promover el empleo de los pobladores de la región dentro de la industria. La inversión total asciende a 2514692.47 dólares se ve afectada por la inversión tangible e intangible. En el estado de ganancias y pérdidas con una proyección de 6 años da como resultado un valor negativo por lo que es irrelevante realizar un estudio de factibilidad económica financiera, llegando a la conclusión de que el proyecto no es viable.

Dentre as fibras vegetais estudadas como reforço para produção de compósitos cimentícios, as fibras de coco verde e sisal se destacam por suas características mecânicas de interesse industrial, baixo custo e baixa densidade. O objetivo deste trabalho é o estudo da funcionalização de fibras de coco verde e sisal, pela técnica de polimerização com plasma frio de metano, bem como a análise do efeito do tratamento, a fim de reduzir a hidrofilicidade natural das fibras, preservar suas propriedades mecânicas e aumentar sua durabilidade em meio alcalino. Fibras de coco verde e sisal foram tratadas com plasma frio de metano durante 4, 10 e 20 min. O experimento também incluiu ensaio de degradação das fibras, antes e após tratamento, em solução saturada de cimento Portland. Por meio de análise de molhabilidade e de espectroscopia de fotoelétrons excitados por raios X foi identificado que o tratamento tornou a superfície das fibras de sisal tratadas por 10 e 20 min menos hidrofílica, e das fibras de coco verde tratadas durante o mesmo tempo mais hidrofílica. Corroborando esses resultados, ensaio de arrancamento foi realizado em fibras de sisal tratadas por 20 min indicando boa aderência entre a fibra tratada e a matriz cimentícia. Após ensaio de degradação em solução cimentícia de ambas as fibras tratadas durante 10 e 20 min os resultados da espectroscopia na região do infravermelho por transformada de Fourier indicaram que o tratamento retardou o processo de degradação alcalina da hemicelulose e lignina das fibras de sisal, enquanto que para as fibras de coco verde a degradação das fibras sem tratamento foi igual ao daquelas sem com tratamento. Os ensaios mecânicos indicaram que as fibras de sisal tratadas tiveram maior resistência mecânica quando comparadas àquelas sem tratamento, e com relação às fibras de coco verde não houve diferença significativa entre fibras tratadas e sem tratamento. Além disso, não houve alteração do módulo de elasticidade das fibras de coco verde e sisal (sem tratamento e tratadas). Nesse contexto, os resultados obtidos indicaram que o tratamento com plasma frio de metano é eficaz para redução da hidrofilicidade da superfície das fibras de sisal, podendo vir a ser um tratamento promissor para minimizar a degradação alcalina da hemicelulose e lignina. / Among the studied plant fibres as reinforcement for the production of cement composites, green coconut and sisal fibres stand out for its mechanical characteristics of industrial interest, low cost, and low density. The aim of this work is to study of the plasma functionalization of green coconut and sisal fibres with methane cold plasma, as well as the analysis of the effect of this treatment in order to reduce the hydrophilicity of natural fibres, preserving its mechanical properties and increase its durability in alkaline medium. Green coconut and sisal fibres were treated with methane cold plasma for 4, 10 and 20 min. The experiment also included fibre degradation test before and after treatment in saturated solution of Portland cement. Wettability and XPS analyses indicated that the sisal fibres treated for 10 and 20 min presented surface more hydrophobic than green coconut fibres in the same treatment condition. Pullout test was performed in the sisal fibres treated by 20 min indicating good adherence between treated fibre and cement matrix. Both kinds of fibres were submited to degradation test imersed in the cementitious solution. The FTIR results indicated that the treatment retarded the alkaline degradation of the hemicellulose and lignin from sisal fibres whereas treated green coconut fibres showed the same degradation presented by untreated ones. The mechanical tests showed that the treated sisal fibres had higher mechanical strength compared to those without treatment, and regarding green coconut fibres there was no significant difference between treated and untreated fibres. Furthermore, there was no change in the modulus of elasticity of the green coconut and sisal fibre (treated and untreated). In this context, the results indicated that treatment with cold plasma of methane is effective in reducing the excessive hydrophilicity of the surface of sisal fibres and could be a promising treatment to minimize the alkaline degradation of hemicellulose and lignin.

