Made available in DSpace on 2014-06-11T19:27:24Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-03-29Bitstream added on 2014-06-13T18:31:32Z : No. of bitstreams: 1 rodrigues_hdp_me_rcla.pdf: 1125128 bytes, checksum: 8d675663432f7ca84bc84f1a57d6be8c (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Este trabalho apresenta uma avaliação comparativa do potencial biossortivo e biodegradativo da levedura Saccharomyces cerevisiae na remoção de corantes têxteis de efluentes quando imobilizada em alginato de cálcio e quando em célula livre. Para isto foram preparadas soluções experimentais dos corantes Acid Blue 40 e Acid Red 151, com concentrações equivalentes a 100 μg/mL e a estas foram adicionadas esferas com a levedura imobilizada a partir de uma suspensão 10% e gotas de células livres a partir de uma suspensão 2%. Os testes comparativos de remoção dos corantes foram analisados através de espectrofotômetros Ultravioleta- Visível e Infravermelho com Transformada de Fourier, com os quais foi possível determinar a porcentagem de remoção dos corantes das soluções, os valores das Absorbâncias Relativas que revelaram se o processo predominante na descoloração foi o da biossorção e/ou biodegradação, a quantidade de biomassa em miligramas (peso seco) necessária para fazer a remoção total da cor e também determinar as alterações moleculares ocorridas nas estruturas dos corantes após os tratamentos. Os resultados mostraram que a maior porcentagem de descoloração alcançada para o Acid Blue 40 foi de 61,7% após 360 horas de tratamento com 20 esferas com a levedura imobilizada e para o Acid Red 151 foi de 81,9% após 216 horas de tratamento também com 20 esferas com o microrganismo imobilizado. Através dos valores das Absorbâncias Relativas foi possível verificar que o processo predominante na remoção da cor do Acid Blue 40 com 72 horas de tratamento com 10 e 20 esferas com Saccharomyces cerevisiae imobilizada foi o da biossorção seguido da biodegradação e para o Acid Red 151 com esse mesmo tempo de tratamento e com a mesma quantidade de biomassa imobilizada foi o da biodegradação. A quantidade de biomassa imobilizada e livre... / This paper presents a comparative assessment of the biodegradative and biosorptive potential of the yeast Saccharomyces cerevisiae in textile dyes removal of effluents when in immobilized alginate and in free cells. Therefore, experimental solutions were prepared with concentrations of the dye Acid Blue 40 and Acid Red 151 equivalent to 100 mg/mL and those were added with beads containing the immobilized yeast from a 10% suspension and drops of free cells from a 2 % suspension. Comparative tests of dye removal were analyzed by UV-Visible spectrometers and Infrared Fourier Transform on which it was possible to determine the percentage of dye removal from the solutions, the values of Relatives Absorbances that the discoloration have been proved to predominant by biosorption and / or biodegradation, the amount of biomass in milligrams (dry weight) required for a complete color removal and also to determine the molecular changes occurring in the dye structures after the treatment. The results showed that the highest decolorization percentage achieved for Acid Blue 40 was 61.7% after 360 hours of treatment with 20 immobilized yeast beads and for the Acid Red 151 it was 81.9% after 216 hours of treatment with 20 beads also with immobilized microorganism. Through the values of Relatives Absorbances it was concluded that the predominant process in dye removal of Acid Blue 40 in 72 hours of treatment with 10 and 20 beads containing imobilized Saccharomyces cerevisiae was the biosorption followed by biodegradation and in Acid Red 151 with the same treatment time and the same amount of immobilized biomass it was the biodegradation. The amount of immobilized and free biomass to obtain total removal of Acid Blue 40 solution was 87 and 38 mg/mL, respectively, and to completely remove the Acid Red 151, the required amount of free and immobilized biomass was 64 and 2 mg/mL, respectively, which... (Complete abstract click electronic access below)

O presente trabalho avaliou o potencial da enzima HRP no descoramento dos corantes têxteis: Azul Drimaren X-3LR (DMBLR), Azul Drimaren X-BLN (DMBBLN), Rubinol Drimaren X-3LR (DMR) e Azul Drimaren CL-R (RBBR). Parâmetros como concentração do corante, temperatura, concentração de peróxido de hidrogênio (H2O2) e tempo de reação foram otimizados. Os ensaios de descoramento dos corantes foram realizados a partir desses resultados. As melhores condições reacionais determinadas para os corantes estudados foram: concentração do corante = 120 mg L-1, temperatura = 35C, concentração de H2O2 = 0,55 mM e tempo de reação = 1 hora. Os percentuais de descoramento dos corantes DMBLR, DMBBLN, DMR e RBBR, após o tratamento enzimático foi de 99, 77, 94 e 97%, respectivamente. O tempo reacional de 5 minutos foi suficiente para os corantes DMBLR e RBBR apresentarem elevada porcentagem de descoramento, 96% para ambos. Já os corantes DMBBLN e DMR só apresentaram elevado grau de descoramento após 1 hora de reação, sendo o corante DMBBLN o mais recalcitrante, apresentando uma melhora de 10% na porcentagem de descoramento, após 24 horas de reação. Além do grau de descoramento, também foi avaliada a toxicidade dos corantes antes e após o tratamento enzimático utilizando Daphnia pulex e Artemia salina como bioindicadores de toxicidade. Resultados toxicológicos utilizando Daphnia pulex não foram conclusivos, indicando que esse bioindicador não foi adequado para avaliar a toxicidade