Efeito da sinerese "pos-maturação" na infiltração marginal de materiais hibridos de ionomero de vidro/resina compostaSantos, Alex Jose Souza dos 13 February 2001 (has links)
Orientador : Jose Roberto Lovadino / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-27T15:51:54Z (GMT). No. of bitstreams: 1
Santos_AlexJoseSouzados_M.pdf: 3948991 bytes, checksum: c59e4e3b93890b3a53ecb5d5e67e339c (MD5)
Previous issue date: 2001 / Resumo: O objetivo desse estudo in vitro foi avaliar o efeito da sinérese "pós. maturação" na infiltração marginal de materiais restauradores. Cavidades cilíndricas foram preparadas em blocos de esmalte e de dentina, obtidos de superficies coronárias e radiculares de 120 incisivos bovinos. As ~4 - ;F cavidades foram restauradas com Dyract (Dy), Compoglass F (Co), Vitremer (Vi), Fuji II LC (Fu), Ketac-Fil PLus (Ke) e Z 100 (Zl). Os espécimes foram termociclados por 3000 ciclos, entre temperaturas de 5I2°C e 55I2°C, e metade foi submetida à desidratação por 45 minutos em temperatura de 30°C e 60% de umidade relativa do ar. Os espécimes foram imersos em solução aquosa de azul de metileno a 2%, por 12 horas, e a infiltração marginal foi mensurada quantitativamente através de espectrofotometria. A análise estatística ANOV A, seguida pelo teste de Tukey (p < 0,05), mostrou diferenças estatísticas significativas entre as médias de infiltração marginal entre os materiais testados no esmalte (Ke<Vi=Dy; Dy=Fu=ZI; Fu=ZI=Co) e na dentina (Ke<Vi=Co=Fu=ZI; Co= Fu=ZI=Dy). A sinérese aumentou significativamente as médias de infiltração marginal para todos os materiais (p < 0,05) e de forma menos acentuada na dentina (11,6%) que no esmalte (27,8%). Os resultados permitiram concluir que nenhum dos sistemas restauradores foi capaz de conter a infiltração marginal. Os materiais híbridos foram melhores que o cimento de ionômero de vidro convencional e a maioria foi similar à resina composta. A sinérese aumentou significativamente a infiltração marginal em todos os materiais híbridos, mostrando que eles ainda são susceptíveis à desidratação / Abstract: The aim of this in vitro study was to evaIuate the effect of the dehydration "post-maturaty" in the microIeakage of gIass-ionomer composite resins hybrids materiaIs. CylindricaI cavities were prepared in scraps of enameI and dentin. These scraps were obtained of the root and coronary surfaces of 120 teeth bovine incisive. The cavities were filling with Dyract (Dy), CompogIass F (Co), Vitremer (Vi), Fuji II LC (Fu) Ketac-FiI PLus (Ke) and Z 100 (Zl). All the sampIes were thermally stressed for 3000 cieles with dwell time at 5:t2°C e 55:t2°C. HaIf of aII the sampIes were submitted to the dehydration by 45 minutes at 30°C and 60% ofreIative humidity ofthe air. The sampIes were immersed in methyIene bIue for 12 hours. The microleakage was quantified spectrophotometrically, and the data were statistically anaIyzed by ANOV A and Tukey test (P < 0.05). The resuIts showed significant differences among the microIeakage the materiaIs tested (P < 0.01), in the enameI (Ke<Vi=Dy; Dy=Fu=ZI; Fu=ZI=Co) and in the dentin (Ke<Vi=Co=Fu=ZI; Co=Fu=ZI =Dy). The dehydration increased the averages of microIeakage of aIl the materiaIs significantly (P < .01) and in a Iess way accentuated in the dentin (11.6%) that in the enameI (27.8%). The resuIts showed that no one ofthe restorative systems was able to prevent leakage compIeteIy. The hybrid materiaIs were better than the gIass-ionomer cement and aImost aII the materiaIs were similar to the resin composite tested. The deydration increased the microleakage in aIl the hybrid materiais tested, showing that they are still susceptibIe to dehydration conditions / Mestrado / Dentística / Mestre em Clínica Odontológica
|
132 |
Estudo de propriedades mecanicas : resistencia a compressão e compressão diametral de uma resina composta modificada por poliacido (compomero)Gevaerd, Sylvio Palermo 27 July 2018 (has links)
Orientador: Luis Roberto Marcondes Martins / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-27T14:27:29Z (GMT). No. of bitstreams: 1
Gevaerd_SylvioPalermo_M.pdf: 1075765 bytes, checksum: 5d4fa0ff2529154e6b43e9dbe15f8d55 (MD5)
Previous issue date: 2000 / Resumo: Este trabalho teve por objetivo estudar a resistência à compressão e resistência à compressão diametral de uma resina composta modificada por poliácido (compômero). O estudo foi realizado com vinte corpos de prova de 4,0mm de diâmetro e 6,0mm de altura nos tempos de 10 minutos após a fotopolimerização e de 24 horas, com armazenamento em água à temperatura de 37°C. Foi utilizada uma máquina de ensaio Universal EMIC DL 500 com velocidade de 0,75 mm/min para determinar o valor em MPa (Mega Pascal) necessário para fratura do material. Os resultados foram submetidos ao teste de "t" ao nível de 5% de significância. Verificou-se que ocorreu aumento na resistência à compressão após 24 horas com armazenamento em água e pequeno aumento na resistência à compressão diametral, sem diferença estatística significativa. Os resultados nos permitiram concluir que ocorre endurecimento do material após armazenamento em