The increase in the volume of industrial wastes and continuous production of solid waste of various kinds cause many environmental concerns. In this context, the disposal of packaging and bottles of poly(ethylene terephthalate) (PET) has become a major problem because of the little attention given to the final destination. Therefore, this research proposes a technical analysis of the use of PET waste, from primary recycling, as feedstock for textile industry. Yarns of recycled PET were compared with commercial polyester yarns through of various analysis, such as, tensile test and solidification color analysis. At the same time, scanning electron microscopy (SEM) was used to investigate the morphology of the yarns and better interpretation of results. It might be noted that yarns of PET recycled have satisfactory performance, although tensile strength and solidity color to light are inferior to conventional polyester yarns. / O aumento no volume de rejeitos industriais e a contínua produção de resíduos de naturezas diversas causam muitas preocupações no âmbito ambiental. Neste contexto, o descarte de embalagens e garrafas de poli(tereftalato de etileno) (PET) tem se tornado um grande problema por conta da pequena atenção que se dá à sua destinação final. Assim sendo, essa pesquisa propõe a análise técnica da utilização de resíduos de PET, oriundos de reciclagem primária, como matéria-prima para a indústria têxtil. Fios de PET reciclado foram comparados aos fios comerciais de poliéster através de diversos ensaios como, por exemplo, resistência à tração e ensaios para solidificação da cor. Ao mesmo tempo, a microscopia eletrônica de varredura (MEV) foi usada para a investigação da morfologia dos fios e melhor interpretação dos resultados. Pôde ser verificado que os fios de PET reciclado apresentam satisfatório desempenho, embora a resistência mecânica e a solidez a cor à luz sejam inferiores àquelas dos fios convencionais de poliéster.

The increase in the volume of industrial wastes and continuous production of solid waste of various kinds cause many environmental concerns. In this context, the disposal of packaging and bottles of poly(ethylene terephthalate) (PET) has become a major problem because of the little attention given to the final destination. Therefore, this research proposes a technical analysis of the use of PET waste, from primary recycling, as feedstock for textile industry. Yarns of recycled PET were compared with commercial polyester yarns through of various analysis, such as, tensile test and solidification color analysis. At the same time, scanning electron microscopy (SEM) was used to investigate the morphology of the yarns and better interpretation of results. It might be noted that yarns of PET recycled have satisfactory performance, although tensile strength and solidity color to light are inferior to conventional polyester yarns. / O aumento no volume de rejeitos industriais e a contínua produção de resíduos de naturezas diversas causam muitas preocupações no âmbito ambiental. Neste contexto, o descarte de embalagens e garrafas de poli(tereftalato de etileno) (PET) tem se tornado um grande problema por conta da pequena atenção que se dá à sua destinação final. Assim sendo, essa pesquisa propõe a análise técnica da utilização de resíduos de PET, oriundos de reciclagem primária, como matéria-prima para a indústria têxtil. Fios de PET reciclado foram comparados aos fios comerciais de poliéster através de diversos ensaios como, por exemplo, resistência à tração e ensaios para solidificação da cor. Ao mesmo tempo, a microscopia eletrônica de varredura (MEV) foi usada para a investigação da morfologia dos fios e melhor interpretação dos resultados. Pôde ser verificado que os fios de PET reciclado apresentam satisfatório desempenho, embora a resistência mecânica e a solidez a cor à luz sejam inferiores àquelas dos fios convencionais de poliéster.

