Thesis (M.S.)--University of Alabama at Birmingham, 2009. / Title from PDF title page (viewed on Sept. 3, 2009). Includes bibliographical references (p. 32-37).

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / O uso de primers autocondicionantes e de bráquetes com compósito pré-incorporado tem sido apresentado como uma alternativa para a redução de passos clínicos. O propósito deste estudo foi avaliar o efeito de um primer autocondicionante (Transbond Plus Self-Etching Primer - SEP) na resistência ao cisalhamento de bráquetes com compósito pré-incorporado colados in vivo. A amostra consistiu de 92 dentes obtidos de 23 pacientes com indicação prévia de extração de 4 pré-molares. Os dentes foram divididos em 4 grupos, sendo os bráquetes colados pelo mesmo operador, alternando os quadrantes em cada paciente: Grupo 1 (controle) - Ácido fosfórico à 37% + primer (Transbond XT Primer) + compósito (Transbond XT Adhesive Paste) + bráquete convencional; Grupo 2 - Ácido fosfórico à 37% + primer + bráquete com compósito pré-incorporado; Grupo 3 SEP + compósito + bráquete convencional; Grupo 4 - SEP + bráquete com compósito pré-incorporado. Após 30 dias os pré-molares foram extraídos, sendo submetidos ao teste de resistência ao cisalhamento através da uma Máquina de Ensaios Universal, com velocidade de 0,5mm/min. Os dados obtidos pelos grupos foram analisados com 2-way ANOVA (p<0,05). As forças médias e desvios padrão obtidos foram os seguintes: Grupo 1 = 11,35 (2,36) MPa; Grupo 2 = 9,77 (2,49) MPa; Grupo 3 = 10,89 (2,60) MPa; e Grupo 4 = 10,16 (2,75) MPa. Não foi observada diferença significativa entre o uso do SEP e o de condicionador e primer tradicionais (p = 0,948). De qualquer modo, diferenças significativas na força de adesão foram observadas quando utilizados bráquetes com compósito pré-incorporado (p = 0,032). Pode ser concluído que a combinação do primer autocondicionante com o bráquete com compósito pré-incorporado apresentou valores de força de adesão adequados, sendo promissora para uso clínico. / The use of self-etching primers and precoated brackets are presented as alternatives to shorten the clinical bonding steps. The aim of this study was to evaluate the influence of a self-etching primer - SEP (Transbond Plus SEP, 3M Unitek) on shear bond strength of adhesive uncoated and precoated Victory brackets (3M Unitek). The sample group consisted of 23 patients with 4 premolars each one, equally divided in four different groups according to the bracket and enamel preparation. Brackets were bonded in vivo, by the same operator, using a split mouth random technique: Group 1- 37% Phosphoric acid + primer + composite + conventional Victory bracket; Group 2- 37% Phosphoric acid + primer + precoated Victory bracket; Group 3- SEP + composite + conventional bracket; Group 4- SEP + precoated bracket. After 30 days premolars were extracted for orthodontic reasons, and a Universal Testing Machine was used to apply an occlusal shear force directly to the enamel-bracket interface at a speed of 0.5 mm/min. Mean results and standard deviation for the groups were: Group 1 = 11,35 (2,36) MPa; Group 2 = 9,77 (2,49) MPa; Group 3 = 10,89 (2,60) MPa; e Group 4 = 10,16 (2,75) MPa. The groups were compared using 2-way ANOVA. No difference was observed while a conventional etching and primer or self-etching primer was used (p = 0.948). But, it was indicated significant differences in bond strength between uncoated and precoated brackets (p = 0.032). However, it could be concluded that the self etching primer combined with adhesive precoated brackets showed adequate shear bond strength, and may be suitable for clinical use.