água por 24 horas / Abstract: The aim of the present study is to survey the mechanical properties ¿ compressive strength and diametral compressive strength - of a polyacid-modified composite resin (compomer) The specimens used in this study were 4.0mm in diameter and 6.0mm inheight. They were tested at two different times: 10 minutes after light curing and also after being stored in water for 24 hours at 37°C. A Universal testing machine EMIC OL 500 at the speed of 0.75 mm/min was used to determine the necessary strength to fracture the material. The results were submitted to t Student analysis at a 0.5% significance leveI. After 24 hours of storage in water an increase in the compressive strength was observed. It was also observed a slight increase in the diametral compressive strength, however it was not statistically significant. The results allowed us to conclude that the material is hardened after 24 hours of storage in water / Mestrado / Mestre em Materiais Dentários
|
133 |
Avaliação in vitro da microinfiltração marginal de tres sistemas adesivos em restaurações classe II com resina composta em dentes bovinosCosta, Jose Ferreira 29 March 2001 (has links)
Orientador : Luiz Andre Freire Pimenta / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-27T20:55:39Z (GMT). No. of bitstreams: 1
Costa_JoseFerreira_M.pdf: 2100309 bytes, checksum: 6cda6593f7b4e18b39d5880552b2b201 (MD5)
Previous issue date: 2001 / Resumo: A proposta deste estudo foi investigar in vítro a microinfiltração marginal em restaurações classe 11 realizadas com três sistemas adesivos e resina composta em dentes bovinos. Setenta e cinco cavidades classe 11, do tipo "slot vertical" foram preparadas, com margem gengival localizada 1,0 mm além da junção esmalte / Abstract: The aim of this study was to evaluate in vitro marginal microleakage of three bonding systems on composite resin restorations in bovine teeth. Seventy-five slot vertical class 11 cavities were prepared with gingival margin located 1,0 mm into cementum and they were numbered and divided in three different groups according to the bonding system used: group SBMP - several steps bonding system, Mutipurpose Scotchbond®; group PB2.1 - one step bonding system, Prime & Bond 2.1®; group CLB2V - self-ecthing bonding system, Clearfil Liner Bond 2V®. The cavities were filled with Tetric Ceram® composite resin with three increments. They were polished and the teeth were impermeabilized properly and submetted to 1000 cycles in distilled water at 5°C±2°C and 55°C±2°C temperatures. Following that process, the teeth were immersed in 2% Methylene Blue tamponed for 4 hours. They were sectioned in the center of the restorations and the specimens were obtained and analyzed with regard to the degree of leakage in stereocope magnifying glass 50X magnitication. The results of the present study: group SBMP - 936,50; group PB2.1 - 1053,00; group CLB2V - 860,50. Although the Clearfil Liner Bond 2®, has showed best performance, a Kruskal Wallis test revealed no statistically siggniticant difference in microleakage to a=0,4531 and p>0,05. It is concluded that three bonding systems were not able to prevent the microleakage in gingival margin of class " composite resin restorations at ali and the self-etching adhesive had equal behavior comparing to bonding system which use phosphoric acid as a conditioner / Mestrado / Dentística / Mestre em Clínica Odontológica
|
134 |
Avaliação "in vitro" da infiltração marginal em restaurações de resina composta em cavidades classe II utilizando diferentes combinações restauradorasCastro, Ana Karina Barbieri Bedran de 29 March 2001 (has links)
Orientador : Luiz Andre Freire Pimenta / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-27T21:06:54Z (GMT). No. of bitstreams: 1
Castro_AnaKarinaBarbieriBedrande_M.pdf: 3358547 bytes, checksum: f08d2334343db4f45a8c783fca6a268f (MD5)
Previous issue date: 2001 / Resumo: O objetivo deste trabalho, "in vitro", foi avaliar qualitativamente, através da penetração de corante, dois sistemas restauradores, e o efeito de uma camada intermediária de resina composta de baixa viscosidade. Foram selecionados 90 dentes bovinos, os quais tiveram parte da coroa seccionada a fim de padronizar comprimento de 4 mm no sentido ocluso-gengival. Em seguida, foram realizados preparos cavitários padronizados, nas faces mesial e distal, simulando classe II tipo "slot" vertical, com término em dentina, totalizando 180 preparos. As cavidades foram aleatoriamente divididas em 6 grupos (n=30): Gl- sistema adesivo Etch & Prime 3.0 (EP) (Oegussa) + resina "compactável" Oefinite (OEF) (Oegussa); G2- sistema adesivo Prime & Bond NT (PB) (Oentsply) + OEF; G3- EP + resina "flow" Wave (W) (SOl) + OEF; G4- PB + resina composta TPH Spectrum (TPH) (Oenstply); G5- EP + TPH; G6- PB + W + TPH. Após o acabamento e polimento, os espécimes foram submetidos a 1500 ciclos térmicos em banhos de 5 :t 2°C e 55 :t 2°C, com duração de 60 segundos para cada banho. Após ciclagem térmica, os dentes foram vedados com esmalte de unha e imersos em solução de azul de metileno a 2%, durante 4 horas. Em seguida, foram