dos corantes estudados no meio reacional utilizado. Com o uso da Artemia salina na avaliação toxicológica foi observado uma redução da toxicidade para os corantes DMBLR, DMR e RBBR após tratamento enzimático, e um aumento da toxicidade não significativo para o corante DMBBLN. Os resultados obtidos no trabalho ressaltam a eficiência da enzima HRP no descoramento dos corantes têxteis estudados, sem a geração de produtos tóxicos e prejudiciais ao meio ambiente / The aim of the present study was to evaluate the potential of the Horseradish peroxidase (HRP) enzyme in the decolorization of textile dyes Drimaren Blue X-3LR (DMBLR), Drimaren Blue X-BLN (DMBBLN), Drimaren Rubinol X-3LR (DMR) and Drimaren Blue CL-R (RBBR). Parameters such as concentration of the dye, temperature, concentration of hydrogen peroxide (H2O2) and reaction time were optimized. The optimum reaction conditions determined for the studied dyes were: concentration of the dye = 120 mg L-1, temperature = 35 C, concentration of H2O2 = 0.55 mM and reaction time = 1 h. The decolorization percentage of dyes DMBLR, DMBBLN, DMR and RBBR after enzymatic treatment was 99, 77, 94 and 97%, respectively. The reaction time of only 5 minutes presented high decolorization percentage for both dyes DMBLR and RBBR, about 96 %. However dyes DMBBLN and DMR showed high decolorization degree in 1 h of reaction and the dye DMBBLN, being the most recalcitrant, exhibited an improvement of 10% in the decolorization percentage after 24 h of reaction. Besides the decolorization degree, the toxicity of the studied dyes was also evaluated before and after enzymatic treatment using Daphnia pulex and Artemia salina as bioindicators. The toxicological results using Daphnia pulex were not conclusive, indicating that it was not an appropriate bioindicator to evaluate the toxicity of the tested dyes. Meanwhile when using Artemia salina for toxicological evaluation it was observed a reduction of toxicity for dyes DMBLR, DMR and RBBR after enzymatic treatment, and a not significant increase in toxicity for the dye DMBBLN. In conclusion, the obtained results emphasize the efficiency of the HRP enzyme in the decolorization of the studied textile dyes, without the generation of toxic and harmful products to the environment

A presente pesquisa descreve o preparo, caracterização e aplicação de novos adsorventes aplicados ao tratamento de efluentes contendo corantes. Os adsorventes produzidos neste estudo foram: Carvão ativado produzido por pirólise assistida por micro-ondas (AMWCST), a partir de um lodo coletado em uma Estação de Tratamento de Efluentes de curtume; e, biomassa fúngica tratada termicamente (BTV) a partir do fungo Trametes sp SC-10, os quais foram caracterizados de acordo a suas propriedades de textura e química de superfície e foram aplicados na remoção de corantes em solução aquosa e efluentes. Nesta pesquisa também se avaliou a eficiência do processo combinado entre coagulação-floculação e adsorção usando o AMWCST. Em suas propriedades estruturais, o AMWCST apresentou uma área superficial BET de 491,0 m2 g-1 e um volume total do poro de 0,440 cm3g-1, com distribuição de tamanho de poro majoritariamente mesoporosa; entretanto o BTV apresentou baixa área superficial destacando-se a formação de mesoporos. Foram estudados os equilíbrios e cinéticas de adsorção e sua correlação com modelos empíricos, para os sistemas AMWCST/PA-210 (Preto Ácido 210), e VA-357(Vermelho Ácido 357) e BTV/ AA-161 (Azul ácido 161). Para os dois primeiros sistemas empregando carvão ativado, a isoterma de adsorção de Liu foi a que descreveu melhor os dados de adsorção com capacidades máximas de 1108 mg g-1 e 589,5 mg g-1 a 298 K para PA-210 e VA-357. Para os estudos cinéticos, o modelo de ordem fraccionário de Avrami foi o melhor modelo ajustado para os dados experimentais. A BTV no entanto, mostrou uma capacidade máxima de biossorção de AA-161 de 221,7 mg g-1 a 303 K. O modelo de Langmuir foi o modelo que melhor descreveu os dados experimentais de equilibrios de biossorção e o Modelo Fraccionário de Avrami foi o que melhor descreveu a cinética de biossorção para o corante. A eficiência de remoção do adsorvente AMWCST no efluente sintético simulado foi de 93,79% e do BTV em um efluente simulado similar ao do processo de acabamento molhado de couro foi de 89,47%, indicando que a BTV é também um bom biossorvente para o tratamento de efluentes industriais. Finalmente, enquanto ao estudo de combinação de processos de coagulação-floculação com adsorção usando o AMWCST, este mostrou resultados eficazes na remoção do corante PA-210, em efluentes do processo de acabamento molhado, obtendo 85,20% de remoção do corante em comparação com o carvão comercial, o qual apresentou 88,64%. Além disso, utilizando o AMWCST, obtiveram-se reduções de 68,44%, 13,44% e 42,81% para COT, sódio total e amônio. / The present research describes the preparation, characterization and application of new adsorbents for the treatment of effluents contaminated with dyes. An adsorbent was activated carbon produced by pyrolysis microwave-assisted (AMWCST), from a sludge collected at a tannery Treatment Plant; The other adsorbent was a thermally treated fungal biomass (BTV) from Trametes sp. SC-10 fungi, which were characterized according to their texture and surface chemistry properties and were applied in the removal of dyes in aqueous solution and effluents. In this research, the efficiency of the combined coagulation-flocculation and adsorption process using the AMWCST was also evaluated. As for the texture properties, the