Submitted by Geyciane Santos (geyciane_thamires@hotmail.com) on 2015-10-02T14:43:08Z No. of bitstreams: 1 Dissertação - Antonio Cleiton Lopes da Silva.pdf: 4158609 bytes, checksum: df0a9c601a830a898dc186dd5c7baec7 (MD5) / Approved for entry into archive by Divisão de Documentação/BC Biblioteca Central (ddbc@ufam.edu.br) on 2015-10-02T20:01:05Z (GMT) No. of bitstreams: 1 Dissertação - Antonio Cleiton Lopes da Silva.pdf: 4158609 bytes, checksum: df0a9c601a830a898dc186dd5c7baec7 (MD5) / Approved for entry into archive by Divisão de Documentação/BC Biblioteca Central (ddbc@ufam.edu.br) on 2015-10-02T20:07:10Z (GMT) No. of bitstreams: 1 Dissertação - Antonio Cleiton Lopes da Silva.pdf: 4158609 bytes, checksum: df0a9c601a830a898dc186dd5c7baec7 (MD5) / Made available in DSpace on 2015-10-02T20:07:11Z (GMT). No. of bitstreams: 1 Dissertação - Antonio Cleiton Lopes da Silva.pdf: 4158609 bytes, checksum: df0a9c601a830a898dc186dd5c7baec7 (MD5) Previous issue date: 2014-03-31 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / In mechanistic analysis, the complex modulus is a parameter of fundamental importance for the construction of constitutive models of the behavior of asphalt concrete. Among the more modern options for obtaining it, are the bending tests to four points, widespread in Europe. As an alternative to national evaluation of these parameters, in this study is carried out four-points bending tests to obtain the dynamic modulus and phase angle of the asphalt concrete, employing conditions representative of the Amazônia on the coarse aggregate and temperature on the road surface, with almost 60 ° C for many hours a day. As aggregate, against a regional shortage of stone material, we used the ASAC - Synthesized Calcined Clay Aggregate, promising material in front of plenty of raw materials and feasibility financial and technical. As a result of the tests, it has been found dynamic modulus and phase angle at different frequencies and temperatures. Master curves were constructed by applying the principle of time-temperature superposition and data fit to a phenomenological model representing the dynamic module by a continuous function. Furthermore, it was demonstrated that some imperfections recorded by the device in low loads are not only noise or errors but arise from interference of natural vibration of the beam. Finally, considering the local conditions of temperature and traffic, the dynamic module presented abrupt change, showing a drop of up to 93.3 % in value, in which the surface appears very susceptible to permanent deformation, recurring problem in pavements local asphalt. / Na análise mecanicista, o módulo complexo é um parâmetro de importância fundamental para construção de modelos constitutivos do comportamento do concreto asfáltico. Dentre as opções mais modernas para sua obtenção, encontram-se os testes de flexão a quatro pontos, amplamente difundidos pela Europa. Como alternativa nacional para avaliação desses parâmetros, no presente estudo realiza-se testes de flexão a quatro pontos para obtenção do módulo dinâmico e ângulo de fase do concreto asfáltico, empregando-se condições representativas da Amazônia no tocante ao agregado graúdo e temperatura, que na superfície dos pavimentos alcança quase 60°C por longas horas do dia. Como agregado graúdo, ante a escassez regional de material pétreo, utilizou-se o ASAC – Agregado Sinterizado de Argila Calcinada, material promissor diante da abundância de matéria prima e viabilidade financeira e técnica. Como resultado dos testes, obteve-se pontualmente o módulo dinâmico e ângulo de fase a diversas frequências e temperaturas. Construíram-se curvas mestras aplicando-se o princípio da superposição tempo-temperatura e ajustaram-se os dados a um modelo fenomenológico, representando-se o módulo dinâmico por uma função contínua. Além disso, demonstrou-se que algumas imperfeições registradas pelo equipamento em condições de baixas solicitações não são apenas ruídos ou erros, mas decorrem da interferência da vibração natural da viga. Por fim, consideradas as condições locais de temperatura e tráfego, o módulo dinâmico apresentou variações abruptas, apresentando queda de até 93,3% em seu valor, situação em que o pavimento apresenta-se muito suscetível a deformações permanentes, problema recorrente nos pavimentos asfálticos locais.

