• Refine Query
  • Source
  • Publication year
  • to
  • Language
  • 1
  • 1
  • Tagged with
  • 2
  • 1
  • 1
  • 1
  • 1
  • 1
  • 1
  • 1
  • 1
  • 1
  • 1
  • 1
  • 1
  • 1
  • 1
  • About
  • The Global ETD Search service is a free service for researchers to find electronic theses and dissertations. This service is provided by the Networked Digital Library of Theses and Dissertations.
    Our metadata is collected from universities around the world. If you manage a university/consortium/country archive and want to be added, details can be found on the NDLTD website.
1

Delaktighet i förskolan : Möjlighet eller hinder?

Cervin, Nicklas January 2014 (has links)
Syftet med uppsatsen är att göra en undersökning av diskurser om delaktighet i förskolan. Metoden för datainsamlingen är kritisk diskursanalys utifrån Norman Fairclough (1992). Det är en diskursanalys av texter och inte en undersökning av diskurser hämtade från verkligheten i någon förskola. Diskursanalysen görs på fem akademiska avhandlingar, som studeras i förhållande till barns delaktighet. Urvalet av avhandlingarna baseras på att de är relevanta för ämnet delaktighet. Slutsatser i studien är att diskurser av struktur, individualitet och makt- och kategoriseringsprocesser är övergripande områden som påverkar barns delaktighet. Diskurserna inom respektive områden uppvisar tydliga tendenser på att vara öppna för förändring inom forskningen genom avhandlingarna. Fyra av de fem avhandlingarna visar på resultat om att barns delaktighet har stora svårigheter att få genomslag ute i förskoleverksamheterna. Den femte (Hamerslag) beskriver delaktighetsmöjligheterna vara mer framtidspositiva. Specialpedagogik finns med som teoretisk utgångspunkt i de avhandlingar som är undersökta. Specialpedagogiken med dess mångfaldighet kan till synes vara med och påverka de pedagogiska svårigheterna i rätt riktning. Det krävs då att samspelet fungerar mellan olika parter i förskolan, och med det omgivande samhället.
2

Tuning the Curie temperature and phase fraction of FeNi25-based alloys with Mn and Co for magnetocaloric applications

Sanglé-Ferrière, Marie January 2020 (has links)
This paper discusses the search of an FeNi25-based alloy with a face-centered cubic crystal structure exhibiting a Curie point around room temperature, for magnetocaloric applications. Fe was substituted in various amounts with FCC-stabilising elements Mn and Co as these elements respectively decrease and increase the Curie Temperature, thus enabling to tune the Curie point. Three characterization methods were carried out on the samples: Magneto- thermo-gravimetry (MTG), X-ray diffraction (XRD) and finally, vibrating sample magnetometer (VSM) measurements were performed. All samples displayed several Curie points, each corresponding to various FCC phases. Also, the last sample, FeNi25Mn6Co2, had an FCC phase fraction of almost 99% and presented two Curie points in the continuity of one another one at -35°C and another at 91°C. Hence, at room temperature, the sample underwent a magnetic phase transition passing from its ferromagnetic state to a paramagnetic one. / Detta arbete består i att utröna möjligheterna att med utgångspunkt från den binära sammansättningen FeNi25 erhålla en ytcentrerad kubisk fas (fcc) med en Curie punkt vid rumstemperatur. Syftet är att använda dessa legeringar i magnetokaloriska tillämpningar. Strategin är att både Mn och Co är fcc stabliliserande grundämnen, och att Mn sänker och Co ökar Curie temperaturen. Tre olika karakteriseringsmetoder användes; röntgendiffraktometri (struktur), Magneto-Termo-Gravimetri (magnetisering vs temperatur) och konventionell magnetometri vid rumstemperatur (magnetisering vs magnetiskt fält, Vibrating Sample Magnetometry VSM). Resultaten visar att även om kristallstrukturen i det närmaste är fullständigt fcc, så ger de magnetiska mätningarna vid handen att flera olika faser är vid handen med avesvärt olika Curie temperaturer. Som en illustration av detta förhållande kan nämnas att sammansättningen FeNi25Mn6Co2 uppvisar en fcc-fraktion på i det närmaste 99%, men har vid en M(T) mätning ett förlopp som enklast förklaras med en Curie punkt vid ca -35C och en ytterligare vid ca 90°C. Denna observation signalerar att de magnetiska egenskaperna torde vara mer beroende av exakt distribution av de ingående atomslagen i fcc strukturen än vad de röntgendiffraktometriska undersökningarna kan detektera.