31 |
Restaurações cerâmicas minimamente invasivas executadas por cirurgiões dentistas com diferentes níveis de experiência profissional: estudo clínico cego, longitudinal e prospectivoMelo, Régis Alexandre da Cunha [UNESP] 27 July 2015 (has links) (PDF)
Made available in DSpace on 2016-02-05T18:30:09Z (GMT). No. of bitstreams: 0
Previous issue date: 2015-07-27. Added 1 bitstream(s) on 2016-02-05T18:34:20Z : No. of bitstreams: 1
000857862.pdf: 141657 bytes, checksum: c1cbd779d6d47891f1cd1f7ce4af3ac3 (MD5) Bitstreams deleted on 2016-07-29T12:53:59Z: melo_rac_me_araca.pdf,. Added 1 bitstream(s) on 2016-07-29T12:54:52Z : No. of bitstreams: 1
000857862.pdf: 11011651 bytes, checksum: 5400882cac48c7b0ec5838928d648161 (MD5) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Objetivo: Avaliar a influência da experiência profissional de cirurgiões-dentistas na taxa de sobrevida de restaurações cerâmicas delgadas cimentadas sobre dentes anteriores e/ou posteriores. Material e Método: Um total de 16 profissionais em nível de especialização realizaram tratamentos restauradores com cerâmica delgada, que foram divididos em quatro grupos (n=4) de acordo com o tempo de formação profissional - Grupo 1: recém-formados com até 2 anos de formados; Grupo 2: de 2 a 5 anos de formado; Grupo 3: de 5 a 10 anos de formado; Grupo 4: mais de 10 anos de formado. Todos os profissionais foram instruídos e treinados a seguirem o mesmo protocolo clínico de trabalho, embora desconhecessem os objetivos da pesquisa. Um único avaliador acompanhou os atendimentos clínicos realizados em 24 pacientes, totalizando 274 restaurações unitárias em dissilicato de lítio, sendo 158 na região anterior e 116 na posterior, distribuídas entre os arcos maxilar (186) e mandíbular (88). A espessura das cerâmicas variou entre 0,3 mm e 4,0 mm. As intercorrências ocorridas durante a execução dos protocolos clinicos, bem como os tempos de condicionamento ácido, de fotopolimerização e o tipo de cimento foram anotados. As restaurações foram cimentadas com diferentes cimentos em função da espessura da cerâmica, sendo: Rely X U200 (n=120), Rely X Veneer (n=95) e Variolink Veneer (n=58); totalizando 91 coroas totais, 137 facetas com preparo e 46 facetas sem preparo. As avaliações clínicas foram realizadas após a instalação das restaurações e nos controles de 30, 180, 360 dias posteriores à cimentação. Os parâmetros para a avaliação foram baseados nos critérios modificados do USPHS, adaptados ao estudo. Julgou-se insucesso quando houve fratura ou soltura das restaurações. As fraturas foram replicadas e submetidas à análise... / Objective: To evaluate if the dentist experience can influence the survival rate of cemented anterior and/or posterior thin ceramic restorations. Materials and Methods: A total of 16 professionals with different expertise level with thin ceramic restorations were divided into four groups (n=4) - Group 1: up to 2 years of the graduation; Group 2: 2 to 5 years of graduation; Group 3: 5-10 years of graduation; Group 4: more than 10 years of graduation. All professionals have been educated and trained to follow the same clinical protocol, but were unaware of the research objectives. A single evaluator accompanied the clinical treatments performed in 24 patients, totaling 274 single restorations in lithium disilicate, 158 in the anterior region and 116 in the posterior distributed region among the arches, 186 in the maxillae and 88 in the jaw. The thickness of the ceramic varied between 0.3 mm and 4.0 mm. Minor complications that occurred during the execution of the protocols, the etching and the light curing times and the type of cement were recorded. The restorations were cemented with different cements according to the thickness of ceramic, which: Rely X U200 (n = 120), Rely X Veneer (n = 95) and Variolink® Veneer (n = 58); totaling 91 full crowns, 137 laminated with preparation and 46 laminated with no prepare. Clinical assessments were performed after the installation of the restorations and at the controls of 30, 180 and 360 days after the cementing period. The parameters for evaluation were based on the modified USPHS criteria, adapted to the study. It was deemed unsuccessful when there was fracture or loosening of the restorations. Fractures were replicated and submitted to fractographic analysis. Results: The least number of failures were observed in Group 2 (1 debonding), the largest number in Group 1 (5 fractures) and highest... / FAPESP: 13/11938-0
|
32 |
Análise do comportamento da cor de restaurações cerâmicas sem metal avaliadas por diferentes métodos: estudo clínico prospectivoMartini, Ana Paula [UNESP] 08 September 2015 (has links) (PDF)
Made available in DSpace on 2016-02-05T18:30:14Z (GMT). No. of bitstreams: 0
Previous issue date: 2015-09-08. Added 1 bitstream(s) on 2016-02-05T18:34:24Z : No. of bitstreams: 1
