Made available in DSpace on 2017-07-24T19:22:11Z (GMT). No. of bitstreams: 1 Giovana Mongruel Gomes.pdf: 1282438 bytes, checksum: 3923d5e2e659866f5b3a3e842b6cceb4 (MD5) Previous issue date: 2010-02-22 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The aim of this study was to evaluate the influence of the operator skill and resin cement system on the bond strength (BS) of glass fiber post to radicular dentin in different root thirds. Forty-eight extracted human upper central incisors were sectioned transversally immediately below the cement-enamel junction and the roots were treated endodontically. After one week, standardized post space cavities were prepared, and the roots randomly divided into two groups (n=24), according to the operator skill: professional (CD) vs academic (AC). The roots were then subdivided into three subgroups (n=8) according to the cementation system: CD1 and AC1 (Adper Scotchbond Multi-Purpose [SBMP] + RelyX ARC [ARC]), CD2 and AC2 (Adper Single Bond 2 [SB] + ARC) and CD3 and AC3 (RelyX U100 [U100]). The glass fiber post (Tenax Fiber Trans Esthetic Post System) were cemented following the manufacturer’s instructions of each cementation system. After water storage at 37o C for one week, each root was sectioned transversely into six 1-mm thick discs and the coronal (TC), middle (TM) and apical (TA) thirds of the root canal identified. A push-out test was carried out at a crosshead speed of 0,5 mm/min. The data were statistically analyzed by ANOVA and post-hoc Tukey's tests (p=0.05). The mean bond strengths (BS) values (MPa) and standard deviations (SD) of each subgroup were: CD1: 12.83±7.26; CD2: 11.46±4.22; CD3: 14.27±6.59; AC1: 9.70±4.37; AC2: 8.02±5.25 and AC3: 13.40±4.93. The BS of the CD and AC groups were 12.85±6.18 and 10.37±5.30, respectively. In regard to the root thirds, the means and SD were: TC: 14.46±5.55; TM: 10.04±5.07 and TA: 10.35±6.01. The mean and SD for the cementation systems were: SBMP + ARC: 11.27±6.13; SB + ARC: 9.74±5.03 and U100: 13.83±5.77. The highest BS means were obtained for CD group (p=0.004); no significant differences were detected among the three cementation systems for CD group (p=0.294); U100 cement reached statistically higher BS than the other cementation systems for AC group (p=0.001). The resin cement U100 was statistically higher than the other materials (p=0.0010) regardless the operator skill. The BS in the cervical third was statistically higher than in the TM and TA (p<0.0001). It can be concluded that the bond strength to the root canal is significantly affected by the operator skill, cementation system and root region. / O propósito desse estudo foi avaliar a influência do operador e do sistema de cimentação na resistência de união (RU) de pino de fibra de vidro à dentina radicular nos diferentes terços radiculares. Quarenta e oito incisivos centrais superiores humanos extraídos foram seccionados transversalmente imediatamente após a junção cemento-esmalte, e as raízes foram tratadas endodonticamente. Após uma semana, foi realizado o preparo padronizado dos condutos, e as raízes foram aleatoriamente divididas em dois grupos (n=24), de acordo com o operador: profissional (CD) vs acadêmico (AC). As raízes foram então subdivididas em três subgrupos cada (n=8) de acordo com o sistema de cimentação: CD1 e AC1 (Adper Scotchbond Multi-Purpose [SBMP] + RelyX ARC [ARC]), CD2 e AC2 (Adper Single Bond 2 [SB] + ARC) e CD3 e AC3 (RelyX U100 [U100]). Os pinos de fibra de vidro (Tenax Fiber Trans Esthetic Post System) foram cimentados de acordo com as recomendações dos fabricantes de cada sistema de cimentação. Após o armazenamento em água a 37o C por uma semana, cada raiz foi seccionada transversalmente em seis discos com 1 mm de espessura, e os terços coronário (TC), médio (TM) e apical (TA) do canal radicular foram identificados. O teste de push-out foi realizado a uma velocidade de 0,5 mm/min. Os dados obtidos foram analisados estatisticamente por meio do teste ANOVA e pós teste de Tukey (p=0,05). Os valores médios de RU (MPa) e desvio padrão (DP) para cada subgrupo foram: CD1: 12,83±7,26; CD2: 11,46±4,22; CD3: 14,27±6,59; AC1: 9,70±4,37; AC2: 8,02±5,25 e AC3: 13,40±4,93. A RU e DP para o grupo dos CD e dos AC foram 12,85±6,18 e 10,37±5,30, respectivamente. Em relação aos terços radiculares, as médias e o DP foram: TC: 14,46±5,55; TM: 10,04±5,07 e TA: 10,35± 6,01. As médias e DP para os sistemas de cimentação foram: SBMP + ARC: 11,27±6,13; SB + ARC: 9,74±5,03 e U100: 13,83±5,77. As maiores médias de RU foram obtidas para o grupo dos CD (p=0,004); não houve diferenças significativas entre os três sistemas de cimentação para o grupo dos CD (p=0,294); o cimento U100 foi estatisticamente superior aos demais sistemas de cimentação para o grupo dos AC (p=0,001). O cimento resinoso U100 foi estatisticamente superior aos demais sistemas de cimentação (p=0,001) independente do operador. A RU no terço coronário foi estatisticamente superior aos TM e TA (p<0,0001). Pode-se concluir que a resistência de união do canal radicular foi significativamente afetada pelo operador, sistema de cimentação e região radicular.