Estudos anteriores utilizando matriz cimentícia reforçada exclusivamente com fibras vegetais propiciaram a produção de telhas com desempenho aceitável nas idades iniciais. Porém, com o envelhecimento natural, as telhas apresentaram significativa redução do desempenho mecânico, fato este atribuído principalmente ao ataque alcalino da matriz cimentícia. A presente pesquisa teve como objetivo o aprimoramento de telhas onduladas de fibrocimento sem amianto, a partir de processo automatizado. A primeira etapa do trabalho consistiu na avaliação do efeito da intensidade de refino da polpa Kraft de sisal (Agave sisalana) nas propriedades mecânicas e físicas de placas planas baseadas em matriz de cimento Portland, e o uso conjunto com fibras de poliproprileno (PP). Esta etapa envolveu também a caracterização dos principais atributos das polpas celulósicas refinadas, bem como a caracterização microestrutural (microscopia eletrônica de varredura e porosimetria por intrusão de mercúrio) do material resultante após envelhecimento acelerado e em ambiente natural. Na segunda etapa, séries de telhas onduladas de fibrocimento foram produzidas por técnica de sucção do excesso de água e prensagem, utilizando os melhores parâmetros definidos na etapa anterior. Os efeitos da cura acelerada em autoclave e dos envelhecimentos acelerados (carbonatação acelerada, imersão-secagem e calor-chuva) nas propriedades mecânicas e físicas das telhas foram avaliados. Os resultados obtidos mostraram a grande contribuição do refino da polpa celulósica na melhoria da resistência dos compósitos. Altas intensidades de refino apresentaram os melhores resultados para compósitos reforçados somente com polpa celulósica, mesmo após os envelhecimentos, porém intensidades intermediárias em compósitos híbridos mostraram-se suficientes. A adição das fibras de polipropileno como reforço híbrido teve como ponto forte a manutenção da resistência ao impacto, propriedade esta fortemente afetada pelo envelhecimento acelerado nos compósitos reforçados somente com polpa de sisal. As telhas produzidas mostraram-se mais eficientes no amortecimento térmico do que telhas comerciais de fibrocimento amianto. Melhorias no processo de produção das telhas mostraram efetiva contribuição no desempenho mecânico em relação aos trabalhos anteriores, tanto no curto como no longo prazo. Os resultados também indicaram a utilização da carbonatação acelerada como um procedimento eficiente na mitigação da degradação sofrida pelas fibras celulósicas em meios menos agressivos, no caminho para tornar viáveis os materiais reforçados com fibras vegetais. / Previous studies using exclusively vegetal fibres as the sole reinforcement of cement matrix have propitiated the production of roofing tiles with acceptable performance at the first ages. However, with the natural ageing, the roofing tiles have presented significant reduction in the mechanical performance, attributed to the alkaline attack of the cimentitious matrix mainly. The present research had as objective the improvement of undulate fibrecement roofing tiles without asbestos with automated equipment for production. The study also evaluated the physical, mechanical and microstructural behaviour of the obtained composites. The first stage consisted of evaluating the refinement effect of sisal Kraft pulp on mechanical and physical properties of flat pads based on Ordinay Portland cement and the jointly use of polypropylene fibres (PP). This stage also involved the characterization of the main attributes of refined cellulosic pulps, as well as the microstructural characterization (scanning electron microscopy and mercury intrusion porosimetry) of the resultant material after the accelerated and natural ageing. In the second stage, series of fibrecement roofing tiles were produced by slurry dewatering technique and pressing, using the best parameters of the first stage. Efects of autoclaved curing and accelerated ageing (accelerated carbonation, soak-dry and heat-rain) on mechanical and physical properties of tiles were evaluated. Results showed the great contribution of pulp refinement on mechanical strengh improvement. Higher intensities of refinement provided the best results for composites only reinforced with sisal pulp, despite ageing mechanism. Intermediate refinement revealed to be enough for hybrid composites. Adition of polypropylene fibres as hybrid reinforcement provided toughness maintenance after ageing, which was strongly affected only in sisal reinforced composites. Asbestos free tiles showed to be more efficient on thermal insulating properties than commercial asbestos cement. Improvements on tiles production process showed effective contribution on mechanical performance in relation to the previous works, both at initial ages and after ageing. The results have also indicated the utilization of accelerated carbonation as an effective procedure to mitigate the degradation suffered by the cellulosic fibres in the less aggressive medium, in way of the viability of the cement based materials reinforced by vegetal fibres.

