CoordenaÃÃo de AperfeÃoamento de Pessoal de NÃvel Superior / The present work describes the use of a grinding dust almost granite raw feedstock to the process of ceramic injection molding at low pressures. The main objective was to demonstrate the technical feasibility of using a low-cost raw material for parts for applications where these were not subjected to large mechanical stresses. Initially it selected a powder from the extraction of a granite commercial value called White Savannah. The material was characterized by chemical and petrographic analysis (for microprobe), and microscopy Scanning electron diffraction and X-ray. After several unsuccessful attempts to use the powder in the raw state, it was subjected to a simple procedure for comminution by grinding and subsequent selection by sieving. The obtained fines were mixed with binder to carnauba wax base, developed in previous research. Rheological studies helped determine the optimum amount of binder and powder in the mixture to be injected. Thermogravimetric analysis was used to establish a ramp for removal of the binder by thermal degradation after injection. The binder removal step was performed without introducing macrodefeitos. The parts were sintered in air in a muffle furnace at temperatures between 1200 0 C to 1280 0 C. Next, the pieces were evaluated in terms of density, porosity, shrinkage and hardness. The best results in terms of appearance, shape maintenance and combination of physical and mechanical properties were obtained with the parts sintered at 1250 0 C. The values ​​obtained for these properties were deemed reasonable when compared to results obtained with previously manufactured parts using other granite waste. / O presente trabalho descreve a utilização de um pó residual de granito em estado quase bruto como matéria-prima para o processo de moldagem cerâmica por injeção a baixas pressões. O objetivo principal era demonstrar a viabilidade técnica de se utilizar uma matéria-prima de baixo custo para obter peças para aplicações em que essas não fossem submetidas a grandes esforços mecânicos. Inicialmente foi selecionado um pó proveniente da extração de um granito de valor comercial denominado Branco Savana. O material foi caracterizado por análises petrográfica e quı́mica (por microssonda), além de microscopia eletrônica de varredura e difração de raios-X. Após algumas tentativas infrutı́feras de se utilizar o pó no estado bruto, o mesmo foi submetido a um procedimento simples de cominuição por moagem e posterior seleção por peneiramento. Os finos obtidos foram misturados ao ligante à base de cera de carnaúba, desenvolvido em pesquisas anteriores. Estudos reológicos ajudaram a determinar a quantidade ótima de ligante e pó na mistura a ser injetada. A análise termogravimétrica foi utilizada para se estabelecer uma rampa para a retirada do ligante por degradação térmica, após a injeção. A etapa de retirada do ligante foi realizada sem introdução de macrodefeitos. As peças foram sinterizadas ao ar, em forno mufla, a temperaturas entre 1200 0 C e 1280 0 C. Em seguida as peças foram caracterizadas quanto à densidade, porosidade, contração, e microdureza. Os melhores resultados em termos de aparência, manutenção do formato e combinação de propriedades fı́sicas e mecânicas foram obtidos com as peças sinterizadas a 1250 0 C. Os valores obtidos para essas propriedades foram considerados razoáveis, quando comparados aos resultados atingidos com peças fabricadas anteriormente, utilizando outros resı́duos granı́ticos.

Orientadores: Maria Alvina Krahenbuhl, Lisandro Pavie Cardoso / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-08-10T02:11:46Z (GMT). No. of bitstreams: 1 Gorga_RejaneCesarioPereira_M.pdf: 3579870 bytes, checksum: 225a43b57d7e0201a548070f1721a7f8 (MD5) Previous issue date: 2007 / Resumo: o estudo do comportamento dos ácidos graxos, presentes em óleos e gorduras de origem vegetal é importante, pois eles se apresentam sob a forma sólida à temperatura ambiente por apresentarem uma longa cadeia carbônica. Assim, para a modelagem de suas propriedades termo físicas, o conhecimento da estrutura cristalina dos sistemas binários compostos de ácidos graxos toma-se essencial. O potencial da difratometria de raios-X na análise de materiais policristalinos aumenta quando é associado ao método de Rietveld para o refinamento de estruturas cristalinas, pois fornece simultaneamente os parâmetros estruturais da amostra, a análise quantitativa das fases, a determinação da orientação preferencial, o tamanho de cristalitos e a microdeformação das amostras analisadas, entre outras análises possíveis. Nesse trabalho investigou-se a formação de soluções na fase sólida dos sistemas binários formados a partir dos ácidos graxos: Mirístico(x) + Palmítico(l-x) (sistema D e Láurico(x) + Mirístico(l-x) (sistema 2), usando a difração de raios-X associada ao método de Rietveld. Amostras dos dois sistemas foram preparadas em várias concentrações com fração molar na faixa de O < x < 1 em intervalos de x = 0,1. A análise dos difratogramas de raios X para o sistema 1 mostra o efeito da adição do ácido mirístic_ no palmítico, com a ocorrência das duas fases simultaneamente entre 0,3 < x < 0,7. Fora desse intervalo, apenas as fases puras dos ácidos foram observadas. No sistema 2 observou-se