Submitted by Lucienne Costa (lucienneferreira@ufcg.edu.br) on 2018-05-09T22:57:45Z No. of bitstreams: 1 DEIVID SOUSA DE FIGUEIROA – TESE (PPGEQ) 2017.pdf: 3775696 bytes, checksum: fa41c967cc6e968469d644b18254cfe7 (MD5) / Made available in DSpace on 2018-05-09T22:57:45Z (GMT). No. of bitstreams: 1 DEIVID SOUSA DE FIGUEIROA – TESE (PPGEQ) 2017.pdf: 3775696 bytes, checksum: fa41c967cc6e968469d644b18254cfe7 (MD5) Previous issue date: 2017-02-20 / Capes / A etapa de pré-tratamentos (físicos, químicos e combinados) aplicados a biomassa vegetal vem sendo considerada determinante no tocante a potencialização do rendimento de produtos químicos de alto valor agregado e de subprodutos que são obtidos a partir do refino de materiais lignocelulósicos. Uma planta promissora para ser utilizada como substrato em biorrefinarias é o sisal, pois possui 90 % de açúcares fermentáveis e 10 % a mais de celulose que a cana-de-açúcar, além do que o Brasil é o maior produtor de sisal do mundo, sendo o seu bagaço obtido durante sua manufatura e descartado no campo, sem aplicações tecnologias desenvolvidas para seu melhor aproveitamento. Dentre os métodos utilizados para pré-tratar biomassas estão os que fazem uso de agentes ácidos, alcalinos e oxidantes. Nesse contexto visando realizar um pré-tratamento efetivo no bagaço do sisal, foram aplicados pré-tratamentos nesta biomassa objetivando a desconstrução da barreira promovida pela recalcitrância inerente aos vegetais. Esses pré-tratamentos tem por finalidade a remoção da lignina, solubilização da hemicelulose e exposição da celulose. Neste trabalho foram avaliados pré-tratamentos ácido (H2SO4) com concentração ácida a 1% temperatura 120ºC por 1h , alcalino (NaOH) com concentração alcalina a 4% temperatura 120ºC por 1h e oxidante (Fenton) com concentrações de FeSO4 e H2O2 4,25 e 5000 mmol, respectivamente por 1h no bagaço do sisal. Para a determinação das condições ótimas para os pré-tratamentos aplicados, a biomassa submetida ao tratamento combinado (ácido-base) foi hidrolisada através de enzimas comerciais Celluclast 1.5L da Novozyme e beta-glicosidase da Proenzyme, obtendo rendimento de 23.561 mg.L-1 de glicose, para o pré-tratamento Fenton realizou-se o processo de hidrólise fazendo uso do tempo ótimo de 36 h obtendo-se a concentração de 4987,28 mg.L-1 de glicose . Para a avaliação dos pré-tratamentos e da hidrólise enzimática realizou-se a aplicação de planejamentos experimentais fatoriais. As biomassas foram caracterizadas através de protocolo físico-químico (Embrapa 236) e de técnicas instrumentais (TG/DTG e DRX) antes e depois da aplicação dos pré-tratamentos, o que evidenciou as mudanças estruturais causadas pelos mesmos. / The pre-treatment step (physical, chemical and combined) applied to plant biomass has been considered a determinant in the potentialization of the yield of high value-added chemical products and by-products that are obtained from the refining of lignocellulosic materials. A promising plant to be used as a substrate in biorefineries is sisal, as it has 90% fermentable sugars and 10% more cellulose than sugarcane, in addition to which Brazil is the largest sisal producer in the world, Being its bagasse obtained during its manufacture and discarded in the field, without applications technologies developed for its better use. Among the methods used to pre-treat biomass are those that use acid, alkaline and oxidizing agents. In this context, in order to perform an effective pretreatment in the sisal bagasse, pre-treatments were applied in this biomass aiming at the deconstruction of the barrier promoted by the recalcitrance inherent to the plants. These pre-treatments have the purpose of lignin removal, hemicellulose solubilization and cellulose exposure. In this work, acid (H2SO4) pre-treated with 1% acid concentration at 120ºC for 1h, alkaline (NaOH) with 4% alkaline concentration at 120ºC for 1h and oxidant (Fenton) with FeSO4 and H2O2 concentrations 4,25 And 5000 mmol, respectively for 1 h in the sisal bagasse. To determine the optimum conditions for the pre-treatments applied, the biomass submitted to the combined treatment (acid-base) was hydrolyzed through the commercial enzymes Celluclast 1.5L of Novozyme and beta-glucosidase of Proenzyme, obtaining a yield of 23,561 mg.L-1 of glucose, for the Fenton pretreatment the hydrolysis process was carried out using the optimum time of 36 h obtaining the concentration of 4987.28 mg.L-1 of glucose. For the evaluation of the pre-treatments and the enzymatic hydrolysis, the experimental factorial designs were applied. For the evaluation of the pre-treatments and the enzymatic hydrolysis, the experimental design was applied to the factorial. The biomasses were characterized by physical-chemical protocol (Embrapa 236) and instrumental techniques (TG / DTG and XRD) before and after of the pre-treatments, which evidenced the structural changes caused by them.

