This research focuses on a study of the material parameters of horse hoof. The study of the problem with the factors that affect to the fastening of the shoe is not performed. Three different tests are carried out to obtain the behavior of the horn wall of the horse hoof in different ways, under physiological conditions and variation of hydration level. The first one is a tensile test to obtain both the force/displacement relation and the stress/strain relation and the parameters derived from them. The second is a hardness test to determine how the material resists to several kinds of permanent-shape changes when a force is applied.Finally, a microscopic study is performed to analyze the fracture surface after testing the specimens. A meticulous analysis of the results and a broad comparison with several researches are performed. The end of the thesis work suggests future works needed to solve the problem.

Made available in DSpace on 2014-06-11T19:23:35Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-08-03Bitstream added on 2014-06-13T19:09:28Z : No. of bitstreams: 1 jasse_ff_me_arafo.pdf: 3143943 bytes, checksum: db74ccbc66112c4a240ca5402754512c (MD5) / Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) / Numerosos tipos e marcas comerciais de resinas compostas são constantemente introduzidos no mercado odontológico, em função de modificações na composição, tipo, formato e quantidade das partículas inorgânicas, assim como na porção orgânica. Sempre, com a finalidade de proporcionar propriedades mecânicas e estéticas superiores aos materiais, aumentando dessa forma sua longevidade. Assim, o propósito neste estudo foi avaliar o grau de conversão (GC) pelo método FT-IR e a degradação hidrolítica por meio do teste de dureza Vickers (dV), de duas resinas compostas (uma nanoparticulada e uma micro-híbrida). Para isso, oito espécimes (4 mm de diâmetro x 2 mm de espessura, ISO 4049) de cada material foram confeccionados para cada teste. As resinas compostas foram inseridas em única porção na matriz metálica e fotoativadas com aparelho LED (Celalux, Voco®, 776 mW/cm²), por 40 segundos. Dezesseis leituras de dV (8 no topo e 8 na base) foram realizadas para cada espécime em durômetro digital MMT-3 (Buehler Lake Bluff, Illinois USA), utilizando carga de 50 gf aplicada durante 30 segundos, em intervalos de tempo prédeterminados: imediatamente após fotoativação (controle), 24, 48, 72 horas, 7, 14, 21, 30 dias e 6 meses. Logo após a fotoativação foi feita a medida da dureza inicial e os espécimes foram então imersos em saliva artificial a 37°C. Para o GC (%), os espécimes foram triturados, prensados com KBr e analisados em espectrofotômetro FT-IR (Nexus-470). Os resultados foram submetidos à análise estatística e permitiram concluir que: não foi observada diferença entre as resinas quanto ao grau de conversão; a proporção entre as medidas de dureza de topo e base foi semelhante para os dois materiais, tendo sido mantida ao longo de todo o tempo experimental; a resina Z-250 apresentou os maiores valores de dureza tanto na superfície de topo quanto na de base... / Numerous types and brands of composite resins are constantly introduced into the dental market, due to changes in the composition, type, shape and quantity of inorganic particles as well as the organic portion. Always with the aim of providing superior mechanical and aesthetic properties to materials, thereby increasing their longevity. Thus, the purpose of this study was to evaluate the degree of conversion (DC) and hydrolytic degradation through the Vickers hardness test (hV) of two composites (a nanofilled and a microhybrid). For this, eight specimens (4 mm diameter x 2 mm thick, ISO 4049) of each material were prepared for each test. The composites were inserted into single increment in the metallic matrix and photoactivated with a LED unit (Celalux, Voco ®, 776 mW / cm ²) for 40 seconds. Sixteen hV readings (8 on each top and bottom surfaces) were performed for each specimen in MMT-3 digital hardness tester (Buehler Lake Bluff, Illinois USA), using load of 50 gf applied for 30 seconds, at predetermined intervals: immediately after polymerization (control), 24, 48, 72 hours, 7, 14, 21, 30 