Orientadores: Mirela Sanae Shinohara, Mário Fernando de Góes / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-21T23:51:52Z (GMT). No. of bitstreams: 1 Freitas_MarcelaSantiago_M.pdf: 38797129 bytes, checksum: 16869befa66eba198d1cb13ad5c9ac1d (MD5) Previous issue date: 2013 / Resumo: Estudos mostram que a resistência de união (RU) alcançada pelos sistemas adesivos autocondicionantes em superfície de esmalte pré-condicionado é significativamente maior se comparada aos valores obtidos em esmalte não condicionado. A partir destas evidências, este estudo teve como objetivo avaliar a RU e a morfologia da interface adesiva (MI) em esmalte e dentina de um adesivo autocondicionante de passo único multi-mode e um adesivo autocondicionante de dois passos com e sem pré-condicionamento ácido da superfície comparado a dois sistemas adesivos de condicionamento total, de dois e três passos. Terceiros molares humanos recém-extraídos foram seccionados para obtenção de superfícies planas em esmalte e dentina, as quais foram desgastadas com lixa SiC #600 para padronização da smear layer. Estas amostras foram divididas aleatoriamente em 6 grupos: (SBU) Scotchbond Universal; (SBUcond) SBU précondicionado; (CSE) Clearfil SE Bond; (CSEcond) CSE pré-condicionado; (SBMP) Scotchbond Multi-Purpose; e (EX) Excite F. Os grupos de condicionamento total e os autocondicionantes a serem avaliados com pré-condicionamento receberam a aplicação do ácido fosfórico por 15s em dentina e 30s em esmalte. Todos os sistemas adesivos foram aplicados de acordo com as recomendações dos fabricantes. Em seguida, um bloco de resina composta (Filtek Supreme Plus) foi construído incrementalmente sobre cada superfície preparada para o teste de RU, e para a MI, as superfícies foram restauradas com resina flow (Filtek Z-350 Flowable Restorative) formando um "sanduíche", de esmalte ou dentina. Após 24h, para avaliação da RU, as amostras foram seccionadas em palitos com área transversal de 0,8mm2 e submetidos ao teste de microtração com velocidade de 1,0mm/min. Os resultados foram analisados estatisticamente pelos testes one-way ANOVA e Fisher's PLSD (?=0.05) e os padrões de fratura analisados em Microscopia Eletrônica de Varredura (MEV). Para análise da MI, duas amostras de cada grupo foram incluídas em resina epóxica, polidas e observadas em MEV. Para esmalte, os resultados de RU mostraram que o SBUcond e CSEcond obtiveram os maiores valores, seguidos dos grupos SBMP, SBU e CSE que não apresentaram diferenças entre si. O grupo EX obteve os menores valores comparados aos outros grupos. Na análise da MI, os grupos SBUcond e CSEcond apresentaram nítidas extensões do adesivo penetrado no esmalte desmineralizado, semelhante aos sistemas de condicionamento total. Já para dentina, os resultados de RU mostraram que o condicionamento ácido prévio diminuiu significativamente os valores de RU dos sistemas autocondicionantes. Os maiores valores foram obtidos pelo SBU, CSE e SBMP, com valores de RU estatisticamente equivalentes entre si. Como em esmalte, o sistema adesivo EX obteve os menores valores. A análise em MEV da MI mostrou que o condicionamento prévio da dentina com adesivos autocondicionantes forma uma camada híbrida mais espessa com formação de tags resinosos, semelhantes aos sistemas adesivos de condicionamento total. Pode-se concluir que em esmalte, o condicionamento prévio aumentou significativamente os valores de RU para os sistemas autocondicionantes. Contudo, estes sistemas adesivos não apresentaram diferença estatística do adesivo convencional SBMP. E para dentina, o pré-condicionamento dos adesivos autocondicionantes diminuiu significativamente os valores de RU, entretanto, os valores de SBUcond não foram diferentes significativamente dos obtidos pelo sistema adesivo convencional SBMP / Abstract: Studies show that the bond strength (BS) achieved by self-etching adhesive systems on pre-etched enamel surface is significantly higher compared with the values obtained on unetched enamel. From this evidence, this study aimed to assess the BS and morphology of the adhesive interface (AI) on enamel and dentin of a one-step self-etching adhesive multi-mode and a two-step selfetching adhesive with and without pre-etching of surface compared with two totaletching adhesive systems, two and three steps. Recently extracted human third molars were sectioned to obtain flat surfaces in enamel and dentin, which were ground with #600 SiC sandpaper to standardize the smear layer. These samples were randomly assigned into 6 groups: (SBU) Scotchbond Universal; (SBU-et) SBU pre-etched; (CSE), Clearfil SE Bond, (CSE-et) CSE pre-etched; (SBMP) Scotchbond Multi-Purpose, and (EX) Excite F. The groups total-etching and selfetching to be evaluated with pre-etching received the application of phosphoric acid for 15s in dentin and 30s in enamel. All adhesive systems were applied according to manufacturers' recommendations. Then, a block of composite resin (Filtek Supreme Plus) was constructed incrementally on each surface prepared for BS testing. For AI, the areas were filled with flowable resin (Filtek Flowable Restorative Z-350) forming a "sandwich" of enamel or dentin. After 24 hours, to review the BS, the specimens were sectioned into sticks with cross-sectional area of 0.8mm² and submitted to microtensile test at a speed of 1.0mm/min. The results were statistically analyzed by one-way ANOVA test and Fisher's PLSD (?