000857916.pdf: 3361545 bytes, checksum: 05e359e822d36e17b2cdd2f6036cc13f (MD5) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Introdução: O processo de interpretação da cor em restaurações cerâmicas delgadas pré e pós-tratamento é um desafio. Os métodos de avaliação dos resultados são diversos e a literatura não é clara em apontar o mais eficaz e eficiente. A questão é ainda mais relevante diante da variação do cimento resinoso utilizado. Proposição: Após variar o tipo de cimento resinoso utilizado, o objetivo deste estudo foi avaliar o comportamento da cor de restaurações cerâmicas em dentes com demanda estética, ao longo de 1 ano após o tratamento, com o auxílio de diferentes métodos de acompanhamento (espectrofotômetro, fotografias, vídeos e avaliação clínica) em um estudo clínico longitudinal e prospectivo. Materiais e Métodos: Foram selecionados 28 pacientes, perfazendo um total de 204 dentes restaurados (89 facetas laminadas, 57 coroas totais ou parciais e 58 lentes de contato). 76 restaurações foram cimentadas com Rely X veneer, 71 com Variolink veneer e 57 com Rely X U200. Foram realizadas mensurações de cor com espectrofotômetro, fotografias digitais e vídeos gravados no decorrer do tratamento e em controles periódicos (inicial, 30 dias, 180 dias e 1 ano após a cimentação). Grupos formados por observadores externos (pacientes, alunos de 1º e último ano de graduação, pós-graduandos e especialistas) avaliaram, aleatoriamente, as imagens obtidas inicialmente e ao final do tratamento, segundo perguntas sobre a satisfação ou não com o resultado estético do caso. Resultados: Os dados obtidos com o espectrofotômetro foram submetidos a testes estatísticos que revelaram diferença significativa apenas entre os tempos avaliados, contudo, para todos os tipos de restauração foi observada estabilidade de cor após, no máximo, 180 dias da cimentação. Não houve diferença estatística entre a satisfação dos diferentes grupos... / Introduction: The process of interpretation of color in thin ceramic restorations pre- and post-treatment is challenging. The evaluation methods of the results are diverse and literature is not clear in pointing out the most effective method. The question is even more relevant given the variation of the resin cement used. Purpose: After changing the type of resin cement used, the aim of this study was to evaluate the color behavior of ceramic restorations in teeth with aesthetic demand, over 1 year after treatment, with the help of different monitoring methods (spectrophotometer, photographs, videos and clinical assessment) in a longitudinal and prospective study. Materials and Methods: 28 patients were selected, for a total of 204 restored teeth (89 veneers, 57 crowns and 58 contact lenses). 76 restorations were cemented with Rely X veneer, 71 with Variolink veneer and 57 with Rely X U200. Color measurements were made with a spectrophotometer, digital photos and videos taken during treatment and periodic controls (initial, 30 days, 180 days and 1 year after cementation). Groups formed by outside observers (patients, students of 1st and last year of undergraduate, graduate students, and experts) evaluated, randomly, images obtained initially and after treatment, according to questions on satisfaction or not with the aesthetic outcome of the case. Results: The data obtained with the spectrophotometer were subjected to statistical tests which showed a significant difference only between the time periods; however, for all types of restoration, color stability was observed after a maximum of 180 days after cementation. There was no statistical difference between the satisfaction of different groups of outsiders observers with the aesthetic result of the cases for both the photos and for videos, although they videos have obtained the highest... / FAPESP: 12/14574-6
|
33 |
Efeito de protocolos de jateamento na resistência à flexão e transformação de fase cristalina em cerâmicas de Y-TZPTurci, Priscilla Cristoforides Pereira [UNESP] 24 April 2014 (has links) (PDF)
Made available in DSpace on 2015-06-17T19:34:49Z (GMT). No. of bitstreams: 0
Previous issue date: 2014-04-24. Added 1 bitstream(s) on 2015-06-18T12:47:01Z : No. of bitstreams: 1
000829403.pdf: 678241 bytes, checksum: e51ad21d05ccf2fa4a8b92a572ce754a (MD5) / O objetivo deste estudo foi avaliar o efeito de diferentes protocolos de jateamento na resistência à flexão biaxial e transformação de fase cristalina de cerâmica policristalina de Y-TZP. Foram confeccionados 740 discos de zircônia estabilizada parcialmente por ítrio - Cercon®Zirconia (DENTSPLY Ceramco, EUA) e In Ceram 2000 YZ cubes (Vita Zahnfabrik, Alemanha) segundo a norma ISO 6872 (15 mm diâmetro x 2 mm espessura). As amostras foram jateadas com partículas de óxido de alumínio (30 μm) revestido por sílica (RocatecSoft - 3M ESPE) e divididas em 74 grupos (n = 10), incluindo-se os grupos controle (ausência de jateamento)(n = 10) para cada cerâmica, de acordo com os fatores: pressão de jateamento (2, 3 e 4 bar); ângulo formado entre a ponta do jateador e a superfície da cerâmica (45º, 60º, 90º); distância do microjateador à cerâmica (5 e 10 mm) e tempo de jateamento (15 s e 20 s). Foi realizado teste de resistência à flexão biaxial em máquina de ensaio universal (1 mm/min, 1000 kg). Os dados (MPa) foram submetidos a análise de variância e ao teste de Duncan. Parte das amostras (n=3) foram submetidas à difração por raios-X (DRX) para quantificação das fases cristalinas e à microcopia eletrônica de varredura (MEV) para análise da topografia superficial. Pressão (p = 0,00) afetou significativamente os resultados, porém tempo (p = 0,49), distância (p = 0,46) e angulação (p = 0,13) não afetaram a Cercon. Já para Vita YZ, a pressão (p = 0,00) foi estatisticamente significante, porém tempo (p=0,66), distância (p = 0,70) e angulação (p=0,14) não foram. Fase monoclínica foi encontrada nos grupos da Cercon (0 a 11%), enquanto para Vita YZ, nenhuma fase foi encontrada. Para Vita YZ, a pressão 3 bar teve maior resistência à flexão biaxial e 4 bar apresentou menor valor. Angulação de 45° associado a 2 bar foi a melhor combinação (1012,21 ± 108,36 MPa)... / The aim of this study was to evaluate the effect of different sandblasting protocols on biaxial flexural strength and crystalline phase transformation in Y - TZP ceramic. 