Made available in DSpace on 2017-07-24T19:22:21Z (GMT). No. of bitstreams: 1 Felipe Villa Verde.pdf: 899114 bytes, checksum: 339db35f81d16c1053ac909db81b72f5 (MD5) Previous issue date: 2012-02-27 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The aim of this study was to evaluate in vitro through the push-out test, if the use of opaque glass fiber posts (Exacto – Angelus [PO]) and translucent (Exacto Translucent – Angelus [PT]), adhesively cemented into the root with dual resin cement (Variolink II - Ivoclar Vivadent) under different polymerization time had an influence on the bond strength in three different root canal thirds. Forty-eight singlerooted extracted human premolars were selected from the Tooth Bank UEPG for research. They had their crowns sectioned to form roots with 15 mm in length. All teeth received endodontic treatment and then were divided into 6 groups (n=8), to receive the cementation according to the type of glass fiber post (opaque vs.translucent) and the time of photoactivation of resin cement (20, 40 and 60 seconds). After storage in water at 37° C for one week, the teeth were embedded in acrylic resin and sectioned perpendicular to its long axis to form discs 1 mm thick, with two discs for each root third, and then were taken to the machine universal testing. The push-out test was performed at a speed of 0.5 mm/min. The data were statistically analyzed by ANOVA and Tukey's test (p = 0.05). The mean values of bond strength (MPa) and standard deviation (SD) for groups in the cervical third, middle and apical regions were: PO20 - 21.02 ± 3.52, 15.83 ± 4.94 and 5.20 ± 10:48; PO40 - 14.42 ± 3.98, 12.12 ± 4.40 and 11.59 ± 4.89; PO60 - 16.27 ± 7.14, 13.33 ± 5.22 and 16.99 ± 7.82; PT20 - 18.34 ± 5.47, 10.83 ± 4.63 and 9.98 ± 4.76; PT40 - 17.51 ± 6.55, 14.06 ± 3.85 and 10.95 ± 4.65; PT60 - 19.42 ± 5.86, 15.35 ± 5.43 and 12.77 ± 5.93). There were no significant differences between the types of fiber posts used and the different times of polymerization (p>0.05) in relation to the root area were statistically significant differences only between the cervical and the other thirds (p>0.05). It can be concluded that the bond strength of the root canals was not affected by the type of glass fiber post (opaque vs. translucent) and photoactivation time. / O objetivo deste estudo in vitro foi avaliar por meio do teste de push-out, se a utilização de pinos de fibra de vidro opaco (Exacto – Angelus [PO]) e translúcido (Exacto Translúcido – Angelus [PT]), cimentados adesivamente no canal radicular com cimento resinoso de presa dual (Variolink II – Ivoclar Vivadent) sob diferentes tempos de fotoativação apresentavam influência na resistência de união nos três diferentes terços do canal radicular. Quarenta e oito pré-molares unirradiculares humanos extraídos foram selecionados no Banco de Dentes da UEPG para a pesquisa. Tiveram suas coroas seccionadas para formar raízes com 15 mm de comprimento. Todos os dentes receberam tratamento endodôntico e em seguida foram divididos em 6 grupos (n=8), para receber a cimentação de acordo com o tipo de pino de fibra de vidro (opaco vs translúcido) e com o tempo de fotoativação do cimento resinoso (20, 40 e 60 segundos). Após o armazenamento em água a 37o C por uma semana, os dentes foram embutidos em resina acrílica e seccionados perpendicularmente ao seu longo eixo para formar discos de 1 mm de espessura, sendo 2 discos para cada terço radicular, e em seguida foram levados à máquina de ensaios universal. O teste de push-out foi realizado a uma velocidade de 0,5 mm/min. Os dados obtidos foram analisados estatisticamente por meio do teste ANOVA e pós-teste de Tukey (p=0,05). Os valores médios de RU (MPa) e desvio padrão (DP) para os grupos nos terços cervical, médio e apical foram respectivamente: PO20 – 21,02 ± 3,52, 15,83 ± 4,94 e 10,48 ± 5,20; PO40 – 14,42 ± 3,98, 12,12 ± 4,40 e 11,59 ± 4,89; PO60 – 16,27 ± 7,14, 13,33 ± 5,22 e 16,99 ± 7,82; PT20 – 18,34 ± 5,47, 10,83 ± 4,63 e 9,98 ± 4,76; PT40 – 17,51 ± 6,55, 14,06 ± 3,85 e 10,95 ± 4,65; PT60 – 19,42 ± 5,86, 15,35 ± 5,43 e 12,77 ± 5,93. Não foram observadas diferenças significativas entre os tipos de pino de fibra utilizados e os diferentes tempos de fotoativação (p > 0,05); em relação à região radicular foram encontradas diferenças estatisticamente significativas somente entre o terço cervical e os demais terços (p > 0,05). Pode-se concluir que a resistência de união do canal radicular não foi afetada pelo tipo de pino de fibra de vidro (opaco vs translúcido) e tempo de fotoativação. O objetivo deste estudo in vitro foi avaliar por meio do teste de push-out, se a utilização de pinos de fibra de vidro opaco (Exacto – Angelus [PO]) e translúcido (Exacto Translúcido – Angelus [PT]), cimentados adesivamente no canal radicular com cimento resinoso de presa dual (Variolink II – Ivoclar Vivadent) sob diferentes tempos de fotoativação apresentavam influência na resistência de união nos três diferentes terços do canal radicular. Quarenta e oito pré-molares unirradiculares humanos extraídos foram selecionados no Banco de Dentes da UEPG para a pesquisa. Tiveram suas coroas seccionadas para formar raízes com 15 mm de comprimento. Todos os dentes receberam tratamento endodôntico e em seguida foram divididos em 6 grupos (n=8), para receber a cimentação de acordo com o tipo de pino de fibra de vidro (opaco vs translúcido) e com o tempo de fotoativação do cimento resinoso (20, 40 e 60 segundos). Após o armazenamento em água a 37o C por uma semana, os dentes foram embutidos em resina acrílica e seccionados perpendicularmente ao seu longo eixo para formar discos de 1 mm de espessura, sendo 2 discos para cada terço radicular, e em seguida foram levados à máquina de ensaios universal. O teste de push-out foi realizado a uma velocidade de 0,5 mm/min. Os dados obtidos foram analisados estatisticamente por meio do teste ANOVA e pós-teste de Tukey (p=0,05). Os valores médios de RU (MPa) e desvio padrão (DP) para os grupos nos terços cervical, médio e apical foram respectivamente: PO20 – 21,02 ± 3,52, 15,83 ± 4,94 e 10,48 ± 5,20; PO40 – 14,42 ± 3,98, 12,12 ± 4,40 e 11,59 ± 4,89; PO60 – 16,27 ± 7,14, 13,33 ± 5,22 e 16,99 ± 7,82; PT20 – 18,34 ± 5,47, 10,83 ± 4,63 e 9,98 ± 4,76; PT40 – 17,51 ± 6,55, 14,06 ± 3,85 e 10,95 ± 4,65; PT60 – 19,42 ± 5,86, 15,35 ± 5,43 e 12,77 ± 5,93. Não foram observadas diferenças significativas entre os tipos de pino de fibra utilizados e os diferentes tempos de fotoativação (p > 0,05); em relação à região radicular foram encontradas diferenças estatisticamente significativas somente entre o terço cervical e os demais terços (p > 0,05). Pode-se concluir que a resistência de união do canal radicular não foi afetada pelo tipo de pino de fibra de vidro (opaco vs translúcido) e tempo de fotoativação.

