Dissertação (mestrado)—Universidade de Brasília, Faculdade de Ceilândia, Programa de Pós-Graduação em Ciências da Reabilitação, 2017. / Submitted by Raquel Almeida (raquel.df13@gmail.com) on 2018-03-22T17:20:16Z No. of bitstreams: 1 2017_KareninaArraisGuidaModesto.pdf: 642204 bytes, checksum: 254c36e2881f635e3a7b287c35428fc0 (MD5) / Approved for entry into archive by Raquel Viana (raquelviana@bce.unb.br) on 2018-03-26T17:54:59Z (GMT) No. of bitstreams: 1 2017_KareninaArraisGuidaModesto.pdf: 642204 bytes, checksum: 254c36e2881f635e3a7b287c35428fc0 (MD5) / Made available in DSpace on 2018-03-26T17:54:59Z (GMT). No. of bitstreams: 1 2017_KareninaArraisGuidaModesto.pdf: 642204 bytes, checksum: 254c36e2881f635e3a7b287c35428fc0 (MD5) Previous issue date: 2018-03-26 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES). / Desenho do estudo: Estudo randomizado, controlado e cego. Introdução. A estimulação elétrica neuromuscular (EENM) é amplamente utilizada para induzir aumento da força muscular, no entanto, nenhum estudo comparou os efeitos da corrente russa (CR) com uma corrente pulsada (CP) após um programa de treinamento. Objetivos. Avaliar os efeitos das correntes russa e pulsada no sistema neuromuscular após um período de treinamento de seis semanas. Métodos. Vinte e sete jogadores de futebol do sexo masculino foram randomizados em três grupos: 1) grupo controle, 2) CR (2500 Hz, burst 100 Hz, duração da fase 200 μs) e 3) CP (100 Hz e 200 μs). Os grupos experimentais foram treinados durante seis semanas, com três sessões por semana. Torque voluntário máximo e torque evocado, arquitetura muscular, desconforto sensorial e atividade eletromiográfica foram avaliados antes e após o período de seis semanas. Resultados. O torque evocado aumentou nos grupos CR (169,5 ± 78,2%, p<0,01) e CP (248,7 ± 81,1%, p<0,01) sem diferença entre eles. A espessura muscular e o ângulo de penação aumentaram em CR (8,7 ± 3,8% e 16,7 ± 9,0%, p<0,01) e CP (16,1 ± 8,0% e 27,4 ± 11,0%, p<0,01). CP demonstrou valores mais baixos para EVA (38,8 ± 17,1%, p<0,01). Não há diferença significativa para CIVM e RMS (p>0,05). Conclusão. Embora o uso generalizado de CR na prática clínica, os programas de treinamento de CR e CP produziram adaptações neuromusculares semelhantes em jogadores de futebol. No entanto, a CP gerou menor desconforto percebido. / Study design: Blinded randomized controlled trial. Background. Neuromuscular electrical stimulation (NMES) is widely used to induce muscular strength increase, however, no study has compared Russian current (RC) with Pulsed current (PC) effects after a training program. Objectives. To evaluate the effects of RC and PC NMES currents on the neuromuscular system after a six-week training period. Methods. Twenty-seven male soccer players were randomized in three groups: 1) control group, 2) RC (2500 Hz, burst 100 Hz, phase duration 200 μs) and 3) PC (100 Hz and 200 μs). Experimental groups were trained during six weeks, with three sessions per week. Maximal voluntary and evoked torque, muscle architecture, sensory discomfort and electromyographic activity were evaluated before and after the six weeks period. Results. Evoked torque increased in RC (169.5±78.2 %, p<0.01) and PC groups (248.7±81.1 %, p<0.01) without difference amongst them. Muscle thickness and pennation angle increased in RC (8.7±3.8 % and 16.7±9.0%, p<0.01) and PC (16.1±8.0 % and 27.4±11.0 %, p<0.01). PC demonstrated lower values for VAS (38.8±17.1 %, p<0.01). There is no significant difference for MVIC and RMS (p>0.05). Conclusion. Although the widespread use of RC in clinical practice, RC and PC training programs produced similar neuromuscular adaptations in soccer players. Nonetheless, PC generated less perceived discomfort.

