Objective: This study aimed to assess the impact of in vitro erosion provoked by different cola-based drinks (Coke types), associated or not with toothbrushing, to bonding to enamel. Material and methods: Forty-six bovine enamel specimens were prepared and randomly assigned into seven groups (N=8): C- Control (neither eroded nor abraded), ERO-RC: 3x/1-minute immersion in Regular Coke (RC), ERO-LC: 3x/1-minute immersion in Light Coke (LC), ERO-ZC: 3x/1-minute immersion in Zero Coke (ZC) and three other eroded groups, subsequently abraded for 1-minute toothbrushing (EROAB-RC, EROAB-LC and EROAB-ZC, respectively). After challenges, they were stored overnight in artificial saliva for a total of 24 hours and restored with Adper Single Bond 2/Filtek Z350. Buildup coronal surfaces were cut in 1 mm2-specimens and subjected to a microtensile test. Data were statistically analyzed by two-way ANOVA/Bonferroni tests (a=0.05). Failure modes were assessed by optical microscopy (X40). The Interface of the restorations were observed using Confocal Laser Scanning Microscopy (CLSM). Results: All tested cola-based drinks significantly reduced the bond strength, which was also observed in the analyses of interfaces. Toothbrushing did not have any impact on the bond strength. CLSM showed that except for Zero Coke, all eroded specimens resulted in irregular hybrid layer formation. Conclusions: All cola-based drinks reduced the bond strength. Different patterns of hybrid layers were obtained revealing their impact, except for ZC. / This study was supported in part by grants given by the São Paulo Research Foundation (FAPESP), Process no. 2009/14986-0, and the National Council for Scientific and Technological Development (CNPq), Process no. 480038/2007-4. In Addition, this study was performed by V.D.M. and A.C.H. as fulfillment of their graduation research, which was supported by FAPESP (Processes no. 2009/01376-9 and 2009/01377-5, respectively). The authors are also grateful to Oral B and SDI, which donated the materials used in the study. / Revisión por pares

This study evaluated the impact of orange juice on the bond strength (BS) of dentin bonding systems (DBSs) to enamel surface after simulation with an in situ/ ex vivo erosive cycling. One hundred and ninety two bovine enamel fragments (4x4x2 mm) were obtained and randomized regarding superficial microhardness and distributed to palatal devices for 8 volunteers, in three phases (one for each DBS), containing 8 blocks, which were, allocated in 4 pairs. Daily, these pairs were subjected extraorally to the following conditions: CONTneither erosive nor abrasive challenge; ERO- erosive challenge only; ABR- abrasive challenge only and ERO + ABR- with erosive and abrasive challenges. Erosive cycles (immersion in orange juice, 3 times/day/5 min/5 days) or/and abrasive challenges (electric toothbrush, 3 times/day/1 min/5 days) were performed. After these cycles, all specimens were restored with the adhesive systems Adper Scotchbond Multi Purpose (MP), Adper Single Bond 2 (SB) or Clearfil SE Bond (SE), and the composite resin Filtek Z250. After 7 days, sticks (area ≅1 mm2) were obtained and subjected to the microtensile bond strength test (μTBS) at 0.5 mm/min. Data was statistically analyzed by ANOVA and Tukey tests (a=0.05). Failure modes were determined using a digital microscope (40×). DBS was the only statistical significant factor. SE was the unique DBS not affected in any challenge, whereas MP and SB performed according to the scenario. The adhesive and mixed failures were predominant in all groups. Overall performance suggested that BS to enamel after erosive /abrasive challenged by orange juice was not affected and it was material-dependent

Este projeto teve como objetivos investigar o efeito do íon ferro (Fe+2), associado ou não ao íon flúor (F-), na redução da erosão do esmalte e da dentina bovinos, bem como desenvolver e avaliar um dentifrício enriquecido com Fe+2 para a prevenção da erosão associada à abrasão. Foram realizados 4 subprojetos: (1) Determinação do efeito protetor de concentrações crescentes do Fe+2 (0 a 120 mmol/L) associadas ou não ao F- (0 a 4 g/mL), contra a dissolução do pó de esmalte bovino in vitro; (2) Avaliação, in vitro, do efeito protetor do Fe+2 a 10 mmol/L contra a dissolução mineral da superfície do esmalte bovino; (3) Desenvolvimento e avaliação, in vitro, de dentifrícios fluoretados enriquecidos com diferentes concentrações de Fe+2, visando à prevenção da perda mineral do esmalte bovino; (4) Avaliação, in situ, do efeito inibidor do dentifrício acrescido de Fe+2 e F- na desmineralização do esmalte e dentina bovinos sadios ou previamente erodidos. As variáveis de resposta utilizadas foram a quantificação da perda de fósforo (colorimetria) e o desgaste (perfilometria, m) para os subprojetos 