Made available in DSpace on 2014-06-11T19:31:08Z (GMT). No. of bitstreams: 0 Previous issue date: 2007-03-28Bitstream added on 2014-06-13T20:21:57Z : No. of bitstreams: 1 doreaneto_fa_dr_jabo.pdf: 1608125 bytes, checksum: 3f4786116d52404397afbb4ba51cd232 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Objetivou-se nesta pesquisa estudar o comportamento e a bioatividade do cimento de alfa-fosfato tricalcico de dupla pega em artrodeses tarsocrurais. Utilizaram-se seis caes, adultos, macho ou femeas, sem raca definida, com idades entre dois e cinco anos e pesando entre 18 e 30 kg. Foram constituidos dois grupos com 3 animais cada: um grupo onde empregou-se o cimento de ¿-fosfato tricalcico de dupla pega (Grupo I) e outro utilizando osso esponjoso autogeno (Grupo II). A avaliacao radiografica ocorreu aos 30, 45, 60, 90 e 120 dias apos o procedimento cirurgico. Radiograficamente, a fusao dos ossos das articulacoes ocorreu em ambos os grupos apos o 30o dia, sem qualquer reacao adversa ou do tipo corpo estranho. A estabilidade das articulacoes foi satisfatoria com a utilizacao de fixadores esqueleticos externos. Histologicamente, aos 120 dias, observaram-se diferencas na maturidade das celulas osseas entre os dois grupos ocorrendo absorcao lenta e remodelacao da bioceramica (Grupo I). Relativamente a microscopia eletronica de varredura, foi observada formacao de osso novo diretamente na superficie da bioceramica, sem causar formacao de lacuna entre a interface osso-ceramica. O cimento de alfa-fosfato tricalcico de dupla pega demonstrou ter uma boa resistencia mecanica, propriedades de biocompatibilidade, crescimento osseo direto sobre a ceramica, osteoconducao e, ainda, ocorrencia de lenta absorcao quando comparado ao enxerto ósseo. / The purpose of this research was to estuding the behaviour and bioactivity of the á-tricalcium phosphate cement double setting in tarsocrural arthrodesis. Therefore, six canines, both male and female adults mongrel dogs, aged between two and five years old and weighing between 12 and 18kg, were the objects of this study. They were vi divided into two groups with three animals each. On Group I á-tricalcium phosphate cement double setting was used. The Group II, also considered the control group, autogenous cancellous bone graft was used. The periods chosen for the radiographic analysis were 30, 45, 60, 90 and 120 days after surgery. Radiographyc bone fusions on the joints were observed on both groups after 30 days. The stabilization of the joints with external fixators proved to be very satisfactory. No reaction of foreigh body or infection process due to the material used was observed. The histological analysis performed after 120 days after surgery revealed differences in terms of the maturity of the bone cells between the two groups, showing slow absorption and remodelling of the bioceramic (Group I). In terms of the scanning electronic microscopy, bone growth was detected, right on the surface of the bioceramic, without causing gap formation on the bone-ceramic joint. The á-tricalcium phosphate cement double setting demonstrated to have a good mechanical resistance, bioacompatibility properties, direct bone growth on the ceramic and osteocondution and, still, the occurrence of slow absorption when compared to the bone graft.

Made available in DSpace on 2014-06-11T19:31:09Z (GMT). No. of bitstreams: 0 Previous issue date: 2006-05-03Bitstream added on 2014-06-13T20:27:20Z : No. of bitstreams: 1 moraes_pc_dr_jabo.pdf: 795188 bytes, checksum: 42b1e329c08d5dc84c409bddce314a86 (MD5) / Universidade Estadual Paulista (UNESP) / Foi utilizado na presente pesquisa o ultra-som pulsado de baixa intensidade, com a finalidade de avaliar, experimentalmente, seus efeitos sobre a reparação de falhas ósseas produzidas em rádio de coelhos, preenchidas ou não com o cimento de fosfato de cálcio adicionado com fibras de náilon. Foram utilizados 12 coelhos, raça Nova Zelândia, separados em dois grupos experimentais iguais (n=6) e escolhidos aleatoriamente (Grupo Tratado- GT e Grupo Controle-GC). As falhas ósseas de aproximadamente oito milímetros de extensão foram produzidas na diáfise de ambos os rádios, sendo as do membro direito preenchidas com o cimento de fosfato de cálcio sob a forma granulada e as do esquerdo, não preenchidas. Os animais do grupo tratado receberam estímulo pelo ultra-som pulsado de baixa intensidade durante 15 minutos nos primeiros cinco dias e dez minutos nos cinco dias seguintes, em ambos os membros. Os animais do grupo controle não foram estimulados pelo ultra-som. O controle radiográfico foi realizado