a formação de uma nova fase cristalina entre 0,4 < x < 0,6, que não pode ser identificada como fase láurico ou mirístico. A melhor simulação para o Rietveld da amostra x = 0,4 foi obtida para as proporções 80% da nova fase e 20% da fase mirístico, enquanto que para a amostra x = 0,5, apenas a contribuição da nova fase foi considerada. O modelo para a nova fase cristalina no refinamento leva em consideração o arranjo de uma cadeia de C com 13 átomos para essa fase, seguindo o mesmo arranjo dos átomos de C nas células unitárias dos ácidos nos dois sistemas, e um bom ajuste (Rwp = 10,5%) foi obtido por Rietveld. Uma forte interação entre os grupos carboxila conduzindo a um possível ordenamento da estrutura explicaria a nova fase obtida do refinamento. Os resultados para x > 0,8 indicam a fase do ácido láurico como única contribuição / Abstract: The X-ray diffraction potential in the analysis of polyerystalline materiaIs enhances when it is associated with the Rietveld method for refinement of crystalline structures, since one can obtain simultaneously: the sample structural parameters, the quantitative phase analysis, the preferred orientation determination, crystallite size and sample micro strain, among other possible information. ln this work, the formation of solutions in the solid phase of the binary fat acid systems: Miristic(x) + Palmitic(1-x) (system 1) e Laurie(x) + Miristic(1-x) (system 2) by using the X-ray diffraction associated with the Rietveld method is investigated. Samples of the two systems were prepared with several concentrations in the range of O < x <1 with increments of O.1. The system 1 X-ray diffractogram analysis exhibits the effect of the addition of the Miristic acid in the Palmitic, with the occurrence of two simultaneous phases for 0.3 < x < 0.7. Out of this range, only the pure fat acid phases were observed. ln system 2, it was observed the formation of a novel crystalline phase for 0.4< x < 0.6, which could not be identified as none of the two acid phases of the system. The best Rietveld simulation for x = 0.4 sample was obtained for 80% of the new phase and 20% of the Miristic phase, whereas for x = 0.5 sample, only the new phase contribution was obtained. A possible model for the new phase obtained through the refinement takes into consideration the packing of a Carbon chain with 13 atoms in the unit cell, following the same disposition of the C atoms in the unit cell of the fat acids of both systems. A very good Rietveld fit (Rwp= 10,5%) was obtained for this new phase. A possible structure ordering due to a strong interaction among the carboxylic groups should explain the new phase obtained from the Rietveld refinement. The results for x > 0.8 show only the contribution of the Laurie acid phase / Mestrado / Desenvolvimento de Processos Químicos / Mestre em Engenharia Química

Orientadores: Carlos Raimundo Ferreira Grosso / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia de Alimentos / Made available in DSpace on 2018-08-10T13:38:28Z (GMT). No. of bitstreams: 1 Leonel_AldaJusceline_M.pdf: 1114899 bytes, checksum: 0e2498fa7d8941ce552ac5eced6c86a2 (MD5) Previous issue date: 2008 / Resumo: Apesar de micropartículas lipídicas possuírem vantagens, como baixa toxicidade e não utilizarem solventes orgânicos em sua produção, elas apresentam alguns inconvenientes como a baixa capacidade de encapsulação do recheio e a possibilidade de expulsão do material de recheio encapsulado durante o armazenamento. Este trabalho teve como objetivo estudar a formação e a estabilidade de micropartículas de lipídios preparadas por spray cooling compostas por ácidos graxos (esteárico e oléico) e gordura vegetal hidrogenada como matriz, lecitina de soja como tensoativo e solução de glicose como material de recheio. Foram avaliados morfologia de superfície, tamanho de partícula, quantidade de recheio encapsulada e não encapsulada (superficial) e comportamento de liberação do recheio em solução aquosa. Para o estudo da estabilidade, medidas da retenção do recheio ao longo do tempo em temperatura controlada, medidas de difração de raios-X (0, 7, 14, 21 e 28 dias) e medidas calorimétricas (tempo zero) foram efetuadas. Valores de eficiência de encapsulação foram superiores a 70%, e as maiores quantidades de glicose não encapsulada foram encontradas nas formulações nas quais foram adicionadas maiores quantidades de recheio. A liberação do recheio também apresentou correlação com a quantidade de recheio utilizado, onde menores quantidades de recheio foram mais bem retidas. Os diâmetros médios das micropartículas situaram-se entre 25 e 32 µm, e as partículas apresentaram paredes rugosas porém contínuas. No estudo da estabilidade, as formulações com maiores quantidades de recheio (solução de glicose 80%) ou sem a adição de tensoativo (solução de glicose 40%, sem lecitina) apresentaram, na quantidade de glicose superficial, 18 e 56% de recheio não encapsulado no último dia de análise, respectivamente, sendo significativamente diferente das outras duas formulações, uma com solução de glicose 60% e outra com solução de glicose 40%, que apresentaram resultados de 5% e 2% no último dia de análise. Os resultados de difração de raios-X não apresentaram alterações ao longo dos 28 dias de estudo e os resultados de DSC foram semelhantes no tempo zero