AMWCST presented a BET surface area of 491.0 m2g-1 and a total pore volume of 0.440 cm3g-1, with mesoporous pore size distribution; However, BTV presented low surface area, highlighting the formation of mesopores. As for adsorption equilibria and kinetics and their correlation with theoretical models, for the AMWCST / AB-210, and AR-357 and BTV/AB-161 systems. For the first two systems using activated carbon, the Liu adsorption isotherm was the model that best described the adsorption data with maximum capacities of 1108 mg g-1 and 589,5 mg g-1 at 298 K for AB- 210 and AR- 357. For the kinetic studies, the Avrami fractional order model was the best-fit model for the experimental data. BTV however, showed a maximum AB-161 biosorption capacity of 221.7 mg g-1 at 303K. The Langmuir model was the model that best described the experimental data of biosorption equilibria and the Avrami Fractional Model best described the kinetics of biosorption for the dye. The adsorption efficiency of the AMWCTS in the synthetic simulated effluent was 93.79% and the BTV in a simulated effluent similar to that of the wet-end process in the leather industry was 89.47%, indicating that BTV is also a good biosorbent for the treatment of industrial effluents. Finally, while studying the combination of coagulation-flocculation processes with adsorption using the AMWCST, it showed efficient results in the removal of the AB-210 dye in wet-end process effluents, obtaining 85.20% dye removal compared with commercial activated carbon, which had 88.64%. In addition, using AMWCST, reductions of 68.44%, 13.44% and 42.81% were obtained for TOC, total sodium and ammonium.

Submitted by Jean Medeiros (jeanletras@uepb.edu.br) on 2017-09-12T13:42:05Z No. of bitstreams: 1 PDF - Kamila Deys Rodrigues Lacerda.pdf: 12829551 bytes, checksum: 36388c5a40ba241cf64f1f9b81270fd5 (MD5) / Made available in DSpace on 2017-09-12T13:42:05Z (GMT). No. of bitstreams: 1 PDF - Kamila Deys Rodrigues Lacerda.pdf: 12829551 bytes, checksum: 36388c5a40ba241cf64f1f9b81270fd5 (MD5) Previous issue date: 2017-04-27 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / In the productive process of the textile industry have stages that uses dye, which generates effluents that can degrade the environment. This paper looks for producing an alternative adsorbent made from Green Coconut Mesocarp (MCV) for removing the Blue Cassafix - CA 2G, a reactive dye. The adsorbent was produced by drying the MCV in air circulation oven at temperatures of 60 and 80°C, among the tested models for the drying process, the Midili model fitted at most the experimental data. The factorial planning 2^4 analyzed the influence of variables: mass, concentration, pH and time; the factors mass and concentration were statistically significant while the factors pH and time had no influence to the process within the studied levels. In the factorial planning of 2^5 the analyzed variables were mass of MCV, dye concentration, pH, time and washing or not the MCV with an albumin solution; the pH was the only factor that did not show statistically significant effect in the process within the studied levels. The adsorption kinetics tests were carried out with the in naturain natura bioadsorbent and the adsorbent washed with albumin, with a volume of 25 mL of solution and concentration of 100 mg.L^-1, the pseudo-first order and the pseudo- second order models agreed to the experimental data. The best results of qt were found in the kinetics of adsorption with experiment 4, with 3.4 mg.g^-1. In the -1 equilibrium study, 10 erlemmeyers with concentrations ranging from 10 to 100 mg.L^-1 and 0.10 g of MCV were in contact for 30 min at 200 rpm, the Sips model had the best fit for the experimental data. The MCV has potential as a bioadsorbent, has low cost and is found in plenty. / Dentro do processo produtivo da indústria têxtil, há etapas em que a utilização de corante gera efluentes com características que degradam o meio ambiente. O presente estudo busca produzir um adsorvente alternativo a partir do mesocarpo do coco verde (MCV) para remoção do corante reativo Azul Cassafix – CA 2G. O adsorvente foi produzido através da secagem em estufa de recirculação de ar forçado nas temperaturas de 60 e 80 °C, dentre os modelos testados para o processo de secagem o que melhor se ajustou aos dados experimentais foi o de Midili. O planejamento fatorial 2^4 analisou a influência das variáveis massa, concentração, pH e tempo, os fatores massa e concentração foram estatisticamente significativos e os fatores pH e tempo não influenciaram o processo dentro dos níveis estudados. No planejamento fatorial de 2^5 as variáveis analisadas foram a massa, a concentração, o pH, o tempo e a lavagem do MCV com uma solução de albumina, o pH foi o único fator que não apresentou efeito estatisticamente significativo no processo dentro dos níveis estudados. Os ensaios de cinética da adsorção foram realizados com o adsorvente in natura e após lavagem com albumina, com volume de 25 mL de solução e concentração de 100 mg.L^-1 modelo de pseudo-segunda ordem apresentou melhor concordância com os dados experimentais. Os melhores resultados de qt foram encontrados na cinética da adsorção com o experimento 4 no valor de 3,4 mg.g^-1. No estudo do equilíbrio, 10 erlemmeyers com concentrações variando de 10 a 100 mg.L^-1 e 0,10 g de MCV ficaram em contato pelo tempo de 30 min e 200 rpm, o modelo de Sips foi o que melhor se ajustou aos dados experimentais. O MCV apresenta potencial como adsorvente, tem baixo custo e é encontrado em abundância.

