Made available in DSpace on 2014-08-20T13:42:10Z (GMT). No. of bitstreams: 1 Dissertacao_Franciela_Spier.pdf: 855733 bytes, checksum: b77db27392fb17bb6c91b99ba915397c (MD5) Previous issue date: 2010-03-30 / The starch market has been growing and improving, leading to search for products with unique functional properties that industry requirements. The use of native starches is limited, depending on the processing conditions such as temperature, pH, pressure restricting its application in industrial scale. The production of modified starch is an alternative that has been in development for some time in order to overcome one or more limitations of native starches, increasing its use in industry. The objective of this research was to evaluate the properties of corn starch chemically modified, alone or combined action by the acid, oxidative and alkaline. The corn starch granules were treated with a solution of sodium hydroxide at concentrations of 0.09% and 0.18%, with lactic acid solution, 2% and 4%, and a solution of sodium hypochlorite 1% and 2%. Later were neutralized, washed, dried, ground and stored. The starches were evaluated for amylose content, content of carbonyl and carboxyl, paste properties, diffraction of X-ray, swelling power and solubility and enzymatic susceptibility. The corn starch oxidized with sodium hypochlorite (2%) showed a reduction in levels of amylose and treated with alkali and acid increased. The oxidative treatment increased gradually, the levels of carbonyl and carboxyl with increasing concentration of sodium hypochlorite. Among the treatments studied the oxidative treatment was more interference in the pasting properties of starch increased the maximum viscosity and breakdown and reduce the pasting temperature and final viscosity. The interaction between the alkaline and acid treatments affected the crystallinity of maize starch. The oxidative treatment increased the solubility of corn starch at all temperatures examined, especially in the incubation temperatures are higher than the highest concentration (2%), significantly increased the rate of hydrolysis / O mercado de amidos vem crescendo e se aperfeiçoando, levando à busca de produtos com características específicas que atendam às exigências da indústria. A utilização de amidos nativos é limitado, em função das condições de processamento como temperatura, pH e pressão que restringem sua aplicação em escala industrial. A produção de amidos modificados é uma alternativa que vem sendo desenvolvida há algum tempo com o objetivo de superar uma ou mais limitações dos amidos nativos, aumentando sua utilização na indústria. O objetivo do trabalho foi avaliar as propriedades de amido de milho modificado quimicamente, de forma isolada ou combinada, pela ação alcalina, ácida e oxidativa. Os amidos de milho foram tratados com solução de hidróxido de sódio nas concentrações de 0,09% e 0,18%, com solução de ácido lático, 2% e 4%, e com solução de hipoclorito de sódio 1% e 2%. Posteriormente foram neutralizados, lavados, secos, moídos e armazenados. Os amidos foram avaliados quanto ao teor de amilose, teor de carbonila e carboxila, propriedades de pasta, difração de raio-X, poder de inchamento e solubilidade e suscetibilidade enzimática. Os amidos de milho oxidados com hipoclorito de sódio (2%) apresentaram uma redução nos teores de amilose e os tratados com álcali e ácido um acréscimo. O tratamento oxidativo aumentou os teores de carbonila e carboxila com o aumento da concentração de hipoclorito de sódio. Dentre os tratamentos estudados o oxidativo foi o que interferiu mais nas propriedades de pasta do amido, aumentando a viscosidade máxima e a quebra, além de reduzir a temperatura de pasta e a viscosidade final. A interação entre os tratamentos alcalino e ácido aumentou a cristalinidade relativa do amido de milho. O tratamento oxidativo aumentou a solubilidade do amido de milho em todas as temperaturas analisadas, principalmente nas temperaturas de incubação mais elevadas, sendo que na maior concentração (2%), aumentou significativamente a taxa de hidrólise.