no pós-operatório imediato e aos sete, 15 e 30 dias, de acordo com o tempo de observação de cada subgrupo (15 e 30 dias). Após o sacrifício, as áreas que continham as falhas ósseas foram processadas para a avaliação histopatológica. Os resultados das análises radiográfica e histolopatológica revelaram uma evolução mais rápida e intensa da proliferação de tecido ósseo nas falhas, preenchidas ou não pelo cimento, porém que receberam estímulo pelo ultra-som. Os resultados obtidos neste trabalho mostraram que o ultra-som pulsado de baixa intensidade é ser um recurso extremamente eficaz na aceleração do processo de ossificação e que, associado ao cimento de fosfato de cálcio com fibras de náilon, tem este processo intensificado, demonstrando, assim, o poder osteoindutor deste biomaterial. / The present experimental research evaluated the effects of low intensity pulsed ultrasound for repair bone defects produced in rabbit's radius, filled in or not with calcium phosphate cement incorporated with nylon fibers. Twelve rabbits, from the New Zealand lineage, were randomly allocated in two equal experimental groups. An eight millimeters bone gap was surgically produced in the radius bone diaphysis and filled with the cement (right radius). The left limb bone gap remained empty. Animais were submitted to dessions of pulsed ultrasonic stimulus for 15 minutes during five days and ten minutes during more five days, in both radius. Radiological examinations were performed in the immediate postoperative and seven, 15 and 30 days after surgery (according with the postoperative follow-up -15 and 30 days). The bone defects were collected and submitted to optical microscopy. The results showed an increase and faster evolution of ossification's process in the bone defects, filled or not with the bone cement, but that received stimulus by ultrasound when compared to the control group. These results suggest that low-intensity pulsed ultrasound is an effective resource for acceleration of the ossification process and, when combined with calcium phosphate cement, this effect was increased.

Made available in DSpace on 2014-06-11T19:31:25Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-07-16Bitstream added on 2014-06-13T19:20:21Z : No. of bitstreams: 1 rocha_dm_dr_sjc.pdf: 501808 bytes, checksum: d965f3ab0fb785017ed14a552084fe08 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / A proposta desse estudo foi avaliar a deflexão cuspídea e a resistência à fratura de pré-molares, com e sem tratamento endodôntico, restaurados com diferentes técnicas e materiais restauradores. Para tal foram utilizados 60 pré-molares hígidos, extraídos por motivos ortodônticos que foram divididos em 6 grupos. Seis dentes foram mantidos hígidos, formando o grupo controle positivo (C POS), outros 6 receberam preparos tipo MOD e não receberam procedimentos restauradores formando o Grupo controle negativo (C NEG). Os demais 48 dentes foram divididos em 4 grupos de 12 dentes que foram restaurados de acordo com cada grupo. No grupo RC os dentes foram restaurados diretamente com resina composta, os demais grupos receberam tratamento endodôntico. No grupo CIV, os dentes tiveram as suas câmaras pulpares preenchidas com cimento de ionômero de vidro e posteriormente restauradas com resina composta, no grupo PM os dentes receberam pinos metálicos e foram restaurados com resina composta e por fim, os dentes do grupo PF receberam pinos de fibra de vidro e foram restaurados diretamente com resina composta. Os corpos-de-prova foram então submetidos a um ensaio não destrutivo de compressão a fim de se realizar a medição de deflexão das cúspides dos dentes de cada grupo e posteriormente, realizou-se o ensaio destrutivo a fim de registrar as medidas de resistência à fratura de cada grupo envolvido. Podem-se perceber diferenças estatisticamente significantes entre os grupos experimentais e os grupos controle, tanto para a deflexão das cúspides (CNEG: 81,0 με; CPOS: 5,20 με; RC: 17,73 με; CIV: 17,63 με; PF: 20,61 με; PM: 24,29 με) quanto para os valores de resistência à fratura (CNEG: 5,212 Kgf; CPOS: 128,22 Kgf; RC: 48,89 Kgf; CIV: 18,41 Kgf; PF: 29,81 Kgf; PM: 37,51 Kgf). Entre os grupos experimentais podem-se notar diferenças estatisticamente significantes... / The aim of this study was to evaluate de cuspal deflection and the fracture resistance of pre-molars, with and without endodontic therapy, using different restorative techniques and materials. Sixty sound teeth, extracted by orthodontic reasons were divided in 6 groups. Six teeth remained unprepared and formed the positive control