No description available.

No description available.

Made available in DSpace on 2018-05-09T12:03:29Z (GMT). No. of bitstreams: 1 000488731-Texto+Completo-0.pdf: 9521284 bytes, checksum: c69cc2ad925316be0c15638aac8f5999 (MD5) Previous issue date: 2017 / Carbon geological storage in depleted wells has been identified as an important solution to mitigate the environmental impacts caused by the release of CO2 into the atmosphere. However, the degradation of the materials used in the construction of the wells over the years has been one of the major concerns of the application of this technology, due the possibility of CO2 escape to the surface. The most susceptible region of CO2 leakage is through the wellbore at the interface between the cement paste and rock formation. The degradation of the cement paste occurs due to the presence of CO2 and water or brine, occurring acid carbonation that causes loss on mechanical resistance and increase in porosity. This work aims to study the chemical alteration of the class G cement paste in the presence of arenite rock of the Rio Bonito Formation (Paraná Basin-Brazil) by humid CO2, CO2 saturated water and brine saturated with CO2, simulating the geological storage conditions with a depth of 1,500 m, corresponding to a temperature of 70°C and the pressure of 15MPa. For the degradation test, samples were made by pouring a cement into the hole of an arenite cylinder. The tests were performed in two exposure times, 28 and 180 days, and the chemical degradation of the cement phases was evaluated by Scanning Electron Microscopy (SEM / FEG) and X-Ray Diffraction. The density of cement and rock before and after exposure to CO2 was obtained by pycnometry and the surface area of the rock pores and the diameter of them were evaluated by the BJH method. In addition, the percentage of inorganic carbon present in the rock was determined before and after the degradation tests.The carbonation of the cement was less accelerated in the samples exposed to the saline solution than in the supercritical environment of CO2 and CO2 saturated water, probably due to the decreasing of CO2 solubility in the aqueous medium in the presence of salts and also due to the higher precipitation of carbonate in the pores of the rock that make difficult the CO2 percolation. The density measurements showed that there was an increase in the density of rock and cement (near the interface with the rock) after exposure to CO2 and the density increased with the time of exposure. The surface area of the rock pores, for both times and all mediums, increased after expusure to CO2 due the precipitation of CaCO3, while the radius of the pore have a tendence to decrease. In addition, an increase in the amount of carbon present in the rock after CO2 exposure was observed for the three studied environment and the two exposure times, and a higher amount of carbon was observed for the rock samples exposed to the saline solution, and in this case the carbon content significantly increased from exposure time from 28 days to 180 days. / O armazenamento geológico de carbono em poços depletados tem sido apontado como uma solução importante para a mitigação de impactos ambientais causados pela liberação do CO2 na atmosfera. No entanto, a degradação dos materiais utilizados na construção dos poços ao longo dos anos tem sido uma das maiores preocupações da aplicação desta tecnologia, uma vez que pode favorecer o vazamento do CO2 para a superfície. A região do poço mais suscetível à fuga de CO2 é a interface da pasta de cimento com a formação rochosa. A degradação da pasta de cimento se dá devido a presença de CO2 e água ou salmoura, ocorrendo a carbonatação ácida que gera perda de resistência mecânica e aumento da porosidade. Este trabalho tem como objetivo estudar a alteração química da pasta de cimento classe G em presença da rocha sedimentar arenosa da Formação de Rio Bonito (Bacia do Paraná-Brasil) nos meios de CO2 úmido, água saturada com CO2 e solução salina saturada com CO2, simulando as condições de armazenamento geológico com profundidade de 1.500m, correspondendo a uma temperatura de aproximadamente 70°C e a pressão de 15MPa. Para os ensaios de degradação foram confeccionados corpos de prova constituídos de rocha e cimento. Os ensaios