Made available in DSpace on 2014-06-11T19:24:07Z (GMT). No. of bitstreams: 0 Previous issue date: 2013-03-18Bitstream added on 2014-06-13T19:30:40Z : No. of bitstreams: 1 cioffi_ss_me_arafo.pdf: 226725 bytes, checksum: e69424b0b101d7404c408391d46af41f (MD5) / Proposição: o presente estudo tem como objetivo avaliar a resistência à compressão de restaurações de resina composta em preparos classe II, observando o tipo de preparo que possui maior resistência à compressão permitindo obter um modelo de restauração classe II com características adequadas, garantindo a qualidade da restauração, assim como sua durabilidade. Material e método: os dentes foram divididos em cinco grupos contendo oito dentes por grupo, sendo eles; Grupo 1-controle, Grupo 2- preparo mésio-oclusal com bisel, Grupo 3- preparo mesial sem canaleta e com bisel, Grupo 4- preparo mesial com canaleta e com bisel e Grupo 5- preparo mésio-oclusal sem bisel. Resultado: os resultados obtidos mostraram que o grupo controle obteve os maiores valores porém não foi estatisticamente significante quando comparado com os Grupos 2 e 5. Conclusão: preparos com extensão para oclusal apresentam valores satisfatórios porém devemos considerar que preparos preventivos não obtiveram diferença estatística quando comparados a esses preparos podendo ser indicados em casos de lesões de cárie apenas proximais. / Objective: The present study aims to evaluate the compressive strength of composite resin restorations in Class II preparations, noting the type of preparation that has greater compressive strength allowing to obtain a Class II restoration model with appropriate characteristics, ensuring the quality of restoration, as well as its durability. Methods: The teeth were divided into five groups containing eight teeth each group; Group 1- control, Group 2- mesio-occlusal preparation with bevel; Group 3- mesial preparation without groove and with bevel; Group 4- mesial preparation with groove and bevel; Group 5- mesio-occlusal preparation without bevel. Results: The results showed that the control group had higher values but not statistically significant when compared with Groups 2 and 5. Conclusion: Preparations with occlusal extension exhibited satisfactory values but we must consider that preventive preparations did not obtain satatistical difference when compared to these preparations and may be indicated in cases of only proximal carious lesions.

Submitted by Samira Nascimento Stain null (samirastain@hotmail.com) on 2018-03-14T19:59:05Z No. of bitstreams: 1 MORAES, S.N.S. DISSERTAÇÃO-FINAL aprovada.pdf: 3124598 bytes, checksum: 2f90002ac800ae1fd2e713c1c838eff3 (MD5) / Approved for entry into archive by Ana Carolina Gonçalves Bet null (abet@iq.unesp.br) on 2018-03-19T19:09:16Z (GMT) No. of bitstreams: 1 moraes_sns_me_araiq_int.pdf: 3156975 bytes, checksum: b6848b17d6500a3a3ab853f49a4404f6 (MD5) / Made available in DSpace on 2018-03-19T19:09:16Z (GMT). No. of bitstreams: 1 moraes_sns_me_araiq_int.pdf: 3156975 bytes, checksum: b6848b17d6500a3a3ab853f49a4404f6 (MD5) Previous issue date: 2018-02-20 / Outra / O grande interesse das indústrias de embalagens de vidro está focado na redução de custos que envolvem o processo contínuo da produção dos frascos e seus impactos na produtividade. Para isso, os frascos de vidro devem estar de acordo com as necessidades do mercado consumidor. Assim, é de grande importância para esta indústria o conhecimento dos padrões de qualidade dos frascos produzidos, identificando os possíveis problemas, analisando suas origens e sanando os mesmos. Neste contexto, o presente trabalho foi baseado no estudo da melhoria do processo de conformação de frascos de vidro utilizados no armazenamento de medicamentos e perfumes, através do controle de propriedades mecânicas e ópticas. As propriedades mecânicas foram analisadas com o intuito de evitar-se a presença de trincas e fraturas, e através das propriedades ópticas avaliou-se a cor, propriedades relacionadas ao brilho e transparência, assim como os processos de oxi-redução que são responsáveis pela coloração dos