days and 6 months. After curing, initial hardness measurements were performed and the specimens were immersed in artificial saliva at 37 °C. For the DC (%), the specimens were ground, pressed with KBr and analyzed by FT-IR spectrophotometer (Nexus-470). The results were subjected to statistical analysis and concluded that: there was no difference between the resins for degree of conversion; the ratio between top and bottom hardness values was similar for both materials and was maintained throughout the experimental period; the composite resin Z-250 showed the highest hardness values in both the top surface as the bottom throughout the evaluation period. The materials tested showed no evidence of hydrolytic degradation in a significant way, in a six-month storage-time in artificial saliva

O objetivo deste estudo foi avaliar a microdureza do cimento resinoso Variolink II ( Ivoclar Vivadent, Schaan, Liechtenstein) empregado na cimentação de coroas totais de cerâmica (IPS e.max Press, Ivoclar Vivadent, Schaan, Liechtenstein) em preparos com 3 substratos (dentina, metal e resina composta). Foram utilizados 30 molares distribuídos em 3 grupos de acordo com o tipo de substrato. No grupo com substrato em dentina (D), as coroas foram cimentadas em dentes preparados em dentina. Nos grupos com substrato em metal (M) e resina (R), as coroas foram seccionadas no nível da junção cemento-esmalte e restauradas com núcleos metálicos e de preenchimento em resina composta, respectivamente. Cada um dos grupos foi subdividido em subgrupos para avaliação após 7 dias e 3 meses de armazenamento em água deionizada. Os espécimes foram seccionados no centro das coroas, no sentido vestíbulo-lingual e as superfícies foram polidas para a realização dos testes de microdureza ao longo da linha de cimento. Os valores de microdureza foram obtidos nos terços cervical, médio, oclusal das faces vestibular e lingual e na face oclusal. Os resultados foram submetidos a uma análise estatística prévia ANOVA a 3 critérios (substratos/ armazenamento/ terços e face oclusal), a qual não mostrou diferenças significativas entre os terços e face oclusal nos 2 períodos de armazenamento. Em seguida foi realizada a ANOVA a 2 critérios (substrato e armazenamento) e o teste de Tukey que mostraram os resultados do substrato em resina estatisticamente inferiores aos de dentina e metal, após o período de armazenamento de 7 dias. Conclui-se que a microdureza do cimento resinoso não variou nos diferentes terços e face e que a influência do substrato em resina no cimento foi tempo-dependente. / The aim of this study was to evaluate the microhardness of resin cement Variolink II (Ivoclar Vivadent, Schaan, Liechtenstein) used to cement full ceramic crowns (IPS e.max Press, Ivoclar Vivadent, Schaan, Liechtenstein) in three preparations substrates (dentin, metal and composite resin). Thirty molars were divided into three groups, according to the type of the substrate. In the dentin substrate group (D), the crowns were prepared in dentin; the metal (M) and resin (R) substrates groups, the crowns were sectioned at cement enamel junction level and restored with metal cast post and composite resin filler, respectively. Each group was subdivided into subgroups to evaluation after 7 days and 3 months of storage in deionized water. After cementing the specimens were sectioned buccolingually at the center of the crowns, and the surfaces were polished to microhardness test along the cement line. The microhardness values were obtained in the cervical, medium and occlusion thirds of the buccal and lingual surfaces and in the occlusal surface. The results were submitted to a three-way ANOVA (substrates / storage / thirds and occlusal surface) to a prior statistical analysis and did not show significant differences between the occlusal surface and thirds in the two storage periods. Then two-way ANOVA (substrate and storage) and the Tukey test were performed. The results in the resin group were statistically lower than those of dentin and metal, after 7 days of storage. Therefore, the microhardness of resin cement did not change in the different thirds and face and that the influence of the resin substrate was time-dependent.