Made available in DSpace on 2015-09-25T12:20:41Z (GMT). No. of bitstreams: 1 PDF - Crislanne Lemos Viriato.pdf: 999955 bytes, checksum: d188456a9fec81608ef06cc2348919f2 (MD5) Previous issue date: 2013-03-28 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / One of the great problems of our time is associated with increased generation of municipal solid waste (MSW) from human activities, these arising, among other factors, industrialization and rapid growth of urban centers. In Brazil are daily collected about 260 tons of MSW, and due to lack of proper management, such waste is improperly discarded into the environment, which has about 50.8% disposal in dumps (IBGE, 2008). The MSW is constituted by about 50 to 60% of organic solid waste (RSO), which undergoes biodegradation organic material leached and generating greenhouse gases, contaminated soil, water and air. In this sense, it becomes necessary to apply methods which can be used as alternatives for treatment. One alternative that has been highlighted within the RSO treatment is anaerobic digestion to generate biogas, which is considered as a renewable energy source. Some factors may influence the efficiency of anaerobic biostabilization, including the particle size of the substrate and the concentration of total solids in the waste to be treated. This study aimed to evaluate the behavior of the RSO in biostabilization anaerobic batch anaerobic reactors (RAB), analyzing the influence of particle size and concentration of total solids in ambient temperature conditions. The experimental system was installed and monitored in physical dependencies Experiment Station Biological Sewage Treatment (EXTRABES) State University of Paraíba (UEPB), Campina Grande-PB, Northeast Brazil (7° 13´11˝ S, 35° 52´´31´). The substrates used to fuel the reactors were prepared from the mixture of solid vegetable (RSV) crushed anaerobic sludge and sewage coming from UASB (ratio of 80% to 20% of RSV sludge wet basis). The particle sizes of substrates were determined by the aperture size of the mesh sieves which the mixture was passed. Due to be analyzed the influence of two factors, each with three levels, nine different treatments were applied, and be performed in triplicate, totaled twenty and seven-RAB, with unit volume capacity of 2 liters, reserved 25% of this volume for the head-space. Quantification of the amount of biogas was performed daily with the aid of a manometer tube "U". After 200 days of monitoring the reactors were partially unloaded and substrates bioestabilizados subjected to physicochemical characterization. The results showed that among the conditions studied, the best treatment that favored the anaerobic biostabilization went to the substrate with smaller particle size (1.68 mm) and lower total solids (29.25 GST / L), yielding efficiency 37,77% removal of DQOapl, 37,49% and 32,60% of STV TKN and an average rate of approximately 17mL of biogas biogas/gDQOapl. / Um dos grandes problemas da atualidade está associado ao aumento da geração de resíduos sólidos urbanos (RSU), oriundos das atividades humanas, estes originados, dentre outros fatores, da industrialização e do crescimento acelerado dos centros urbanos. No Brasil são coletados diariamente cerca de 260 mil toneladas de RSU, e devido a falta de gerenciamento adequado, tais resíduos são descartados inadequadamente no meio ambiente, onde cerca de 50,8% tem destinação final em vazadouros (IBGE, 2008). Os RSU são constituídos por cerca de 50 a 60% de resíduos sólidos orgânicos (RSO), matéria orgânica que sofre biodegradação gerando lixiviado e gases estufas, contamina ndo o solo, a água e o ar. Neste sentido, faz-se necessário a aplicação de métodos que possam ser utilizados como alternativas de tratamento. Uma das alternativas que vem se destacando, no âmbito do tratamento de RSO é a digestão anaeróbia por gerar biogás, considerado como fonte de energia renovável. Alguns fatores podem influenciar na eficiência do processo de bioestabilização anaeróbia, dentre eles a granulometria do substrato e a concentração de sólidos totais presentes nos resíduos a serem tratados. Este estudo teve como objetivo avaliar o comportamento da bioestabilização anaeróbia dos RSO em reatores anaeróbios em batelada (RAB), analisando a influência da granulometria e da concentração de sólidos totais nas condições de temperatura ambiente. O sistema experimental foi instalado e monitorado nas dependências físicas da Estação Experimental de Tratamentos Biológicos de Esgotos Sanitários (EXTRABES) da Universidade Estadual da Paraíba (UEPB), Campina Grande-PB, Nordeste do Brasil (7° 13΄11˝ S, 35° 52΄31˝ O). Os substratos utilizados para alimentar os reatores foram preparados a partir da mistura de resíduos sólidos vegetais (RSV) triturados e lodo anaeróbio de esgoto sanitário oriundo de reator UASB (proporção de 80 % de RSV para 20 % de lodo em base úmida). As granulometrias dos substratos foram determinadas pelo tamanho da abertura de malha das peneiras as quais a mistura foi passada. Devido ser analisadas a influência de dois fatores, com três níveis cada, nove diferentes condições de tratamentos foram aplicadas, e por serem realizadas em triplicata, totalizou-se vinte e sete RAB, com capacidade volumétrica unitária de 2 litros, sendo reservados 25% deste volume para o head -space. A quantificação do volume de biogás foi realizada diariamente com o auxílio de um Manômetro de tubo em U . Após 200 dias de monitoramento os reatores foram descarregados e os subst ratos parcialmente bioestabilizados submetidos a caracterização físico -química. Os resultados apontaram que, dentre as condições estudadas, o tratamento que melhor favoreceu o processo de bioestabilização anaeróbia foi para o substrato com menor granulomet ria (1,68mm) e menor concentração de sólidos totais (29,25gST/L), obtendo -se eficiência de remoção de 37,77% de DQOapl, 37,49% de STV e 32,60% de NTK, com taxa média aproximada de biogás de 17mL de biogás/gDQO apl.