1 e 2, e 3 e 4, respectivamente. Os dados foram submetidos à análise estatística (p<0,05). Para o Subprojeto (1), a ANOVA a 2 critérios e o teste de Bonferroni revelaram que soluções contendo Fe+2 a 1,25, 2,5, 5,0, 10, 15 e 30 mmol/L reduziram significativamente a dissolução do pó de esmalte bovino em 18, 18, 23, 35, 35 e 55%, respectivamente, em comparação ao controle (sem Fe+2). Na presença de F-, o efeito do Fe+2 na inibição da dissolução do esmalte foi reduzido, não havendo efeito sinérgico entre estes íons nas condições testadas. No Subprojeto (2), a ANOVA a 2 critérios e o teste de Bonferroni, mostraram uma redução significativa na desmineralização da superfície do esmalte bovino em torno de 30 a 40%, quando se utilizou solução de Fe+2 a 10 mmol/L. No Subprojeto (3), a ANOVA revelou diferença significativa entre os grupos (Placebo, 1100 g/mL de F-, Crest®, Fe+2 1,0 mg/g, Fe+2 2,5 mg/g, Fe+2 5,0 mg/g, F- (1100 g/mL) + Fe+2 1,0 mg/g, F- (1100 g/mL) + Fe+2 2,5 mg/g e F- (1100 g/mL) + Fe+2 5,0 mg/g) (F=4,734, p<0,0001). O menor desgaste (0,48±0,24 m) foi apresentado pelo grupo em que foi utilizado o dentifrício contendo 1100 g/mL F- e 5 mg/g Fe+2. No Subprojeto (4), para o esmalte hígido a ANOVA a 2 critérios revelou uma diferença significativa entre os dentifrícios, (F=21,72, p<0,0001), mas não entre as condições (só erosão, erosão + slurry, erosão + abrasão) (F=1,20, p=0,32) e nem para a interação entre ambos (F = 1,04, p=0,41). O teste de Bonferroni revelou que os blocos que receberam o dentifrício contendo Fe+2 e F- apresentaram valores de desgaste significativamente menores quando comparados aos blocos submetidos aos demais dentifrícios, os quais não diferiram significativamente entre si. Para a dentina hígida, o esmalte previamente erodido e a dentina previamente erodida, o mesmo padrão foi seguido, apesar destes dois últimos terem apresentado valores de desgaste maiores que aqueles observados para os blocos hígidos. / The aims of this study were to investigate the effect of iron (Fe+2) associated or not to fluoride (F-) on the reduction of bovine enamel and dentin erosion, as well as to develop and evaluate a dentifrice containing Fe+2 to prevent erosion associated to abrasion. Four subprojects were done: (1) In vitro determination of the protective effect of increasing Fe+2 concentrations (0 to 120 mmol/L) associated or not to F- (0 to 4 g/mL) against the dissolution of powdered enamel; (2) In vitro evaluation of the protective effect of 10 mol/L Fe+2 against the mineral dissolution of superficial bovine enamel; (3) Development and in vitro evaluation of fluorided dentifrices containing different Fe+2 concentrations in order to prevent the mineral loss of bovine enamel; and (4) In situ evaluation of the effect of a dentifrice containing Fe+2 and F- on the demineralization of sound or previously eroded bovine enamel and dentin. The response variables were quantification of phosphate loss (colorimetry) and tooth wear (perfilometry, m) for the subprojects 1 and 2, and 3 and 4, respectively. Data were submitted to statistical analyses (p <0.05). In subproject (1), two-way ANOVA and Bonferronis test revealed that solutions containing 1.25, 2.5, 5.0, 10.0, 15.0 and 30.0 mmol/L Fe+2 significantly reduced the dissolution of powdered enamel at 18, 18, 23, 35, 35 and 55%, respectively, in comparison to control (without Fe+2). In the presence of F-, the effect of Fe+2 on the dissolution of enamel was reduced and no synergistic effect between these ions was observed in the tested conditions. In Subproject (2), two-way ANOVA and Bonferronis test showed a significant reduction on surface demineralization of bovine enamel (around 30-40%), when the solution containing Fe+2 at 10 mmol/L was used. In Subproject (3), ANOVA revealed a significant difference among the groups (Placebo, 1,100 g/mL F, Crest®, 1.0 mg/g Fe+2, 2.5 mg/g Fe+2, 5.0 mg/g Fe+2, F- (1, 100 g/mL) + 1,0 mg/g Fe+2, F- (1100 g/mL) + 2,5 mg/g Fe+2 and F- (1,100 g/mL) + 5,0 mg/g Fe+2) (F=4,734, p<0,0001). The lowest wear (0.48±0.24 m) was observed when the dentifrice containing F + Fe was used. In Subproject (4), for sound enamel, two-way ANOVA revealed a significant difference among the dentifrices, (F=21.72, p<0.0001), but not among the conditions (erosion only, erosion + slurry, erosion + abrasion) (F=1.20, p=0.32) or for the interaction of both (F = 1.04, p=0.41). The Bonferronis test revealed that the blocks which received the dentifrice containing Fe+2 and F- presented significantly lesser wear when compared to the blocks submitted to the other dentifrices, which did not differ significantly among each other. As for sound dentin as well as for previously eroded enamel and dentin, the same pattern was obtained but the latter two presented wear values higher than those seen for the sound blocks.