Submitted by Emanuel Varela Cardoso (emanuel.varela@ufcg.edu.br) on 2018-06-22T18:16:20Z No. of bitstreams: 1 JÉSSICA CAMILLA DA COSTA LIMA – DISSERTAÇÃO (UAEMa) 2016.pdf: 6436164 bytes, checksum: 0eb0aed4e907b380df345b619174c509 (MD5) / Made available in DSpace on 2018-06-22T18:16:20Z (GMT). No. of bitstreams: 1 JÉSSICA CAMILLA DA COSTA LIMA – DISSERTAÇÃO (UAEMa) 2016.pdf: 6436164 bytes, checksum: 0eb0aed4e907b380df345b619174c509 (MD5) Previous issue date: 2016-02-24 / Capes / Com o intuito de superar algumas limitações do poli(ácidolático) (PLA), foi feita sua mistura com o copolímero poli(estireno/etileno-butileno/estireno) (SEBS), em diferentes concentrações e avaliadas diversas propriedades. As blendas contendo 5,10, 15 e 20% em massa do SEBS foram preparadas por extrusão seguida de injeção e caracterizadas por ensaios reológicos, difratometria de raios X (DRX), espectroscopia na região do infravermelho com transformada de Fourier (FTIR), calorimetria exploratória diferencial (DSC), análise térmica dinâmico-mecânica (DMTA), temperatura de deflexão térmica (HDT), propriedades mecânicas e a morfologia foi investigada por microscopia eletrônica de varredura (MEV). Estas propriedades foram avaliadas antes e após tratamento térmico de recozimento. Os resultados de reometria de torque indicaram que as blendas apresentam maior estabilidade quando comparadas ao PLA puro. Em baixas frequências (reômetro oscilatório) o PLA e as blendas PLA/SEBS contendo 5 e 10% de SEBS apresentam um comportamento de fluido newtoniano, já as blendas contendo 15 e 20% apresentam um comportamento de fluido pseudoplástico, observa-se também a presença de dois arcos distintos para todas as blendas, indicando que as fases de PLA e SEBS são imiscíveis. Verifica-se para as blendas PLA/SEBS contendo 15 e 20% de SEBS, há uma mudança na inclinação das curvas, esta mudança indica que as mesmas passam a apresentar um comportamento de pseudo-sólido. Nos padrões de DRX das amostras submetidas ao tratamento térmico de recozimento observa-se um pico intenso e bem definido caracterizando cristalinidade considerável das amostras. As análises de DSC e DMTA indicaram que com tratamento térmico ocorreu o desaparecimento da temperatura de cristalização a frio (Tcc) doPLA. As amostras recozidas apresentaram valores de HDT mais elevados. Observou-se um balanço de propriedades mecânicas, no qual o módulo elástico e a resistência à tração tiveram uma pequena redução para as blendas sem tratamento e aumento destas propriedades com tratamento térmico, enquanto que o alongamento, a tenacidade e resistência ao impacto tiveram aumento significativo para as amostras sem e com tratamento térmico. Os resultados de MEV indicaram que com o aumento da concentração do copolímero observa-se aumento do tamanho médio das partículas, provavelmente devido à ocorrência de coalescência. Os resultados de MEV após tratamento térmico em geral, pode-se observar um refinamento no tamanho médio das partículas 7 dispersas de SEBS que influenciou nas propriedades mecânicas. As blendas estudadas no presente trabalho apresentam propriedades muito atrativas, contendo pequenas quantidades do copolímero sintético. Omaterial desenvolvido advém, em sua maior proporção, de fontes renováveis, contribuindo assim, com o meio ambiente. / In order to overcome certain limitations of poly (lactic acid) (PLA) biopolymer, the same was modified with poly (styrene / ethylene-butylene / styrene)(SEBS) copolymer, and the effect of different content of this copolymer on the properties of the blends, before and after heat treatment, was evaluated. The blends containing 5, 10, 15 and 20 wt% of SEBS were prepared by extrusion followed by injection molding and characterized by rheological measurements, X-ray diffraction (XRD) Fourier transform infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), dynamic mechanical thermal analysis (DMTA) and heat deflection temperature (HDT). The results of