realizados seccionamentos ao meio das restaurações e analisadas qualitativamente em lupa estereoscópica (45X), seguindo um padrão de escores em dentina (O a 4). Também foi avaliado o padrão de infiltração (adesivo ou dentinário) dos espécimes que infiltraram. Os dados foram submetidos ao Teste Kappa de reprodutibilidade interexaminadores, e a média dos escores dos 3 examinadores foi analisada pelo Teste não-paramétrico de Kruskall-Wallis e Teste não-paramétrico de Comparação Múltipla com p<0,05. O padrão de infiltração foi analisado pelo Teste Exato de Fisher. Os postos médios dos grupos foram dispostos em ordem crescente dos valores: G4-6723(a). G3- 7258 (ab). G6- 7843 (ab). G5- 93 19 (be). G2- 11297 (e). Gl- 11352 (e) Conclui-se que nenhum dos sistemas utilizados foi capaz de impedir a microinfiltração, e o uso de uma resina "flow" reduziu os valores de infiltração para a resina OEF. O padrão de infiltração para os grupos que utilizaram PB foi dentinário, apresentando-se predominantemente adesivo para EP / Abstract: The purpose of this study was to evaluate the "in vitro", marginalleakage, with dye penetration, of two restorative systems and the application of a flowable composite resin as an intermediate layer. Ninety bovine teeth were selected and had part of the crown sectioned allowing a standardization of 4 mm of height from ocluso-gengival proximal margins. Standardized cavities preparations simulating class 11 type box were design with gingival margin at dentin, on mesial e distal faces. The cavities were randomly divided in 6 groups (n=30): G1- adhesive system Etch & Prime 3.0 (EP) (Oegussa) + Oefinite composite resin (OEF) (Oegussa); G2- adhesive system Prime & Bond NT (PB) (Oentsply) + OEF; G3- EP + Wave flowable resin (W) (501) + DEF; G4- PB + TPH Spectrum composite resin (TPH) (Oenstply); G5- EP + TPH; G6- PB + W + TPH. After finishing and polishing, the specimens were subjected to 1500 thermal cycles in bath of 5 :i: 2°C e 55 :i: 2°C with 60 seconds dwell time each bath. After thermocycling, the specimens were sealed with nail vamish and immersed for 4 hours in a 2% solution of methylene blue. Than the specimens were sectioned longitudinally through the center of the restoration and qualitatively evaluated by stereomicroscopy (45X), following a ranked score for dentin margin (O a 4). The leakage partem (adhesive or dentin) was also evaluated for those specimens that had leakage. The data were subjected to a reproducibility Kappa T est and the mean of the 3 examiners scores were analyzed by Kruskall-Wallis non-parametric Test and multiple comparison non-parametric Test (p<0.05). For leakage partem Fisher Exact Test was used. The ranked values of the groups were expressed in decreasing order: G4- 67.23 (a); G3- 72.58 (ab); G6- 78.43 (ab); G5- 93.19 (be); G2- 112.97 (e); G1- 113.52 (e). It was concluded that all systems used were not able to impede the microleakage, and the use of a flowable resin decrease the values of leakage for the resin OEF. The partem of leakage for the groups that used PB was at dentin, showing mostly adhesive to EP / Mestrado / Dentística / Mestre em Clínica Odontológica
|
135 |
Estudo in situ do efeito do polimento e da proteção superficial no manchamento de ionomeros de vidro modificados por resinaRibeiro, Ana Paula Granato 19 October 2000 (has links)
Orientador: Monica Campos Serra / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-28T12:12:07Z (GMT). No. of bitstreams: 1
Ribeiro_AnaPaulaGranato_D.pdf: 10599603 bytes, checksum: ccdbdc527654c4da49f87605bf32b908 (MD5)
Previous issue date: 2000 / Resumo: O objetivo deste estudo in situ foi avaliar o efeito do polimento e da proteção superficial no manchamento de ionômeros de vidro modificados por resina (VITREMER e PHOTAC-FIL) O polimento imediato foi comparado ao tardio, realizado em diferentes estágios da reação da presa (1, 24 e 168 horas após a fotoativação). Para a avaliação da proteção superficial, os materiais foram divididos em três grupos: sem proteção, protetores indicados pelos fabricantes (FINISHING GLoss e KETAC GLAZE)e resina fluida HELIOBOND. O efeito do polimento foi avaliado para cada um destes grupos. Espécimens foram confeccionados, fotopolimerizados e, em seguida, os respectivos protetores foram aplicados. Parte dos espécimens recebeu o polimento imediato e os demais foram fixados em dispositivos palatais utilizados por 23 voluntários. Após 1, 24 e 168 horas de permanência na cavidade oral, os espécimens foram sucessivamente removidos dos dispositivos e submetidos ao polimento. Após este procedimento, foram inseridos em tubos de ensaio contendo uma solução de azul de metileno a 0,5%, onde permaneceram por 23 horas. Posteriormente, foram triturados e imersos em ácido nítrico a 65% durante 24 horas. As soluções experimentais foram diluídas, centrifugadas e os sobrenadantes utilizados para as leituras espectrofotométricas (607 ?m).Os resultados foram avaliados pela análise de variância com três fatores (material, proteção superficial e polimento). A decomposição da soma de quadrados e a diferença mínima significativa de TuKEY