=0.05) and fracture patterns were analyzed through Scanning Electron Microscopy (SEM). For analysis of AI, two samples from each group were embedded in epoxy resin, polished and observed through SEM. For enamel, the results of BS showed that SBU-et and CSE-et obtained the highest values, followed by SBMP groups, SBU and CSE with no differences among them. The EX group obtained the lowest values of all other groups. In the analysis of AI, and CSE-et and SBU-et groups showed sharp tag extensions of the adhesive penetrated in the demineralized enamel, similar to total-etching systems. As for dentin, BS results showed that acid etching significantly reduced the BS values of self-etching systems. The highest values were obtained by the SBU, CSE and SBMP with BS values statistically equivalent to each other. As in enamel, the adhesive system EX obtained the lowest values. SEM analysis showed that BS for pre-etched dentin with selfetching adhesive forms a thicker hybrid layer with resin tags formation, similar to total-etching adhesive systems. It can be concluded that on enamel, the preetching significantly increased BS for self-etching systems. However, these adhesive systems showed no statistical difference from conventional adhesive SBMP. And to dentin, pre-etching of sel-etching adhesives significantly reduced BS, however, SBU-et values were not significantly different from those obtained by the conventional adhesive system SBMP / Mestrado / Dentística / Mestra em Materiais Dentários

Orientador: Luís Alexandre Maffei Sartini Paulillo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-24T07:41:05Z (GMT). No. of bitstreams: 1 Coppini_ErickKamiya_M.pdf: 3349153 bytes, checksum: e0323d6512c30cee2e8ea17128a4c6e6 (MD5) Previous issue date: 2013 / Resumo: The aim of this study was to evaluate the cavosuperficial enamel acid-etching influence in class I cavities, filled with composites on microtensile bond strength, Knoop microhardness and nanoleakage after thermomechanic ageing. It was selected 76 sound molar splitted on: 32 teeth to microtensile test (n=8); 32 teeth to Knoop microhardness (n=8); and 12 teeth (n=3) to nanoleakage analysis. The cavities were prepared on a standard cavity preparation machine. Half of the teeth had the cavosuperficial enamel etched with 35% phosphoric acid and restored with a Silorane restorative system or a Methacrylate restorative system. After the conclusion of the restoration procedures, the teeth were taken to a thermomechanic cycling machine where the artificial ageing was performed with 200.000 mechanical cycles with an 80 N load in a 2HZ frequency and thermocycling by filling the chambers for 30 seconds and 15 seconds drainage with the temperatures varying between 5ºC and 55ºC. The samples were submitted to the microtensile bond strength test, Knoop microhardness and nanoleakage evaluation. To statistical analysis it was performed the ANOVA two-way and Tuckey test (p ? 0,05). The group restored with methacrylate without acid-etching showed the lowest values of microtensile bond strength and it was statistically different to the other groups that have no difference between them. The methacrylate composite presented statistically higher values on Knoop microhardness compared to silorane composite. The nanoleakage analysis showed low infiltration to silorane restorative system and moderate infiltration to the methacrylate restorative system. The methacrylate group restored without enamel acid-etching showed the formation of Water Trees. It can be concluded that the acid-etching improved the bond strength to the methacylate system. The methacrylate composite has bigger Knoop microhardness than silorane composite. The methacrylate restorative system showed moderate infiltration on nanoleakage analysis / Abstract: The aim of this study was to evaluate the cavosuperficial enamel acid-etching influence in class I cavities, filled with composites on microtensile bond strength, Knoop microhardness and nanoleakage after thermomechanic ageing. It was selected 76 sound molar splitted on: 32 teeth to microtensile test (n=8); 32 teeth to Knoop microhardness (n=8); and 12 teeth (n=3) to nanoleakage analysis. The cavities were prepared on a standard cavity preparation machine. Half of the teeth had the cavosuperficial enamel etched with 35% phosphoric acid and restored with a Silorane restorative system or a Methacrylate restorative system. After the conclusion of the restoration procedures, the teeth were taken to a thermomechanic cycling machine where the artificial ageing was performed with 200.000 mechanical cycles with an 80 N load in a 2HZ frequency and thermocycling by filling the chambers for 30 seconds and 15 seconds drainage with the temperatures varying between 5ºC and 55ºC. The samples were submitted to the microtensile bond strength test, Knoop microhardness and nanoleakage evaluation. To statistical analysis it was performed the ANOVA two-way and Tuckey test (p ? 0,05). The group restored with methacrylate without acid-etching showed the lowest values of microtensile bond strength and it was statistically different to the other groups that have no difference between them. The methacrylate composite presented statistically higher values on Knoop microhardness compared to silorane composite. The nanoleakage analysis showed low infiltration to silorane restorative system and moderate infiltration to the methacrylate restorative system. The methacrylate group restored without enamel acid-etching showed the formation of Water Trees. It can be concluded that the acid-etching improved the bond strength to the methacylate system. The methacrylate composite has bigger Knoop microhardness than silorane composite. The methacrylate restorative system showed moderate infiltration on nanoleakage analysis / Mestrado / Dentística / Mestre em Clínica Odontológica

Este estudo in vitro avaliou a influência do clareamento ativado com luz híbrida, em função da variação do pH e concentração de géis clareadores, e do condicionamento ácido prévio do esmalte bovino na alteração da rugosidade e desgaste após escovação simulada. Fragmentos de esmalte (1,5cm x 0,5cm x 0,4cm) foram divididos em duas partes, ficando uma metade como controle e a outra como área teste. Esta última foi subdividida em duas metades, sendo que uma recebeu o condicionamento ácido somado ao gel clareador e a outra somente o gel clareador. Os espécimes foram divididos aleatoriamente em seis grupos (n=10): C = controle; TBO35LH = Total Blanc Office 35% 1 sessão (5x8) + ativação com luz híbrida LED/Laser; LPS35LH= Lase Peroxide Sense 35% - 1 sessão (5x8) + ativação com luz híbrida LED/Laser; LPS25LH = Lase Peroxide Sense 25% - 1 sessão (5x8) + ativação com luz híbrida LED/Laser; LPL15LH = Lase Peroxide Lite 15% - 1 sessão (5x8) + ativação com luz híbrida LED/Laser; LPL10LHV = Lase Peroxide Lite 10% - 1 sessão (5x8) + ativação com luz híbrida LED/Laser violeta. A rugosidade aritmética (Ra) inicial, após clareamento e após escovação, foi determinada pela média (&mu;m) de três leituras (em cada área sem e com ácido totalizando seis leituras por espécimes) com o rugosímetro Hommel Tester T 1000. Os valores médios do pH foram determinados pelo peagômetro digital Sentron Model 1001 nos tempos inicial e final. Os espécimes foram armazenados em saliva artificial por sete dias, submetidos a 100.000 ciclos de escovação simulada. Após 24 horas o desgaste superficial foi determinado (&mu;m) empregando o mesmo rugosímetro. Em relação ao desgaste e a alteração de rugosidade superficial, os resultados foram submetidos à Anova a dois critérios e a dois critérios de medidas repetidas e posteriormente ao teste de Tukey. Os dados obtidos das leituras de pH foram submetidos à ANOVA a um critério e a dois critérios de medidas repetidas e ao teste de Kruskal Wallis e Tukey para comparações individuais entre os grupos. Para todos os testes o nível de significância foi de 5%. A rugosidade e o desgaste apontaram diferenças estatísticas entre os grupos, principalmente quando comparado à área com e sem ácido. Os géis clareadores apresentaram tendência de diminuição dos valores de pH do tempo inicial para o tempo final, contudo, uma correlação com a rugosidade e com o desgaste não pôde ser estabelecida de forma clara. / This in vitro study evaluated the influence of whitening activated with hybrid light on the function variations of the pH level and concentration of bleaching gels and prior acid etching of bovine enamel and the change in roughness and wear after simulated tooth brushing. Fragments of enamel (1.5 cm x 0.5 cm x 0.4 cm) were divided into two parts, one half as the control and the other as the test area. The latter was divided into two halves, one of which received the etching added to the whitening gel and the other with only the whitening gel. The specimens were randomly divided