Made available in DSpace on 2017-07-24T19:22:21Z (GMT). No. of bitstreams: 1 lucas m ruiz.pdf: 809225 bytes, checksum: 4f9a5e3d41d46a1259de31458f886bd4 (MD5) Previous issue date: 2012-02-27 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The purpose of this study was to evaluate the influence of root canal sealers on the bond strength (BS) of glass fiber posts to root dentin using two cementation systems, two storage periods and the different root regions. It was used 56 human teeth,healthy canines, transversely sectioned immediately after the cement-enamel junction. Then the roots were divided into two groups (n = 28) according to the sealer (with or without eugenol [Endofill and Sealer 26, respectively]). Subsequently, the roots were subdivided into two subgroups each (n = 14) according to the period of storage before the adhesive cementation, 7 and 180 days. Each subgroup was further again subdivided according to the resin cement to be used, being a conventional dual resin cement (Variolink® II ) and a dual adhesive system (Excite DSC), and the other a dual resin cement autoconditioning and self-adhesive (RelyX™ U100). The glass fiber posts (White Post DC) were cemented according to manufacturer's instructions for each cementation system. All roots were stored for one week after adhesive cementation, and were subsequently sectioned transversely into six discs about 1 mm thick each, and the coronal (CT), middle (MT) and apical (AT) thirds of the root canal identified. The push-out test was carried out at a crosshead speed of 0.5 mm/min. The data were statistically analyzed by ANOVA factorial and post-hoc Tukey`s test (p=0.05). The analysis of variance showed a statistically significant effect for the factors time (F=6.58, p=0.01) and root third (F=26.67, p=0.0005). The specimens that received intra-canal posts 6 months after the endodontic treatment had higher BS than the specimens treated 7 days after endodontic treatment. The AT showed statistically lower BS than those of CT and MT. It can be concluded that the bond strength of fiber posts to root dentin was not affected by the root canal sealers and cementation systems. / O propósito deste estudo foi avaliar a influência dos cimentos endodônticos na resistência de união (RU) de pinos de fibra de vidro à dentina radicular, utilizando dois sistemas de cimentação, dois períodos de armazenamento e as diferentes regiões radiculares. Foram utilizados 56 dentes humanos, caninos hígidos, seccionados transversalmente imediatamente após a junção cemento-esmalte. Em seguida, as raízes foram divididas em dois grupos (n=28) de acordo com o cimento endodôntico (com ou sem eugenol [Endofill e Sealer 26, respectivamente]).Posteriormente, as raízes foram subdivididas em dois subgrupos cada (n=14) de acordo com o período de armazenamento antes da cimentação adesiva, sendo 7 e 180 dias. Cada subgrupo foi novamente subdividido de acordo com o cimento resinoso a ser utilizado sendo um cimento resinoso convencional dual (Variolink II) e sistema adesivo dual (Excite DSC), e outro cimento resinoso dual auto condicionante e auto adesivo (RelyX U100). Os pinos de fibra de vidro (White Post DC) foram cimentados de acordo com as instruções do fabricante de cada sistema de cimentação. Todas as raízes foram armazenadas por uma semana após a cimentação adesiva, e posteriormente seccionadas transversalmente em seis discos de aproximadamente 1 mm de espessura cada, e os terços coronário (TC), médio (TM) e apical (TA) do canal radicular foram identificados. O teste de push-out foi realizado a uma velocidade de 0,5 mm/min. Os dados obtidos foram analisados estatisticamente por meio do teste ANOVA fatorial e pós teste de Tukey (p=0,05). A análise de variância demonstrou um efeito estatisticamente significante para os fatores tempo (F=6,58; p=0,01) e terço radicular (F=26,67; p=0,0005). Os espécimes que receberam pino intra-canal após 6 meses do tratamento endodôntico apresentaram maior RU do que os espécimes tratados após 7 dias do tratamento endodôntico. O TA demonstrou valores de RU estatisticamente inferiores às dos TC e TM. Pode-se concluir que a resistência de união dos pinos de fibra à dentina radicular não foi afetada pelos cimentos endodônticos e sistemas de cimentação.

O objetivo deste estudo foi avaliar a influência do tipo de sistema de cimentação (condicionamento ácido total ou autoadesivo), do modo de ativação (autoativado ou dual), do terço do conduto radicular (cervical, médio ou apical) e da espessura do filme de cimento sobre a resistência de união de pinos de fibra de vidro cimentados em dentes humanos. Quarenta raízes foram incluídas em resina epóxi, submetidas a tratamento endodôntico e obturadas com guta percha e cimento endodôntico sem eugenol. Decorridos sete dias, os condutos foram preparados a uma profundidade de 10mm com brocas padronizadas do sistema dos pinos de fibra (WhitePost DC #2) e aleatoriamente divididos em 4 grupos, conforme o sistema de cimentação e o modo de ativação: (G1) RelyX ARC/Adper Scotchbond Multi-Purpose Plus (condicionamento ácido total), ativação dual, (G2) RelyX ARC/Adper Scotchbond Multi-Purpose Plus, autoativado, (G3) RelyX U100 (autoadesivo), dual e (G4) RelyX U100, autoativado. Após uma semana, cada raiz foi seccionada em máquina de corte, originando 6 fatias de 1 mm de espessura (n=60). Antes do ensaio de push-out cada fatia foi fotografada em ambas as faces, para determinação do raio dos pinos e da espessura do filme de cimento. Após o ensaio mecânico, novas imagens foram capturadas para determinação do modo de falha. Para automatizar a determinação da espessura de cimento, foi desenvolvida uma macro no software KS 400. Os dados foram estatisticamente analisados com ANOVA 3 fatores (resistência de união) e teste de Kruskall-Wallis (espessura do cimento). Comparações múltiplas foram realizadas com o teste Student-Newman-Keuls. Análise de regressão, modelo linear, foi empregada para verificar a correlação entre espessura do cimento e resistência de união. Todos os testes foram aplicados com &#945; = 0,05. O fator cimento exerceu influência significativa para a resistência de união (p = 0,0402): o RelyX U100 apresentou a maior média. A ativação dual elevou os valores de resistência de união em comparação ao modo quimicamente ativado (p < 0,0001). Houve diferenças significantes entre os grupos, sendo G1 (22,4 4,0 MPa) > G3 (20,4 3,6 MPa) > G4 (17,8 5,2 MPa) > G2 (13,5 4,3 MPa). O terço do conduto não exerceu influência significativa sobre a resistência adesiva (p = 0,4749). As espessuras dos filmes de cimento foram estatisticamente diferentes nos diferentes terços: cervical (102 45 m) > médio (75 29 m) > apical (52 28m). Não foi observada forte correlação entre os valores de espessura e os de resistência ao push-out (r = - 0,2016, p = 0,0033). O tipo de falha predominante foi a mista, exceto para o G2, que apresentou 74% das falhas na interface cimento-pino. Dessa forma, o cimento autoadesivo apresentou melhor desempenho que o