Made available in DSpace on 2014-06-12T22:59:25Z (GMT). No. of bitstreams: 2 arquivo8476_1.pdf: 5038082 bytes, checksum: 0cb3583859984a2f9505d6348cd18d26 (MD5) license.txt: 1748 bytes, checksum: 8a4605be74aa9ea9d79846c1fba20a33 (MD5) Previous issue date: 2004 / Verificou-se a influência da remoção do colágeno sobre a adesão dentinária de sistemas restauradores adesivos através de avaliações da resistência adesiva à microtração (RAμT) e da análise morfológica das interfaces adesivas em microscopia eletrômica de varredura (MEV). Molares humanos tiveram a dentina oclusal exposta, sendo distribuídos conforme os grupos: GSB (Single Bond/3M); GPB (Prime & Bond NT/Dentsply); GOC (One Coat Bond/Coltene/Vigodent); GPQ (PQ1/Ultradent); GSE (Clearfil SE Bond/Kuraray); GOU (One Up Bond F/Tokuyama). Cada grupo (n=12 - RaμT; n=3 - MEV) foi subdividido em 2 subgrupos quanto à forma de tratamento dentinário: 1 protocolo adesivo recomendado pelos fabricantes; 2 remoção do colágeno (H3PO4 15 s + NaOCl 5% por 2 min) + protocolo adesivo. Para os testes de RAμT foram obtidos 9 corpos de prova por dente, com área de interface adesiva de 0,8 mm2 (± 0,2), os quais foram submetidos ao ensaio mecânico de RAμT à velocidade de 0,5 mm/min. Para a MEV, após o preparo e tratamento das interfaces adesivas, realizou-se a metalização das superfícies e análise na linha de união. Os valores médios dos submetidos a ANOVA e teste de Tukey (α=5%) foram em MPa(letras iguais = similaridade estatística): GSB1=60,70 (ab); GSB2=39,08 (de); GPB1=31,73 (e); GPB2=61,53 (a); GOC1=54,30 (abcd); GOC2=51,24 (abcd); GPQ1=39,11 (de); GPQ2=58,18 (abc); GSE1=44,11 (abcde); GSE2=51,00 (abcd); GOU1=42,2 (bcde); GOU2=40,18 (cde). A análise em MEV evidenciou ausência de camada híbrida em todos os grupos submetidos à desproteinização. A remoção das fibras colágenas interferiu positivamente sobre a adesão do sistema adesivo Prime & Bond NT/Dentsply e PQ1/Ultradent e negativamente para o Single Bond/3M ESPE

O objetivo deste trabalho foi avaliar a resistência adesiva e o padrão de condicionamento do esmalte e da dentina após aplicação do ácido bórico a 2%. Foram utilizados terceiros molares humanos, condicionados com o ácido fosfórico a 35%, em forma de gel, e com diferentes formas de apresentações do ácido bórico a 2%. Para o estudo do padrão de condicioname nto, utilizaram-se discos de dentina e espécimes quadrangulares de esmalte que sofreram o condicionamento com as soluções de ácido fosfórico a 35% e diferentes formulações de ácido bórico a 2% utilizadas por diferentes tempos de aplicações. Após os condicionamentos, os espécimes foram preparados para observação no microscópio eletrônico de varredura. Para a avaliação da resistência adesiva do esmalte e da dentina, através de testes de microtração, foram utilizadas as soluções de ácido fosfórico a 35% e diferentes formulações de ácido bórico a 2% previamente à aplicação de dois sistemas adesivos (Single-Bond e Prime & Bond NT) e de duas resinas composta (Z-250 e TPH). Após os procedimentos adesivos, os dentes sofreram seccionamentos seriados a fim de que fossem obtidos espécimes para os testes de resistência adesiva. Os valores adesivos foram submetidos ao teste de análise de variância (ANOVA) e ao teste de Tukey, para a verificação de possíveis diferenças estatísticas entre os grupos, e em ambos os testes foi adotado um nível de significância de 5% (p< 0,05%). Na dentina e no esmalte, a solução de ácido fosfórico a 35% apresentou um maior poder desmineralizante comparado com as soluções de ácido bórico a 2%. Com relação aos valores de resistência adesiva na dentina, quando se utilizaram as diferentes soluções ácidas com o sistema adesivo Single-Bond e a resina composta Z-250, o grupo condicionado com ácido fosfórico apresentou valores adesivos significantemente maiores que os grupos que sofreram condicionamento com as soluções de ácido bórico a 2%. Porém, quando se utilizou o sistema adesivo Prime & Bond NT e a resina composta TPH, os valores adesivos dos grupos que sofreram os diferentes condicionamentos ácidos não apresentaram diferenças estatísticas entre si. No esmalte, quando se utilizaram as diferentes soluções ácidas em associação com o sistema adesivo Single-Bond e a resina composta Z-250, e também com o sistema adesivo Prime & Bond NT e a resina composta TPH, os grupos que sofreram o condicionamenmto com o ácido fosfórico a 35% apresentaram valores adesivos significantementre maiores que os grupos que sofreram condicionamento com as soluções de ácido bórico a 2%. Assim, pode-se concluir que o tratamento superficial da dentina e do esmalte com as soluções de ácido bórico a 2% não forneceu substratos com características suficientes para proporcionar resistência adesiva semelhante à fornecida pelo ácido fosfórico a 35%. / The aim of this laboratory work was to evaluate the bond strength and etching pattern of dentin and enamel conditioned by 2% boric acid. In this study, human third molars etched with 35% phosphoric acid and different solutions of 2% boric acid were utilized. For the etching pattern determination discs of dentin and square enamel specimens were conditioned (35% phosphoric acid and 2% boric acid solutions) and prepared for scanning electron microscopic observations. For dentin and enamel bond strengths evaluation the microtensile test was used. Phosphoric acid (35%) and boric acid (2%) were utilized in combination with two adhesive systems (Single-Bond and Prime & Bond NT) and two different composite resins (Z-250 and TPH). After bonding procedures, the teeth were sectioned and the obtained specimens submitted for microtensile tests. The results were analyzed by ANOVA followed Tukey’s analysis at a significance level of 5% (p<0,05). The 35% phosphoric acid solution presented higher demineralization power when compared to 2% boric acid solutions either in dentin or enamel. Regarding to the bond strength in dentin, when 35% phosphoric acid solution was used in combination with Single-Bond adhesive system and Z-250 composite resin the values were significantly higher when compared to other acid solutions. Therefore,whem the Prime & Bond NT adhesive system and TPH composite resin were utilized,no statisticaly different values were demonstrated for bond strenght among different acid solutions. In enamel, different acid solutions were also combined with Single-Bond and Prime & Bond adhesive systems and Z-250 and TPH composite resins. Groups etched with 35% phosphoric acid solution presented bond strength values significantly higher than other acid solutions. In conclusion, the utilization of 2% boric acid solution for etching dentin or enamel did not provide characteristics in this substrates and bond strength values similar to 35% phosphoric acid solution.