tiveram duração de 28 ou 180 dias e a degradação química das fases do cimento foi avaliada por meio de microscopia eletrônica de varredura (MEV/FEG) e difração de raios X. A densidade do cimento e da rocha antes e após exposição ao CO2 foi obtida por picnometria e a área superficial dos poros da rocha o diâmetro médio dos mesmos foram avaliados pelo método BJH. Além disso, foi determinado o percentual de carbono inorgânico presente na rocha antes e após os testes de degradação.A carbonatação do cimento foi menos acelerada para os corpos de provas expostos à solução salina que nos meios de CO2 supercrítico úmido e água saturada com CO2, provavelmente devido a presença de sais diminuir a solubilidade do CO2 no meio aquoso e também devido a maior precipitação de carbonato nos poros da rocha que dificultaram a percolação do CO2. As medidas de densidade mostraram que houve um aumento na densidade da rocha e do cimento (próximo à interface com a rocha) após exposição ao CO2 e a densidade aumentou com o tempo de exposição ao CO2. A área superficial dos poros da rocha medidas, para ambos os tempos e todos os meios, aumentou com a precipitação de CaCO3 enquanto que o raio médio do poro tendeu a diminuir para a maioria dos casos. Adicionalmente, observou-se um aumento na quantidade de carbono presente na rocha após exposição ao CO2 para os três meios estudados e os dois tempos de exposição, sendo que uma maior quantidade de carbono foi observada para as amostras de rocha expostas à solução salina, sendo que neste caso o teor de carbono aumentou significativamente do tempo de exposição de 28 dias para 180 dias.

A utilização de biomateriais a base de fosfato de cálcio tem revolucionado a medicina no reparo de partes danificadas do sistema ósseo. Dentre estes, os cimentos a base de fosfatos de cálcio de pega hidráulica tem despertado grande interesse em função de sua biocompatibilidade e endurecimento “in situ”, o que permite uma maior facilidade de manipulação e adaptação à forma e dimensões do defeito ósseo. Entretanto, estes cimentos possuem baixa resistência mecânica quando comparados com os ossos do corpo humano. Neste presente trabalho foi estudado a obtenção de pós de cimento de fosfato de cálcio e adicionados a fibras de poli(ácido co-glicólico) (PLGA) e Alginato de Sódio, visando o aumento das propriedades mecânicas destes cimentos. Foi utilizado um novo método de obtenção de fibras por gotejamento em reagente, tanto para o PLGA e o Alginato de Sódio, sendo depois congeladas essas fibras e liofilizadas. Ambos os métodos de obtenção de fibras por gotejamento foram Patenteados, além de publicações em revistas e congressos internacionais. Com este mecanismo foi possível obter-se fibras por método inovador e reforçar a matriz, o que favoreceu o aumento das propriedades mecânicas, permitindo, assim, a obtenção de materiais mais resistentes. Os materiais obtidos foram utilizados na construção de scaffolds para crescimento tecidual, possibilitando manter uma maior integridade mecânica. / The use of biomaterials based on the calcium phosphate has revolutionized the medicine to repair damaged parts of the skeletal system. Among these, the cements based calcium phosphates handle hydraulic has been much interest due to its biocompatibility and hardening "in situ", allowing greater ease of handling and adjustment to the shape and dimensions of the bone defect. However, these cements have lower mechanical strength when compared with the bones of the human body. In the present work to obtain powders of cement of calcium phosphate and added to fibers of poly (co-glycolic acid) (PLGA) and sodium alginate, in order to increase the mechanical properties of these cements. We used a novel method for obtaining fibers in drip reagent for both PLGA and sodium alginate; the fibers are then frozen and lyophilized. Both methods of obtaining fibers were patented drip, as well as publications in international journals and conferences. With this mechanism it was possible to obtain novel method for fibers and strengthen the matrix, thus favoring increased mechanical properties, thus allowing obtaining more resistant materials. The materials were used in the construction of scaffolds for tissue growth, allowing greater maintain mechanical integrity.