740 discs of Yttria-Partially-Stabilized Zirconia were made - Cercon ® Zirconia (DENTSPLY Ceramco, USA) and In Ceram 2000 YZ cubes (Vita Zahnfabrik, Germany) according to the standards of ISO 6872 (15 mm diameter x 2 mm thick) . The samples were sandblasted with aluminum oxide - coated silica 30 μm (Rocatec Soft - 3M ESPE ) and divided into 74 groups (n = 10 ) , according: pressure (2, 3 and 4 bar) ; nozzle angle (45°, 60°, 90°); nozzle distance (5 and 10 mm) and time (15 s and 20 s) . The biaxial flexural strength on universal testing machine (1mm/min, 1,000 kg) was performed. Data (MPa) were submitted to ANOVA and to Duncan's test (α = 0.05). Samples (n = 2) were subjected to X- ray diffraction to quantify crystalline phases. Pressure (p = 0.00) significantly affected the results, but deposition time (p = 0.49), nozzle distance (p = 0.46) and nozzle angles (p=0.13) did not affect to Cercon ceramic. Pressure (p = 0.00) affected significantly the results to Vita YZ, but deposition time (p = 0.66), nozzle distance (p = 0.70) and nozzle angles (p = 0.14) did not affect. Some monoclinical phase was achieved in Cercon groups (0 a 11%) and none for Vita YZ. For Vita YZ ceramic, 3 bar pressure had the biggest flexural strength value and 4 bar was the worst one and angle 45° associated to 2 bar were the best combination (1012.21 ± 108.36 MPa) compared to 4 bar (556.65 ± 117.41 MPa) (p < 0.001). EDS analysis demonstrated regular superficial grains. SEM images indicated grain size of 0.712 μm (Vita YZ), and 0.705 μm (Cercon). The Cercon density was 98% compared to the theoretical density of zirconia, while VITA YZ was 99%
|
34 |
Estudo da influência das características químicas e microestruturais nas propriedades mecânicas de sistemas totalmante cerâmicosDias, Alexandre Henrique de Moura [UNESP] 29 November 2002 (has links) (PDF)
Made available in DSpace on 2014-11-10T11:09:56Z (GMT). No. of bitstreams: 0
Previous issue date: 2002-11-29Bitstream added on 2014-11-10T11:57:35Z : No. of bitstreams: 1
000200299.pdf: 5347548 bytes, checksum: bfbf67b7f74116d15c5f3e17aa246b7d (MD5) / O propósito deste estudo foi analisar a influência das características químicas e microestruturais nas propriedades mecânicas dos materiais de infra-estrutura (A –lPSEmpress 2 e B - In Ceram Alumina) e de recobrimento estético (C – Empress cerâmico e D -Vitadur Alfa) de sistemas totalmente cerâmicos. Para determinação dos valores dos parâmetros de propriedades mecânicas foram utilizados os ensaios de flexão em quatro pontos, cisalhamento (com e sem ciclagem) e microdurezasuperficialVickers. As superfícies das cerâmicas foram analisadas por dífração de raios X emicroscopia eletrônica de varredura (MEV). Após os ensaios mecânicos, as superfícies de fratura dos materiais A e B e as interfaces A/C e B/Dforam analisadas quimicamente por EDX e microestruturalmente por MEV. Os resultados foram consistentes com a literatura, onde os materiais são compostos de fases cristalinas e C e D são vítreos. Os valores médios de resistência à fratura por flexão foram coerente com os compostos presentes nas cerâmicas e os desvios padrões foram relacionadosà quantidade de defeitos microestruturais. Os tratamentos estatísticos não paramétrico de Kruskal-Wallis e Weibulldestes dados mostraram uma diferença estatisticamente significante do conjunto A/C em relação aos demais materiais, e do B/Dcom o material B. Não foi observada diferença significativa entre os valores de resistência à fratura obtida nos ensaios de cisalhamento estático e por ciclagem mecânica para um mesmo sistema. No ensaio semciclagern mecânica, verificou-se umamaior resistência adesiva para o sistema A/C, que foi associado à formação de interface química / The purpose of this study was 10 analyze the influence of chemical and microestrutural characteristics in the mechanical properties of infrastructurematerials (A –IPS Empress 2 and B - ln Ceram Alumina) and of aesthetic revestiment (C –ceramic Empress and D -VltadurA!fa) of systems all ceramic. Inorder to determine the parameters values for mechanical properties involving 4 points flexural oftest in four points were used, shear bond strength (with andwithout cyclic loading) and Vickers superficialmicrohardness. The ceramic surfaces were analyzed trough X-raydiffraction and scanning electron microscopy (SEM). After the mechanical test, the fracture surfaces of the materials A and B andthe interfaces A/C and B/D were analyzed chemically by EDS andmicrostruturally by SEM. The results complied with the literature,where A and B materials consists of crystalline phases and C andD are vitreous.The average flexure fracture strength values were consistenwiththe present compositions in the ceramic and the standard deviations were related to amount of microstrutural defects. Non parametric statistical treatment refering to Kruskal-Wallis and Weibull and involving these e data evidenced a significant difference in the A/C group compared to the remaining materials, and of B/D group compared to Bmaterial. It was not evidenced significant difference between the fracture strength values originated form the test of static shear bond strength and cyclic loading for one same system. ln the test without cyclic loading, evidenced greater adhesive strengthfor the A/C system andthis was associated to the formation of chemical interface