Orientador: Edson Alves de Campos / Resumo: O objetivo deste trabalho foi avaliar a resistência de união de diferentes sistemas adesivos autocondicionantes, frente a diferentes tratamentos em dentina hipermineralizada artificialmente. Oitenta (N = 80) dentes bovinos foram selecionados e tiveram ampla exposição dentinária. Os grupos foram divididos de acordo com o sistema adesivo autocondicionante de dois passos: AdheSE (Ivoclar) e Clearfil SE Bond (Kuraray). Cada subgrupo recebeu cinco diferentes tratamentos: (1) aplicação do sistema adesivo segundo recomendações do fabricante, (2) condicionamento com ácido fosfórico 37% por 15" + laser Er,Cr:YSGG + adesivo, (3) laser Er,Cr:YSGG + condicionamento com ácido fosfórico 37% por 15" + adesivo, (4) condicionamento com ácido fosfórico 37% + adesivo, (5) aplicação do laser Er,Cr:YSGG + adesivo. Em seguida, cilindros de resina composta (FiltekTM Z350 XT - 3M ESPE) foram posicionados e fotoativados por 40s. Após preparação dos espécimes, parte deles (n=8) ficou armazenada em ambiente úmido a 37°C por 24h para então ser submetida a teste de resistência de união ao microcisalhamento. Os resultados de resistência de união foram obtidos em MPa e submetidos à Análise de Variância e Teste de Tukey ao nível de significância de 5%. Os resultados demonstram que o grupo tratado com ácido + adesivo, utilizando o sistema AdheSE apresentou os maiores valores médios de resistência de união ao microcisalhamento. Pode-se concluir que o pré-tratamento a laser não interferiu negativamente nos... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The objective of this study was to evaluate the bond strength of different adhesive systems after different treatments of normal and artificially hypermineralized dentin. Eighty (N=100) healthy bovine teeth had been selected and will have extensive dentin exposure. The groups were divided according to the adhesive system used: AdheSE and Clearfil SE Bond. Each subgroup received five different treatments: (1) applying the adhesive system following manufacturer's recommendations, (2) etching with 37% phosphoric acid for 15 " + Er, Cr: YSGG laser + adhesive, (3) Er, Cr: YSGG laser + etching with 37% phosphoric acid for 15 " + adhesive, (4) etching with 37% phosphoric acid + adhesive, (5) Er,Cr: YSGG laser + adhesive. Cylinders of composite resin (Z350 XT FiltekTM - 3M ESPE) were positioned and photoactivated for 40s. After a period of storage in a humid environment for 24 hours at 37°C, the specimens were submitted to the microshear bond strength test. Differences between groups were determined using ANOVA and Tukey's statistical tests at a significance level of 5%. The results showed that the group treated with acid + adhesive using the AdheSE system provided the highest values of microshear bond strength. It can be concluded that laser pretreatment did not affect negatively the bond strength of the self-etching adhesive systems on artificially hypermineralized dentin. / Mestre

Souza, André Mattos de Brito. Avaliação clínica do uso do oxalato de potássio em restaurações de lesões cervicais não-cariosas. 2011. 46 f. Dissertação (Mestrado em Odontologia) - Universidade Federal do Ceará. Faculdade de Farmácia, Odontologia e Enfermagem, Fortaleza, 2011. / Submitted by denise santos (denise.santos@ufc.br) on 2012-11-01T13:32:00Z No. of bitstreams: 1 2011_dis_ambsouza.pdf: 363240 bytes, checksum: 9e5ec280e16cd594f85fd01e044365ff (MD5) / Approved for entry into archive by Erika Fernandes(erikaleitefernandes@gmail.com) on 2012-11-06T13:52:48Z (GMT) No. of bitstreams: 1 2011_dis_ambsouza.pdf: 363240 bytes, checksum: 9e5ec280e16cd594f85fd01e044365ff (MD5) / Made available in DSpace on 2012-11-06T13:52:48Z (GMT). No. of bitstreams: 1 2011_dis_ambsouza.pdf: 363240 bytes, checksum: 9e5ec280e16cd594f85fd01e044365ff (MD5) Previous issue date: 2011 / The aim of this study was to evaluated the efficiency of the use of potassium oxalate (BisBlock - Bisco) in restorations of non-carious cervical lesions. Twenty volunteers patients of both sexes, aged between twenty-four and fifty-five years old, with at least two lesions that were restored with the techniques to be evaluated were selected. Ninety teeth were randomly divided into two groups: Group 1- Restoration with total-etch technique and Group 2 – Restoration with pre-treatment with potassium oxalate followed by application of adhesive system. The adhesive restorative system used was XP Bond (Dentisply) - Durafill (Kulzer). The clinical evaluation was employed USPHS modified method, taking into account the following criteria: retention (R), marginal integrity (MI), marginal discoloration (MD), postoperative sensitivity (S), caries (C), anatomic form (AF). Clinical assessments were conducted by two examiners in the periods baseline, 6 months and 1 year. The intensity of pain sensitivity was assessed before and after treatment using a verbal rating scale. After one year the results of restorations clinically satisfactory (Alfa and Bravo) obtained for the control and experimental group were: R (97% / 89%), MI (100% / 100%), MD (100% / 100%), S (100% / 100%), C (100% / 100%), FA (100% / 100%). The results were analyzed statistically with Kruskal-Wallis and Mann-Whitney tests for levels of sensitivity and the Fisher exact test for the other criteria with a significance level of 5% (p <0.05). Based on statistical analysis, we conclude that the use of potassium oxalate as an agent of dentin pre-treatment did not influence the clinical performance of restorations in non-carious cervical lesions after one year. / Avaliou-se a eficiência do uso do oxalato de potássio (BisBlock – Bisco) em restaurações de lesões cervicais não-cariosas. Para a realização do estudo, foram selecionados vinte pacientes voluntários de ambos os sexos, com idades entre vinte e quatro e cinquenta e cinco anos, com no mínimo duas lesões que foram restauradas com as técnicas a serem avaliadas. Noventa dentes foram aleatoriamente divididos em dois grupos, a saber: Grupo 1 - Restauração pela técnica convencional com o condicionamento ácido total e Grupo 2 - Restauração com pré-tratamento de oxalato de potássio seguido da aplicação do sistema adesivo. O sistema restaurador adesivo empregado foi o XP Bond (Dentisply) – Durafill (Kulzer). Para a realização das avaliações clínicas, foi empregado o método USPHS modificado, levando-se em consideração os seguintes critérios: retenção (R), integridade marginal (IM), descoloração marginal (DM), sensibilidade pós-operatória (S), cárie (C), forma anatômica (FA). As avaliações clínicas foram realizadas por dois avaliadores nos períodos imediato (Baseline), seis meses e um ano. A intensidade da sensibilidade dolorosa foi avaliada antes e após o tratamento utilizando-se uma escala de medida verbal. Ao final de um ano, os resultados de restaurações clinicamente satisfatórios (Alfa e Bravo) obtidos para o grupo controle e experimental foram respectivamente: R (97%/89%), IM (100%/100%), DM (100%/100%), S (100%/100%), C (100%/100%), FA (100%/100%). Os resultados foram submetidos à análise estatística com os testes de Kruskal-Wallis e Mann-Whitney para os níveis de sensibilidade e o exato de Fisher para os demais critérios com o nível de significância de 5% (p<0,05). Com base na análise estatística dos resultados, conclui-se que o emprego do oxalato de potássio como agente de pré-tratamento dentinário não influenciou no desempenho clínico das restaurações de lesões cervicais não-cariosas ao final de um ano.

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2014. / Made available in DSpace on 2015-02-05T20:46:19Z (GMT). No. of bitstreams: 1 327728.pdf: 1775198 bytes, checksum: 71fd40fde69664480e569ccd87e6e444 (MD5) Previous issue date: 2014 / Este estudo teve como objetivo avaliar a resistência de união adesiva sob teste de microtração à dentina humana, comparando um sistema adesivo universal e suas diferentes técnicas de aplicação com um sistema adesivo convencional. Vinte terceiros molares foram divididos aleatoriamente em 4 grupos, variando o sistema adesivo e a técnica de acordo com o fabricante, seguido da reconstrução da porção coronal com resina composta Filtek Z350: G1- Adper Single Bond, com condicionamento ácido; G2- Single Bond Universal, modo autocondicionante; G3- Single Bond Universal, modo condicionamento ácido (dentina úmida); G4-Single Bond Universal, modo condicionamento ácido (dentina ressecada). Para a análise estatística dos dados, foi empregada análise de variância (Anova) (p=0,05). As comparações individuais foram realizadas com teste de diferença significativa de Tukey (HSD) (p=0,05). Os resultados revelaram que não houve diferenças estatísticas entre os grupos avaliados em relação aos valores de microtração. Pode-se concluir que o adesivo Single Bond Universal apresentou resultados estatisticamente semelhantes ao adesivo Adper Single Bond, independentemente do modo utilizado.

