Modifica??o de membranas de quitosana por plasma para uso biol?gicoMac?do, Marina de Oliveira Cardoso 30 April 2009 (has links)
Made available in DSpace on 2014-12-17T14:06:52Z (GMT). No. of bitstreams: 1
MarinaOCM.pdf: 1314082 bytes, checksum: d274baae2a0c41a00f40857ec722c88a (MD5)
Previous issue date: 2009-04-30 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / Chitosan membranes have been modified by plasma, utilizing the following gases: nitrogen (N2), methane (CH4), argon (Ar), oxygen (O2) and hydrogen. The modified membranes by plasma were compared to the unmodified ones. The membranes were characterized by absorption assay, contact angle, atomic force microscopy (AFM). Also, permeability assay of sodium sulfamerazine from such membranes
were carried out. Through the absorption assay and contact angle it was possible to obtain information of the wettability of the membranes and what changes the plasma treatment can promote in relation to it. The plasma treatment using oxygen promoted increase of the wetability and swelling while the samples treated with methane decrease of the wetability and swelling. Through the Optical Emission Spectroscopy
(OES) it was possible to identify which species were present in the plasma during the treatment. And through the AFM analysis it was possible to observe the changes
nanotopography occurred on the surface of the samples. Permeability assay were archived for all treated membranes and compared to no treated ones. Due to that assay it was possible verify which the plasma treatment increased the permeability spectrum of the membranes which has varied from 1,4548 *10-5cm2.min-1 to 2,7713*10-5cm2.min-1. Chitosan membranes with permeability varied are importance
in systems drug delivery, to liberate a wide variety of drugs / Membranas de quitosana foram modificadas por plasma, utilizando os seguintes gases: nitrog?nio (N2), metano (CH4), arg?nio (Ar), oxig?nio (O2) e hidrog?nio (H2). Membranas n?o tratadas foram utilizadas para compara??o com as tratadas. As amostras foram caracterizadas por ensaio de ganho de massa (capacidade de absor??o de ?gua), ?ngulo de contato, microscopia de for?a at?mica (MFA) e quanto ? sua permeabilidade em rela??o ao f?rmaco sulfamerazina de s?dio. Atrav?s dos ensaios de absor??o e ?ngulo de contato foi poss?vel obter informa??es sobre a molhabilidade das membranas e quais mudan?as o tratamento a plasma pode
promover em rela??o ? molhabilidade. O tratamento por plasma utilizando o oxig?nio promoveu um aumento da hidrofilicidade e do ganho de massa enquanto as amostras tratadas com metano tiveram uma diminui??o da hidrofilicidade e do ganho de massa. Atrav?s da Espectroscopia de Emiss?o ?tica (EEO) identificaram-se
quais esp?cies estavam presentes no plasma durante o tratamento, pois estas influenciam o grau de molhabilidade das amostras, tornando-as mais hidrof?licas ou hidrof?bicas atrav?s da inser??o de grupos funcionais. Nos resultados da MFA foi poss?vel observar as modifica??es nanotopogr?ficas ocorridas na superf?cie das amostras, como o aumento da rugosidade em amostras tratadas com hidrog?nio e a
diminui??o dessa rugosidade nas amostras tratadas com arg?nio. Ensaios de permea??o foram realizados para todas as membranas tratadas e comparados com as membranas n?o tratadas. Atrav?s desse ensaio foi poss?vel verificar que os
tratamentos a plasma ampliaram o espectro de permeabilidade das membranas que variou de 1,4548 *10-5cm2.min-1 a 2,7713*10-5cm2.min-1. As amostras tratadas com oxig?nio apresentaram a menor permeabilidade enquanto que a amostras tratada com arg?nio apresentaram a maior permeabilidade. A obten??o de membranas de quitosana com permeabilidade variada ? de grande import?ncia na tecnologia de libera??o de f?rmacos, pois as mesmas podem ser utilizadas nos mais diversos sistemas carreadores de f?rmacos. Liberando uma ampla variedade de f?rmacos
e/ou agente bioativos
|
222 |
An?lise de propriedades t?rmicas e mec?nicas de comp?sitos de argamassa e res?duo de borrachaFerreira, Carlos Ren? Gomes 21 August 2009 (has links)
Made available in DSpace on 2014-12-17T14:06:53Z (GMT). No. of bitstreams: 1
CarlosRG.pdf: 3095179 bytes, checksum: 8f85422621006a6dd669bfabb5747ac9 (MD5)