torque rheometry indicated that the blends exhibited increased stability compared to pure PLA. At low frequencies (oscillation rheometer) PLA and PLA / SEBS blends containing 5 and 10% of SEBS exhibited a Newtonian fluid behavior, and the blends containing 15 and 20% SEBS showed a shear thinning behavior. It was also observed the presence two distinct arcs for all blends, indicating that the SEBS and PLA phases are immiscible. It was also observed that in the PLA / SEBS blends containing 15 and 20% SEBS, there is a change in the slope of the curves. This change indicates that they begin to present a pseudo-solid behavior. In the XRD patterns of the samples subjected to annealing heat treatment a well-defined intense peak was observed for PLA indicating its considerable crystallinity in the samples. The FTIR analysis pointed out, by the presence of characteristic bands, that the PLA presented higher crystallinity after the annealing heat treatment. The annealed samples showed higher HDT values. There was a balance of mechanical properties, wherein the elastic modulus and the tensile strength proved to be inversely proportional to the content of the copolymer, while the elongation and tenacity were directly proportional to this content. The addition of the copolymer caused a significant increase in the impact strength for samples with and withoutheat treatment. The SEM results showed that when the SEBS copolymer content was increased, an increase in the average particle size of SEBS dispersed phase was observed, probably due to the occurrence of coalescence. SEM results for samples after heat treatment showed a decrease in average size of dispersed particles of SEBS, which affected the mechanical properties. The blend studied in this paper presented very attractive properties, and contains small amounts of the synthetic 9 copolymer. The developed material comes, in its most proportion, from renewable sources, thus contributing to the environment.

Made available in DSpace on 2016-12-08T17:19:26Z (GMT). No. of bitstreams: 1 Marindia Decol.pdf: 3575085 bytes, checksum: bed6c0ed662d3c76c64b6cfdac902d8b (MD5) Previous issue date: 2015-07-15 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Poly (lactic acid) (PLA) is a rigid and brittle thermoplastic polymer, and poly (ε-caprolactone) (PCL) is a thermoplastic polymer of lower rigidity and higher toughness than PLA. Combination of these properties through the blend PLA/PCL has been studied successfully to change the final properties of the PLA. The addition of multiwalled carbon nanotubes (MWCNT) in the blend PLA/PCL may induce peculiar orphologies depending on their location, resulting in the getting new properties or modifying the properties of the PLA matrix. This study aimed to evaluate the effect of adding the PCL, the compatibilizer Cesa-mix and MWCNT the final properties of the PLA. Mixtures were prepared in internal mixer chamber coupled to a torque rheometer and subjected to characterizations of morphological, thermal, mechanical and electrical properties. In the morphological analysis, there was a 37% reduction in the average size of the phases of the PCL blends PLA/PCL with the addition of compatibilizer Cesa®- mix, a heterogeneous distribution of MWCNT the PLA matrix and a selective location of MWCNT in phase PCL. With respect to thermal properties, the addition of the compatibilizing PCL and did not significantly affect the thermal degradation onset temperature (Tonset) of the PLA, but the addition of the MWCNT in PLA resulted in decreased Tonset nanocomposites. The melting temperature did not change significantly with the addition of PCL, the compatibilizer and MWCNT on the PLA matrix. Already cold crystallization temperature decreased and the degree of crystallinity of the PLA increased with the addition of PCL blends and MWCNT in nanocomposites. Decreases of 35% on elastic hardness and 29% in modulus of elasticity was observed with the addition