|
35 |
Cinética de degradação de zircônias odontológicas com alta translucidez / Degradation kinetics of high transluscent dental zirconiasPrado, Pedro Henrique Condé Oliveira 12 January 2018 (has links)
Submitted by Pedro Henrique Conde Oliveira Prado (pedrohcop@hotmail.com) on 2018-01-30T04:57:56Z
No. of bitstreams: 1
PRADO_phco_me_SJC.pdf: 11588382 bytes, checksum: b5aad78aae05251739002f306dd6e1be (MD5) / Approved for entry into archive by Silvana Alvarez null (silvana@ict.unesp.br) on 2018-02-05T12:03:17Z (GMT) No. of bitstreams: 1
prado_phco_me_sjc.pdf: 11588382 bytes, checksum: b5aad78aae05251739002f306dd6e1be (MD5) / Made available in DSpace on 2018-02-05T12:03:17Z (GMT). No. of bitstreams: 1
prado_phco_me_sjc.pdf: 11588382 bytes, checksum: b5aad78aae05251739002f306dd6e1be (MD5)
Previous issue date: 2018-01-12 / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Com o avanço da ciência e processamento de materiais, a zircônia odontológica deixou de ser um material opaco para apresentar certa translucidez, possibilitando a confecção de peças ultrafinas. Sabe-se que a água em contato com a superfície das zircônias convencionais acarreta na transformação de fase T-M e subsequente decréscimo de resistência, mas esses efeitos nas zircônias translúcidas ainda não foram explorados. Para avaliar, mapear e caracterizar os efeitos da cinética de envelhecimento acelerado em zircônias de alta translucidez, foram cortados 39 blocos de Y-TZP (VITA YZ, VITA HT, InCoris TZI) para cada zircônia comercial, onde posteriormente foram sinterizados (1530 ºC, 2h) e atribuídos a 13 grupos com 3 amostras cada: Um controle e 12 envelhecidos hidrotermicamente a 134 ºC com pressão constante de 2 bars por 6, 10, 14, 18, 22, 26, 30, 40, 60, 80, 100 e 140 horas. A análise em DRX foi utilizada para quantificar a transformação de fase da zircônia (tetragonal-monoclínica) em diferentes profundidades do material ao se trocar o ânodo do tubo irradiador (Cr, Co e Cu). Uma curva cinética de envelhecimento foi feita para cada profundidade para as 3 zircônias comerciais. Para avaliar os efeitos do envelhecimento hidrotermal nas propriedades mecânicas, 270 discos de Y-TZP foram cortados, 90 para cada tipo, sinterizados e atribuídos a 3 grupos: C-Controle; E1- envelhecido até 26h e E2- envelhecido até 140 horas. Os discos foram testados em uma máquina de teste universal (EMIC). A microestrutura dos discos foi avaliada sob MEV. As curvas de cinética do envelhecimento funcionaram de forma semelhante para todas as zircônias utilizadas neste estudo, caracterizadas por uma rápida transformação de fase T-M em função do tempo e estabilização de um platô após uma média de 26 horas. As camadas superficiais apresentam concentrações mais elevadas de fase monoclínica à medida em que essa concentração diminuiu em camadas mais profundas. O envelhecimento hidrotermal através de 140h diminuiu a tenacidade da cerâmica VITA YZ em 17% (681,78 ± 121,18) quando comparado ao seu grupo controle (841,69 ± 56,01), enquanto que as zircônias de alta translucidez não mostraram diferenças estatísticas de resistência flexural após o envelhecimento. O envelhecimento hidrotermal induz a transformação da fase martensítica de fora para dentro do material e não afeta as propriedades mecânicas das cerâmicas VITA HT e INCORIS TZI, enquanto diminui a dureza do material da zircônia VITA YZ. / To evaluate, map and characterize the effects of the accelerated aging kinetics of high translucency zirconias, this study was split into 2 parts: One part evaluating the superficial changes after in vitro hydrothermal aging and the second part aiming the effects of this aging on the mechanical properties of those ceramics. 117 Y-TZP (VITA YZ, VITA HT, InCoris TZI) blocks were cut, 39 for each commercial zirconia, sintered (1530 ºC, 2h) and assigned to 13 groups with 3 samples each: One being a control, aging-free group, and 12 groups that were prematurely aged hydrothermally at 134 ºC and constant pressure of 2 bars through 6, 10, 14, 18, 22, 26, 30, 40, 60, 80, 100 and 140 hours. XRD was used to quantify the amount of zirconia phase transformation (tetragonalmonoclinic) on different depths of the material by swapping the anode tube (Cr, Co, and Cu). An aging kinetic curve was made for each depth for the 3 commercial zirconias. To evaluate the effects of the hydrothermal aging on the mechanical properties, Y-TZP blocks were rounded to a cilindrical shape. 270 discs were cut, 90 for each kind, sintered as mentioned above and assigned to 3 groups: C-Control; E1- Aged through 26h and E2- Aged through 140h. Disks were then tested in a universal testing machine (EMIC) under a load of 1000 kg till fracture of the specimen and the surface was evaluated under SEM. The aging kinetics curves work similarly for all the YTZP used in this study, characterized by phase transformation ascendant and plateau stabilization as far as the aging goes. Superficial layers present higher concentrations of monoclinic phase as it decreases in deeper layers. Hydrothermal aging through 140h decreased VITA YZ toughness by 17% (681,78 ± 121,18) when compared with its control group (841,69 ± 56,01), while high translucency zirconias didn't show any statistical differences after aging.Hydrothermal aging does induce martensitic phase transformation from the outside-to-inside the material and doesn't affect the mechanical properties of VITA HT and INCORIS TZI ceramics, while it decreased the material toughness of VITA YZ zirconia. / FAPESP: 16/03688-1