Submitted by Divisão de Documentação/BC Biblioteca Central (ddbc@ufam.edu.br) on 2018-03-02T13:48:25Z No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Dissertação_Claudio A. P. Lima.pdf: 4892807 bytes, checksum: b82d422f5f06eb53d8ee36cb6f7715be (MD5) / Approved for entry into archive by Divisão de Documentação/BC Biblioteca Central (ddbc@ufam.edu.br) on 2018-03-02T13:48:38Z (GMT) No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Dissertação_Claudio A. P. Lima.pdf: 4892807 bytes, checksum: b82d422f5f06eb53d8ee36cb6f7715be (MD5) / Made available in DSpace on 2018-03-02T13:48:38Z (GMT). No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Dissertação_Claudio A. P. Lima.pdf: 4892807 bytes, checksum: b82d422f5f06eb53d8ee36cb6f7715be (MD5) Previous issue date: 2017-11-10 / FAPEAM - Fundação de Amparo à Pesquisa do Estado do Amazonas / The historical retrospective of the pavements in Manaus and an expressive fraction of the municipalities in the State of Amazonas proves its early structural failure due to the scarcity of petrous materials and sublayers with low support. Literature shows the use of industrial waste for soil stabilization, as well as gains in mechanical performance of asphalt mixtures as an alternative solution to the paving regions where there is shortage of aggregates and high cost on transportation of these materials. In the present work, the effect of industrial waste on the chemical and physical stabilization of a soil from the region of Iranduba/AM was evaluated, and on the asphalt concrete dosage, aiming to increase the capacity of support as well as the final destination of environmental liabilities. The waste used were carbide lime (LC), a by-product of acetylene gas produced in the Industrial Pole of Manaus (IPM) and the residue of Curauá fiber, a natural and region material used by the automobile indrustry. Beams were molded with soil and soil-lime, soil-fiber and soil-lime-fiber compositions, in proportions of 2% lime and 1,5% fiber, related to the dry soil mass. Curing of the samples was carried out in a oven for 24 and 48 hours at 60oC. It was also molded traditional asphalt concrete beams with the addition of carbide lime. The mechanical behavior was determined by the 4-point flexural test, considering regional traffic and temperature conditions. Results for soil compositions with industrial waste revealed an increase in the dynamic stiffness modulus, such as a decrease in the phase angle reflecting the negligible viscous portion of the natural material. The asphalt beams presented a contrary answer. The results of dynamic stiffness module of the traditional and alternative asphalt compositions were compared, according to the theory of Euller-Bernoulli. It was verified the perfect adjustment of the theoretical function with the experimental points. Therefore, the present work corroborates the technical feasibility of the use of carbide lime and Curauá fiber residue in pavement engineering. / O retrospecto histórico dos pavimentos de Manaus e de uma fração expressiva dos Municípios do Estado do Amazonas comprova a falência estrutural precoce, em virtude da escassez de materiais pétreos e de subcamadas com baixo suporte. A literatura mostra a utilização de resíduos industriais para estabilização de solos, assim como ganhos no desempenho mecânico de misturas asfálticas, como solução alternativa à pavimentação em regiões onde há a escassez de agregados e elevado custo de transporte desses materiais. Avaliou-se no presente trabalho o efeito de resíduos industriais na estabilização química e física de um solo proveniente da região de Iranduba/AM, e na dosagem de concreto asfáltico, visando ao aumento da capacidade de suporte, bem como à destinação final de passivo ambiental. Os resíduos utilizados foram a cal de carbureto (CC), subproduto do gás acetileno produzido em no Polo Industrial de Manaus (PIM), e o resíduo da fibra do Curauá, material natural e regional utilizado pela indústria automobilística. Moldaram-se vigas com solo e com as composições solo-cal, solo-fibra e solo-cal-fibra, nas proporções de 2% de cal e 1,5% de fibra, em relação à massa seca do solo. Realizou-se o processo de cura das amostras, em estufa, por 24hs e 48hs, a 60° C. Moldaram-se, também, vigas de concreto asfáltico tradicional e com a participação da cal de carbureto. Determinou-se o comportamento mecânico pelo ensaio de flexão a 4 pontos, considerando-se as condições de tráfego e temperatura regional. Os resultados para as composições do solo com resíduos industriais revelaram um aumento no módulo de rigidez dinâmico, tal como um decréscimo do ângulo de fase refletindo a insignificante parcela viscosa do material natural. Resposta contrária apresentaram as vigas asfálticas. Comparou-se os resultantes do módulo de rigidez dinâmico das composições asfálticas, tradicional e alternativa, segundo a teoria de Euller-Bernoulli. Verificou-se o perfeito ajuste da função teórica com os pontos experimentais. Portanto, o presente trabalho corrobora a viabilidade técnica do uso da cal de carbureto e do resíduo da fibra do curauá na engenharia de pavimentação.