group, other 6 teeth were MOD prepared and remained unrestored forming the negative control group. The remaining 48 teeth were divided in 4 groups with 12 teeth each and were restored following the groups. The RC group teeth were directly restored with composite resins. The other 3 groups received endodontic therapy. At the CIV group, the pulpal chambers of the endodontic treated teeth were fulfilled with glass ionomer cements an then directly restored with composite resin, the PM group teeth were restored with a metallic post and then directly restored with composite resin, in the PF group were used a fiber glass post and then direct composite restoration. The specimens was submitted first to non-destructive compression test due to cuspal deflection measurements, and then submitted to a destructive compression test to evaluate the fracture resistance of the specimens. Statistical differences were perceived when the experimental groups were compared to the control groups thus cuspal deflection (CNEG: 81,0 με; CPOS: 5,20 με; RC: 17,73 με; CIV: 17,63 με; PF: 20,61 με; PM: 24,29 με) and fracture resistance (CNEG: 5,212 Kgf; CPOS: 128,22 Kgf; RC: 48,89 Kgf; CIV: 18,41 Kgf; PF: 29,81 Kgf; PM: 37,51 Kgf). Differences between the experimental groups were verified both cuspal deflection, with a better performance of the RC and the CIV groups. The PM group showed the highest values of cuspal deflection. Concerning fracture resistance, the highest values were presented by the RC and CIV groups and the worst performance presented... (Complete abstract click electronic access below)

Na engenharia em geral existem técnicas consagradas de construção e materiais com comportamentos exaustivamente estudados para um melhor aproveitamento de suas características a favor do engenheiro. Pode-se dizer que uma construção está cada vez mais integrada com o meio ambiente, tanto na economia de materiais quanto no reaproveitamento dos mesmos. O uso mais racional dos materiais também é uma importante alternativa para minimizar custos em uma obra, tais como transporte, escolha do material mais adequado a ser utilizado, tanto por suas características quanto por sua disponibilidade de uso. Já foram realizadas e ainda hoje têm sido realizadas inúmeras pesquisas sobre solos artificialmente cimentados na Universidade Federal do Rio Grande do Sul, visando seu emprego como camada de suporte para fundações superficiais, no encapsulamento de solos contaminados e como barreiras de contenção de contaminação. Analisando as características mecânicas de areia fina artificialmente cimentada, o objetivo desta pesquisa é verificar a validade do uso do fator vazios/cimento na estimativa da resistência à compressão simples, rigidez inicial, resistência à compressão triaxial em condições drenadas com medidas de G0, comportamento tensão-dilatância e comportamento tensão-deformação da areia de Osório. Para tanto foi verificado que o fator vazios/cimento mostrou-se ser um parâmetro muito eficaz e confiável no que diz respeito à previsão de comportamento do material para dosagem de solo-cimento, em projetos geotécnicos que utilizem a areia de Osório. / In traditional engineering, there are special construction techniques and exhausted studies in materials behavior, for a better employment of it due to the characteristics by the engineer. Today, constructions are increasingly integrated in the environment, both in the economy as in the reuse of materials from them. The more rational use of materials is also important alternative to minimize costs in a work such as transportation, choice of the most appropriate material to be used, either by their characteristics, or their availability for use. Many researches have been made until today on artificially cemented soils in the Federal University of Rio Grande do Sul, targeting their employment as layer of support for foundations surface in the encapsulation of contaminated soil and barriers of contamination containment. Analyzing the mechanical characteristics of fine artificially cemented sand, the objective of this research is to verify the validity of the use of the void/cement ratio in the estimation of the unconfined compressive strength, initial stiffness, triaxial compressive strength in drained conditions with measures of shear modulus (G0), stress-dilatancy behavior and stress-strain behavior of the Osório sand. Thus was verified that the void/cement ratio has proven to be a very effective and reliable parameter regarding prediction of material behavior for soil-cement, dosage in geotechnical projects that use the sand of Osório.