convencional, e ambos os sistemas duais, sobretudo o RelyX ARC, apresentaram dependência da fotoativação para atingirem maiores valores de resistência de união. / The aim of this study was to evaluate the influence of adhesive cementation system approach (total-etch or self-adhesive), activation mode (self-cure or dual-cure), canal third (cervical, middle or apical) and cement thickness on push-out bond strength of glass fiber post bonded on human roots. Forty roots were embebed in epoxy resin and endodontically treated (filled with guta percha and non-eugenol endodontic sealer). Following 7 days, the post spaces were prepared with low-speed post drills provided by the manufacturer (WhitePost DC #2, FGM) at a depth of 10 mm and the roots were randomly divided in 4 groups, according to cementation system and activations mode: (G1) RelyX ARC/Adper Scotchbond Multi-Purpose Plus (total-etch), dual-cure (G2) RelyX ARC/Adper Scotchbond Multi-Purpose Plus, self-cure, (G3) RelyX U100 (self-adhesive), dual-cure and (G4) RelyX U100, self-cure. After 7 days, each root was sectioned with water-cooled diamond blade, generating six 1-mm thickness slices (n=60). Before push-out bond strength test, digital images of both sides of the slices were captured with digital camera, in order to measure the post radius and the cement thickness. After mechanical test, new images were captured to evaluate the failure mode. A macro was developed in KS 400 software to speed and standardize the evaluation of cement thickness. Results were analyzed using three-way ANOVA (push-out) and Kruskall-Wallis test (cement thickness). Post-hoc multiple comparisons were performed using the Student-Newman-Keuls test. The correlation between resin cement thickness and bond strength was evaluated with regression analysis, linear model. All tests were performed with significance level set at 0.05. Push-out bond strength was significantly influenced by cement type (p= 0.0402): the RelyX U100 cement presented higher mean value. The dual-activated mode increased the bond strength in comparison to self-activated mode (p < 0.0001). Statically differences were observed between groups: G1 (22.4 4.0 MPa) > G3 (20.4 3.6 MPa) > G4 (17.8 5.2 MPa) > G2 (13.5 4.3 MPa). Bond strength was not affected by post space depth (p = 0,4749). The resin cement thicknesses were significantly different in root thirds: cervical (102 45 m) > middle (75 29 m) > apical (52 28m). No strong correlation between cement thickness and push-out bond strength was observed (r = - 0.2016, p = 0.0033). The main failure mode was mixed, except for G2 (74% adhesive failures at post-cement interface). It was concluded tha the self-adhesive cement showed a better performance than the conventional one, and both dual resin systems, specially the RelyX ARC, presented photo-activation dependence to attain greater adhesive bond strength.

Objetivos: o presente estudo teve como objetivo determinar a aplicabilidade e eficácia adesiva de diferentes monômeros ácidos quando aplicados em formulações de cimentos resinosos autoadesivos experimentais sob o grau de conversão, propriedades físico-químicas e resistência de união à dentina e à zircônia tetragonal policristalina estabilizada por ítrea (Y-TZP), após um período de 3 meses de armazenamento em água. Material: dois tipos de cimentos do tipo pasta-pasta foram formulados contendo monômeros convencionais UDMA, HEMA, BISGMA, TEGDMA e monômeros ácidos 2MP e GDMAP como matriz orgânica. Um grupo contendo apenas monômeros convencionais foi formulado como grupo controle. Os componentes canforoquinona/EDMAB e peróxido de benzoíla/DHPT foram empregados como sistema de ativação dual. O sal sódico do ácido benzenosulfônico 98% (BAS) foi incorporado nos grupos experimentais. Partículas de carga foram incorporadas na proporção ±55% em peso final. Método: A técnica de espectroscopia no infravermelho (FT-IR) foi empregada para análise do grau de conversão (n=3) imediato e após 24 h. A avaliação do pH (n=3) foi feita através do emprego de um equipamento medidor de pH. Os corpos de provas foram imersos em água destilada e o pH foi analisado de forma imediata e após 5 min, 24 h e 48 h. Os testes de sorção e solubilidade (n=6) e espessura de película (n=5) seguiram as recomendações da ISO 4049. A análise de resistência de união (n=12) foi realizada em dentina e Y-TZP, através do teste de cisalhamento em área reduzida após um protocolo de envelhecimento em água destilada por 3 meses. No caso da Y-TZP, metade dos espécimes receberam um tratamento superficial cojet (30 ?m), associado a aplicação de um agente de união silano. O padrão de fratura foi analisado com o auxílio de um estereomicroscópio. Resultados: O grupo controle (91,7%) e o grupo formulado com 2MP (92%) apresentaram superiores valores de grau de conversão em relação ao grupo GDMAP (77,7%). O pH dos grupos experimentais 2MP e GDMAP se apresentou mais ácido após 48 h em comparação ao grupo controle. Em contrapartida, esses grupos experimentais apresentaram uma maior sorção e solubilidade em relação ao grupo controle. A espessura da película formada foi semelhante em todos os grupos testados (p=0,266). Em dentina o grupo controle (27,0 MPa) e GDMAP (24,1 MPa) não apresentaram diferença estatística após 3 meses de estocagem. O grupo 2MP (13,7 MPa) apresentou resultados inferiores aos demais grupos. O tratamento de superfície empregado não foi capaz de manter ou de elevar os valores de resistência de união à Y-TZP após o período de envelhecimento em água. Todos os grupos experimentais apresentaram falhas precoces ou baixos valores de resistência de união após 3 meses, independente da presença ou não do tratamento de superfície. Conclusão: os grupos experimentais 2MP e GDMAP apresentaram resultados promissores. Entretanto, a adesão dos CRAs experimentais testados em Y-TZP ainda se apresenta frágil e instável. / Objectives: the purpose of this study was to evaluate the applicability and adhesive efficiency of different acid monomers utilized in formulations of experimental self-adhesive resin cement under degree of conversion, physico-chemical properties and bond strength to dentin and Y-TZP after 3 months aging period. Materials: two paste-paste luting agents were formulated containing UDMA, HEMA, BISGMA, TEGDMA and acid adhesive monomers 2MP and GDMAP as organic matrix. The control group was formulated containing only conventional monomers. Camphoroquinone/EDMAB and benzoyl peroxide/DHPT were used as dual activation system. BAS salt was incorporated into the experimental groups. Filler particles were added in a proportion of ±55% final weight. Method: Infrared spectroscopy technique (FTIR) was employed for degree of conversion analysis (n=3) immediately and after 24 hours. The pH assessment (n=3) was made using a pH meter. All the specimens were immersed in distilled water and pH assessment was performed immediately and after 5 min, 24 h and 48 h. Tests for sorption and solubility (n=6) and thickness (n=6) were carried out according