into six groups (n = 10): C = control; TBO35LH = 35% Total Blanc Office 1x session (5x8\') + activation with hybrid light LED/Laser; LPS35LH = 35% Lase Peroxide Sense - 1x session (5x8\') + activation with hybrid light LED/Laser; LPS25LH = 25% Sense Lase Peroxide - 1x session (5x8\') + activation with hybrid light LED/Laser; LPL15LH = 15% Lase Peroxide Lite - 1x session (5x8 \') + activation with hybrid light LED/Laser; LPL10LHV = 10% Lase Peroxide Lite - 1x session (5x8\') + activation with violet hybrid light LED/Laser. The arithmetic roughness (Ra) started after bleaching and after brushing was determined by averaging (&mu;m) the three readings (in each area - with and without acid for a total of six readings per specimen) with a Rugosimeter Hommel Tester T 1000. The mean pH values were determined by the Sentron Model 1001 digital pH meter at the start and end times. The specimens were stored in artificial saliva for seven days, and subjected to 100,000 cycles of simulated brushing. After 24 hours, the surface wear was determined (&mu;m) employing the same roughness meter. In relation to the change in wear and surface roughness, the results were evaluated by two way ANOVA testing for repeated measures and later, a Tukey\'s test. The data obtained from the pH readings were submitted to two way ANOVA testing for repeated measures and the Kruskal Wallis and Tukey tests for the comparisons between the individual groups. The significance level was set at 5% for all the tests. The roughness and wear showed statistical differences between the groups, especially when compared to the area with and without acid. The bleaching gels tended to decrease in pH from the starting time to the final time, however, a correlation with the roughness and wear could not be clearly established.

Orientador: Josimeri Hebling / Banca: Ricardo Marins de Carvalho / Banca: Luís Geraldo Vaz / Resumo: O presente estudo teve como objetivo investigar o efeito da redução do tempo de condicionamento da dentina decídua na resistência de união imediata de um sistema convencional e um autocondicionante, e na degradação da união resina-dentina após 6 meses de armazenagem em água. Foram utilizados quarenta e oito molares decíduos hígidos foram aleatoriamente divididos em 4 grupos (n=12) de acordo com o sistema adesivo (Adper Single Bond e Clearfil SE Bond) e o tempo de condicionamento da dentina (como recomendado pelo fabricante e metade desse tempo). Desta forma, o sistema Single Bond foi aplicado sobre a dentina condicionada com ácido fosfórico a 35% por 15 ou 7 segundos, enquanto que o sistema Clearfil SE Bond foi aplicado à dentina condicionada com SE Primer por 20 ou 10 segundos. Em seguida, coroas em resina composta foram reconstruídas incrementalmente e os dentes foram mantidos hidratados em estufa à 37o C por 24 horas. Dez dentes de cada grupo foram utilizados para o ensaio mecânico de microtração. Os demais foram preparados para análise da interface adesiva em MEV. Espécimes em forma de pilar de secção transversal quadrangular (0,49 mm2) foram obtidos e divididos de acordo com a condição de armazenagem, 24 horas em água (controle), 6 meses em água e 6 meses em óleo. Os espécimes foram tracionados a velocidade de 0,5 mm/min em máquina de ensaios mecânicos e as fraturas classificadas em adesiva, coesiva em dentina, coesiva em resina ou mista. Os dados foram analisados estatisticamente pela análise de variância e testes complementares de comparação múltipla, considerando-se o nível de significância de 5%. Após 24 horas de armazenagem, os sistemas adesivos apresentaram valores de resistência de união comparáveis estatisticamente, não influenciados pela redução do tempo de condicionamento ácido... (Resumo completo, clicar acesso eletrônico abaixo). / Abstract: To evaluate the effect of reducing the acid etching of primary dentin on the immediate bond strength of a conventional and a self-etching primer system, and on the degradation of the resin-dentin bonds after 6 months aging. Forty-eight sound primary molars were randomly divided into 4 groups of investigation (n=12) according to the adhesive system (Adper Single Bond and Clearfil SE Bond) and the period of acid etching (as recommended by the manufacturers and half of this time). Single Bond was applied to dentin after 35% phosphoric acid etching for 15 seconds or 7 seconds, whereas Clearfil SE Bond was applied to dentin after the application of SE Primer for 20 seconds or 10 seconds. Following the adhesive systems, composite resin crowns were incrementally built-up and the teeth were stored in water at 37o C for 24 hours. Specimens with a cross-sectional area of 0,49 mm2 were produced from each one of the teeth (10 teeth per group) and further divided according to the storage