Previous issue date: 2009-08-21 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / Although already to exist alternative technique and economically viable for destination of used tires, quantitative data on properties of constructive elements that use the rubber waste as aggregate still are restricted. In the present work, the waste proceeding from industry of retreading as material for manufacture of composite destined to the production of constructive elements was considered. Mechanical and thermal properties of mortar had been analyzed Portland cement with addition of waste without treatment, in the ratios of 10%, 20% and 30% in mass in relation to the mass of the cement, substituting the aggregate in the trace in mortar 1:5 mass cement and sand. The size of the used residue varied between 0,30mm and 4,8mm (passing in the bolter 4,8mm and being restrained in the one of 0,30mm), being it in the formats fibers and granular. The influences of the size and the percentage of residue added to the mortar (in substitution to the aggregate) in the thermal and mechanical properties had been considered. Assays of body-of-test in thestates had been become fullfilled cool (consistency index) and hardened (absorption of water for capillarity, strength the compression, traction and strength flexural). The work is centralized in the problem of the relation thermal performance /strength mechanics of used constructive systems in regions of low latitudes (Been of the Piau?), characterized for raised indices of solar radiation. / Apesar de j? existirem alternativas t?cnica e economicamente vi?veis para destina??o de pneum?ticos usados, dados quantitativos sobre propriedades de elementos construtivos que utilizam o res?duo de borracha como agregado ainda s?o restritos. No presente trabalho, considerou-se o res?duo proveniente de ind?stria de recauchutagem como material para fabrica??o de comp?sito destinado ? produ??o de elementos construtivos. Foram analisadas propriedades mec?nicas e t?rmicas de argamassa de cimento Portland com adi??o de res?duo sem tratamento, nas propor??es de 10%, 20% e 30% em massa em rela??o ? massa do cimento, substituindo o agregado no tra?o em massa 1:5 de argamassa cimento e areia. A granulometria do res?duo utilizado variou entre 0,30mm e 4,8mm (passando na peneira 4,8mm e ficando retido na de 0,30mm), sendo ele nos formatos fibroso e granular. Consideraram-se as influ?ncias da granulometria e do percentual de res?duo adicionado ? argamassa (em substitui??o ao agregado) nas propriedades t?rmicas e mec?nicas. Realizaram-se ensaios de corpos-deprova nos estados fresco (?ndice de consist?ncia) e endurecido (absor??o de ?gua por capilaridade, resist?ncia a compress?o e tra??o). O trabalho est? focado no problema da rela??o desempenho t?rmico /resist?ncia mec?nica de sistemas construtivos utilizados em regi?es de baixas latitudes (Estado do Piau?), caracterizadas por elevados ?ndices de radia??o solar.
|
223 |
Avalia??o espectrofotom?trica do manchamento de resinas odontol?gicas contendo nanopart?culas / Avalia??o espectrofotom?trica do manchamento de resinas odontol?gicas contendo nanopart?culasGomes, Larissa Bezerra de Mesquita 02 June 2010 (has links)
Made available in DSpace on 2014-12-17T14:06:55Z (GMT). No. of bitstreams: 1
LarissaBMG_DISSERT.pdf: 3976426 bytes, checksum: c7a9c5605953e13f9ff21ef4453a3aef (MD5)
Previous issue date: 2010-06-02 / Composite resins have been subjected to structural modifications aiming at
improved optical and mechanical properties. The present study consisted in an in vitro
evaluation of the staining behavior of two nanohybrid resins (NH1 and NH2), a
nanoparticulated resin (NP) and a microhybrid resin (MH). Samples of these materials
were prepared and immersed in commonly ingested drinks, i.e., coffee, red wine and
acai berry for periods of time varying from 1 to 60 days. Cylindrical samples of each
resin were shaped using a metallic die and polymerized during 30 s both on the bottom
and top of its disk. All samples were polished and immersed in the staining solutions.
After 24 hours, three samples of each resin immersed in each solution were removed
and placed in a spectrofotome ter for analysis. To that end, the samples were previously
diluted in HCl at 50%. Tukey tests were carried out in the statistical analysis of the
results. The results revealed that there was a clear difference in the staining behavior of
each material. The nanoparticulated resin did not show better color stability compared
to the microhybrid resin. Moreover, all resins stained with time. The degree of staining
decreased in the sequence nanoparticulated, microhybrid, nanohybrid MH2 and MH1.
Wine was the most aggressive drink followed by coffee and acai berry. SEM and image
analysis revealed significant porosity on the surface of MH resin and relatively large
pores on a NP sample. The NH2 resin was characterized by homogeneous dispersion of
particles and limited porosity. Finally, the NH1 resin depicted the lowest porosity level.