vidros e bolhas. Os vidros foram caracterizados empregando-se as seguintes técnicas: espectroscopia na região do Ultravioleta-vísivel (UV-Vis), espalhamento Raman, calorimetria exploratória diferencial (DSC), microscopia óptica e perfilometria. Dentre as técnicas de caracterizações citadas anteriormente, a principal técnica utilizada neste trabalho foi a espectroscopia Raman, com a qual foi possível caracterizar e identificar as impurezas contidas nos frascos de vidro analisados. A presença de impurezas pode gerar trincas, bolhas e influenciar na coloração dos frascos, sendo estes os grandes problemas desta indústria. Através dos resultados obtidos pela espectroscopia Raman constatou-se uma diversidade de impurezas cristalinas, as quais, primeiramente, foram comparadas com uma base de dados feita a partir das matérias-primas, refratários e isolantes fornecidos pela empresa. A identificação das impurezas permitiu encontrar as possíveis fontes de impurezas na indústria, as quais estão atualmente sendo controladas para minimizar as perdas durante o processo de fabricação. / The great interest of the glass packaging industries is focused on reducing costs that involve the continuous process of bottle production and its impacts on productivity. For this, the glass jars must conform to the needs of the consumer market. Thus, it is of great importance for this industry the knowledge the quality standards of the bottles produced, identifying the possible problems, analyzing its origins and healing them. In this context, the present work was based on the study of the improvement of the process of conformation of glass bottles used in the storage of medicines and fragrances, through the control of mechanical and optical properties. The mechanical properties were analyzed in order to avoid the presence of cracks and fractures, and the optical properties were used to evaluate the color, properties related to brightness and transparency, as well as the oxi-reduction processes that are responsible for the color of glasses and bubbles. Glasses were characterized using the following techniques: ultraviolet-visible (UV-Vis) spectroscopy, Raman scattering, differential scanning calorimetry (DSC), optical microscopy and profilometry. Among the characterization techniques mentioned above, the main technique used in this work was Raman spectroscopy, with which it was possible to characterize and identify the impurities contained in the analyzed glass bottles. The presence of impurities can generate cracks, bubbles and influence the coloring of the jars, these being the major problems of this industry. The results obtained by Raman spectroscopy revealed a diversity of crystalline impurities, which were first compared to a database made from the raw materials, refractories and insulatings provided by the company. The identification of the impurities allowed to find the possible sources of impurities in the industry, which are currently being controlled to minimize losses during the manufacturing process.

Made available in DSpace on 2015-04-01T12:17:41Z (GMT). No. of bitstreams: 1 arquivototal.pdf: 2182019 bytes, checksum: f16ae6c6befcaa27f593134ca7fa0f5d (MD5) Previous issue date: 2013-08-23 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / Brazil is one of the references in the world market of ceramic tiles, ranking second in production and consumption. Only in 2012 were produced 865.9 million square feet, for a total installed capacity of 1.004 million square meters. An important aspect of the ceramic industry in the global context, is the continuous technological development, the widespread use of ceramics in various applications and environments and the increasing incorporation of waste from other sectors, giving sustainability concepts in the industry. Brazil produces on average 980 000 tonnes of glass packaging a year and has about a recycling rate of 47%. This study aimed to present one more option to the use of waste glass, which is still poorly recycled in Brazil, analyzing the influence of the replacement of feldspar in a