condition, 24 hours in water, 6 months in water and 6 months in mineral oil, when they were tested under tension until failure in a machine operating at a cross-head speed of 0.5 mm/min. After the microtensile test, the failures were classified as adhesive, cohesive in dentin, cohesive in resin or mixed. The two remaining teeth per group were prepared to SEM evaluation of the interfaces. Two-way analysis of variance and multiple comparison testes were applied at a significance level of 5%. When bond strength was evaluated after 24 hours storage in water there was no significant difference between the adhesive systems, irrespective of the periods of acid etching. For Single Bond, water storage for 6 months in water significantly reduced bond strength, especially when the dentin was phosphoric acid conditioned for 15 seconds (36.7% reduction). For Clearfil SE Bond... (Complete abstract, click electronic address below). / Mestre

Made available in DSpace on 2014-06-11T19:28:58Z (GMT). No. of bitstreams: 0 Previous issue date: 2006-05-12Bitstream added on 2014-06-13T20:58:53Z : No. of bitstreams: 1 saavedra_gsfa_me_sjc.pdf: 2452196 bytes, checksum: b3f2463bbb388a1fe5fbb2276e959c7e (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo deste trabalho foi avaliar três hipóteses: a) o processo de neutralização influencia nos valores de resistência de união entre uma cerâmica feldspática e um cimento resinoso; b) limpeza sônica dos precipitados do ácido fluorídrico aumenta os valores de resistência de união; c) associação entre o do processo de neutralização e a limpeza sônica melhora a resistência de união. Confeccionou-se 32 blocos cerâmicos (VM7 VITA Zahnfabrik), os quais foram duplicados em resina composta (W3D Master). Os resultados deste estudo confirmaram que: a) o processo de neutralização influencia nos valores de resistência de união entre uma cerâmica feldspática e um cimento resinoso; b) a limpeza sônica dos precipitados do ácido fluorídrico aumenta os valores de resistência de união; c) a associação entre o processo de neutralização e a limpeza sônica melhora a resistência de união. / This study evaluated three hypotheses: a) the neutralization process influences the bond strength values between a feldspar ceramic and a resin cement; b) ultrasonic cleaning of hydrofluoric acid precipitates increases the bond strength values; c) association between the neutralization process and ultrasonic cleaning improves the bond strength. The present results confirmed that: a) the neutralization process influences the bond strength values between a feldspar ceramic and a resin cement; b) ultrasonic cleaning of hydrofluoric acid precipitates increases the bond strength values; c) association between the neutralization process and ultrasonic cleaning improves the bond strength.

Made available in DSpace on 2014-06-11T19:27:47Z (GMT). No. of bitstreams: 0 Previous issue date: 2005-02-28Bitstream added on 2014-06-13T20:17:11Z : No. of bitstreams: 1 sanabe_me_me_arafo.pdf: 801888 bytes, checksum: c29d9fba1c2e1a1219458d7df6abd318 (MD5) / Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) / O presente estudo teve como objetivo investigar o efeito da redução do tempo de condicionamento da dentina decídua na resistência de união imediata de um sistema convencional e um autocondicionante, e na degradação da união resina-dentina após 6 meses de armazenagem em água. Foram utilizados quarenta e oito molares decíduos hígidos foram aleatoriamente divididos em 4 grupos (n=12) de acordo com o sistema adesivo (Adper Single Bond e Clearfil SE Bond) e o tempo de condicionamento da dentina (como recomendado pelo fabricante e metade desse tempo). Desta forma, o sistema Single Bond foi aplicado sobre a dentina condicionada com ácido fosfórico a 35% por 15 ou 7 segundos, enquanto que o sistema Clearfil SE Bond foi aplicado à dentina condicionada com SE Primer por 20 ou 10 segundos. Em seguida, coroas em resina composta foram reconstruídas incrementalmente e os dentes foram mantidos hidratados em estufa à 37o C por 24 horas. Dez dentes de cada grupo foram utilizados para o ensaio mecânico de microtração. Os demais foram preparados para análise da interface adesiva em MEV. Espécimes em forma de pilar de secção transversal quadrangular (0,49 mm2) foram obtidos e divididos de acordo com a condição de armazenagem, 24 horas em água (controle), 6 meses em água e 6 meses em óleo. Os espécimes foram tracionados a velocidade de 0,5 mm/min em máquina de ensaios mecânicos e as fraturas classificadas em adesiva, coesiva em dentina, coesiva em resina ou mista. Os dados foram analisados estatisticamente pela análise de variância e testes complementares de comparação múltipla, considerando-se o nível de significância de 5%. Após 24 horas