Submitted by Fabio Sobreira Campos da Costa (fabio.sobreira@ufpe.br) on 2016-07-12T15:24:09Z No. of bitstreams: 2 license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5) DISSERTAÇÃO Crisleide Maria da Siolva Nascimento Acioly.pdf: 1856527 bytes, checksum: 9769ca344829feac7bd75efa5065a57c (MD5) / Made available in DSpace on 2016-07-12T15:24:09Z (GMT). No. of bitstreams: 2 license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5) DISSERTAÇÃO Crisleide Maria da Siolva Nascimento Acioly.pdf: 1856527 bytes, checksum: 9769ca344829feac7bd75efa5065a57c (MD5) Previous issue date: 2015-04-24 / FACEPE / A indústria de refino de óleo vegetal encontra-se em expansão na demanda produtiva nos últimos anos, consequentemente tem aumentado os resíduos gerados no processo produtivo. A argila impregnada com óleo, resultante da etapa de clarificação deste, passa a ser um resíduo considerado altamente contaminante. A proposta deste trabalho consiste na reutilização da argila contaminada, pós tratamento térmico, como adsorvente dos corantes NB 180 - Nylosan Azul Brilhante (ácido) e RR 133 - Remazol Red (reativo), estes utilizados na indústria têxtil e fortemente presentes no efluente gerado por esta. Inicialmente foi realizado um planejamento fatorial completo 23 , tendo como variáveis de entrada a massa de argila, bem como a temperatura e o tempo de calcinação, a fim de verificar a melhor condição para a remoção do óleo da argila pela redução da massa (variável resposta). Foi realizada a caracterização do material por análises de Difração de Raio X (DRX), área superficial (BET) e Microscopia Eletrônica de Varredura (MEV). Em seguida todas as amostras de argila do planejamento fatorial foram submetidas a um processo adsortivo, no qual foi utilizando 0,5 g de adsorvente, submetido a uma agitação de 300 rpm na temperatura de 30 ºC. Os experimentos foram conduzidos em batelada e em duplicata para a minimização de erros. Os resultados mostraram que a argila beneficiada, pós tratamento térmico apresentou uma capacidade de remoção de 96,7 % para o corante ácido NB 180 e 58,7 % para o corante Reativo RR 133, resultado este que indica a viabilidade de utilização da argila recuperada no tratamento de efluentes advindos da indústria têxtil. / The vegetable oil refining industry is booming in the production demand in recent years, as a result has increased the waste generated in the production process. The clay impregnated with oil, resulting from the clarification stage of this, it becomes a residue considered highly polluting. The purpose of this work is the reuse of contaminated clay, after heat treatment, as adsorbent of dyes NB 180 - Nylosan Brilliant Blue (acid) and RR 133 - Remazol Red (reactive), these used in the textile and strongly present in the effluent generated it is. Initially we performed a full factorial design 23, having as input variables the mass of clay, as well as the temperature and time of calcination, in order to establish the best condition for the clay oil removal by reducing the mass (dependent variable ). The characterization of the material by diffraction of X-ray analysis (XRD), surface area (BET) and Scanning Electron Microscopy (SEM) was performed. Then all samples clay factorial design were subjected to an adsorptive process, which was using 0.5 g of adsorbent, undergoes a 300 rpm agitation at a temperature of 30 ° C. The experiments were conducted in batch and in duplicate to minimize errors. The results showed that the clay favored, after heat treatment had a 96.7% removal capacity for acid dye NB 180 and 58.7% for the dye Reactive RR 133, a result that indicates the feasibility of the use of recovered clay in the treatment of effluent coming from the textile industry.