of PCL and compatibilizer Cesa®-mix in the blends PLA/ PCL/AC/2,5%. With the addition of MWCNT was observed an increase of 6,8% on elastic hardness and 8% in the modulus of elasticity of PLA/CNT mixtures with 1,0% w/w. Blends of PLA/PCL with 0,5% and 1,0% w/w CNT with and without compatibilizer, had a decrease in modulus of elasticity and elastic hardness. No significant changes were observed in the electric resistance of the samples with the addition of the compatibilizer, the PCL and MWCNT with 0,5% and 1,0% w/w. Selective location of MWCNT the PCL phase had great influence on morphological, thermal, mechanical and electrical properties of nanocomposites. / O poli(ácido lático) (PLA) é um polímero termoplástico rígido e frágil, e a poli(ε-caprolactona) (PCL) é um polímero termoplástico de menor rigidez e maior tenacidade que o PLA. A combinação destas propriedades através da blenda PLA/PCL tem sido estudada com êxito no auxílio à alteração das propriedades finais do PLA. A adição de nanotubos de carbono de paredes múltiplas (NTCPM) na blenda PLA/PCL pode induzir a morfologias peculiares dependendo da sua localização, resultando na obtenção de novas propriedades ou na alteração das propriedades da matriz PLA. Este trabalho teve como objetivo avaliar o efeito da adição do PCL, do compatibilizante Cesa-mix e dos NTCPM nas propriedades finais do PLA. As misturas foram preparadas em misturador de câmara interna acoplado a reômetro de torque e submetidas à caraterizações das propriedades morfológicas, térmicas, mecânicas e elétricas. Na análise morfológica, observou-se uma redução de 37% no tamanho médio das fases de PCL nas blendas PLA/PCL com a adição do compatibilizante Cesa®- mix, uma distribuição heterogênea dos NTCPM na matriz PLA e uma localização seletiva dos NTCPM na fase PCL. Em relação às propriedades térmicas, a adição do PCL e do compatibilizante não afetaram significativamente na temperatura de início de degradação térmica (Tonset) do PLA, porém a adição de NTCPM no PLA resultou em decréscimo na Tonset dos nanocompósitos. A temperatura de fusão não apresentou variação significativa com a adição do PCL, do compatibilizante e dos NTCPM na matriz PLA. Já a temperatura de cristalização a frio diminuiu e o grau de cristalinidade do PLA aumentou com a adição de PCL nas blendas e dos NTCPM nos nanocompósitos. Diminuições de 35% na dureza elástica e de 29% no módulo de elasticidade foram observadas com a adição do PCL e do compatibilizante Cesa®-mix nas blendas PLA/PCL/AC 2,5%. Com a adição de NTCPM foi observado um aumento de 6,8% na dureza elástica e de 8% no módulo de elasticidade das misturas PLA/NTC com 1,0% m/m. As misturas de PLA/PCL com 0,5% e 1,0% m/m de NTC com e sem compatibilizante, tiveram um decréscimo no módulo de elasticidade e na dureza elástica. Não foram verificadas alterações significativas na resistência elétrica das amostras com a adição do compatibilizante, do PCL e dos NTCPM com 0,5% e 1,0% m/m. A localização seletiva dos NTCPM na fase PCL teve grande influência nas propriedades morfológicas, térmicas, mecânicas e elétricas dos nanocompósitos.

A incorporação e encapsulamento de fertilizantes em blendas poliméricas são métodos que podem ser usados para reduzir perdas e minimizar a poluição ambiental. Neste trabalho, blendas de Proteína Isolada de Soja (SPI) e Poli(ácido lático) (PLA) foram usadas para incorporar o fertilizante NPK (nitrogênio, fósforo e potássio) granular. A influência de concentração dos biopolímeros na mistura foi examinada por Calorimetria exploratória Diferencial (DSC), Análise Termogravimétrica (TGA) e Microscopia Eletrônica de Varredura (SEM). A incorporação efetiva dos nutrientes no solo é dependente do controle da liberação dos mesmos. Porém as aplicações destes nutrientes estão relacionadas aos métodos e às condições do solo. Um método para reduzir perdas de nutrientes é a liberação controlada dos mesmos. Sendo assim, a preparação de blendas