Conselho Nacional de Desenvolvimento Científico e Tecnológico / Revestimentos produzidos a partir de ligas de Zn-Co são comumente utilizados em indústrias (aeronáutica, de isoladores elétricos e automobilística, por exemplo) devido à sua ótima resistência à corrosão, principalmente quando comparados aos tradicionais revestimentos de Zn puro. Na co-deposição de zinco com metais, como o ferro, cobalto e níquel, ocorre o que se chama de deposição anômala, onde o metal menos nobre (zinco) é preferencialmente depositado, independente do modo de corrente aplicada (contínua ou pulsada). Recentemente, diversos trabalhos relacionam a produção de eletrodepósitos de liga Zn-Co a partir de banhos ambientalmente não agressivos, a fim de substituir os banhos alcalinos extremamente tóxicos, a base de cianeto. Na presente dissertação foram produzidos revestimentos de ligas de Zn-Co sobre substrato de aço carbono, empregando corrente contínua ou corrente pulsada simples, a partir de banhos contendo diferentes concentrações de Co2+ (0,05 mol/L e 0,10mol/L), 0,05 mol/l de Zn2+ e citrato de sódio (0,10 mol/L) como agente complexante, sob condições agitadas. Quatro diferentes valores de densidade de corrente (10 A/m2, 20 A/m2, 40 A/m2 e 80 A/m2) e de frequência de pulso (100 Hz, 500 Hz, 1000 Hz, 2000 Hz) foram aplicados para a produção da liga a partir dos dois banhos, tendo como objetivo avaliar a influência dos parâmetros de deposição(concentração de Co (II), densidade de corrente aplicada e, no caso de deposição por corrente pulsada simples, também da frequência de pulso), nas variáveis eficiência de corrente catódica, composição da liga, densidade de corrente de corrosão, microestrutura e morfologia dos depósitos de liga Zn-Co. As cores das camadas obtidas variaram do cinza claro ao escuro, quase sempre sem brilho, independente do modo de corrente empregado. Foi verificado que o processo normal de eletrodeposição foi prevalente na produção de revestimentos por corrente contínua, enquanto que apenas deposição anômala foi observada quando do uso de corrente pulsada. A maior eficiência de corrente catódica (60%) foi obtida, para corrente contínua, nas condições de menor concentração de Co2+ (0,05 mol/L) e maior densidade de corrente (80 A/m2). Nestas mesmas condições foi determinada uma eficiência de corrente catódica de 98% para corrente pulsada simples na freqüência de 2000 Hz. Maiores teores do metal mais nobre (cobalto) foram alcançados em maiores densidades de corrente para todas as condições empregadas. Os revestimentos assim obtidos apresentavam os menores valores de tamanho de grão, para cada uma das soluções estudadas. Os demais parâmetros estudados também influenciaram na granulometria e na morfologia das ligas obtidas. Revestimentos com melhor resistência à corrosão, contendo teores de cobalto entre aproximadamente 8 e 10% m/m, foram produzidos a partir do banho com maior concentração de Co2+, sob corrente pulsada simples / Zn-Co alloys coatings are commonly used in the industry (aerospace, automotive and electrical insulators, for example) due to their great corrosion resistance, mainly when compared to pure zinc coatings. In the zinc co-deposition with different metals, such as iron, cobalt or nickel, it is observed an anomalous deposition, in which the less noble metal (zinc) is preferably deposited, regardless the current type applied (direct or pulsed). Recently, several studies relate the production of electrodeposited Zn-Co alloys from environmentally non-aggressive baths to substitute the extremely toxic cyanide-based alkaline baths. In this dissertation, Zn-Co alloy coatings were produced on carbon steel substrate using direct or simple pulsed currents, from baths with different Co2+ concentrations (0.05 mol/L and 0.10 mol/L), 0.10 mol/L of Zn2+and sodium citrate (0.10 mol/L) as a complexing agent, under stirring. Four different current densities values (10 A/m2, 20 A/m2, 40 A/m2 and 80 A/m2) and four different pulse frequencies values (100 Hz, 500 Hz, 1000 Hz and 2000 Hz) were applied in order to obtain the alloys from both baths, aiming to assess the influence of the deposition parameters (Co (II) concentration, current density applied, and also pulse frequency, for the simple pulsed current process) in the variables cathodic current efficiency, alloy composition, current corrosion density, and