Embora haja grande exigência por restaurações estéticas livres de metal, restaurações metalocerâmicas, cujas subestruturas feitas com ligas de metais básicos, são procedimentos de rotina nos planejamentos restauradores protéticos. No entanto, a alta resistência ao desgaste destas ligas, caracterizada pela grande dificuldade de acabamento e polimento, tem sido associada à dureza, geralmente elevada. A proposta deste estudo foi avaliar resistência à abrasão e dureza de seis ligas de metais básicos (4 ligas de Ni-Cr, 1 liga de Co-Cr e 1 Ti comercialmente puro – 99,5% Ti) disponíveis comercialmente para uso com cerâmica. A resistência à abrasão foi determinada pela perda de peso dos corpos-de-prova, ao longo de 4 séries de ciclos de abrasão. A dureza Rockwell 30N também foi avaliada nos mesmos intervalos. Os dados foram analisados com o nível de significância a = 0,05. O teste de regressão e correlação da resistência à abrasão e dureza mostrou que para 3 ligas de Ni-Cr (Vera Bond, Vera Bond II e Wiron 99) a linha de regressão foi descendente, indicando que um aumento na dureza correspondeu a uma redução nos valores de perda de peso, enquanto para 1 liga de Ni-Cr (Neochrom) a linha de regressão foi ascendente, indicando um aumento nos valores de perda de peso, apesar de um aumento na dureza. Por outro lado, para a ligas de Co-Cr (New Ceram) e de titânio (Rematitan), os valores de perda de peso se mantiveram constantes. As ligas avaliadas tiveram baixos coeficientes de correlação entre resistência à abrasão e dureza. A análise metalográfica revelou particularidades que podem ter sido determinantes para as taxas de desgaste de cada material. Com exceção da liga de titânio, não houve mudanças metalográficas das ligas avaliadas, durante as séries de ciclos de abrasão. / In spite of the demand for metal free restorations, metal ceramic restorations using base metal alloys are routine in prosthodontics. Nevertheless, the high abrasion resistance of base metal alloys, characterized by difficulty in finishing and polishing, has been related to excessive hardness. The purpose of this study was to evaluate abrasion resistance and hardness of six base metal alloys (4 Ni-Cr alloys, 1 Co-Cr alloy and 1 commercially pure Ti alloy – 99.5% Ti) available commercially for use with fused porcelain. Abrasion resistance was determined by specimen weight loss along 4 series of abrasion cycles. The Rockwell 30N hardness was also determined in the same periods. Data were analyzed statistically with the level of significance set at a = 0.05. Regression and correlation analysis of abrasion resistance and hardness showed that for three Ni-Cr alloys (Vera Bond, Vera Bond II and Wiron 99) the regression lines descended indicating that an increase in hardness corresponded to a reduction in weight loss, whereas for one Ni-Cr alloy (Neochrom) the regression line ascended indicating an increase in weight loss in spite of an increase in hardness. On the other hand, for the Co-Cr alloy (New Ceram) and Ti (Rematitan), the weight loss remained constant. The alloys tested had low correlation coefficients between abrasion resistance and hardness. Microscopic analysis showed details that may have been determining for the weight loss rate of each material. With the exception of the titanium alloy, there were no metallographic changes of the alloys tested during the abrasion tests.