baseadas em biopolímeros constituídos de SPI e PLA, para a liberação controlada, se torna viável. SPI e PLA ou SPI, PLA e NPK foram misturados previamente com plastificante e processados através de mistura mecânica, em um misturador de alto torque do tipo Haake , a temperatura de processo foi mantida a 165 ºC durante 5 minutos à velocidade de 90 rpm. Estes parâmetros foram aplicados para todas as blendas. As blendas foram preparadas seguindo a razão SPI/PLA de 1,5, 2,3 e 4,0, usando diferentes porcentagens de plastificante (5 a 16%). Para a mistura que contém NPK o mesmo método foi utilizado. A adição do fertilizante ocorreu após da fusão do PLA. A taxa de liberação dos nutrientes foi calculada pela condutividade do sistema, decorrente da ionização dos sais dos fertilizantes. A concentração dos íons monitorados aumentou com o tempo, evidenciando a liberação dos fertilizantes. Os testes dinâmicos foram realizados sob agitação contínua com 100 mL de água, 1,6 ±0,2g de amostra e 180 horas. A taxa de liberação é uma função da morfologia das blendas e pode ser controlada pela porosidade das mesmas. O uso de blendas como veículo para o fertilizante diminui a liberação deste de forma apreciável (aproximadamente oito vezes) quando comparado ao componente puro. A redução acontece quando a fase amorfa aumenta, esta fase está relacionada à SPI. / Submitted by Marcelo Teixeira (mvteixeira@ucs.br) on 2014-05-29T19:38:04Z No. of bitstreams: 1 Dissertacao Luciane Calabria.pdf: 2695342 bytes, checksum: 30e97111b374f9a53e5091c1e5632c46 (MD5) / Made available in DSpace on 2014-05-29T19:38:05Z (GMT). No. of bitstreams: 1 Dissertacao Luciane Calabria.pdf: 2695342 bytes, checksum: 30e97111b374f9a53e5091c1e5632c46 (MD5) / The incorporation and encapsulation of fertilizers in polymers blends are methods that can be used to reduce losses and to minimize environmental pollution. In this work, blends of Soy Protein Isolate (SPI) and Polylactide Acid (PLA) were used to incorporate the granular fertilizer NPK (nitrogen, phosphorus and potassium). The blends were obtained from mechanical mixture in a Haake´s high shear mixer. The influence of concentration of the biopolymers in the blends, was examined by differential scanning calorimetry (DSC), Thermogravimetric Analysis (TGA) and Scanning Electron Microscopy (SEM). The morphology of the blends can control the diffusion of the fertilizers, also modulating the release. The effective incorporation of the nutrients to the soil is related to the control release control. However, the applications of these nutrients are linked to the methods and the soil conditions. One method for to reduce losses of nutrients is the slow-release. In this way, the preparation of biopolymers blends based in Soy Protein Isolate (SPI) and Polylactide Acid (PLA) for the controlled-release becomes viable. SPI and PLA or SPI, PLA and NPK were previously mixed whit plasticizers and submited to mechanical mixture, in a Haake high shear mixer. The process was performed at 165 ºC for 5 minutes at speed of 90 rpm. These parameters were applied for all blends containing SPI/PLA rate of 1.5, 2.3 and 4.0. For some blends 5 to 15% of plasticizer was added to study its effects. For the blend containing NPK the same method was utilized with addiction of the fertilizer, after the fusion of the PLA. The release rate of nutrients was estimated by the conductivity promoted by the ionization of thefertilizer salts. The ions concentration increase with time due to the release of the fertilizers. The dynamic tests were conducted in a beaker under continuously agitation with 100 mL of water, 1.6 ±0.2g. of sample and 180 hours. The release rate is a function of the blends morphology, and it can be controlled by the porosity. The use of blends as vehicle decreases the release of the fertilizer when compared to the pure component, for about eight times. The relationship increase with the amorphous phase which is related to the SPI.