to ISO 4049 recommendations. Bond strength analysis (n=12) was performed in dentin and Y-TZP through microshear after an aging 3 months protocol in distilled water. Regarding Y-TZP, half of the specimens were submitted to a cojet surface treatment (30 ?m) in association to silane bonding agent application. Fracture toughness standard was evaluated with the assistance of a stereomicroscope. Results: The control (91,7%) and 2MP (92%) groups presented higher degree of conversion than GDMAP group (77,7%). The 2MP and GDMAP experimental groups showed the highest pH compared to control group. In contrast, experimental groups showed a high hydrolytic degradation. The thickness of the formed film was similar among all the tested groups (p=0,266). Regarding the dentin, control and GDMAP groups had statistically similar bond strength (27,0 and 24,1 MPa respectively) after 3 months storage. While 2MP group (13,7 MPa) showed lower results compared the other groups. The surface treatment employed was not capable to maintain or elevate bond strength to Y-TZP results after the aging period in water. All experimental groups showed low bond strength values and even early failures after 3 months, regardless the surface treatment or its abscence. Conclusion: the experimental groups 2MP and GDMAP presented promising results. However, chemical adhesion to Y-TZP still remains weak and instable.

O objetivo deste estudo foi avaliar a influência do tipo de sistema de cimentação (condicionamento ácido total ou autoadesivo), do modo de ativação (autoativado ou dual), do terço do conduto radicular (cervical, médio ou apical) e da espessura do filme de cimento sobre a resistência de união de pinos de fibra de vidro cimentados em dentes humanos. Quarenta raízes foram incluídas em resina epóxi, submetidas a tratamento endodôntico e obturadas com guta percha e cimento endodôntico sem eugenol. Decorridos sete dias, os condutos foram preparados a uma profundidade de 10mm com brocas padronizadas do sistema dos pinos de fibra (WhitePost DC #2) e aleatoriamente divididos em 4 grupos, conforme o sistema de cimentação e o modo de ativação: (G1) RelyX ARC/Adper Scotchbond Multi-Purpose Plus (condicionamento ácido total), ativação dual, (G2) RelyX ARC/Adper Scotchbond Multi-Purpose Plus, autoativado, (G3) RelyX U100 (autoadesivo), dual e (G4) RelyX U100, autoativado. Após uma semana, cada raiz foi seccionada em máquina de corte, originando 6 fatias de 1 mm de espessura (n=60). Antes do ensaio de push-out cada fatia foi fotografada em ambas as faces, para determinação do raio dos pinos e da espessura do filme de cimento. Após o ensaio mecânico, novas imagens foram capturadas para determinação do modo de falha. Para automatizar a determinação da espessura de cimento, foi desenvolvida uma macro no software KS 400. Os dados foram estatisticamente analisados com ANOVA 3 fatores (resistência de união) e teste de Kruskall-Wallis (espessura do cimento). Comparações múltiplas foram realizadas com o teste Student-Newman-Keuls. Análise de regressão, modelo linear, foi empregada para verificar a correlação entre espessura do cimento e resistência de união. Todos os testes foram aplicados com &#945; = 0,05. O fator cimento exerceu influência significativa para a resistência de união (p = 0,0402): o RelyX U100 apresentou a maior média. A ativação dual elevou os valores de resistência de união em comparação ao modo quimicamente ativado (p < 0,0001). Houve diferenças significantes entre os grupos, sendo G1 (22,4 4,0 MPa) > G3 (20,4 3,6 MPa) > G4 (17,8 5,2 MPa) > G2 (13,5 4,3 MPa). O terço do conduto não exerceu influência significativa sobre a resistência adesiva (p = 0,4749). As espessuras dos filmes de cimento foram estatisticamente diferentes nos diferentes terços: cervical (102 45 m) > médio (75 29 m) > apical (52 28m). Não foi observada forte correlação entre os valores de espessura e os de resistência ao push-out (r = - 0,2016, p = 0,0033). O tipo de falha predominante foi a mista, exceto para o G2, que apresentou 74% das falhas na interface cimento-pino. Dessa forma, o cimento autoadesivo apresentou melhor desempenho que o convencional, e ambos os sistemas duais, sobretudo o RelyX ARC, apresentaram dependência da fotoativação para atingirem maiores valores de resistência de união. / The aim of this study was to evaluate the influence of adhesive cementation system approach (total-etch or self-adhesive), activation mode (self-cure or dual-cure), canal third (cervical, middle or apical) and cement thickness on push-out bond strength of glass fiber post bonded on human roots. Forty roots were embebed in epoxy resin and endodontically treated (filled with guta percha and non-eugenol endodontic sealer). Following 7 days, the post spaces were prepared with low-speed post drills provided by the manufacturer (WhitePost DC #2, FGM) at a depth of 10 mm and the roots were randomly divided in 4 groups, according to cementation system and activations mode: (G1) RelyX ARC/Adper Scotchbond Multi-Purpose Plus (total-etch), dual-cure (G2) RelyX ARC/Adper Scotchbond Multi-Purpose Plus, self-cure, (G3) RelyX U100 (self-adhesive), dual-cure and (G4) RelyX U100, self-cure. After 7 days, each root was sectioned with water-cooled diamond blade, generating six 1-mm thickness slices (n=60). Before push-out bond strength test, digital images of both sides of the slices were captured with digital camera, in order to measure the post radius and the cement thickness. After mechanical test, new images were captured to evaluate the failure mode. A macro was developed in KS 400 software to speed and standardize the evaluation of cement thickness. Results were analyzed using three-way ANOVA (push-out) and Kruskall-Wallis test (cement thickness). Post-hoc multiple comparisons were performed using the Student-Newman-Keuls test. The correlation between resin cement thickness and bond strength was evaluated with regression analysis, linear model. All tests were performed with significance level set at 0.05. Push-out bond strength was significantly influenced by cement type (p= 0.0402): the RelyX U100 cement presented higher mean value. The dual-activated mode increased the bond strength in comparison to self-activated mode (p < 0.0001). Statically differences were observed between groups: G1 (22.4 4.0 MPa) > G3 (20.4 3.6 MPa) > G4 (17.8 5.2 MPa) > G2 (13.5 4.3 MPa). Bond strength was not affected by post space depth (p = 0,4749). The resin cement thicknesses were significantly different in root thirds: cervical (102 45 m) > middle (75 29 m) > apical (52 28m). No strong correlation between cement thickness and push-out bond strength was observed (r = - 0.2016, p = 0.0033). The main failure mode was mixed, except for G2 (74% adhesive failures at post-cement interface). It was concluded tha the self-adhesive cement showed a better performance than the conventional one, and both dual resin systems, specially the RelyX ARC, presented photo-activation dependence to attain greater adhesive bond strength.