Fundação de Amparo a Pesquisa do Estado de Minas Gerais / Este trabalho apresenta o desenvolvimento de técnicas hidrometalúrgicos para o tratamento de licores gerados a partir de resíduos industriais da metalurgia extrativa do zinco. Um dos licores (ZnCu) contém teores significativos de zinco e cobre (29,6 g/L Zn e 37,4 g/L Cu) e o outro licor (ZnCd) contém elevados teores de zinco e cádmio (141 g/L Zn e 53,4 g/L Cd). A recuperação dos metais Zn e Cd, a partir da amostra ZnCd, foi realizada pela técnica de cementação. As variáveis de processo investigadas foram: temperatura, pH inicial do licor, tempo de reação e o excesso de pó de zinco metálico. Após a definição das melhores condições, foi obtida uma solução de sulfato de zinco com teor de 150 g/L de Zn e 0,005 g/L de Cd, passível de alimentar a etapa de eletrólise para a obtenção do zinco metálico. O cádmio metálico obtido apresentou pureza superior a 90% com uma recuperação de 99,9%. No estudo com a amostra ZnCu utilizou-se a técnica de extração por solventes (extração líquido-líquido). Foram realizados experimentos descontínuos e contínuos. Nos experimentos descontínuos, investigou-se as seguintes variáveis de processo: tipo e concentração do agente extratante, acidez da fase aquosa, relação volumétrica entre as fases e concentração do agente reextratante (solução de ácido sulfúrico). Os experimentos foram realizados em temperatura ambiente, (25 2oC) e velocidade de agitação de 500 rotações por minuto (rpm). Foram testados seis extratantes trocadores catiônicos. Três da classe dos extratantes ácidos (D2EHPA, IONQUEST801 e CYANEX272) e três da classe dos extratantes quelantes (LIX63, LIX984N e LIX612N-LV). Todos os extratantes apresentaram elevados fatores de separação, indicando alta potencialidade de obtenção dos metais zinco e cobre, separadamente, em elevada pureza. Com os extratantes D2EHPA, IONQUEST e CYANEX, os fatores de separação Zn/Cu foram 296, 323 e 361, respectivamente. Com o LIX612N-LV, obteve-se um fator de separação Cu/Zn 94, enquanto para o LIX63 e o LIX984N este fator foi de 62 e 37, respectivamente. Dentre os extratantes testados, foi selecionado o D2EHPA para o estudo das variáveis de processo e realização dos experimentos contínuos. O melhor resultado foi obtido com o D2EHPA 1 mol/L em pH de equilíbrio próximo de 2, em uma relação de fases A/O igual a 1 e tempo de contato de 10 minutos. Os ensaios de reextração foram realizados com solução de H2SO4. Os resultados mostraram que o cobre co-extraído, juntamente com o zinco, pode ser removido da fase orgânica através de uma etapa de lavagem utilizando solução diluída de ácido sulfúrico e o zinco reextraído com uma solução de H2SO4 mais concentrada (2 mol/L). Depois de selecionadas as melhores condições de processo, foram realizados cinco ensaios contínuos, até se atingir a condição ótima de separação dos metais Zn e Cu. Os experimentos de 1 a 4 foram realizados com uma solução preparada no laboratório, simulando o licor industrial. O experimento contínuo 5 foi realizado com a solução original, gerada na lixiviação do resíduo industrial, contendo 29,6 g/L Zn, 37,4 g/L Cu, 1,94 g/L Cd, 0,127 g/L Co e 0,100 g/L Ni. O experimento foi realizado nas mesmas condições operacionais do experimento 4, onde foi obtido o melhor resultado. O circuito de extração constou de 3 estágios de extração, 3 estágios de lavagem e 5 estágios de reextração. Neste experimento foi obtido um reextrato com 125 g/L Zn, 0,05 g/L Cu e teores de Cd, Co e Ni menores que 0,005 g/L. A concentração dos metais no rafinado foi de 28,6 g/L Cu, 0,49 g/L Zn, 1,48 g/L Cd, 0,080 g/L Ni e 0,098 g/L Co. / This paper presents a development of hydrometallurgic techniques for the treatment of liquors obtained from industrial residues generated in the zinc extractive metallurgy. One of the liquors (ZnCu) contains significant amounts of zinc and copper (29.6 g/L zn and 37.4 g/L Cu) and the other (ZnCd) containing high levels of zinc and cadmium (141 g/L Zn and 53.4 g/L Cd). The recovery of the Zn and Cd metals from the ZnCd sample was carried out using the cementation technique. The process variables investigated were: temperature, initial pH of the liquor, reaction time and the metallic zinc powder excess. After establishing the best conditions, a zinc sulphate solution containing 150 g/L of Zn and 0.005 g/L of Cd was obtained. This solution is capable of feeding the electrolysis stage in order to obtain metallic zinc. The level of purity of the metallic cadmium obtained by the cementation technique was higher than 90%, and the recovery rate was 99.9%. The separation of zinc and copper from the ZnCu sample was carried out using the solvent