The results revealed that staining is likely related to the concentration of inorganic pa
rticles and surface porosity / Nos ?ltimos anos, as resinas compostas t?m passado por uma s?rie de
modifica??es estruturais na busca de melhores propriedades ?pticas e mec?nicas. O
presente estudo avaliou in vitro o grau de manchamento em duas resinas nanoh?bridas
(NH1 e NH2), uma nanoparticulada (NP) e uma microh?brida (MH), quando expostas ?s
solu??es corantes, caf?, vinho tinto e a?a?, nos per?odos de 1, 7, 30 e 60 dias. Foram
confeccionadas 192 amostras atrav?s de uma matriz met?lica e realizadas duas
polimeriza??es de 30s cada, sendo uma na base da amostra, e a outra no lado oposto
dela. As amostras foram ent?o analisadas por microscopia eletr?nica de varredura. Foi
visualizada uma grande quantidade de poros na resina MH e presen?a de poros ainda
maiores na NP. J? a resina NH2 mostrou uma melhor distribui??o de part?culas e menor
quantidade de poros, mas a NH1 foi a que apresentou um menor n?vel de porosidade.
Em seguida, as amostras passaram pela sequ?ncia de discos de acabamento, discos de
feltro com pasta polidora e imersas nas solu??es corantes. Aguardando-se o primeiro
per?odo de 24h, foram escolhidas aleatoriamente tr?s amostras de cada recipiente e
submetidas ? leitura do espectrofot?metro. Para a leitura, as amostras foram
previamente dilu?das em HCl a 50%. A cada 5 dias, as solu??es foram trocadas. Foram
utilizados os testes de Tukey para an?lise estat?stica de vari?ncia. De acordo com a
metodologia proposta, foi poss?vel verificar que houve diferen?a significativa no
manchamento superficial quando os 4 comp?sitos foram comparados ap?s os intervalos
de tempo estudados. A resina nanoparticulada (NP) estatisticamente n?o apresentou
desempenho superior ao comp?sito microh?brido (MH). Todos os comp?sitos
mostraram certa quantidade de manchamento com o decorrer do tempo, a resina
composta exclusivamente nanoparticulada (NP), foi a que apresentou o maior
manchamento, seguido da resina microh?brida (MH) e da nanoh?brida NH2 e, por
?ltimo, o nanoh?brida da NH1. Os resultados sugerem que o grau de manchamento
pode estar relacionado com a porosidade e a concentra??o de part?culas de carga da
resina. Dos meios de imers?o, o que mais influenciou no grau de manchamento foi o
vinho tinto, seguido do caf? e do a?a?
|
224 |
Desenvolvimento de um sistema de nitreta??o por plasma em fonte pulsada e sua influencia sobre a nitreta??o do tit?nioOliveira, Jos? Antonio Bernardino de 15 October 2011 (has links)
Made available in DSpace on 2014-12-17T14:06:56Z (GMT). No. of bitstreams: 1
JoseABO_DISSERT.pdf: 1955916 bytes, checksum: ab738b441db6538b6bc4159b47e66186 (MD5)
Previous issue date: 2011-10-15 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / The pulsed plasma nitriding is a solution currently used in the metallurgical industry to resolve problems earlier in the processing of parts by using plasma DC voltage. These problems consisted mainly of edge effect and opening arches caused due to non-uniformity of electric fields on uneven surfaces. By varying the pulse width can reduce these effects. However, variations in pulse width can drastically affect the population of the plasma species and hence the final microstructure of the nitrided layer. In literature, little is known about the effect of process parameters on the properties of the plasma species and, consequently, the surface properties. We have developed a system of nitriding with pulsed source with fixed period of 800  pulse width is variable. Examined the variation of these parameters on the properties of nitrided surface when keeping constant temperature, gas composition, flow, pressure and power. It was found that the values of width and pulse repetition time of considerable influence in the intensities of the species present in plasma. Moreover, we observed the existence of the edge effect for some values of pulse widths, as well as changes in surface roughness and hardness / A nitreta??o por plasma pulsado ? uma solu??o utilizada atualmente na ind?stria metal?rgica para resolver problemas existentes anteriormente durante