O presente trabalho experimental, tem como objetivo avaliar \"in vitro\" possíveis falhas na cimentação de fragmentos cerâmicos sobre substrato de esmalte dentário previamente submetido ao clareamento dental e analisados pelo sistema de tomografia por coerência ótica. O ensaio experimental foi realizado in vitro, fazendo uso de trinta pré-molares superiores humanos. Cada elemento dental teve sua porção de esmalte vestibular aplainada por meio de disco de sílica na granulação 120, foram cimentados fragmentos cerâmicos retangulares de 1.5mm de espessura. Os dentes foram distribuídos aleatoriamente em 3 grupos de 10 dentes cada (n=10), Grupo 1: Fragmentos cimentados sem serem submetidos ao tratamento clareador; Grupo 2: Fragmentos cimentados 24 hrs. Após serem submetidos ao clareamento dental; Grupo 3: Fragmentos cimentados 7 dias após serem submetidos ao clareamento dental. Os espécimes foram transferidos para o sistema de tomografia por coerência óptica para seus respectivos monitoramentos após exposição ao agente clareador e cimentação da restauração indireta e ao final dos ensaios de envelhecimento artificial por termociclagem. A variável de resposta, falhas na interface esmalte e cimento resinoso, foi avaliada por escores (0,1 e 2) que representam em ordem crescente as falhas entre o substrato dental e a restauração indireta. Os valores obtidos foram analisados por meio de testes não paramétricos (Kruskal-Wallis e Wilcoxon). Os resultados constituíram de 60 escores de fendas referentes aos 3 grupos (G1;G2;G3) analisados imediatamente após a cimentação e após a termociclagem. A comparação entre os 3 grupos após termociclagem demonstrou haver diferença estatisticamente significante (p<0,0001) pela comparação dois a dois pelo teste complementar de Dunn e detectou-se que o G2 cimentado após 24 horas do clareamento apresentou mais fendas que G1 e G3. Com base nestes resultados e na metodologia utilizada pode-se concluir que, dentes submetidos ao tratamento clareador, o protocolo clinico de cimentação de restaurações cerâmicas indiretas, quando realizado 7 dias após o clareamento gerou menor quantidade de fendas na interface, propondo assim melhor qualidade na adaptação dente/restauração. / The present experimental study has the objective of evaluating in vitro possible failures in the cementation of ceramic fragments over dental enamel substrate previously submitted to dental bleaching and analyzed by optical coherence tomography system. The experimental trial was performed in vitro using thirty human maxillary premolars. Each dental element had have it\'s portion of vestibular enamel planed by a silic disk in granulation 120, ceramic fragments with a diameter of 1.5mm thickness were cemented. The teeth were randomly distributed in 3 groups of 10 teeth each (n = 10), Group 1: Bonded Veneer without being subjected to bleaching treatment Group 2: Bonded Veneer 24 hours after being submitted to dental bleaching Group 3: Bonded Veneer 7 days after being submitted to dental bleaching. The specimens were transferred to the optical coherence tomography system for their respective monitoring after being exposured to the whitening agent and cementation of the indirect restoration and at the end of the artificial aging tests by thermocycling. The variable of response, at faults in the interface enamel and resin cement, was evaluated by scores (0,1 and 2) that represent in increasing order the failures between dental substrate and indirect restoration. The values obtained were analyzed by non-parametric tests (Kruskal-Wallis and Wilcoxon). The results consisted of 60 gaps scores for the three groups (G1, G2, G3) analyzed immediately after bonding and after thermocycling. The comparison between the 3 groups after thermocycling, showed a statistically significant difference (p <0.0001) by the two-to-two comparison by Dunn\'s complementary test and it was detected that G2 after 24 hours of bleaching, showed more gaps than G1 and G3. Based on these results and the methodology used, it was concluded that, when teeth were submitted to the bleaching treatment, the clinical cementation protocol of indirect ceramic restorations, when performed 7 days after bleaching, generated fewer gaps at the interface, thus proposing a better quality in the relation Tooth / restoration.

