Made available in DSpace on 2014-06-11T19:32:59Z (GMT). No. of bitstreams: 0 Previous issue date: 2009-03-18Bitstream added on 2014-06-13T20:27:55Z : No. of bitstreams: 1 bier_cas_dr_arafo.pdf: 458795 bytes, checksum: df3d3967d50d9e31912505515f745092 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo desse estudo foi a avaliação da liberação de íons cálcio, do pH e da adesividade de alguns cimentos utilizados em Endodontia: Sealapex (G1), Sealer 26 (G2), Acroseal (G3), Epiphany (G4), MTA Branco (G5), Endo CPM Sealer (G6). Após a espatulação, os materiais foram inseridos em tubos de polietileno medindo 1,5 mm de diâmetro interno e 1 cm de comprimento com ambas extremidades abertas e imersos em frascos de vidro contendo 10 mL de água ultra pura. Nos períodos de 2, 6, 12, 24 e 48 horas, 7, 14 e 28 dias foram realizadas as análises, sendo o tubo contendo o cimento transferidos para novo frasco a cada período. O pH e a liberação de íons cálcio foram avaliados, respectivamente por meio de pH metro e espectrofotometria de absorção atômica. Para a avaliação da adesividade dos cimentos endodônticos às paredes dentinárias, os canais radiculares de 28 dentes humanos uniradiculados foram dilatados com brocas de Gates Glidden número 1, 2 e 3 e brocas largo número 1, 3 e 5. As raízes foram cortadas em máquina de corte para confecção de discos de 2 mm de espessura. Durante o preparo e depois da secção os espécimes foram irrigados com solução de hipoclorito de sódio a 2,5% e com EDTA a 17 % para a remoção da smear layer. Após a divisão aleatória nos grupos experimentais, os espécimes foram secos e preenchidos com os cimentos endodônticos, sendo mantidos em estufa a 37oC e 95% de umidade relativa do ar por 48 hs. Em seguida, cada conjunto dentina/cimento endodôntico foi submetido ao teste push-out em uma máquina de ensaio mecânico e a tensão necessária para a remoção do cimento medida em Mega Pascal (MPa). Após a coleta dos dados estes foram submetidos à análise estatística de Análise Variância e teste Tukey, com nível de 5% de significância. Os maiores valores de pH foram obtidos pelos G6, seguido por G2 e G5 após 2 horas (P<0,05)... / The aim of this study was to evaluate in vitro the pH, calcium ion release and adhesiveness provide by 6 endodontic filling materials: Sealapex (G1), Sealer 26 (G2), Acroseal (G3), Epiphany (G4), White MTA (G5), Endo CPM Sealer (G6). After manipulation, the sealers (n=10) were placed in tubes with 10 mm-long and 1.5 mm in diameter and immediately immersed in a glass flask containing 10 ml of ultra pure water, which was hermetically sealed and stored at 37°C. At 2, 6, 12, 24 and 48 hr, and at 7, 14 and 28 days after mixing the tubes were moved to new flask with fresh solution and the water in which they were immersed was analyzed for pH with a pH meter and for released calcium by atomic absorption spectrophotometry. To evaluate the adhesiveness of the sealers to the root canal wall, 28 teeth were enlarged to size 5 Largo drill and cut in a cutting machine to create 2 mm thickness slices. During all this procedure the root canal was irrigated with sodium hypochlorite 2.5% and with EDTA 17% to remove the smear layer. The slices were randomly allocated to one of the groups, dried and filled with the sealers and kept in a controlled environment (37oC and 95% humidity) to allow the setting of the sealers. After that, the slice root/endodontic sealer was submitted to push out test in a mechanical testing machine and the results were expressed in Mega Pascal (MPa). The results obtained at each time were statistically evaluated. After 2 hours the uppermost pH was found in the G6, followed by G2 and G5 (P<0,05). From 6 h till 24 h the highest value were observed in groups G5, G6 and G2. After 48 hours, the pH of groups G5 and G6 were stood out. Finally from the 7th to 28th days of evaluation G2, G5 and G6 presented the utmost pH. With regards to calcium ions release in beginning periods the G6 was statistical significantly from the other groups until the 7th day (P<0.05)... (Complete abstract click electronic access below)

Made available in DSpace on 2014-06-11T19:33:01Z (GMT). No. of bitstreams: 0 Previous issue date: 2006-02-10Bitstream added on 2014-06-13T20:44:33Z : No. of bitstreams: 1 murata_ss_dr_araca.pdf: 3025122 bytes, checksum: d6ebabe611a7dce5412ed2e2cf0535db (MD5) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / A dentição decídua é passível de ser acometida por traumatismos, lesões cariosas precoces (cárie de mamadeira) ou outro tipo de injúria, que podem comprometer a vitalidade pulpar desses dentes, inclusive com rizogênese incompleta. A escassez de trabalho específico sobre o assunto, bem como a importância de solucionar adequadamente esse tipo de problema, em dentes decíduos com rizogênese incompleta, estimulam a realização de investigações sobre o assunto. Portanto, o objetivo deste estudo foi avaliar, histologicamente, a resposta dos tecidos apicais e periapicais de dentes decíduos de cães, com rizogênese incompleta, após biopulpectomia e obturação dos canais radiculares com hidróxido de cálcio em diferentes