Zn-Co alloy deposit microstructure and morphology. The obtained layers colours varied from light to dark grey, normally dull, regardless the current type used. Normal electrodeposition process was predominant when direct current was used, whereas only anomalous deposition was observed when using pulsed current. The highest cathodic current efficiency (60%) was obtained in direct current for the lowest Co2 + concentration (0.05 mol / L). Under these same conditions it was determined a cathodic current efficiency of 98% for single pulsed current, employing the frequency of 2000 Hz Higher content of the noblest metal (cobalt) were achieved for higher current densities for all conditions studied. These coatings presented the smallest grain sizes, for each of the evaluated solutions. The other studied parameters have also influenced in the granulometry and the morphology of the obtained alloys. Coatings presenting the best corrosion resistance, showing the cobalt content between 8 and 10% m/m, were obtained from the highest Co2+ concentration bath, using simple pulsed current

Conselho Nacional de Desenvolvimento Científico e Tecnológico / Revestimentos produzidos a partir de ligas de Zn-Co são comumente utilizados em indústrias (aeronáutica, de isoladores elétricos e automobilística, por exemplo) devido à sua ótima resistência à corrosão, principalmente quando comparados aos tradicionais revestimentos de Zn puro. Na co-deposição de zinco com metais, como o ferro, cobalto e níquel, ocorre o que se chama de deposição anômala, onde o metal menos nobre (zinco) é preferencialmente depositado, independente do modo de corrente aplicada (contínua ou pulsada). Recentemente, diversos trabalhos relacionam a produção de eletrodepósitos de liga Zn-Co a partir de banhos ambientalmente não agressivos, a fim de substituir os banhos alcalinos extremamente tóxicos, a base de cianeto. Na presente dissertação foram produzidos revestimentos de ligas de Zn-Co sobre substrato de aço carbono, empregando corrente contínua ou corrente pulsada simples, a partir de banhos contendo diferentes concentrações de Co2+ (0,05 mol/L e 0,10mol/L), 0,05 mol/l de Zn2+ e citrato de sódio (0,10 mol/L) como agente complexante, sob condições agitadas. Quatro diferentes valores de densidade de corrente (10 A/m2, 20 A/m2, 40 A/m2 e 80 A/m2) e de frequência de pulso (100 Hz, 500 Hz, 1000 Hz, 2000 Hz) foram aplicados para a produção da liga a partir dos dois banhos, tendo como objetivo avaliar a influência dos parâmetros de deposição(concentração de Co (II), densidade de corrente aplicada e, no caso de deposição por corrente pulsada simples, também da frequência de pulso), nas variáveis eficiência de corrente catódica, composição da liga, densidade de corrente de corrosão, microestrutura e morfologia dos depósitos de liga Zn-Co. As cores das camadas obtidas variaram do cinza claro ao escuro, quase sempre sem brilho, independente do modo de corrente empregado. Foi verificado que o processo normal de eletrodeposição foi prevalente na produção de revestimentos por corrente contínua, enquanto que apenas deposição anômala foi observada quando do uso de corrente pulsada. A maior eficiência de corrente catódica (60%) foi obtida, para corrente contínua, nas condições de menor concentração de Co2+ (0,05 mol/L) e maior densidade de corrente (80 A/m2). Nestas mesmas condições foi determinada uma eficiência de corrente catódica de 98% para corrente pulsada simples na freqüência de 2000 Hz. Maiores teores do metal mais nobre (cobalto) foram alcançados em maiores densidades de corrente para todas as condições empregadas. Os revestimentos assim obtidos apresentavam os menores valores de tamanho de grão, para cada uma das soluções estudadas. Os demais parâmetros estudados também influenciaram na granulometria e na morfologia das ligas obtidas. Revestimentos com melhor resistência à corrosão, contendo teores de cobalto entre aproximadamente 8 e 10% m/m, foram produzidos a partir do banho com maior concentração de Co2+, sob corrente pulsada simples / Zn-Co alloys coatings are commonly used in the industry (aerospace, automotive and electrical insulators, for example) due to their great corrosion resistance, mainly when compared to pure zinc coatings. In the zinc co-deposition with different metals, such as iron, cobalt or nickel, it is observed an anomalous deposition, in