Dissertação (mestrado)—Universidade de Brasília, Centro de Estudos Avançados Multidisciplinares, Pós-Graduação em Desenvolvimento Sociedade e Cooperação Internacional, 2013. / Submitted by Alaíde Gonçalves dos Santos (alaide@unb.br) on 2014-01-20T13:44:15Z No. of bitstreams: 1 2013_PriscillaOtoni.pdf: 4280530 bytes, checksum: 4be505e4de6f016436f1a734ee3b8e1a (MD5) / Approved for entry into archive by Guimaraes Jacqueline(jacqueline.guimaraes@bce.unb.br) on 2014-03-31T11:42:26Z (GMT) No. of bitstreams: 1 2013_PriscillaOtoni.pdf: 4280530 bytes, checksum: 4be505e4de6f016436f1a734ee3b8e1a (MD5) / Made available in DSpace on 2014-03-31T11:42:27Z (GMT). No. of bitstreams: 1 2013_PriscillaOtoni.pdf: 4280530 bytes, checksum: 4be505e4de6f016436f1a734ee3b8e1a (MD5) / Esta dissertação de mestrado identifica e analisa as implicações da expansão do capitalismo globalizado para as relações de poder entre Estado, Mercado e Sociedade. Para compreender essa dinâmica, realiza-se um estudo de caso sobre a indústria de cimento no Distrito Federal (DF), localizada na Região Administrativa (RA) Fercal, cujo campo de atuação envolve a interação permanente entre três atores principais. São eles: o poder público, as fábricas, Tocantins e CIPLAN, e as comunidades residentes nas proximidades dos parques industriais. A realidade estudada envolve um contexto de conflito no território, de relações assimétricas de poder e de injustiça e transgressão sócio-ambiental. Os atores considerados, em nível local, representam, por similaridade, o Estado, o Mercado e a Sociedade em âmbito global. Portanto, tendo como pano de fundo das interveniências sistêmicas sob estudo a influência do global no local, considerada a associação da dinâmica da RA Fercal (local) à dinâmica do capitalismo desregulamentado (global), foram realizadas análises para orientar diagnóstico para a seguinte premissa: As relações mantidas entre Estado, Mercado e Sociedade no contexto do capitalismo desregulamentado determinam ou contribuem de modo significativo para a situação de transgressão sócio-ambiental das atividades da indústria de cimento observada na RA Fercal, no DF, e influenciam a atuação do poder público em relação aos problemas locais. Embora a analise envolva os três atores, a pesquisa é desenvolvida com foco na atuação do poder público (Estado), cuja eficácia é colocada em cheque pela persistência, por quase meio século, dos problemas identificados. A partir de análise comparativa entre o processo de expansão capitalista e o processo de segregação sócioambiental na Fercal, verificou-se ser a realidade local fortemente influenciada por fatores exógenos associados ao novo modelo capitalista mundializado, principalmente no que se refere aos processos das fábricas, à atuação do poder público e à interação entre esses atores e a comunidade. Foram identificadas omissões e falhas na gestão do poder público, determinantes, em grande medida, do desajuste social detectado na região. Ao comparar a dinâmica da apropriação e da territorialização do espaço do aglomerado urbano de Brasília (aí compreendida a RA Fercal) com a dinâmica do capitalismo, identificou-se interdependência constante e contínua na produção de “territórios usados”, em qualquer nível e escala, os quais seguem o mesmo modelo civilizatório/desenvolvimentista. Ficou demonstrada a importância da indústria de cimento, basilar para o desenvolvimento do atual modelo civilizatório, ainda que seus processos produtivos e industriais acarretem sérios danos ambientais e, no caso da RA Fercal, também sociais. Por fim, adotando-se como instrumento de análise a Análise do Discurso Crítica (ADC), foi possível perceber construções ideológicas, bem como identificar o modo particular pelo qual os indivíduos partícipes deste estudo, representativos dos três atores analisados, concebem a realidade tratada e utilizam recursos do mundo material para agir e interagir uns com os outros estabelecendo relações de poder por meio do uso da linguagem. _______________________________________________________________________________________ ABSTRACT / Desregulamentado. Análise do Discurso Crítica (ADC). This Master's degree dissertation identifies and analyses the implications of the globalized capitalism expansion for power relationships between State, Market and Society. To understand this dynamics, a case study has been carried out about the cement industry in Distrito Federal (DF), located in the administrative area, called Fercal, which field of activity involves the interaction between three main participants. They are: public authorities, factories Tocantins and Ciplan, and the communities who live around the industrial park. The studied event involves a context of conflict in the area, unequal power and unfair relationships, and yet social and environmental transgression. The participants involved in the study, at local level, represent by similarity, State, Market and Society in global context. Therefore, against a backdrop of systemic