A composição do clínquer controla a cinética da hidratação do cimento, devido às fases potencialmente mais reativas. O aluminato tricálcico (C3A) é a fase que reage mais rápido quando em contato com a água, formando rapidamente os aluminatos de cálcio hidratado (C3AH6, C4AH19 e C2AH8), com a liberação de elevada quantidade de calor. Para casos práticos, o sulfato de cálcio é adicionado ao clínquer para retardar esta reação. Na presença do sulfato de cálcio, o produto formado da reação com o C3A é o trissulfoaluminato de cálcio hidratado (etringita). Geralmente, a forma cristalina do C3A sintetizado durante o processo de clinquerização é cúbica. No entanto, o íon Na+, pode ser incorporado na estrutura cristalina do C3A, em substituição ao Ca2+, levando à modificação da forma cristalina de cúbica para ortorrômbica. Alguns estudos realizados apresentam interessantes resultados sobre a interferência desta fase modificada na hidratação do cimento, afetando o início de pega e a trabalhabilidade da matriz cimentícia. Os maiores problemas são observados em cimentos Portland branco onde, em função da necessidade de redução da quantidade de ferroaluminato tetracálcico (C4AF), ocorre um incremento na quantidade de C3A. Existe uma grande lacuna referente às características específicas de cada aluminato na ausência e na presença de gipsita e hidróxido de cálcio. Desta forma, mostra-se interessante a observação das características das fases do clínquer, principalmente quando se trata dos aluminatos, visto que este seria um passo importante no entendimento dos problemas de início de pega. O presente estudo utiliza fases puras (C3A cúbico e ortorrômbico) sintetizadas em laboratório, para, desta forma, focar as reações independentemente, isolando-as das demais. A associação de diferentes técnicas que possibilitam avaliar a hidratação in situ, com dois métodos originais de análise, utilizando radiações síncrotron, bem como análise de características reológicas e utilização de técnicas clássicas possibilitaram traçar algumas contribuições. Os resultados mostraram que existem grandes diferenças na hidratação de cada aluminato, sendo o ortorrômbico mais reativo nas primeiras idades quando em presença de gipsita, formando primeiramente a etringita. Na ausência de gipsita, o C3A cúbico se mostrou mais reativo, formando primeiro os aluminatos de cálcio hidratados e com maior liberação de calor. O hidróxido de cálcio, saturando a água da mistura, retardou as reações iniciais do C3A ortorrômbico na ausência de gipsita e, em maiores idades, retardou a formação de etringita em pastas de C3A com gipsita e 10% de hidróxido de cálcio. / The clinker composition controls the kinetics of cement hydration mainly due to the presence of potentially more reactive phases. The reaction of tricalcium aluminate C3A with water is almost immediate. Crystalline hydrates, such as C3AH6, C4AH19 and C2AH8 are quickly formed with generation of a large amount of heat. In presence of calcium sulfate, the product formed from the C3A reaction is ettringite or high-sulfate calcium aluminate. The alkalis can be incorporated into a number of phases in the clinker and often Na2O is taken up by the C3A. When C3A is synthesized in the presence of these elements, it changes its crystal lattice and the formation of the orthorhombic phases occurs. Earlier studies have already shown interesting interference from this phase on the cement hydration. Significant problems are found in white Portland cement, where the necessity of reducing the amount of tetracalcium ferroaluminate (C4AF) leads to an increase of the C3A content. There is a large gap in understanding the specific characteristics of each crystalline form of C3A in presence and absence of gypsum and calcium hydroxide. Therefore, characterization of the cement phases is important, especially when it is related to the aluminates (cubic and orthorhombic), since this would be a step to further understand the setting problems. The present study uses pure phases (cubic and orthorhombic C3A) synthesized in laboratory, to focus on the reactions independently, isolating the reactions of the others phases. The experimental research integrated two different synchrotron radiation techniques that enable the study of the hydration in situ with rheological analysis and classical techniques allowing to obtain contributions in the hydration of each C3A. The results showed that there are significant differences in the hydration of each aluminate, and the orthorhombic C3A is more reactive in early ages when in presence of gypsum, by forming ettringite first. In absence of gypsum the cubic C3A was more reactive, forming first calcium aluminates hydrates and generating a higher amount of heat. The ettringite formation and the heat evolution of pastes in presence and absence of gypsum were delayed when calcium hydroxide was present in the mixture.

Sob o ponto de vista de durabilidade, os concretos cromáticos merecem atenção especial, não apenas pelas suas propriedades físicas e químicas, mas principalmente pela sua utilização como elemento arquitetônico, o qual permite a confecção de elementos estruturais aparentes, deixando-os assim mais suscetíveis à ação destrutiva das intempéries. Poucos são os trabalhos publicados que apresentam o comportamento deste material ao longo do tempo e em sua maioria, os pesquisadores avaliam a resistência à compressão como forma de parâmetro de sua qualidade. Neste contexto, o objetivo do trabalho é analisar a influência da adição de pigmentos em algumas propriedades de durabilidade e na cromacidade de concretos de cimento Portland branco. Para isso, montou-se um programa experimental composto por 21 traços diferentes, onde foram realizadas combinações entre 2 tipos de pigmentos inorgânicos de bases químicas diferentes, adicionados em 4 teores (0, 3, 6 e 10%) e com 3 relações a/c (0,40; 0,55 e 0,70). Para cada traço foram moldados 17 cp's os quais se destinam aos ensaios de resistência à compressão, penetração acelerada de cloretos, carbonatação, absorção de água por capilaridade e cromacidade. Todos os resultados experimentais, foram modelados estatisticamente. Os modelos obtidos nos ensaios mostram que o teor de adição e o tipo de pigmento não exercem influência significativa sobre a durabilidade do concreto. O teor de adição, apesar de significativo, pouco alterou a resistência à compressão; houve um acréscimo de cerca de 2 e 5% para os pigmentos verde e vermelho, respectivamente. Quanto à cromacidade; com a adição de 6% do pigmento vermelho o concreto já atinge tonalidades próximas a cor original do pigmento, ao passo que os concretos com pigmentos verde é necessária a adição de 10% para se obter tonalidades mais escuras e mais próximas a cor do pigmento. / Considering the durability of chromatic concrete, one can see it deserves special attention, not only because of its physical and chemical properties, but manly for its use as an architectonic element, which allows the making of apparent structural elements more susceptible to weather destructions. There are few publications reporting the situation of this material towards time, since most of the researchers evaluate the resistance of chromatic concrete to compression as a parameter to its quality. Within this context, the present study aims to analyze the influence of the addition of pigments into some durability proprieties and into the chromaticity of the white Portland cement concrete. An experimental program, with 21 different traces, was designed; combinations between 2 types of inorganic pigments from different chemical bases added with 4 contents (0, 3, 6 and 10%) and with 3 relations a/c (0,40; 0,55 e 0,70) were conducted. For each content, 17 cp’s were molded to the trials of: resistance to compression, chlorite accelerated penetration, carbonation, water absorption due to capillarity, and chromaticity. All the experimental results were statistically molded. The models obtained in the trials show that the addition content and the type of pigment do not exert significant influence upon the durability of concrete. The addition content, although significant, demonstrated a little difference in terms of resistance to compression; there was an increase around 2 and 5% for the green and red pigments, respectively. For chromaticity, the 6% addition of red pigment makes the concrete color similar to the original pigment, whereas the green pigment requires a 10% addition in order to obtain a darker and more similar color to the original green.