tratamento de pe?as usando plasma de tens?o cont?nua. Esses problemas consistiam, principalmente, em efeito de bordas e abertura de arcos causados devido a n?o uniformidade de campos el?tricos em superf?cie irregular. Atrav?s da varia??o da largura do pulso ? poss?vel reduzir estes efeitos. Entretanto, as varia??es de largura de pulso podem afetar drasticamente a popula??o de esp?cies do plasma e, conseq?entemente, a microestrutura da camada nitretada final. Na literatura, pouco se sabe sobre o efeito dos par?metros do processo nas propriedades das esp?cies do plasma e, conseq?entemente, nas propriedades superficiais. Neste trabalho foi desenvolvido um sistema de nitreta??o com fonte pulsada com per?odo fixo de 800 s e largura de pulso vari?vel. Analisou a varia??o desses par?metros sobre as propriedades da superf?cie nitretada quando se mant?m constantes a temperatura, composi??o do g?s, fluxo, press?o e pot?ncia. Verificou-se que os valores da largura e tempo de repeti??o do pulso influem fortemente nas intensidades das esp?cies presentes no plasma. Al?m disto, foi observada a exist?ncia do efeito de borda para alguns valores de larguras de pulso, bem como varia??o na rugosidade e dureza superficiais
|
225 |
Estudo sobre a influ?ncia do massar? no processo de forma??o de salitre em rebocos na regi?o de Teresina - PIFernandes, Paulo Henrique Campos 20 December 2010 (has links)
Made available in DSpace on 2014-12-17T14:06:56Z (GMT). No. of bitstreams: 1
PauloHCF_DISSERT.pdf: 1512576 bytes, checksum: ec50ef7eb7dc51a6d221e75854fea430 (MD5)
Previous issue date: 2010-12-20 / This work had to verify the influence of massar?, while mortar component, in the process of formation of saltpeter in cementitious plaster walls of buildings. The massar? is a ceramic material, texture areno usually found in large volumes argillaceous sediments in Teresina, Piaui State capital, which is associated with the Portland cement mortar form for fixing and finishing in construction. Saltpeter or flowering is a pathology that happens in gypsum wallboard, which invariably reaction between soluble salts present in materials, water and oxygen. This pathology, supposedly credited to massar? caused its use to suffer significant reduction in the market of the buildings. Verify this situation with particular scientific rigor is part of the proposal of this work. Grading tests Were performed, consistency limits (LL, LP and IP), determination of potential hydrogen, capacity Exchange (CTC), electrical conductivity (EC), x-ray fluorescence (FRX) and x-ray diffraction (DRX). Massar? analysed samples in number six, including sample plastering salitrado presented potential hydrogen medium 5.7 in water and 5.2 on KCl n and electrical conductivity (EC), equal to zero. These results pointed to the affirmative that massar? is a material that does not provide salinity content that can be taken into consideration. It is therefore concluded that the material analyzed not competing, at least with respect to the presence of soluble salts, for the formation of saltpeter / Este trabalho teve o objetivo de verificar a influ?ncia do massar?, enquanto componente de argamassa, no processo de forma??o do salitre em rebocos de paredes de edifica??es. O massar? ? um material cer?mico, geralmente de textura areno argilosa encontrado em grandes volumes na cidade de Teresina, capital do Estado do Piaui, que associado ao cimento portland, forma argamassa para assentamento e para reboco na constru??o civil. O salitre ou floresc?ncia ? uma patologia que acontece nos rebocos, provindo, invariavelmente, da rea??o entre sais sol?veis presentes nos materiais, ?gua e oxig?nio. Esta patologia, supostamente creditada ao massar? fez com que seu uso sofresse redu??o significativa no mercado das edifica??es. Verificar esta situa??o com determinado rigor cient?fico faz parte da proposta deste trabalho.
Foram executados ensaios de granulometria, limites de consist?ncia (LL, LP e IP), determina??o do potencial de hidrog?nio (pH), capacidade de troca de c?tions (CTC), condutividade el?trica (CE), fluoresc?ncia de raios X (FRX) e difra??o de raios X (DRX).