O presente estudo, composto por 2 experimentos in situ, buscou avaliar o efeito da irradiação com laser de CO2 no controle da progressão de lesões de erosão e, posteriormente, analisar a influência da abrasão em superfícies irradiadas e erodidas. No primeiro experimento, 56 fragmentos de incisivos bovinos (5x3x2.5mm) tiveram suas superfícies de esmalte divididas em 4 áreas: 1. Hígida (área de referência); 2. Erosão inicial; 3. Tratamento (irradiado ou não com laser de CO2); 4. Após fase in situ. O desafio erosivo inicial foi realizado com ácido cítrico 1% (pH=2,3) por 5 minutos, 2x/dia, por 2 dias. Os espécimes foram divididos em 2 grupos de acordo com o tratamento da superfície: irradiados com laser de CO2 ( &lambda;= 10,6 m; 0,5 W) e não irradiados. Após um período de lead-in de 2 dias, 14 voluntários usaram um dispositivo intraoral palatino contendo 2 espécimes (irradiado e não irradiado), em 2 fases intraorais de 5 dias cada. Seguindo um desenho cross-over, durante a primeira fase, metade dos voluntários imergiu seu dispositivo em 100mL de ácido cítrico por 5 minutos, 3x/dia, enquanto a outra metade usou água deionizada (controle). Os voluntários foram cruzados quanto aos desafios na segunda fase. O desgaste do esmalte foi determinado quantitativamente por um perfilômetro óptico e a morfologia da superfície do esmalte foi avaliada qualitativamente por microscopia eletrônica de varredura. ANOVA a três critérios para medidas repetidas mostrou que não houve interação significativa entre desafio erosivo e irradiação com laser de CO2 (p=0,419). O desafio erosivo aumentou significativamente o desgaste do esmalte (p=0,001), independente de ter sido realizada ou não a irradiação com laser de CO2. Não houve diferença no desgaste do esmalte entre os espécimes irradiados e não irradiados (p=0,513). No segundo experimento, o preparo e seleção dos espécimes de esmalte bovino, a indução das lesões de erosão iniciais e os tratamentos foram realizados como no primeiro experimento. Após um período de 2 dias de lead-in, 12 voluntários usaram um dispositivo palatino contendo dois espécimes irradiados e dois não irradiados, em duas fases intraorais de 5 dias cada. Seguindo um protocolo split-mouth, os voluntários imergiram extraoralmente, durante 5 minutos, os dispositivos em ácido cítrico 3x/dia por 5 dias. Uma hora após cada desafio erosivo, um espécime irradiado e um não irradiado foram escovados usando uma escova elétrica e slurry de dentifrício. As variáveis de resposta foram as mesmas empregadas no primeiro experimento. ANOVA a dois critérios revelou que não houve interação significativa entre desafio erosivo-abrasivo e irradiação com laser de CO2 (p=0,614). A irradiação laser não influenciou no desgaste do esmalte (p=0,742). O desgaste do esmalte dos espécimes submetidos a erosão + abrasão não foi diferente daquele verificado quando a erosão foi realizada sozinha (p=0,626), independente do laser de CO2 ter sido aplicado ou não. Pode-se concluir que, em condições intraorais, a irradiação com laser de CO2 não controlou a progressão de lesões de erosão nem de lesões de erosivo-abrasivas no esmalte. / This study, composed of 2 in situ experiments, aimed to evaluate the effect of CO2 laser irradiation to control the progression of erosive lesions and, after, analyze the influence of abrasion on irradiated and eroded surfaces. At the first experiment, 56 slabs of bovine incisors (5x3x2.5mm) had its enamel surface divided in 4 areas: 1. Sound (reference area); 2. Initial erosion; 3. Treatment (irradiated or not with CO2 laser); 4. After in situ phase. The erosive challenge was performed with 1% citric acid (pH 2.3), during 5 minutes, 2x/day, for 2 days. The specimens were divided in 2 groups according to the surface treatment: CO2 laser irradiated (&lambda; = 10.6 m; 0.5 W) and non-irradiated. After a 2-day-lead-in period, 14 volunteers wore an intraoral palatal device containing 2 specimens (irradiated and non-irradiated), in 2 intraoral phases of 5 days each. Following a crossover design, during the first phase, half of the volunteers immersed its device on 100mL of citric acid during 5 minutes, 3x/day, while the other half immersed on deionized water (control). Volunteers were crossed on the challenges on the second phase. The enamel wear was quantitatively determined by an optical profilometer and the morphology of enamel surface was qualitatively evaluated by scanning electron microscopy. Three-way ANOVA for repeated measures showed that there was no significant interaction between erosive challenge and CO2 laser irradiation (p=0.419). The erosive challenge significantly increased the enamel wear (p=0.001), regardless of irradiated or not with CO2 laser. There was no difference on the enamel wear of irradiated and non-irradiated specimens (p=0.513). At the second experiment, preparation and selection of bovine enamel specimens, induction of initial erosive lesion and treatments were performed as already described for the first experiment. After a 2-day-lead-in period, 12 volunteers wore and intraoral palatal device containing 2 irradiated and 2 non-irradiated specimens, at two intraoral phases of 5 days each. Following a split-mouth protocol, volunteers immersed the devices extra orally, during 5 minutes, in 1% citric acid, 3x/day for 5 days. One hour after each erosive challenge, one irradiated and one non-irradiated specimen were brushed with an electrical toothbrush and dentifrice slurry. The response variables were the same studied at the first experiment. Two-way ANOVA revealed that there was no significant interaction between erosive-abrasive challenge and CO2 laser irradiation (p=0.614). The laser irradiation did not influence on the enamel wear (p=0.742). The enamel wear presented by the specimens subjected to erosion + abrasion did not differ from that verified when the erosion was performed alone. It can be concluded that, in intraoral conditions, the CO2 laser irradiation did not controlled the progression of erosive lesions or erosive-abrasive lesions on enamel

