Dissertação (Mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico. / Made available in DSpace on 2012-10-17T05:47:35Z (GMT). No. of bitstreams: 0Bitstream added on 2016-01-08T23:07:36Z : No. of bitstreams: 1 144718.pdf: 13437244 bytes, checksum: f64727ae8979a037f2fd7a695b909b74 (MD5)

Made available in DSpace on 2014-06-12T17:36:07Z (GMT). No. of bitstreams: 2 arquivo2110_1.pdf: 4695184 bytes, checksum: b9271d7ed8aa7f614a9250b4c6ff7da1 (MD5) license.txt: 1748 bytes, checksum: 8a4605be74aa9ea9d79846c1fba20a33 (MD5) Previous issue date: 2010 / A influência da ação dos ventos nas propriedades microestruturais e mecânicas de juntas soldadas do aço ASTM A36 soldado pelos processos FCAW com proteção gasosa (FCAW-G) e FCAW autoprotegido (FCAW-S) foi estudada neste trabalho. Apesar de décadas de utilização do processo FCAW, há pouca literatura disponível sobre a ação dos ventos nesse processo de soldagem. Para a realização desse estudo foram utilizados os arames comerciais Supercored 71 (E71T-1C) e Fabshield XLR-8 (E71T-8J H8). Para a proteção gasosa do primeiro, utilizou-se a Mistura Stargold Plus (75% Ar / 25% CO2). As soldagens para os dois casos foram realizadas em quatro situações: ausência de ventos e sob ação de ventos com velocidades de 2,3 m/s, 3,3 m/s e 4,4 m/s gerados por insuflamento artificial controlado. O ensaio com líquido penetrante já demonstrou claramente que o processo com proteção gasosa é extremamente susceptível a ação do vento, resultando em porosidade excessiva, o mesmo não ocorrendo para o processo com arame tubular autoprotegido. As análises microestruturais por microscopia ótica (MO), assim com os ensaios de dobramento guiados, ratificaram os resultados obtidos por líquidos penetrantes. Os perfis de microdureza levantados mostraram que os efeitos do vento influenciam a convecção de calor sobre o cordão, repercutindo nas propriedades. O ensaio de tração mostrou que o processo FCAW-S pode produzir juntas soldadas sem e com ação do vento com as mesmas qualidades desde que cuidados sejam tomados na remoção da escória. Pontos frágeis podem ser observados se a escória não for corretamente removida, com efeitos deletérios sobre a junta soldada

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2014. / Made available in DSpace on 2014-08-06T18:07:28Z (GMT). No. of bitstreams: 1 326861.pdf: 3302654 bytes, checksum: 2a2ff2f9f8b7c7c1627e43bd29848571 (MD5) Previous issue date: 2014 / As ligas de alumínio-magnésio apresentam uma posição de destaque na indústria naval por se constituírem em materiais estruturais com baixo peso específico e de excelente resistência à corrosão em ambientes marítimos. A soldagem se apresenta como principal processo de fabricação neste setor, e é por isso, que o Laboratório de Soldagem da UFSC (LABSOLDA) se encarregou em desenvolver soluções tecnológicas utilizando diferentes modalidades de soldagem do processo MIG/MAG, levando em consideração o objetivo de construção de um veleiro oceanográfico utilizando a liga de alumínio naval 5083/H116. Esta dissertação de mestrado apresenta uma contribuição técnico-científico com relação aos processos variantes do MIG Convencional: (I) com transferência metálica por curto-circuito controlada designada CMT (Cold Metal Transfer) e, (II) de uma tecnologia que utiliza a pulsação da corrente com transferência metálica que evita o curto-circuito. Quanto à modalidade CMT, verificou-se a compatibilidade dos programas já existentes no equipamento de soldagem, com os metais de adição ER 5183 e ER 5087, com foco na obtenção de passe de raiz para chapas de 6 mm, a qual se mostrou com alta capacidade de obtenção de passe de raiz. Averigou-se também a incursão deste processo sobre os efeitos metalúrgicos para as duas opções de metais de adição, sendo que a liga 5087 apresentou-se como melhor alternativa. Num segundo momento, o trabalho trata do estudo da soldagem MIG Pulsada em aplicações onde a transferência por curto-circuito não era mais admissível, mais especificamente nos passes de preenchimento. Com relação ao MIG Pulsado com corrente contínua foram avaliados alguns conjuntos de parâmetros pré-definidos considerando o expoente da corrente de pulso de 1,83 na equação do coeficiente de destacamento de gota D=Ipn.tp. Como esta modalidade permite o uso de corrente alternada com introdução de período negativo, também foi desenvolvido uma metodologia para definição de parâmetros com propósito de se obter um programa sinérgico, já que esta variante trouxe benefícios em relação à soldagem pulsada com corrente constante. Ambos os processos da versão pulsada já estão sendo utilizados na soldagem do veleiro e também apresentam programas em fontes comerciais.