entre as diferentes formulações estudadas. A utilização da mesma matriz lipídica nas formulações parece responsável pelos resultados da difração de raios-X e calorimétricos obtidos / Abstract: Although lipid microparticles have advantages, just as low toxicity and no use of organic solvents in their production, they present some incovenients, as low capacity of encapsulation of core material and the expulsion of encapsulated core during its storage. The aim of this work was to study the formation and the stability of lipid microparticles prepared by spray cooling, composed by fatty acids (stearic and oleic) and hydrogenated vegetable fat as matrix, soya lecithin as surfactant and glucose solution as core material. For this propose, surface morphology, particle size, no encapsulated (surficial) core measure, total encapsulated core material and core release behavior in aqueous solution were evaluated. The stability study was evaluated with measures of core retention along of the time in controlled temperature, X-ray diffraction measurements (0, 7, 14, 21 and 28 days) and calorimetric measurements (zero time). The efficiency of encapsulation was above 70% and the biggest amounts of glucose no encapsulated were found in the formulations in which were added the biggest amount of core material. Results of release of core material also showed correlation with the amount of core material utilized, where low amount of core material showed better retention. The mean diameters of microparticles remained between 25 and 32 µm and they exhibited rough walls, but continuous. In the stability study, formulations with high amounts of core material (solution of glucose 80%) or without the addition of surfactant (solution of glucose 40%, without lecithin) showed 18 and 56% of no encapsulated core material in the last day of analysis, respectively. This result were significantly different compared with the other two formulations, one with solution of glucose 60% and the other with solution of glucose 40%, that showed results of 5% and 2% of superficial glucose in the last day of analysis. The X-ray diffraction results didn¿t show alterations after 28 days. The DSC results showed similar profile for the formulations studied at zero time. The use of the same lipid materials to produce the microparticles during the stability study may be responsible for X-ray and calorimetric results obtained. / Mestrado / Nutrição Experimental e Aplicada à Tecnologia de Alimentos / Mestre em Alimentos e Nutrição

Orientador: Marco Antonio Bica de Moraes / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin / Made available in DSpace on 2018-08-06T01:12:05Z (GMT). No. of bitstreams: 1 Gadioli_GiovanaZanini_M.pdf: 816711 bytes, checksum: 5d38a2c08f13049d8af5fd4659ded22e (MD5) Previous issue date: 2006 / Resumo: As propriedades de filmes obtidos por co-deposição de um material ferromagnético e um não-magnético são objetos de intensa investigação. Neste trabalho, foram investigadas as propriedades de filmes Gdx W1-x, com x variando de 0 a 1. Os filmes foram depositados por magnetron-sputtering a partir de alvos de Gd e W. Para a análises dos filmes foram usadas as técnicas EPMA (microanálise eletrônica) e difratometria de raio-x de baixo ângulo para determinar a composição atômica e a estrutura cristalina, respectivamente. O momento magnético, m , de cada filme foi medido em função da temperatura, T, e do campo magnético aplicado, H, usando um magnetômetro SQUID (superconducting quantum interference device). Os filmes são amorfos para para 0,15 < x < 0,85, mas a coercividade foi observada em todos as amostras. A partir das curvas m vs T, foi observado um forte ordenamento magnético para T < TB. Para T > T B as amostras se mostram paramagnéticas. Os valores de T B foram observados em baixa temperatura (entre 5 e 50 K). A temperatura de Curie-Weiss, deduzida a partir das curvas x -1 vs T, onde x é a suscetibilidade, aumentaram com x. O efeito magnetocalórico foi estudado a partir das isotermas de magnetização, M vs H, das quais a variação de entropia magnética, D S M, foi obtida. As curvas D SM vs T exibiram máximos que variam entre 5 K e temperatura ambiente, dependendo da proporção de Gd / Abstract: The magnetic properties of films obtained by the co-deposition of a ferromagnetic and a non-magnetic components are the subject of intense investigation. In this work, the magnetic properties of Gdx W1-x, with x ranging from 0 to 1, were investigated. The films were deposited by magnetron sputtering from Gd and W targets. EPMA (electron probe microanalysis) and low-angle XRD (x-ray diffraction) were used to determine the film atomic composition and structure, respectively. The magnetic moment, m , of the films was measured as a function of temperature, T, and applied field H, using a SQUID (superconducting quantum device) magnetometer. The films were amorphous for 0.15 < x < 0.85 but coercivity was observed in all samples. From plots of m vs T, a strong magnetic ordering was observed for T < TB. For T > T B the samples were paramagnetic. TB-values occurred at low temperatures (between 5 K and 50 K). The Curie paramagnetic temperature, deduced from the x -1 vs T plots, where x is the susceptibility, was observed to increase with increasing x. The magnetocaloric effect was investigated from the magnetization isotherms, M vs H, from which the magnetic entropy change, D SM, caused by the application and removal of a 50 kOe field, was deduced. The D SM vs T curves exhibited maxima which varied from 5 K to about room temperature, depending on the Gd concentration / Mestrado / Física da Matéria Condensada / Mestre em Física