Submitted by Cássia Santos (cassia.bcufg@gmail.com) on 2015-03-27T13:42:08Z No. of bitstreams: 2 Dissertação - Wanderlei Malaquias Pereira Júnior - 2014.pdf: 7970008 bytes, checksum: f601259b1df84616f459fd009136794b (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) / Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2015-03-27T15:44:42Z (GMT) No. of bitstreams: 2 Dissertação - Wanderlei Malaquias Pereira Júnior - 2014.pdf: 7970008 bytes, checksum: f601259b1df84616f459fd009136794b (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) / Made available in DSpace on 2015-03-27T15:44:42Z (GMT). No. of bitstreams: 2 Dissertação - Wanderlei Malaquias Pereira Júnior - 2014.pdf: 7970008 bytes, checksum: f601259b1df84616f459fd009136794b (MD5) license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) Previous issue date: 2014-08-21 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / The work is a contribution to the mechanical numerical modeling of concrete structures with steel fibers using constitutive models based on Damage Mechanics behavior. The same, presents the formulation of a model proposed Damage admits that the concrete as initially isotropic elastic material, but with the evolution of the damage process, the material exhibits plastic deformations, anisotropy and bimodularidad induced damage. The incorporation of fibers in the modeling is performed through a homogenization procedure. The constitutive model for the concrete as well as the homogenization technique for dealing with the case of fiber concrete are implemented on a structural analysis program bar finite element laminated in layers. The parametric identification of the constitutive model together with the proposed homogenization is carried out using experimental results from the literature. Finally, numerical analysis of reinforced concrete beams reinforced with steel fibers and subjected to bending are conducted to assess the applicability of the constitutive model considered in this work. An attempt is thus contribute to the study of the deformation of fibrous concrete beams in service, in order to aggregate results and discussions in a future proposal of Brazilian technical standard for this type of structure. / O trabalho trata de uma contribuição à modelagem numérica do comportamento mecânico de estruturas de concreto com fibras de aço utilizando modelos constitutivos baseados na Mecânica do Dano. O mesmo, apresenta a formulação de um modelo de Dano proposto que admite o concreto como material inicialmente isótropo e elástico, mas com a evolução do processo de danificação o material exibe deformações plásticas, anisotropia e bimodularidade induzidas pelo dano. A incorporação das fibras na modelagem é efetuada através de um procedimento de homogeneização. O modelo constitutivo para o concreto, assim como a técnica de homogeneização para tratar do caso do concreto com fibras são implementados em um programa para análise de estruturas de barras com elementos finitos estratificados em camadas. A identificação paramétrica do modelo constitutivo, juntamente com a proposta de homogeneização, é realizada utilizando resultados experimentais encontrados na literatura. Por fim, análises numéricas de vigas de concreto armado reforçado com fibras de aço e sujeitas à flexão são conduzidas no sentido de avaliar a aplicabilidade do modelo constitutivo tratado neste trabalho. Procura-se, assim, contribuir para o estudo da deformabilidade de vigas de concreto fibroso em serviço, com o intuito de agregar resultados e discussões numa futura proposta de norma técnica brasileira para este tipo de estrutura.

Este trabalho apresenta um estudo de aplicabilidade de diferentes critérios de falhas para materiais compósitos poliméricos reforçados, especificamente laminados compostos de fibras unidirecionais, submetidos a carregamento de flexão. Consiste inicialmente de um levantamento bibliográfico para descrever os principais mecanismos de falhas e como estes podem ser analisados. É realizada uma avaliação dos principais critérios de falhas existentes, em estudos de casos de vigas do material submetidas a esforços de flexão três pontos. Para tal avaliação utilizou-se o método dos elementos finitos, devido à complexidade da análise de tensões em compósitos poliméricos reforçados. Posteriormente foram implementadas rotinas computacionais para o cálculo de alguns dos critérios de falhas encontrados na literatura. Assim, analisou-se as potencialidades e limitações desses critérios nos estudos de caso abordados. / This work presents a study about the applicability of different failure criteria for laminated reinforced composite materials made of unidirectional fibers, under flexural loads. First, it is described the failure mechanisms of this material, and how this can be evaluated. Some of the most important failure criteria are tested for beams under flexural loads. Because of the complexity of composite stress analysis, it was used the Finite Element Method. After that, some computational routines were implemented to calculate the failure criteria. The advantages and limitations of these theories could be verified for the flexural case studies.