|
36 |
Tenacidade à fratura e dureza de porcelana feldspática adicionada de óxido de zircônio : efeito da concentração e da temperatura de sinterização /Ribeiro, João Gustavo Rabelo. January 2009 (has links)
Resumo: O objetivo deste estudo foi avaliar o efeito da adição de óxido de zircônio, em diferentes concentrações e temperaturas de sinterização, na tenacidade à fratura (KIC) e na dureza Vickers (HV) da porcelana feldspática Duceragold. Foram confeccionados discos cerâmicos (9,0 x 3,0mm; n=10) para os grupos: (G1) Duceragold sem adição de ZrO2, (G2) Duceragold adicionada de 1% de ZrO2, (G3) 2% de ZrO2, (G4) 3% de ZrO2, (G5) 4% de ZrO2, (G6) 5% de ZrO2, (G7) 6% de ZrO2 e (G8) 7% de ZrO2, sinterizados a: (a) 800 ºC, (b) 850 ºC, (c) 900 ºC, (d) 950 ºC e (e) 1000 ºC, totalizando 400 corpos-de-prova. Após a sinterização, em forno Alumini Press, procedeu-se sua inclusão e polimento até lixa 1500 em politriz. A HV foi mensurada em durômetro Buelher, com carga de 9,8 N, por 20 segundos; as imagens obtidas foram capturadas por meio de câmera JVC e os cálculos de KIC, executados com auxílio do software Laica. Para observação da superfície das amostras, foram realizadas fotomicrografias por MEV. Os resultados de KIC e HV foram submetidos a ANOVA e teste de Tukey (p!0,05). Observou-se que, independentemente da temperatura de sinterização, o aumento da concentração de óxido de zircônio, aumenta o KIC, todavia, a partir de 6%, a HV diminui; independentemente da concentração, o aumento da temperatura de sinterização proporciona aumento dos valores de HV, contudo, temperaturas de 950ºC e 1000ºC diminuem o KIC; com o aumento da concentração de óxido de zircônio e da temperatura de sinterização, aumentam o número de poros tanto na fase vítrea da porcelana, quanto na fase dispersa de zircônia. Considerando as propriedades estudadas e a caracterização da superfície, pode-se observar que as amostras com adição de até 4% de óxido de zircônio à porcelana feldspática Duceragold, sinterizadas em temperaturas de até 900ºC apresentam-se como as mais promissoras. / Abstract: The objective of this study was to evaluate the effect of adding zirconium oxide at different concentrations and temperatures of sintering, on the fracture toughness (KIC) and Vickers hardness (HV) of feldspathic porcelain Duceragold. Ceramic discs were prepared (9.0 x 3.0 mm, n = 10) for the groups: (G1) Duceragold without the addition of ZrO2, (G2) Duceragold added 1% of ZrO2, (G3) 2% of ZrO2, (G4) 3% of ZrO2, (G5) 4% of ZrO2, (G6) 5% of ZrO2, (G7) 6% of ZrO2 and (G8) 7% of ZrO2, sintered at: (a) 800 ºC, (b) 850 ºC, (c) 900 ºC, (d) 950 °C and (e) 1000 ºC, totaling 400 specimens of the samples. After sintering at Alumini Press furnace, inclusion and polishing by sandpaper polishing (# 1500) were proceeded. The HV was measured in a Buelher durometer, with a load of 9.8 N for 20 seconds, the images were captured using a JVC camera and calculation of KIC, performed with the aid of software Laica. To observe the surface of the samples were performed by SEM photomicrographs. The results of KIC and HV were submitted to ANOVA and Tukey's test (p ! 0.05). It was observed that regardless of sintering temperature, the concentration of zirconium oxide, increases the KIC, however, from 6%, HV decreases; regardless of the concentration, the increase of sintering temperature gives increased HV values, however, temperatures of 950 °C and 1000 °C decrease the KIC; with increasing concentration of zirconium oxide and sintering temperature, increase the number of pores in the vitreous and dispersed phase of zirconia. Considering the studied properties and characterization of the surface can be observed that the samples with the addition of up to 4% zirconium oxide in Duceragold feldspathic porcelain, sintered at temperatures up to 900 º C are presented as the most promising. / Orientador: Carlos Alberto dos Santos Cruz / Coorientador: José Cláudio Martins Segalla / Banca: Paulo Henrique dos Santos / Banca: Marcos Ribeiro Moysés / Banca: João Neudenir Arioli Filho / Banca: Renata Garcia Fonseca / Doutor
|
37 |
Resistência à flexão, resistência à tração diametral e dureza de sistemas cerâmicos para infra-estrutura /Schalch, Max von. January 2003 (has links)
Orientador: Carlos Alberto dos Santos Cruz / Banca: Renata Garcia Fonseca / Banca: Alma Blásida Concepción Elizaur Benitez Catirse / Resumo: O objetivo deste estudo foi comparar a resistência à flexão, a resistência à tração diametral e a dureza do material de infra-estrutura dos sistemas cerâmicos IPS-Empress 2/Ivoclar (dissilicato de lítio, processado por injeção) e In-Ceram Zirconia/Vita (óxidos de alumínio e zircônio, processados por dupla sinterização). Foram confeccionadas dez amostras de cada material para o ensaio de flexão (em forma de barra, 25mm de comprimento, 5mm de largura, 2mm de espessura - ISO 6872) e 15 amostras para o ensaio de tração diametral (em forma de disco, 6mm de diâmetro, 3mm de espessura). Os testes foram realizados em equipamento MTS 810 (Material Test System - EUA), com célula de carga de 10kN e velocidade de 0,5mm/minuto, gerenciado por programa Test Star II (IBM, EUA). Para o ensaio de dureza, na escala Vickers, cinco fragmentos de cada cerâmica foram incluídos em resina