Submitted by Cláudia Bueno (claudiamoura18@gmail.com) on 2016-03-21T20:56:51Z No. of bitstreams: 2 Dissertação - Ana Paula Rodrigues de Magalhães - 2014.pdf: 1363967 bytes, checksum: f5dfff9110b37529ad94b507a41dae6b (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) / Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2016-03-22T14:22:48Z (GMT) No. of bitstreams: 2 Dissertação - Ana Paula Rodrigues de Magalhães - 2014.pdf: 1363967 bytes, checksum: f5dfff9110b37529ad94b507a41dae6b (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) / Made available in DSpace on 2016-03-22T14:22:48Z (GMT). No. of bitstreams: 2 Dissertação - Ana Paula Rodrigues de Magalhães - 2014.pdf: 1363967 bytes, checksum: f5dfff9110b37529ad94b507a41dae6b (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) Previous issue date: 2013-12-20 / Fundação de Amparo à Pesquisa do Estado de Goiás - FAPEG / This study aims to evaluate the antibacterial effect of resin luting cements with and without NAg addition, and their influence on color, sorption and solubility. NAg were incorporated to two dual-cured resin luting cements (RelyX ARC - color A1 - and RelyX U200 - color A2 -) in two concentrations (0.05% and 0.07%) and the disc specimens obtained were tested for bacteria inhibition growth against Streptococcus mutans through optical density readings and scanning electron microscopy (SEM) analysis, for color changes with a spectrophotometer and for sorption and solubility after storage in water or 75% ethanol for 28 days, according to the ISO 4049:2010 specifications. Data were subjected to statistycal analysis with ANOVA and Tukey (p=0.05). The optical density of the culture broth indicated bacterial growth, but on SEM the only species identified was Bacillus subtilis. NAg produced significant color change on the resin cements, especially in the lighter color (RelyX ARC). Solubility values were very low for all groups, while sorption values were raised with NAg addition. The resin luting cements with NAg addition did not show antibacterial activity against S. mutans. They also showed perceptible color change and higher sorption than the materials without Nag. / O objetivo deste trabalho foi avaliar o efeito antibacteriano de cimentos resinosos com e sem adição de NAg, e a influência das mesmas na cor, sorção e solubilidade. Soluções de NAg foram incorporadas a dois cimentos resinosos de dupla polimerização (RelyX ARC - cor A1- e RelyX U200 – cor A2) em duas concentrações (0,05% e 0,07%) e os espécimes confeccionados em forma de discos foram testados quanto: à inibição de crescimento bacteriano (Streptococcus mutans) por meio de leituras de densidade ótica e análise em microscopia eletrônica de varredura (MEV); quanto à mudança de cor com um espectrofotômetro e quanto a sorção e solubilidade após armazenamento em água ou etanol 75% por 28 dias, de acordo com as normas da ISO 4049:2010. Os dados obtidos foram tabulados e submetidos a ANOVA e Tukey com p=0,05. A densidade ótica medida nos meios de cultura indicou crescimento bacteriano, mas a análise em MEV somente revelou a bactéria Bacillus subtilis. A NAg induziu mudança de cor significante nos cimentos resinosos, especialmente no de cor mais clara (RelyX ARC). Os valores de solubilidade foram muito baixos para todos os grupos, enquanto a sorção aumentou com a adição de NAg. Os cimentos resinosos adicionados de NAg não apresentaram efeito antibacteriano contra S mutans. Também apresentaram mudança de cor perceptível e maior sorção do que os materiais sem NAg.

Objetivos: o presente estudo teve como objetivo determinar a aplicabilidade e eficácia adesiva de diferentes monômeros ácidos quando aplicados em formulações de cimentos resinosos autoadesivos experimentais sob o grau de conversão, propriedades físico-químicas e resistência de união à dentina e à zircônia tetragonal policristalina estabilizada por ítrea (Y-TZP), após um período de 3 meses de armazenamento em água. Material: dois tipos de cimentos do tipo pasta-pasta foram formulados contendo monômeros convencionais UDMA, HEMA, BISGMA, TEGDMA e monômeros ácidos 2MP e GDMAP como matriz orgânica. Um grupo contendo apenas monômeros convencionais foi formulado como grupo controle. Os componentes canforoquinona/EDMAB e peróxido de benzoíla/DHPT foram empregados como sistema de ativação dual. O sal sódico do ácido benzenosulfônico 98% (BAS) foi incorporado nos grupos experimentais. Partículas de carga foram incorporadas na proporção ±55% em peso final. Método: A técnica de espectroscopia no infravermelho (FT-IR) foi empregada para análise do grau de conversão (n=3) imediato e após 24 h. A avaliação do pH (n=3) foi feita através do emprego de um equipamento medidor de pH. Os corpos de provas foram imersos em água destilada e o pH foi analisado de forma imediata e após 5 min, 24 h e 48 h. Os testes de sorção e solubilidade (n=6) e espessura de película (n=5) seguiram as recomendações da ISO 4049. A análise de resistência de união (n=12) foi realizada em dentina e Y-TZP, através do teste de cisalhamento em área reduzida após um protocolo de envelhecimento em água destilada por 3 meses. No caso da Y-TZP, metade dos espécimes receberam um tratamento superficial cojet (30 ?m), associado a aplicação de um agente de união silano. O padrão de fratura foi analisado com o auxílio de um estereomicroscópio. Resultados: O grupo controle (91,7%) e o grupo formulado com 2MP (92%) apresentaram superiores valores de grau de conversão em relação ao grupo GDMAP (77,7%). O pH dos grupos experimentais 2MP e GDMAP se apresentou mais ácido após 48 h em comparação ao grupo controle. Em contrapartida, esses grupos experimentais apresentaram uma maior sorção e solubilidade em relação ao grupo controle. A espessura da película formada foi semelhante em todos os grupos testados (p=0,266). Em dentina o grupo controle (27,0 MPa) e GDMAP (24,1 MPa) não apresentaram diferença estatística após 3 meses de estocagem. O grupo 2MP (13,7 MPa) apresentou resultados inferiores aos demais grupos. O tratamento de superfície empregado não foi capaz de manter ou de elevar os valores de resistência de união à Y-TZP após o período de envelhecimento em água. Todos os grupos experimentais apresentaram falhas precoces ou baixos valores de resistência de união após 3 meses, independente da presença ou não do tratamento de superfície. Conclusão: os grupos experimentais 2MP e GDMAP apresentaram resultados promissores. Entretanto, a adesão dos CRAs experimentais testados em Y-TZP ainda se apresenta frágil e instável. / Objectives: the purpose of this study was to evaluate the applicability and adhesive efficiency of different acid monomers utilized in formulations of experimental self-adhesive resin cement under degree of conversion, physico-chemical properties and bond strength to dentin and Y-TZP after 3 months aging period. Materials: two paste-paste luting agents were formulated containing UDMA, HEMA, BISGMA, TEGDMA and acid adhesive monomers 2MP and GDMAP as organic matrix. The control group was formulated containing only conventional monomers. Camphoroquinone/EDMAB and benzoyl peroxide/DHPT were used as dual activation system. BAS salt was incorporated into the experimental groups. Filler particles were added in a proportion of ±55% final weight. Method: Infrared spectroscopy technique (FTIR) was employed for degree of conversion analysis (n=3) immediately and after 24 hours. The pH assessment (n=3) was made using a pH meter. All the specimens were immersed in distilled water and pH assessment was performed immediately and after 5 min, 24 h and 48 h. Tests for sorption and solubility (n=6) and thickness (n=6) were carried out according to ISO 4049 recommendations. Bond strength analysis (n=12) was performed in dentin and Y-TZP through microshear after an aging 3 months protocol in distilled water. Regarding Y-TZP, half of the specimens were submitted to a cojet surface treatment (30 ?m) in association to silane bonding agent application. Fracture toughness standard was evaluated with the assistance of a stereomicroscope. Results: The control (91,7%) and 2MP (92%) groups presented higher degree of conversion than GDMAP group (77,7%). The 2MP and GDMAP experimental groups showed the highest pH compared to control group. In contrast, experimental groups showed a high hydrolytic degradation. The thickness of the formed film was similar among all the tested groups (p=0,266). Regarding the dentin, control and GDMAP groups had statistically similar bond strength (27,0 and 24,1 MPa respectively) after 3 months storage. While 2MP group (13,7 MPa) showed lower results compared the other groups. The surface treatment employed was not capable to maintain or elevate bond strength to Y-TZP results after the aging period in water. All experimental groups showed low bond strength values and even early failures after 3 months, regardless the surface treatment or its abscence. Conclusion: the experimental groups 2MP and GDMAP presented promising results. However, chemical adhesion to Y-TZP still remains weak and instable.