Elementos tipo sanduíche, com placas de argamassa projetada, têm sido utilizados na construção de edificações em alguns países, inclusive no Brasil, apresentando boas características de resistência mecânica, térmica e acústica. De maneira geral, a aplicação desse tipo de elemento tem se restringido a obras de edificações, sendo utilizado principalmente como painéis de fechamento, portantes ou não, existindo ainda um potencial a ser explorado em obras de infra-estrutura, tais como: muros de arrimo, canais, galerias e reservatórios de água. Apesar de ser um método utilizado na construção de edificações, existem dúvidas, tais como: resistência efetiva da argamassa projetada, colaboração entre as placas resistentes em função do tipo de núcleo, modo de combater os efeitos de retração da argamassa, etc. Apresenta-se neste trabalho um estudo sobre a resistência efetiva da argamassa projetada, no qual se obteve que a sua resistência é de aproximadamente 80% da resistência à compressão de corpos-de-prova cilíndricos. Realizaram-se ainda ensaios para analisar a ligação entre elementos tipo sanduíche e seu comportamento à flexão, que comprovam o bom desempenho estrutural. Acredita-se que essa técnica de construção sanduíche possa ser aplicada em obras de infra-estrutura de interesse social, trazendo vantagens tecnológicas e econômicas em relação a sistemas tradicionais / Sandwich–type elements, with plates made of projected mortar, have been used in the construction of buildings in some countries, including Brazil, showing expressive thermical, acoustical and mechanical strength characteristics. In general, the application of this kind of element have been limited to buildings, mainly used as cladding panels, with carrying load capacity or not, and have other potential uses in infra-structural works to be explored such as bearing walls, channels, and water reservoirs. Although it is a method that have been conventionally applied in the construction of buildings, there are uncertainties in some parameters, like the effective strength of the projected mortar, interaction between the plates related to the type of core, the mode against shrinkage of the mortar etc. It is showed in this work a study concerning the effective strength of the projected mortar. As a result of a series of tests in walls made of projected mortar, it is determined that the effective strength of the projected mortar is 80% of that one measured from cylindrical specimens in compression tests. As well, some tests have been executed to analise the bending behaviour and the connections between the plates of the sandwich-type specimens, which demonstrated a relatively high structural performance. It is believed that this technical solution can be well applied to public works of social interest, and can offer technological and economical advantages in contrast to the traditional systems

O sucesso da terapia reabilitadora com implantes requer um equilíbrio entre fatores biológicos e mecânicos. Os fatores biológicos são inúmeros, já os mecânicos associam-se à instabilidade da interface implante-intermediário protético. Com base nestas informações, este estudo busca criar um aparelho com o qual será possível avaliar e comparar a resistência e a estabilidade da interface implante-intermediário protético em implantes de diferentes tipos de sistema de conexão e componentes protéticos, após a aplicação de carga simulada, que será realizada por meio de um ensaio dinâmico de fadiga rotacional, também conhecido como flexão rotativa. Para a criação deste aparelho, vários procedimentos com base em princípios de usinagem CNC (Controle Numérico Computadorizado), engenharia elétrica e física foram utilizados. Os futuros testes e resultados, utilizando-se esse aparelho para realizar o ensaio de fadiga, serão publicados em trabalhos futuros. Para o desenvolvimento dos modelos de corpos de prova a serem analisados na máquina de ensaio, foram utilizados implantes do tipo hexágono externo (Neodent) de 3,75mm de diâmetro x 11.5mm de comprimento. Ao término do desenvolvimento, obteve-se um aparelho confiável, resistente e extremamente versátil; podendo-se facilmente variar a carga exercida e a frequência de rotação, sendo assim possível executar inúmeras combinações de ensaios de fadiga. Esse estudo demonstrou a possibilidade e viabilidade de desenvolver um aparelho adequado para realizar um ensaio de fadiga, de pequena dimensão (portátil) e a um custo significativamente inferior do que comprar um aparelho próprio para tal fim. / The success of a rehabilitation therapy with implant fixtures requires a balance between biological and mechanical factors. The biological factors are innumerable, however the mechanics associate it whit instability of the implant-abutment interface. On the basis of these information, the aim of this study is to create a device which it will be possible to evaluate and to compare the resistance and the stability of the implant-abutment interface whith implants of different connection system and abutments, after the simulated load application, that will be carried through a dynamic assay of rotational fatigue load, also known as rotary bending. For the creation of this device, some procedures on the basis of principles of milling CNC (Computerized Numerical control), electric and physical engineering had been used. The future tests and results, using this device to carry through the fatigue assay, will be published in future works. For the development of the body test to be analyzed in the assay machine, implant fixtures of external hexagon type (Neodent) of 3,75mm of diameter x 11mm of length had been used. In the ending of the development, a trustworthy, resistant and extremely versatile device was gotten; being able itself easily to vary the exerted load and the frequency of rotation, being been thus possible to execute innumerable combinations of fatigue assays. This study demonstrated the possibility and viability of it developing an adequate device to carry through an assay of fatigue, of small dimension (portable) and the significantly inferior cost of what if to buy a proper device for such end.