foram empregadas para a análise das interações significativas e das comparações pareadas (? = 5%). Para ambos materiais, os maiores índices de manchamento foram obtidos quando submetidos ao polimento imediato e sem proteção superficial. Os materiais apresentaram diferença estatística somente no estágios iniciais da reação de presa, sendo que os maiores índices de manchamento foram observados no material PHoTAC-FIL.Não houve diferença significativa na efetividade dos protetores superficiais. Concluiu-se que, os protetores superficiais apresentaram efetividade satisfatória, mesmo quando submetidos às condições clínicas, e que o polimento dos ionômeros de vidro modificados por resina não deve ser realizado na mesma sessão clínica / Abstract: The purpose of this in situ study was to evaluate the effect of polishing and surface protection on staining of resin-modified glass-ionomers (VITREMER e PHOTAC-FIL). lmmediate polishing was compared to delayed polishing that was carried out at different stages of the setting process (1, 24 and 168 hours afier light curing). To evaluate surface
protection, the materials were divided in three groups: no protection, manufacturer indicated protectors (FINISHING GLOSS e KETAC GLAZE)and a light-activated bonding resin - HELIOBOND. Immediate and delayed polishing were compared for alI of these groups. Specimens were prepared, subjected to photopolimerization and treated with the respective protectors. Some specimens received immediate polishing while the others were fixed unto palatal appliances used by 23 volunteers. After 1, 24 and 168 hours in the oral environment, the specimens were successively removed from the appliances and polished. Then the
specimens were immersed one by one in tubes containing a 0,5% methylene blue solution during 23 hours. Afterwards they were ground , immersed in 65% nitric acid and kept there for 24 hours. The experimental solutions were diluted, centrifuged and the supematant used by spectrophotometrical measurement (607?m).The data were subjected to analysis of
variance with three factors (material, surface protector and polishing). Sums of squares decompositions followed by TuKEY's least significant difference were used for the analysis of significance interactions and pairwise comparisons (?= 5%). There was a significant effect of materials on staining, which differed in their susceptibility. For both materiaIs, the highest staining indices were obtained by immediate polishing and without surface protection. The materials were only statistically different in the earliest stages of the maturing process, where the highest staining indices were observed in the PHOTAC-FIL. Differences related to the surface protectors were not statistical significant. The conclusions can be drawn that surface protectors reduce the staining of resin-modified glass-ionomers significantly even when submitted to clinical conditions and that the polishing should not be carried out during the same clinic session / Doutorado / Dentística / Doutor em Clínica Odontológica
|
136 |
Avaliação da pigmentação superficial por cafe e vinho em compositos odontologicosDorini, Andre Luis 07 March 2001 (has links)
Orientador : Jose Roberto Lovadino / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-29T01:25:00Z (GMT). No. of bitstreams: 1
Dorini_AndreLuis_D.pdf: 3345552 bytes, checksum: 9ffde2a7b6258c6423593300f5ff791e (MD5)
Previous issue date: 2001 / Resumo: O objetivo deste trabalho foi avaliar a influência de três diferentes sistemas de acabamento e polimento na pigmentação superficial de um compósito de micropartículas (A 110), um para uso universal (Z 250) e um para dentes posteriores (P 60). Corpos-de-prova em forma de disco foram confeccionados em contato com uma matriz de poliéster, estocados por 24 horas em estufa, acabados e polidos com três diferentes técnicas, e após 24 horas imersos por sete dias em duas bebidas corantes, café e vinho. Após a imersão, os espécimes foram triturados e imersos em álcool absoluto, para a remoção do corante absorvido. O manchamento dos espécimes foi avaliado quantitativamente, através de espectrofotometria. Os resultados de manchamento foram A 110 < Z250 < P60, independente do acabamento e polimento aplicado à superfície. O maior manchamento foi obtido com a polimerização contra a matriz de poliéster. Dentre os acabamentos, os resultados foram pontas diamantadas finas e extrafinas < brocas carbide < discos de óxido de alumínio. Dentre os alimentos, o vinho manchou os espécimes significativamente mais do que o café. Este estudo conclui que: a) dentre os materiais testados para o acabamento e polimento da superfície, as brocas carbide e as pontas diamantadas foram os melhores; b) o compósito de micropartículas A 110 tem melhor resistência ao manchamento que o compósito para uso universal Z 250 e o compósito para dentes posteriores P 60; e c) o vinho mancha mais os compósitos odontológicos do que o café / Abstract: The purpose of this study was to evaluate the influence of the three different techniques of finishing and polishing on the pigmentation of a microfilled