Orientador: Iris Concepcion Linares de Torriani / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin / Made available in DSpace on 2018-08-08T13:36:14Z (GMT). No. of bitstreams: 1 Aguero_OscarEnrique_D.pdf: 9568417 bytes, checksum: db4b9632a94f1d1cb2691c4eeb1404ec (MD5) Previous issue date: 2007 / Resumo: Uma serie de compostos ineditos ou pouco estudados foram sintetizados e as propriedades físicas foram estudadas usando difração de raios X e medidas magneticas em função da temperatura. Neste tipo de compostos as propriedades estruturais estão fortemente correlacionadas com as propriedades magnéticas e de transporte. Neste trabalho apresentaremos a síntese, caracterização estrutural e magnética de ligas metálicas nanoestruturadas de Cu-Fe, compostos intermetálicos R3M4Sn13(R= terra rara, M= Co e Ir), e cobaltitas (Nd1-xC axCoO3 e GdBaCo2O5,5). Parâmetros de cela, tamanho de domínios e tensões de ligas nanoestruturadas Cu1-xFex (0<x<0,5) preparadas por ball-milling foram determinados usando difração de pó. Todos as amostras apresentam a estrutura FCC do Cu. Os parâmetros de cela aumentam com x. Usando métodos de análise do perfil de difração (largura integrada e Warren-Averbach), determinamos o tamanho dos domínios cristalinos e tensões na rede. O tamanho dos domínios decresce e as tensões aumentam com x. As estruturas cristalinas dos compostos R3M4Sn13(R= terra rara, M= Co e Ir) foram determinadas por difração de monocristais à temperatura ambiente. Todos os compostos R3C o4Sn13 e Eu3I r4Sn13 cristalizam com uma cela cúbica Pm-3n, com parâmetros de cela a~ 9,5- 9,8 Å. Os compostos R3I r4Sn13 (R= La, Ce, Pr, Nd) apresentam uma superestrutura cúbica de corpo centrado com a¿~2a. Os compostos de Yb e Eu mostram um comportamento anômalo associado a um estado de valência diferente das outras terras raras. Estudos de difração de pó a baixas temperaturas para os compostos R3Co4Sn13 (R= La, Ce, Pr, Nd e Gd) mostram uma transição abaixo de T=150 K para uma superestrutura cúbica de corpo centrado com parâmetro de cela a¿~2a. Os compostos R3Ir4Sn13 não apresentam transições de fase até 20 K. As propriedades estruturais e magnéticas das cobaltitas Nd1-xCaxCoO3 (0 =x =0,4), foram estudadas usando difração de pó, magnetização dc e susceptibilidade ac em função da temperatura (2-800 K). Todos os compostos cristalizam com uma estrutura ortorrômbica (Pnma) no intervalo de temperatura estudado (20-800 K). Para x =0,1 o sistema mostra um comportamento paramagnético até 2 K, com os íons Co3+ e Co 4+ em estados de baixo spin (LS) para T<180 K. Para 0,2 =x =0,4, duas transições magnéticas são observadas para T<60 K. Estas transições estão associadas a estados de "spin glass" ou "cluster glass". Um diagrama de fases magnéticas e de estados de spin foi construído e comparado com outros sistemas similares. Foi realizada a síntese do composto GdBaCo2O5,50 e estudadas as propriedades estruturais e de transporte em função da temperatura (2-800 K). Sucessivas transições de fase magnéticas foram observadas a: TPM= 70 K, TN~ 260 K; TC~ 273 K. Observamos uma transição metal isolante a TMI~ 360 K, simultânea com uma transição de spin dos íons de Co3+ . Os resultados magnéticos são compatíveis com estados de spin: 50%Co3+ (IS)+50% Co3+ (LS) para T<TMI e 50% Co3+ (IS)+50% Co3+ (HS) para T > TMI. Estudos estruturais usando difração de pó com fonte convencional e luz de síncrotron, mostram que a TMI uma transição de spin LS ÎHS ocorre para os íons Co3+ nos octaedros. Uma transição ortorrômbica-tetragonal, de tipo ordem-desordem, foi observada a TOD~ 760 K / Abstract: A series of new compounds have been synthesized and their physical properties studied using X-ray diffraction and magnetic measurements as a function of temperature. In this type of compounds, structural properties are strongly correlated with their magnetic and transport properties. In this work we present details of the synthesis as well as the structural and magnetic characterization of nanostructured metallic alloys (Cu-Fe), intermetallic compounds of the type R3M4Sn13 (R=rare earth, M= Co, Ir), and the cobaltates Nd1-xCaxCo03 and GdBaCo2O5,5. The lattice parameters, crystallite size and lattice strain of nanostructured Cu1-xFex(0< x <0,5) alloys prepared by the ball milling method were determined from X-ray powder diffraction analysis. All samples present the Cu FCC structure. The lattice parameter of the Cu1-xFex phases increases with x. The X-ray diffraction peaks were analyzed using the Warren-Averbach and Integral Breadth methods. The crystallite size decreases and the lattice strain increases with Fe concentration. Crystal structures of the R3M4Sn13 (R= rare earth, M=Co, Ir) intermetallic compounds were determined from single crystal X-ray diffraction at room temperature. All R3Co4Sn13 and Eu3Ir4Sn13 compounds crystallize in the cubic Pm-3n space group with cell parameters a~9,5-9,7 ÿ. The R3IrSn13(R= La, Ce, Pr, Nd) compounds present a body centered cubic superstructure