Dentre as fibras vegetais estudadas como reforço para produção de compósitos cimentícios, as fibras de coco verde e sisal se destacam por suas características mecânicas de interesse industrial, baixo custo e baixa densidade. O objetivo deste trabalho é o estudo da funcionalização de fibras de coco verde e sisal, pela técnica de polimerização com plasma frio de metano, bem como a análise do efeito do tratamento, a fim de reduzir a hidrofilicidade natural das fibras, preservar suas propriedades mecânicas e aumentar sua durabilidade em meio alcalino. Fibras de coco verde e sisal foram tratadas com plasma frio de metano durante 4, 10 e 20 min. O experimento também incluiu ensaio de degradação das fibras, antes e após tratamento, em solução saturada de cimento Portland. Por meio de análise de molhabilidade e de espectroscopia de fotoelétrons excitados por raios X foi identificado que o tratamento tornou a superfície das fibras de sisal tratadas por 10 e 20 min menos hidrofílica, e das fibras de coco verde tratadas durante o mesmo tempo mais hidrofílica. Corroborando esses resultados, ensaio de arrancamento foi realizado em fibras de sisal tratadas por 20 min indicando boa aderência entre a fibra tratada e a matriz cimentícia. Após ensaio de degradação em solução cimentícia de ambas as fibras tratadas durante 10 e 20 min os resultados da espectroscopia na região do infravermelho por transformada de Fourier indicaram que o tratamento retardou o processo de degradação alcalina da hemicelulose e lignina das fibras de sisal, enquanto que para as fibras de coco verde a degradação das fibras sem tratamento foi igual ao daquelas sem com tratamento. Os ensaios mecânicos indicaram que as fibras de sisal tratadas tiveram maior resistência mecânica quando comparadas àquelas sem tratamento, e com relação às fibras de coco verde não houve diferença significativa entre fibras tratadas e sem tratamento. Além disso, não houve alteração do módulo de elasticidade das fibras de coco verde e sisal (sem tratamento e tratadas). Nesse contexto, os resultados obtidos indicaram que o tratamento com plasma frio de metano é eficaz para redução da hidrofilicidade da superfície das fibras de sisal, podendo vir a ser um tratamento promissor para minimizar a degradação alcalina da hemicelulose e lignina. / Among the studied plant fibres as reinforcement for the production of cement composites, green coconut and sisal fibres stand out for its mechanical characteristics of industrial interest, low cost, and low density. The aim of this work is to study of the plasma functionalization of green coconut and sisal fibres with methane cold plasma, as well as the analysis of the effect of this treatment in order to reduce the hydrophilicity of natural fibres, preserving its mechanical properties and increase its durability in alkaline medium. Green coconut and sisal fibres were treated with methane cold plasma for 4, 10 and 20 min. The experiment also included fibre degradation test before and after treatment in saturated solution of Portland cement. Wettability and XPS analyses indicated that the sisal fibres treated for 10 and 20 min presented surface more hydrophobic than green coconut fibres in the same treatment condition. Pullout test was performed in the sisal fibres treated by 20 min indicating good adherence between treated fibre and cement matrix. Both kinds of fibres were submited to degradation test imersed in the cementitious solution. The FTIR results indicated that the treatment retarded the alkaline degradation of the hemicellulose and lignin from sisal fibres whereas treated green coconut fibres showed the same degradation presented by untreated ones. The mechanical tests showed that the treated sisal fibres had higher mechanical strength compared to those without treatment, and regarding green coconut fibres there was no significant difference between treated and untreated fibres. Furthermore, there was no change in the modulus of elasticity of the green coconut and sisal fibre (treated and untreated). In this context, the results indicated that treatment with cold plasma of methane is effective in reducing the excessive hydrophilicity of the surface of sisal fibres and could be a promising treatment to minimize the alkaline degradation of hemicellulose and lignin.