ceramic, for residue from glass bottles are not returnable to the market. We tested three different percentages of glass waste, but also the influence on the behavior of the residue the technological properties with variation of firing temperature. Previously, all materials used in this work were characterized by the techniques of X-ray fluorescence, X-ray diffraction, thermal analysis and particle size. After established formulations, manufacturing and burning the bodies of the test piece, checked the technological properties and microstructure of established formulations. The results indicate that the glass waste has the potential to be used as a flux alternative to replace feldspar in the production of ceramic tiles for different purposes, according to NBR 13817/1997. / O Brasil é uma das referências no mercado mundial de revestimentos cerâmicos, ocupando a segunda posição em produção e consumo. Só no ano de 2012 foram produzidos 865,9 milhões de metros quadrados, para uma capacidade instalada de 1.004 milhões de metros quadrados. Um aspecto importante da indústria cerâmica, no contexto mundial, é o contínuo desenvolvimento tecnológico, a disseminação do uso de cerâmica em diferentes aplicações e ambientes e a crescente incorporação de resíduos provenientes de outros setores, dando conceitos de sustentabilidade no setor. O Brasil produz em média 980 mil toneladas de embalagens de vidro por ano e possui, aproximadamente, um índice de reciclagem de 47%. Este trabalho teve como objetivo apresentar mais uma opção para o aproveitamento do resíduo de vidro, que ainda é pouco reciclado no Brasil,analisando a influência da substituição do feldspato, em uma massa cerâmica, por resíduo de vidro proveniente de garrafas não retornáveis ao mercado. Foram testadas três diferentes percentuais de resíduo de vidro, como também a influência no comportamento do resíduo nas propriedades tecnológicas com a variação de temperatura de queima. Previamente, todos os materiais utilizados no trabalho foram caracterizados pelas técnicas de fluorescência de raios X, difração de raios X, análise térmica e granulométrica. Após estabelecidas as formulações, confecção e queima dos corpos-de-prova, foram verificadas as propriedades tecnológicas e microestruturais das formulações estabelecidas. Os resultados obtidos apontam que o resíduo de vidro apresentou potencial de ser utilizado como fundente alternativo em substituição ao feldspato, na produção de revestimentos cerâmicos para diferentes finalidades, de acordo com a norma NBR 13817/1997.

Submitted by Ana Guimarães Pereira (agpereir@ucs.br) on 2017-12-20T10:57:46Z No. of bitstreams: 1 Tese Daniel Teixeira.pdf: 146154 bytes, checksum: 7c1e5b79cce0b660c6eff1df7e5cb84d (MD5) / Made available in DSpace on 2017-12-20T10:57:46Z (GMT). No. of bitstreams: 1 Tese Daniel Teixeira.pdf: 146154 bytes, checksum: 7c1e5b79cce0b660c6eff1df7e5cb84d (MD5) Previous issue date: 2017-12-20 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior, CAPES

Orientador: José Roberto Rodrigues / Resumo: Este estudo ín vitro avaliou a influência da inclusão de fibras de vidro em resinas compostas lndiretas, visando confirmar a possibilidade de redução de sua espessura, sem prejuízo a resistência flexural e módulo de elasticidade. Foram constituídos 18 grupos de três materiais restauradores, cada um com diferente padrão de polimerização (Artglass - Heraeus Kulzer; BelleGiass - KerrLab e Targis -lvoclar Vivadent), em três diferentes espessuras (1mm; 1,5mm e 2mm), sem ou com inclusão de fibras (Fibrex Medial, Angelus e Vectris, lvoclar Vlvadent), além de três grupos experimentais, de diferentes espessuras, associando Targis/Fibrex. Os corpos-de-prova (25x2x2mm) foram armazenados em água destilada a 37ac por 24h, e, após, submetidos a ensaio de flexão em máquina universal de ensaios (EMIC DL2000). Os resultados, analisados por ANOVA one-way e testes de Ounnet e Tukey (u=0,05), apontaram diferenças entre os materiais, com BelleGiass exibindo maiores médias de resistência flexural e módulo de elasticidade, e, ainda, aumento significativo