MAGALHÃES, Deborah Cavalcante Bezerra. Efeito da remoção de colágeno e da termociclagem na resistência de união de dois adesivos convencionais à dentina. 2014. 51 f. Dissertação (Mestrado em Odontologia) - Universidade Federal do Ceará. Faculdade de Farmácia, Odontologia e Enfermagem, Fortaleza, 2014. / Submitted by denise santos (denise.santos@ufc.br) on 2015-01-29T16:10:53Z No. of bitstreams: 1 2014_dis_dcbmagalhães.pdf: 681863 bytes, checksum: 309eaa2b85d3bbe54840dcef371c12b7 (MD5) / Approved for entry into archive by denise santos(denise.santos@ufc.br) on 2015-01-29T16:13:21Z (GMT) No. of bitstreams: 1 2014_dis_dcbmagalhães.pdf: 681863 bytes, checksum: 309eaa2b85d3bbe54840dcef371c12b7 (MD5) / Made available in DSpace on 2015-01-29T16:13:21Z (GMT). No. of bitstreams: 1 2014_dis_dcbmagalhães.pdf: 681863 bytes, checksum: 309eaa2b85d3bbe54840dcef371c12b7 (MD5) Previous issue date: 2014 / The increase of the adhesive infiltration in the dentin may reduce the gaps in bond interface. The sodium hypochlorite (NaOCl) has been employed for removing the demineralized dentin collagen, transforming it into a more permeable substrate, thus facilitating the diffusion of the adhesive resins intra and intertubular level. Objective: To assess the effect of dentin collagen removal by 10% NaOCl for 60 s on microtensile bond strength of two simplified conventional adhesive systems to this substrate, immediately after or after thermocycling. Methods: Forty freshly extracted third molars had the dentin surface exposed and were divided into four groups according to the type of adhesive solvent used (water/ethanol - Adper Single Bond 2 or acetone - Stae) and the proposed dentin surface treatment (acid-etch or acid-etched + 10% NaOCl). Then, the restoration incrementally with resin Z100 (3M ESPE) was performed. After 24 hours of storage in distilled water at 37 ºC all teeth were sectioned for microtensile test. The specimens in each group were subdivided into two subgroups: immediate test and test after 10,000 cycles. µTBS data were analyzed by two-way ANOVA and Tukey´s test (p<0.05). Failure mode was analyzed and classified as cohesive in dentin, cohesive in resin and mixed/adhesive. Results: The use of NaOCl resulted in a significant decrease on immediate and long-term microtensile bond strength for Single Bond 2 (p<0.001), while Stae was unaffected by the deproteinization and the thermocycling (p=0.194). Conclusion: The collagen removal promoted by 10% NaOCl for 60 s as well as the thermocycling, showed an adverse effect for the water/ethanol-based adhesive. These treatments have no influence on the microtensile bond strength of acetone-based adhesive to dentin. / O aumento da infiltração do adesivo no substrato dentinário pode diminuir as falhas na interface adesiva. O hipoclorito de sódio (NaOCl) tem sido empregado para remoção do colágeno da dentina desmineralizada transformando-a em um substrato mais permeável e facilitando a difusão do adesivo. Objetivo: Avaliar o efeito da remoção do colágeno da dentina por meio da aplicação do NaOCl 10% por 60 s na resistência de união de dois sistemas adesivos convencionais simplificados a esse substrato, de forma imediata ou após envelhecimento por termociclagem. Metodologia: Quarenta terceiros molares recém-extraídos tiveram a dentina superficial exposta e foram divididos em quatro grupos de acordo com o solvente do sistema adesivo utilizado (etanol/água - Adper Single Bond 2 ou acetona - Stae) e o tipo de tratamento da dentina (condicionamento ácido seguido ou não da remoção de colágeno). Platôs foram construídos de forma incremental com a resina composta Z100 (3M-ESPE). Após 24 horas de armazenamento em água destilada a 37ºC, os dentes foram seccionados para o teste de microtração. Os palitos de cada grupo foram subdivididos em dois subgrupos: teste imediato e teste após 10.000 ciclos térmicos. Os dados foram submetidos aos testes de ANOVA two-way e de Tukey (p<0.05). As falhas foram analisadas em lupa e classificadas como coesivas em dentina, coesivas em resina e mistas/adesivas. Resultados: O uso do NaOCl resultou em significante diminuição da resistência de união imediata e após termociclagem para o Single Bond 2 enquanto que o Stae não foi afetado pelo tratamento da dentina ou pela termociclagem. Conclusão: A remoção do colágeno através da aplicação do hipoclorito de sódio, bem como a termociclagem, mostraram efeito adverso para o adesivo convencional de dois passos à base de etanol/água. Tais tratamentos não tiveram influência na resistência de união dos adesivos à base de acetona à dentina.