<br> / Abstract : Aluminum-magnesium alloys have great prominence in the naval sector as they represented structural materials with low specific weight and excellent corrosion resistance in marine environments. The welding represents the major manufacturing process in this sector, and that's why the LABSOLDA undertook to develop technology solutions using different modalities of the welding process MIG/MAG, taking into account the aim of building an oceanographic sailboat in 5083 H116 naval aluminum alloy. This dissertation presents both technical and scientific contribution in relation to the conventional MIG process variants: (I) with metal transfer by short circuit designated CMT (Cold Metal Transfer) and (II) a technology that uses the pulse current with metal transfer that avoids short circuit. About the CMT, was verified the compatibility of existing programs in welding equipment, with welding wires that were investigated, the ER 5183 and ER 5087 focused on obtaining root and fill pass to 6 mm plates, which showed high capacity to obtain the root pass. It was also investigated the incursion of this process on metallurgical effects for the different kinds of welding wires, and alloy 5087 was presented as the best alternative. In a second moment, the work deals with the study of Pulsed GMAW welding in applications where the transfer by short circuit was no longer permissible, more specifically in the fill passes. With respect to Pulsed GMAW direct current, some sets of preset parameters were evaluated considering de equation D=Ip1,83.tp. This technique allows the use of alternating current, introducing negative period, also a study was developed aiming to obtain a synergistic program, since this variant provided benefits in relation to pulsed welding with direct current. Both processes of pulsed version are already being used in welding sailboat and also feature programs from commercial sources.

O desempenho de serras de fita bimetálica depende principalmente das características da junção de suas extremidades, executada pelo processo de soldagem topo-a-topo por centelhamento. Este é um processo de soldagem por resistência, constituído por um aquecimento elétrico, seguido por um rápido forjamento dos materiais. O presente trabalho tem como objetivo, estudar a influência da variação da corrente elétrica, força de recalque e tratamento térmico de revenimento nas microestruturas e propriedades mecânicas das juntas soldadas topo-a-topo por centelhamento. Neste estudo, foram utilizadas amostras de serras de fita bimetálica de 27 mm de largura e 0,9 mm de espessura. O material é um composto bimetálico constituído por aço rápido M42 para os dentes, soldado a um corpo de aço carbono de baixa liga e alta resistência D-6a. As microestruturas e as propriedades mecânicas das amostras soldadas foram investigadas. Foi observado que os parâmetros de soldagem e o revenimento afetam as propriedades mecânicas. A dureza na seção transversal à linha central da solda apresentou valores levemente superiores à respectiva dureza na seção longitudinal. Amostras não revenidas resultaram em maior resistência à tração, associada ao parâmetro de menor temperatura de revenimento. Ficou evidenciado que o revenimento reduziu a dureza e a resistência à tração de todas as amostras. / The performance of bimetal band saw blades depends mainly on the features of joining their ends, carried out by flash butt welding process. This is a resistance welding method, which consists of electrical heating followed by a fast material forging. The present work has the objective of studying the influence of changing the electrical current, upset force and tempering heat treatment on the microstructures and mechanical properties of the flash butt welded joints. In this study, samples of bimetal band saw blades having width of 27 mm and thickness of 0.9 mm were employed. The material consists of a composite M42 high speed steel for the teeth welded together with a D-6a ultra-high strength carbon low alloy steel for the backer. The microstructure and mechanical properties have been investigated. It is pointed out that welding parameters and tempering affected the mechanical properties. The transversal hardness to the welding center line has shown values slightly higher than the respective longitudinal hardness. Non-tempered samples gave the highest tensile strength with the parameter of lowest tempering temperature. It is also found that the tempering reduces the hardness and the tensile strength of all samples.