Orientador: Renata Garcia Fonseca / Resumo: Pouco se sabe sobre o efeito do jateamento pré-sinterização da zircônia na sua resistência mecânica, sob condições de envelhecimento. Este estudo avaliou a influência do tamanho da partícula, do momento do jateamento e do envelhecimento na resistência mecânica de uma zircônia estabilizada por ítria. Quatrocentos discos de uma zircônia estabilizada por ítria pré-sinterizados foram alocados como segue: sem jateamento; jateamento com partículas de óxido de alumínio (Al2O3) de 50 µm ou 120 µm antes (50/PRÉ ou 120/PRÉ) ou após (50/PÓS ou 120/PÓS) sua sinterização. Os discos foram não envelhecidos (24h) ou envelhecidos por: ciclagem mecânica (CM); envelhecimento hidrotérmico (EH) ou CM+EH, totalizando 20 grupos (n=20). Os espécimes foram submetidos ao teste de resistência à flexão biaxial (RFB) e, posteriormente, foram analisados fractograficamente. A análise de difração de raios-X (DRX) foi realizada em determinadas condições para caracterizar cristalograficamente o efeito do jateamento na zircônia. Os dados de RFB (MPa) foram analisados por ANOVA a 3 fatores e pós teste de Games Howell (α=0,05). Também foi realizada análise de Weibull. A RFB e a resistência característica (σ0) dos grupos 120/PÓS, envelhecidos ou não, foram significativamente maiores que as dos demais grupos jateados, e estatisticamente similares ou maiores que as dos respectivos grupos sem jateamento. Em contrapartida, o grupo 120/PRÉ/não envelhecido e todos os grupos 50/PRÉ apresentaram os menores valores. Em to... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Little is known about the effect of air-abrasion before zirconia sintering on its strength, under aging challenge. This study aimed to verify the influence of the airabrasion moment (before or after zirconia sintering), particle size (50 or 120 µm) and aging on the mechanical strength of a Y-TZP ceramic. Four hundred pre-sintered zirconia discs were allocated as follows: non-air-abraded; air-abraded with 50 µm or 120 µm Al2O3 particles before (50/BS or 120/BS) or after sintering (50/AS or 120/AS). The discs were non-aged (24h) or aged by: mechanical cycling (MC); hydrothermal aging (HA) or by both methods (MC+HA), totaling 20 groups (n=20). Specimens were subjected to biaxial flexural strength test (BFS). Fractographic analysis was performed to identify the fracture origin. The X-ray diffraction analysis (XRD) was performed under certain conditions to characterize the crystallographic effect of airabrasion on the zirconia. The BFS data (MPa) were analyzed by ANOVA and Games Howell post hoc test (α=.05). Weibull statistics was also applied. The BFS and the characteristic resistance (σ0) of the 120/AS groups, aged or not, were significantly higher than those of the other air-abraded groups, and statistically similar or higher than the respective groups without air-abrasion. In contrast, the 120/BS/non-aged group and all those 50/BS presented the lowest values. In all groups, the initial defect had its origin on the tensile stress side. Neither air-abrasion nor aging (except for 50/AS/MC+HA) reduced the zirconia reliability compared with the respective controls. Air-abrasion promotes an increase in the monoclinic phase content, while sintering zeroed this phase. Air-abrasion before zirconia sintering yields worse performance for BFS than after sintering, under aging challenges. The BFS and σ0 were strongly determined by the particle size and air-abrasion moment / Doutor

As aderências intra-abdominais são complicações relativamente comuns das cirurgias abdominais dos equinos após uma intervenção cirúrgica, podendo resultar em processos obstrutivos, dor abdominal recorrente e vôlvulos. Os avanços técnicos e farmacológicos são direcionados a minimizar o trauma e a inflamação peritoneal, aumentar o processo de fibrinólise, promover movimentação intestinal e separar tecidos potencialmente adesiogênicos durante a fase inicial de cicatrização. No presente trabalho foram utilizados 10 equinos, machos, SRD, entre 4 e 15 anos e peso entre 300 e 400kg. Incluíram-se no experimento os animais que não apresentaram alterações no exame físico e laboratorial, prévios. A membrana biológica utilizada era proveniente do banco de membranas biológicas do HOVET da FMVZ-USP. O protocolo anestésico consistiu de sedação com associação de xilazina 10% (0,7mg/kg) e tartarato de butorfanol (0,04mg/kg). A laparotomia foi realizada pelo flanco esquerdo com os animais em posição quadrupedal. No ponto médio de sua exteriorização (flexura pélvica) foi induzida lesão por abrasão em superfície serosa, com dimensão de 7x7 cm. Após a indução das lesões, nos animais do grupo 1 (cinco animais), a área lesionada foi recoberta com membrana biológica. Nos animais do grupo 2 (cinco animais), o segmento intestinal exteriorizado, após a criação das lesões, foi lavado com solução fisiológica e reposicionado na cavidade abdominal. Em ambos os grupos foi realizada a sutura de um ponto simples no centro da lesão utilizando-se fio de nylon 2-0, com o objetivo de referendar a lesão criada. As suturas dos planos musculares e subcutâneo foram realizadas com sutura contínua com fio absorvível Poliglactina 910 n0 2 e n0 00 respectivamente, e a pele foi suturada de maneira contínua utilizando-se nylon n0 0. A avaliação pós-operatória consistiu de avaliação física diária e coleta de material para análise laboratorial (sangue, soro e líquido peritoneal) semanalmente, durante quatro semanas. Decorridos 30 dias após o procedimento cirúrgico, os animais foram submetidos à nova laparotomia a fim de verificar a presença de aderências intra-abdominais, aspecto macroscópico das lesões e do implante, e realização de biópsia intestinal. A coleta do material para a realização dos exames laboratoriais foi realizada nos momentos: M0- período pré-operatório imediato, M7- 7 dias de pós-operatório, M14- 14 dias de pós-operatório, M21- 21 dias de pós-operatório, M28- 28 