As amostras de massar? analisadas, em n?mero de seis, inclusive amostra de reboco salitrado, apresentaram potencial de hidrog?nio (pH) m?dio igual a 5,7 em ?gua e 5,2 em KCl N e condutividade el?trica (CE), igual a zero. Estes resultados apontaram para a afirmativa que o massar? ? um material que n?o apresenta teor de salinidade que possa ser levado em considera??o. Conclui-se, portanto, que o material analisado n?o concorre, pelo menos com rela??o ? presen?a de sais sol?veis, para a forma??o do salitre
|
226 |
Desevolvimento de nanocomp?sitos de poli(metacrilato de metila)/argila processados por mistura no estado fundidoMedeiros, Antonio Marcos de 15 October 2010 (has links)
Made available in DSpace on 2014-12-17T14:06:57Z (GMT). No. of bitstreams: 1
AntonioMM_DISSERT.pdf: 3167534 bytes, checksum: a8247e394e6c3656375c3f16b429e065 (MD5)
Previous issue date: 2010-10-15 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / Poly(methyl methacrylate)/clay nanocomposites were prepared by melt mixing using a
montmorillonite-rich clay (MMT). The clay in natura was treated with acrylic acid to
facilitate the dispersion in the polymer matrix. A masterbatch of PMMA/clay was prepared
and combined with the pure PMMA and then subjected to extrusion process using singlescrew
and twin-screw extruders followed by injection. Nanocomposites were processed with
clay contents of 1, 3, 5 and 8 wt.%. The effect of shear processing on the morphology of the
nanocomposites was evaluated by XRD, SEM and TEM. Thermal and mechanical properties
of the nanocomposites were investigated through TGA, DSC, HDT, VICAT, tensile and
impact tests, to evaluate the effect of the addition of clay to the PMMA matrix. Flammability
tests were also conducted to investigate the effect of the addition of clay on the flame
retardation properties. SEM images of the nanocomposites indicated the presence of clay
agglomerates, which resulted in the reduction of properties such as thermal stability,
mechanical strength and impact resistance, and increased the rate of burning for materials
processed by both extrusion routes / Nanocomp?sitos de poli(metacrilato de metila) (PMMA) foram preparados a partir da
t?cnica de mistura no estado fundido com argila rica em montmorilonita (MMT). A argila in
natura foi inicialmente tratada com ?cido acr?lico para facilitar a dispers?o na matriz
polim?rica. Depois, foi preparado um concentrado de PMMA e argila que foi combinado com
o PMMA puro e submetido ao processo de extrus?o realizado em extrusoras monorosca e
dupla rosca com posterior inje??o. Nanocomp?sitos foram processados com 1, 3, 5 e 8% em
massa de argila. O efeito do cisalhamento sobre a morfologia dos nanocomp?sitos foi
avaliado por DRX, MEV e MET. Para avaliar o efeito da adi??o de argila na matriz de
PMMA foram investigadas propriedades t?rmicas e mec?nicas, atrav?s de an?lises de TG,
DSC, HDT, VICAT, tra??o e impacto. Ensaios de inflamabilidade foram tamb?m realizados
para investigar o efeito da adi??o de argila sobre as propriedades de retardo de chama. As
an?lises morfol?gicas mostraram a presen?a de aglomerados de argila distribu?dos na matriz
de PMMA, o que resultou na redu??o de propriedades como estabilidade t?rmica, resist?ncia
mec?nica e ao impacto, e elevou a taxa de queima para os materiais processados por ambas as
rotas de extrus?o
|
227 |
Aproveitamento de res?duos minerais na formula??o de argamassas para a constru??o civilSantos, Maria Luiza Lopes de Oliveira 25 August 2008 (has links)
Made available in DSpace on 2014-12-17T14:06:57Z (GMT). No. of bitstreams: 1
MariaLLOS.pdf: 1560615 bytes, checksum: 3380ba58cfe3314d3e58ae0d9f253793 (MD5)
Previous issue date: 2008-08-25 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / Current environmental concerns include the excessive consumption and inefficient use of non-renewable natural resources. The construction industry is considered one of the largest consumers of natural raw materials, significantly contributing to the environmental degradation of the planet. The use of calcareous quarry (RPPC) and porcelain tile polishing residues (RPP) as partial replacements of the cement in mortars is an interesting alternative to minimize the exploration of considerably large amounts of natural resources. The present study aimed at investigating the properties of fresh and hardened mortars produced using residues to replace cement. The residues used were fully characterized to determine their specific mass, unitary mass, particle size distribution and morphology, and composition. The