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2013 / Made available in DSpace on 2013-12-06T00:11:19Z (GMT). No. of bitstreams: 1 319295.pdf: 2898907 bytes, checksum: e7aae313fd966a84349a407b38f302cd (MD5) / O processamento de materiais compósitos tem despertado interesse dos engenheiros pelo fato de combinar propriedades termomecânicas, ópticas e magnéticas em um único material de engenharia. Este trabalho propõe estudar a moagem de alta energia como meio de produção de um material compósito de matriz metálica a base dos elementos Sn e Ag reforçada com partículas cerâmicas nanométricas de alumina (Al2O3) com o intuito de se obter um material funcional para soldagem branda de componentes eletrônicos em placas de circuito impresso com melhores propriedades termomecânicas. Analisaram-se, especificamente, os parâmetros de processamento e qualidade final do material quanto à homogeneidade de distribuição das nanopartículas na matriz metálica. Inicialmente, três composições diferentes foram estudadas, alterando-se a quantidade em massa das nanopartículas cerâmicas nas seguintes proporções: (SnAg3,5:Al2O3) 99:01, 95:05 e 90:10. Os parâmetros de moagem de alta energia foram estudados com auxílio de caracterização microestrutural por microscopia ótica e eletrônica, difração de raios-X e análise de energia dispersiva. Estudou-se posteriormente o processo de preparação do pó para a fabricação de corpos de prova consistentes para ensaios termomecânicos. Também nesta parte, a análise microestrutural revelou a qualidade da dispersão do material de adição na matriz metálica com o aumento da inserção de energia no sistema, levando a produção de um pó com tamanho médio de partícula oscilando entre 70 e 200 µm. Como investigação final procurou-se identificar as melhores rotas de processo para se preparar corpos de prova para ensaios termomecânicos. Primeiramente procurou-se utilizar técnicas de fusão, porém averiguou-se que acima da temperatura de fusão da matriz metálica de SnAg3,5 as nanopartículas perdiam sua distribuição homogênea ao segregarem. Para evitar perder a distribuição homogênea das nanopartículas, procurou-se dominar uma rota alternativa considerando-se técnicas de sinterização. Um estudo aprofundado do diagrama de Ellingham mostrou que não seria possível produzir pó livre de óxido nas condições existentes de trabalho <br>

O desempenho de serras de fita bimetálica depende principalmente das características da junção de suas extremidades, executada pelo processo de soldagem topo-a-topo por centelhamento. Este é um processo de soldagem por resistência, constituído por um aquecimento elétrico, seguido por um rápido forjamento dos materiais. O presente trabalho tem como objetivo, estudar a influência da variação da corrente elétrica, força de recalque e tratamento térmico de revenimento nas microestruturas e propriedades mecânicas das juntas soldadas topo-a-topo por centelhamento. Neste estudo, foram utilizadas amostras de serras de fita bimetálica de 27 mm de largura e 0,9 mm de espessura. O material é um composto bimetálico constituído por aço rápido M42 para os dentes, soldado a um corpo de aço carbono de baixa liga e alta resistência D-6a. As microestruturas e as propriedades mecânicas das amostras soldadas foram investigadas. Foi observado que os parâmetros de soldagem e o revenimento afetam as propriedades mecânicas. A dureza na seção transversal à linha central da solda apresentou valores levemente superiores à respectiva dureza na seção longitudinal. Amostras não revenidas resultaram em maior resistência à tração, associada ao parâmetro de menor temperatura de revenimento. Ficou evidenciado que o revenimento reduziu a dureza e a resistência à tração de todas as amostras. / The performance of bimetal band saw blades depends mainly on the features of joining their ends, carried out by flash butt welding process. This is a resistance welding method, which consists of electrical heating followed by a fast material forging. The present work has the objective of studying the influence of changing the electrical current, upset force and tempering heat treatment on the microstructures and mechanical properties of the flash butt welded joints. In this study, samples of bimetal band saw blades having width of 27 mm and thickness of 0.9 mm were employed. The material consists of a composite M42 high speed steel for the teeth welded together with a D-6a ultra-high strength carbon low alloy steel for the backer. The microstructure and mechanical properties have been investigated. It is pointed out that welding parameters and tempering affected the mechanical properties. The transversal hardness to the welding center line has shown values slightly higher than the respective longitudinal hardness. Non-tempered samples gave the highest tensile strength with the parameter of lowest tempering temperature. It is also found that the tempering reduces the hardness and the tensile strength of all samples.