dias de pós-operatório. A laparotomia realizada em posição mais ventral e seguindo a técnica de grade possibilitou menor trauma cirúrgico, mas esta abordagem ofereceu ao cirurgião menor campo operatório, determinando alguma dificuldade de exteriorização do segmento intestinal. A evolução clínica dos animais foi satisfatória apresentando vantagem quando comparada a citação da literatura. Durante a reavaliação cirúrgica verificou-se presença de tecido cicatricial fibroso entre os planos musculares que determinou pequena dificuldade para o acesso da cavidade abdominal. Não foram observadas aderências intra-abdominais em ambos os grupos. O aspecto macroscópico das lesões no grupo experimental caracterizou-se por extensa área de hiperemia com cobertura de tecido seroso; e no grupo controle, verificou-se pequeno tecido cicatricial recobrindo o material de sutura. A realização das biópsias intestinais foi executada com facilidade bem como sua sutura. A avaliação histológica demonstrou em ambos os grupos intensa infiltração eosinofílica, presença de colágeno em fase de maturação além de evidências de intensa neovascularização. A partir da análise dos valores laboratoriais observaram-se diferenças estatísticas significativas nos valores sanguíneos de bilirrubinas, hematócrito, monócito, uréia; e no líquido peritoneal estas diferenças foram manifestadas em proteína, densidade e número de leucócitos segmentados. Conclui-se que a abrasão focal de serosa de cólon maior como único fator promotor de aderências intra-abdominais fibrosas foi insuficiente. Além disso, a utilização de pericárdio equino como proteção de áreas de lesão intestinal, mesmo não tendo sido comprovada sua eficácia na minimização das aderências intra-abdominais, apresenta-se viável e possível, pois não foram observadas diferenças estatisticamente significativas (hematológicas, bioquímicas ou do líquido peritoneal) na comparação entre os grupos, ou alterações que determinasse efeitos deletérios aos animais. / The intra-abdominal adhesions are relatively common complications of abdominal surgery in horses and they can result in obstructive processes, abdominal pain and recurrent volvulus. The technical and pharmacological advances are aimed to minimize trauma and peritoneal inflammation, increase the fibrinolysis process, promote intestinal peristalsis and separate potentially adhesiogenic tissues during the initial phase of healing. In this study were used 10 horses, male, mixed breed, between 4 and 15 years old and weighing between 300 and 400kg. The experiment included animals that showed no changes in physical and laboratorial examination. The biological membrane was from the bank of biological membranes of the HOVET-FMVZ-USP. The anesthetic protocol consisted of sedation with a combination of ketamine 10% (0.7 mg / kg) and butorphanol (0.04 mg / kg). The laparotomy was performed by the left flank and the animal was kept in standing position. At the midpoint of the pelvic flexure was induced the injury by abrasion in serous surface, with a size of 7x7 cm. After the lesion induction, the group 1 (five animals) had the injured area covered with a biological membrane. The group 2 (five animals) had the intestinal segment exteriorized, and after the lesion creation it was washed with saline and repositioned in the abdominal cavity. In both groups was performed suturing a single point in the center of the lesion using 2-0 nylon, in order to endorse the lesion created. The sutures of the muscle layers and subcutaneous tissue were performed with continuous suture with Polyglactin 910 n0 2 and n0 00 respectively, and the skin was sutured continuously using nylon n0 0. The postoperative evaluation consisted of daily physical assessment and collection of material for laboratory analysis (blood, serum and peritoneal fluid) weekly for four weeks. After 30 days, the animals underwent another laparotomy to verify the presence of intra-abdominal adhesions, macroscopic aspect of the lesions and implant, and intestinal biopsy. The collection of material for the completion of laboratory tests was performed at moments M0- pre-operative, M7- 7 days post-operatively, M14- 14 days post-operatively, M21- 21 days post-operatively, M28- 28 days post-operatively. The laparotomy was performed in ventral position following the technique of grid that´s promoted less surgical trauma, but this approach offered to surgeon less surgical field, causing some difficulty for exteriorization of the intestinal segment. The clinical outcome was satisfactory showing advantage when compared literature. During the surgical reassessment verified the presence of fibrous scar tissue between the muscle layers that determined some trouble to access the abdominal cavity. There were no intra-abdominal adhesions in both groups. The macroscopic aspect of lesions in the experimental group was characterized by extensive area of redness covered serous tissue, and the control group there was little scar tissue overlying the suture material. The intestinal biopsies and suture were performed easily. The histological evaluation showed in both groups intense eosinophilic infiltration, presence of collagen in the maturation stage in addition to evidence of intense neovascularization. The laboratory results showed statistically significant differences in blood levels of bilirubin, hematocrit, monocyte, urea, and into peritoneal fluid, these differences were manifested in protein density and leukocytes. Concluded that the focal serosal abrasion of the large colon as the single factor promoting intra-abdominal fibrous adhesions was insufficient. Furthermore, the use of equine pericardium as protecting areas of intestinal injury, even without prove their effectiveness in minimizing intra-abdominal adhesions, it appears feasible and possible, because there were no statistically difference (hematological, biochemical or peritoneal fluid) between the groups, or changes that would determine deleterious effects to the animals.