veículos. Assim, os canais radiculares de 80 dentes decíduos anteriores de 6 cães da mesma ninhada, com 50 dias de idade, e com rizogênese incompleta, foram empregados neste estudo. Após o preparo biomecânico, os canais radiculares foram obturados com os seguintes materiais: Grupo 1- pasta Vitapex (hidróxido de cálcio, iodofórmio e óleo de silicone), Grupo 2- hidróxido de cálcio acrescido de iodofórmio e soro fisiológico, Grupo 3- hidróxido de cálcio associado ao Lipiodol e, Grupo 4 - controle - dentes com canais preparados e não obturados. Trinta dias após o tratamento, os animais foram mortos e os espécimes preparados para análise histomorfológica. A análise estatística dos resultados permitiu que os materiais estudados fossem ordenados do melhor para o pior resultado da seguinte forma: a) hidróxido de cálcio acrescido de iodofórmio e soro fisiológico, b) pasta Vitapex (hidróxido de cálcio acrescido de iodofórmio e óleo de silicone), c) hidróxido de cálcio associado ao lipiodol, d) controle. / The deciduous teeth with open apex are susceptible to be traumatized by carious lesions or other offence type that can engage the pulp vitality of those teeth. The lacking of specific work on the subject, as well as the importance of solving this kind of problem appropriately stimulates the accomplishment of investigations on the subject. Therefore, the subject of this study was to evaluate, histologically, the behavior of apical tissues of deciduous dogs teeth with open apex, after biopulpectomy and root canal filling with calcium hydroxide in different vehicles. The root canals of 80 deciduous teeth, from 6 dogs of the same hatch, with 50 days of age, and with open apex, were used in this study. After the biomechanical preparation, the root canals were filled with the following materials: Vitapex - calcium hydroxide added to iodoform and silicon oil; paste of calcium hydroxide with iodoform and saline; paste of calcium hydroxide with lipiodol, and as control group, teeth with root canal prepared but not filled. Thirty days after the treatment, the animals were killed and the specimens were prepared for histomorphological analysis. The statistical analysis of the results allowed the studied materials to be ordered from the best to the worst in the following way: a) calcium hydroxide added to iodoform and saline, b) Vitapex - calcium hydroxide added to iodoform and silicon oil, c) calcium hydroxide added to Lipiodol, d) control. It was observed statistical significant difference (p=0.05) among the results of the groups of calcium hydroxide associated to iodoform and saline with the calcium hydroxide group associated to lipiodol, as well as the 3 groups filled with calcium hydroxide pastes with the control group (p=0.001). It was concluded that the 3 pastes of calcium hydroxide studied can be used as root canal filling material in the treatment of deciduous teeth with open apex.

Resumo: O objetivo do presente estudo foi o de avaliar comparativamente, dois cimentos obturadores de canal radicular à base de resina epóxica, AH Plus e Sealer Plus, através de duas diferentes metodologias. 1. Teste in vivo - Avaliação histopatológica em dentes de cães. Foram utilizados 36 canais radiculares de dentes pré-molares superiores e inferiores de 2 cães, com vitalidade pulpar, os quais, após o preparo biomecânico coadjuvado pela irrigação/aspiração e inundação com solução de hipoclorito de sódio a 1% (Líquido de Dakin), foram obturados pela técnica clássica complementada pela condensação lateral ativa, empregando os cimentos Sealer Plus (Grupo I) e AH Plus (Grupo II). Decorridos 90 dias após a obturação, os animais foram sacrificados por sobredose anestésica, as maxilas e mandíbulas removidas e fixadas em formol a 10%, durante 48 horas. Após processamento histológico de rotina, os cortes foram corados pela hematoxilina e eosina, pelo tricrômico de Mallory e Brown e Brenn. A análise histopatológica evidenciou que o cimento AH Plus, quanto à compatibilidade biológica, mostrou-se superior ao Sealer Plus, sendo o cimento que melhor permitiu a deposição de tecido mineralizado à nível apical, oferecendo um selamento quase completo na maioria dos casos, com infiltrado inflamatório ausente e quando presente era suave no tecido intersticial e/ou junto ao material obturador, assim como na região periapical. Já, com o cimento Sealer Plus, ocorreu predominantemente, selamento parcial, porém sempre acompanhado de infiltrado inflamatório de grau suave, no tecido intersticial, porém, mais concentrado, junto ao cimento obturador. Quando o material obturador era observado na região periapical, o infiltrado inflamatório apresentava-se, classificado como de grau moderado, concentrado próximo ao... (Resumo completo, clicar acesso eletrônico abaixo). / Abstract: The scope of the present study was to evaluate comparativily, two root canal resin - based sealers - AH Plus and Sealer Plus through two different methodologies. 