A incorporação e encapsulamento de fertilizantes em blendas poliméricas são métodos que podem ser usados para reduzir perdas e minimizar a poluição ambiental. Neste trabalho, blendas de Proteína Isolada de Soja (SPI) e Poli(ácido lático) (PLA) foram usadas para incorporar o fertilizante NPK (nitrogênio, fósforo e potássio) granular. A influência de concentração dos biopolímeros na mistura foi examinada por Calorimetria exploratória Diferencial (DSC), Análise Termogravimétrica (TGA) e Microscopia Eletrônica de Varredura (SEM). A incorporação efetiva dos nutrientes no solo é dependente do controle da liberação dos mesmos. Porém as aplicações destes nutrientes estão relacionadas aos métodos e às condições do solo. Um método para reduzir perdas de nutrientes é a liberação controlada dos mesmos. Sendo assim, a preparação de blendas baseadas em biopolímeros constituídos de SPI e PLA, para a liberação controlada, se torna viável. SPI e PLA ou SPI, PLA e NPK foram misturados previamente com plastificante e processados através de mistura mecânica, em um misturador de alto torque do tipo Haake , a temperatura de processo foi mantida a 165 ºC durante 5 minutos à velocidade de 90 rpm. Estes parâmetros foram aplicados para todas as blendas. As blendas foram preparadas seguindo a razão SPI/PLA de 1,5, 2,3 e 4,0, usando diferentes porcentagens de plastificante (5 a 16%). Para a mistura que contém NPK o mesmo método foi utilizado. A adição do fertilizante ocorreu após da fusão do PLA. A taxa de liberação dos nutrientes foi calculada pela condutividade do sistema, decorrente da ionização dos sais dos fertilizantes. A concentração dos íons monitorados aumentou com o tempo, evidenciando a liberação dos fertilizantes. Os testes dinâmicos foram realizados sob agitação contínua com 100 mL de água, 1,6 ±0,2g de amostra e 180 horas. A taxa de liberação é uma função da morfologia das blendas e pode ser controlada pela porosidade das mesmas. O uso de blendas como veículo para o fertilizante diminui a liberação deste de forma apreciável (aproximadamente oito vezes) quando comparado ao componente puro. A redução acontece quando a fase amorfa aumenta, esta fase está relacionada à SPI. / The incorporation and encapsulation of fertilizers in polymers blends are methods that can be used to reduce losses and to minimize environmental pollution. In this work, blends of Soy Protein Isolate (SPI) and Polylactide Acid (PLA) were used to incorporate the granular fertilizer NPK (nitrogen, phosphorus and potassium). The blends were obtained from mechanical mixture in a Haake´s high shear mixer. The influence of concentration of the biopolymers in the blends, was examined by differential scanning calorimetry (DSC), Thermogravimetric Analysis (TGA) and Scanning Electron Microscopy (SEM). The morphology of the blends can control the diffusion of the fertilizers, also modulating the release. The effective incorporation of the nutrients to the soil is related to the control release control. However, the applications of these nutrients are linked to the methods and the soil conditions. One method for to reduce losses of nutrients is the slow-release. In this way, the preparation of biopolymers blends based in Soy Protein Isolate (SPI) and Polylactide Acid (PLA) for the controlled-release becomes viable. SPI and PLA or SPI, PLA and NPK were previously mixed whit plasticizers and submited to mechanical mixture, in a Haake high shear mixer. The process was performed at 165 ºC for 5 minutes at speed of 90 rpm. These parameters were applied for all blends containing SPI/PLA rate of 1.5, 2.3 and 4.0. For some blends 5 to 15% of plasticizer was added to study its effects. For the blend containing NPK the same method was utilized with addiction of the fertilizer, after the fusion of the PLA. The release rate of nutrients was estimated by the conductivity promoted by the ionization of thefertilizer salts. The ions concentration increase with time due to the release of the fertilizers. The dynamic tests were conducted in a beaker under continuously agitation with 100 mL of water, 1.6 ±0.2g. of sample and 180 hours. The release rate is a function of the blends morphology, and it can be controlled by the porosity. The use of blends as vehicle decreases the release of the fertilizer when compared to the pure component, for about eight times. The relationship increase with the amorphous phase which is related to the SPI.