As aderências intra-abdominais são complicações relativamente comuns das cirurgias abdominais dos equinos após uma intervenção cirúrgica, podendo resultar em processos obstrutivos, dor abdominal recorrente e vôlvulos. Os avanços técnicos e farmacológicos são direcionados a minimizar o trauma e a inflamação peritoneal, aumentar o processo de fibrinólise, promover movimentação intestinal e separar tecidos potencialmente adesiogênicos durante a fase inicial de cicatrização. No presente trabalho foram utilizados 10 equinos, machos, SRD, entre 4 e 15 anos e peso entre 300 e 400kg. Incluíram-se no experimento os animais que não apresentaram alterações no exame físico e laboratorial, prévios. A membrana biológica utilizada era proveniente do banco de membranas biológicas do HOVET da FMVZ-USP. O protocolo anestésico consistiu de sedação com associação de xilazina 10% (0,7mg/kg) e tartarato de butorfanol (0,04mg/kg). A laparotomia foi realizada pelo flanco esquerdo com os animais em posição quadrupedal. No ponto médio de sua exteriorização (flexura pélvica) foi induzida lesão por abrasão em superfície serosa, com dimensão de 7x7 cm. Após a indução das lesões, nos animais do grupo 1 (cinco animais), a área lesionada foi recoberta com membrana biológica. Nos animais do grupo 2 (cinco animais), o segmento intestinal exteriorizado, após a criação das lesões, foi lavado com solução fisiológica e reposicionado na cavidade abdominal. Em ambos os grupos foi realizada a sutura de um ponto simples no centro da lesão utilizando-se fio de nylon 2-0, com o objetivo de referendar a lesão criada. As suturas dos planos musculares e subcutâneo foram realizadas com sutura contínua com fio absorvível Poliglactina 910 n0 2 e n0 00 respectivamente, e a pele foi suturada de maneira contínua utilizando-se nylon n0 0. A avaliação pós-operatória consistiu de avaliação física diária e coleta de material para análise laboratorial (sangue, soro e líquido peritoneal) semanalmente, durante quatro semanas. Decorridos 30 dias após o procedimento cirúrgico, os animais foram submetidos à nova laparotomia a fim de verificar a presença de aderências intra-abdominais, aspecto macroscópico das lesões e do implante, e realização de biópsia intestinal. A coleta do material para a realização dos exames laboratoriais foi realizada nos momentos: M0- período pré-operatório imediato, M7- 7 dias de pós-operatório, M14- 14 dias de pós-operatório, M21- 21 dias de pós-operatório, M28- 28 dias de pós-operatório. A laparotomia realizada em posição mais ventral e seguindo a técnica de grade possibilitou menor trauma cirúrgico, mas esta abordagem ofereceu ao cirurgião menor campo operatório, determinando alguma dificuldade de exteriorização do segmento intestinal. A evolução clínica dos animais foi satisfatória apresentando vantagem quando comparada a citação da literatura. Durante a reavaliação cirúrgica verificou-se presença de tecido cicatricial fibroso entre os planos musculares que determinou pequena dificuldade para o acesso da cavidade abdominal. Não foram observadas aderências intra-abdominais em ambos os grupos. O aspecto macroscópico das lesões no grupo experimental caracterizou-se por extensa área de hiperemia com cobertura de tecido seroso; e no grupo controle, verificou-se pequeno tecido cicatricial recobrindo o material de sutura. A realização das biópsias intestinais foi executada com facilidade bem como sua sutura. A avaliação histológica demonstrou em ambos os grupos intensa infiltração eosinofílica, presença de colágeno em fase de maturação além de evidências de intensa neovascularização. A partir da análise dos valores laboratoriais observaram-se diferenças estatísticas significativas nos valores sanguíneos de bilirrubinas, hematócrito, monócito, uréia; e no líquido peritoneal estas diferenças foram manifestadas em proteína, densidade e número de leucócitos segmentados. Conclui-se que a abrasão focal de serosa de cólon maior como único fator promotor de aderências intra-abdominais fibrosas foi insuficiente. Além disso, a utilização de pericárdio equino como proteção de áreas de lesão intestinal, mesmo não tendo sido comprovada sua eficácia na minimização das aderências intra-abdominais, apresenta-se viável e possível, pois não foram observadas diferenças estatisticamente significativas (hematológicas, bioquímicas ou do líquido peritoneal) na comparação entre os grupos, ou alterações que determinasse efeitos deletérios aos animais. / The intra-abdominal adhesions are relatively common complications of abdominal surgery in horses and they can result in obstructive processes, abdominal pain and recurrent volvulus. The technical and pharmacological advances are aimed to minimize trauma and peritoneal inflammation, increase the fibrinolysis process, promote intestinal peristalsis and separate potentially adhesiogenic tissues during the initial phase of healing. In this study were used 10 horses, male, mixed breed, between 