Made available in DSpace on 2016-08-19T12:56:33Z (GMT). No. of bitstreams: 1 Janilson Lima Souza.pdf: 1888741 bytes, checksum: afd5433449dae962b746bb158a2b3c5e (MD5) Previous issue date: 2009-10-15 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / In this work the green coconut mesocarp was used as adsorbent towards two textile dyes: Turquoise Remazol and Blue Remazol. The adsorbent was triturated, washed several times with water for extraction of soluble matter, dried in oven and sieved to obtain particle size between 0.088 and 0.177 mm. Determinations of C/H/N content were performed and the obtained results were: 45.20, 6.24 and 0.74%, respectively. The study of the thermal stability showed that adsorbent is mainly affected up to 200 °C. The infrared and 13C RMN spectra allowed assigning unambiguously vibrational bands the chemical shift characteristics of lignocellulosic materials. According to X-ray and micrographies techniques the adsorbent has an amorphous and irregular structure. The most of the pores diameter values are around 10 to 20 μm, meaning that it can be classified as a macroporous material. The pHzpc of the mesocarp was estimated in 4.1, and the best removal efficiency and uptake were reached at pH 2.0 for both dyes. The kinetic studies were performed at different temperatures (10, 20, 30, 40, 50 oC) , and the best observed uptake results were 91.95%, at 50 ºC, for the Turquoise Remazol, and 97.12%, at 10 ºC, for the Blue Remazol. The best kinetic model that fit well with all the experimental results was the pseudo-second order model (R2 > 0.999), and the observed average contact time for the systems reach the equilibrium was 90 min. The graphic model of adsorption intraparticular presented three lineal segments, indicating that in the adsorption of these dyes three processes are involved: external diffusion or superficial interaction adsorbent/adsorbate, diffusion of the adsorbate into the pores of the adsorbent and interaction of the adsorvate with the active sites inside the pores. The adsorption isotherms followed the Langmuir´s model, and the maximum adsorption values varied between 49.27 to 60.25 mg/g (Turquoise Remazol) and 84.75 to 80.64 mg/g (Blue Remazol) at the temperature interval from 10 to 50 ºC. The thermodynamic parameters confirmed the spontaneity for the two processes of adsorption being endothermic with entropy increase for the Turquoise Remazol and exothermic with entropy increase for the Blue Remazol. The dessorption of the dyes were accomplished in alkaline medium (pH 8,0), and the recovered amounts dyes were of 41.5% (turquoise remazol) and 52.5%, for an equilibrium time of 90 minutes. / Neste trabalho o mesocarpo de coco verde foi utilizado como adsorvente para os dois corantes têxteis: Turquesa Remazol e Azul Remazol. O adsorvente foi triturado, submetido à diversas lavagens para extração de matéria solúvel em água, secado e peneirado obtendo uma granulometria entre 0,088 a 0,177 mm. Teores de microanálise determinaram % de C, H e N sendo iguais a 45,20; 6,24 e 0,74 %, respectivamente. Estudos de estabilidade térmica do adsorvente mostraram que este se mantém inalterado até 200 °C. As principais freqüências vibracionais apresentaram bandas características de materiais lignocelulósicos. A técnica de raios-X determinou um caráter amorfo, e as micrografias mostraram que a superfície do material apresenta morfologia irregular, com diâmetros de poros entre 10-20 μm e uma estrutura macroporosa. O espectro de RMN de 13C é característico de materiais celulósicos. O pHzpc do mesocarpo foi estimado em 4,1, sendo observado uma melhor eficiência de remoção em pH 2,0 para ambos os corantes. As cinéticas foram realizadas em diferentes temperaturas (10, 20, 30, 40 e 50ºC) cujas quantidades máximas removidas foram 91,95 % (50 ºC) para o turquesa remazol e 97,12 % (10 ºC) para o azul remazol, sendo o modelo de pseudo-segunda ordem (R2 > 0,999) o mais adequado com quantidades adsorvidas variando entre 29,93 36,78 mg/g (turquesa remazol) e 38,63 38,29 mg/g (azul remazol) nas faixas de 10 a 50 ºC para um tempo de equilíbrio de 90 minutos. O modelo gráfico de adsorção intraparticular apresentou três segmentos lineares, indicando que na adsorção dos dois corantes estão envolvidos três processos: interação adsorvente/adsorvato superficial externa, difusão do adsorvato dentro dos poros do adsorvente e interação do adsorvato com os sítios ativos dentro dos poros. As isotermas de adsorções foram avaliadas, sendo que as quantidades máximas adsorvidas variaram entre 49,27 60,25 mg/g (turquesa remazol) e 84,75 80,64 mg/g (azul remazol) nas faixas de temperatura de 10 a 50 ºC. Os resultados obtidos seguiram o modelo de Langmuir (R2 > 0,985). Os parâmetros termodinâmicos confirmaram a espontaneidade para os dois processos de adsorção sendo endotérmico com aumento de entropia para o turquesa remazol e exotérmico com aumento de entropia para o azul remazol. A dessorção dos corantes foi realizada em meio alcalino (pH 8,0), sendo recuperado 41,5 % para o turquesa remazol e 52,5 % para o azul remazol em um tempo de equilíbrio de 90 minutos.