A obtenção de cerâmicas de SiC pela sinterização com a presença de aditivos que promovam a formação de uma fase líquida (SFL) durante o processo tem sido uma forma adequada para garantir a menor temperatura de sinterização. Pelo fato de o SiC ser frágil, a busca por melhores propriedades mecânicas e avaliação correta das mesmas, para ser aplicado em ambientes agressivos, é contínua. Com base nisso, na primeira etapa, foram estudados, quanto à molhabilidade sobre o SiC, os sistemas AlN/Re2O3 (Re = Dy, Yb) para serem utilizados como aditivos. Os ângulos de contato medidos foram menores que 10° e considerados adequados para a SFL. O SiC sinterizado com esses aditivos permitiu produzir microestruturas diferentes com o aumento da temperatura. Na segunda etapa, foram sinterizadas amostras na forma de pastilhas em várias temperaturas, cujas condições que apresentaram os melhores resultados de massa específica real e densidade relativa foram tomadas como referência para a sinterização na forma de barras prismáticas. Na terceira etapa, essas amostras foram avaliadas quanto à sua tenacidade à fratura (KIC) pelo método da barra entalhada em V, dureza e resistência à flexão. O comportamento de KIC foi avaliado em função da profundidade e raio de curvatura dos entalhes. Os valores variaram entre 2,59 e 3,64 MPam1/2. Verificou-se que os valores de KIC confiáveis foram aqueles encontrados com pequeno raio de curvatura na ponta do entalhe. Quando o raio foi grande, o mesmo não manteve a singularidade da raiz quadrada da ponta do entalhe, e forneceu valores de KIC superestimados. Foram realizados testes para determinar KIC em ar atmosférico e em água, cujos resultados foram menores em água que em ar, com queda entre 2,56 e 11,26%. A maior resistência sob flexão determinada em 4 pontos foi de 482 MPa. Observou-se correlação direta do tamanho dos grãos nos valores de KIC, dureza e módulo de ruptura das cerâmicas de SiC. / Obtaining SiC ceramics by sintering in the presence of additives that promote a liquid phase formation (LPS) during the process has been a proper manner to ensure the lowest sintering temperature. Because SiC is brittle, an ongoing search for better mechanical properties and proper evaluation of these properties for application in aggressive environments maintained. Thus, in the first stage we studied AlN/Re2O3 systems (Re = Dy, Yb), as to their wettability on SiC, for use as additives. The measured contact angles were smaller than 10° and considered suitable for the LPS. The sintered SiC with these additives allowed the production of different microstructures with the increase in temperature. In the second stage, pellet-shaped samples were sintered at various temperatures, and the conditions showing the best density results were taken as reference for sintering prism-shaped bars. In the third stage, these samples were evaluated for toughness (KIC) by single edge V-notched beam method, hardness, and flexural strength. The behavior of KIC was assessed for notch depth and notch radius of curvature. Values ranged between 2.59 and 3.64 MPa/m1/2. The reliable values of KIC were those found with small radius of curvature at the notch tip. When the radius was large, it did not maintain the singularity of the square root of notch tip and provided overestimated KIC values. Tests were performed to determine KIC in atmospheric air and water, and results were lower in water than in air, dropping between 2.56 and 11.26%. The greatest strength under the 4-point bending test was 482 MPa. We observed a direct correlation of grains size in KIC values, hardness and bending strength of SiC ceramics.

Objectives: to verify if women with migraine present altered neck muscles function and altered muscle activity in comparison to non-headache subjects. Moreover, we aimed to identify if there is any relationship between neck muscles dysfunction and the chronicity of migraine attacks. Methods: women with migraine, stratified by episodic and chronic, and age-matched non headache women were the subject of the current thesis. Neck pain relateddisability was assessed by the Neck Disability Index. Neck muscles strength was assessed by a customized hand-held dynamometer. Myoelectrical signals of the sternocleidomastoid, anterior scalene, splenius capitis and upper trapezius were assessed using surface electromyography. Experimental conditions involved maximal isometric voluntary contractions in flexion, extension and lateral bending directions and; craniocervical flexion test, a low load test applied to verify deep cervical flexors ability to supply adequate cervical spine stability. Finally, identification of myofascial trigger points and head and cervical posture photogrammetric evaluation were made in order to be correlated to the muscles electrical activity in the craniocervical flexion test. Results: Although both groups presents high prevalence of neck related