performance of the mortars was compared to that of reference compositions, prepared without residues. A total of 18 compositions were prepared, 16 using residues and 2 reference ones. The mortars were prepared using Portland CP II F 32 cement, CH I hydrated lime, river sand and tap water. The compositions of the mortars were 1:1:6 and 1:0.5:4.5 (vol%), and water to cement ratios of 1.87 and 1.45 were used, respectively. The mortars in the fresh state were evaluated by consistency index, water retention, density of mass and incorporated air content tests. In their hardened state, the mortars were evaluated by apparent mass density, modulus of elasticity, flexural tensile strength, compressive strength and water absorption by capillarity. The mortars were also analyzed by scanning electron microscopy, energy dispersive spectroscopy, X-ray diffraction and fluorescence. Finally, they were classified according to NBR 13281 standards. The mortars prepared using residues partially replacing the cement exhibited lower modulus of elasticity compared to the reference compositions, thus improving the performance in their intended use. On the downside, the water absorption by capillarity was affected by the presence of residues and both the tensile and compressive
strength were reduced. However, from the overall standpoint, the replacement of cement by calcareous quarry or porcelain tile polishing residues did not result in significant changes in the properties of the mortars. Therefore, compositions containing these residues can be used in the construction industry / A preocupa??o ambiental diz respeito, entre outras coisas, ao consumo excessivo ou ineficiente de recursos naturais n?o-renov?veis (LEITE, 2001). A ind?stria da constru??o civil
? considerada como a maior consumidora de mat?rias-primas naturais, contribuindo assim, de maneira relevante, para uma maior degrada??o do meio ambiente. A utiliza??o do res?duo de
pedreira de rocha calc?ria (RPPC) e res?duo do polimento do porcelanato (RPP), em substitui??o parcial do cimento, pode ser um caminho alternativo para minimiza??o deste problema. Esta pesquisa teve como objetivo estudar as propriedades no estado fresco e endurecido das argamassas mistas produzidas com res?duos (RPPC e RPP), comparando o desempenho das mesmas com as argamassas de refer?ncia. Na produ??o dessas argamassas se utilizou o cimento Portland CP II F 32, cal hidratada CH I, areia de rio e ?gua da concession?ria local. Os res?duos utilizados foram caracterizados quanto a massa espec?fica, massa unit?ria, granulometria a laser,microscopia eletr?nica de varredura, difratometria de raios-X e fluoresc?ncia de raios-X. Os tra?os utilizados foram 1:1:6 e 1:0,5:4,5, ambos em volume, com a rela??o ?gua/cimento fixada, respectivamente, em 1,87 e 1,45. Foram produzidas 18 composi??es de argamassas, 16 utilizando RPPC e RPP e 02 composi??es convencionais que serviram de refer?ncia. Com as argamassas no estado fresco, foram realizados os ensaios de ?ndice de consist?ncia, reten??o de ?gua, densidade de massa e teor de ar incorporado. J? no estado endurecido, os ensaios realizados foram: densidade de massa aparente, m?dulo de elasticidade, resist?ncia ? tra??o na flex?o, resist?ncia ? compress?o e absor??o de ?gua por capilaridade. As argamassas foram analisadas por microscopia eletr?nica de varredura, espectroscopia de raios-X por energia dispersiva (EDS), difra??o de raios-X e fluoresc?ncia de raios-X. Al?m disso, foram classificadas quanto aos padr?es estabelecidos pela NBR 13281 (ABNT, 2005). Os resultados encontrados mostram que as argamassas formuladas com res?duos n?o sofreram altera??es significativas no que se refere ao ?ndice de consist?ncia, reten??o de ?gua, densidade de massa no estado fresco, teor de ar incorporado e densidade de massa aparente no estado endurecido. J? em rela??o ao m?dulo de elasticidade a presen?a dos res?duos na mistura ocasionou a diminui??o do mesmo, melhorando assim o desempenho da argamassa. Por?m, a resist?ncia ? tra??o na flex?o e ? resist?ncia ? compress?o, al?m da absor??o de ?gua por capilaridade, tiveram o seu desempenho comprometidos
|
228 |
Estudo de revestimentos inorg?nicos com inibidor de corros?o aplicado na superf?cie do concretoNunes, Pollyanna Tha?s Tavares Batista 01 July 2011 (has links)
Made available in DSpace on 2014-12-17T14:06:58Z (GMT). No. of bitstreams: 1
PollyannaTTBN_DISSERT.pdf: 3294347 bytes, checksum: 23d933599f7d6d6327054ef468580147 (MD5)
Previous issue date: 2011-07-01 / The corrosive phenomenon on reinforced concrete structures is one of the
most founded pathologies on the coastal area. With the objective to prevent the
process development, or even, retard its beginning, it was studied the application of
inorganic covering over concrete surfaces, after its cure, as well as, evaluate the
efficiency of the covering applied on the concrete in reducing its porosity of concrete