intervention, the influence of global on local, and considering the association of Fercal dynamics with the deregulated capitalism dynamics, analyses were carried out in order to make a diagnosis for the following premise: The relationships between State, Market and Society in the context of deregulated capitalism determine or contribute considerably to social and environmental transgression of cement industry activities noticed at Fercal, in DF, and influence the actions of public authorities regarding the local problems. Although the analysis involves three participants, the research is developed with focus on the actions of public authorities (State), which effectiveness is called into question because of the persistance, for almost half century, of the identified problems. From the comparative analysis between capitalism expansion process and social and environmental segregation process at Fercal, it proved to be the local reality strongly influenced by exogenous factors associated with the new globalized capitalist model, especially with regard to the processes of the factories, the actions of the public authorities and the interaction between these participants and the community. Omissions and failures of public authorities management were identified, to a large extent, as decisive factors of social disarrangement detected in the area. By comparing appropriation and territorialization dynamics of Brasília's urban space (including the administrative area Fercal) with capitalism dynamics, it was identified constant and continuous interdependence in the production of "used territories" at any level and scale, which follow the same model of civilization and development. It was demosntrated the importance of the cement industry, which is essential for the development of the current model of civilization, although their industrial and productive processes bring serious environmental damage and, in case of Fercal, also social problems. Finally, using Critical Discourse Analysis (CDA) as an analitical instrument, it was possible to observe ideological constructions, as well as identify how the three participants of this study, who represent the analysed actors, understand the studied reality and how they use features of the material world to act and interact with each other, establishing power relationships through the use of language.

O presente trabalho apresenta os resultados de estudos mineralógicos de seis clinqueres de cimento Portland produzidos comercialmente por indústrias nacionais, com matérias primas domésticas. Esses seis exemplos representam, em verdade, uma seleção de numerosos produtos analisados, por se prestarem melhor às diagnoses dos tipos, condições de preparação e cuidados no controle de matéria prima, bem como dos processos de clinquerização de resfriamento. A parte fundamental deste estudo é desenvolvida por microscopia óptica. Para esse fim são descritas, minuciosamente, as técnicas de amostragem e de preparação das amostras (seções polidas), assim como o uso de reagentes seletivos (\"spot test\") para identificação das fases presentes: Alita - silicato tricálcico (3CaO.Si\'O IND.2\'); Belita - silicato bicálcico (2CaO.Si\'O IND.2\'); Celita - fase intersticial, que pode ser diferenciada em aluminato tricálcico (3CaO.\'Al IND.2\'\'O IND.3\') e ferroaluminato tetracálcico (4CaO.\'Al IND.2\'\'O IND.3\'.\'Fe IND.2\'\'O IND.3\'); componentes secundários - Cal livre (CaO), Periclásio (MgO), fase métalica - metal e seus óxidos e sulfetos. O presente estudo é corroborado por análises químicas, que constituem base para a determinação da composição \"mineralógica\" normativa através dos cálculos propostos por Bogue. Baseados nos conceitos termodinâmicos de equilíbrio entre as fases presentes nos clínqueres, aliados a conceitos mineralógicos-cristalográficos (difusão iônica, reações de estado sólido, soluções sólidas, crescimento cristalino, etc) e a critérios petrográficos (estrutura e textura), o estudo microscópico fornece informações sobre: composição granulometria e homogeneidade da matéria prima (calcáreo e argila); temperatura e tempo de clinquerização; e velocidade de resfriamento do clinquer. É feita uma comparação entre a análise modal obtida por microscopia e a análise normativa calculada a partir das análises químicas, evidenciando as vantagens diagnósticas do método microscópico para definir a composição do clinquer. Conclue-se que: 1. As análises químicas são imprescindíveis no controle rotineiro da matéria prima, permitindo correções imediatas na sua composição. Elas definem ainda, supondo-se um processamento industrial adequado, os módulos de hidraulicidade, de sílica e de fundentes do clinquer. 2. A microscopia, através do estudo das relações paragenéticas e texturais do estabelecimento de uma composição modal, constitui um excelente método de semi-rotina para o controle da fabricação industrial do clinquer, fornecendo, implicitamente, recomendações para melhorar a sua qualidade. / Not available.