1. In vivo study - Histopathological evaluation in teeth of dogs. 36 root canals of lower and upper bicuspide teeth of 2 dogs with vital pulp, which after biomechanic preparation utilizing sodium hypochloride solution at 1% (Milton solution) were filling by classical technique complemented by active lateral condensation, using Sealer Plus (Group I) and AH Plus (Group II). 90 days after treatment, the animals were sacrificed by overdose anesthetical. After histopathological processing of routine, the sections were stained with hematoxiline and eosine, Mallory Trichromic and Brown and Brenn. The histopathological analysis had evidenced that the AH Plus sealer shows more biological compatibility in relation to the Sealer Plus being the sealer that shows more good deposition of mineralized tissue to the apical level, offering an almost full apical sealing in the majority of the cases, with infiltrated inflammatory absent and when present was mild in the interstitial tissue and/or together to the material sealer, as well as in the periapical region. With the Sealer Plus, partial apical sealing occurred, however always followed by infiltrated inflammatory of mild degree in the intersticial tissue, however, more concentrated, together to the filling material when in the periapical region, the inflammatory infiltrated was presented, classified as of moderate degree. 2. In vitro study - With the objective to analyze pH and clearing of total calcium by periods that had varied from 0 to the 5 days, the filling materials. AH Plus and Sealer Plus had been manipulated according to the manufacturers instructions. Samples of each sealer were... (Complete abstract, click electronic address below). / Orientador: Mario Roberto Leonardo / Coorientador: Léa Assed B. da Silva / Banca: Idomeo Bonetti Filho / Banca: Francisco José de Souza Filho / Banca: Jesus Djalma Pécora / Doutor

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / O objetivo desse trabalho foi avaliar a biocompatibilidade de um material a base de guta-percha autoadesiva (Bio-Gutta) em tecido subcutâneo de camundongos. A guta-percha convencional foi utilizada como referência para comparação. Para isso, foram utilizados 30 camundongos, os quais foram distribuídos aleatoriamente em dois grupos (Bio-Gutta e guta-percha convencional). Os materiais avaliados foram implantados na região dorsal dos camundongos. Após 7, 21 e 63 dias, os animais foram sacrificados e 5 amostras por grupo por tempo experimental foram obtidas. As amostras histológicas foram seccionadas em 5 m de espessura e coradas convencionalmente com hematoxilina e eosina. Um escore de I-IV foi utilizado para graduar a reação inflamatória. O teste U de Mann-Whitney com correção de Bonferroni foi utilizado para análise estatística (p < 0,05). Os resultados mostraram que, após 7 dias, a Bio-Gutta induziu uma reação tecidual de leve a moderada (II) e a guta-percha convencional apresentou uma resposta inflamatória de moderada a intensa (III). Após 21 dias, a Bio-Gutta induziu uma leve reação tecidual (I), enquanto que a guta-percha convencional ainda apresentava uma resposta inflamatória moderada (III). Uma reação tecidual de leve a ausente (I) foi observada na Bio-Gutta após 63 dias, ao passo que na guta-percha convencional observou-se uma resposta inflamatória de leve a moderada (II). Houve diferença significativa na mediana do grau de inflamação entre os grupos em cada tempo experimental (p = 0,005, aos 7 dias; p = 0,011, aos 21 dias; e p = 0,003, aos 63 dias). Concluiu-se então que a Bio-Gutta foi mais biocompatível que a guta-percha convencional em tecido subcutâneo de camundongos apresentando uma boa resposta tecidual. / The purpose of this study was to evaluate the biocompatibility of a self-adhesive gutta-percha material (Bio-Gutta) in connective tissue of mice. Conventional gutta-percha was used as reference for comparison. Thirty mice were used in this study and they were randomly assigned into two groups (Bio-Gutta and conventional gutta-percha). The tested materials were implanted in the dorsal region of mice. After 7, 21 and 63 days, animals were sacrificed and 5 samples per group per time-point were obtained. Histologic samples were sectioned in 5 m thickness and stained with conventional hematoxylin and eosin. A grade from I-IV was used to graduate the inflammatory reaction. Bonferroni-corrected Mann-Whitney U test was used for statistical analysis (p < 0,05). The results showed that after 7 days Bio-Gutta induced a slight to moderate tissue reaction (II) and conventional gutta-percha presented a moderate to intense inflammatory response (III). After 21 days, Bio-Gutta presented a slight tissue reaction (I), while conventional gutta-percha still showed a moderate inflammatory response (III). A slight to absent tissue reaction (I) was observed in Bio-Gutta after 63 days, whereas conventional gutta-percha showed a slight to moderate inflammatory response (II). There was a significant difference in the median degree of inflammation between the groups at each time-point (p = 0,005, at 7 days; p = 0,011, at 21 days; and p = 0,003, at 63 days). It was concluded that Bio-Gutta was more biocompatible than conventional gutta-percha in subcutaneous tissue of mice showing a good tissue response.

Orientador: Juliane Maria Guerreiro Tanomaru / Resumo: Os instrumentos de níquel-titânio usados durante o preparo dos canais radiculares podem sofrer diferentes processos de tratamento na liga durante a fabricação. Sistemas de instrumentação mecanizada apresentam formatos individuais dos instrumentos, sendo sugeridas diversas cinemáticas de atuação durante a ação de corte da dentina. Os sistemas de único instrumento usados em cinemática reciprocante e novos instrumentos com tratamento térmico das ligas devem ser estudados quanto ao efeito sobre o preparo do canal e dentina radicular. A anatomia do canal, as técnicas obturadoras e o emprego de diferentes materiais podem influenciar na qualidade da obturação. O objetivo do estudo foi avaliar o preparo de canais achatados de incisivos inferiores e canais mesiais de molares inferiores com instrumento rotatório e/ou reciprocante, bem como a qualidade da obturação usando diferentes técnicas ou cimento de silicato de cálcio. Noventa incisivos inferiores apresentando canais achatados foram preparados com sistema Mtwo em rotação contínua (Mtwo rot) até 40/.06; Mtwo 40/.06 instrumento único em cinemática reciprocante horária (Mtwo rec) e Reciproc (R40) (n=30). Os dentes foram escaneados por microtomografia computadorizada (Micro-CT) antes e após o preparo. Os dados foram expressos em porcentagem do aumento de volume do canal (%V), redução da espessura de dentina (%DTR), área de superfície não instrumentada (%S) e debris remanescente (%D). O tempo necessário para o preparo foi anotado. Cana... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The nickel-titanium instruments used during the preparation of root canals can present different treatment processes in alloy during manufacturing. Mechanized instrumentation systems present instruments with individual formats, being suggested various kinematics during the action on the dentin. Single instrument systems used in reciprocating kinematics and the new instruments with thermal treatment of alloys should be studied as to the effect on the preparation of the root canal and dentin. The anatomy of the root canal, the filling techniques and the use of different materials can influence in the quality of filling. The objective of this study was to evaluate the flattened root canal preparation of mandibular incisors and mesial root canals mandibular molars using rotatory and/or reciprocating instruments, as well the quality of root canal obturation using different techniques or calcium silicate sealer. Ninety mandibular incisors presenting flattened canals were prepared using Mtwo system in continuous rotation (Mtwo rot) up to 40/.06; Mtwo 40/.06 single instrument in reciprocating motion (Mtwo rec) and Reciproc (R40) (n = 30). The teeth were scanned by computed microtomography (Micro-CT) before and after the preparation. Data were expressed as a percentage of the increase in volume of root canal (% V), reduction of the thickness dentin (% DTR), uninstrumented surface area (% S) and remaining debris (% D). The time required for the preparation was noted. Mesial root canals... (Complete abstract click electronic access below) / Doutor

Considerando-se a necessidade da obturação tridimensional e o adequado selamento marginal do sistema de canais radiculares, como fatores decisivos para o êxito da terapia endodôntica, este estudo objetivou avaliar as respostas inflamatórias periapicais resultantes da infiltração coronária em dentes de cães obturados com diferentes cimentos resinosos (AH Plus®, RealSeal® e RealSeal SE®) e técnicas obturadoras (condensação lateral e termoplástica). Para tanto, pré-molares e incisivos centrais e laterais de 5 cães tiveram o tratamento endodôntico realizado empregando-se limas de NiTi e creme de Endo PTC associado ao hipoclorito de sódio a 1%, estabelecendo-se como limite de instrumentação à distância de 1mm a 1.5mm aquém do vértice radiográfico. A seguir os condutos foram obturados de acordo com os grupos experimentais (n=12) e grupos controles (n=10): GI- AH Plus/condensação lateral, GII- AH Plus/termoplástificação, GIIIRealSeal/ condensação lateral, GIV- RealSeal/ termoplástificação, GV- RealSeal SE/condensação lateral, GVI- RealSeal SE/ termoplástificação, Grupo controle positivo e Grupo controle negativo. As cavidades coronárias ficaram expostas ao meio bucal por um período de 75 dias e, passado este período experimental, os cães foram eutanásiados por superdosagem de anestésico. Foi realizada a remoção cirúrgica das partes correspondentes aos pré-molares e incisivos da maxila e da mandíbula, fixação das mesmas em solução de formol a 10% por 72h e desmineralização em solução de ácido fórmico a 20% + citrato de sódio a 10% pelo período mínimo de 90 dias. Posteriormente, realizou-se a rotina histológica com cortes seriados com espessura de 6m e estes foram corados com hematoxilina e eosina (HE). Cada corte histológico foi digitalizado e analisado em relação à existência de patologia periapical por três avaliadores independentes. Os dados obtidos foram confrontados estatisticamente utilizando o teste de Kruskal-Wallis seguido do teste comparativo de Dunn, observando-se que em relação às técnicas, a termoplástificação por ondas contínuas de condensação associada à técnica de injeção mostrou melhores condições periapicais quando comparada à técnica de condensação lateral (p=0.0055), sendo que a utilização desta técnica resultou em reações inflamatórias mais intensas para o cimento RealSeal SE (p=0.002). Em relação aos cimentos avaliados, o RealSeal SE mostrou-se menos eficaz em evitar a percolação, produzindo maiores níveis de inflamação crônica independentemente do sistema de obturação (p=0.0088). / Considering the need for three-dimensional obturations and adequate marginal sealing of the radicular canal system as being decisive factors for successful endodontic therapy, this study had as its objective the evaluation of periapical inflammatory responses resulting from coronary infiltration in dog\'s teeth obturated using different resin sealers (AH Plus, RealSeal and RealSeal SE) and different obturation techniques (lateral condensation and thermoplastic). For this study, premolars, central and lateral incisors from five dogs had endodontic treatment employing NiTi files and Endo PTC cream associated with 1% sodium hypochlorite. The working length was established at a distance of 1.0 to 1.5mm short of the radiographic apex. After this, the teeth were obturated according to their experimental groups (n=12) and control groups (n=10). The groups were defined as follows: GI - AH Plus/lateral condensation, GII - AH Plus/thermoplastic, GIII - RealSeal/lateral condensation, GIV - RealSeal/thermoplastic, GV - RealSeal SE/lateral condensation, GVI - RealSeal SE/ thermoplastic, a positive control group and a negative control group. The coronal access were left exposed to the oral environment for a period of seventy-five days, and after this experimental period, the dogs were euthanized by anesthetic overdose. The parts corresponding to the premolars and the maxilar incisors were surgically removed. These were then submitted to a solution of 10% formol for 72 hours and then demineralized in a solution of 20% formic acid and 10% sodium citrate for a minimum period of ninety days. Before hand, a histological routine of serial cuts having a width of 6m was undertaken and these were colored with hematoxilin and eosin (HE). Each histological cut was digitalized and analyzed with respect to the existence of periapical inflammation by three independent evaluators. The data obtained was statistically compared, firstly using the Kruskal-Wallis test and then the comparative Dunn test, where it was noted that in relation to the techniques, thermoplastification by continuous wave of condensation associated with the injection technique showed better periapical conditions than what was seen for the lateral condensation technique (p=0.0055). On the other hand, for the sealers evaluated, the condensation technique resulted in more intense inflammatory reactions when the sealer RealSeal SE was used (p=0.002). In relation to the sealers evaluated, RealSeal SE was seen to be less effective against percolation, thus producing greater levels of chronic inflammation irrespective of the obturation system employed (p=0.0088).

Avaliou-se a influência do curativo intra-canal com pasta de hidróxido de cálcio na penetração do cimento EpiphanyTM no interior dos túbulos dentinários e na adaptação do cimento às paredes dos canais radiculares utilizando-se a microscopia confocal de varredura a laser (MCVL). Foram utilizados 30 incisivos centrais inferiores humanos, extraídos, com apenas um canal radicular. O acesso ao canal foi realizado de forma convencional utilizando-se pontas diamantadas montadas em alta rotação, sob refrigeração. Os canais foram preparados pela técnica progressiva empregando-se instrumentos manuais e rotatórios de níquel-titânio, Protaper e Profile (conicidade 0.4). A irrigação foi realizada usando solução de hipoclorito de sódio a 1% e, ao final do preparo, o soro fisiológico. Após o preparo, os canais radiculares de todos os dentes receberam aplicação de EDTA a 17% por 3 minutos e irrigação final com soro fisiológico. A seguir, os dentes foram divididos em 3 grupos como segue: grupo 1 sem tratamento adicional (controle); grupo 2 curativo de Ca (OH)2 e grupo 3 - curativo de Ca (OH)2 e nova aplicação de EDTA. O curativo de Ca (OH)2 foi empregado na forma de pasta viscosa com propilenoglicol que foi inserida no canal com espiral de Lentulo. Após o curativo, os dentes foram armazenados a ± 37 °C por 14 dias. A remoção do curativo foi feita com irrigação com soro fisiológico e com instrumento manual. A seguir, os canais radiculares de todos os 30 espécimes foram obturados com o Sistema EpiphanyTM utilizando-se o primer, o cimento EpiphanyTM, cones principais de Resilon 40/0.4 e cones auxiliares fino-médio pela técnica da condensação lateral ativa. Antes da obturação, o cimento foi corado com Rodamina B. Foram feitas secções transversais a 3, 7 e 10 milímetros distantes do forame apical (terços apical, médio e cervical), cujas imagens foram analisadas em microscopia confocal por varredura a laser (MCVL). Os resultados foram submetidos aos testes estatísticos de Análise de Variância (ANOVA) e teste Tukey, ambos com 5% de significância. Os resultados indicaram que a maior penetração de cimento no interior dos túbulos dentinários foi verificada nas secções dos terços cervical e médio do grupo II comparado aos grupos I e III. A penetração do cimento em todas as secções foi maior e estatisticamente significante nas faces vestibular e lingual. Em relação à adaptação do cimento às paredes dos canais radiculares, a fluorescência do cimento, considerando o perímetro total do canal mostrou regiões com falhas na interface dentina-cimento. A menor porcentagem de adaptação foi observada no grupo I (78%) comparado com os grupos II (93%) e III (86%) (p<0,05). Em canais obturados com o Sistema EpiphanyTM pela técnica da condensação lateral, o hidróxido de cálcio influenciou positivamente na profundidade de penetração do cimento no interior dos túbulos dentinários e na sua adaptação às paredes dos canais. / The aim of this study was to evaluate the influence of calcium hydroxide on the depth of dentinal tubule sealer penetration and the percentage of sealer-dentin interface in the coronal, middle and apical thirds teeth obturated with the EpiphanyTM Obturation System using 5 x and 40x confocal laser scanning microscopy. Thirty extracted single-rooted mandibular incisor human teeth were instrumented using 1.0 % NaOCl. The smear layer was removed using 17% EDTA for 3 minutes. The teeth were randomly assigned to 3 groups (n=10), according to the presence or absence of intracanal dressing and its removal: GI= non Ca(OH)2 dressing (control); G II= Ca(OH)2 + removal using saline solution and kfile # 40; and G3= Ca(OH)2 + removal using saline solution + kfile # 40 and 17% EDTA. One tooth from groups II and III were ramdomly selected for calcium hydroxide analysis. The calcium hidroxyde was labeled with fluorescent fluorescein and after 14 days of storage in 100% humidity at 37 degrees C, the dressings were removed from experimental groups. All root canals (control and experimental groups) were obturated with Resilon master points 40/0.4, Resilon points fine-medium and EpiphanyTM sealer labeled with fluorescent Rhodamine B dye. The sections cut from the coronal, middle and apical thirds of each root were viewed using 5x and 40x confocal laser scanning microscopy. Twoway ANOVA and Tukey test found significantly lower average depth of sealer penetration in apical sections than middle or coronal sections (p<0,05). The deepest sealer penetration was observed in the coronal and middle secctions of group II compared to the groups I and III. The sealer penetration in all sections was deeper and statistically different in the vestibular and lingual faces. A fluorescent sealer ring was seen around the canal wall in all sections presenting some gaps in the sealerdentin interface. Two-way ANOVA and Tukey tests showed significantly less percentage of sealer-dentin interface in the group I (78%) compared to groups II (93%) and III (86%) (p<0,05). Calcium hydroxide dressing affected positively the deep of sealer penetration and percentagem of sealer dentin interface in the root canals filled with EpiphanyTM resin based sealer.

Orientadores: Fernanda Miori Pascon, Regina Maria Puppin Rontani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-20T05:29:10Z (GMT). No. of bitstreams: 1 Iwamoto_AlexsandraShizue_M.pdf: 5068520 bytes, checksum: 5edcd14cf180873ed3b9ce319f696504 (MD5) Previous issue date: 2012 / Resumo: O objetivo do estudo foi avaliar in vitro a influência de diferentes materiais obturadores e agentes de limpeza na resistência da união de pinos de fibra de vidro à dentina radicular e na qualidade da interface adesiva. 156 raízes de dentes bovinos decíduos foram selecionadas, preparadas endodonticamente e distribuídas em 4 grupos de acordo com os materiais obturadores (39 dentes): 1- Controle (sem material); 2- Pasta Calen® + óxido de zinco (OZ); 3- Pasta Vitapex®; 4- Pasta Calcipex II®. Após 7 dias, as raízes foram desobturadas e subdivididas de acordo com os agentes de limpeza (13 dentes): A - Controle (sem limpeza); B - Etanol a 70%; C - Tergenform®. A cimentação do pino foi realizada com cimento resinoso RelyXMR ARC após condicionamento com ácido fosfórico a 35 % e aplicação do sistema adesivo Adper Single BondTM 2. Os espécimes foram armazenados por 7 dias, seccionados e preparados para avaliação da resistência da união (n=10) e análise da interface por meio da infiltração por nitrato de prata (n=3). O teste push-out foi conduzido na máquina de ensaio universal EMIC com velocidade 0,5mm/min. Os dados obtidos em Kgf foram convertidos em MPa e submetidos à ANOVA dois fatores (materiais obturadores x agentes de limpeza) e ao teste Tukey (p<0,05). Amostras representativas dos grupos foram observadas em Microscopia Eletrônica de Varredura (MEV) após a realização do teste push-out para ilustrar a fratura ocorrida. Para avaliação qualitativa da interface adesiva entre dentina/cimento e cimento/pino, as áreas infiltradas pela solução de nitrato de prata foram observadas em MEV e mensuradas por um único examinador previamente calibrado (nível de coincidência intra-examinador=98%), calculadas em porcentagem e submetidas ao teste Kruskal-Wallis (p<0,05) e à análise descritiva. Para os resultados da resistência da união, verificou-se que houve interação entre os fatores de estudo (p=0.0043). A pasta Calen®+OZ e limpeza com etanol apresentou o maior valor de resistência da união, diferindo estatisticamente do grupo sem limpeza. Valores intermediários foram encontrados para a limpeza com Tergenform®. As pastas Vitapex® e Calcipex® não apresentaram diferenças entre os agentes de limpeza e menores valores de resistência da união foram para o grupo controle (sem material obturador) e limpeza com Tergenform®, diferindo dos outros agentes de limpeza. Observou-se que não houve diferença entre os grupos para a infiltração de prata nas interfaces adesivas entre cimento e dentina radicular, que variou de 20,63% a 56,62%. Dessa forma, pode-se concluir que: (1) os materiais obturadores e os agentes de limpeza interferiram na resistência da união de pinos de fibra de vidro e dentina radicular; (2) ao realizar a obturação do canal radicular com pasta Calen®+OZ o melhor agente de limpeza foi o etanol a 70%; (3) para as pastas Vitapex® e Calcipex II® não há necessidade de agentes de limpeza; e (4) todos os grupos sofreram infiltração na interface de união entre cimento/dentina radicular, independente dos materiais obturadores e agentes de limpeza estudados / Abstract: The aim of this in vitro study was to evaluate the post-cement-dentin adhesive interface quality and the effect of different filling materials and cleaning agents on the bond strength of glass fiber posts to primary root dentin. This study included 156 roots of bovine primary teeth which were endodontically treated and assigned to four groups (39 teeth each group) according to filling materials: 1 - control (no material); 2 - Calen® paste + zinc oxide (ZO); 3 - Vitapex® paste; and 4 - Calcipex II® paste. After seven days, the filling materials were removed and the roots for each material subdivided into 3 groups (13 teeth) according to cleaning agents: A - No cleaning (control); B - 70% ethanol; and C - Tergenform®. Glass fiber posts were luted using dual polymerized resin cement (RelyXMR ARC) after 35% acid etching, rinsing and application of the adhesive system (Adper Single BondTM 2). The specimens were stored for 7 days, sectioned and prepared for push-out bond strength test (n=10) and interface analysis by silver nitrate leakage (n=3). A push-out test was performed using a universal test machine (EMIC) at a crosshead speed of 0.5 mm/min. Data obtained in Kgf were converted into MPa and submitted to two-way ANOVA (filling materials x cleaning agents) and Tukey tests (p<0.05). After the push-out test, representative samples of the groups were submitted to scanning electron microscopy (SEM) to illustrate the failure modes. The adhesive interface between dentin/cement and cement/post were also analyzed by SEM. The leakage (expressed in percentage) was measured by a single examiner previously calibrated (intra-examiner coincidence level = 98%) using a silver nitrate solution. Data obtained for leakage were submitted to the Kruskal-Wallis test (p<0.05) and descriptive analysis. Interaction was observed between filling materials and cleaning agents, concerning bond strength values (p=0.0043). Calen® paste+ZO with 70% ethanol showed the highest values, significantly different from the groups using no cleaning agents. Vitapex® and Calcipex® showed no significant difference between cleaning agents. The lowest bond strength values were found for the control with Tergenform®. No statistical difference was observed between groups concerning silver leakage (20.63% to 56.62%) in the adhesive interface between cement and dentin. In conclusion, filling materials and cleaning agents influenced the bond strength, but not the adhesive interface between intracanal posts and root dentin; as a cleaning agent, 70% ethanol responded better to Calen® paste+ZO; cleaning agents are not required for Vitapex® and Calcipex®; all groups showed leakage in the adhesion interface between cement resin/dentin root, regardless of the filling materials and cleaning agents studied / Mestrado / Odontopediatria / Mestre em Odontologia

Introduction: The aim of this study was to evaluate some of the physico-chemical properties of a new root canal sealer. Methodology: The sealers tested were Sealer Plus (MKLife, Porto Alegre, Rio Grande do Sul, Brazil), compared as AH Plus (Dentsply, DeTrey GmbH, Konstanz, Alemanha). For the radiopacity, flow, solubility and fabrication of test specimens relative to setting times the ANSI/ADA No. 57 (2000) and ISO 6876 (2012) specifications were followed. To measure the initial and final setting times the ASTM C266/2008 standard was used. pH was evaluated in the time intervals of 3, 24, 72 and 168 hours). Statistical tests were applied to the results obtained at a level of significance of 5%. Results: The results demonstrated that the Sealer Plus sealer showed a lower radiopacity value than AH Plus sealer (p<0.05), however, this was higher than the minimum value recommended by the specifications; that is 3 mm Al. Relative to flow, the value for Sealer Plus was 19.19 mm and for AH Plus, 19.81 mm (p>0.05). Sealer plus presented initial and final setting times of 138 min. and 210 min., respectively, while the values for AH Plus were 437 min. and 849 min., respectively, (p<0.05). Relative to solubility, Sealer Plus presented 0.21% and AH Plus, 0.27% (p>0.05). None of the sealers showed a significant increase in pH (p>0.05). Conclusion: Sealer Plus sealer presented physico-chemical properties in accordance with ANSI/ADA (2000) No.57 and ISO 6876 (2012) specifications. / Introdução: Este estudo objetivou avaliar algumas propriedades físico-químicas de um novo cimento obturador de canais radiculares. Metodologia: Para os testes de radiopacidade, escoamento, solubilidade e confecção dos corpos de prova para os tempos de presa foram seguidas as especificações nº57 da ANSI/ADA (2000) e ISO 6876 (2012). Para a medição dos tempos de presa, inicial e final, foi empregada a norma ASTM C266/2008. O pH foi avaliado nos períodos de 3, 24, 72 e 168 horas. Sobre os resultados foram aplicados testes estatísticos com nível de significância de 5%. Resultados: Os resultados demonstraram que o cimento Sealer Plus apresentou menor radiopacidade do que o cimento AH Plus (p<0.05), porém, superior ao mínimo recomendado pelas especificações, ou seja, de 3 mm de Al. Com relação ao escoamento, o do Sealer Plus foi 19,19 mm e do AH Plus 19,81 mm (p>0.05). O Sealer Plus apresentou tempos de presa inicial e final de 138 min. e 210 min., respectivamente, enquanto o AH Plus, 437 min. e 849 min., respectivamente, (p<0.05). Em relação à solubilidade, o Sealer Plus apresentou 0,21% e o AH Plus 0,27% (p>0.05). Nenhum dos cimentos apresentou aumento significativo do pH (p>0.05). Conclusão: O cimento Sealer Plus apresentou propriedades físico-químicas de acordo com as especificações nº 57 da ANSI/ADA (2000) e ISO 6876 (2012).