composite (A 110), a composite for universal use (Z 250) and a composite for posterior use (P60). The specimens were prepared against a matrix band, finished and polished after 24 hours and submitted to staining in two food dyes (coffee and wine) by seven days. After the staining, the specimens were triturated and immersed in alcohol absolute, to extraction of the dyes. The analysis of the staining was performed quantitatively, by a spectrophotometer. The results showed that staining was P 60 > Z 250 > A 110, independent of the finishing or polishing. The bigger staining was obtained with the matrix band, followed by Sof-Lex discs and, at last, with the best results, the diamond burs and the carbide burs. The specimens submitted to wine showed bigger pigmentation that the specimens submitted to coffee. This study conclude: a) that to prevent the staining, the finishing and polishing of the surface is a necessary step during the confection of a composite restoration, and that the best materials for this purpose are the diamond burs and the carbide burs; b) the microfilled composite A 110 have a better resistance to staining that the composite for universal use Z 250 and the composite for posterior use P 60; and c) the wine stain the composites more than coffee / Doutorado / Dentística / Doutor em Clínica Odontológica
|
137 |
Estudo de diferentes fotoiniciadores em cimentos resinosos experimentais fotoativados com duas fontes de luz / Study of diferent photoinitiators in experimental resin cements photoactivated by two light curing unitsSegreto, Dario Raimundo 12 August 2018 (has links)
Orientador: Mario Alexandre Coelho Sinhoreti / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-12T19:29:40Z (GMT). No. of bitstreams: 1
Segreto_DarioRaimundo.pdf: 5148462 bytes, checksum: a1ecd55c05c3403479a26112b9c9eab1 (MD5)
Previous issue date: 2009 / Resumo: O objetivo deste estudo foi avaliar o efeito de diferentes fotoiniciadores no grau de conversão e na resistência da união de cimentos resinosos experimentais, utilizados para
fixação de uma cerâmica à estrutura dental. Sete cimentos resinosos experimentais foram manipulados de maneira que, na matriz orgânica padrão, o único componente variável fosse
o fotoiniciador. Diferentes concentrações e combinações de Canforoquinona (CQ) e Fenilpropanodiona (PPD) foram adicionadas aos cimentos, conforme segue: C5=0,5% p CQ; C8=0,8% p CQ; P5=0,5% p PPD; P8=0,8% p PPD; C1P4=0,1% p CQ e 0,4% p PPD; C4P1=0,4% p CQ e 0,1% p PPD; e C4P4=0,4% p CQ e 0,4% p PPD. O primeiro estudo avaliou o grau de conversão de cimentos resinosos fotoativados através de um disco cerâmico com unidades de fotoativação a base de LED e lâmpada de quartzo-tungstêniohalogênio (QTH). Quarenta e duas amostras foram preparadas para Espectroscopia FTIR (n=3). As amostras foram confeccionadas em molde circular de teflon, sobre o qual foi posicionado um disco de cerâmica feldspática da cor A3 (IPS e.max Ceram, Ivoclar /Vivadent) e a fotoativação realizada através da cerâmica com QTH (XL2500, 3M/ESPE) e LED (Ultralume Led5, Ultradent), por 100 s. Após armazenagem por 24 h a 37oC em ambiente escuro, as amostras foram trituradas, misturadas com Brometo de Potássio (KBr) e prensadas para obtenção de pastilhas para análise por Espectroscopia FTIR. A análise estatística não mostrou diferença significativa entre as fontes de luz (p>0,05), independente dos demais fatores. O cimento P8 apresentou a maior média de grau de conversão. Com QTH, P8 foi maior (60 % ± 1,6) e apresentou diferença estatística significativa em relação à C1P4 (50,7 % ± 1,8), C4P1 (50,4 % ± 1,2) e C5 (47,1 % ±1,2). Com LED, P8 foi maior (58,8 % ± 4,3), porém com diferença estatística significativa apenas em relação à C4P1 (50,9 % ± 3,3) e C5 (48,4 % ± 2,5). O segundo estudo investigou o efeito dos diferentes fotoiniciadores e das fontes de luz na resistência da união de uma cerâmica à dentina bovina. Discos cerâmicos silanizados foram unidos à dentina bovina com os cimentos experimentais, que foram fotoativados com LED (Ultralume Led 5) e QTH (XL 2500), por 100 s. Após 24 h a 37oC e 100% de umidade relativa, foram submetidos ao teste de microtração (µTS) em máquina de ensaios universal Instron (Mod. 4411, USA). Os cimentos P5, C5 e C4P1 mostraram diferença estatística quando ativados pelas duas fontes de luz, sendo que P5 e C5 foram superiores com QTH e C4P1 com o LED. Além disso, P5 obteve a maior média de resistência (19,6 MPa ± 3,51) com QTH, porém foi estatisticamente igual C5 (16,8 MPa ± 1,62), C4P4 (16,2 MPa ±2,93) e P8 (15,4 MPa ± 2,34). Para o LED, C4P1 obteve a maior média de resistência (20,1 MPa ± 3,4) e foi estatisticamente superior aos demais grupos. Portanto, QTH e LED são efetivos na fotoativação de cimentos resinosos mesmo através da cerâmica da cor A3 com 1,4 mm de espessura. O PPD mostrou ser alternativa viável como fotoiniciador em cimentos resinosos e pode ser adequadamente fotoativado com aparelhos LED. / Abstract: The aim of this study was to evaluate the effect of different photoinitiators on the degree of conversion and microtensile bond strength of the photoactivated resin cement used to fix a ceramic veneer on the dental structure. Seven experimental resin cements was
