Made available in DSpace on 2014-10-09T12:51:15Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:06:05Z (GMT). No. of bitstreams: 1 11259.pdf: 8455233 bytes, checksum: c710358f0ad3ff6d959e43d6d7c72aad (MD5) / Tese (Doutoramento) / IPEN/T / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP

Made available in DSpace on 2014-10-09T12:41:06Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:09:09Z (GMT). No. of bitstreams: 1 04673.pdf: 4338286 bytes, checksum: 9b40b59ddc2764691461410ae0194329 (MD5) / Dissertacao (Mestrado) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP

Submitted by Maria Eneide de Souza Araujo (mearaujo@ipen.br) on 2015-10-07T12:39:18Z No. of bitstreams: 0 / Made available in DSpace on 2015-10-07T12:39:18Z (GMT). No. of bitstreams: 0 / Dissertação (Mestrado em Tecnologia Nuclear) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP

Submitted by Claudinei Pracidelli (cpracide@ipen.br) on 2015-12-17T09:09:06Z No. of bitstreams: 0 / Made available in DSpace on 2015-12-17T09:09:06Z (GMT). No. of bitstreams: 0 / Dissertação (Mestrado em Tecnologia Nuclear) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP

O objetivo deste estudo foi comparar in vitro o desgaste dental de pré-molares (PM) e molares (M) e sua relação com o valor de dureza Vickers dos materiais utilizados como antagonistas em uma máquina de abrasão simulada para provocar o desgaste nos dentes testados. Os materiais antagonistas utilizados foram VeraBond II (liga de Ni-Cr), Solidex (resina composta) e IPS Empress 2 (cerâmica). Para cada ensaio de dureza, foram preparados seis corpos-de-prova de cada material, os quais foram polidos sob refrigeração, com ciclo de 20 min para cada granulação. Num microdurômetro (HMV-2), foram realizadas três mossas por quadrante, cada uma sob carga de 19,614 N por 30 s, totalizando 12 mossas de base quadrada com ângulo de 136 entre os planos. O teste de abrasão foi realizado numa máquina simuladora de abrasão, freqüência de 265 ciclos/min e 4,4 Hz, com um percurso do antagonista de 10 mm à velocidade de 88 mm/s. Cada dente foi testado em oposição a um antagonista (foram 6 pares dente/material para cada grupo), em água deionizada, sob carga de 5 N, por 150 min, num total de 39.750 ciclos. Foram utilizados dezenove dentes 1 pré-molares, dezenove 3 molares e confeccionados doze antagonistas em cada material em forma de pastilha. Cada grupo de seis dentes foi testado em oposição a seis antagonistas do mesmo material. Ademais, um dente 1 pré-molar (PM) e um dente 3 molar (M) foram testados em oposição ao Plexiglass. Com relação ao desgaste do esmalte dentário (PM+M) segundo o material antagonista, o teste de Kruskal-Wallis evidenciou diferença significativa com p-valor < 0,001 e o teste de Mann-Whitney evidenciou diferença significativa nas comparações PM+M/resina X PM+M/metal (p-valor < 0,001), PM+M/resina X PM+M/cerâmica (p-valor < 0,001) e PM+M/metal X PM+M/cerâmica (p-valor = 0,002). A análise isolada, considerando pré-molares e molares separadamente, encontrou diferença significativa em relação ao desgaste do esmalte dentário no teste de Kruskall-Wallis, porém não detectou diferença significativa no teste de comparação múltipla Mann-Whitney quando comparou o desgaste sofrido pelo PM/metal em relação ao PM/cerâmica. Em relação à dureza Vickers detectou-se diferença significativa da dureza dos materiais no teste de Kruskall-Wallis (p-valor < 0,001) e também no teste de Mann-Whitney nas comparações múltiplas com p-valor = 0,002. Comparando-se a dureza com a perfilometria, observou-se uma correlação estatisticamente significativa (p &#8804; 0,05) na correlação negativa (&#961;= -0,829) entre a dureza do metal como material antagonista e o desgaste do esmalte dentário do dente molar. Os resultados sugeriram que todo material restaurador indireto estudado causou desgaste ao esmalte dentário quando submetido a forças de simulação de abrasão com carga. Embora tenha sido observada correlação entre dureza e resistência à abrasão, essa correlação foi pouco significativa. / The objective of this study was to compare the dental wear of pre-molars (PM) and molars (M) in vitro, and the relationship between dental wear and the Vickers hardness values of the materials used as antagonists in a machine simulating abrasion to produce wear on the teeth tested. The materials used as antagonists were VeraBond II (Ni-Cr alloy), Solidex (composite resin) and IPS Empress 2 (ceramic). Six specimens of each material were prepared for each hardness trial. The specimens were polished under refrigeration, with a 