Cimentos ósseos são materiais desenvolvidos há aproximadamente uma década para aplicações biomédicas. Um cimento deste tipo pode ser preparado misturando um sal de fosfato de cálcio com uma solução aquosa para que se forme uma pasta que possa reagir à temperatura corporal dando lugar a um precipitado que contenha hidroxiapatita [Ca10(PO4)6(OH)2]. A similaridade química e morfológica entre este biomaterial e a parte mineral dos tecidos ósseos permite a osteocondução, sendo o cimento substituído por tecido ósseo novo com o tempo e com a vantagem de não desencadear rejeição. Estes cimentos são usados principalmente para as operações de preenchimento ósseo, que requer operações cirúrgicas extremamente invasivas. O desafio atual é colocar este biomaterial no local de enxerto pelo método menos agressivo possível. A inovação consiste em formular composição de cimento ósseo injetável pela incorporação de aditivos. No entanto, propriedades como reduzido tempo de cura, limitada dissolução em meio líquido e resistência mecânica adequada ao local do enxerto devem ser preservadas. Neste estudo, foram abordados oito diferentes aditivos que foram incorporados ao fosfato tricálcico [Ca3(PO4)2] sintetizado, juntamente com a solução do acelerador de cura (2,5%massa de Na2HPO4 dissolvido em água destilada): CMC (carboximetilcelulose), polímero de AGAR (polissacarídeo de algas vermelhas), alginato de sódio, quitosana (fibra natural derivada da quitina), pirofosfato de sódio, lignosulfonato de sódio (polissacarídeo de algas marrons), glicerina e ácido láctico nas concentrações 0,4%; 0,8%; 1,6%; 3,2%; 6,4% em massa. Os resultados demonstraram que foi possível obter composições de cimento de fosfato de cálcio injetáveis para uso biomédico. Constatou-se uma relação de proporcionalidade direta entre a injetabilidade do cimento e tempo de injeção, sendo a injetabilidade dependente do comportamento reológico das pastas. Todas formulações testadas seguiram a mesma tendência de redução da resistência mecânica à compressão e aumento da porosidade com o aumento da quantidade de aditivo incorporado. Verificou-se que as formulações com 1,6% de carboxi-metil-celulose, 1,6% de AGAR e 0,8% de alginato de sódio, permitiram a obtenção de uma viscosidade suficiente para uma boa homogeneização e injeção, apresentando ao final da cura resistência mecânica à compressão semelhante ao do osso esponjoso.