manipulated, as the organic matrix was standardized the only variable component was the photoinitiators. Different concentrations and combinations of Canphoroquinone (CQ) and Phenylpropanodione (PPD) were added in cements as following: C5=0.5% wt CQ; C8=0.8% wt CQ; P5=0.5% wt PPD; P8=0.8% wt PPD; C1P4=0.1% wt CQ and 0.4% wt PPD; C4P1=0.4% wt CQ and 0.1% wt PPD; and, C4P4=0.4% wt CQ and 0.4% wt PPD. The first study evaluated the influence of different combinations of photoinitiators in the degree of conversion on the resin cement photoactivated by LED and quartz- tungstenhalogen (QTH) through ceramic veneer. Forty two samples was prepared to Spectroscopy FTIR (n=3). The samples was made in round teflon mold and a feldspatic ceramic disc shade A3 (IPS e.max Ceram, Ivoclar /Vivadent) was placed over the mold and the photoactivation was carried through the ceramic with QTH (XL2500, 3M/ESPE) and LED (Ultralume Led5, Ultradent) for 100s. After 24 h at 37oC of dark storage, the samples were triturate, mixed with 100 mg of KBr powder salt and pressed to obtain a pellet to analyze Spectroscopy FTIR. The statistical analyze showed no significant difference between the light curing units (p>0,05), independent of the other factors. The P8 cement presented the major means of the degree of conversion. With QTH, P8 was major (60 % ± 1,6) and presented significant statistical different when was compared to C1P4 (50,7 % ± 1,8), C4P1 (50,4 % ± 1,2) and C5 (47,1 % ±1,2). With LED, P8 was major (58,8 % ± 4,3), but with significant statistical different only the C4P1 (50,9 % ± 3,3) and C5 (48,4 % ± 2,5) cements (p>0,05). The second work investigated the effect of different photoinitiators on the microtensile bond strength of photoactivated resin cement used to fix a ceramic to the bovine dentin. Silanized Ceramic discs were bonded to the bovine dentin with the experimental cement photoactivated by LED and QTH for 100s. After 24hs at 37oC and 100% relative wetting, the samples was submitted to the microtensile test in universal trail machine Instron (Mod. 4411, USA). The P5, C5 and C4P1 cements showed significant statistical different to the light curing units, however P5 e C5 was superiors with QTH and C4P1 was better with LED. Additionally, P5 obtain the major means of bond strength (19,6
MPa ± 3,51) with QTH, but no statistical difference was observed with C5 (16,8 MPa ± 1,62), C4P4 (16,2 MPa ±2,93) and P8 (15,4 MPa ± 2,34). With LED, C4P1 obtain the major means of bond strength (20,1 MPa ± 3,4) and presented significant statistical different to the other groups. Therefore, QTH and LED are effectives in the photoactivation of the resin cements through the ceramic with 1,4 mm height. More and then, PPD is viable alternative like photoinitiator in resin cements and it can be adequately photoactivated by LED light curing units. / Tese (doutorrado) - Universida / Doutor em Materiais Dentários
|
138 |
Analise histologica e histomorfometrica do reparo osseo perimplantar em cães submetidos a instalação de implantes endosseos com um modelo de carga precoce em dois diferentes desenhos de implantes / Histological and histomorphometric analysis of perimplant osseous repair in dogs submitted to endosseous implant installation with early load model in two different implant designOlate Morales, Sergio Adrian 02 December 2009 (has links)
Orientador: Jose Ricardo de Albergaria-Barbosa / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T01:32:19Z (GMT). No. of bitstreams: 1
OlateMorales_SergioAdrian_M.pdf: 2518502 bytes, checksum: 379ec7fb825eca639d7e7c3aa4e052a8 (MD5)
Previous issue date: 2009 / Resumo: Diferentes protocolos para a reabilitação com prótese implanto assistida têm sido reportados. Deles, é possível que a carga imediata em implantes unitários sejam um dos mais controversos. O objetivo deste estudo foi estabelecer quantitativamente as características de reparo ósseo em implantes submetidos a um modelo de carga precoce. Foi desenvolvido um modelo experimental em cães para a avaliação de dois protocolos de instalação de implantes dentais com dois desenhos diferentes. Foi realizada a exodontia dos pré-molares bilaterais mandibulares dos animais e após de três meses foi realizada a instalação de dois implantes bilateriais. No implante mesial foi realizada a instalação do parafuso cicatrizador de 7 mm (modelo de carga imediata unitária sem contato oclusal) e no implante distal foi instalado o parafuso cobertor (técnica de implante submerso). Cada hemimandíbula recebeu um implante cilíndrico (Neodent Titamax CM®) e um implante cônico (Conexão Conect Ar®) com seu parafuso cicatrizador. Inicialmente os primariamente foram avaliados com microscopia eletrônica de varredura. Os sacrifícios dos animais foram após de três e seis semanas. Os blocos foram descalcificados e processados para análise com histológica descritiva e histomorfométrica. Foi aplicado o teste estatístico t teste para variáveis independentes com nível de significância de 5%. De forma