O crescimento de células em arcabouços tridimensionais porosos tem se tornado progressivamente ativo na engenharia de tecidos. Os arcabouços guiam o crescimento celular, sintetizam uma matriz extracelular e outras moléculas biológicas, e facilitam a formação de tecidos e órgãos funcionais. Um cimento deste tipo pode ser preparado misturando um sal de fosfato de cálcio com uma solução aquosa para que se forme uma pasta que possa reagir à temperatura corporal dando lugar a um precipitado que contenha hidroxiapatita (Ca10(PO4)6(OH)2). A similaridade química e morfológica entre este biomaterial e a parte mineral dos tecidos ósseos permite a osteocondução, sendo o cimento substituído por tecido ósseo novo com o tempo e com a vantagem de não desencadear processos inflamatórios e de corpo estranho, com eventual expulsão do material implantado. O objetivo do presente trabalho foi a obtenção e caracterização de suportes tridimensionais para a engenharia de tecido, com o uso de matérias-primas nacionais, por meio da utilização de microesferas de parafina como corpos geradores de poros. As microesferas foram produzidas por suspensão em solução aquosa de poli (álcool vinílico) (PVA) e sulfato de sódio (Na2SO4). Foram analisadas as fases presentes no cimento sintetizado e após a reação de cura do mesmo, a variação do tamanho de partícula e da resistência mecânica com o tempo de moagem. Foi analisada a porosidade dos suportes e a forma de extração da parafina daqueles que a utilizaram na sua formação. O tamanho de poro dos suportes gerados com a variação da quantidade de fase líquida ficou aquém do tamanho considerado ideal para o crescimento de tecido ósseo. A porosidade dos arcabouços fabricados com esferas de parafina foi observada por microscopia eletrônica de varredura (MEV), e seu comportamento foi analisado a partir de ensaios in vitro em solução SBF (simulated body fluid) e em cultura de células. A utilização de esferas de parafina permitiu a formação de poros com tamanho tal que possibilitam potencialmente o crescimento tecidual e celular. / The growth of cells in three-dimensional porous scaffolds has been extensively studied for use in tissue engineering. They guide grow of cells, synthesize extra cellular matrix and other biological molecules, and facilitate the formation of functional tissues and organs. Bone cements has been developed for biomedical applications for a decade approximately. This kind of cement can be prepared mixing a calcium phosphate salt with aqueous solution forming a paste that can react at body temperature generating a hydroxyapatite precipitated (Ca10(PO4)6(OH)2). The chemical and morphological similarity between the cement composition and the mineral part of the bones allows osteoconduction in the tissue with replacement of cement by new bone formed with the advantage to not unchain inflammatory processes and of strange body. The objective of this work was the use of the α-TCP cement for making these scaffolds, through the variation of the amount of liquid phase in the cement and of the use of paraffin spheres as pore source. These spheres were produced by suspension in water solution of poly (vinyl alcohol) and sodium sulphate (Na2SO4). The phases had been analyzed in the synthesized cement and after the reaction of cure of cement, beyond variation of the particle size and the resistance mechanics with the milling time. It was analyzed the porosity of the scaffolds and the extraction of the paraffin in that supports. The pore size of the supports generated with the variation of the amount of liquid phase was on this side of the size considered ideal for the bone tissue growth. The porosity of scaffolds manufactured with paraffin spheres was observed by Scanning Electron Microscopy (SEM), and its behavior was analyzed from test in vitro in SBF solution (simulated body fluid). The use of paraffin spheres allowed the formation of pores size able to permit tissue growth.