O concreto normalmente oferece um alto grau de proteção contra a corrosão ao aço, devido à formação de uma fina película protetora na sua superfície, causada pela alta alcalinidade do concreto. Entretanto, essa película pode ser rompida tanto pela diminuição do pH da solução dos poros do concreto (por carbonatação, por exemplo) ou pela penetração de íons agressivos (como cloretos, por exemplo) até a superfície do aço. O presente trabalho tem por objetivo comparar o desempenho de concretos feitos com diferentes tipos de cimento Portland normalizados no Brasil frente à ação de íons cloreto provenientes de fontes externas. O programa experimental foi realizado com cinco diferentes tipos de cimento (CPII-E, CPII-F, CPIV, CPV ARI e CPV ARI-RS), com e sem adições, e cinco relações água/aglomerante (0,30; 0,35; 0,45; 0,60 e 0,80) em ensaios acelerados de despassivação por cloretos, por meio de ciclos de imersão e secagem dos corpos-de-prova em solução contendo 3,5% de cloreto de sódio. O método de Potencial de Eletrodo foi utilizado para monitorar a corrosão ao longo do tempo. Paralelamente foram realizados ensaios de resistência à compressão do concreto aos 28 dias, de perda de massa da armadura e de teor de cloretos livres no cobrimento da armadura. Os resultados obtidos mostraram que a escolha do tipo de cimento tem influência tanto na resistência à compressão simples quanto na resistência à corrosão das armaduras, verificada através dos ensaios de potencial de eletrodo, de perda de massa gravimétrica da armadura e de teor de cloretos livres. No entanto não houve um tipo de cimento que apresentasse os melhores resultados para todos os tipos de ensaio. / Concrete usually provides a high level of protection against steel corrosion, due to the formation of a fine protecting film on its surface, caused by concrete alkalinity. However, this film can be torn both as a result of the decrease in the pH of the solution of the concrete pores (by carbonation, for example) or as a result of the penetration of aggressive ions (such as chlorides, for example) up to the surface of the steel. The present work has the objective of comparing the performance of concrete made with different kinds of Portland cement regulated in Brazil before the action of chloride ions derived from external sources. The experimental program was performed with five different types of cement (CPII-E, CPII-F, CPIV, CPV ARI and CPV ARI-RS), with and without additions, and five water/agglomerative relations (0.30; 0.35; 0.45; 0.60 and 0.80) in acceleration assays of inactivation by chlorides, by means of immersion cycles and drying of proof bodies in a solution contained 3.5% of sodium chloride. The method of Electrode Potential was used to monitor corrosion over time. Concomitantly, resistance tests were performed as to the compression of the concrete at 28 days, from the loss of mass of the armature and content of free chlorides in the armature coating. The results obtained showed that the selection of the kind of cement has an impact both on the simple compression resistance and on the resistance to armature corrosion, verified through tests of electrode potential, of armature gravimetric mass loss and free chloride content. However, there was not a kind of cement presenting the best results for all types of assay.