preventing the entrance of aggressive agents to preserve the integrity of the existing
armor inside it, comparing the result obtained with the body-of-proof reference, that
didn?t receive covering protection. On the concrete production it was used Portland
Cement CP II 32, coarse aggregate, fine aggregate and water from the local
distributive. Two types of covering were used, one resin based of silicon and solvent
and other white cement based, selected sands and acrylic resin. The concrete
mixture adopted was 1:1,5:2,5 (cement, fine aggregate, coarse aggregate) and 0.50
water/cement ratio. With the concrete on fresh state was made the experiment test
to determinate the workability. On the hardened state was made the concrete
resistance experiment, absorption of water and electrochemical experiments,
through polarization curves. Also was held optical microscopy and Scanning Electron
Microscopy experiments to analyze the layer of the covering applied to the concrete
surface and the interface between the concrete and the layer. The obtained results
shows that the covering applied to the concrete surface didn?t affect the resistance
towards compression. On the absorption of water occurred a diminution of the
percentage absorbed, improving the concrete development by making it more
impermeable towards the entrance of aggressive agents. The electrochemical
experiment results confirmed the water absorption results; the body-of-proof covered
presented larger protection towards the development of corrosives process and
retarded the evolution of the corrosive phenomenon / O fen?meno de corros?o em estruturas de concreto armado ? uma das
patologias mais encontradas em ?reas litor?neas. Com o objetivo de impedir que o
processo se desenvolva ou mesmo retardar o seu in?cio, estudou-se a aplica??o de
revestimentos inorg?nicos sobre a superf?cie do concreto, ap?s sua cura, bem como,
foi avaliado a efici?ncia dos revestimentos aplicados a superf?cie do concreto em
reduzir a sua porosidade, impedindo a entrada dos agentes agressivos para
preservar a integridade da armadura existente no seu interior, comparando o
resultado obtido com corpos-de-prova refer?ncia, que n?o receberam nenhum
revestimento de prote??o. Na produ??o do concreto utilizou-se o Cimento Portland
CP II F 32, agregado gra?do, agregado mi?do e ?gua da concession?ria local.
Como revestimentos foram utilizados dois tipos, um ? base de resina de silicone e
solvente e o outro, ? base de cimento branco, areias selecionadas e resina acr?lica.
O tra?o adotado para o estudo foi 1:1,5:2,5 (cimento, areia e brita) e rela??o a/c =
0,50. Com o concreto no estado fresco, realizou-se o ensaio de abatimento de
tronco de cone para determina??o da trabalhabilidade. J? no estado endurecido,
realizou-se o ensaio de resist?ncia ? compress?o, absor??o de ?gua e os ensaios
eletroqu?micos, atrav?s de curvas de polariza??o. Tamb?m foram realizados ensaios
de Microscopia ?ptica e Microscopia Eletr?nica de Varredura para an?lise da
camada de revestimento aplicada ? superf?cie do concreto e a interface entre o
concreto e a camada. Os resultados obtidos mostram que os revestimentos
aplicados ? superf?cie do concreto n?o afetaram a resist?ncia ? compress?o. J? em
rela??o ? absor??o de ?gua houve uma diminui??o do percentual absorvido,
melhorando o desempenho do concreto por torn?-lo mais imperme?vel ? entrada
dos agentes agressivos. Os resultados dos ensaios eletroqu?micos confirmaram o
resultado do ensaio de absor??o de ?gua; os CP?s revestidos apresentaram uma
maior prote??o ao desenvolvimento de processos corrosivos e retardaram a
evolu??o do fen?meno de corros?o
|
229 |
Caracteriza??o de atapulgita visando aplica??o para refor?o de materiais polom?ricosCosta, Antonio Carlos Silva da 14 March 2011 (has links)
Made available in DSpace on 2014-12-17T14:07:00Z (GMT). No. of bitstreams: 1
AntonioCSC_DISSERT.pdf: 3611638 bytes, checksum: 66d2009e96e503fa1be4ca56924e34a1 (MD5)
Previous issue date: 2011-03-14 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / The clay mineral attapulgite is a group of hormitas, which has its
structures formed by microchannels, which give superior technological
properties classified the industrial clays, clays of this group has a very versatile
range of applications, ranging from the drilling fluid for wells oil has applications
in the pharmaceutical industry. Such properties can be improved by activating
acid and / or thermal activation. The attapulgite when activated can improve by
up to 5-8 times some of its properties. The clay was characterized by X-ray
diffraction, fluorescence, thermogravimetric analysis, differential thermal