O presente trabalho avaliou o comportamento hidráulico e reativo de um solo argiloso compactado na energia proctor modificada, com adição de cimento Portland, para fins de aplicação em barreiras impermeáveis de fundo em aterros de resíduos sólidos industriais e de mineração, quando submetido à ação de carga estática de resíduos e em contato com lixiviado ácido enriquecido com os metais cádmio e chumbo. Um Latossolo argiloso residual da cidade de Passo Fundo - RS foi utilizado para moldagem de corpos de prova. A adição de cimento nas proporções de 0% a 2% teve como objetivo melhorar as condições reativas da barreira. Para verificação do comportamento hidráulico foram executados ensaios de condutividade hidráulica. O comportamento reativo foi avaliado por meio de ensaios de difusão, os quais foram realizados com aplicação de carga estática variável (0 kPa a 500 kPa). Soluções contaminantes contendo respectivamente 10 mg/L de cádmio e 10 mg/L de chumbo foram elaboradas com pH variando na faixa de 1 a 6. A partir de ensaio de difusão foram determinados o fator de retardamento (Rd), o coeficiente de distribuição (Kd) e o coeficiente de difusão efetiva (D*), para cada combinação de pH, % cimento e carga estática aplicada. Os resultados obtidos para a mistura compactada investigada indicaram um baixo coeficiente de condutividade hidráulica (<10-9 m/s) e valores que sofreram redução com o acréscimo de cimento. Em relação ao comportamento reativo, os valores de Rd e Kd sofreram incrementos, principalmente com o aumento do pH da solução contaminante, evidenciando o aumento da retenção dos metais. O D* não sofreu influência para os ensaios com Cd e sofreu redução devido à intensa precipitação química em solução que ocorreu devido ao acréscimo de cimento nos ensaios com Pb. A ação conjunta do aumento do pH e da adição de cimento à barreira ocasionou a maior ocorrência de reações de precipitação na barreira, do que reações de adsorção, o que não foi favorável porque possibilita que o contaminante permaneça em solução e possa ser solubilizado em presença de meio ácido. Nesse sentido, a condição que se apresentou mais favorável para o projeto de uma barreira impermeável e reativa foi de 0% de cimento para Pb e 1% de cimento para Cd, as quais desencadearam maiores os valores de Rd e Kd, considerando o contaminante na sua condição mais ácida (pH 1). Em relação à magnitude dos parâmetros Rd e Kd, Pb apresentou maiores valores do que Cd, indicando menor mobilidade. / This study evaluated the hydraulic and reactive behavior of a clayey soil compacted at modified energy proctor, with and without the addition of Portland cement, aiming at its use as containment barriers for industrial and mining solid waste disposal facilities, when subjected to the action of a static load simulating the solid waste mass and to an acid leachate enriched with metals cadmium and lead. A clayey residual Oxisol from Passo Fundo - RS was used for molding specimens. The cement addition in the proportions of 0% to 2% aimed to improve the reactive potential of barrier. Tests of hydraulic conductivity were performed to investigate the hydraulic behavior. The reactive behavior was evaluated through diffusion tests which were conducted with variable static load (0 kPa to 500 kPa). Contaminant solutions were prepared with pH varying from 1 to 6 and 10 mg/L, for both cadmium and lead. The retardation factor (Rd), the distribution coefficient (Kd) and the effective diffusion coefficient (D*) were determined for each combination of pH, % cement and static load. The results obtained showed a low hydraulic conductivity coefficient (<10-9 m/s) and values that decreased with the increasing cement content. Regarding the reactive behavior, the values of Kd and Rd increased mainly with the pH solution increment, causing the increase of metals retention. D* was not affected in the tests with Cd, but was reduced in the tests with Pb, probably by the intense chemical precipitation that occurred due to the cement addition. The combined action of increasing both the pH and the cement addition caused a higher level of precipitation reactions, which allows the contaminant to remain in solution and be solubilized in acid environment. In this sense, the condition which was most favorable for the design of an reactive and impermeable barrier was 0% cement for Pb and 1% cement for Cd, which provided the highest Rd and Kd values, considering the contaminant at its most acidic condition. Regarding the parameters Rd and Kd magnitudes, Pb showed higher values than Cd, indicating less mobility.