[pt] Este trabalho apresenta um estudo da soldabilidade do aço API 5L X-80 utilizando os Testes Tekken e de Implante. A pesquisa avalia a soldabilidade do aço X-80 para a soldagem circunferencial com eletrodo revestido e arame tubular com relação à formação de trincas induzidas por hidrogênio. O objetivo é viabilizar diferentes opções de processos de soldagem para o aço em questão. Para o Teste Tekken foram soldados dois pares de chapas pelo processo SMAW utilizando o consumível E8010-G e mais dois pares pelo processo FCAW-G com o consumível E101T1-GM-H8. Para o Teste de Implante foram utilizados três chapas de suporte e dez implantes, sendo que quatro implantes foram soldados pelo processo SMAW com E8010-G e seis pelo processo FCAW- G com E101T1- GM-H8. Todos os implantes apresentavam 6 mm de diâmetro. Para todos os testes a temperatura de preaquecimento foi de 100°C. A quantidade de hidrogênio difusível nos metais de solda produzidos pelos dois consumíveis foi medida pelo processo de Cromatografia Gasosa. Após a realização dos testes, todas as amostras foram observadas sem e com ataque no MO e no MEV para que as trincas induzidas por hidrogênio na ZTA e no MS (no caso do Teste Tekken) pudessem ser analisadas e medidas. A partir desse procedimento foi possível observar que todas as amostras apresentaram trincas transgranulares com comprimentos da ordem de 17,68 um, muito pequenas e improváveis de serem prejudiciais ao aço. Isso possibilita dizer que o aço X- 80 pode ser soldado utilizando os consumíveis avaliados, sem riscos de danos maiores para o material. / [en] This work shows a study of the weldability of API 5L X-80 steel using the Tekken Test and the Implant Test. The research analises the weldability of HSLA X-80 steel for orbital circunferencial welding with the Shielded Metal Arc Weld and the Flux Core Arc Weld processes with regard to hydrogen induced cracking formation. The aim is to make feasible different options of welding process for the steel at issue. For the Tekken Test two pairs of plates were welded by SMAW process using E8010-G consumable and two more pairs by FCAW- G process using E101-T1-GM-H8. The Implant Test used three base plates and ten implants, being four implants welded by SMAW process and with E8010-G consumable and six by FCAW-G process with E101T1-GM-H8 consumable. All the implants have 6 mm of diameter. For all tests the preheating temperature was 100°C. The diffusible hydrogen content deposited by both consumables was measured by the Gas Chromatography Method. After the tests all the samples were examined without and with attack by means of optical microscope and SEM to allow hydrogen induced cracking in the HAZ and in the weld metal (for Tekken Test) to be viewed and measured. By means of this procedure it was possible to observe that all samples showed transgranular cracking with length of 17,68 um, too small and unlikely to the be bad to the steel. It allows saying that X-80 steel can be welded using the consumables tested, without a risk of damage of the material.