Made available in DSpace on 2016-08-19T12:56:34Z (GMT). No. of bitstreams: 1 Monica Silva Monteiro.pdf: 1311772 bytes, checksum: b05d364e4195cc17956cfde6cd0f2232 (MD5) Previous issue date: 2010-03-26 / In this work the efficiency of two Brazilian waste materials, wood residues and coconut mesocarp, as adsorbents towards metallic ions (Ni2+, Cu2+) and two representative textile dyes (Red and Violet Brilliant Remazol) was investigated. The humidity, carbohydrates, protein, grease, ash and fiber contents of both natural matrices were measured, and they were also characterized by infrared spectroscopy, X-ray diffratometry, scanning electron microscopy, specific surface area analysis and thermogravimetry. The adsorption of dyes was monitored by using UV-Vis spectroscopy. It was verified that while both adsorbents, coconut mesocarp and wood residue can adsorb towards the investigated dyes, they release extractives to the solution and showed no affinity towards those metal ions. Furthermore, it was verified that the adsorption is strongly pH dependent and, as a general behavior, an increase in the pH value is associated with a decrease of the total amount of adsorbed dye. The adsorption of violet dye onto coconut mesocarp is well described by the Langmuir model, while all the others systems fitted not well by the Langmuir and Freundlich´s equations. / Neste trabalho, a eficiência de dois resíduos agrícolas, serragem de madeira e mesocarpo de coco verde, como adsorventes para íons de metais (Ni2+, Cu2+) e dois corantes têxteis (vermelho e violeta brilhante Remazol) foi investigada. Os teores de umidade, carboidratos, proteínas, gorduras, cinzas e fibras de ambas as matrizes naturais foram medidos. Os sólidos foram também caracterizados por espectroscopia no infravermelho, difratometria de raios-X, microscopia eletrônica de varredura, área superficial específica e termogravimetria. A adsorção de corantes foi monitorada por espectrofotometria UV-Vis. Verificou-se que ambos os materiais, mesocarpo de coco e serragem de madeira embora adsorvam os corantes investigados, liberam extrativos para o meio e não mostraram nenhuma afinidade por íons metálicos. Além disso, foi verificado que a adsorção é fortemente dependente do pH e, como tendência geral, um aumento no valor do pH está associado a uma diminuição da quantidade total de corante adsorvida. A adsorção do corante violeta no mesocarpo de coco foi bem descrita pelo modelo de Langmuir, os demais sistemas não foram convenientemente modelados pelas equações de Langmuir e de Freundlich.

Made available in DSpace on 2016-08-19T12:56:41Z (GMT). No. of bitstreams: 1 Dissertacao Geyse25052012.pdf: 2143069 bytes, checksum: 882b4c8e39847d938ac718cd5055555a (MD5) Previous issue date: 2012-05-25 / FUNDAÇÃO DE AMPARO À PESQUISA E AO DESENVOLVIMENTO CIENTIFICO E TECNOLÓGICO DO MARANHÃO / In this study we investigated the potential of rice husk in nature (CAN) and treated with nitric acid (CAT) as adsorbents for the removal of textile dyes Remazol brilliant violet and Remazol Turquoise. The adsorbents were characterized by elemental analysis, vibrational spectroscopy in the infrared, NMR, 13 C solid state, TGA, X-ray diffraction and zero point of charge (pHpcz). Tests for adsorption of the dyes were examined by a batch system by changing the initial experimental factors as pH, concentration of the dyes, the contact time and temperature. Adsorption kinetic models were used to analyze interactions colorants/adsorbents and reaction equilibrium time. The adsorption kinetic data were fitted to the second order model (R2> 0.999). The intraparticle diffusion model showed three linear segments, indicating the three stages of the adsorptive process. The isotherm models of Langmuir and Freundlich were used in the evaluation of experimental results. For both adsorbents (CAN and CAT), the model proposed by Freundlich resulted in the best fit of experimental data for the violet dye, while the Langmuir equation showed the best fit for the Turquoise dye. The thermodynamic parameters obtained by evaluating the isotherms at temperatures 10, 25, 40 and 55 ° C, confirmed the spontaneity of the adsorption processes, which are endothermics, with a high degree of disorder.The systems tested showed low values of desorption of the dyes in alkaline pH's (8 and 11), indicating high affinity between matrices and dye and that the electrostatic interaction was not the predominant mechanism in the adsorption. Finally, this materials seems to be an excellent alternative, as it is an abundant biomass available at low cost. / Neste