Este trabalho visa à quantificação da carbonatação em argamassas de cimento branco em comparação à carbonatação de argamassas de cimento cinza convencional. O estudo experimental foi dividido em 2 fases distintas. Na primeira foram produzidos 12 cimentos pela substituição de 0, 5, 10 e 20% de 3 clínqueres de diferentes procedências por um calcário calcítico. Nesta etapa do trabalho o clínquer e o calcário foram moídos conjuntamente, de forma que não havia controle sobre a granulometria do calcário e do clínquer individualmente. Na segunda fase foram produzidos 21 cimentos, os quais foram constituídos pela adição ao clínquer de 0, 5 10 e 20% do mesmo calcário da primeira fase e de um fíler quartzoso moído de forma a possuir a mesma granulometria do calcário. Nesta etapa os materiais foram previamente moídos, de forma que sua granulometria inicial era controlada, constituindo-se, portanto, 21 cimentos com a mesma finura e 21 argamassas com a mesma relação água/aglomerante. Os resultados dos ensaios de carbonatação, resistência à compressão, porosimetria, termogravimetria, difração de raios-X e análise do pH da solução aquosa dos poros indicam que o calcário tem um efeito potencializador da hidratação das argamassas, com efetivo refinamento da estrutura porosa. Entretanto, a comparação entre os resultados de ambas as fases do estudo mostra que a melhora do desempenho de cimentos acrescidos de calcário não se deve apenas ao efeito de fíler desta adição, mas a uma melhora na eficiência dos cimentos compostos, possivelmente pelo maior moabilidade da mistura clínquer-calcário induzida pelo calcário, isto é, o calcário, quando co-moído com o clínquer, faz com este atinja uma maior superfície específica, aumentando, desta forma, a sua reatividade. Argamassas feitas com cimentos brancos apresentaram menor carbonatação do que argamassas feitas com cimentos cinzas, considerando uma mesma relação água/aglomerante e uma mesma superfície inicial. Os resultados indicam algum tipo de interação química do calcário com a pasta que aumenta a carbonatação, mas este efeito é perceptível para teores elevados de adição. / The present study aims to quantify white cement mortars carbonation when compared to carbonation of conventional gray cement mortars. In the first part of the research, 12 cements were produced by substitution of 0, 5, 10 and 20% of 3 different clinkers by limestone. Clinker and limestone were ground together, so that there was no control over the fineness of limestone and clinker individually. In the second stage of the research 21 cements were produced, which were formed by adding to clinker 0, 5, 10 and 20% of limestone and a crushed quartz filler with the same fineness of limestone. In this second part of the research the materials were first milled, so that their initial particle size was controlled, criating therefore 21 cements with the same finess and 21 mortars with the same water / binder ratio. The test results of carbonation and porosimetry show that limestone has a potentiating effect on mortars hydration with effective refinement of the porous structure. However, the results show that the performance improvement of cement with limestone is not only due to the limestone effect as a filler, but also due to an improvement in the efficiency of blended cements, possibly due to greater efficiency of the clinkers that were milled together with limestone. White cement mortars showed less carbonation than gray cement mortars, assuming the same water / binder ratio and the same initial specific surface. The results show a possible chemical interaction between limestone and the cement paste that eventually increase carbonation depth. This effect was only observable with high addition contents.

O objetivo do presente estudo foi avaliar a remoção da smear layer e a penetração intratubular do cimento obturador AH Plus utilizando diferentes protocolos de irrigação. Após aprovação do Comitê de Ética em Pesquisa da Faculdade de Odontologia de Ribeirão Preto - FORP/USP, noventa incisivos centrais superiores foram selecionados e fornecidos pelo banco de dentes da mesma instituição. Estes foram radiografados no sentido mésio - distal e vestíbulo - lingual para comprovar a presença de canais únicos, sem curvaturas abruptas, reabsorções ou tratamentos endodônticos prévios. Após a remoção da porção coronal para a obtenção de raízes com comprimentos padronizados de 15 milímetros, os diâmetros anatômicos foram determinados e as instrumentações realizadas por meio da técnica coroa ápice estabelecendo os diâmetros cirúrgicos utilizando 3 instrumentos acima dos anatômicos. Durante este processo, os espécimes foram divididos em seis grupos de acordo com os protocolos de irrigação: Grupo 1 (controle - n. 15) - 2,5ml de água destilada a cada troca de instrumentos e 2,5ml de água destilada por 3 minutos ao final da instrumentação; Grupo 2 (n. 15) - 2,5ml de hipoclorito de sódio a 2,5% a cada troca de instrumentos e 2,5ml de hipoclorito de sódio a 2,5% por 3 minutos ao final da instrumentação; Grupo 3 (n. 15) - 2,5ml de hipoclorito de sódio a 2,5% a cada troca de instrumentos e 2,5ml de EDTA a 17% por 3 minutos ao final da instrumentação; Grupo 4 (n. 15) - 2,5ml de hipoclorito de sódio a 2,5% e 2,5ml de EDTA a 17% a