de armazenagem, os sistemas adesivos apresentaram valores de resistência de união comparáveis estatisticamente, não influenciados pela redução do tempo de condicionamento ácido... . / To evaluate the effect of reducing the acid etching of primary dentin on the immediate bond strength of a conventional and a self-etching primer system, and on the degradation of the resin-dentin bonds after 6 months aging. Forty-eight sound primary molars were randomly divided into 4 groups of investigation (n=12) according to the adhesive system (Adper Single Bond and Clearfil SE Bond) and the period of acid etching (as recommended by the manufacturers and half of this time). Single Bond was applied to dentin after 35% phosphoric acid etching for 15 seconds or 7 seconds, whereas Clearfil SE Bond was applied to dentin after the application of SE Primer for 20 seconds or 10 seconds. Following the adhesive systems, composite resin crowns were incrementally built-up and the teeth were stored in water at 37o C for 24 hours. Specimens with a cross-sectional area of 0,49 mm2 were produced from each one of the teeth (10 teeth per group) and further divided according to the storage condition, 24 hours in water, 6 months in water and 6 months in mineral oil, when they were tested under tension until failure in a machine operating at a cross-head speed of 0.5 mm/min. After the microtensile test, the failures were classified as adhesive, cohesive in dentin, cohesive in resin or mixed. The two remaining teeth per group were prepared to SEM evaluation of the interfaces. Two-way analysis of variance and multiple comparison testes were applied at a significance level of 5%. When bond strength was evaluated after 24 hours storage in water there was no significant difference between the adhesive systems, irrespective of the periods of acid etching. For Single Bond, water storage for 6 months in water significantly reduced bond strength, especially when the dentin was phosphoric acid conditioned for 15 seconds (36.7% reduction). For Clearfil SE Bond... (Complete abstract, click electronic address below).

Orientador: Estevão Tomomitsu Kimpara / Banca: Rander Pereira Avelar / Banca: Tarcisio José de Arruda Paes / Resumo: O objetivo deste trabalho foi avaliar três hipóteses: a) o processo de neutralização influencia nos valores de resistência de união entre uma cerâmica feldspática e um cimento resinoso; b) limpeza sônica dos precipitados do ácido fluorídrico aumenta os valores de resistência de união; c) associação entre o do processo de neutralização e a limpeza sônica melhora a resistência de união. Confeccionou-se 32 blocos cerâmicos (VM7 VITA Zahnfabrik), os quais foram duplicados em resina composta (W3D Master). Os resultados deste estudo confirmaram que: a) o processo de neutralização influencia nos valores de resistência de união entre uma cerâmica feldspática e um cimento resinoso; b) a limpeza sônica dos precipitados do ácido fluorídrico aumenta os valores de resistência de união; c) a associação entre o processo de neutralização e a limpeza sônica melhora a resistência de união. / Abstract: This study evaluated three hypotheses: a) the neutralization process influences the bond strength values between a feldspar ceramic and a resin cement; b) ultrasonic cleaning of hydrofluoric acid precipitates increases the bond strength values; c) association between the neutralization process and ultrasonic cleaning improves the bond strength. The present results confirmed that: a) the neutralization process influences the bond strength values between a feldspar ceramic and a resin cement; b) ultrasonic cleaning of hydrofluoric acid precipitates increases the bond strength values; c) association between the neutralization process and ultrasonic cleaning improves the bond strength. / Mestre

Orientador: Mario Fernando de Goes / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T13:06:43Z (GMT). No. of bitstreams: 1 Caiado_AnaCarolinaRochaLima_M.pdf: 12410221 bytes, checksum: 10dff9d1f7b58797480e9a00a97d0a78 (MD5) Previous issue date: 2006 / Resumo: Este estudo teve como objetivos: (a) caracterizar a morfologia, a densidade e a área transversal de túbulos dentinários da dentina coronária (profunda) e radicular (terço cervical) intactas e após condicionamento com ácido fosfórico 32% (AF) e primer condicionante do sistema adesivo Clearfill Protect Bond (P); e (b) avaliar e comparar a resistência de união e os padrões de fratura obtidos na dentina coronária (profunda) e dentina radicular (terço cervical). Pré-molares humanos hígidos foram fixados em gluteraldeído (2,5%). Secções da dentina coronária profunda e dentina radicular (região cervical) foram obtidas por clivagem. Cada dente recebeu os seguintes tratamentos: G1- dentina coronária + AF; G2- dentina coronária + P; G3 - dentina coronária sem tratamento; G4- dentina radicular + AF; G5- dentina radicular + P; G6- dentina radicular sem tratamento. As secções condicionadas com primer foram imersas em etanol e acetona. Todos os grupos foram desidratados em concentrações ascendentes de álcool e HMDS e visualizadas por microscopia eletrÃ'nica de varredura em ampliação de 1500X. As imagens obtidas foram usadas para calcular a densidade (D) e a área (A) da secção transversal dos túbulos dentinários em µm2 utilizando o programa Leica IM50. Para o teste de microtração foram utilizados fatias de dentina coronária profunda e dentina radicular cervical de 12 dentes que foram divididas em quatro grupos de acordo com a região dentinária e o sistema adesivo utilizado: G7- dentina radicular + Single Bond II; G8- dentina radicular + Clearfill Protect Bond; G9- dentina coronária + Single Bond II; G10- dentina coronária + Clearfill Protect Bond. Resina composta foi acrescentada em ambos os lados das fatias. Foram obtidas dessas fatias espécimes em forma de palito. Após armazenamento em água (37ºC) os espécimes foram submetidos ao teste de microtração em uma máquina de ensaio universal (Instron), a uma velocidade de 0,5mm/min. A dentina radicular intacta do terço cervical apresentou uma superfície irregular formada por calcosferitos, o que a difere estruturalmente da dentina coronária. Já a densidade (42.627/mm2) e a área transversal média (2,9035/ µm2) dos túbulos dentinários na raiz não revelou diferença estatisticamente significante (p> 0,05) aos valores encontrados na coroa. Os dados de resistência de união foram estatisticamente superiores na dentina coronária (26.63 MPa) do que na dentina radicular (19.76 MPa). O padrão de fratura mais frequentemente encontrado para ambas as regiões foi a fratura mista (coesiva no adesivo e na camada híbrida). ÿ possível concluir que as dentinas coronária (profunda) e radicular do (terço cervical) apresentam diferenças morfológicas e nos valores de resistência de união, porém apresentam semelhanças quanto à densidade de túbulos e padrões de fratura independente do sistema adesivo utilizado / Abstract: The aim of this study was to: (a) characterize the morphology, density and transversal cross-section area of tubules of deep crown and cervical root dentine, intact and after etched with 32% phosphoric acid (AF) or the self-etch primer of the Clearfill Protect Bond adhesive system (P); and (b) evaluate and compare the bond strength and the fracture patterns obtained from deep crown dentine and cervical root dentine. Human carie-free premolars (n=5) were fixed in 25% glutaraldehyde. Deep crown and root dentine sections were obtained by cleavage. Each tooth was treated as follows: G1- crown dentine + AF; G2- crown dentine and P; G3-intact crown dentine; G4- root dentine + AF; G5- root dentine + P; G6- intact root dentine. The sections etched with primer were immersed in ethanol and acetone. All groups were dehydrated in increasing alcohol concentration and Hexamethyldisilazane, nd were visualized by Scanning Electron Microscopy. A magnification of 1500X was used to calculate the density (D) and the dentinal tubule transversal cross-section area per mm2, using the program Leica IM50. For microtensile testing, twelve premolars were cut to obtain slices of deep crown dentine and cervical root dentine. These were divided in four groups according to dentine region and adhesive system employed: G7- root dentine + Single Bond II; G8- root dentine + Clearfill Protect Bond; G9- crown dentine + Single Bond II; G10- crown dentine + Clearfill Protect Bond. Restorative was added to both sides of the slices. Beam specimens were obtained from these restored slices which were kept in water at 37ºC. The specimens were microtensile tested using a universal testing machine (Instrom) at a speed of 0,5mm/min. Intact cervical root dentine presented an irregular surface formed with calcospherites, demonstrating its structural difference from coronary dentine. On the other hand, root dentine tubule density (42,627/mm2) and average transversal area (2.9035/ µm2) did not reveal statistically significant difference (p>0.05) when compared to values obtain in crown. Bond strength results were statistically superior for crown dentine (26.63 MPa) then root dentine (19.76 MPa). Mixed fractures (cohesive in adhesive and hybrid layer) were the most frequent fracture patterns found for both regions. It is possible to conclude that deep crown dentine and cervical root dentine present morphological and bond strength differences, however, are similar in relation to tubule density and fracture patterns independent of the adhesive system employed. / Mestrado / Endodontia / Mestre em Clínica Odontológica