extraction technique. Non-continuous and continuous experiments were done. In the non-continuous experiment, the following process variables were investigated: type and concentration of the extractants, acidity of the aqueous phase, volume relation between the phases and the stripping agent concentration (sulphur acid solution). The experiments were carried out in a room temperature (25 2oC), and with an agitation of 500 rpm. Six cationic extractants were investigated - three acid extractants (D2EHPA, IONQUEST801 and CYANEX272) as well as three chelating extractants (LIX63, LIX984N and LIX612N-LV). All extractants presented a high separation factor and could be used in the separation process. The Zn/Cu separation factor obtained with D2EHPA, IONQUEST and CYANEX was 296, 323 and 361 respectively. The Cu/Zn separation factor obtained with LIX612N-LV was 94, whereas the one obtained for LIX63 and LIX984N was 62 and 37 respectively. Amongst the extractants tested, the D2EHPA was the one selected for the study of the variables of this process. The best result was attained with the D2EHPA 1 mol/L at an equilibrium pH near 2, and contact time of 10 minutes. The metal stripping was carried out with H2SO4. The results showed that the co-extracted copper may be scrubbed from the organic phase through a diluted sulphuric acid solution, and the zinc can be stripped with a more concentrated H2SO4 solution (2mol/L). Fifth continuous experiments were realized until an optimal condition for the separation of the metals Zn and Cu was achieved. The experiments from 1 to 4 were carried out with a solution prepared in a laboratory simulating the industrial liquor. Experiment 5, was carried out with the industrial liquor, in the same conditions of the experiment 4, which presented the best results. It was carried out in three extraction stages, three scrubbing stages and 5 stripping stages. In this experiment, a pregnant strip solution containing 125 g/L Zn, and 0.050 g/L Cu, with less than 0.005 g/L Cd, Co and Ni, from a solution containing 29.6 g/L Zn, 37.4 g/L Cu, 1.94 g/L Cd, 0.127 g/L Co and 0.100 g/L Ni was obtained. The concentration of the metals in the raffinate was 28.6 g/L Cu, 0.49 g/L Zn, 1.48 g/L Cd, 0.080 g/L Ni and 0.098 g/L Co.

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Atualmente grande parte dos resíduos descartados rotineiramente no Brasil é composta por material plástico como, por exemplo, o polietileno de alta densidade (PEAD), o qual é muito comum no lixo doméstico. Nesta Dissertação, embalagens de PEAD pós-consumo foram coletadas e moídas. Após processamento em extrusora, o material definido como PEAD reciclado (mistura de embalagens brancas, marfins e incolores) foi injetado e as propriedades mecânicas foram avaliadas e comparadas com uma amostra de PEAD comercial (HD7600U). A análise térmica através da calorimetria exploratória diferencial (DSC), em conjunto com a análise estatística dos resultados experimentais, também foi conduzida. Em relação à resistência à tração, a diferença entre as amostras de PEAD reciclado e PEAD comercial foram tão pouco expressivas que, dentro das condições experimentais adotadas, se pode afirmar que o material reciclado é equivalente ao comercial.Por sua vez, os modelos cinéticos aplicados na análise térmica revelaram quea amostra de PEAD comercial demonstra um processo de nucleação e crescimento dos cristais mais homogêneo e simples, embora a energia de ativação seja consideravelmente maior do que o das demais amostras de PEAD. / Currently a large part of the waste routinely discarded in Brazil is composed of plastic material such as, for example, high density polyethylene (HDPE), which is very common in household waste. In this thesis, HDPE post-consumer packaging were collected and ground. After processing in the extruder, the material defined as recycled HDPE (mixture of white containers, ivory and colorless) was injected and the mechanical properties were evaluated and compared with commercial HDPE sample (HD7600U). Thermal analysis by differential scanning calorimetry (DSC), together with the statistical analysis of the experimental results was also conducted. Regarding the tensile strength, the difference between the samples of recycled HDPE and commercial HDPE were so insignificant that within the adopted experimental conditions, it can be said that the recycled material is equivalent to commercial. In turn, the kinetic models applied to the thermal analysis showed that the sample of commercial HDPE shows a process of nucleation and growth of single crystals and more homogeneous, while the activation energy is significantly higher than the other samples of HDPE.