Submitted by Marta Toyoda (1144061@mackenzie.br) on 2018-05-14T18:21:27Z No. of bitstreams: 2 André da Silva Siqueira.pdf: 3776282 bytes, checksum: 6603b366db594cfde0276b33c03a1968 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Approved for entry into archive by Paola Damato (repositorio@mackenzie.br) on 2018-05-21T13:34:35Z (GMT) No. of bitstreams: 2 André da Silva Siqueira.pdf: 3776282 bytes, checksum: 6603b366db594cfde0276b33c03a1968 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2018-05-21T13:34:35Z (GMT). No. of bitstreams: 2 André da Silva Siqueira.pdf: 3776282 bytes, checksum: 6603b366db594cfde0276b33c03a1968 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2018-02-06 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The present work aims to obtain and characterize a composite filament based on poly (lactic acid) (PLA), hydroxyapatite (HA) and graphene oxide, to process it by fused deposition modeling (FDM), and then make scaffolds for bone tissue growth and order to evaluate the properties of the obtained structure. To achieve these goals composite of PLA/HA, PLA/GO and PLA / HA / GO with concentrations of 0.05 wt %, 0.1 wt % and 0.3 wt % GO and 30 wt % HA were obtained by melt state blending and subsequently processed by FDM. The graphite oxide was obtained by modified Hummers method and characterized by X-ray diffraction (XRD), thermogravimetric analysis and Raman spectroscopy. The PLA and composites were characterized by molar mass measurements, infrared and Raman spectroscopy, tensile strength tests, contact angle measurements (surface energy), differential scanning calorimetry (DSC) and rheological tests. The insertion of GO into PLA and PLA/HA composites led to improvements in the mechanical properties (tensile) and also modified significantly the surface properties of the materials and the composition with 0.05 wt % of GO has shown the better results in both characteristics. These improvements occurred due to the strong interaction of the GO sheets with the PLA matrix that indicates the process of obtaining the composites via the melting state was correctly conducted. All PLA / HA / GO compositions presented rheological characteristics compatible with of scaffolds production process via FDM. The insertion of the GO into the PLA matrix and the PLA / HA composite has been shown to be extremely promising, and possibly to increase the variety of PLA / HA based biomaterials application. / O presente trabalho visa obter e caracterizar um filamento compósito baseado em poli(ácido lático) (PLA), hidroxiapatita (HA) e óxido de grafeno, processá-lo por Fused deposition modeling (FDM), fabricar scaffolds para crescimento de tecido ósseo. Para alcançar esses objetivos fcompósitos de PLA/HA, PLA/GO e PLA/HA/GO com concentrações de 0,05%, 0,1% e 0,3% de GO e 30% de HA (em massa) foram preparados por meio de mistura no estado fundido e posteriormente processados por FDM. Comprovou-se a obtenção do óxido de grafite por técnicas de difração de raios-X (DRX), análise termogravimétrica e espectroscopia Raman. O PLA e os compósitos foram caracterizados por medidas de massa molar da matriz polimérica, espectroscopia no infravermelho e Raman, ensaios mecânicos de tração, medidas de ângulos de contato (energia de superfície), calorimetria exploratória diferencial (DSC) e ensaios reológicos. A inserção do GO no PLA e no compósito PLA/HA conduziu a melhorias das propriedades mecânicas (tração) dos materiais e também modificou significativamente as propriedades de superfície dos materiais estudados, sendo a concentração de 0,05% em massa a que apresentou melhor desempenho em ambas as características. Essas melhorias aconteceram devido à forte interação das folhas de GO com a matriz de PLA, o que indica que o processo de obtenção dos compósitos via estado fundido foi corretamente conduzido. Todas as composições PLA/HA/GO apresentaram características reológicas compatíveis com o processo de produção dos scaffolds via FDM. A inserção do GO na matriz de PLA e no compósito PLA/HA demonstrou-se ser extremamente promissora, e possivelmente aumentarão a variedade de aplicações dos biomateriais baseados em PLA/HA.