da resistência flexural em todos os materiais quando reforçados por fibras, sem benefício ao módulo de elasticidade. A fibra Fibrex foi superior à Vectris, sem diferença estatística. Em relação às espessuras, verificou-se que os espécimes de 1 mm, com reforço, exibiram comportamento semelhante aos de 2mm, sem retorço, com todos os materiais. Foi possível concluir que a inclusão de fibras de vidro propiciou aumento da resistência flexural dos materiais testados, sugerindo viabilidade da redução de desgaste dentário sem prejuízo às propriedades flexurais / Abstract: The aim of thís in vitro study was to evaluate the influence of glass-fiber reínforcement on indirect composíte resins, to confírm the víabílity of thickness reduction with no damage of ffexural strength and elastic modulus. Eighteen groups (n=10) of three restoratíve materiais with different pofymerization patterns (Artglass- Heraeus-Heraeus Kulzer; BelleG/ass- KerrLab and Targis- /voclar Vivadent-Vivadent) and wíth three tickness (1mm, 1,5mm and 2mm) were constituted and half of them received glass-fiber reinforcement (Vectris, lvoclar Vivadent and Fibrex, Angelus). Therefore, three experimentais groups were constituted with Targis!Fibrex. The specimens (25x2x2mm) were stored in distilled water at 37"'C for 24h and them submitted a three-poínt bend test on universal testing machine (EM/C DL2000). The statistical analysis (One-way ANOVA and post-hoc comparisons, a =. 05) of the resufts suggested differences ln polymerization patterns among the materiais with BelleGiass exihibiting greater flexural strength (FS) and elastic modulus (EM). The strength of Fibrex was slightly greater than Vectrís. There were no statistic dífferences. As for the thicknesses, the 1 mm reínforced-composites were similar in strength to the 2mm samples without g/ass-fiber reinforcement for ali materiais. Jt was concluded that the inc/usion of glass-fiber a!lowed greater FS of the tested materiais, suggesting the decreasíng of the dental wear with no damage to the flexural properties for avaliated indirect composite resíns / Doutor

Orientador: Sandro Donnini Mancini / Banca: Marcia Aparecida da Silva Spinacé / Banca: Maria Zanin / O Programa de Pós-Graduação em Ciência e Tecnologia de Materiais, PosMat, tem caráter institucional e integra as atividades de pesquisa em materiais de diversos campi da Unesp / Resumo: A reciclagem química de Poliamida 6,6 já é conhecida em patentes e aplicada por empresas de matéria-prima. Entretanto, a reciclagem química de poliamida 6,6 com cargas de fibras de vidro é pouco conhecida. O presente trabalho buscou estudar em escala laboratorial e Reciclagem Química, via Hidrólise, de resíduos dos processos de injeção de Poliamida 6,6 reforçada com 25% de fibras de vidro, descartados pela indústria automotiva após a reciclagem mecânica. Um procedimento de experimentos foi realizado para determinar qual a melhor proporção de água e do material compósito deveria ser reagido para obter o maior teor de fibras de vidro em um menor tempo. Os resultados mostraram que foi possível despolimerizar a Poliamida 6,6 partindo de um material já submetido a três ciclos de reciclagem mecânica com Massa Molar Viscosimétrica Média de 27.604 g.mol-1 obtendo Sal de Nylon com 322 g.mol-1 e 39,29% dos monômeros de base como Ácido adípico e hexametileno diamina em reações a 260ºC por 3 horas e 30 minutos apenas com água desmineralizada. Já a separação das fibras do material polimérico foi bem sucedida por filtragem a vácuo seguida de queima do resíduo orgânico, obtendo até 97,87 das fivras de vidro. Com base nestes resultados, concluiu-se que a reciclagem química deste material foi viável para a obtenção de Ácido Adípico, Hexametileno diamina e o reaproveitamento das fibras de vidro / Abstract: Chemical recycling of polyamide 6,6 is already known in patents and applied by companies of raw material. However, the chemical recycling of polyamide 6,6 with fillers of glass fibers is not well known. The present work studies in laboratory scale the Chemical Recycling, via hydrolysis, waste