Submitted by Renata Lopes (renatasil82@gmail.com) on 2016-05-18T14:35:18Z No. of bitstreams: 1 mariellaagostinhogoncalves.pdf: 2206097 bytes, checksum: 736acf1d28715f5b3a331257446b5b23 (MD5) / Approved for entry into archive by Adriana Oliveira (adriana.oliveira@ufjf.edu.br) on 2016-07-01T18:48:04Z (GMT) No. of bitstreams: 1 mariellaagostinhogoncalves.pdf: 2206097 bytes, checksum: 736acf1d28715f5b3a331257446b5b23 (MD5) / Made available in DSpace on 2016-07-01T18:48:04Z (GMT). No. of bitstreams: 1 mariellaagostinhogoncalves.pdf: 2206097 bytes, checksum: 736acf1d28715f5b3a331257446b5b23 (MD5) Previous issue date: 2012-03-30 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Neste estudo, avaliou-se a resistência da união ao push-out de dois cimentos resinosos auto-adesivos e de um cimento resinoso convencional em dentina radicular. Em 60 dentes terceiros molares humanos, tratados endodonticamente, um pino de fibra de vidro foi cimentado com um dos três cimentos resinosos. Cada raiz foi seccionada em sentido transversal para a obtenção de três fatias (dentina-pino) de 1 mm de espessura. As fatias, correspondentes aos terços cervical, médio e apical do canal radicular, foram armazenadas em água deionizada a 37 ºC, durante 24 horas ou 30 dias. Após o teste de push-out, os valores de resistência da união foram submetidos aos testes estatísticos ANOVA three way e Tuckey (p = 0,05) e os tipos de fratura foram avaliados através de microscopia eletrônica de varredura. A resistência da união do cimento resinoso auto-adesivo RelyX U100 foi superior à do cimento convencional RelyX ARC, após os dois períodos de armazenamento (p < 0,05). No terço cervical, os valores de resistência da união do cimento resinoso convencional RelyX ARC foram maiores que nos terços médio e apical (p < 0,05) na análise de 24 horas. Após 30 dias de armazenamento, os valores nos três terços radiculares não diferiram entre si. Os valores de resistência da união do cimento resinoso RelyX U100, nas três regiões do canal radicular, não diferiram entre si (p > 0,05), em ambos os momentos de avaliação. Após 24 horas, BisCem apresentou maior resistência da união no terço apical, seguido pelo terço cervical. Após 30 dias, os valores de resistência da união nos três terços radiculares não diferiram entre si (p > 0,05). RelyX U100 não sofreu alteração nos valores de resistência da união após 30 dias de envelhecimento (p > 0,05). BisCem não apresentou diferenças nos valores obtidos após 24 horas e 30 dias de envelhecimento nos terços cervical e médio (p > 0,05). Para RelyX ARC, o tempo de 30 dias reduziu os valores de resistência da união nos três terços radiculares. RelyX U100 e BisCem apresentaram maior número de falhas coesivas da zona de interação. Para RelyX ARC, observou-se maior número de falhas coesivas da camada híbrida. Concluiu-se que o cimento resinoso auto-adesivo RelyX U100 apresentou maior resistência da união que o cimento resinoso convencional RelyX ARC, nos três terços radiculares, nos dois momentos de avaliação. BisCem demonstrou resistência da união comparável a do cimento RelyX U100. O tempo de armazenamento por 30 dias provocou alteração na resistência da união dos cimentos resinosos RelyX ARC e BisCem. / This study evaluated the push-out bond strength of two self-adhesive resin cements and a conventional etch-and-rinse resin cement on root dentin. Sixty human third molars were endodontically treated and a glass fiber post was cemented with one of three resin cements. Each root was cut transversely to obtain three slices (dentin-post) of 1 mm thick. The slices of the cervical, middle and apical root canal were stored in deionized water at 37 °C for 24 hours or 30 days. After storage, the push-out test was performed. The values of bond strength were evaluated by ANOVA three way and Tuckey’ test (p = 0,05) and the types of fracture were evaluated by scanning electron microscopy. The bond strength of the self-adhesive resin cement RelyX U100 was superior to the RelyX ARC etch-and-rinse cement, after the two storage periods (p > 0.05). The analysis of 24 hours showed that at the cervical third, the values of bond strength of RelyX ARC were higher than that of the middle and apical thirds (p < 0.05). After 30 days of storage, the values at the three root thirds did not differ. The values of RelyX U100, on the three regions of the root canal did not differ, in both evaluations (p > 0.05). After 24 hours, BisCem showed higher bond strength at the apical third, followed by cervical. After 30 days, the values of bond strength at the three root thirds did not differ (p > 0.05). RelyX U100 did not exhibit changes in bond strength values after 30 days of storage (p > 0.05). BisCem showed no differences in the values obtained after 24 hours and 30 days of aging at the cervical and middle thirds (p > 0.05). The storage time of 30 days reduced the values of bond strength at the three root thirds of RelyX ARC. RelyX U100 e BisCem had the highest number of cohesive failures of the zone of interaction. RelyX ARC presented a higher number of cohesive failures of the hybrid layer were observed. It was concluded that the RelyX U100 self-adhesive resin cement showed higher bond strength than the conventional resin cement RelyX ARC, on the three root thirds, in both periods. BisCem showed bond strength comparable to RelyX U100. The storage time for 30 days caused changes on the bond strength of the RelyX ARC and BisCem resin cements.