20-min cycle for each grit number. Three dents per quadrant were made in a microhardness tester (HMV-2), under a 19.614 N load for 30 s, for a total of 12 square-base dents with a 136 angle between planes. The abrasion test was performed in an abrasion-simulating machine set to a frequency of 265 cycles/min and 4,4 Hz. The course of the antagonist was 10 mm, at a speed of 88 mm/s. Each tooth was tested against an antagonist material (6 tooth/material pairs per group), in deionized water, under a 5 N load, for 150 min, for a total of 39,750 cycles. Nineteen first pre-molars (PM) and 19 third molars (M) were used, and 12 antagonistic discs were made in each material, for the tests. Each group of six teeth was tested against six antagonists of the same material. Additionally, 1 first pre-molar (PM) and one third molar (M) were tested against Plexiglass. Regarding the dental enamel wear on pre-molars and molars (PM+M) according to the antagonist material, the Kruskal-Wallis test revealed significant differences (p-value < 0.001) and the Mann-Whitney test also revealed significant differences for the following comparisons: PM+M/resin versus PM+M/metal (p-value < 0.001), PM+M/resin versus PM+M/ceramic (p-value < 0.001), and PM+M/metal versus PM+M/ceramic (p-value = 0.002). An analysis conducted with the Kruskall-Wallis test, considering pre-molars (PM) and molars (M) separately, found significant differences in relation to dental enamel wear (PM+M). However, when the multiple-comparison Mann-Whitney test was used, no significant difference was detected between the wear produced in the pre-molar/metal pair and that produced in the pre-molar/ceramic pair. Regarding Vickers hardness, both the Kruskall-Wallis test (p-value < 0.001) and Mann-Whitneys multiple-comparisons test (p-value = 0.002) revealed significant differences between materials. When hardness was compared with the profilometry data, a significant negative correlation was observed (p &#8804; 0.05, &#961; = -0.829) between the hardness of the metal as an antagonist material and the dental enamel wear of the molar tooth. The results suggested that all the indirect restorative materials tested caused wear of the dental enamel when submitted to the forces of simulated abrasion with load. Although a correlation was observed between hardness and resistance to abrasion, this correlation was hardly significant.

Made available in DSpace on 2014-10-09T12:28:54Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T13:57:01Z (GMT). No. of bitstreams: 0 / Um dos mais críticos problemas encontrados na união de materiais distintos é a formação de tensões residuais, que ocorre principalmente pelo fato desses materiais possuírem coeficientes de expansão térmica e condutividades térmicas diferentes. Neste trabalho foi estudada a técnica de soldagem laser entre o aço carbono AISI 1010 e o aço inoxidável AISI 304. Os materiais foram unidos por solda autógena de topo com um laser de Nd:YAG contínuo. O principal objetivo do estudo foi a identificação da influência dos parâmetros de soldagem, pela análise das tensões residuais na zona termicamente afetada (ZTA). Foi executado um planejamento fatorial de três fatores a dois níveis com uma réplica, em que foram variadas a potência, a velocidade de soldagem e a posição focal do feixe laser. Na superfície da amostra foram realizadas medidas de tensão residual pela técnica de difração de raios X, para estudar sua variação em função dos parâmetros investigados. O método do furo cego foi também utilizado para avaliar a tensão residual ao longo da profundidade das amostras até a profundidade de 1 mm. Além das medidas de tensão residual, os cordões de solda foram avaliados por microscopia óptica e eletrônica de varredura (MEV), que tiveram como objetivos determinar a geometria do cordão e mudanças na microestrutura, também foram feitas medidas de microdureza Vickers para se avaliar a extensão da ZTA. Para se avaliar as propriedades mecânicas da união foram realizados ensaios de tração e fadiga. O software MINITAB 15 foi utilizado para a análise das tensões residuais nas diferentes profundidades da ZTA obtidas pelo método do furo cego. Foi utilizada também a regressão estatística baseada nas diferentes influências da entrada e combinação dos fatores na tensão residual geradas nessa união. Os resultados indicam que o desenvolvimento de modelos pode prever as respostas satisfatoriamente e fornecer aos usuários um guia para definir os melhores parâmetros de união. / Dissertacao (Mestrado) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP

Made available in DSpace on 2014-10-09T12:51:15Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:06:05Z (GMT). No. of bitstreams: 1 11259.pdf: 8455233 bytes, checksum: c710358f0ad3ff6d959e43d6d7c72aad (MD5) / Tese (Doutoramento) / IPEN/T / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP

Made available in DSpace on 2014-10-09T12:41:06Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:09:09Z (GMT). No. of bitstreams: 1 04673.pdf: 4338286 bytes, checksum: 9b40b59ddc2764691461410ae0194329 (MD5) / Dissertacao (Mestrado) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN/CNEN-SP

Submitted by Maria Eneide de Souza Araujo (mearaujo@ipen.br) on 2015-10-07T12:39:18Z No. of bitstreams: 0 / Made available in DSpace on 2015-10-07T12:39:18Z (GMT). No. of bitstreams: 0 / Neste trabalho foram realizados experimentos de soldagem de chapas de Tântalo e Monel 400 com 100 m de espessura. Foram realizadas soldas em um laser de Nd:YAG operando em modo pulsado e em um Laser de Fibra operando em modo contínuo. Em seguida a microestrutura das amostras foram analisadas através de microscopia ótica e foram realizados ensaio de microdureza Vickers. As amostras que apresentaram melhores resultados foram submetidas a ensaios de tração e a ensaios de corrosão. Após análise dos resultados observou-se que a soldagem a laser apresenta muitos benefícios em relação a outros processos convencionais para chapas finas. A soldagem no modo pulsado apresentou maior relação de aspecto se comparado a soldagem em modo contínuo. A soldagem em modo contínuo apresentou uma velocidade de soldagem muito superior ao modo pulsado. Os resultados indicaram que a soldagem no modo pulsado apresenta maior aplicabilidade para chapas finas, devido à necessidade um controle preciso sobre a intensidade aplicada. / Dissertação (Mestrado em Tecnologia Nuclear) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP

Submitted by Claudinei Pracidelli (cpracide@ipen.br) on 2015-12-17T09:09:06Z No. of bitstreams: 0 / Made available in DSpace on 2015-12-17T09:09:06Z (GMT). No. of bitstreams: 0 / Superligas de níquel são materiais mundialmente empregados nas áreas de petróleo e gás natural, aeroespacial e nuclear. A Incoloy® 945 uma liga desenvolvida em meados dos anos 2000, para ser uma liga hibrida entre a Inconel® 718 e Incoloy® 925, concebendo uma liga com propriedades mecânicas e anticorrosivas capaz de suportar as mais adversas operações de serviço. Neste trabalho foram determinadas algumas características mecânicas do material, após laminação a frio, seguindo duas diferentes rotas de tratamento térmico. Foram realizados testes de dureza Vickers e tração, onde mostrou que a rota experimental criada no IPEN (por intermédio da análise por calorimetria exploratória diferencial), tem a mesma resistência mecânica do que a rota comercialmente usada, contudo possui uma maior ductilidade. O material demonstra uma excepcional união resistência mecânica e ductilidade, podendo ser empregada no uso de tubulações e válvulas de alta complexidade de manufatura, para a exploração das camadas do pré-sal. / Dissertação (Mestrado em Tecnologia Nuclear) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP