Orientador: Paulo Henrique dos Santos / Coorientador: Wirley Gonçalves Assunção / Banca: Eduardo Passos Rocha / Banca: Carlos Alberto dos Santos Cruz / Resumo: O objetivo deste estudo foi avaliar o grau de conversão de agentes cimentantes resinosos polimerizados sob diferentes espessuras de cerâmica feldspática e diferentes sistemas cerâmicos de mesma espessura. No primeiro estudo, oitenta amostras dos cimentos resinosos RelyX ARC (3M Espe) e RelyX Veneer (3M Espe) foram confeccionadas sob discos de cerâmica convencional Starlight (DeguDent) com espessuras de 0,5mm, 1,2mm, 1,8mm e 2,4mm. No segundo estudo, oitenta amostras dos cimentos resinosos RelyX ARC (3M Espe) e Maxcem Elite (Kerr) foram confeccionadas sob discos de diferentes sistemas cerâmicos: Starlight (DeguDent), Empress (Ivoclair Vivadent), E-max (Ivoclair Vivadent), In Ceram Alumina (Vita) e In Ceram Zircônia (Vita) com espessuras de 2,0mm. A leitura do grau de conversão dos cimentos resinosos foi realizada 10 minutos, 1 hora e 24 horas após a fotoativação dos cimentos, em espectrofotômetro FTIR Nexus 670 (Nicolet). Os resultados do primeiro estudo mostraram que o cimento resinoso dual RelyX ARC apresentou maior grau de conversão que o cimento fotoativado RelyX Veneer em todas as espessuras de cerâmica, inclusive sem interposição (p<0.0001). Os valores de grau de conversão obtidos após 1 hora e 24 horas não diferiram estatisticamente entre si (p=0.7433), mas foram superiores aos analisados após 10 minutos (p<0.0001). Para o cimento fotoativado, houve aumento gradativo no grau de conversão de 10 minutos até 24 horas (p<0.0001). No segundo estudo, os maiores valores de grau de conversão foram obtidos para as amostras polimerizadas sob as cerâmicas reforçadas por leucita e dissilicato de lítio, sem diferença estatisticamente significante entre si (p=0.1181), enquanto os menores valores do grau de conversão obtidos foram das amostras polimerizadas sob cerâmicas reforçadas por alumina e zircônia, sem diferença entre si (p=0.2374). Com base nos resultados destes... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of this study was to evaluate the degree of conversion of resin cements polymerized under different thicknesses of feldspatic ceramic and different ceramic systems with the same thickness. In the first study, eighty samples of RelyX ARC (3M Espe) and RelyX Veneer (3M Espe) were polymerized under conventional ceramic discs (Starlight, DeguDent) with thickness of 0.5 mm 1.2 mm, 1.8 mm and 2.4 mm. In the second study, eighty samples of RelyX ARC (3M Espe) and Maxcem Elite (Kerr) resin cements were polymerized over ceramics systems: Starlight (DeguDent), Empress (Ivoclar Vivadent), E-max (Ivoclar Vivadent), In Ceram Alumina (Vita) and In Ceram Zircon (Vita) with 2.0 mm of thickness. The degree of conversion of the resin cements was calculated 10 minutes, 1 hour and 24 hours after the curing of cements using a Nexus 670 FTIR spectrophotometer (Nicolet). The RelyX ARC showed higher values of degree of conversion than RelyX Veneer considering all the ceramics thickness in the first study. The measurements obtained after 1 hour and 24 hours did not differ significantly (p=0.7433), but were higher than those analyzed after 10 minutes (p<0.0001). Comparing the ceramic systems in the second study, the highest degree of conversion were obtained for samples polymerized under Empress and e.max ceramics, without statistically difference between them (p= 0.1181) and the lower values of conversion were obtained for the samples polymerized under In Ceram Alumina and In Ceram Zircon ceramics (p= 0.2374). Based on the results of these studies, we can conclude that the thickness of feldspatic porcelain as well as the ceramic system itself could influence the degree of conversion of light- and dual-cured resin cements. All the resin cements showed an increase on the degree of conversion after 24 hours, which could create an especial guideline for the clinical procedures using resin cements / Mestre

Objetivos: O objetivo deste ensaio clínico randomizado foi avaliar o comportamento de restaurações de resina composta bulk-fill em dentes posteriores (classes I e II). Metodologia: Dezessete pacientes que necessitavam de restaurações em pelo menos dois dentes posteriores foram selecionados para participar do estudo. As causas para indicação das restaurações foram: substituição de restauração deficiente de amálgama ou resina composta e/ou lesão de cárie. Em cada paciente foram realizadas duas restaurações. Randomicamente, uma cavidade foi restaurada com a resina nanohíbrida Esthet-X HD (grupo controle) e a outra restaurada com a resina Esthet-X HD associada à resina de baixa contração Surefil SDR Flow (grupo teste). Em ambos os grupos, um sistema adesivo convencional de dois passos (XP Bond) foi utilizado. Todos os pacientes receberam tratamento global para a atividade cariosa. Após um período de quatro anos, a qualidade das restaurações foi avaliada por 1 examinador previamente calibrado, através de uma modificação do método USPHS e através do método FDI. Os dados obtidos foram submetidos à análise estatística pelo teste não-paramétrico Mann-Whitney (p<0,05) e a concordância intra-observador avaliada através de teste Kappa. Resultados: No quarto ano de acompanhamento, 26 dentes (18 restaurações classe I e 8 classe II) foram avaliadas, e não foram observadas diferenças estatisticamente significantes entre as restaurações dos grupos controle e teste para os métodos de avaliação utilizados. Não houve falhas em nenhuma das restaurações ao longo do tempo. Conclusão: A qualidade das restaurações classe I e II com resina bulk-fill foi semelhante à das restaurações com resina nanohíbrida convencional. A técnica com resina bulk-fill mostrou bom desempenho clínico tão bom quanto a convencional durante os 4 anos de acompanhamento. / Objectives: The objective of this randomized clinical trial was to evaluate the behavior of bulk-fill composite restorations in posterior teeth (classes I and II). Methodology: Seventeen patients who required restorations on at least two posterior teeth were selected to participate in the study. The causes for indication of restorations were: replacement of deficient amalgam or composite resin restoration and/or caries lesion. In each patient, two restorations were performed. Randomly, one cavity was restored with Esthet-X HD nanohybrid composite (control group) and the other was restored with Esthet-X HD resin associated with the bulk-fill composite Surefil SDR Flow (test group). In both groups, a two-step total-etch adhesive system (XP Bond) was used. All patients received global treatment for carious activity. After a period of four years, the quality of the restorations was evaluated by a previously calibrated examiner, through a modification of the USPHS method and through the FDI method. The data were submitted to statistical analysis by the non-parametric Mann-Whitney test (p <0.05) and the intra-observer agreement was evaluated by Kappa test. Results: At the 4-year follow-up, 26 teeth (18 class I and 8 class II restorations) were evaluated, and no statistically significant differences between control and test groups were observed for both evaluation methods used. There were no failures in any of the restorations over time. Conclusion: The quality of class I and II restorations with bulk-fill resin was similar to that of conventional nanohybrid resin. The bulk-fill composite technique showed good clinical performance as well as the conventional one during the 4 years of follow-up.

O presente estudo objetivou avaliar a profundidade de polimerização através de testes de microdureza em dois tipos de resina composta com matrizes distintas utilizando um aparelho fotoativador do tipo LED, empregando-se diferentes densidades de energia, sendo avaliados no período inicial (baseline) e após 7 dias. O método utilizado foi o teste de dureza Knoop em amostras de dois compósitos fotoativáveis (P 90, 3M/ESPE, cor A2; Z 250, 3M/ESPE, cor A2). Os corpos-de-prova foram subdivididos em 8 grupos (n=10), metade realizado com cada resina testada. Cada grupo foi definido através de diferentes densidades de energia (600 mW/cm2 x 40s; 1000 mW/cm2 x 40s; 1000 mW/cm2 x 20s; 1400 mW/cm2 x 20s), cada corpo-de- prova obtinha 4 medidas, diferentes profundidades (0, 1, 2 e 3 mm). Cada corpo-de-prova foi confeccionado com o auxilio de uma matriz metálica, constituída por 3 partes, superior, intermediaria e inferior, cada uma com 1 mm de espessura e orifício central com diâmetro de 5 mm. Sobre cada parte preenchida com resina, era colocado um pedaço de tira de poliéster, sobre o qual, com uma lâmina de vidro era exercida uma pressão para promover uma superfície lisa e plana. A unidade fotoativadora utilizada foi LED, para conseguir as diferentes densidades de potência, anéis de plástico foram acoplados na ponta do aparelho fotoativador. A fotoativação foi realizada com a ponta da unidade fotoativadora em contato com a tira de poliéster colocada na parte superior do corpo-de-prova (0 mm). Assim , cada espécime era composto por três partes, cada uma com 1 mm de espessura. Logo após a fotoativação, as partes dos espécimes eram separadas e realizavam-se 5 impressões de dureza Knoop (dureza inicial), com carga de 50g durante 30s, em 4 superfícies, que eram: 1ª) superfície superior da parte superior do espécime, voltada para a fonte de luz (0 mm); 2ª) superfície inferior da parte superior do espécime (1 mm); 3ª) superfície inferior da parte intermediária do espécime (2 mm); e 4ª) superfície inferior da parte inferior do espécime (3 mm). Após 7 dias de estocagem numa estufa a 37ºC, novas leituras de dureza eram realizadas (dureza final). Verificou-se que: 1) A resina composta P 90 obteve menores médias dos valores de dureza Knoop em relação à outra resina composta estudada, Z 250; 2) Quanto maior a profundidade, menores alores de dureza Knoop foram mensurados; 3) Valores de dureza Knoop final foram maiores após 7 dias em comparação a dureza Knoop inicial; 4) De acordo com o aumento da densidade de potência, maiores médias dos valores de dureza Knoop foram mensurados. Esses resultados permitem concluir que: 1) A resina melhora sua propriedade de dureza num período de 7 dias; 2) Quanto maior a profundidade, menor a dureza; 3) quanto maior a densidade de potência utilizada neste trabalho, maior dureza foi avaliado; 4) a resina P 90 obteve valores inferiores a resina Z 250 avaliadas nas mesmas condições. / This study aimed to evaluate the depth of cure through microhardness tests on two types of resin composite with different matrices using LED curing unit, using different energy densities and are assessed during the initial (baseline) and after 7 days. Knoop hardness test was performed in samples made of two light cured composites (P 90, 3M/ESPE, A2; Z 250, 3M/ESPE, A2). The specimens were divided into 8 groups (n=10), and half of them were made with each composite resin tested. Each group was defined by different power densities (600 mW/cm2 x 40s, 1000 mW/cm2 x 40s, 1000 mW/cm2 x 20s; mW/cm2 1400 x 20s), each specimens obtained four measures, different depths (0, 1, 2 and 3 mm). Each specimens was made with the aid of a metal matrix, consisting of 3 parts, superior, intermediate and bottom, each with 1 mm thickness and center hole diameter of 5 mm. On each side filled with resin, was placed a piece of polyester strip, on which, with a glass slide was exerted pressure to promote a flat surface. A unit LED curing was used and to achieve different power densities, plastic rings were attached at the tip of the curing unit. The polymerization was carried out with the tip of the curing unit in contact with the polyester strip placed on top of the specimen (0 mm). Thus, each specimen was composed of three parts, each part with 1 mm thick. Immediately after curing, the parts of the specimens were separated and held up five impressions of Knoop hardness (initial hardness), with a load of 50g for 30s on 4 surfaces, which were: 1) the upper surface of the upper specimen directed to the light source (0 mm), 2) lower surface of the upper specimen (1 mm); 3) lower surface of the middle section of the specimen (2 mm) and 4) lower surface of the bottom of the specimen (3 mm). After 7 days of storage in an oven at 37°C, new hardness re adings were made (final hardness). It was found that: 1) The composite P 90 had lower average values of Knoop hardness in relation to the other studied composite, Z 250, 2) The greater the depth, lower Knoop hardness values were measured, 3) Final values of Knoop hardness were higher after 7 days compared with initial hardness, 4) In accordance with the increase of power density, higher average values of Knoop hardness were measured. These results indicate that: 1) The resin improves the hardness property over a period of 7 days, 2) The greater the depth, the lower the hardness, 3) the higher the power density used in this study, higher hardness was evaluated; 4 ) P 90 resin obtained values less than Z 250 resin, evaluated under the same conditions.

Made available in DSpace on 2014-06-11T19:31:05Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-03-26Bitstream added on 2014-06-13T19:20:03Z : No. of bitstreams: 1 portero_pp_dr_arafo.pdf: 2044562 bytes, checksum: cef64f9c8b79fc9e1bd9e092f4b40fb3 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Este estudo avaliou por meio do espectrofotômetro de reflectância Vita Easyshade® a correspondência de cor entre 3 escalas de referência [Vita Lumin Vacuum (Vita Classical), Vitapan 3D-Master e Chromascop] – Experimento 1, e a correspondência de cor de 2 resinas compostas (4 Seasons® e FiltekTM Supreme XT), nas tonalidades A2E e B2E, em relação a essas 3 escalas de referência por diferirem em sua composição – Experimento 2. Foram confeccionados 5 corpos-de-prova com dimensões de 8 mm de diâmetro e 10 diferentes espessuras (0,2 a 2,0 mm) fotoativados pelo aparelho LED Ultrablue (440 mW/cm2). Em cada amostra foram realizadas 3 mensurações de cor e os valores de diferença de tonalidade (ΔE) obtidos, analisados por regressão quadrática. Os resultados do experimento 1 demonstraram que: houve pouca correspondência de cor entre as tonalidades das 3 escalas avaliadas; no experimento 2, a resina composta nano-aglomerada (FiltekTM Supreme XT) apresentou maior correspondência de cor com as 3 escalas de referência analisadas, quando comparada à resina 4 Seasons®; não houve correspondência de cor entre as resinas compostas avaliadas; as espessuras de resinas compostas que apresentaram maior correspondência de cor com todas as escalas estudadas foram: 1,0; 1,2; 1,4; 1,6; 1,8 e 2,0 mm. Porém, estes corpos-de-prova apresentaram correspondência com a cor de referência (A2E e B2E) e também com outras diferentes tonalidades, demonstrando baixa relação direta entre a cor da escala e a do material restaurador. Concluiu-se de acordo com os resultados que: 1) As escalas de cor Vita Classical, Vitapan 3D-Master e Chromascop não apresentaram correspondência entre suas tonalidades, demonstrando apenas semelhança variada entre si; 2) Composição e propriedades ópticas interferem na correspondência de cor entre... / This study evaluated by the spectrophotometer Vita Easyshade®/Vita, the color correspondence among three shade guides [Vita Lumin Vacuum (Vita Classical), Vitapan 3D-Master/Vita e Chromascop/Ivoclar Vivadent] – experiment 1, and the color correspondence of two composite resins (4 Seasons® and FiltekTM Supreme XT) in the colors A2E and B2E with these three shade guides, for they differ in its composition – experiment 2. Five specimens were made with 8.0 mm in diameter and 10 different thickness (0.2 to 2.0 mm) and light polymerized by LED Ultrablue (440 mW/cm2). The color of specimens were measured 3 times and the values of color difference (ΔE) were obtained, analyzed by analysis of quadratic regression. The results of experiment 1 demonstrated that: there were a little color correspondence among three shade guides; in the experiment 2, the composite resin (FiltekTM Supreme XT) presented higher color correspondence in 3 shade guides than the composite resin 4 Seasons®, there wasn’t color matching between the composite resins analysed; the composite resin thickness that presented larger color correspondence with all shade guides evaluated were: 1.0; 1.2; 1.4; 1.6; 1.8 e 2.0 mm. However, these specimens presented correspondence with the reference color (A2E and B2E) and also with other different shades, showing low direct relationship among the color of the shade guides and of the restoring material. It could be concluded that: 1) The shade guides Vita Classical, Vitapan 3D-Master e Chromascop did’nt presented correspondence among its shades, just demonstrating likeness varied to each other; 2) Composition and optical properties ópticas interfere in the color correspondence between composite resins 4 Seasons® e FiltekTM Supreme XT; 3) The composite resin nanoclusters FiltekTM Supreme XT presented larger color... (Complete abstract click electronic access below)

Orientador: Marco Antonio Compagnoni / Banca: Débora Barros Barbosa / Banca: Lucimar Falavinha Vieira / Resumo: O objetivo do presente trabalho foi avaliar a porosidade em bases de resina acrílica de prótese total maxilar, processadas em diferentes ciclos de polimerização e confeccionadas em três espessuras (2,0, 3,5 e 5,0 mm). Cinco grupos foram estabelecidos, de acordo com os ciclos de polimerização: A) Onda-Cryl, ciclo curto em microondas; B) Onda-Cryl, ciclo longo em microondas; C) Onda-Cryl, ciclo do fabricante; T) Clássico, banho de água; Q) Jet, ciclo em câmara de pressão. Após o seu processamento, as bases de resina acrílica foram pesadas em ar e em água e a porcentagem de porosidade foi relacionada com a absorção de água no interior desse material. Os dados de % de porosidade foram submetidos ao teste de Kruskal-Wallis para a comparação entre os grupos (a= 5%). Dentro das limitações do presente estudo, concluiu-se que os ciclos de polimerização e a espessura do espécime de resina acrílica têm influência na porosidade, já que diferenças estatisticamente significantes foram encontradas entre os ciclos e espessuras avaliados. Não houve diferença de porosidade entre as bases de resina polimerizadas no ciclo T para qualquer uma das espessuras. / Abstract: The aim of this study was to evaluate the porosity on (acrylic resin) maxilar complete denture bases, processed through diferent polimerization cycles, procedure done in three different kinds of thickness (2,0, 3,5 e 5,0 mm). Five groups were proposed, according to the polimerization cycles: A) Onda-Cryl, short microwave cycle; B) Onda-Cryl, long microwave cycle; C) Onda-Cryl, manufacturing microwave cycle; T) Clássico, water bath; Q) Jet, press chamber cycle. After the process, the denture bases were weighted in air and in water, and the percent of porosity was related to the water absorption within this material. The porosityþs % data were submitted to the Kruskal-Wallis test to promote the comparison among the groups. In despite of the present paperþs limitations, we have concluded that the polimerization cycles and the specimenþs thickness of acrylic resin really influence the porosity. This result was reached because statistically significant differences were found in the cycles and thickness evaluated. It has been not observed porosity differences in the polimerized resin bases in T cycle in relation to any thickness. / Mestre

Resumo: O propósito deste estudo foi avaliar a influência do selante de superfície (Biscover LV, Bisco) na microdureza Knoop, rugosidade de superfície e alteração de cor de resinas compostas microhíbridas e nanoparticulada submetidas a envelhecimentos artificiais. Cem espécimes foram confeccionados para cada resina composta, Supreme XT (3M/Espe), Vit-l-escence (Ultradent) e Opallis (FGM). Após 24h, as superfícies das amostras foram polidas e o selante foi aplicado em 50 amostras de cada compósito. A rugosidade de superfície (Ra) foi determinada com um perfilômetro (SJ-400, Mitutoyo) e cut-off de 0,25mm; a microdureza Knoop foi avaliada em um microdurômetro (HMV-2000, Shimadzu), com carga de 50g durante 15s; e a análise cromática inicial foi avaliada de acordo com o sistema CIE L*a*b* em espectrofotômetro de reflexão (UV-2450, Shimadzu). Após as avaliações iniciais, 10 espécimes de cada grupo foram envelhecidos durante 252h em câmara de envelhecimento acelerado de UV (EQUV, Equilam) ou imersos por 4 semanas em uma das três soluções corantes (refrigerante de cola, suco de laranja ou vinho tinto) ou água destilada como controle. Após os envelhecimentos, as propriedades testadas foram re-avaliadas. Os dados de microdureza, rugosidade, alteração de cor foram analisados pela ANOVA e teste de Fischer (α=0,05). Os envelhecimentos artificiais causaram mudanças de cor em todos os grupos e diminuíram os valores de microdureza para todos os materiais, exceto para os compósitos Vit-l-escence e Supreme XT selados, mas não alteraram os valores de rugosidade. O armazenamento em água destilada teve o menor efeito sobre a microdureza e os menores valores de ΔE comparado com os outros processos de envelhecimento (p<0,05). Os materiais selados apresentaram os menores valores de rugosidade e microdureza comparados aos compósitos não selados. Independente do material estudado... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The purpose of this study was to evaluate the influence of surface sealant (Biscover LV, Bisco) on the Knoop microhardness, surface roughness and color alteration of microhybrids and nanofilled composite resins submitted to artificial aging. One hundred specimens were made for each of the composite resins; Supreme XT (3M/Espe), Vit-l-escence (Ultradent) and Opallis (FGM). After 24h, the samples' surfaces were polished and sealant was applied to 50 samples of each composite. The surface roughness (Ra) was determined using a perfilometer (SJ-400, Mitutoyo) and cut-off of 0.25mm; the Knoop microhardness was evaluated in a microdurometer (HMV-2000, Shimadzu), with 50g load during 15s; and the initial chromatic analysis was evaluated in accordance with CIE L*a*b* system in reflection spectrophotometer (UV-2450, Shimadzu). After the initial evaluations, 10 specimens of each group were aged during 252h in a UV-accelerated aging chamber (EQUV, Equilam) or immersed for 4 weeks in one of three staining solutions (cola soft drink, orange juice or red wine) or distilled water as control. After aging, the properties tested were reevaluated. The microhardness, surface roughness and color alteration data were analyzed by ANOVA and Fischer's test (α=0.05). The artificial aging caused color changes in all the groups and decreased the microhardness values for all the materials, except for the Vit-l-escence and Supreme XT sealed composites, but had no effect on the roughness values. The storage in distilled water had the least effect on microhardness and resulted in the lowest values of TE compared with other aging processes (p<0.05). The sealed materials presented the lowest values of surface roughness and microhardness compared to the unsealed composites. Regardless of the material studied, the red wine solution demonstrated the highest level of staining (p<0.0001). Intermediate ΔE values were... (Complete abstract click electronic access below) / Orientador: Paulo Henrique dos Santos / Coorientador: André Luiz Fraga Briso / Banca: Renato Herman Sundfeld / Banca: Flávio Henrique Baggio Aguiar / Mestre

Foram confeccionados corpos-de-prova para testar a resistência flexural (MF), para testar a sorção de água (Wsp) e material solúvel (Ws) em resina quimicamente ativada (RAAQ), baseados nas especificações no 12 da ADA e ISO 1567 utilizando matrizes especiais à temperatura de 37±1oC. Os espécimes foram preparados em contato com um papel contaminado ou não com 20 mg de eugenol e em cinco condições de tratamento superficial: controle (C), Vaselina (V), PanOxyl 10% (P), PanOxyl 10% + DMT (P10D) e PanOxyl 20% + DMT (P20D). Foram utilizados dois tipos de monômero: MMA, como fornecido pelo fabricante, e com EGDMA. O teste de resistência flexural foi aplicado aos 30 minutos ou com 50 horas a partir do início da mistura. A análise de Wsp e Ws foi aplicada sobre espécimes com 7 dias. A análise dos resultados mostrou que a presença do eugenol afetou a polimerização das RAAQ quando não se utilizou nenhum tratamento paliativo, resultando em queda significativa do módulo flexural aos 30 minutos, enquanto que para a idade de 50 horas, houve apenas uma tendência de diminuição dos valores de módulo flexural. O eugenol, provocou uma diminuição significativa da sorção de água, aumentando porém a solubilidade dos espécimes. Os tratamentos superficiais P10D e P20D aplicados durante a polimerização da resina, conseguiram reverter os efeitos negativos da presença do eugenol sobre o módulo flexural, independentemente da presença do agente de ligação cruzada no monômero. Nesses casos, a sorção de água e solubilização não são afetadas significativamente quando comparadas com os espécimes controle. O tratamento com vaselina provocou uma diminuição significativa do módulo flexural independentemente da idade ou presença de EGDMA, embora não tenha aumentado a sorção de água, nem a solubilidade da resina quando o EGDMA esteve presente. Na ausência de EGDMA, este tratamento aumentou a solubilidade. O tratamento P10 apresentou um comportamento pouco seguro, uma vez que não conseguiu anular os efeitos da presença do eugenol em todas as propriedades e situações estudadas, provocando ainda, uma queda significativa do módulo flexural na idade de 50 horas. / Specimens for flexural strength test (FS), water sorption test (Wsp) and soluble matter test (Ws) were built using a chemically-activated acrylic resin, according to ADA\'s no 12 and ISO 1567 specifications. Using a metallic mould under room temperature of 37±1oC, specimens were prepared with the mould placed on contaminated paper slab or not by 20 mg of eugenol. Five experimental conditions were tested: control (C), petrolatum (P), PanOxyl 10% (P10), PanOxyl 10% + DMT (P10D), PanOxyl 20% + DMT (P20D). Two types of monomer were tested: MMA as supplied by manufacturer and MMA + EGDMA. Flexural test was performed at 30 minutes or at 50 hours, after resin manipulation start. The Wsp and Ws analyses were performed after 7 days. The results showed that eugenol significantly reduced the FS at 30 minutes. At 50 hours, only a trend of decrease was found. The presence of eugenol reduced the water sorption and increased the solubility of the specimens. P10D and P20D applied during polymerization reverted the negative effect of eugenol on FS, regardless of the presence of the crosslinking agent. Wsp and Ws were not significantly altered. Petrolatum application reduced FS significantly, regardless of the storage time or the presence of EGDMA. Nevertheless when EGDMA was present, the petrolatum did not interfere with Wsp and Ws. In the absence of EGDMA, petrolatum increased resin solubility. Treatment with P10 was not reliable, because it was not effective for all the properties studied and, moreover, it led to a significant decrease in FS at 50 hours.

A resina de silorano e a sua polimerização catiônica apresentam diferenças quanto aos materiais a base de metacrilato. Como materiais restauradores, estes poderiam ser utilizados juntos, no entanto suas moléculas diferentes poderiam provocar incompatibilidade. Por isso é importante avaliar a união interfacial desses materiais tendo como objetivo a comparação da resistência de união a microtração entre camadas de Filtek P90 aderidas a Filtek Z350, Filtek P90 ou Vitremer utilizando Adper Single Bond 2 ou o Sistema Adesivo P90. Os substratos dos espécimes a serem testados foram fabricados utilizando uma matriz de silicone (5mm x 5mm x 2.5mm) e fotoativados por 40 segundos (Blue Star 3, Microdont; 1076mW/cm2). De acordo com o grupo testado, foi usada ou não uma camada de adesivo fotoativado por 10 segundos. O segundo substrato (2,5mm) foi aplicado e fotoativado por 40 segundos. Os espécimes foram secionados com formato de palito, com uma área de 0,64mm2, e armazenados em água destilada a 37ºC por 24 horas. Realizou-se o teste de microtração utilizando a máquina de ensaios universal com uma velocidade de 0,5mm/min. Foi analizado o tipo de fratura resultante. Os resultados foram analisados utilizando ANOVA e o teste de Tukey (p<0.05). A média e desvio-padrão dos resultados da resistência de união em MPa são: G1 Pad (P90/adesivo P90/P90) 50.9±15.3, G2 P (P90/sem adesivo/P90) 40.2±10.2, G3 Z (Z350/sem adesivo/Z350) 62.1±15.2, G4 Ppol (P90/sem adesivo, tira de poliéster/P90) 28.8±9.2, G5 ZadP (Z350/adesivo P90/P90) 62.1±8.2, G6 PSBZ (P90/Single Bond 2/Z350) 37.1±12.5, G7 ZSB (Z350/Single Bond 2/Z350) 54.3±12.3, G8 VitrZ (Vitremer/Single Bond 2/Z350) 37.4±7.4 e G9 VitrP (Vitremer/adesivo P90/P90) 34.9±4.1. Diferença significativa foi observada entre os grupos G2 e G3, e G5 e G6. Não foi observada diferencia significativa entre os grupos G8 e G9, G5 e G7, G1 e G6. Dentro das limitações do estudo, pode-se concluir que a resina de silorano demonstrou propriedades de adesão similares quando aderida com resina de metacrilato. Valores significativamente menores foram observados entre camadas de P90 (G2) quando comparados com Z350 (G3). / Silorane resin and its cationic polymerization are different from resin-based materials. As restorative materials, their use together could cause some incompatibility that raises the question about the importance of interfacial bonding properties. This study aimed to compare the microtensile bond strengths between layers of Filtek P90 bonded with itself, Filtek Z350 or Vitremer using Adper Single Bond 2 and P90 Adhesive System. Initially, substrates for the testing specimens were fabricated using a silicone mold (5mm x 5mm x 2.5mm) and light-cured for 40 s (Blue Star 3, Microdont; 1076mW/cm2). According to the testing group, it was used or not an adhesive layer, light-cured for 10 s. The second increment (2.5mm) was cured for 40 s. The specimens were sectioned in beams with 0.64mm2 cross-sectional area and stored in distilled water at 37ºC for 24 h. Microtensile bond strength test was performed using a universal testing machine with a 0.5mm/min crosshead speed. Failure modes were assessed. Values were calculated in MPa. Data were analyzed with ANOVA and Tukeys post-hoc tests at a 5% significance level. Microtensile bond strength means and standard deviation are: G1 Pad (P90/P90 adhesive/P90) 50.9±15.3, G2 P (P90/without adhesive/P90) 40.2±10.2, G3 Z (Z350/without adhesive/Z350) 62.1±15.2, G4 Ppol (P90/without adhesive, polyester strip/P90) 28.8±9.2, G5 ZadP (Z350/P90 adhesive/P90) 62.1±8.2, G6 PSBZ (P90/Single Bond 2/Z350) 37.1±12.5, G7 ZSB (Z350/Single Bond 2/Z350) 54.3±12.3, G8 VitrZ (Vitremer/Single Bond 2/Z350) 37.4±7.4 e G9 VitrP (Vitremer/P90 adhesive/P90) 34.9±4.1. Significant difference was showed among G2 and G3, G5 and G6. No significant difference was found between G8 and G9, G5 and G7, G1 and G6. Conclusions: Within the limitations of this study, it can be concluded that silorane composite showed similar bonding properties when bonded with methacrylate-based materials. Significantly lower bond strength was observed between layers of P90 than of Z350.

O objetivo neste trabalho foi avaliar a influência da variação do tempo de fotopolimerização para diferentes cores (I, B1, B3 e C4) de uma resina composta (FiltekTM Z250, da 3M ESPE), sobre a taxa de desgaste abrasivo através do método do disco retificado. Cada espécime de resina composta fotopolimerizada estava contido numa cavidade semicircular localizada na periferia de um disco constituído por polimetilmetacrilato (PMMA), denominado disco estático, sendo que a superfície curva da resina no disco sofria desgaste por um rebolo de porcelana, denominado tecnicamente de disco dinâmico, sob carga padronizada e velocidade controlada, criando no espécime uma cavidade de aspecto semicircular. O deslocamento vertical do disco estático, ao ser desgastado, era detectado por um palpador, o qual transferia estes dados a um computador e criava os arquivos de desgaste, em função do tempo. Os dados obtidos foram tratados estatisticamente. Pôde-se concluir que 1) a resistência à abrasão do PMMA foi a maior de todas e 2) a resina de cor C4, a mais resistente de todas. / The aim at this study was estimate the influence of light-curing time variation of different colors (I, B1, B3 and C4) of composite resin (FiltekTM Z250, 3M ESPE), upon abrasive wear through the retified disc method. The porcelain existent in the named dynamic disc promoted a wear of each resin specimen located in the polimethylmetacrylate (PMMA) static disc, under a standardized charge and with controlled velocity. Vertical displacement of static disc was detected by a sensor that send data to a computer where wear arquives were plotted in function of time. After data statistical analysis, it could be concluded that: 1) PMMA resistance was greater than anyone of resins and 2) C4 was more resistant than all the other colors.

Statement of the problem. The insertion and polymerization of the first resin composite layer in the proximal cavity of class II restorations require attention to achieve cervical sealing as well as good physical properties and clinical longevity. Objective. To evaluate the polymerization efficiency of four resin composites (Filtek Z250XT- 3M ESPE, Filtek One Bulk-Fill-3M ESPE, Filtek Bulk-Fill Flow-3M ESPE and Opus Bulk Fill- FGM) in the cervical region of class II restorations. Material and methods. Sixteen groups (n = 12) were prepared by inserting 2mm increments of the resin composites in a bipartite matrix and being cured with a lightsource of 1000mW/cm2 in continuous mode during 20 or 40 seconds directly on the material (M group) or through a slot preparation (S group) in typodont teeth and all were stored at 37 +/- 1°C, for 24 hours. The Knoop microhardness was evaluated with 25-g-load and 5-s dwell time. Data were analysed with three-way Anova and Tukeys HSD ( = 5%). Results. The results of relative hardness did not show significant difference for the M groups, regardless of the time and type of resin. All the resins had a relative hardness higher than 0.80. In contrast, for S groups, Z250 20s (0.39+0.08) and Bulk FGM 20s (0.47+0.04) showed significant lowest ratios. Bulk Flow 20s (0.70+0.12) and 40s (0.72+0.09), One Bulk 20s (0.65+0.05) and 40s (0.71+0.06) presented no statistical difference with group Z250 40s (0.63+0.05). Conclusion. It would beneficial to increase the time of photoactivation for resins Z250XT and Bulk FGM, differently for Bulk Flow and One Bulk in class 2 proximal slot restorations to ensure adequate hardening. / Problematização. A inserção e polimerização do primeiro incremento de resina composta na caixa proximal de restaurações classe II deve ser efetuada com atenção para garantir um bom selamento cervical, bem como alcançar boas propriedades físicas e longevidade clínica. Objetivo. Avaliar a eficiência da polimerização de quatro resinas compostas (Filtek Z250XT- 3M ESPE, Filtek One Bulk-Fill-3M ESPE, Filtek Bulk-Fill Flow-3M ESPE e Opus Bulk Fill- FGM) na parede cervical de restaurações classe II. Material e métodos. Dezesseis grupos (n=12) foram preparados através da inserção de incrementos de 2mm das resinas em uma matriz bipartida, sendo fotoativados com uma fonte de luz de 1000mW/cm2 em modo contínuo durante 20 e 40 segundos diretamente no material (M) ou através do preparo slot (S) em um dente artificial e armazenados em estufa a 37 +/- 1ºC, por 24 horas. A microdureza Knoop foi avaliada com carga de 25gramas e tempo de permanência de 5segundos. Todos os grupos foram submetidos aos testes estatísticos e avaliados pela análise de variância com três fatores (Anova) e pelo teste de Tukey HSD ( = 5%). Resultados. Os resultados de dureza relativa não apresentaram diferença significante para os grupos M, independente do tempo e tipo de resina. Todas as resinas apresentaram dureza relativa superior a 0.80. Por outro lado, para os grupos S, Z250 20s (0.39+0.08) e Bulk FGM 20s (0.47+0.04) apresentaram valores significativamente menores. Bulk Flow 20s (0.70+0.12) e 40s (0.72+0.09), One Bulk 20s (0.65+0.05) e 40s (0.71+0.06) não apresentaram diferença estatística com o grupo Z250 40s (0.63+0.05). Conclusão. Seria benéfico aumentar o tempo de fotoativação para as resinas Z250XT e Bulk FGM, ao contrário das resinas Bulk Flow e One Bulk em restaurações de classe 2 com preparo slot para melhorar a dureza.