BARROS, Lívia de Oliveira. Estabilidade da interface de união de sistemas adesivos convencionais aplicados à dentina saturada com alcoóis. 2011. 50 f. Dissertação (Mestrado em Odontologia) - Faculdade de Farmácia, Odontologia e Enfermagem, Universidade Federal do Ceará, Fortaleza, 2011. / Submitted by denise santos (denise.santos@ufc.br) on 2015-10-21T15:16:50Z No. of bitstreams: 1 2011_dis_lobarros.pdf: 840593 bytes, checksum: bb384edc1f750fa69323f9aa3daf978b (MD5) / Approved for entry into archive by denise santos(denise.santos@ufc.br) on 2015-10-21T15:25:42Z (GMT) No. of bitstreams: 1 2011_dis_lobarros.pdf: 840593 bytes, checksum: bb384edc1f750fa69323f9aa3daf978b (MD5) / Made available in DSpace on 2015-10-21T15:25:42Z (GMT). No. of bitstreams: 1 2011_dis_lobarros.pdf: 840593 bytes, checksum: bb384edc1f750fa69323f9aa3daf978b (MD5) Previous issue date: 2011 / There is a consensus that the resin-dentin bond instability is correlated with increased hydrophilic resin monomer content in dentin adhesive. Thus, more durable bonds could be created when more hydrophobic resins were used. One way to bond hydrophobic monomers to acid-etched dentin is saturating the demineralized dentin with ethanol instead of water (ethanol-wet bonding technique). The objective of this in vitro study was to evaluate the effect of “alcohol wet bonding” technique on the stability of adhesive interface produced by two-step etch-and-rinse adhesives systems. For this, it was used 20 human third molars that had superficial dentin exposed and were randomly divided into four experimental groups (n=5): Adper Single Bond 2 (SB) bonded to acid-etched dentin saturated with water or ethanol; and XP Bond (XP) bonded acid-etched dentin saturated with water or 99.5% tert-butanol. The simplified dentin dehydration protocol was performed using 2 μl 100% ethanol or 99.5% tert-butanol directly applied in dentin for 60 s. Composite build-ups were built on dentin surface and specimens were cut into non-trimming dentin-composite beams to microtensile testing. Beams from each tooth were divided equally in two subgroups: immediately tested and aged by immersion in 10% NaOCl solution for 1 h. Specimens were pulled until failure at crosshead speed of 1 mm/min and bond strength was calculated. Fractured sticks were analyzed and classified according to the failure mode as mixed, adhesive, cohesive in dentin and cohesive in composite; and expressed in percentage. Data from μTBS test were statistically analyzed using three-way ANOVA and Tukey tests (α=0.05). Additional dentin disks were bonded using the same groups tested and the morphological characteristics of adhesive interface were investigated by light microscopy after immersion in ammoniacal silver nitrate solution. μTBS results showed that NaOCl solution reduced significantly bond strength comparing with the control groups (p<0.05) and increased the silver nitrate interfacial deposit for all adhesives tested. SB used in ethanol saturated-dentin showed significant lower bond strength values in comparison with SB control group, and this same tendency was observed in the silver nitrate deposition. The use of tert-butanol did not influence XP bond strengths values and silver nitrate deposits. Conclusion: The “alcohol wet bonding” simplified technique used in the present study was not able to improve resin-dentin bond stability for simplified etch-and-rinse adhesive systems. / Existe um consenso de que a instabilidade da interface de união resina-dentina está relacionada com a quantidade de monômeros hidrofílicos presentes no sistema adesivo. Dessa forma, interfaces adesivas mais duradouras seriam alcançadas com a utilização de sistemas adesivos mais hidrofóbicos. Uma maneira de unir monômeros hidrófobos à dentina é através da saturação da matriz dentinária desmineralizada por etanol ao invés de água (ethanol-wet bonding technique). O objetivo deste trabalho in vitro foi avaliar o efeito do protocolo de saturação dentinária, utilizando alcoóis, na estabilidade da interface de união produzida por sistemas adesivos convencionais de dois passos. Para isso, foram utilizados 20 terceiros molares humanos, que tiveram a dentina coronária exposta e foram distribuídos aleatoriamente em quatro grupos experimentais (n=5): Adper Single Bond 2 (SB) aplicado sobre dentina saturada com água ou etanol; e XP Bond (XP) aplicado sobre dentina saturada com água ou tert-butanol. O protocolo de saturação da dentina foi realizado através da aplicação de 2 μl de etanol 100% ou tert-butanol 99,5% diretamente sobre a dentina por um período de 60 s. Um platô de resina composta foi confeccionado sobre superfície dentinária após a aplicação do sistema adesivo e os espécimes foram cortados pela técnica non-trimming de obtenção de palitos para o teste de microtração. Os palitos de cada dente foram igualmente divididos em dois subgrupos: imediatamente testado ou envelhecido em solução de NaOCl a 10% por 1 hora. Os espécimes foram tracionados até a ruptura da união a uma velocidade de 1 mm/min e sua força de união mensurada. Os palitos fraturados foram analisados e classificados de acordo com o modo de fratura em mista, adesiva, coesiva em dentina e coesiva em compósito, e os valores expressos em porcentagem. Os valores de resistência de união foram estatisticamente analisados usando os testes ANOVA a três critérios e Tukey (α=0.05). Discos extras de dentina foram submetidos aos procedimentos adesivos de cada grupo testado e utilizados para investigar as características morfológicas da interface de união através de microscopia óptica após imersão em solução amonical de nitrato de prata. Os resultados do teste de microtração mostraram que a imersão em solução de NaOCl reduziu significativamente a força de união em comparação aos grupos controle (p<0.05) e aumentou a nanoinfiltração das interfaces adesivas de todos os sistemas adesivos testados. A saturação da dentina com etanol 100% reduziu os valores de resistência adesiva para SB quando comparado ao grupo controle, e esta mesma tendência foi observada na infiltração de prata. O uso do tert-butanol 99,5% não afetou os valores de resistência adesiva para o XP, assim como a deposição de nitrato de prata na interface adesiva. Conclusão: Os protocolos simplificados de saturação da dentina com alcoóis utilizados no presente estudo não foram capazes de melhorar a estabilidade da interface de união para sistemas adesivos convencionais de dois passos.