which the less noble metal (zinc) is preferably deposited, regardless the current type applied (direct or pulsed). Recently, several studies relate the production of electrodeposited Zn-Co alloys from environmentally non-aggressive baths to substitute the extremely toxic cyanide-based alkaline baths. In this dissertation, Zn-Co alloy coatings were produced on carbon steel substrate using direct or simple pulsed currents, from baths with different Co2+ concentrations (0.05 mol/L and 0.10 mol/L), 0.10 mol/L of Zn2+and sodium citrate (0.10 mol/L) as a complexing agent, under stirring. Four different current densities values (10 A/m2, 20 A/m2, 40 A/m2 and 80 A/m2) and four different pulse frequencies values (100 Hz, 500 Hz, 1000 Hz and 2000 Hz) were applied in order to obtain the alloys from both baths, aiming to assess the influence of the deposition parameters (Co (II) concentration, current density applied, and also pulse frequency, for the simple pulsed current process) in the variables cathodic current efficiency, alloy composition, current corrosion density, and Zn-Co alloy deposit microstructure and morphology. The obtained layers colours varied from light to dark grey, normally dull, regardless the current type used. Normal electrodeposition process was predominant when direct current was used, whereas only anomalous deposition was observed when using pulsed current. The highest cathodic current efficiency (60%) was obtained in direct current for the lowest Co2 + concentration (0.05 mol / L). Under these same conditions it was determined a cathodic current efficiency of 98% for single pulsed current, employing the frequency of 2000 Hz Higher content of the noblest metal (cobalt) were achieved for higher current densities for all conditions studied. These coatings presented the smallest grain sizes, for each of the evaluated solutions. The other studied parameters have also influenced in the granulometry and the morphology of the obtained alloys. Coatings presenting the best corrosion resistance, showing the cobalt content between 8 and 10% m/m, were obtained from the highest Co2+ concentration bath, using simple pulsed current

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / This Master s Dissertation is proposes the development of a charge management system of a bank of 16 lead-acid batteries with 7Ah load capacity, commonly used in Uninterruptible Power Supplies (UPS). This system aims to ensure that these batteries reach a full charge status faster than the conventional way. To this, it was chosen to make the modification of the pulsed current charging method, in order to reduce problems, such as elevation of bus voltage to return the energy to it, or dissipation of that energy in a resistance, resulting in lower system efficiency, inherent in the method taken as a basis when the battery power withdrawal interval occurs. For the development of the suggested charging system the static converter Full-Bridge Isolated with modulation Phase Shift was chosen. To implement the digital control as well as its practical development in the same laboratory the simplified modeling of this converter was made. The results of simulation and experimental to validate the method are presented. / Esta dissertação de mestrado tem como proposta o desenvolvimento de um sistema de gerenciamento de carga de um banco de 16 baterias de chumbo ácido, com capacidade de carga de 7Ah, comumente utilizado em Fontes Ininterruptas de Energia (UPS). Este sistema visa garantir que estas baterias cheguem a um estado de carga completo e de forma mais rápida que a convencional. Para isto, foi escolhido fazer a modificação do método de carga de corrente pulsada, com o objetivo de reduzir problemas inerentes do método tomado como base, quando ocorre o intervalo de retirada de energia da bateria, tais como: elevação da tensão do barramento ao retornar a energia para ele, ou, dissipar esta energia em uma resistência, o que acarreta em baixa eficiência do sistema. Para o desenvolvimento do sistema de carga sugerido foi escolhido o conversor estático Full-Bridge Isolado com modulação Phase Shift. Foi feita a modelagem simplificada deste conversor, para a implementação do controle digital, assim como o desenvolvimento prático do mesmo em laboratório. São apresentados os resultados de simulação e experimentais para validar o método.