trabalho foi investigada a potencialidade da casca de arroz in natura (CAN) e tratada com ácido nítrico (CAT) como adsorventes para a remoção dos corantes têxteis Violeta brilhante remazol e Turquesa remazol. Os adsorventes foram caracterizados por análise elementar, espectroscopia vibracional na região do infravermelho, RMN de 13C no estado sólido, análise termogravimétrica, difratometria de raios-X e ponto de carga zero (pHpcz). Os ensaios de adsorção dos corantes foram examinados por um sistema de bateladas, alterando fatores experimentais como pH inicial, concentração dos corantes, tempo de contato e temperatura. Modelos cinéticos de adsorção foram utilizados para analisar interações corantes/adsorventes e tempo de equilíbrio reacional. Os dados cinéticos de adsorção foram ajustados ao modelo de segunda ordem (R2> 0,999). O modelo de difusão intrapartícula apresentou três etapas no processo de adsorção. Os modelos isotérmicos de Freundlich e Langmuir, foram aplicados na avaliação dos resultados experimentais, sendo para ambos adsorventes (CAN e CAT), o modelo proposto por Freundlich resultou no melhor ajuste dos dados experimentais para o Violeta, enquanto a equação de Langmuir apresentou o melhor ajuste para o Turquesa.Os parâmetros termodinâmicos, obtidos pela avaliação das isotermas nas temperaturas 10, 25, 40 e 55 oC, confirmaram a espontaneidade dos processos de adsorção, os quais apresentaram-se endotérmicos e com elevado grau de desordem. Os sistemas examinados apresentaram valores baixos de dessorção dos corantes em pH's alcalinos (8 e 11), indicando afinidade entre corantes e adsorventes e que a interação eletrostática não foi o mecanismo predominante na adsorção. Finalmente, estes materiais mostraram ser uma excelente alternativa, como abundante biomassa disponível e de baixo custo.

Made available in DSpace on 2017-07-10T18:07:57Z (GMT). No. of bitstreams: 1 Jacqueline Ferandin Honorio.pdf: 4266327 bytes, checksum: 1a3607097a182468e16f0370c8918398 (MD5) Previous issue date: 2013-02-19 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The textile industry is known for high use of chemicals such as dyes, and generating large volumes of wastewater that contaminates water, a fact that has encouraged the research and improvement of treatment techniques. This study aimed to employ in natura soybean hulls in the removal of reactive dyes Crimson Sidercron HEXL (RCS-HEXL) and Blue BF-5G (RABF-5G). The point of zero charge (PZC) of soybean hulls was 6.76. The kinetics of the dye RCS-HEXL performed under the experimental conditions C0= 350 mg L-1, Dp= 0.215 mm, dosage= 8 g L-1, pH 2, temperature 30 °C was reached experimental qeq 38.039 mg g-1 in a time of 10 hours. In the kinetics of dye RABF-5G one experimental qeq of 57.473 mg g-1 was obtained under the conditions C0= 400 mg L-1, Dp= 0.725 mm, dosage= 6 g L-1, pH 2, temperature 30 °C 24 hours. The model of the pseudo-second order kinetics represented best of both dyes, showing R2= 0.989. The Langmuir isotherm model for 30 oC showed the maximum adsorption capacity of 44.356 mg g-1 and 72.427 mg g-1 for dyes RCS-HEXL and RABF-5G, respectively. Soybean hulls being a low-cost agro-industrial by-product proves to be a potential adsorbent for the removal of textile dyes investigated. / O setor têxtil é conhecido pela elevada utilização de produtos químicos, como os corantes, e gerador de grandes volumes de efluente que contaminam águas, fato que tem incentivado a pesquisa e o aprimoramento de técnicas de tratamento. Este trabalho teve como objetivo empregar a casca de soja in natura na remoção dos corantes reativos Crimson Sidercron HEXL (RCS-HEXL) e Azul BF-5G (RABF-5G). O ponto de carga zero (PCZ) da casca de soja foi de 6,76. A cinética do corante RCS-HEXL realizada nas condições experimentais de C0= 350 mg L-1, Dp=0,215 mm, dosagem=8 g L-1, pH 2, temperatura 30°C foi obtido um qeq experimental de 38,039 mg g-1 em um tempo de 10 horas. Na cinética do corante RABF-5G um qeq experimental de 57,473 mg g-1 foi obtido nas condições de C0= 400 mg L-1, Dp=0,725 mm, dosagem=6 g L-1, pH 2, temperatura 30°C em 24 horas. O modelo de pseudo-segunda ordem representou melhor a cinética de ambos os corantes, apresentando R2 de 0,989. O modelo de isoterma de Langmuir para a temperatura de 30oC apresentou capacidade máxima de adsorção de 44,356 mg g-1 e 72,427 mg g-1, para os corantes RCS-HEXL e RABF-5G, respectivamente. A casca de soja por ser um subproduto agroindustrial de baixo custo demonstra ser um adsorvente potencial para a remoção dos corantes têxteis investigados.