Made available in DSpace on 2015-03-26T13:28:30Z (GMT). No. of bitstreams: 1 texto completo.pdf: 402091 bytes, checksum: c86b326d507251f55728ecbdac152bce (MD5) Previous issue date: 2007-02-15 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Bleached kraft pulp and textile effluents contain hard to degrade and, or toxic substances, and these industries often cannot meet legal limits for effluent chemical oxygen demand using conventional effluent treatment. Use of advanced oxidation processes (AOPs) is therefore being studied to treat their effluents. AOPs use a strong oxidizing agent to degrade organic matter but present high cost and data on their application in industrial effluents is lacking. The objective of this study was therefore to evaluate efficiency of combining AOPs (TiO2/UV, H2O2/UV, H2O2/TiO2/UV) with aerobic biological treatment to increase removal of recalcitrant organic matter in industrial effluents. Neither pretreatment of alkaline bleached kraft pulp effluent nor post-treatment of combined bleached kraft pulp effluent by the AOPs resulted in increased effluent biodegradability probably because of high effluent chloride levels. Under the conditions studied, the AOPs were not able to attack and degrade the recalcitrant organic matter in the kraft pulp effluent, contrary to literature reports. However, AOP treatment of acid bleached kraft pulp effluent should be evaluated since a beneficial effect of the AOPs was observed at low effluent pH. Pretreatment of textile effluent presented favorable results with the best treatment being 5 mmol L-1 H2O2/TiO2/UV. However, the efficiency of the process decreased with the increase in concentration of organic matter in the raw effluent. Even after aerobic biological treatment to reduce COD (755 mg L-1), satisfactory results were not obtained. For the textile effluent, the effect of COD concentration on AOP efficiency should be studied in greater detail since these processes present potential as a pretreatment. / Os efluentes das indústrias de celulose kraft branqueada e têxtil contêm substâncias de difícil degradação e, ou tóxicas. Estas indústrias, através de tratamentos convencionais não conseguem atingir a legislação com relação à demanda química de oxigênio. Devido a este fato, estuda-se o uso de processos oxidativos avançados (POAs) para tratar estes efluentes. Os POAs são processos que utilizam um oxidante forte para degradar a matéria orgânica, no entanto, apresentam altos custos, faltando dados de sua aplicação em efluentes reais. Portanto, o objetivo deste trabalho foi avaliar a eficiência dos POAs no tratamento de efluentes reais, juntamente com o tratamento biológico para aumentar a remoção da matéria orgânica recalcitrante. Para o efluente de celulose kraft, os POAs, tanto no pré-tratamento do efluente alcalino como no pós-tratamento do efluente combinado, não resultaram em aumento da biodegradabilidade, provavelmente devido ao alto teor de cloretos no efluente. Contudo, recomenda-se que se faça um estudo com o efluente ácido já que se observou um efeito benéfico de realizar o pré-tratamento oxidativo em pH baixo. Portanto, nas condições estudadas os POAs não conseguiram atacar a matéria orgânica recalcitrante nos efluentes da indústria de celulose, ao contrário dos relatos encontrados na literatura. O efluente têxtil apresentou resultados favoráveis no pré-tratamento, com o melhor tratamento sendo com 5 mmol L-1 H2O2/TiO2/UV. Porém, a eficiência do processo diminuiu com o aumento da concentração da matéria orgânica no efluente bruto. Mesmo após o tratamento biológico aeróbio no laboratório para reduzir a DQO (DQO = 755 mg L-1) não foi obtido um resultado satisfatório. Para o efluente têxtil, recomenda-se estudar mais detalhadamente o efeito da concentração de DQO do efluente sobre os POAs, uma vez que os mesmos apresentam potencial como pré-tratamento.