Compósitos de fibras naturais com matriz polimérica tem sido foco de estudos por possuírem boas propriedades mecânicas e baixo peso, o que permite sua utilização em diversos meios, incluindo ambientes hospitalares, salas de radioterapia e radiodiagnóstico. Sua grande dificuldade é a falta de afinidade dos materiais componentes, causando distanciamento da interface e baixa transferência de carga entre a matriz e o reforço. Uma alternativa podem ser os compósitos à base de fibras naturais e poliuretana derivada do óleo de mamona. A incidência de radiação pode levar à degradação do material polimérico e à alteração de suas propriedades mecânicas. O objetivo do presente trabalho foi a obtenção e caracterização de compósitos de fibras dispersas e tecido de sisal com matriz poliuretana a base de óleo de mamona, sem adição de agentes de compatibilização, que possam ser utilizados em ambientes que recebam radiação em alta intensidade. Os compósitos foram obtidos por prensagem a frio, irradiados com radiação gama, dose de 25 kGy, e avaliados antes e após irradiação através de ensaios térmicos, de infravermelho, de superfície e mecânicos. Foi observado que pode haver afinidade química entre o material de reforço e a matriz, sendo que não foi evidenciado distanciamento da interface fibra/polímero. Os materiais obtidos podem ser considerados hidrofílicos pela análise de ângulo de contato. Foram obtidos valores máximos de tensão de flexão de 80,33 MPa e módulo elástico em flexão de 4,40 GPa para o compósito de tecido de sisal / poliuretana sem irradiação e resistência ao impacto de 13,14 kJ/m2 para o compósito de fibras dispersas de sisal após irradiação. Pode-se concluir que os materiais são adequados para utilização em salas de radioterapia e radiodiagnóstico. / Natural fiber composites with polymeric matrix has been the focus of studies by having good mechanical properties and low weight, which allows its use in various environments, including hospital, radiotherapy and radiology rooms. Its major difficulty is the lack of affinity of the component materials, causing detachment of the interface and lower load transfer between matrix and reinforcement. An alternative may be composites based on natural fibers and polyurethane derived from castor oil. The incidence of radiation can lead to degradation of polymeric material and change its mechanical properties. The objective of this study was to obtain and characterize composites of dispersed sisal fibers and sisal fabric with polyurethane matrix based on castor oil without addition of compatibilizing agents, which may be used in environments that receive radiation at high intensity. The composites were obtained by cold pressing, irradiated with gamma radiation, dose of 25 kGy, and evaluated before and after irradiation with thermal, infrared, surface and mechanical testing. It was observed that there may be chemical affinity between the reinforcing material and the matrix, since was not observed detachment from the fiber / polymer interface. The materials can be considered hydrophilic by contact angle analysis. Maximum values of bending stress of 80.33 MPa and elastic modulus in bending of 4.40 GPa for the sisal fabric / polyurethane composite without irradiation were obtained, such as impact resistance of 13.14 kJ / m2 for the dispersed sisal fibers composite after irradiation. It can be concluded that the materials are suitable for use in radiotherapy and radiology rooms.