A utilização de biomateriais a base de fosfato de cálcio tem revolucionado a medicina no reparo de partes danificadas do sistema ósseo. Dentre estes, os cimentos a base de fosfatos de cálcio de pega hidráulica tem despertado grande interesse em função de sua biocompatibilidade e endurecimento “in situ”, o que permite uma maior facilidade de manipulação e adaptação à forma e dimensões do defeito ósseo. Entretanto, estes cimentos possuem baixa resistência mecânica quando comparados com os ossos do corpo humano. Neste presente trabalho foi estudado a obtenção de pós de cimento de fosfato de cálcio e adicionados a fibras de poli(ácido co-glicólico) (PLGA) e Alginato de Sódio, visando o aumento das propriedades mecânicas destes cimentos. Foi utilizado um novo método de obtenção de fibras por gotejamento em reagente, tanto para o PLGA e o Alginato de Sódio, sendo depois congeladas essas fibras e liofilizadas. Ambos os métodos de obtenção de fibras por gotejamento foram Patenteados, além de publicações em revistas e congressos internacionais. Com este mecanismo foi possível obter-se fibras por método inovador e reforçar a matriz, o que favoreceu o aumento das propriedades mecânicas, permitindo, assim, a obtenção de materiais mais resistentes. Os materiais obtidos foram utilizados na construção de scaffolds para crescimento tecidual, possibilitando manter uma maior integridade mecânica. / The use of biomaterials based on the calcium phosphate has revolutionized the medicine to repair damaged parts of the skeletal system. Among these, the cements based calcium phosphates handle hydraulic has been much interest due to its biocompatibility and hardening "in situ", allowing greater ease of handling and adjustment to the shape and dimensions of the bone defect. However, these cements have lower mechanical strength when compared with the bones of the human body. In the present work to obtain powders of cement of calcium phosphate and added to fibers of poly (co-glycolic acid) (PLGA) and sodium alginate, in order to increase the mechanical properties of these cements. We used a novel method for obtaining fibers in drip reagent for both PLGA and sodium alginate; the fibers are then frozen and lyophilized. Both methods of obtaining fibers were patented drip, as well as publications in international journals and conferences. With this mechanism it was possible to obtain novel method for fibers and strengthen the matrix, thus favoring increased mechanical properties, thus allowing obtaining more resistant materials. The materials were used in the construction of scaffolds for tissue growth, allowing greater maintain mechanical integrity.

Orientador : Gladis Camarini / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Civil / Made available in DSpace on 2018-07-28T20:36:45Z (GMT). No. of bitstreams: 1 DeMilito_JoseAntonio_M.pdf: 10481944 bytes, checksum: a714bee8c0079194a2c251118b5dc6fe (MD5) Previous issue date: 2001 / Resumo: O uso crescente de revestimento de gesso nas edificações tem sido uma alternativa prática e econômica. O gesso tem a vantagem de endurecer rapidamente e proporcionar um acabamento fino, mas está limitado ao uso interno devido à sua sensibilidade a água. Por outro lado, o cimento Portland é um aglomerante que resiste bem em contato permanente com a água. Além disso, com a presença da sílica ativa, suas propriedades são ainda mais favorecidas. Neste sentido, o objetivo deste trabalho foi o de observar as propriedades de pastas das misturas de gesso-cimento Portland-sílica ativa aplicadas em painéis de alvenaria de bloco de concreto submetidos a duas condições: ambiente interno, protegido das intempéries e em ambiente externo sujeito às variações ambientais. Realizaram-se ensaios fisicos, químicos e fisico-químicos. Dos resultados obtidos observou-se que a adição de sílica ativa na mistura reduz a formação de etringita, especialmente nos revestimentos sujeitos à umidade. Da mesma forma, houve melhoria à abrasão e menor perda de massa ao longo do tempo nas misturas com adição de cimento e, após 180 dias de sua aplicação, não houve o aparecimento de fissuras ou gretamento visíveis na superficie dos revestimentos. Assim, os resultados obtidos permitem concluir uma possível coexistência de sucesso entre o gesso e o cimento / Abstract: The growing use of plaster in the constructions has been a practical and economical alternative. The plaster has the advantage of to harden quickly and to provide a fme fmish, but limited to the internal use due to its water sensibility. In other hand, Portland cement is a hydraulic binder and have an excellent behaviour in water. Besides that, silica fume improves its properties. So, the aim of this work was to observe the properties of pastes made from the mixture of plaster-Portland cement-silica fume in concrete block walls. These pastes were submitted to two kinds of expositions: internal and external walls. These pastes were submitted to several tests: physical, chemical and physico-chemical. From these results it was observed that the addition of silica fume diminished the ettringite formation in the walls subjected to humidity. The plaster-Portland cement had the abrasion resistance improved and the weight loss was also diminished. The panels are until now with the same aspects-from the fIrst day of the paste application and there were not observed cracks on them. In this way, its is possible to conclude that the mixture of plaster and Portland cement can be a reality / Mestrado / Edificações / Mestre em Engenharia Civil