geral, os implantes apresentaram maior formação óssea no nível cervical e menor no nível apical. Os resultados demonstram também maior formação óssea em implantes com o modelo de carga precoce que em aqueles sem carga, com ausência de diferença estatística. Por outra parte, os implantes cônicos apresentaram maior formação óssea que os cilíndricos, também sem significância estatística. Concluiu-se que os implantes com instalação do parafuso cicatrizador, como modelo de restauração imediata sem contato oclusal, apresenta maior quantidade óssea nos vales quando comparados aos implantes não submetidos a carga / Abstract: Several treatment types using prosthesis over implants have been reported, being the singles immediate loading therapy with more controversy. The meaning of the present study is established the characteristics of bone repair in dental implant submitted to immediate loading. It was performed a experimental model using dogs to value two different installations protocols of dental implants. It was done the extraction of the bilateral premolars of the jaw, installing the dental implants after 3 months of healing. The anterior implant was submitted to healing screw install of 7 mm (unitary immediate load model without oclusal contact) and the posterior ones were covered with cove screrw (immerse implant technique). Each hemi-jaw presented one cylindrical (Neodent Titamax CM®) or conical (Conexão Conect Ar®) with with anterior or posterior position, that was evaluated with scanning electron microscopy. The sacrifices were performed on three and six months. The specimens were decalcified and processed to begging its histological evaluation using descriptive and histomorphometric analyses. The statistical test T test was performed using significance index of 5%. In general, dental implants showed more bone formation on cervical region and less on apical area. The results demonstrated more bone formation on the immediate loading types, with no statistical significance. The conical ones presented more bone formation that cylindrical, but without statistical significance. This way it is possible to conclude that implants with immediate installation of healing screw, how immediately load model without oclusal contact (immediately restauration), have more osseous presence when compared to non load implant / Mestrado / Cirurgia e Traumatologia Buco-Maxilo-Faciais / Mestre em Clínica Odontológica
|
139 |
Avaliação do comportamento mecanico de proteses fixas implantossuportadas por meio da tecnica de extensometria eletrica / Evaluation of mechanic behavior of fixed prosthesis implantsupported by means of electric extensometry technicPrado, Devanir Silva Vieira, 1951- 13 August 2018 (has links)
Orientador: Wilkens Aurelio Buarque e Silva / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T01:38:34Z (GMT). No. of bitstreams: 1
Prado_DevanirSilvaVieira_M.pdf: 895028 bytes, checksum: fe09fdf9bad8a966f0302b161600791e (MD5)
Previous issue date: 2009 / Resumo: Muitas vezes, as tensões são causadas por alterações nas adaptações das estruturas protéticas ao implante, além dos desajustes marginais entre as fixações e as reabilitações protéticas. Este trabalho tem como objetivo, avaliar a distribuição de compressão e tração dos pilares protéticos e infra-estrutura metálica fundida em liga de cobalto-cromo, pela técnica de monobloco, simulando uma prótese fixa implantossuportadas sobre 06 implantes com distância de 10 mm entre implantes e com extremo livre (cantilever) bilateral com extensão de 20 mm, colocados através da curvatura da linha oclusal mandibular. Em cada pilar foram colados quatro extensômetros e um em cada cantilever, após o apertamento de todos pilares e a infra-estrutura aos implantes, foi submetido a um ensaio mecânico com cargas compressivas verticais de 150 N, analisando quantitativamente os resultados bem precisos através da extensometria. Os resultados foram obtidos usando os maiores valores de carga axial registrados em cada ponto de força aplicado, registrando deformação para infra-estrutura, pilares e os cantilevers. Com aplicação de carga nos pontos entre os pilares, foi obtido nos pilares mais próximos a aplicação da carga um maior grau de compressão e nos pilares mais distantes, em menor grau de acordo com a distribuição de carga deformação por compressão e ou/ tração. Com aplicação de carga vertical máxima no cantilever, o pilar adjacente foi o mais solicitado por compressão, independente do ponto de aplicação da carga e o último pilar do lado oposto em menor intensidade, também solicitado por compressão, formando um eixo de rotação, no qual os componentes anteriores foram solicitados em regime de tração (alavanca). O carregamento mecânico registrou deformação para a infraestrutura, pilares e cantilever. / Abstract: Frequently, stresses are caused by changes in adaptations of prosthetic structures to the implant besides marginal disajustment between prosthetic fixing and rehabilitations. This study aims to evaluate the distribution of compression and traction of the prosthetic sustainers and the methalic framework melted in