disability, subjects with chronic migraine are more likely to report neck related disability, especially the most disabling forms, than episodic migraine. Episodic migraine demonstrated to different neck muscle control only under maximal voluntary tasks. Chronic migraine presented alterations in comparison with controls at maximal conditions, i.e., lower extension force; more time to produce maximal force; greater antagonist coactivation and greater fatigability. During craniocervical flexion test, chronic migraine also differs from control group presenting greater activity of neck extensors. Presence of active trigger points in neck muscles and extended head posture can influence the neck muscles activity during the craniocervical flexion test. Conclusions: migraine is associated to a deterioration of neck muscles functions and to an altered motor control. We can assume an interaction between chronicity of migraine frequency and cervical dysfunction, specially related to neck extensors. More severe disabilities and the majority of the altered function or motor control could only be evidenced in the chronic form / Objetivos: verificar se mulheres com migrânea apresenta alteração na função e atividade dos músculos do pescoço quando comparados a mulheres sem cefaleia. Ainda, objetivamos identificar se há relação entre disfunção cervical muscular e a cronicidade da frequência de crises migranosas. Materiais e métodos: mulheres com migrânea, estratificada entre episódica e crônica, e mulheres sem cefaleia com idade semelhante foi o objeto de estudo dessa tese. Foi investigada a incapacidade relacionada à dor cervical pelo questionário Neck Disability Index e a força muscular cervical utilizando um dinamômetro manual customizado. Ainda, a atividade elétrica dos músculos esternocleidomastoideo, escaleno anterior, esplênio da cabeça e trapézio superior foi verificada pela eletromiografia de superfície. Os procedimentos experimentais foram contração isométrica voluntária máxima em flexão, extensão e inclinação lateral; e o teste de flexão craniocervical, que avalia a habilidade dos músculos flexores cervicais profundos em prover adequada estabilidade para esse segmento. Por fim, a identificação de pontos gatilhos nos músculos cervicais e a avaliação da postura da cabeça e do pescoço por foto foram realizadas a fim de correlacionar os achados com a atividade eletromiográfica. Resultados: embora ambos os grupos de migrânea tenham apresentado alta prevalência de incapacidade relacionada à dor cervical, a migrânea crônica apresenta maior risco de relatar incapacidades mais severas em relação a migrânea episódica. O grupo de migrânea episódica apresentou controle muscular cervical alterado em condição de contração voluntária máxima. Já o grupo migrânea crônica apresentou alterações sob condições máximas, como por exemplo, redução da força dos extensores, mais tempo para gerar pico de força em flexão e inclinação lateral, maior coativação do antagonista e maior susceptibilidade à fadiga. Ainda, durante o teste de flexão craniocervical, o grupo migrânea crônica apresentou maior atividade dos extensores indicando alteração no controle motor. A presença de pontos gatilhos nos músculos do pescoço e a postura em extensão de cabeça pode influenciar a atividade elétrica dos músculos cervicais durante a execução do teste de flexão craniocervical. Conclusões: a migrânea está associada a uma deteriorização da função e do controle motor cervical. Podemos assumir ainda que há uma interação entre a cronicidade da frequência das crises migranosas e a disfunção muscular cervical, especialmente relacionada aos extensores. Incapacidades mais severas e a maioria das disfunções musculares e alteração no controle motor só puderam ser evidenciadas para o grupo com migrânea crônica

O objetivo do trabalho foi avaliar a resistência à flexão, microdureza e grau de conversão de 9 resinas compostas para uso indireto: Solidex (Sl), Epricord (Ep), Belleglass (Be), Signum (Sg), Sinfony (Sy), Tescera (Te), Cristobal (Cr), Targis (Ta) e Adoro (Ad); e uma resina para uso direto como controle, Esthet X (Et), em função da cor: esmalte (E), dentina (D) e translúcido (T). O teste de resistência à flexão (n=15) obedeceu ao método dos três pontos (Kratos) e, após a obtenção dos valores de carga, os corpos de prova fraturados eram posicionados em fita matriz de poliéster e fixados com resina quimicamente polimerizável (Adaptic) no paralelômetro. Em seguida, os corpos de prova eram levados ao microdurômetro (Shimadzu), para obtenção dos valores de microdureza Knoop (n=15), através da aplicação de uma carga de 50gramas por 30 segundos. Para o grau de conversão (n=3), os corpos eram construídos na mesma matriz usada para resistência à flexão, e posicionados em frente ao feixe de infravermelho do espectrofotômetro Raman (Bruker RFS 100/S - 64 scans) para leitura do grau de conversão. A análise de Variância e teste