with aÂ' ~2a. In this series, the Yb and Eu compounds exhibit an anomalous behavior associated to valence states different from those of the other rare earths. Low temperature X-ray powder diffraction studies for R3Co4S n13(R= La, Ce, Pr, Nd and Gd) show a phase transition below 150 K from a simple cubic to a body centered cubic superstructure with cell parameter aÂ'~ 2 a. The temperature of the phase transition decreases with the rare earth ionic radii. No phase transitions were observed for the R3Ir4Sn13 series for temperatures down to 20 K. The structural and magnetic properties of the cobaltates Nd1-xCaxCoO3(0 =x =0,4), were studied using powder X-ray diffraction, dc magnetization and ac susceptibility measurements as a function of temperature (2-800 K). All compounds crystallize with an orthorhombic (Pnma) structure in the temperature range (20- 800 K). For x =0,1 the Nd1-xCaxCoO3system shows a paramagnetic behavior down to 2 K, with the Co3+e Co4+ions in low spin state (LS) for T<180 K. For 0,2 =x =0,4, two magnetic transitions were observed for T<60 K. These transitions are associated to a spin or cluster glass states. A magnetic phase and spin state diagram was constructed for comparison with similar systems. The compound GdBaCo2 O5.50was synthesized and the structural and transport properties were studied as a function of temperature [2-800 K]. Successive magnetic phase transitions were observed: TPM= 70 K, TN~ 260 K; TC~ 273 K. A metal-insulator transition is observed at TMI~ 360 K, with a simultaneous spin transition of the Co 3+ions. The magnetic measurements results are compatible with the spin states 50%Co3+(IS)+50% Co3+(LS) for T<TMI and 50%Co3+(IS)+50%Co3+(HS) for T>TMI. Structural studies using powder diffraction with a conventional X-ray source and synchrotron radiation show that the LS Ã?HS spin state transition occurs only for the Co3+ions in the octahedrons. An orthorhombic-tetragonal transition of the order-disorder type was observed at TOD~ 760 K / Doutorado / Física da Matéria Condensada / Doutor em Ciências

Orientador: Eduardo Granado Monteiro da Silva / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin / Made available in DSpace on 2018-08-14T22:43:44Z (GMT). No. of bitstreams: 1 Moreira_AlessandroFerreiraLisboa_M.pdf: 8996770 bytes, checksum: 0836e45112c5212268c2e5514f1232a9 (MD5) Previous issue date: 2009 / Resumo: Nesse trabalho foram realizados estudos em duas famílias de compostos de perovskitas duplas Ba2FeReO6 e S r2UO6 (B'= Co, Ni) por espectroscopia Raman e difração de raios-X com luz síncrotron. No primeiro composto há uma transição de uma estrutura cúbica Fm3m paramagnética para uma tetragonal I4/mmm ferrimagnética abaixo de TC~305 K. O mecanismo de acoplamento magnético neste material ainda permanece uma incógnita. Dois grupos de medidas de espalhamento Raman foram realizados em regiões distintas da amostra à base de FeRe. Foi verificado que o fônon associado às vibrações de estiramento dos oxigênios nos octaedros sofre um desvio na freqüência em relação ao comportamento convencional abaixo de TC nos dois grupos de medidas. Isso pode ser associado a dois possíveis mecanismos: acoplamento spin-fônon gigante e acoplamento órbita-spin-fônon. Na segunda família de compostos contendo urânio, os compostos estudados apresentam uma estrutura cristalina monoclínica com grupo espacial P 21/n e um ordenamento antiferromagnético abaixo de TN~21 K para B" = Ni e TN~10 K para B" = Co. A partir dos espectros Raman desses compostos observa-se que a área integrada do modo de estiramento do oxigênio sofre um decréscimo anômalo sob aquecimento até T*~300 K. Além disso, este modo sofre um endurecimento anômalo de ~1 cm -1 sob aquecimento até T*. Para verificar a hipótese de que T* poderia estar associada a uma transição estrutural nesta família, medidas de difração de raios-X de pó com luz síncrotron foram realizadas no LNLS. A análise estrutural de ambos os compostos não mostraram nenhum grau observável de desordem de antisítios entre B' e U e tampouco uma transição de fase ou comportamento anômalo dos parâmetros de rede foi encontrada em torno de T*. Portanto, as anomalias encontradas em espectroscopia Raman nestes materiais são de origem eletrônica / Abstract: In this work, studies on two families of double perovskite compounds Ba2FeReO6and Sr2B'U O6(B' = Ni, Co) were carried out by Raman spectroscopy and synchrotron X-ray diffraction. In the first compound, a transition from a cubic Fm3m paramagnetic to a tetragonal ferromagnetic structure takes place below TC ~305 K. The magnetic coupling mechanism in this material remains unknown. Two groups of Raman scattering measurements were performed in distinct regions of the FeRe-based sample. It was verified that the phonon associated to stretching vibrations of oxygen octahedra shows a frequency shift with respect to the conventional behavior below TC, in both groups of measurements. This may be associated with two possible mechanisms: giant spin-phonon coupling and orbit-spin-phonon coupling. In the second family of compounds with uranium, the studied compounds present a monoclinic crystal structure with space group P21/n and an antiferromagnetic ordering below TN~21 K for B'' = Ni and TN ~10 K for B'' = Co. From the Raman spectra of these compounds, an anomalous decrease of the integrated area of the oxygen stretching mode was observed upon heating up to T*~300 K. Also, this mode shows an anomalous hardening of ~1 cm -1 under heating up to T*. In order to verify the hypothesis that T* could be associated to a structural transition in this family, powder x-ray diffraction measurements with synchrotron light were perfomed at LNLS. The structural analysis of both compounds did not show any observable degree of antisite disorder between B' and U, and no phase transition or anomalous behavior of lattice parameters was found close to T*. Therefore, the anomalies found by Raman spectroscopy in these materials are electronic in origin / Mestrado / Física da Matéria Condensada / Mestre em Física