acrílica autopolimerizável JET (Artigos Odontológicos Clássico, Brasil), polidos e submetidos ao teste no durômetro Buheler (EUA), com carga de 1,0kgf por 30 segundos. Os resultados mostraram maior resistência à flexão do material In-Ceram Zirconia (439,88MPa) em relação ao IPS-Empress 2 (226,13MPa). Entretanto, observou-se maior resistência à tração diametral do IPS-Empress 2 (175,08MPa) em relação ao In-Ceram Zirconia (150,47MPa). Para a dureza Vickers, o material In-Ceram Zirconia (972,0VHN) mostrou-se superior em relação ao IPS-Empress 2 (488,33VHN). / Abstract: The aim of this study was to compare flexural strength, diametral tensile strength and hardness of infra-structure ceramic systems IPS-Empress 2/Ivoclar (litium dissilicate, heat-pressed) and In-Ceram Zirconia/Vita (aluminum and zirconium oxides, Slip casting). Ten especimens were made for flexural test (25mm length; 5mm width; 2mm thick - ISO 6872), and 15 especimens for diametral test (6mm diameter; 3mm thick). The tests were done in a MTS 810 machine (Material Test System - USA), with load cell of 10kN and crosshead-speed of 0.5mm/minute, managed by Test Star II software (IBM, USA). Five samples of each ceramic were included in autocured resin JET (Artigos odontológicos Clássico, Brazil), polished and submitted to Vickers hardness test in duromer Buheler (USA), with load of 1.0kgf for 30 seconds. In flexural test, In-Ceram Zirconia (439.88MPa) showed greater strength than IPS-Empress 2 (226.13MPa). However, the IPS-Empress 2 (175.08MPa) showed greater diametral strength than In-Ceram Zirconia (150.47MPa). For hardness, the In-Ceram Zirconia (972.0VHN) showed greater than IPS-Empress 2 (488.33VHN). / Mestre
|
38 |
Resistência de união da interface coping cerâmico pilar de implante variando o agente cimentante antes e após ciclagem térmica / Bond strength of the ceramic coping-implant abutment interface varying luting agent before and after thermal cyclingWashington dos Reis Leite 25 October 2010 (has links)
Objetivo: O objetivo do presente estudo foi avaliar a resistência de união da interface coping cerâmico-pilar de implante variando o agente cimentante antes e após ciclagem térmica. Material e métodos: Foram utilizados quarenta conjuntos de copings cerâmicos e.max - pilar sólido 5.5/ análogo regular, sendo estes divididos aleatoriamente de acordo com o agente cimentante (n=10): (OZ) óxido de zinco sem eugenol; (FZ) fosfato de zinco; (CIV) ionômero de vidro modificado por resina; (RES) resinoso autopolimerizável. O teste de resistência da união à tração foi executado em uma máquina de ensaios universal (Versat 2000-Panambra), com velocidade de 1,0mm/min, antes e após ensaio de envelhecimento por ciclagem térmica. Os resultados foram submetidos ao teste de normalidade e posteriormente a ANOVA (two-way) e teste de Tukey, com nível de significância de 5%. Resultados: Antes da ciclagem térmica, os valores variaram entre o mínimo de 50,77N (OZ) e o máximo de 240,21N (CIV). Não foi observada diferença entre OZ e FZ (60,16N), nem entre CIV e RES (230,36N). Após a ciclagem térmica, os valores foram de no mínimo 3,5N (OZ) e máximo de 330,66N (RES). OZ apresentou resultados estatísticamente inferiores se comparado aos demais, enquanto RES obteve resultados estatísticamente superiores em relação aos demais agentes cimentantes, FZ (90,58N) e CIV (280,43N) apresentaram resultados intermediários. Conclusões: O cimento de óxido de zinco sem eugenol foi associado ao pior desempenho comparado aos demais agentes avaliados antes e após a ciclagem. Antes da ciclagem térmica o maior valor médio obtido foi do ionômero de vidro, enquanto que após a ciclagem o maior valor médio foi do cimento resinoso. O envelhecimento das amostras promoveu inversão dos resultados do ionômero e resinoso, com melhor resultado mecânico para o cimento resinoso. / Objective: The aim of the present study was to evaluate the bond strength of the ceramic coping-abutment implant interface according to the luting agent, before and after thermal cycling. Methods: A total of forty sets of ceramic copings (IPS e.max) and solid pillar 5.5/ regular analogue were divided according to the luting agent (n=10): (OZ) zinc oxide with no eugenol; (ZP) zinc phosphate, (CIV) resin modified glass ionomer, (RES) adhesive resin cement. Tensile bond strength test was performed using a universal testing machine (2000-Versat Panambra) with a speed of 1.0mm/min, before and after thermal cycling. Results were submitted to normality test and then analyzed by ANOVA and Tukey test with significance level of 5%. Results: Prior to thermal cycling, values ranged from 50.77N (OZ) to 240.21N (CIV). No difference was observed between OZ and FZ (60.16N), nor between CIV and RES (230.36N). After thermal cycling, values ranged between 3.5N (OZ) and 330.66N (RES). OZ showed statistically lower mean values compared to the others. RES presented statistically higher mean values in comparison to the other luting agents. FZ (90.58N) and CIV (280.43N) showed intermediate results. Conclusions: Zinc oxide with no eugenol was associated with the worst performance compared to the other agents after thermal cycling. Before thermal cycling the highest mean value was obtained for the glass ionomer. However, after this step, adhesive resin cement showed the highest mean value of bond strength. The sample aging inverted results between ionomer and resin cement, with better mechanical performance for the resin cement.