de Tukey foram usados para tratamento dos dados obtidos. A partir dos resultados, chegou-se às seguintes conclusões: 1. Resistência à flexão: O ranqueamento variou em função da cor e as resinas Cr, Sy, Be e Ta tiveram valores de resistência flexural estatisticamente superiores aos dos outros materiais. Os piores materiais foram o Ep, Sg e Sl. A cor não mostrou diferenças significantes (p=12), mas a interação (p<0,0001) e o material (p<0,0001) mostraram. Dois grupos intermediários entre estes foram encontrados. Um deles com valores muito próximos ao grupo com maiores médias de resistência flexural, os quais se encontram os materiais, Et e Te e, um terceiro grupo foi composto pelo material Ad. 2. Microdureza: As resinas Te > Cr > Be > Et, se destacaram com os maiores valores de dureza, (em ordem decrescente de valores de dureza, e com diferenças significantes entre elas). Os piores valores foram obtidos por Ad e Sy com diferenças significantes entre eles. Ep, Sg, Sl e Ta constituíram um grupo com valores intermediários. Portanto, o material (p<0,0001) e a interação (p<0,0001), obtiveram diferenças significantes. Em relação à cor (p<0,0002), a cor indicada para esmalte apresentou valores estatisticamente inferiores do que dentina e translúcido, e deve ser atribuída aos baixos valores em esmalte, em relação a outras cores do material Te. 3. Grau de conversão: Os maiores valores foram obtidos pelo material Te > Be > e = Cr > ou = Sy = Ad. Os materiais Ep e Ta apresentaram valores de grau de conversão logo abaixo destes materiais, e os piores valores de grau de conversão foram mensurados nos materiais Sg, Et e Sl, com diferenças estatisticamente significantes entre eles. Em relação à cor (p<0,0001), a cor indicada como translúcido apresentou valores estatisticamente superiores aos das duas outras cores. Estes resultados são devido aos altos valores apresentados pelos materiais Sy e Ep. Também tiveram valores significantemente diferentes o material (p<0,001) e a interação (p<0,0001). / Objectives: To characterize nine laboratory-processed composite systems (Adoro [Ad], Belleglass [Be], Cristobal [Cr], Epricord [Ep], Sinfony [Sy], Signum [Sg], Solidex [Si], Targis [Ta] andTescera [Te], ) and one composite for direct placement (Esthet-X [Et]) in terms of particle-size distribution and to compare the flexural strength (FS), Knoop hardness (KH) and degree of conversion (DC) of these composites. Materials and methods: Approximately 5 g of composite paste were dissolved in acetone pro analysi, mixed and centrifuged for 30 min at 3000 rpm. The remaining filler particles were dried (37 °C/12 h) and ultrasonically agitated. A computer-controlled apparatus using laser-diffraction technology was used to determine particle size distribution. Specimens (10 x 2 x 1 mm) were fractured with a 3-point bending test (n=15). KH was measured on fragments obtained after the flexural test (25g/30s). Raman spectra of both unpolymerized and polymerized resins were measured at room temperature in the backscattering geometry using the FT-Raman spectrometer. FS, KH and DC data were analyzed with one-way ANOVA and Tukey\'s post-hoc test (?=0.05). Results: The range of particle sizes was dramatically different for each composite. The composite Et showed the narrowest range of particle size while Sg showed the widest range. The highest DC means were observed for Te, Be and Cr. The lowest means were observed for Sg, Et and Si. Cr, Sy and Ta showed the highest FS values, while Ep, Sg and Si showed the lowest FS values. Te, Cr, Be and Et showed the highest KH means, while Ad and Sy the lowest. Conclusions: The composites Te, Cr and Be showed the best performance in all methods evaluated. On the other hand, the indirect composites Ep, Sg and Si demonstrated the worst performance.

Visando otimizar as propriedades químicas e mecânicas de compósitos de uso direto aplicados na forma indireta, associados a tratamentos térmicos experimentais (TT), torna-se necessária uma caracterização térmica que permita a determinação de uma temperatura de TT segura (abaixo da temperatura de início de perda de massa). Assim, a primeira etapa deste estudo consistiu em caracterizar termicamente dez compósitos comerciais (Z100, Filtek Z250, Z350 e Supreme XT- 3M ESPE, Esthet-X e TPH Spectrum Dentsply, Charisma Heraeus Kulzer, Tetric Ceram Ivoclar Vivadent, Herculite XRV e Point 4 - Kerr), fotoativados pelo método contínuo (C) e pulse-delay (PD) (20 J.cm-2), por termogravimetria (TG) (n=1) e calorimetria exploratória diferencial (DSC) (n=3). Foram escolhidas duas temperaturas de TT: 100 e 170°C, aplicadas por 10 min, 24h após a fotoativação. A partir disto, avaliaram-se: 1) o grau de conversão (GC), por espectroscopia FT-Raman (n=3); 2) a resistência à flexão em três pontos (RF) (n=10); e 3) a dureza Knoop (KHN) para as faces topo e base (n=3) de quatro destes compósitos (Filtek Z250 e Supreme XT, Esthet-X e