A soldagem altera as propriedades mecânicas dos aços ligados ao níquel, em especial seu desempenho em aplicações criogênicas. Assim, este trabalho apresenta um estudo sobre a soldabilidade metalúrgica do aço com 9% níquel e tem como objetivos: identificar se a fragilização em temperatura abaixo da temperatura Ac3 ocorre em ZACs com dois e três ciclos térmicos simulados fisicamente; analisar as características da junta soldada pelo processo de soldagem por atrito linear com mistura e os efeitos da soldagem multipasse; e analisar a influência dos passes de enchimento e acabamento sobre o comportamento mecânico da ZAC da raiz de uma junta soldada pelo processo de soldagem MIG/MAG. Destacam-se entre os resultados da simulação física da ZAC: as amostras que tiveram a temperatura máxima abaixo da temperatura Ac1, no terceiro ciclo térmico, não apresentaram o efeito de redução da energia absorvida no ensaio Charpy V; a fração volumétrica de austenita retida não aumenta a quantidade de energia absorvida no ensaio Charpy V para as amostras que tiveram a temperatura máxima do segundo ciclo térmico abaixo da temperatura Ac3 (723°C); e a correlação linear múltipla sugere um modelo empírico, baseado nos dados deste trabalho, onde os fatores de fração volumétrica do microconstituinte martensita-austenita, fração volumétrica de austenita retida e tamanho de grão são mais relevantes para a quantidade de energia absorvida no ensaio Charpy V. Destacam-se entre os resultados da soldagem por atrito linear: a energia absorvida no ensaio Charpy V da zona misturada do primeiro cordão (CP1) é menor que o metal de base; o segundo cordão gera duas regiões na zona misturada do primeiro cordão, que tendem a aumentar a energia absorvida no ensaio Charpy V; os valores de energia absorvida no ensaio Charpy V apresentam correlações lineares simples com a microdureza, a fração volumétrica do microconstituinte martensita-austenita e com o tamanho de grão. Destacam-se entre os resultados da soldagem com MIG/MAG: A soldagem do aço com 9% de níquel com a liga Inconel 625 gera uma zona não misturada entre o metal de solda e a ZAC; a amostra com todos os passes de solda (CP3) apresenta a menor energia absorvida no ensaio Charpy V entre todos os experimentos; e a trinca, no ensaio Charpy V, propaga na zona não misturada no CP1 e no CP2, que tiveram as maiores energias absorvidas no ensaio Charpy. O CP3 apresenta propagação de trinca na linha de fusão e possui a menor energia absorvida no ensaio Charpy V. / Welding modify the mechanical properties of nickel steels, especially their performance in cryogenic applications. Thus, this work presents a study on the metallurgical weldability of 9% nickel steel and its objectives are: identify if the embrittlement in temperature below the Ac3 temperature occurs in HAZs with two and three thermal cycles simulated physically; analyze the characteristics of the joint welded by friction stir welding process and the effects of multipass welding; and analyze the influence of the filling and finishing passes on the mechanical behavior of HAZ from the root of a joint welded by the GMAW welding process. The results of the physical simulation of the HAZ were: the samples that had the maximum temperature below the temperature Ac1, in the third thermal cycle, did not present the effect of reduction of the energy absorbed in the Charpy V test; the retained austenite volumetric fraction does not increase the amount of energy absorbed in the Charpy V test for the samples having the maximum temperature of the second thermal cycle below the Ac3 temperature (723 °C); and the multiple linear correlation suggests an empirical model, based on the data of this work, where the volumetric fraction factors of the martensite-austenite microconstituent, retained austenite volumetric fraction and grain size are more relevant for the amount of energy absorbed in the Charpy V test. The FSW welding highlights results: the energy absorbed in the Charpy V test of the mixed zone of the first pass (CP1) is smaller than the base metal; the second pass generates two regions in the mixed zone of the first pass, which tend to increase the energy absorbed in the Charpy V test; the values of energy absorbed in the Charpy V test show simple linear correlations with the microhardness, the volumetric fraction of the martensite-austenite microconstituent and with the grain size. The GMAW welding highlights results: welding of the steel with 9% nickel with the Inconel 625 alloy makes an unmixed zone between the weld metal and the HAZ; the sample with all weld passes (CP3) shows the lowest energy absorbed in the Charpy V test among all the experiments; and the crack, in the Charpy V test, propagates in the unmixed zone in CP1 and CP2, which had the highest energies absorbed in the Charpy test. The CP3 shows crack propagation in the melting line and has the lowest energy absorbed in the Charpy V test.

A soldagem altera as propriedades mecânicas dos aços ligados ao níquel, em especial seu desempenho em aplicações criogênicas. Assim, este trabalho apresenta um estudo sobre a soldabilidade metalúrgica do aço com 9% níquel e tem como objetivos: identificar se a fragilização em temperatura abaixo da temperatura Ac3 ocorre em ZACs com dois e três ciclos térmicos simulados fisicamente; analisar as características da junta soldada pelo processo de soldagem por atrito linear com mistura e os efeitos da soldagem multipasse; e analisar a influência dos passes de enchimento e acabamento sobre o comportamento mecânico da ZAC da raiz de uma junta soldada pelo processo de soldagem MIG/MAG. Destacam-se entre os resultados da simulação física da ZAC: as amostras que tiveram a temperatura máxima abaixo da temperatura Ac1, no terceiro ciclo térmico, não apresentaram o efeito de redução da energia absorvida no ensaio Charpy V; a fração volumétrica de austenita retida não aumenta a quantidade de energia absorvida no ensaio Charpy V para as amostras que tiveram a temperatura máxima do segundo ciclo térmico abaixo da temperatura Ac3 (723°C); e a correlação linear múltipla sugere um modelo empírico, baseado nos dados deste trabalho, onde os fatores de fração volumétrica do microconstituinte martensita-austenita, fração volumétrica de austenita retida e tamanho de grão são mais relevantes para a quantidade de energia absorvida no ensaio Charpy V. Destacam-se entre os resultados da soldagem por atrito linear: a energia absorvida no ensaio Charpy V da zona misturada do primeiro cordão (CP1) é menor que o metal de base; o segundo cordão gera duas regiões na zona misturada do primeiro cordão, que tendem a aumentar a energia absorvida no ensaio Charpy V; os valores de energia absorvida no ensaio Charpy V apresentam correlações lineares simples com a microdureza, a fração volumétrica do microconstituinte martensita-austenita e com o tamanho de grão. Destacam-se entre os resultados da soldagem com MIG/MAG: A soldagem do aço com 9% de níquel com a liga Inconel 625 gera uma zona não misturada entre o metal de solda e a ZAC; a amostra com todos os passes de solda (CP3) apresenta a menor energia absorvida no ensaio Charpy V entre todos os experimentos; e a trinca, no ensaio Charpy V, propaga na zona não misturada no CP1 e no CP2, que tiveram as maiores energias absorvidas no ensaio Charpy. O CP3 apresenta propagação de trinca na linha de fusão e possui a menor energia absorvida no ensaio Charpy V. / Welding modify the mechanical properties of nickel steels, especially their performance in cryogenic applications. Thus, this work presents a study on the metallurgical weldability of 9% nickel steel and its objectives are: identify if the embrittlement in temperature below the Ac3 temperature occurs in HAZs with two and three thermal cycles simulated physically; analyze the characteristics of the joint welded by friction stir welding process and the effects of multipass welding; and analyze the influence of the filling and finishing passes on the mechanical behavior of HAZ from the root of a joint welded by the GMAW welding process. The results of the physical simulation of the HAZ were: the samples that had the maximum temperature below the temperature Ac1, in the third thermal cycle, did not present the effect of reduction of the energy absorbed in the Charpy V test; the retained austenite volumetric fraction does not increase the amount of energy absorbed in the Charpy V test for the samples having the maximum temperature of the second thermal cycle below the Ac3 temperature (723 °C); and the multiple linear correlation suggests an empirical model, based on the data of this work, where the volumetric fraction factors of the martensite-austenite microconstituent, retained austenite volumetric fraction and grain size are more relevant for the amount of energy absorbed in the Charpy V test. The FSW welding highlights results: the energy absorbed in the Charpy V test of the mixed zone of the first pass (CP1) is smaller than the base metal; the second pass generates two regions in the mixed zone of the first pass, which tend to increase the energy absorbed in the Charpy V test; the values of energy absorbed in the Charpy V test show simple linear correlations with the microhardness, the volumetric fraction of the martensite-austenite microconstituent and with the grain size. The GMAW welding highlights results: welding of the steel with 9% nickel with the Inconel 625 alloy makes an unmixed zone between the weld metal and the HAZ; the sample with all weld passes (CP3) shows the lowest energy absorbed in the Charpy V test among all the experiments; and the crack, in the Charpy V test, propagates in the unmixed zone in CP1 and CP2, which had the highest energies absorbed in the Charpy test. The CP3 shows crack propagation in the melting line and has the lowest energy absorbed in the Charpy V test.