cromocobalt alloy, through the monoblock technic simulating a fixed prosthesis implantsupported on 06 implants at the distance of 10mm between each other and with bilateral cantilever extending to 20mm, placed along the mandibular oclusal line curvature, with the extensometry technic. In each abutment there have been placed four strain guages and one in each cantilever, in configuration "Wheatstone Bridge", after all components having been fixed to the framework, it was submitted to a mechanic essay with vertical pressing charges of 150Ncm, checking quantitatively the accurate result through extensometry. Results have been obtained by using the greatest values of axial charge registered in each place of applied force,. On nearest pillars to the charge, It has been obtained a greater degree of compression (fulcrum), what corresponds to the amount of oclusal force applied to the equalizing stress force. And, therefore, the most distant pillars will assimilate a negative deformation ( compression) or a positive deformation (traction, seesaw), proportional to the lever arm. / Mestrado / Protese Dental / Mestre em Clínica Odontológica
|
140 |
Avaliação da retenção de pinos de fibra de vidro reembasados (pinos anatomicos) e não reembasados cimentados em diferentes condições / Evaluation of relined (anatomic post) and non relined fiber glass posts retention cemented in different conditionsMacedo, Vanessa Cruz 02 December 2009 (has links)
Orientador: Luis Roberto Marcondes Martins / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T03:26:12Z (GMT). No. of bitstreams: 1
Macedo_VanessaCruz_M.pdf: 844488 bytes, checksum: b8556c9d46bb61e55024cbbffb39f017 (MD5)
Previous issue date: 2009 / Resumo: O objetivo neste estudo foi avaliar o efeito do reembasamento (pinos
anatômicos), do tipo de cimento e profundidade de cimentação sobre a retenção
de pino de fibra de vidro. Para confecção das amostras, foram selecionados cento
e oitenta incisivos bovinos, que tiveram suas porções coronárias removidas e seus
canais tratados endodonticamente. Após tratamento endodôntico, os canais foram
alargados com pontas diamantadas 4138 e 4137. As raízes foram divididas
inicialmente em dois grupos: G1 - pinos de fibra de vidro sem reembasamento e
G2 - pinos de fibras de vidro reembasados com resina composta (pinos
anatômicos). Cada grupo foi dividido em três subgrupos de acordo com tipo de
cimento utilizado: A - RelyX ARC, B - RelyX Unicem, e C - RelyX Luting. Em cada
um destes subgrupos os pinos foram cimentados em três diferentes profundidades
dentro do canal: 5 mm, 7,5 mm e 10mm, sendo utilizadas 10 raízes para cada
subgrupo (n=10). Depois de preparadas, as amostras foram submetidas a ensaio
de resistência à tração em uma máquina de ensaio universal, com velocidade de
0,5mm/min. Os resultados em kgf foram convertidos em MPa e submetidos
ANOVA de três fatores com nível de significância de 95%, e as médias
comparadas pelo Tukey. Os resultados demonstraram que não houve diferenças
entre os cimentos resinosos RelyX ARC e o RelyX Unicem, quando cimentados
em diferentes profundidades.O cimento RelyX Luting 2 apresentou os menores
valores de resistência de união. Os pinos de fibra de vidro reembasados (pinos
anatômicos) apresentaram valores maiores do que os pinos não reembasados.
Através desses resultados pode-se concluir que os pinos reembasados (pinos
anatômicos), cimentados a profundidade de 5 mm obtiveram os melhores
resultados quando cimentados com os cimentos resinosos RelyX ARC e RelyX
Unicem. / Abstract: This study evaluated the effect of the relining (anatomic posts), of type
cements and the length of the luting on the retention of fiber glass posts. One
hundred and eighty bovine incisors were selected, their coronary portion removed,
and the canals endodontically treated. After endodontic treatment, the canals were
extended with diamonds burs nº 4138 and 4137. The roots were divided initially in
two groups: G1 - fiber glass posts without relining and G2 - fiber glass posts
relined with composite resin (anatomic posts). Each group was subdivided in three
subgroups according with the type of cements used: A - RelyX ARC, B - RelyX
Unicem, and C - RelyX Luting. The subgroups were luting in three different length
in the canals: 5 mm, 7.5 mm and 10 mm, totality 10 roots for each subgroup
(n=10). All samples were submitted to tensile bond strength testing in a universal
testing machine, with speed of the 0.5 mm/min. The results in kgf were converted
in MPa and submitted by ANOVA three factors and significance level at 95%. The
results displayed that there weren't difference between the resins cements RelyX
ARC and RelyX Unicem, when luting in different length. The cement RelyX Luting
2, showed lowers values of bond strength. The fiber glass posts relined (anatomic
post) showed higher values than those posts without relined. Could be concluded
that the fiber glass posts relined (anatomic posts), luting in length of the 5 mm
obtained the best results when luted with the resin cements RelyX ARC e RelyX
Unicem. / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários
|