Point 4), após diferentes condições: imediatamente, 1h, 6h e 24h após a fotoativação e 24h após fotoativação seguida de TT a 100 ou 170°C. Os dados obtidos foram submetidos à análise de variância e ao teste de Tukey (nível de significância de 5%). Quanto ao GC (%), houve significância estatística para o fator material (p=0,000): Point 4 (68,42) > Z250 (63,05) = Esthet-X (61,69) > Supreme (54,27); condição (p=0,000): TT170 (73,20) = TT100 (73,58) > 24h (62,60) = 6h (60,18) > 1h (55,10) = imediato (53,66); e ativação (p=0,006): C (62,97) > PD (60,75). Também foram significantes as interações material × condição (p=0,007) e material × condição × ativação (p=0,013). Para a RF (MPa), foram encontradas significâncias estatísticas para os fatores material (p=0,000): Z250 (165,48) > Supreme (153,96) > Point 4 (131,30) = Esthet-X (128,06); e condição (p=0,000): TT170 (194,56) > TT100 (182,91) > 24h (150,88) > 6h (131,79) > 1h (111,77) > imediato (96,30); assim como para as interações: ativação × condição (p=0,000), material × condição (p=0,000) e material × ativação × condição (p=0,000). Para a dureza, foram encontradas significâncias estatísticas para os fatores: materialativação (p=0,000): Supreme C (82,46) > Supreme PD (80,29) = Z250 C (77,46) > Z250 PD (74,30) > Esthet-X C (69,17) > Esthet-X PD (65,67) > Point 4 C (57,21) = Point 4 PD (56,71); condição (p=0,000): TT170 (81,35) > TT100 (73,72) > 24h (70,36) > 6h (67,92) > 1h (64,99) > imediato (64,12) e face (p=0,000): topo (71,40) > base (69,40); assim como para as interações: material-ativação × face (p=0,011), material-ativação × condição (p=0,000) e face × condição (p=0,000). A partir dos resultados obtidos, pôde-se concluir que os TTs experimentais propostos foram capazes de aumentar as propriedades estudadas, sendo, de maneira geral, os resultados obtidos com 170°C melhores do que os com 100°C, e ambos melhores do que as demais condições. / Aiming to optimize chemical and mechanical properties of direct composites applied in an indirect way, with an association to experimental heat treatments (TT), it is necessary a thermal characterization, in a way to determine a safe temperature for the TT (below the significant mass loss temperature). Thus, the first step of this study was to perform the thermal characterization of ten commercial composites (Z100, Filtek Z250, Z350 and Supreme XT 3M-ESPE, Esthet-X and TPH Spectrum Dentsply, Charisma Heraeus Kulzer, Tetric Ceram Ivoclar Vivadent, Herculite XRV and Point 4 - Kerr) photoactivated by continuous (C) and pulse-delay (PD) methods (20 J.cm-2), by thermogravimetry (TG) (n=1) and differential scanning calorimetry (DSC) (n=3). After that, two temperatures were chosen for the TT: 100 and 170°C, which were applied for 10 min, 24h after photoactivation. Thus, some properties were evaluated for four composites (Filtek Z250 and Supreme XT, Esthet- X and Point 4): 1) degree of conversion (GC) by FT-Raman spectroscopy (n=3); 2) three-point bending test (RF) (n=10); and 3) Knoop hardness (KHN) for top and bottom surfaces (n=3). The conditions were: immediately, 1h, 6h and 24h after photoactivation and 24h after photoactivation followed by TT at 100 or 170°C. Data were analyzed by ANOVA and Tukeys test (level of significance of 5%). In relation to GC (%), there were statistical significance for the factors material (p=0.000): Point 4 (68.42) > Z250 (63.05) = Esthet-X (61.69) > Supreme (54.27); condition (p=0.000): TT170 (73.20) = TT100 (73.58) > 24h (62.60) = 6h (60.18) > 1h (55.10) = immediately (53.66); and activation (p=0.006): C (62.97) > PD (60.75); and for the interactions: material × condition (p=0.007) and material × condition × activation (p=0.013). For RF (MPa), statistical significance were found for the factors material (p=0.000): Z250 (165.48) > Supreme (153.96) > Point 4 (131.30) = Esthet-X (128.06); and condition (p=0.000): TT170 (194.56) > TT100 (182.91) > 24h (150.88) > 6h (131.79) > 1h (111.77) > immediately (96.30); and also for the interactions: activation × condition (p=0.000), material × condition (p=0.000) and material × activation × condition (p=0.000). For KHN, statistical significance were found for the factors material-activation (p=0.000): Supreme C (82.46) > Supreme PD (80.29) = Z250 C (77.46) > Z250 PD (74.30) > Esthet-X C (69.17) > Esthet-X PD (65.67) > Point 4 C (57.21) = Point 4 PD (56.71); condition (p=0.000): TT170 (81.35) > TT100 (73.72) > 24h (70.36) > 6h (67.92) > 1h (64.99) > immediately (64.12), and face (p=0.000): top (71.40) > bottom (69.40); as for the interactions: material-activation × face (p=0.011), material-activation × condition (p=0.000) and face × condition (p=0.000). By the results, it could be concluded that both proposed experimental TTs were capable of increasing the studied properties, with, in a general way, 170°C generating better mechanical properties than 100°C, and both better than the other conditions.