Aços de alta resistência e baixa liga (ARBL) são uma alternativa atraente em aplicações estruturais. Devido ao baixo teor de carbono e de elementos de liga (Ni, V e Ti), os aços ARBL apresentam bons níveis de tenacidade e de resistência mecânica, além de boa soldabilidade, permitindo assim, o uso de componentes estruturais mais leves, a economia no consumo de combustível, bem como o desenvolvimento de construções ambientalmente corretas. A boa combinação de propriedades mecânicas permite que os aços ARBL sejam amplamente utilizados na construção naval, na indústria petrolífera e na indústria automotiva. Para estas aplicações, a tecnologia de soldagem é inevitável, a qual produz alterações microestruturais localizadas e redução dos níveis de resistência mecânica, tensões residuais e defeitos indesejáveis, que geram problemas potenciais de segurança e de confiabilidade. Estes defeitos de soldagem acentuam o processo de falha de fadiga, quando componentes mecânicos são submetidos a cargas cíclicas. Neste trabalho, estudou-se a influência do processo de soldagem por arco elétrico com atmosfera de proteção gasosa (GMAW) na microestrutura, propriedades mecânicas e resistência à fadiga do aço ARBL DIN EN 10149 S700MC, aplicando três velocidades de soldagem e dois diferentes metais de adição (AWS ER 70 S – 6 e AWS E 110C-G-M). Para isso, corpos de prova deste aço ARBL e juntas soldadas desses dois metais de adição foram estudadas por meio de análises microestruturais, ensaios de tração uniaxial, microdureza e ensaios de fadiga por tração uniaxial. Os resultados mostraram que a velocidade de soldagem não causou alterações significativas na microestrutura do metal de solda e da zona termicamente afetada, na microdureza e na resistência à tração, quando foi utilizado o mesmo metal de solda. Porém, maiores velocidades de soldagem causaram o aumento do defeito de mordedura. Além disso, verificou-se um aumento da vida em fadiga do componente com a diminuição da velocidade de soldagem. Quando comparadas as amostras soldadas com uma mesma velocidade de soldagem, observou-se um aumento da proporção de ferrita acicular no metal de solda, um aumento da tensão de ruptura e, consequentemente, uma melhora da vida em fadiga do componente, em função do aumento da resistência mecânica do metal de solda. / Submitted by Ana Guimarães Pereira (agpereir@ucs.br) on 2017-05-10T18:40:43Z No. of bitstreams: 1 Dissertacao Rui Gustavo Lippert Schwanke.pdf: 11672515 bytes, checksum: 14a40d04483fb3216e392d56449ded89 (MD5) / Made available in DSpace on 2017-05-10T18:40:43Z (GMT). No. of bitstreams: 1 Dissertacao Rui Gustavo Lippert Schwanke.pdf: 11672515 bytes, checksum: 14a40d04483fb3216e392d56449ded89 (MD5) Previous issue date: 2017-05-10 / Conselho Nacional de Desenvolvimento Científico e Tecnológico. / High strength and low alloy steels (HSLA) are attractive alternative in structural applications. Due to the low carbon and alloying elements (Ni, V and Ti) contents, HSLA steels show good levels of toughness and mechanical strength, besides good weldability, allowing use of lighter structural components, fuel economy, as well as the development of environmentally-friendly constructions and sustainable societies. The good combination of mechanical properties allows HSLA steels to be widely used in shipbuilding oil industry and automotive industry. For these applications, welding technology is inevitable, however it produces localized microstructural changes and reduction in the levels of mechanical strenght, residual stresses and undesirable defects, which generate potential problems of security and reliability. These welding defects accentuate the fatigue failure process when mechanical components are subjected to cyclic loads. In this work, the influence of the gas metal arc welding process (GMAW) on microstructure, mechanical properties and fatigue life of the HSLA DIN EN 10149 S700MC steel was studied, applying three welding speeds and two different addition metals (AWS ER 70 S-6 and AWS E 110C-G-M). For this purpose, samples of this HSLA steel and welded joints of these two addition metals were studied by microstructural analysis, uniaxial tension tests, microhardness tests and uniaxial tension fatigue tests. The results showed that the welding speed did not cause significant changes in the microstructure of the weld metal and of the heat-affected zone, in the microhardness and in the tensile strength, when the same weld metal was used. However, higher welding speeds caused the increase of the undercut defect. Besides that, an increase in fatigue life of the component with the decrease in welding speed was verified. When welded samples produced with the same welding speed were compared, an increase in the ratio of acicular ferrite in the weld metal zone, in the tensile stress and, consequently, an improvement in the fatigue life of the component was observe as a function of the increase in mechanical resistance of the weld metal.