Dissertação (mestrado)—Universidade de Brasília, Faculdade de Ciências da Saúde, Programa de Pós-Graduação em Ciências da Saúde, 2018. / Submitted by Raquel Almeida (raquel.df13@gmail.com) on 2018-05-18T17:29:27Z No. of bitstreams: 1 2018_RaissaCarneiroAntunes.pdf: 57842534 bytes, checksum: c28ca83f1743bbc2e054101b0de749f9 (MD5) / Approved for entry into archive by Raquel Viana (raquelviana@bce.unb.br) on 2018-05-29T18:39:18Z (GMT) No. of bitstreams: 1 2018_RaissaCarneiroAntunes.pdf: 57842534 bytes, checksum: c28ca83f1743bbc2e054101b0de749f9 (MD5) / Made available in DSpace on 2018-05-29T18:39:18Z (GMT). No. of bitstreams: 1 2018_RaissaCarneiroAntunes.pdf: 57842534 bytes, checksum: c28ca83f1743bbc2e054101b0de749f9 (MD5) Previous issue date: 2018-05-29 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES). / Os objetivos do presente estudo consistiram em avaliar in vitro, por meio de teste de condutância hidráulica, a redução da permeabilidade dentinária ao longo do tempo e, por meio de teste de microtração, a resistência de união de sistemas adesivos universais à dentina de sistemas adesivos universais variando-se o modo de aplicação (convencional e autocondicionante) e o tipo de smear layer (espessa e delgada). Foram testados dois sistemas adesivos universais em suas técnicas autocondicionante e convencional: Single Bond™ Universal e Clearfil™ Universal. Como controle positivo foram utilizados os sistemas adesivos: Adper™ Scotchbond Multi-Purpose e o Clearfil™ SE Bond. Cento e vinte terceiros molares humanos foram utilizados, sendo sessenta destinados para cada teste. Para o teste de permeabilidade, os dentes foram seccionados em discos de dentina com auxílio de uma máquina de cortes e, após uma leitura de permeabilidade inicial, os procedimentos adesivos foram executados. As leituras de permeabilidade foram realizadas nos tempos: T0- após remoção da smear layer; T1 – imediatamente ao procedimento adesivo; T2 – 24 horas após ao procedimento adesivo; T3 – 7 dias após ao procedimento adesivo; T4 – 21 dias após ao procedimento adesivo; T5 – 6 meses após ao procedimento adesivo. Foram realizadas moldagem das superfícies adesivas de um espécime de cada grupo e preparo de réplicas em resina epóxica para análise em Microscopia Eletrônica de Varredura (MEV). Para o teste de microtração, os dentes foram seccionados em hemi-dentes, seguida de remoção a parte coronal, expondo dentina. Os procedimentos adesivos foram realizados seguido de restauração em resina composta de 4mm de altura. Com as restaurações prontas, cada hemi-dente foi seccionado em palitos com área adesiva de 0,8mm2. Após um período de 48h, os palitos foram fixados em jigs plásticos e submetidos à teste de microtração. As fraturas foram classificadas em: adesiva, coesiva em dentina, coesiva em resina e mista. Após o término do experimento, alguns palitos de cada tipo de fratura foram levados para metalização seguida de posterior análise em MEV. Os valores de condutância hidráulica foram avaliados ao longo do tempo utilizando o teste two-way ANOVA para medidas repetidas. Observou-se que a interação entre as variáveis tratamento (diferentes sistemas adesivos e tipo de smear layer) e tempo (T1 a T5) foi significativa (p=0.0020), assim como ambas as variáveis isoladamente, sendo o valor de p igual a 0.0279 para a variável tratamento e de 0.0023 para a variável tempo. Até o período T4, não houve diferença entre os grupos experimentais (p >0.05). Entretanto, para o período de avaliação de 6 meses (T5), observou-se um aumento significativo na permeabilidade dentinária Single Bond™ Universal utilizado na técnica autocondicionante associado a smear layer espessa), quando comparados aos demais grupos (two-way ANOVA; p<0.05). As imagens de MEV confirmam esse resultado, uma vez, que para esse grupo foram observadas uma maior quantidade de bolhas de agua na superfície do disco. Os valores de resistência de união foram analisados pelo teste de Kruskall Wallis e não foram observadas diferenças significativas entre os grupos (p=0.078). A partir dos dados obtidos, foi possível concluir que o adesivo Single-Bond Universal apresentou uma redução na sua capacidade de selamento dentinário apos 6 meses quando aplicado sobre smear-layer espessa. / The aims of this study were to evaluate, by hydraulic conductance, the sealing effectiveness over time and the resin-dentin microtensile bond strength of universal adhesive systems in its two techniques (self-etch and etch-and-rinse), ranging the thickness of smear layer (SL - thick and thin). Two universal adhesive systems were tested: Single Bond™ Universal and Clearfil™ Universal. The positive controls were: Adper™ Scotchbond Multi-Purpose and Clearfil™ SE Bond. Sixty human thirdmolars were used for each test. To the hydraulic conductance test, the teeth were sectioned in discs, and after an initial permeability measurement, the adhesive procedures were executed. The hydraulic conductance tests were performed in the following periods: T0 – after removal of smear layer; T1 – immediately after the adhesive application; T2 – 24 hours after the adhesive application; T3 – 7 days after the adhesive application; T4 – 21 days after the adhesive application; T5 – 6 months after the adhesive application. It was performed an impression with silicon of one specimen of each group and epoxy resin replicas were obtained and analyzed in Scanning Electron Microscope (SEM). To the microtensile test, the teeth had their dentin exposed by removing the coronal layer. The adhesive procedures were executed followed by the construction of 4mm composite restorations. The teeth were sectioned obtaining 0,8mm2 resin-dentin sticks, which were fixed in plastic supports and submitted to microtensile test after 48 hours. The fracture modes were categorized in: adhesive, mixed, cohesive failure within dentin and cohesive failure within resin composite. Some sticks were chosen to be observed under SEM. The hydraulic conductance values were analyzed by two-way repeated measures ANOVA. The interaction between the variables treatment (different adhesive systems and smear layer) and time (T1 to T5) were significant (p=0.0020), as so the variables independently (treatment: p=0.0279; time; p=0.0023). Until T4, there weren’t differences between the experimental groups (p>0.05). However, in T5, a significant increase in hydraulic conductance was observed for Single Bond™ Universal in the self-each mode with thick smear layer (two-way ANOVA; P<0.05). The SEM micrographs confirmed the greater amount of bubbles on the disc surface for this group. The microtensile bond strength values were analyzed by Kruskall Wallis and no statistical differences between groups (p=0.078). Based on the present data, it was concluded that Single Bond™ Universal presented a reduction on its ability of dentin sealing after 6 months when applied over a thicker smear-layer.