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Atualmente grande parte dos resíduos descartados rotineiramente no Brasil é composta por material plástico como, por exemplo, o polietileno de alta densidade (PEAD), o qual é muito comum no lixo doméstico. Nesta Dissertação, embalagens de PEAD pós-consumo foram coletadas e moídas. Após processamento em extrusora, o material definido como PEAD reciclado (mistura de embalagens brancas, marfins e incolores) foi injetado e as propriedades mecânicas foram avaliadas e comparadas com uma amostra de PEAD comercial (HD7600U). A análise térmica através da calorimetria exploratória diferencial (DSC), em conjunto com a análise estatística dos resultados experimentais, também foi conduzida. Em relação à resistência à tração, a diferença entre as amostras de PEAD reciclado e PEAD comercial foram tão pouco expressivas que, dentro das condições experimentais adotadas, se pode afirmar que o material reciclado é equivalente ao comercial.Por sua vez, os modelos cinéticos aplicados na análise térmica revelaram quea amostra de PEAD comercial demonstra um processo de nucleação e crescimento dos cristais mais homogêneo e simples, embora a energia de ativação seja consideravelmente maior do que o das demais amostras de PEAD. / Currently a large part of the waste routinely discarded in Brazil is composed of plastic material such as, for example, high density polyethylene (HDPE), which is very common in household waste. In this thesis, HDPE post-consumer packaging were collected and ground. After processing in the extruder, the material defined as recycled HDPE (mixture of white containers, ivory and colorless) was injected and the mechanical properties were evaluated and compared with commercial HDPE sample (HD7600U). Thermal analysis by differential scanning calorimetry (DSC), together with the statistical analysis of the experimental results was also conducted. Regarding the tensile strength, the difference between the samples of recycled HDPE and commercial HDPE were so insignificant that within the adopted experimental conditions, it can be said that the recycled material is equivalent to commercial. In turn, the kinetic models applied to the thermal analysis showed that the sample of commercial HDPE shows a process of nucleation and growth of single crystals and more homogeneous, while the activation energy is significantly higher than the other samples of HDPE.

Submitted by Fabielle Cheuczuk (fabielle.cheuczuk@unioeste.br) on 2017-09-01T17:41:53Z No. of bitstreams: 2 Tainara_Bruna_Montagna_2017.pdf: 2224704 bytes, checksum: 611557170f0bccd30bb9aa2430a5d3f7 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2017-09-01T17:41:53Z (GMT). No. of bitstreams: 2 Tainara_Bruna_Montagna_2017.pdf: 2224704 bytes, checksum: 611557170f0bccd30bb9aa2430a5d3f7 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2017-02-23 / In the last decades, the Brazilian farming industry has undergone great changes regarding the systems, type and scale of production, predominantly large-scale vertical production. This growth has been a matter of concern, especially when it comes to environmental issues, because when these production systems are poorly designed or poorly conducted, they generate large amounts of waste, which due to lack of control are often released into water bodies or applied as agricultural fertilizers in large quantities and can pollute surface and groundwater. The correct management of pig and poultry waste is a major challenge that the regions of intensive production of pigs and poultry will have to face in the coming years, due to problems of water pollution, storage costs, treatment and utilization of manure as organic fertilizer in agriculture. The purpose of this work is to present the characterization and main impacts on the environment, as well as some techniques for treatment, disposal and reuse of pig and poultry waste in rural establishments that work with a small production scale. This survey was based on the bibliographical analysis of articles, booklets, dissertations, theses, books, besides specific laws and decrees on the subject. It is possible to conclude that, for poultry farming, deep bedding has been presented as the best alternative for storage, provided that it is properly treated. For pig farming, waste ponds have been widely used, but it is necessary to monitor these residues in order to avoid overflows to soils and water bodies. In terms of treatment techniques, it is highlighted the composting and the use of biogas for the two types of wastes analyzed. In the case of swine manure, stabilization ponds are also fundamental, because these residues are not very solid. There are other more advanced treatment techniques, but as the focus of the dissertation was on small plants, it was sought to analyze the cost-benefit of the techniques raised. / Nas últimas décadas, a agropecuária brasileira tem passado por grandes mudanças no que se refere aos sistemas, tipo e escala de produção, predominando a produção vertical em grande escala. Esse crescimento tem sido alvo de preocupação, principalmente, no que se refere às questões ambientais, pois quando esses sistemas de produção são mal projetados ou mal conduzidos, geram grandes quantidades de resíduos, que pela falta de controle, muitas vezes, são lançados em corpos hídricos ou aplicados como fertilizantes agrícolas em grandes quantidades, podendo poluir águas superficiais e subterrâneas. O correto manejo dos dejetos de suínos e de resíduos de avicultura é um grande desafio que as regiões de produção intensiva de suínos e aves terão que enfrentar nos próximos anos, em função dos problemas de poluição das águas, dos custos de armazenamento, tratamento e, aproveitamento dos dejetos como adubo orgânico na agricultura. A proposta deste trabalho é de apresentar a caracterização e os principais impactos no meio ambiente, bem como algumas técnicas de tratamento, destinação e reaproveitamentos dos dejetos de suínos e aves em estabelecimentos rurais que trabalham com uma pequena escala produtiva de produção. Tal levantamento se deu a partir da análise bibliográfica de artigos, cartilhas, dissertações, teses, livros, além de leis e decretos específicos sobre o tema. É possível concluir que, para a avicultura, a cama sobreposta tem se apresentado como melhor alternativa para o armazenamento, desde que devidamente tratada. Já para a suinocultura, as esterqueiras tem sido amplamente utilizadas, porém faz-se necessário um monitoramento destes resíduos com o intuito de evitar transbordamentos para solos e corpos hídricos. Em termos de técnicas de tratamento, destacam-se a compostagem e o uso de biogás para os dois tipos de dejetos analisados. No caso dos dejetos de suínos, as lagoas de estabilização também são fundamentais, em virtude destes resíduos serem pouco sólidos. Existem outras técnicas de tratamento mais avançadas, porém como o foco da dissertação esteve em pequenos plantéis, procurou-se analisar a relação custo-benefício das técnicas levantadas.