injection processes of Polyamide 6,6 reinforced with 25% glass fibers, discarded by the Automotive Industry. A procedure of experiments was conducted to determine the best rate water and composite should be reacter to obtain the highest level of glass fibers in less time. The experimental results show that it was possible to depolymerize the polyamide 6,6 starding form a material already subjected to threee cycles of mechanical recycling with molecular weight of 27.604 g.mol-1 and obtained salt of Nylon with 322 g.mol-1 and 39,29% of basis monomers as Adipic acid and hexamethilene diamina in reactions at 260ºC for 3 hours and 30 minutes only with demineralised water. Now the separation of the fibers of polymeric material succeeded by filtration under vacuum, followed by burning the organic residue, to obtain 97.87% of glass fibers. Based on these results, it was concluded that chemical recycling of this material was feasible to obtain adipic acid, hexamethylene diamine and reusing glass fibers / Mestre

Resumo: Neste trabalho, obteve-se uma matriz porosa com alto teor de sílica a partir de vidros Pyrex® utilizando-se o tratamento hidrotérmico. A matriz porosa é formada principalmente por dois processos: (i) reação da água no estado supercrítico com a rede vítrea e, (ii) separação e lixiviação de fases. A matriz apresenta-se macroporosa, possuindo também baixa percentagem de micro e mesoporos. Através de técnicas espectroscópicas verifica-se que a matriz apresenta grupos silanóis de superfície, os quais foram utilizados em reações de funcionalização. A espectroscopia de ressonância magnética nuclear de 29Si, MAS RMN, indica a presença de grupos ordenados, (SiO)4Si, no interior da matriz e do grupo (SiO)3Si(OAl). Os espectros de 29Si, CPMAS RMN, indicam que a matriz porosa é constituída de átomos de silício localizados em dois ambientes químicos diferentes, (SiO)3Si(OH), e (SiO)4Si. Pelo espectro de 27Al MAS RMN confirma-se a presença do grupo Al-O-Si, o qual é responsável pela formação de sítios ácidos de Brönsted. Pela análise dilatométrica verifica-se que a contração máxima da matriz foi de 6% em 1365oC, aumentando a densidade do material, o tamanho médio dos poros, devido a consolidação de micro e mesoporos, diminuindo assim a área superficial. A matriz cristaliza-se em 950oC como α-cristobalita pertencente ao grupo espacial P41212. A matriz obtida foi então utilizada como suporte para complexos luminescentes. O complexo diaquatris(tenoiltrifluoroacetonato)európio(III), [Eu(tta)3(H2O)2], impregnado ou ancorado na matriz, apresenta emissões com alargamento não-homogêneo indicando que há interações entre o complexo e a superfície da matriz...(Resumo completo, clicar acesso eletrônico abaixo) / Abstract: In the present work, porous silica matrix has been obtained from Pyrex glass by hydrothermal treatment under saturated steam condition. The formation process was principally investigated using scanning and transmission electron microscopies and Raman spectroscopy. The results indicate that the process of phase separation takes place on edge of vitreous sample at lower temperature than of glass-transition temperature at room atmosphere. This process occurs due to the glass hydration by hydrothermal treatment that diminishes both viscosity and glass transition temperature. The segregated orthoborate phase was leached out by water in supercritical condition. The formation and leaching of this phase together with essential reactions between water and silica at supercritical condition contribute to obtain a porous silica matrix. The matrix has a high percentage of porosity, an interconnected macroporous structure, a low percentage of micro and mesopores and also a good thermal stability. It is non-crystalline and after thermal treatment it presented X-ray pattern characteristic of cristobalite and a low contraction of volume. The chemical analysis shows a high concentration of silicon and low concentrations of aluminum and boron. The chemical environments of silicon and aluminum atoms into the porous silica matrix were investigated by solid state NMR spectroscopy. The 29Si MAS NMR spectrum exhibits a broad signal at -110 ppm, typical of an ordered silica phase. The chemical nature of surface was better understood with application of the 1H - 29Si CPMAS NMR technique. This technique leaded to a strong and selective... (Complete abstract, click electronic access below) / Orientador: Marian Rosaly Davolos / Coorientador: Miguel Jafelicci Junior / Banca: Aldo José Gorgatti Zarbin / Banca: Hermi Felinto de Brito / Banca: Henrique Eisi Toma / Banca: Sandra Helena Pulcinelli / Doutor