A casca de pinhão manso é um resíduo abundante da indústria de biocombustível e foi usada em sua forma natural (PN) e tratada por plasma não térmico (PP) como biossorvente para a remoção do corante Vermelho reativo 120 (VR-120) de soluções aquosas. Os nanotubos de carbono de parede múltipla (NTCPM) e carvão ativo (CA) foram investigados como adsorventes na remoção do corante Azul direto 53 (AD-53) a partir de águas residuais. Os materiais adsorventes foram caracterizados por espectroscopia Raman, espectroscopia de infravermelho, isotermas de adsorção/dessorção de N2, microscopia eletrônica de varredura e transmissão. As melhores condições para adsorção dos corantes foram alcançadas em pH 2,0. O tempo de contato para obter o equilíbrio de isotermas, em 298-323 K, foi fixado em 10 horas para os biossorventes PN e PP. Para estes, o modelo cinético de ordem geral forneu o melhor ajuste aos dados experimentais em comparação com as cinéticas pseudo-primeira ordem e pseudo-segunda ordem. Para o corante VR-120, os dados de equilíbrio (298-323 K) foram ajustados para o modelo de isoterma de Liu. A capacidade máxima de adsorção do corante ocorreu a 323 K, atingindo valores de 40,94 e 65,63 mg g-1 para o PN e PP, respectivamente. Os resultados dos estudos de adsorção/dessorção mostraram que a maior porcentagem de remoção de PN e PP foram alcançadas quando a mistura de solventes (acetona a 50% + 50% de 0,050 mol L-1 de NaCl (v/v)) foi utilizada. Os efluentes simulados foram utilizados para verificar a aplicabilidade dos biossorventes propostos. A remoção ocorreu de 68,2 e 94,6%, para PN e PP, respectivamente, em meio com elevada concentração salina. Já para NTCPM e CA os tempos de contato foram fixados em 3 horas e 4 horas, respectivamente. O modelo da cinética de ordem geral forneceu o melhor ajuste aos dados experimentais, se comparado aos modelos de adsorção cinéticos de pseudoprimeira ordem e pseudo-segunda ordem. Para o corante AD-53, os dados no equilíbrio (298-323 K) foram ajustados pelo modelo de isoterma de Sips. A capacidade máxima de adsorção do corante ocorreu a 323 K, com os valores de 409,4 e 135,2 mg g-1 para NTCPM e CA, respectivamente. Os resultados dos estudos de adsorção/dessorção mostraram que os NTCPM carregados com AD-53 podem ser regenerados (97,85%) utilizando uma solução de acetona aquosa (50% de acetona + 50% NaOH 3 mol L-1 (v/v)). Em experimentos de simulação de efluentes têxteis para aplicação dos adsorventes no tratamento de efluentes industriais, foram obtidas as remoções de 99,87% e 97,00% para NTCPM e CA, respectivamente, num meio com alta salinidade e diversos corantes. / Jatropha curcas shell an abundant residue of the biocombustible industry, was used in its natural form (JN) and treated by non-thermal plasma (JP) as biosorbents for the removal of Reactive Red 120 (RR-120) dye from aqueous solutions. Multi-walled carbon nanotubes (MWCNT) and powder activated carbon (PAC) were used as adsorbents for adsorption of Direct Blue 53 dye (DB-53) from aqueous solutions. The adsorbents were characterised using Raman spectroscopy, infrared spectroscopy, N2 adsorption/desorption isotherms, and scanning and transmission electron microscopy. The best conditions to adsorption of the dye by adsorbent were achieved at pH 2.0. The contact time to obtain equilibrium isotherms at 298–323 K was fixed at 10 h for both biosorbents. The general order kinetic model provided the best fit to the experimental data compared with pseudo-first order and pseudo-second order kinetic adsorption models. For RR-120 dye, the equilibrium data (298–323 K) were best fitted to the Liu isotherm model. The maximum sorption capacity for adsorption of the dye occurred at 323 K, attaining values of 40.94 and 65.63 mg g−1 for JN and JP, respectively. The results of adsorption/desorption studies showed that the highest percentage of removal of JN and JP were obtained when the mixture of solvents (acetone 50% + 50% 0.050 mol L-1 NaCl (v/v)) was used. Simulated dyehouse effluents were used to check the applicability of the proposed biosorbents for effluent treatment. The removal was 68.2 and 94.6% for JP and JN, respectively, in media with high salinity. As for NTCPM and CA the contact times were set at 3 h and 4 h, respectively. The general order kinetic model provided the best fit of the experimental data compared to pseudo-first order and pseudo-second order kinetic adsorption models. For DB- 53 dye, the equilibrium data (298 to 323 K) were best fitted to the Sips isotherm model. The maximum sorption capacity for adsorption of the dye occurred at 323 K, with the values of 409.4 and 135.2 mg g-1 for MWCNT and PAC, respectively. The results of adsorption/desorption studies showed that MWCNT loaded DB-53 could be regenerated (97.85%) using mixture 50% acetone + 50% of 3 mol L-1 NaOH (v/v). Simulated dye house effluents were used to evaluate the application of the adsorbents for effluent treatment, with removal of 99.87% and 97.00% for MWCNT and PAC, respectively.