Orientador: Eduardo Granado Monteiro da Silva / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Física Gleb Wataghin / Made available in DSpace on 2018-08-15T22:33:02Z (GMT). No. of bitstreams: 1 Brito_LenilsonTorres_M.pdf: 1651366 bytes, checksum: b943a1a9e24d0c5a36f607cf093af90b (MD5) Previous issue date: 2010 / Resumo: Esta dissertação apresenta um estudo das estruturas magnéticas em um filme de EuSe por difração magnética de raios-X. Usamos um filme de EuSe de 3200 Å , com uma alta qualidade cristalina e crescido por epitaxia de feixe molecular sobre um substrato de BaF2(111). A difração magnética de raios-X revelou um diagrama de fases exibindo uma forte histerese entre 1.8 K e TN ~ 4.7 K, no qual duas fases antiferromagnéticas (AFM) foram observadas. Também foi observada uma fase defeituosa e que compete com uma das fases AFM, fazendo com que essas coexistam em uma determinada região de temperatura. Investigamos a intensidade integrada, vetor de propagação k = [hhh], e largura ? h dos picos nas fases magnéticas observadas, como função da temperatura. O acoplamento magnetoelástico neste composto também foi investigado em detalhes através de pequenas anomalias no seu parâmetro de rede longitudinal. Nossos resultados completam e sistematizam estudos prévios neste material, contribuindo para o entendimento de um complexo diagrama de fases em um sistema de Heisenberg clássico com competição de interações de troca de primeiros e segundos vizinhos / Abstract: This dissertation presents a study of the magnetic structures of a EuSe film by magnetic x-ray diffraction. We used a 3200 Å thick EuSe film with high crystalline quality, grown by molecular beam epitaxy over a BaF2(111) substrate. Magnetic x-ray diffraction revealed a phase diagram with strong hysteresis between 1.8 K and TN ~ 4.7 K, where two antiferromagnetic (AFM) phases were observed. In addition, a defective phase appears, and competes with one of the AFM phases, leading to a phase coexistence in a given temperature interval. We investigated the integrated intensity, propagation vector k = [hhh], and width ? h of these peaks in the observed magnetic phases as function of temperature. The magnetoelastic coupling in this compound was also investigated in detail through small anomalies in its longitudinal lattice parameter. Our results complete and systematize previous studies in this material, contributing for the understanding of the complex phase diagram of a classical Heisenberg system with competition amongst first and second neighbor exchange interactions / Mestrado / Física da Matéria Condensada / Mestre em Física

Orientador: Carlos Kenichi Suzuki / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-07-25T04:29:58Z (GMT). No. of bitstreams: 1 Mendes_Wanderley_M.pdf: 9018563 bytes, checksum: 6fc26478d4581cd787ef07e1923cfa7f (MD5) Previous issue date: 1999 / Resumo: A indústria siderúrgica é historicamente um setor que produz impactos ambientais inerentes ao seus processos de produção. Anualmente são gerados 135 milhões de toneladas de escórias para uma produção de 700 milhões de toneladas de aço. As novas regulamentações dos órgãos ambientais têm motivado a pesquisa em busca de novas aplicações destes resíduos. Atualmente, as escórias tem sua aplicação na indústria de cimento Portland e vidros, na pavimentação de estradas, revestimentos acústicos e térmicos, neutralizante de solos, mas há necessidade de novas aplicações das escórias devido ao montante gerado pelas usinas. Neste contexto, a caracterização física, química e de impactos ambientais das escórias se faz necessária, visando uma nova aplicação tecnólogica, tendo em vista que as suas propriedades físicas e químicas estão diretamente relacionadas as suas estruturas. Com o objetivo de determinar a composição química e determinação estrutural, métodos analíticos foram aplicados em escórias de alto forno (AF) e conversores LD (CLD) utilizando-se das técnicas de espectroscopia de fluorescência (FRX) e difração de raios-X (DRX). O presente trabalho foi desenvolvido em duas etapas: (1) a determinação e quantificação química das escórias por FRX; (2) caracterização estrutural das fases presentes e quantificação da fase mervinita cristalina Ca2Mg(SiO4h que se fez presente em todas as amostras analisadas de escórias de alto forno. Foram utilizadas duas metodologias nas escórias analisadas por FRX: métodos de parâmetros fundamentais (PF) e análise semi-quantitativa (SQ), onde as diferenças nas concentrações foram significativas, justificadas pela maior acuracidade nas medições realizadas pelo PF, haja