Submitted by Edisangela Bastos (edisangela@ufpa.br) on 2013-07-01T22:18:20Z No. of bitstreams: 2 license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5) Tese_EstudoAvaliacaoUso.pdf: 10721559 bytes, checksum: 776cb6f028a953bd6df65c698c045f19 (MD5) / Approved for entry into archive by Irvana Coutinho(irvana@ufpa.br) on 2013-07-02T12:44:39Z (GMT) No. of bitstreams: 2 license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5) Tese_EstudoAvaliacaoUso.pdf: 10721559 bytes, checksum: 776cb6f028a953bd6df65c698c045f19 (MD5) / Made available in DSpace on 2013-07-02T12:44:39Z (GMT). No. of bitstreams: 2 license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5) Tese_EstudoAvaliacaoUso.pdf: 10721559 bytes, checksum: 776cb6f028a953bd6df65c698c045f19 (MD5) Previous issue date: 2010-03 / A grande quantidade de resíduos sólidos, oriundos da indústria de mineração e metalurgia, constitui um sério problema sócio-ambiental. As características físicoquímicas destes resíduos despertam grande interesse para outras indústrias. A indústria cerâmica pode ser uma interessante consumidora da maioria deste material, para suprir a grande escassez das reservas de matérias-primas atual. Neste contexto, este trabalho mostra os estudos realizados para a reciclagem da lama vermelha, como matéria-prima na produção de agregado sintético, visando à construção civil. A lama vermelha, principal rejeito industrial da fabricação de alumina, mostrou-se um insumo de grande interesse na fabricação de diferentes tipos de agregado para ser utilizado na produção de concreto, para a construção civil. Pelas suas características físico-químicas e a grande quantidade que é produzida anualmente (cerca de 10.000.000 t em duas fábricas, só no Norte do Brasil). Estudos realizados neste trabalho mostram a possibilidade de fabricação de agregados, com diferentes propriedades e possibilidades de aplicação, na indústria da construção civil. Estas propriedades dependem do controle de parâmetros, como o teor de sílica livre e argila, a granulometria e a temperatura de sinterização. Tais variáveis permitem controlar perfeitamente a formação de fase vítrea que é a responsável pelas propriedades dos agregados como: porosidade, resistência mecânica e densidade. Este material pode ser utilizado em concreto convencional ou em concretos especiais, para atender a demanda da construção civil. / The large amount of solid waste coming from mines and metallurgical industries became a serious social-environmental problem. The physical and chemical features of this material can raise a great interest in other industries. The ceramic industry might be a great costumer for most of this material, since it can supply the current lack of raw material. The red mud, main industrial residue of the alumina manufacturing, has been a very interesting input for several kinds of aggregates manufacturing used for the concrete production in civil engineering. In this context, this paper deals with studies concerning the red mud recycling to be applied as raw material for the synthetic light aggregate production to be used as an alternative material in the civil construction industry. This is because of its physical-chemical features and the large amount annually produced (around 10 million tons within two factories in the North of Brazil). The studies completed in this work show the feasibility of aggregates manufacturing, with different properties and possibilities. These properties depend on the parameters control such as content of free silica and clay, and the sintering temperature. Such variables allow to perfectly controlling the glassy phase formation which is responsible for the aggregate properties such as: porosity, mechanical resistance and density. This material can be used for conventional or special concretes to supply the civil engineering needs.