cada troca de instrumentos + 2,5ml de EDTA a 17% por 3 minutos ao final da instrumentação; Grupo 5 (n. 15) - 2,5ml de hipoclorito de sódio a 2,5% a cada troca de instrumentos e 2,5ml de ácido cítrico a 10% por 3 minutos ao final da instrumentação; Grupo 6 (n. 15) - 2,5ml de hipoclorito de sódio a 2,5% e 2,5ml de ácido cítrico a 10% a cada troca de instrumentos + 2,5ml de ácido cítrico a 10% por 3 minutos ao final da instrumentação. Após esta fase, cinco espécimes de cada grupo foram clivados no sentido mésio - distal para avaliação da remoção da smear layer em microscopia eletrônica de varredura por meio da análise de 3 imagens de cada terço em aumentos de 300, 1000 e 2000 vezes. Esta variável foi determinada por um score qualitativo estabelecido pelo consenso de 3 avaliadores calibrados. Os demais espécimes foram obturados pela técnica de condensação lateral com cones principais correspondentes ao último instrumento associados ao cimento AH Plus corado com Rodamina B, cones acessórios B8 e mantidos em ambiente com 100% de umidade por 7 dias. Em seguida, os espécimes foram seccionados transversalmente para obtenção de slices de aproximadamente 2mm de espessura em cada terço (cervical, médio e apical) e as faces cervicais submetidas a um tratamento metalográfico para análise da penetração intratubular do cimento obturador em microscopia confocal a laser. Os melhores índices de remoção de smear layer e as maiores porcentagens de penetração intratubular do cimento foram obtidos pelos grupos onde as soluções quelantes foram utilizadas (G3, G4, G5 e G6) com diferenças estatisticamente significantes (p<0,05) em relação aos grupos onde utilizou - se somente a água destilada (G1) e o hipoclorito de sódio a 2,5% (G2) durante o processo de instrumentação. Não foram observadas vantagens em relação ao uso associado do EDTA a 17% e do ácido cítrico a 10% ao hipoclorito de sódio pela ausência de diferenças estatísticas significantes entre os grupos 3 e 4 e 5 e 6, respectivamente. / The aim of this study was to evaluate the smear layer removal and tubular dentine sealer penetration of AH Plus after different irrigation protocols. After approval of the study by the Ethics Committee of the Ribeirão Preto Dental School - FORP/USP, ninety maxillary central incisors were selected and supplied by the tooth bank of the same institution. The teeth were radiographed in the mesiodistal and buccolingual directions to verify the presence of single canals, without abrupt curvatures, resorption or previous endodontic treatment. The coronal portion was removed and roots lengths were standardized at 15 mm. The anatomic diameters were then determined and instrumentations were carried out by the crown-down technique, using 3 higher-diameter instruments to establish the surgical diameters. During this process, the specimens were divided into six groups, according to the following irrigation protocols: Group 1 (control - n. 15) - 2.5ml of distilled water at each change of instruments + 2.5ml of distilled water for 3 minutes at the end of the instrumentation; Group 2 (n. 15) - 2.5ml of 2.5% sodium hypochlorite at each change of instruments + 2.5 ml of 2.5% sodium hypochlorite for 3 minutes at the end of the instrumentation; Group 3 (n. 15) - 2.5ml of 2.5% sodium hypochlorite at each change of instruments + 2.5ml of 17% EDTA for 3 minutes at the end of the instrumentation; Group 4 (n. 15) - 2.5ml of 2.5% sodium hypochlorite and 2.5ml of 17% EDTA at each change of instruments + 2.5ml of 17% EDTA for 3 minutes at the end of the instrumentation; Group 5 (n. 15) - 2.5ml of 2.5% sodium hypochlorite at each change of instruments + 2.5ml of 10% citric acid for 3 minutes at the end of the instrumentation; Group 6 (n. 15) - 2.5ml of 2.5% sodium hypochlorite and 2.5 ml of 10% citric acid at each change of instruments + 2.5 ml of 10% citric acid for 3 minutes at the end of the instrumentation. Following this phase, five specimens from each group were cleaved in the mesiodistal direction to evaluate the smear layer removal by scanning electron microscopy. Evaluation was performed by analyzing 3 images of each third at 300, 1000 and 2000X. This variable was determined by a qualitative score established by the consensus of 3 calibrated examiners. The remaining specimens were filled using lateral condensation with AH Plus sealer labeled with Rhodamine B and kept in an environment with 100% humidity for 7 days. Then, the specimens were sectioned to obtain approximately 2 mm thick slices of each third (cervical, middle and apical). The cervical surfaces were subjected to metallographic treatment for analysis of the tubular dentine sealer penetration by confocal laser microscopy. The highest smear layer removal rates and tubular dentine sealer penetration percentages were obtained by the groups that used chelating solutions (G3, G4, G5 and G6). These showed statistically significant differences (p<0.05) compared with the groups that used just distilled water (G1) and 2.5% sodium hypochlorite (G2) during instrumentation. No benefits were observed for the combined use of 17% EDTA or 10% citric acid with 2.5% sodium hypochlorite, considering that there were no statistically significant differences between groups 3 and 4, and between 5 and 6, respectively.