Orientador: José Roberto Cury Saad / Banca: Marcelo Ferrarezi de Andrade / Banca: Manio de Carvalho Tiburcio / Resumo: Proposição: o presente estudo tem como objetivo avaliar a resistência à compressão de restaurações de resina composta em preparos classe II, observando o tipo de preparo que possui maior resistência à compressão permitindo obter um modelo de restauração classe II com características adequadas, garantindo a qualidade da restauração, assim como sua durabilidade. Material e método: os dentes foram divididos em cinco grupos contendo oito dentes por grupo, sendo eles; Grupo 1-controle, Grupo 2- preparo mésio-oclusal com bisel, Grupo 3- preparo mesial sem canaleta e com bisel, Grupo 4- preparo mesial com canaleta e com bisel e Grupo 5- preparo mésio-oclusal sem bisel. Resultado: os resultados obtidos mostraram que o grupo controle obteve os maiores valores porém não foi estatisticamente significante quando comparado com os Grupos 2 e 5. Conclusão: preparos com extensão para oclusal apresentam valores satisfatórios porém devemos considerar que preparos preventivos não obtiveram diferença estatística quando comparados a esses preparos podendo ser indicados em casos de lesões de cárie apenas proximais. / Abstract: Objective: The present study aims to evaluate the compressive strength of composite resin restorations in Class II preparations, noting the type of preparation that has greater compressive strength allowing to obtain a Class II restoration model with appropriate characteristics, ensuring the quality of restoration, as well as its durability. Methods: The teeth were divided into five groups containing eight teeth each group; Group 1- control, Group 2- mesio-occlusal preparation with bevel; Group 3- mesial preparation without groove and with bevel; Group 4- mesial preparation with groove and bevel; Group 5- mesio-occlusal preparation without bevel. Results: The results showed that the control group had higher values but not statistically significant when compared with Groups 2 and 5. Conclusion: Preparations with occlusal extension exhibited satisfactory values but we must consider that preventive preparations did not obtain satatistical difference when compared to these preparations and may be indicated in cases of only proximal carious lesions. / Mestre

Made available in DSpace on 2011-12-27T14:14:20Z (GMT). No. of bitstreams: 2 000425443-0.pdf: 137763 bytes, checksum: 07c751d4d7073c523bf8aaedf5f3b302 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / Aims: to evaluate the bond strength of fibre-posts luted with two kind of resin cements to dentin of the root canal treated or not with Nd:YAG laser associated to phosphoric acid. Materials and methods: Sixty one-root teeth with similar morphology and length were submitted to the endodontic treatment with manual instrumentation. After, it were divided into six groups according to the luting protocol of the fibre post (n=10): G1 –RelyX Unicem; G2 – Nd:YAG laser + self-etching luting cement RelyX Unicem; G3 – 37% phosphoric acid gel (AG37%) + RelyX ARC; G4 – Nd:YAG laser + AG37% + RelyX ARC; G5 – etching with the Experimental Solution (ES): Patent number BRPI0903355-6) + RelyX ARC; e G6 – Nd:YAG laser + SS solution + RelyX ARC. The Nd:YAG laser were irradiated with the following protocol: 1064 nm, 60 mJ, 15 Hz and 47. 