Submitted by Johnny Rodrigues (johnnyrodrigues@ufcg.edu.br) on 2018-04-06T20:12:23Z No. of bitstreams: 1 TACIANA REGINA DE GOUVEIA - TESE PPG-CEMat 2014..pdf: 4953603 bytes, checksum: ea581c261908041111cd0d411a551545 (MD5) / Made available in DSpace on 2018-04-06T20:12:23Z (GMT). No. of bitstreams: 1 TACIANA REGINA DE GOUVEIA - TESE PPG-CEMat 2014..pdf: 4953603 bytes, checksum: ea581c261908041111cd0d411a551545 (MD5) Previous issue date: 2014-08-28 / Capes / Os polímeros derivados do petróleo têm provocado impactos ambientais devido ao descarte inadequado. Uma alternativa para esse problema é a utilização de polímeros biodegradáveis ou a produção de blendas a partir destes polímeros. Neste trabalho, foram preparadas blendas de poli (ácido lático) - PLA, poli (caprolactona) - PCL, com três copolímeros diferentes: EMA, E-GMA e o EMAGMA que são copolímeros de etileno-acrilato de metila, etileno-metacrilato de glicidila e o terpolímero etileno-acrilato de metila-metacrilato de glicidila, respectivamente. As composições utilizadas para as blendas foram as seguintes: PLA/PCL (90/10), PLA/PCL (80/20), PLA/Copolímeros (90/10) e PLA/PCL/Copolímeros (80/10/10). Estas foram preparadas por fusão em uma extrusora de rosca dupla corrotativa e, em seguida, moldadas por injeção sob a forma de corpos de prova de tração, impacto e HDT. Todas as composições foram caracterizadas por: ensaios mecânicos de tração e impacto, temperatura de distorção térmica - HDT, calorimetria exploratória diferencial - DSC, difração de raios X - DRX, análise térmica dinâmica-mecânica - DMTA, espectroscopia na região do infravermelho por transformada de Fourier - FTIR, microscopia eletrônica de varredura - MEV, reometria de torque, ensaio reológico e reometria capilar. As propriedades mecânicas apresentaram redução nos valores do módulo e da resistência à tração e um aumento no alongamento e na resistência ao impacto para todas as composições quando comparadas com o PLA puro, com destaque para as composições que continham o copolímero EMA-GMA. A HDT não apresentou mudanças significativas para as diferentes composições em comparação com o PLA puro. O comportamento térmico e termomecânico foi avaliado por DSC e por DMTA e foi possível observar a transição térmica das blendas. Por DRX foi possível observar as fases cristalinas das blendas de PLA. A morfologia da superfície de fratura observada por MEV ilustrou que ocorreram mudanças significativas em função da composição. Os resultados de reometria de torque não apresentaram mudanças significativas no comportamento do PLA, enquanto que os resultados obtidos no ensaio reológico ilustraram aumento no módulo de armazenamento em todas as composições. A partir do ensaio de reometria capilar foi visto que houve redução da viscosidade aparente e da tensão de cisalhamento sob altas taxas de cisalhamento para todas as composições. / The polymers derived from petroleum have caused environmental impacts due to improper disposal. An alternative to this problem is the use of biodegradable polymers or blends production from these polymers. In this work, blends of poly (lactic acid) - PLA, poly (-caprolactone) - PCL, were prepared with three different copolymers: EMA, E-GMA and EMA-GMA are copolymers the ethylene-methyl acrylate, ethylene-glycidyl methacrylate and terpolymer ethylene-methyl acrylate-glycidyl methacrylate respectively. The compositions used in the blends were as follows: PLA/PCL (90/10) PLA/PCL (80/20) PLA/ Copolymer (90/10) and PLA/PCL/Copolymer (80/10/10). These were prepared by melting in an extruder twin screw co-rotating and then injection molded in the form of specimens tensile, impact and HDT. All compositions were characterized by: mechanical tensile and impact , heat distortion temperature - HDT, differential scanning calorimetry - DSC, X-ray diffraction - XRD, dynamic mechanical thermal analysis – DMTA, spectroscopy in the infrared region by transform Fourier - FTIR, scanning electron microscopy - SEM, torque rheometer, rheological testing and capillary rheometer. The mechanical properties showed reduced values of modulus and tensile strength and an increase in elongation and impact resistance for all compositions when compared with pure PLA, especially for compositions containing copolymer EMA-GMA. The HDT showed no significant changes for the different compositions compared with pure PLA. The thermal and thermomechanical behavior was evaluated by DSC and DMTA and it was possible to observe the thermal transition of the blends. XRD was possible to observe the crystalline phases of the blends of PLA. The morphology of the fracture surface was observed by SEM illustrated that significant changes as a function of composition. The torque rheometer results showed no significant change in the behavior of PLA, while the rheological test results illustrate the increase in storage modulus in all compositions. From the test capillary rheometer was seen that there was a reduction in the apparent viscosity and shear stress at high shear rates for all compositions.