Dissertação (mestrado)—Universidade de Brasília, Faculdade de Ciências da Saúde, Programa de Pós-Graduação em Ciências da Saúde, 2017. / Submitted by Albânia Cézar de Melo (albania@bce.unb.br) on 2017-09-15T15:13:28Z No. of bitstreams: 1 2017_IngridSilvadeCastro.pdf: 1299627 bytes, checksum: 701360b936a6752f7df1e2489d32082f (MD5) / Approved for entry into archive by Raquel Viana (raquelviana@bce.unb.br) on 2017-09-22T22:36:15Z (GMT) No. of bitstreams: 1 2017_IngridSilvadeCastro.pdf: 1299627 bytes, checksum: 701360b936a6752f7df1e2489d32082f (MD5) / Made available in DSpace on 2017-09-22T22:36:15Z (GMT). No. of bitstreams: 1 2017_IngridSilvadeCastro.pdf: 1299627 bytes, checksum: 701360b936a6752f7df1e2489d32082f (MD5) Previous issue date: 2017-09-22 / O objetivo deste estudo in vitro foi avaliar a resistência de união (RU) à dentina do assoalho da câmara pulpar de diferentes técnicas de preenchimetno coronário e estratégias adesivas. Material e Método: 48 molares humanos foram seccionados perpendicularmente ao longo eixo do dente 1mm acima da margem cervical e o tecido pulpar removido expondo a dentina do assoalho da câmara pulpar. Foram realizados preenchimentos do núcleo coronário pelas técnicas da resina composta (RC) convencional de forma incremental (Z350XT, INC), ou RC bulk fill fluída (Filtek Bulk Flow, BKF) ou RC para preenchimento de polimerização dual (Rebilda, DUAL). Os materiais para preenchimento foram combinados a sistemas adesivos condicione e lave (etch-and-rinse, ER) de 3 passos (Scotchbond Multi Uso Plus, SBMP) ou autocondicionantes (self-etch, SE) universais recomendados pelos fabricantes (Single Bond Universal, SBU, para INC e BKF e FuturaBond U, FBV, para DUAL) formando os grupos experimentais INC/SBMP, INC/SBU, BKF/SBMP, BKF/SBU, DUAL/SBMP e DUAL/FBV. 8 molares foram utilizados para um grupo controle (CTR) em dentina coronária com resina BKF e adesivo SBMP. As amostras foram armazenadas por 24h a 37°C e processadas pelo teste de RU à microtração. Os dados obtidos (em MPa) foram analisados estatisticamente por ANOVA a 2 critérios e teste post hoc de Tukey (α=0,05). Resultados: Não houve efeito estatisticamente significativo para a estratégia adesiva (se ER ou SE) (p=0,147) em dentina do assoalho da câmara pulpar. Quanto às diferentes técnicas de preenchimento coronário houve efeito estatisticamente significativo (p<0,001). A técnica DUAL apresentou os menores valores de RU independente da estratégia adesiva utilizada. Quando comparados à RU obtida em dentina coronária (CRT), apenas INC/SBMP e BKF/SBMP não apresentaram resultados inferiores. Conclusão: Concluiu-se que a técnica de preenchimento coronário influencia a resistência de união à dentina do assoalho da câmera pulpar. A estratégia adesiva, se ER ou SE, não parece influenciar a adesão imediata a esse substrato. / The aim of this in vitro study was to evaluate bond strength to the dentin of the pulp chamber floor of different core build-up techniques and adhesive strategies. Material and Methods: 48 human molars were sectioned perpendicular to the long axis of the tooth 1mm above the cervical margin and the pulp tissue removed exposing the dentin of the floor of the pulp chamber. Coronal core build-ups were performed by incremental conventional composite resin (CR) techniques (Z350XT, INC), or bulk fill CR (Filtek Bulk Flow, BKF) or dual polymerization core build-ups CR (Rebilda, DUAL). Core build-up techniques were combined with 3-step etch-and-rinse (ER) (Scotchbond Multi Purpose Plus, SBMP) or universal self-etch (SE) systems recommended by manufacturers (Single Bond Universal, SBU, for INC and BKF and FuturaBond U, FBV, for DUAL) establishing the experimental groups INC / SBMP, INC / SBU, BKF / SBMP, BKF / SBU, DUAL / SBMP and DUAL / FBV. 8 molars were used for a control group (CRT) in coronal dentin using the BKF tecnique and SBMP adhesive. Samples were stored for 24h at 37°C and processed by the microtensile bond strength test. Data (in MPa) were statistically analyzed by 2-way ANOVA and Tukey post hoc test (α = 0.05). Results: There was no statistically significant effect for the adhesive strategy (ER or SE) (p = 0.147). Regarding the different techniques for core build-up, there was a statistically significant effect (p <0.001). The DUAL resin presented the lowest bond strength values independent of the adhesive strategy. When compared to the bond strenght obtained in coronal dentin (CRT), only INC/SBMP and BKF/SBMP did not present inferior results. Conclusion: It was concluded that the core build-up technique influences bond strength to the dentin of the pulp chamber floor. The adhesive strategy, whether ER or SE, does not seem to influence the immediate adhesion to this substrate.