visto uma maior interação númerica e utilização de curvas de sensitividade para a análise. Também verificamos a presença de impurezas que não foram detectadas no SQ e observadas no PF, tais como: P, N, V, Cr. Com os resultados obtidos na análise por DRX observamos os diferentes graus de cristalização/amorfo; a caracterização de fases presentes, mesmo quando se encontravam em baixas porcentagens nas amostras, além da quantificação da fase mervinita utilizando-se do método de padrão interno / Abstract: Steel plants are historicalIy associated with environrnental impacts because of their manufacture processoIn that process, there are generations of 135 million tons of slag from 700 million tons of steel produced. The new regulations of environrnental agencies have stimulated research of new uses for the generated wastes. Nowadays, slag is re-used in Portland cement plants, glass manufacture, paving highways, acoustic and thermal insulating, and soil neutralization. Despite those applications, the slag generation is large enough to demand new innovative technologies. In this context, it is necessary to accomplish physical and chemical characterization of slag to extend knowledge of its structure and properties. Analytical methods for chemical and structural determination of slag were applied in blast furnace slag (AL) and steel converter unit slag (CLD) by using X-ray Fluorescence Spectroscopy (FRX) and X-ray Diffraction (DRX). The present research was carried out in two stages: (1) determination of chemical elements presents in slag followed by quantitative analysis of these elements (by FRX); (2) structural characterization followed by quantitative determination of merwinite crystalline phase [CazMg(SiO4)z]present in alI analyzed samples. There were used two methods for FRX characterization of slag: Fundamental Parameter (PF) and Semi-Quantitative Analysis (SQ). Those methodologies were divergence in the results, maybe due to the higher accuracy with PF methodology that utilizes more interactions and sensibility curves in the optimization processoAIso in PF method, there were observed presence of impurities that were not detected in SQ method such as: P, Nb, V, Cr, Y. The DRX analysis showed several stages of crystalline/amorphous structures, determination of crystalline phases even in low concentration and quantification of merwinitic phase by using internal standard method in DRX analysis / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica

Orientador: Antonio Jose Ramirez Londono / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-26T15:15:59Z (GMT). No. of bitstreams: 1 Faria_GuilhermeAbreu_M.pdf: 7344692 bytes, checksum: e531c95d64110532e988972471c0e25d (MD5) Previous issue date: 2014 / Resumo: O objetivo deste trabalho foi desenvolver a metodologia de medição e análise de dados para a instalação experimental XTMS. Esta instalação foi projetada para possibilitar a medição simultânea de difração de raios X e informações térmicas e mecânicas de materiais enquanto estes são submetidas a condições termomecânicas controladas. Esta é uma área de grande interesse para cientistas de materiais uma vez que uma vasta gama de propriedades termomecânicas têm suas origens em propriedades microscópicas que são acessíveis através de dados de difração. Durante o trabalho, foram estudadas estratégias de medição, desenhos de amostras, métodos de processamento e análise de dados, assim como foi feita a caracterização da instalação como equipamento de medida de dados de difração. Como parte do trabalho, a instalação foi aplicada no estudo de casos científicos de interesse, que envolvem tanto diferentes metodologias de ensaios quanto dados de difração que exigem diferentes metodologias de análise. Os estudos consistiram em um ensaio de deformação em uma liga com memória de forma, ensaios de decomposição isotérmica em um aço inoxidável Superduplex UNS-S32750, e um ensaio de dilatometria acompanhado por difração do aço supermartensítico SuperCr13 / Abstract: The aim of this work was to develop measurement and data analysis methodologies for the XTMS experimental installation. This facility was engineered to simultaneously collect X-ray diffraction and thermo-mechanical information of materials as they are subjected to controlled thermo-mechanical conditions. This is an area of great interest for material scientists given the wide range of thermo-mechanical properties correlated with microscopic properties which are accessible through X-ray diffraction. Developments performed during this work include the development and/or study of measurement strategies, sample designs, and data processing and analysis, as well as the characterization of the XTMS installation as an X-ray diffraction station. As part of the work, the installation was used to study several cases of scientific interest, involving different testing and data analysis methodologies. The studies performed were the deformation of a shape memory alloy, the isothermal ferrite decomposition on a Superduplex stainless steel UNS-S32750, and phase transformations on a SuperCr13 supermartensitic steel through dilatometry coupled with time resolved X-ray diffraction / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica

Orientador: Lisandro Pavie Cardoso / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Física Gleb Wataghin / Made available in DSpace on 2018-08-30T18:16:34Z (GMT). No. of bitstreams: 1 Freitas_HugoEugeniode_M.pdf: 2201633 bytes, checksum: 992e7c3d4fcb71e7f0d75a25eba2bb39 (MD5) Previous issue date: 2016 / Resumo: No presente trabalho estudou-se a diferença entre dois tratamentos térmicos realizados em amostras de Si(111) implantadas com íons Cr+, utilizando-se a difratometria de raios X para policristais e a refletividade de raios X, assim como, curvas de rocking e difração múltipla de raios X usando radiação sincrotron que são aplicadas aos monocristais. O tratamento térmico posterior das amostras resulta numa melhoria da qualidade cristalina, mas leva à formação de trincas e extensos defeitos, devido à grande diferença na expansão térmica entre siliceto e silício pelas altas tensões induzidas. Portanto, há um grande interesse tecnológico na obtenção de camadas contínuas de alta qualidade com um mínimo de distorções induzidas no substrato. Esta é a motivação do presente trabalho: obter camadas finas de CrSi2 de alta qualidade cristalina na subsuperfície de substratos Si(111) e com o mínimo de deformações na matriz hospedeira usando implantação de íons a baixa energia. Serão explorados dois distintos tipos de tratamentos térmicos: o recozimento tradicional a vácuo em forno do tipo mufla (FA - furnace annealing) e o recozimento térmico rápido (RTA - rapid thermal annealing) em atmosfera de argônio. A formação da fase semicondutora hexagonal do CrSi2 foi confirmada por difratometria de raios X nas amostras tratadas termicamente e mostrou uma melhor qualidade cristalina obtida no recozimento FA. O modelo proposto de uma camada superficial de SiO2 fina (8?2) nm sobre uma ou duas camadas de CrSi2 (21?5) nm acima do substrato de Si(111) foi confirmado, a partir das medidas de refletividade de raios X, que também permitiu observar a maior difusão dos íons de Cr+ na amostra tratada com FA por maior tempo. Devido a este tratamento térmico promover, a altas temperaturas, uma maior difusão dos íons implantados, concluiu-se que o tratamento térmico mais propício para a fabricação de semicondutores baseados em CrSi2 é o tratamento por RTA. Varreduras Renninger obtidas da difração múltipla de raios X mostraram que a implantação de Cr+ em Si(111) e posterior recozimento não induz alteração de simetria nas amostras, apenas uma pequena relaxação da distorção tetragonal detectada para a amostra 800º C com tratamento FA. Mapeamentos acoplados dos ângulos de incidência (?) e azimutal (?) para a condição exata de reflexões secundárias Bragg-Superfície (BSD) da difração múltipla não permitiram detectar modificações estruturais de superfície nas amostras analisadas, após os dois tratamentos térmicos a 800º C que foram considerados / Abstract: In this work, the effect of the two heat treatments suffered by Si(111) samples implanted with Cr+ ions has been studied by means of X rays powder diffraction and X rays reflectivity, as well as, the single crystal techniques rocking curves and synchrotron X rays multiple diffraction. The heat treatment of the samples subsequent to the implantation results in an improved crystal quality, but leads to cracks formation and extensive damage due to the large difference between the thermal expansion coefficients of silicide and silicon induced by the applied high voltages. Therefore, there is a great technological interest in obtaining high quality continuous layers with a minimum induced distortion into the substrate. This is the motivation of the present work: to obtain CrSi2 thin layers of high crystalline quality in the subsurface of Si(111) substrates with minimal deformations in the host matrix using low energy ion implantation. Two distinct thermal treatments are analyzed: traditional annealing in vacuum oven muffle type (FA - furnace annealing) and rapid thermal annealing (RTA - rapid thermal annealing) in argon atmosphere. The formation of the semiconductor CrSi2 hexagonal phase was confirmed by X ray powder diffraction in the annealed samples that has also shown an improved crystalline quality observed in FA annealing process. The proposed model of a thin (8?2) nm SiO2 surface layer on top of one or two (21?5) nm thick CrSi2 layers above the Si(111) substrate was confirmed from the X ray reflectivity measurements, that has also allowed to observe further diffusion of Cr + ions into the sample implanted and FA annealed for a longer time. Since this heat treatment promotes, at high temperatures, a greater diffusion of the implanted ions, it was found that RTA is the most suitable treatment for the fabrication of semiconductor-based CrSi2. Renninger scans of the X ray Multiple Diffraction have shown that the Cr+ ions implantation in Si(111) process with a subsequent annealing does not induce symmetry change in the samples, just a small relaxation of the tetragonal distortion detected for the 800 ºC sample after FA treatment. Mappings of the incidence (?) and azimuthal (?) coupled angles monitoring the exact multiple diffraction condition for the Bragg-Surface Diffraction (BSD) secondary reflections were not able to detect structural changes along the analyzed samples surfaces, after the two distinct annealed processes considered at 800º C / Mestrado / Física / Mestre em Física / 132986/2014-0 / CNPQ