<p>U slučajevima neuspe&scaron;ne endodontske terapije, neophodno je ponovno lečenje kanala korena. Ortogradni endodontski retretman podrazumeva uklanjanje postojećeg materijala za punjenje iz kanala uz dodatno či&scaron;ćenje, dezinfekciju i ponovnu finalnu opturaciju kanala. Važan korak u toku retretmana je &scaron;to potpunije uklanjanje postojećeg kanalnog punjenja kako bi se pristupilo svim delovima kanalnog sistema. Cilj doktorske teze bio je da se ispita kvalitet čis&scaron;ćenja zidova kanala korena nakon endodontskog retretmana pomoću skening elektronske mikroskopije (SEM). Posmatran je uticaj vrste materijala za opturaciju, uticaj upotrebe rastvarača i uticaj ručnih i ma&scaron;inskih instrumenata na količinu zaostalog materijala na zidovima kanala. Takođe, ispitan je uticaj ovih faktora na apikalnu transportaciju materijala i na vreme potrebno za retretman, a utvrđena je i učestalost o&scaron;tećenja kori&scaron;ćenih instrumenata. Materijal i metode: Ukupan uzorak činilo je 125 ekstrahovanih, humanih jednokorenih zuba. Nakon preparacije kanala korena, 120 zuba je podeljeno u dve grupe i napunjeno pomoću dva različita materijala za opturaciju (gutaperkom i resilonom). U zavisnosti od tehnike uklanjanja ovih materijala, grupe su dalje podeljene u odnosu na kori&scaron;ćene instrumente (Hedstrom, ProTaper i Twisted File) i u odnosu na upotrebu rastvarača (sa i bez hloroforma). Preostalih 5 zuba, bez kanalnog punjenja, kori&scaron;ćeni su kao kontrolna grupa. Nakon zavr&scaron;enog retretmana, korenovi su uzdužnim cepanjem razdvojeni, a odabrane polovine posmatrane na SEM-u. Mikrofotografije svake trećine kanala načinjene su pri uveličanju od 500x. Količina preostalog materijala za punjenje ocenjivana je pomoću skale. Otvoreni dentinski kanalići prebrojavani su na mikrofotografijama načinjenim pri uveličanju od 1000x, u odnosu na uvek konstantnu povr&scaron;inu. Rezultati: Analiza rezultata ukazala je na postojanje statistički značajne razlike u kvalitetu či&scaron;ćenja zidova kanala u zavisnosti od uklanjanog materijala za opturaciju. Kvalitet či&scaron;ćenja zidova kanala bio je veći nakon uklanjanja gutaperke nego nakon uklanjanja resilona. Rotirajućim, ma&scaron;inskim instrumentima je efikasnije uklanjana gutaperka, a ručnim Hedstrom turpijama je bolje uklanjan resilon. Posmatrajući ceo uzorak, ProTaper instrumenti ostavljali su velike količine materijala na zidovima kanala nakon endodontskog retretmana. Međutim, uklanjanje materijala pomoću ovih instrumenata bilo je najbrže. Primena rastvarača značajno je doprinela bržem uklanjanju materijala, dok uticaj na kvalitet či&scaron;ćenja zidova kanala nije bio značajan. Posmatrajući kanal korena po trećinama, najveća količina materijala nalazila se u apikalnoj trećini, bez obzira na vrstu uklanjanog materijala i kori&scaron;ćenih instrumenata, i bez obzira na upotrebu rastvarača tokom retretmana. Učestalost o&scaron;tećenja instrumenata bila je značajno veća prilikom upotrebe Twisted File instrumenata. Apikalna transportacija materijala je bila veća tokom uklanjanja resilon materijala i kada su kori&scaron;ćene ručne Hedstrom turpije. Zaključak: Kvalitet či&scaron;ćenja zidova kanala nakon uklanjanja gutaperke je veći nego nakon uklanjanja resilona. Dizajn i vrsta instrumenata utiče na kvalitet či&scaron;ćenja zidova kanala korena. Upotreba rastvarača tokom retretmana ne utiče značajno na smanjenje količine materijala zaostalog na zidovima kanala. Ma&scaron;inski pokretani instrumenti i upotreba rastvarača značajno skraćuju vreme potrebno za endodontski retretman.</p> / <p>In cases when endodontic treatment fails, it is necessary to retreat the root canal. Orthograde endodontic retreatment requires the removal of the existing root filling material with additional cleaning, disinfection and refilling of the canal. An important step during retreatment is complete removal of existing filling materials, to regain access to all parts of the canal system. The aim of the doctoral thesis was to investigate the cleanliness of root canal walls after removal of two different obturation material. The retreatment efficacy was observed depending on the usage of solvent and different hand or rotary instruments. The amount of residual material on the canal walls was assessed using scanning electron microscopy (SEM). Also, apical transportation of the obturation material, working time and frequency of instrument damage during retreatment was recorded. Materials and Methods: The total sample consisted of 125 extracted, single-rooted human teeth. After root canal preparation, 120 teeth were divided in two groups and filled using two different obturation materials (gutta-percha and resilon). Depending on the technique of removing these materials, the groups were further divided, in relation to the used instruments (Hedstrom, ProTaper and Twisted File), as well as in relation to the use of solvent (with or without chloroform). The remaining 5 tooth without canal filling were used as a control group. After root canal desopturation, the longitudinaly splitted root halves were observed on SEM. Microphotography of each third were made at magnification of 500x. The amount of remaining filling material was evaluated by using a scale. Open dentinal tubules were counted on microphotographies made at a magnificiation of 1000x, on a surface that was always constant. Results: Analysis of the results indicated a significant difference in the cleanliness of the canal walls depending on the used obturation material. Cleanliness of the canal walls was higher after gutta-percha removal than after the removal of resilon.&nbsp; Rotary instruments were more effective in removing gutta-percha and Hedstrom hand files better removed resilon. ProTaper instruments left more residual material on canal walls, however endodontic retreatment with these instruments was the fastest. The application of solvent significantly contributed to faster material removal, while the impact on the increase of canal cleanliness was not significant. The largest amount of material remained in the apical third, regardless of the type of material removed and instruments used, and also regardless whether solvent was used for retreatment. The frequency of instrument deformation and fracture was significantly higher when Twisted File instruments were used. Apical transportation of material had a significantly higher occurrence during resilon removal and when manual Hedstrom files were used. Conclusion: Cleanliness of the canal walls was higher after the removal of gutta-percha than after the removal of resilon. The use of solvent is not significant on the increase of canal wall cleanliness, but significantly shortens the time needed for retreatment. There is a difference in the cleanliness of root canal walls depending on the used instruments. Engine-driven rotary instruments and the use of a solvent significantly shortens the time needed for endodontic retreatment.</p>