77 mJ/cm2, 1 min. Afterwards, the teeth with the luted fibre posts were stored in distilled water at 37ºC for 1 week. Next, the roots were sectioned in thirds – cervical, medial and apical – being the slices submitted to the push-out bond strength test. Results: the SS solution group associated to RelyX ARC presented together with the Nd:YAG laser associated to the RelyX Unicem the higher bond strength considering all thirds. Notwithstanding, the phosphoric acid gel associated to the RelyX ARC presented the lower bond strength together with the Relyx Unicem control group. Conclusion: The use of the ES solution increased significantly the bond strength of the RelyX Arc to dentin of the root canal. / Objetivos: Avaliar a resistência de união de pinos de fibra de vidro cimentados à dentina radicular tratada com laser de Nd:YAG, ácido fosfórico gel a 37% ou com uma solução experimental (PATENTE solicitada ao INPI nº PI0903355-6), utilizando dois tipos de cimentos resinosos. Materiais e métodos: Sessenta dentes unirradiculares com morfologia e comprimentos semelhantes foram submetidos ao tratamento endodôntico tradicional ou com laser de Nd:YAG, com instrumentação manual. Após, os dentes foram divididos em seis grupos de acordo com o protocolo de cimentação do pino de fibra de vidro (n=10): G1 –RelyX Unicem; G2 –laser Nd:YAG + RelyX Unicem; G3 –ácido fosfórico gel a 37% (AG37%) + RelyX ARC; G4 –laser Nd:YAG + AG37% + RelyX ARC; G5 – condicionamento com solução experimental (PATENTE solicitada ao INPI nº PI0903355- 6) + RelyX ARC; e G6 – laser Nd:YAG + solução experimental (PATENTE solicitada ao INPI nº PI0903355-6) + RelyX ARC. O laser de Nd:YAG foi irradiado com o seguinte protocolo: 1064 nm, 60 mJ, 15 Hz, 47,77 mJ/cm2 durante 1 min. Os dentes com os pinos cimentados foram armazenados em água destilada a 37ºC por 7 dias. Após esse período, as raízes foram seccionadas em terços cervical, médio e apical, sendo as fatias submetidas ao ensaio de resistência de união por push-out. Ainda, seis dentes foram submetidos aos tratamentos de superfície e levados à microscopia eletrônica de varredura e análise EDS. Resultados: o grupo da solução experimental (PATENTE solicitada ao INPI nº PI0903355- 6) associada ao cimento resinoso RelyX ARC apresentou juntamente com o grupo do laser 4 de Nd:YAG associado ao cimento RelyX Unicem a maior resistência de união considerando todos os terços radiculares. Por sua vez, o ácido fosfórico gel associado ao cimento RelyX ARC apresentou a menor resistência de união juntamente com o grupo do RelyX Unicem. Conclusão: O uso da solução experimental (PATENTE solicitada ao INPI nº PI0903355-6) aumentou significativamente a resistência de união do cimento resinoso RelyX ARC à superfície dentinária do conduto radicular, assim como a irradiação por laser, de uma maneira geral, também aumentou a resistência de união particularmente nos grupos G2 e G4.

Submitted by Ginamara Lima (ginaj@pucrs.br) on 2013-04-30T21:28:22Z No. of bitstreams: 1 447499.pdf: 1220265 bytes, checksum: e49cb6ce6026a77ac053d20f7598d292 (MD5) / Made available in DSpace on 2013-04-30T21:28:22Z (GMT). No. of bitstreams: 1 447499.pdf: 1220265 bytes, checksum: e49cb6ce6026a77ac053d20f7598d292 (MD5) / Este estudo teve como objetivo avaliar a influência da radiação ionizante sobre três cimentos de ionômero de vidro, convencional, modificado por resina e modificado por liga de prata, quanto à tração diametral. A hipótese nula deste estudo testou a ação da radiação ionizante sobre os cimentos de ionômero de vidro submetidos a tração diametral. Para o teste de tração diametral foram confeccionadas amostras para cada grupo de ionômero de vidro: Convencional (n=20), modificado por resina (n=20), modificado por liga de prata (n=20), em uma matriz bipartida de PTFE (politetrafluoetileno) cilíndrica de 6 mm de diâmetro X 3 mm de altura utilizando técnica indicada pelo fabricante. Todas as amostras, após a confecção, foram armazenadas em recipientes plásticos protegidos da luz pelo período de 24h à 37° C em uma estufa para culturas. Após cada grupo foi dividido em um grupo controle ou um grupo submetido a radiação ionizante no Centro de Oncologia do Hospital Mãe de Deus, com dose usual para tratamento de neoplasias de cabeça e pescoço