4 and 15 years old and weighing between 300 and 400kg. The experiment included animals that showed no changes in physical and laboratorial examination. The biological membrane was from the bank of biological membranes of the HOVET-FMVZ-USP. The anesthetic protocol consisted of sedation with a combination of ketamine 10% (0.7 mg / kg) and butorphanol (0.04 mg / kg). The laparotomy was performed by the left flank and the animal was kept in standing position. At the midpoint of the pelvic flexure was induced the injury by abrasion in serous surface, with a size of 7x7 cm. After the lesion induction, the group 1 (five animals) had the injured area covered with a biological membrane. The group 2 (five animals) had the intestinal segment exteriorized, and after the lesion creation it was washed with saline and repositioned in the abdominal cavity. In both groups was performed suturing a single point in the center of the lesion using 2-0 nylon, in order to endorse the lesion created. The sutures of the muscle layers and subcutaneous tissue were performed with continuous suture with Polyglactin 910 n0 2 and n0 00 respectively, and the skin was sutured continuously using nylon n0 0. The postoperative evaluation consisted of daily physical assessment and collection of material for laboratory analysis (blood, serum and peritoneal fluid) weekly for four weeks. After 30 days, the animals underwent another laparotomy to verify the presence of intra-abdominal adhesions, macroscopic aspect of the lesions and implant, and intestinal biopsy. The collection of material for the completion of laboratory tests was performed at moments M0- pre-operative, M7- 7 days post-operatively, M14- 14 days post-operatively, M21- 21 days post-operatively, M28- 28 days post-operatively. The laparotomy was performed in ventral position following the technique of grid that´s promoted less surgical trauma, but this approach offered to surgeon less surgical field, causing some difficulty for exteriorization of the intestinal segment. The clinical outcome was satisfactory showing advantage when compared literature. During the surgical reassessment verified the presence of fibrous scar tissue between the muscle layers that determined some trouble to access the abdominal cavity. There were no intra-abdominal adhesions in both groups. The macroscopic aspect of lesions in the experimental group was characterized by extensive area of redness covered serous tissue, and the control group there was little scar tissue overlying the suture material. The intestinal biopsies and suture were performed easily. The histological evaluation showed in both groups intense eosinophilic infiltration, presence of collagen in the maturation stage in addition to evidence of intense neovascularization. The laboratory results showed statistically significant differences in blood levels of bilirubin, hematocrit, monocyte, urea, and into peritoneal fluid, these differences were manifested in protein density and leukocytes. Concluded that the focal serosal abrasion of the large colon as the single factor promoting intra-abdominal fibrous adhesions was insufficient. Furthermore, the use of equine pericardium as protecting areas of intestinal injury, even without prove their effectiveness in minimizing intra-abdominal adhesions, it appears feasible and possible, because there were no statistically difference (hematological, biochemical or peritoneal fluid) between the groups, or changes that would determine deleterious effects to the animals.

Includes bibliographical references (leaves [1-20]). A systematic analysis of wear involving the in vitro analysis of the wear of standard composite resin and glass ionomer cements restorations under controlled conditions; and, the qualitative and quantitative investigation of wear over a range of pH's and loads which might be encountered clinically in order to develop a "wear map" of the micromorphology of wearing teeth and restorations and a systematic modeling of wear rates.

Summary: Some 250 Australian aboriginal skulls were studied to ascertain differences in tooth dislocation and wear in this ethnic group as compared with those manifested in the pre-European Maori, with consideration of the differences in cultural and botanical background as contributing factors. Other features were studied, including the crowding of anterior teeth, the incidence of caries and abscesses, and of mottled enamel and tooth fracture. Aspects of physical anthropology and biology were found to be relevant to this study, since they offered explanations for some previously unsolved problems such as edge-to-edge bite, and crowding of incisors in well-formed jaws. The work is supported by 28 illustrations of the dentition selected from various sources, and described in the text. Reprints of 18 other published papers reporting various dental studies of relevance to the above major publication are included in this presentation.