|
39 |
Efeito do envelhecimento por ciclagem mecânica sobre a resistência à flexão de cerâmicas odontológicas / Effect of aging by mechanical cycling on the flexural strength of dental ceramicsKaren Akemi Fukushima 22 July 2011 (has links)
Os objetivos deste trabalho foram: 1) avaliar o efeito do envelhecimento por ciclagem mecânica (1 milhão de ciclos a uma freqüência de 2 Hz) sobre a resistência à flexão biaxial de três materiais cerâmicos utilizados para a construção infra-estruturas de próteses parciais fixas: a) uma zircônia tetragonal policristalina estabilizada por ítria (Y-TZP); b) uma alumina policristalina (AL) e c) um compósito de alumina e zircônia infiltrado por vidro (ICZ) e 2) determinar a influência da tensão gerada durante a ciclagem sobre a degradação da resistência das cerâmicas estudadas, já que para cada material a ciclagem foi realizada com dois níveis diferentes de tensão. Material e método: Espécimes em forma de disco (12 mm x 2 mm e 12 mm x 1 mm) foram confeccionados conforme as recomendações dos fabricantes. A resistência à flexão desses materiais foi determinada por meio do ensaio de flexão biaxial. Para o grupo controle de todos os materiais estudados (espécimes de 1 mm de espessura), foi realizada estatística de Weibull para determinação da resistência característica (0) e módulo de Weibull (m). Após o envelhecimento por ciclagem mecânica, realizado para todos os materiais nas duas espessuras, os espécimes foram fraturados e os valores obtidos foram comparados com seus respectivos grupos controle. Resultados: O valor de m foi estatisticamente semelhante para todos os materiais, o ICZ (12,2) apresentou o maior valor comparado ao do Y-TZP (9,0) e do AL (8,4). Os valores de resistência característica, 0, apresentaram diferenças significantes para todos os materiais, 828 MPa para a Y-TZP, 405,8 MPa para a AL e 328 MPa para o ICZ. Não houve diferenças estatisticamente significantes entre as resistências medidas para os grupos controle e ciclado para nenhum dos materiais nas duas espessuras avaliadas. Conclusão: O envelhecimento por ciclagem mecânica não causou alterações significativas nos valores de resistência à flexão de nenhuma das cerâmicas testadas. O aumento no nível de tensão aplicada na ciclagem mecânica não gerou um aumento na degradação da resistência dos materiais estudados. / The objectives of this study were: 1) To evaluate the effect of aging by mechanical cycling (1 million cycles at a frequency of 2 Hz) on the biaxial flexural strength of three dental ceramics used as framework materials for fixed partial dentures (FPDs): a) yttria partially stabilized zirconia tetragonal polycrystals (Y-TZP), b) alumina polycrystals (AL) and c) alumina-based zirconia-reinforced glass infiltrated ceramic (ICZ) and 2) determine the influence of stress level generated during mechanical cycling on the flexural strength degradation of the studied ceramics. Materials and Methods: Disc-shaped specimens (12 mm x 2 mm and 12 mm x 1 mm) were prepared according to manufacturer\'s recommendations. The flexural strength of these materials was determined by biaxial flexure test for the control group of all materials. The Weibull statistics was performed to determine the characteristic strength (0) and Weibull modulus (m). After mechanical aging, the specimens were fractured and the values obtained were compared with their respective control groups. Results: No statistically significant differences were founded between the strength obtained for the control and cycled groups for any of the materials in the two thicknesses tested. The m value was similar for all materials, ICZ (12.2) which showed the highest value, followed by the Y-TZP (9) and AL (8.4). The values for characteristic strength (0) showed significant differences for all materials, 828 MPa for Y-TZP, 405.8 MPa for AL and 328 MPa for ICZ. Conclusion: Aging by mechanical cycling did not cause significant changes in the values of flexural strength for all the ceramics tested. The increase in the stress level during cyclic loading did not cause an increase in the strength degradation of the materials studied.