fracionada em 35 aplicações de 2 Gy (200cGy) ao dia, durante 35 dias, totalizando a dose de 70 Gy (7000cGy), através de um acelerador linear na tentava de simular a dose e o tempo de uma radioterapia de cabeça e pescoço. Para evitar sub dosagem na superfície do material devido ao efeito Build-up (acúmulo), foi utilizado Bólus de 2mm simulando tecidos moles circundantes. O ensaio de resistência à tração diametral foi realizado em uma máquina de ensaio Universal EMIC DL 2000, com velocidade de carregamento de 1mm/min, até a fratura do corpo-de-prova. Os dados foram avaliados pela análise de variância e teste de comparações múltiplas de Tukey (α=0,05). Foram observadas diferenças significativas (p<0,001) entre os três grupos de cimento de ionômero de vidro avaliados (convencional, modificado por resina e modificado por liga de prata) no ensaio de tração diametral. Ao comparar os grupos de mesma classificação, submetidos ou não á radiação, não houve diferença significante, o grupo Riva Light Cure controle obtiveram a média (MPa) de 31,83 e o grupo irradiado 24,82. O grupo Riva Silver controle obteve média (MPa) de 12,06 e no grupo irradiado 17,29. O grupo Riva Self Cure controle apresentaram uma média (MPa) de 14,05 enquanto o grupo irradiado obteve 26,04. Ao comparar todos os grupos de diferentes classificações que foram submetidos á radiação, houve diferença estatisticamente significante entre eles (p<0,001). O grupo Riva Silver controle apresentou menor valor (MPa) (12,03) quando comparado ao grupo Riva Light controle (31,83). A radioterapia aplicada como protocolo no tratamento de pacientes com câncer de cabeça e pescoço não influi negativamente na tração diametral dos três diferentes cimentos de ionômero de vidro pesquisados. / The aim of this study was evaluate the influence of ionizing radiation under three glass ionomer (conventional, resin modified and silver added) on the diametral tensile strength. The null hypothesis tested the action of ionizing radiation under glass ionomer cements submitted to tensile strength. To diametral tensile strength, samples were made with conventional (n=20), resin modified (n=20), silver added glass ionomer cements (n=20) into a cylindrical bipartite mould of PTFE (polytetrafluoroethylene) with 6 mm diameter X 3 mm high according to manufacturer’s instructions. All samples were stored in plastic tubes protected from light for 24 h at 37° C in a culture stove. After that, each group was divided in a control or submitted to ionizing radiation at Centro de Oncologia do Hospital Mãe de Deus, with usual dose for head and neck cancer fractioned in 35 daily applications of 2 Gy (200cGy) for each Day, resulting at 70 Gy (7000cGy) by a linear accelerator. In order to avoid sub dosage at the material surface due to Build-up effect, a Bolus was used with 2mm simulating soft tissues. The diametral tensile strength test was performed in a universal testing machine EMIC DL 2000 (Emic, São José dos Pinhais, Brazil), with 1 mm/min of cross-head speed. Data were submitted to analysis of variance and multiple comparison test of Tukey (α=0.05). Significant differences were recorded (p<0.001) between the glass ionomer tested (conventional, resin modified and silver added) for diametral tensile strength. Comparing groups with the same classification, submitted or not to radiation, there was no significant difference. Riva Light Cure control showed an average (MPa) of 31.83 in comparison to 24.82 of irradiated group. Riva Silver control showed an average (MPa) of 12.06 in comparison to 17.29 for the irradiated group. Riva Self Cure control showed an average (MPa) of 14.05 in comparison to 26.04 irradiated group. Comparing all groups of different classification submitted to ionizing radiation, there were significant difference between them (p<0.001). Riva Silver control showed the lowest average (MPa) (12.03) in comparison to Riva Light control (31.83). The radiotherapy applied as protocol to head and neck cancer therapy do not act negatively in the diametral tensile strength of the three glass ionomer tested.