analysis, scanning electron microscopy and transmission electron microscopy
before and after chemical activation. It can be seen through the results the
efficiency of chemical treatment, which modified the clay without damaging its
structure, as well as production of polymer matrix composites with particles
dispersed atapugita / A atapulgita ? um argilomineral do grupo das hormitas, que tem suas
estruturas formadas por microcanais, que lhe conferem propriedades
tecnol?gicas superiores a argilas classificadas industriais, esse grupo de argilas
tem um leque de aplica??es muito vers?til, que vai de fluido de perfura??o para
po?os de petr?leo at? aplica??es na ind?stria farmac?utica. Tais propriedades
podem ser melhoradas por ativa??o acida e/ou ativa??o t?rmica. A atapulgita
quando ativada pode melhorar em at? de 5 a 8 vezes algumas de suas
propriedades. A argila foi caracterizada por difra??o de raios X, fluoresc?ncia,
an?lise termogravim?trica, an?lise t?rmica diferencial, microscopia eletr?nica
de varredura e microscopia eletr?nica de transmiss?o antes e depois da
ativa??o qu?mica. ? poss?vel observar, atrav?s dos resultados a efici?ncia do
tratamento qu?mico, que modificou a argila sem danificar sua estrutura, assim
como produ??o de composito de matriz polim?rica com part?culas dispersas de
atapugita
|
230 |
S?ntese de pigmentos cer?micos inorg?nicos nanom?tricos e encapsulados com estrutura core-shell pela rota dos precursores polim?ricosMac?do, D?rcia S?mia Santos Moura de 09 April 2012 (has links)
Made available in DSpace on 2014-12-17T14:07:02Z (GMT). No. of bitstreams: 1
DarciaSSMM_DISSERT.pdf: 2144091 bytes, checksum: 373e58cf1ee08b2c45a550ad627238d6 (MD5)
Previous issue date: 2012-04-09 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / The present work has as objective the development of ceramic pigments based
in iron oxides and cobalt through the polymeric precursor method, as well as
study their characteristics and properties using methods of physical, chemical,
morphological and optical characterizations.In this work was used iron nitrate,
and cobalt citrate as precursor and nanometer silica as a matrix. The synthesis
was based on dissolving the citric acid as complexing agent, addition of metal
oxides, such as chromophores ions and polymerization with ethylene glycol.
The powder obtained has undergone pre-ignition, breakdown and thermal
treatments at different calcination temperatures (700 ?C, 800 ?C, 900 ?C, 1000
?C and 1100 ?C). Thermogravimetric analyzes were performed (BT) and
Differential Thermal Analysis (DTA), in order to evaluate the term
decomposition of samples, beyond characterization by techniques such as BET,
which classified as microporous materials samples calcined at 700 ? C, 800 ? C
and 900 ? C and non-porous when annealed at 1000 ? C and 1100 ? C, X-ray
diffraction (XRD), which identified the formation of two crystalline phases, the
Cobalt Ferrite (CoFe2O4) and Cristobalite (SiO2), Scanning Electron
Microscopy (SEM) revealed the formation of agglomerates of particles slightly
rounded;and Analysis of Colorimetry, temperature of 700 ?C, 800 ?C and 900
?C showed a brown color and 1000 ?C and 1100 ?C violet / O presente trabalho tem como objetivo o desenvolvimento de pigmentos
cer?micos a base de ?xidos de ferro e cobalto atrav?s do m?todo dos
precursores polim?ricos, bem como o estudo de suas caracter?sticas e
propriedades atrav?s de m?todos de caracteriza??es f?sicas, qu?micas,
morfol?gicas e ?pticas. Neste trabalho foi utilizado nitrato de ferro e citrato de
cobalto como precursores e s?lica nanom?trica como matriz. A s?ntese foi
baseada na dissolu??o do ?cido c?trico, como agente complexante; adi??o dos
?xidos met?licos, como ?ons crom?foros e polimeriza??o com etileno glicol. O
P? obtido passou por pr?-calcina??o, desagrega??o e tratamentos t?rmicos em
diferentes temperaturas de calcina??o (700 ?C, 800 ?C, 900 ?C, 1000 ?C e 1100
?C). Foram feitas An?lises de Termogravimetria (TG) e An?lise T?rmica
Diferencial (DTA), a fim de se avaliar a termodecomposi??o das amostras,
al?m de caracteriza??es por t?cnicas como BET, que classificou como
materiais microporosos as amostras calcinadas a 700 ?C, 800 ?C e 900 ?C e
n?o porosos quando calcinados a 1000 ?C e 1100 ?C; Difra??o de Raios-X
(DRX), que identificou a forma??o de duas fases cristalinas, a Ferrita de
Cobalto (CoFe2O4) e a Cristobalita (SiO2); Microscopia Eletr?nica de Varredura
(MEV), que revelou a forma??o de aglomerados de part?culas ligeiramente
arredondadas; e an?lise de colorimetria na regi?o do UV-Vis?vel, verificando a
varia??o e o potencial de cromaticidade do pigmento que a temperaturas de
700 ?C, 800 ?C e 900 ?C apresentou a cor marrom e a 1000 ?C e 1100 ?C a cor
violeta
|