|
40 |
Comportamento mecânico de cerâmicas utilizadas na confecção de próteses parciais fixas / Mechanical behavior of ceramic materials used for fixed partial denturesMarcia Borba 23 June 2010 (has links)
Objetivos: determinar a resistência à flexão em três pontos (f), módulo de Weibull (m), coeficiente de susceptibilidade ao crescimento subcrítico de trinca (n) e tenacidade à fratura (KIC) de três cerâmicas usadas para confecção de infraestrutura (IE) de próteses parciais fixas (PPFs) (YZ- zircônia tetragonal parcialmente estabilizada por óxido de ítrio; IZ- cerâmica a base de alumina infiltrada por vidro e reforçada com zircônia; AL alumina policristalina) e duas porcelanas (VM7 e VM9); avaliar o efeito da configuração (uma, duas ou três camadas) nos valores de f e modo de fratura dos corpos-de-prova (CP); avaliar a influência do material de IE, do tamanho dos conectores e da ciclagem mecânica (CM) na carga de fratura (CF) e distribuição de tensões de PPFs; relacionar o comportamento mecânico dos materiais cerâmicos testados na configuração de barra e de PPF. Material e Método: Foram produzidos três tipos de CP em forma de barra (2mm x 4mm x 16mm): monolítico, duas camadas e três camadas. As IE das PPFs foram confeccionadas utilizando o sistema CAD-CAM e recobertas com porcelana. Os ensaios de f foram realizados em saliva artificial a 37ºC. Os valores de m e n foram determinados pela análise de Weibull e ensaio de fadiga dinâmica, respectivamente. As PPFs foram carregadas no centro do pôntico até a fratura. Oito PPFs de cada grupo foram submetidas a CM com freqüência de 2 Hz e carga de 140 N durante 106 ciclos e, posteriormente, ensaiadas até a fratura. A distribuição de tensões nas PPFs foi avaliada com análise de elementos finitos (AEF). Os princípios da fractografia foram utilizados para determinar o padrão de fratura e os valores de KIC. Os dados de f e CF foram analisados estatisticamente com Kruskal-Wallis e Tukey (95%). Resultados: A YZ obteve o maior valor de f (860 MPa) seguida dos materiais IZ (411 MPa) e AL (474 MPa) que não apresentaram diferença estatística. Os menores valores de f foram encontrados para as porcelanas (65 MPa). Os valores de m foram semelhantes para os materiais, com exceção dos grupos IZ e VM7, que apresentaram diferença significante. Os maiores valores de n foram encontrados para as cerâmicas YZ (76) e AL (72), seguidos pela IZ (54) e pelas porcelanas (40). A YZ apresentou o maior valor de KIC. O material submetido à tensão de tração durante o ensaio determinou o valor de f das estruturas. As PPFs de YZ com conector de 16mm2 suportaram os maiores valores de CF. Houve influência significativa do tamanho de conector para o material YZ. A CM não influenciou os valores de CF das PPFs. O padrão de distribuição de tensões foi semelhante entre as PPFs. Foi observada uma boa relação entre os valores de tensão de fratura dos materiais de IE em forma de barra e de PPF. Foram encontradas diferenças no modo de falha dos CP em forma de barra e de PPF. Conclusão: a YZ apresentou o melhor comportamento mecânico tanto na configuração de barra como de PPF. / Objectives: to determine the flexural strength (f), Weibull modulus (m), slow crack growth coefficient (n) and fracture toughness (KIC) of three ceramics used as framework materials for fixed partial dentures (FPDs) (YZ- yttria partially stabilized zirconia tetragonal polycrystals; IZ- alumina-based zirconia-reinforced glass infiltrated ceramic; AL alumina polycrystals) and two veneering porcelains (VM7 and VM9); to evaluate the effect of the specimen design (one, two or three layers) in the f and fracture mode; to evaluate the influence of the framework material, connector size and mechanical cycling (MC) in the fracture load (FL) and stress distribution of FPDs; to relate the mechanical behavior of the ceramic materials tested using bar-shaped specimens and FPDs. Materials and Methods: Bar-shaped specimens (2mm x 4mm x 16mm) were produced in three different designs: monolithic, bilayer and trilayer. FPD frameworks were built using CAD-CAM system and veneered with porcelain. Specimens were tested for three point bending in 37ºC artificial saliva. Weibull analysis and dynamic fatigue testing were used to determine m and n values, respectively. FPDs were tested with a load applied in the middle of the pontic. Eight FPDs of each group were subjected to MC using a frequency of 2Hz and load of 140N for 106 cycles and were subsequently loaded to failure. Stress distribution for FPDs was evaluated using finite element analysis (FEA). Fractography principles were used to determine the fracture mode and KIC values. f and FL data were analyzed using Kruskal-Wallis and Tukey (95%). Results: YZ had the highest f value (860 MPa) followed by IZ (411 MPa) and AL (474 MPa). Lower f values were observed for the porcelains (65 MPa). Except for IZ and VM7, m values were similar among the ceramic materials. Higher n values were found for YZ (76) and AL (72), followed by IZ (54) and the veneering materials (40). YZ presented the highest KIC value. The f values were influenced by the material subjected to tensile stress during testing. YZ FPDs with 16mm2 connector showed higher FL values. There was significant influence of the connector size on the FL values for YZ material. MC had no influence in the FL values for the FPDs. The stress distribution was similar for all FPDs. Considering the framework material, there was a good agreement between the fracture strength values obtained for bar-shaped specimens and FPDs. Different fracture modes were observed for bar-shaped specimens and FPDs. Conclusion: YZ presented the best mechanical performance in both bar-shaped and FPD specimen configuration.
|