Tese (doutorado)—Universidade de Brasília, Faculdade de Ciências da Saúde, Programa de Pós-Graduação em Ciências da Saúde, 2016. / Submitted by Fernanda Percia França (fernandafranca@bce.unb.br) on 2016-12-09T16:30:38Z No. of bitstreams: 1 2016_PaulaCostaPinheiroSampaio.pdf: 7882110 bytes, checksum: 38169828ee4fbad7c36ebd77bf3329e8 (MD5) / Approved for entry into archive by Ruthléa Nascimento(ruthleanascimento@bce.unb.br) on 2017-03-14T13:47:16Z (GMT) No. of bitstreams: 1 2016_PaulaCostaPinheiroSampaio.pdf: 7882110 bytes, checksum: 38169828ee4fbad7c36ebd77bf3329e8 (MD5) / Made available in DSpace on 2017-03-14T13:47:16Z (GMT). No. of bitstreams: 1 2016_PaulaCostaPinheiroSampaio.pdf: 7882110 bytes, checksum: 38169828ee4fbad7c36ebd77bf3329e8 (MD5) / O presente estudo teve como objetivo geral avaliar a influência do tempo de polimerização dos sistemas adesivos (SA) no grau de conversão (GC) e na durabilidade resistência da união (RU) entre dentina e adesivo. Para o teste de grau de conversão e para o teste de microtração foram utilizados 5 SA, divididos em grupos: SB – AdperTM Single Bond 2® (3M ESPE - convencional simplificado), OS - Optibond Solo Plus® (Kerr - convencional simplificado), OA – Optibond All in One® (Kerr - autocondicionante simplificado), SU - Adesivo SchotchBond Universal® (3M ESPE - multi-modo, usado como autocondicionante simplificado), CSE – Clearfil SE Bond® (Kuraray - autocondicionante de 2 passos). Os adesivos foram fotopolimerizados com três diferentes tempos de exposição à luz, 10s, 20s e 40s, nos dois testes realizados. O GC dos grupos foi obtido por meio da Espectroscopia Infravermelha de Transmissão de Fourier, por Reflectância (FTIR-ATR). Para o teste de resistência da união, foram utilizados 75 terceiros molares humanos recém extraídos. Os dentes foram cortados no sentido transversal da coroa de modo que a dentina média fosse exposta e depois restaurados seguindo a estratégia adesiva referente a cada grupo, com, resina composta Z350 XT (3M ESPE, St. Paul/MN - EUA). Após a restauração foram armazenados em estufa a 37ºc por 24h, para depois serem cortados na forma de palitos (0,8 x 0,8 mm) e submetidos ao teste de microtração imediato (T0), e após 2 anos de armazenamento em água deionizada, em estufa à 37ºC (T2). Os resultados do GC e da RU foram submetidos à análise de variância a 2 critérios (ANOVA) e ao teste de Tukey (p< 0,05). Para o grau de conversão houve diferença estatisticamente significante para ambos os fatores, tempo de exposição à luz e SA (p<0,05)). Para a RU os resultados em T0 mostraram que um maior tempo de exposição aumenta a resistência adesiva de todos os sistemas testados, com excessão do CSE. Os resultados obtidos em T2 mostraram que o único adesivo que sofreu uma influencia positiva da exposição à luz foi o OA (10s<40s, 10s=20s e 20s=40s). E quando comparados T0 com T2, foi possível observar que houve perda de RU em todos o SA, mas para alguns sistemas o aumento do tempo de exposição melhorou a estabilidade da interface adesiva (OA - 20s e 40s; OS e SU - 40s). Enquanto para outros sistemas esse aumento não favoreceu a estabilidade (CSE e SB) Um maior tempo de polimerização levou a um maior grau de conversão para todos os SA testados, mas não aumentou a RU imediata e a longo prazo de todos os SA, se mostrando material dependente. / The aim of this study was to evaluate the influence of exposure time on degree of conversion (DC) of dental adhesive systems (AS) and on Bond Strength (BS), between dentin and adhesive. For both test, DC and microtensile bond strength (μTBS), five dental adhesives were used, with 3 different exposure time, 10s, 20s and 40s: SB – AdperTM Single Bond 2® (3M ESPE, total-etch 2 steps); OS – Optibond Solo Plus® (Kerr, total-etch 2 steps); OA - Optibond All in One® (Kerr, self-etch, one step); SU – SchotchBond Unviversal ® (3M ESPE, as self-etch, one step); CSE – Clearfil SE Bond® (Kuraray, self-etch, two steps). DC was obteined by FTIR-ATR. For μTBS test, 75 molars were cut to expose midcoronal dentine and then restored with the group adhesive strategy, polymerized for one of the 3 times, built up with resin composite (350 XT, 3M ESPE). Resin-dentine sticks were processed according to non-trimming technique (1 mm2) after storage in deionized water (37ºC) for 24h. Half os the sticks were tested immediately (T0), half were tested after 2 years (T2y) of storage in deionized water (37ºC). The results for DC and μTBS were analyzed by two ways ANOVA and Tukey`s test (p< 0,05). Statistical diferences were observed in degree of conversion for both adhesive tested (p<0,05). For μTBS, at baseline (T0) only SB and SU showed higher μTBS at 40s compared to other curing time. No difference were observed for CSE and OA in overall curing time. OS, at 10s, showed the lowest μTBS compared to other curing time. After 2 years of storage (T2y) no diference were found for SB, SU, OS and CSE according different curing time. OA was the only one that showed lower μTBS at 10s of curing time. When compared T0 to T2y no diference were observed for different time of light exposure for SB, OS, SU and CSE, only to OA, that showed a decrease in μTBS at 10s. Degree of conversion were positively affected by prolonged exposure time, but BS were not improved neither at T0 nor in T2 for all AS, since it showed to be material dependent.