O Cu e suas ligas têm diferentes aplicações na sociedade moderna devido as excelentes propriedades elétricas, condutividade térmica, resistência à corrosão dentre outras propriedades. Estas aplicações podem ser em válvulas, tubulações, panelas para absorção de energia solar, radiadores para automóveis, condutores de corrente e eletrônico, elementos de termostatos e partes estruturais de reatores nucleares, como, por exemplo, bobinas para campo toroidal para um reator de fusão nuclear. Dentre as ligas utilizadas em reatores nucleares, podemos destacar Cu-Be, Cu-Sn e Cu-Pt. O Ni e o Co, freqüentemente são adicionados às ligas de Cu para que a solubilidade seja deslocada para temperaturas mais elevadas com relação aos sistemas binários de Cu-Sn e Cu-Pt. A adição de Ni-Pt ou Ni-Sn ao Cu em porcentagens iguais ou inferiores a 1,5 % aliado a tratamentos termos-mecânico alteram as propriedades do Cu. Estudamos neste trabalho sete diferentes ligas: três ligas de Cu-Ni-Pt 1 (97,99 % Cu - 1,55 % Ni - 0,46 % Pt), 2 (99,33 % Cu - 0,23 % Ni -0,43 % Pt) 3 (98,01 % Cu - 0,48 % Ni - 1,51 % Pt); três ligas de Cu-Ni-Sn 4 (98,31% Cu - 1,12 % Ni - 0,58 % Sn), 5 (98,79 % Cu – 0,57 % Ni - 0,65 % Sn), 6 (98,39% Cu – 0,46 % Ni – 1,16 % Sn) e Cu eletrolítico 0 (0,0058 % Pb - 0,0007 % Fe - 0,0036 % Ni - 0,0024 % Ag). As referentes ligas foram desenvolvidas a partir de um forno a arco voltaico e passaram por tratamentos termo-mecânicos pré-determinados. As microestruturas foram analisadas diretamente por microscopia óptica e microscopia eletrônica de varredura / EDS e indiretamente por medidas de dureza Vickers e condutividade elétrica. O objetivo deste trabalho, portanto, foi observar e constatar os efeitos da mudança da microestrutura em relação às propriedades dureza e condutividade elétrica. / The Cu and its alloys have different applications in the owed modern society the excellent electric properties, thermal conductivity, resistance to the corrosion and other properties. These applications can be in valves, pipes, pots for absorption of solar energy, radiators for automobiles, current driver, electronic driver, thermostats elements and structural parts of nuclear reactors, as, for example, reels for field toroidal for a reactor of nuclear coalition. The alloys used in nuclear reactors, we can highlight Cu-Be, Cu-Sn and Cu-Pt. Ni and Co frequently are added to the Cu alloys so that the solubility is moved for temperatures more elevated with relationship to the binary systems of Cu-Sn and Cu-Pt. The addition of Ni-Pt or Ni-Sn to the Cu in the same or inferior percentages to 1,5% plus thermomechanical treatments changes the properties of the copper. We studied the electric conductivity and hardness Vickers of the Cu-Ni-Pt and Cu-Ni-Sn and compared with the electrolytic Cu. In the proposed flowcharts, breaking of the obtaining of the ingot, we proceeded with thermo mechanical treatments.

Made available in DSpace on 2014-06-11T19:24:07Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-06-11Bitstream added on 2014-06-13T18:51:39Z : No. of bitstreams: 1 arruda_am_me_araca.pdf: 646025 bytes, checksum: 136184311e9ba76436388867a2d8dcc5 (MD5) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Este trabalho analisou in situ o efeito de um clareador a base de peróxido de hidrogênio a 35%, na microdureza superficial em esmalte bovino. Para tanto, 100 fragmentos dentais com dimensões de 4x4x2mm, foram polidos e submetidos à leitura inicial de microdureza Knoop. Foram selecionados os 44 fragmentos com microdureza mais próxima da mediana e estas unidades experimentais foram aleatoriamente divididas em grupos de 4 elementos que foram adaptados a aparelhos moveis usados por 11 indivíduos. Os voluntários foram orientados a utilizar o dispositivo durante todo o dia, com exceção dos momentos destinados à alimentação, higienização e às sessões clareadoras. Metade dos fragmentos de cada dispositivo foi submetida a uma sessão de clareamento (3 aplicações de 15 minutos) por semana, durante 14 dias, totalizando 3 sessões clareadoras. Os fragmentos não clareados permaneceram no dispositivo sem sofrer qualquer tipo de influência do clareador. Durante o uso do aparelho os fragmentos dentais foram submetidos ao acúmulo bacteriano, sendo gotejada uma gota da solução de sacarose a 20% em cada bloco, oito vezes ao dia, visando aumentar o desafio cariogênico. Após 7 dias, do término dos tratamentos foi realizada nova análise da microdureza e os valores foram submetidos à Análise de Variância ao nível de 5%. Pôde-se observar diminuição nos valores de microdureza, tanto para o grupo clareado (média: 238,9 – 179,4), quanto para o grupo controle (média: 237,3 – 191,7), sendo as médias mais baixas encontradas no grupo clareado. Concluiu-se que o tratamento clareador com peróxido de hidrogênio a 35% potencializou a redução da microdureza em dentes submetidos ao desafio cariogênico / This in situ study analyzed the effect of bleaching using 35% hydrogen peroxide on the enamel microhardness. Therefore, 100 dental fragments with dimensions of 4x4x2mm, were polished and subjected to the initial reading of microhardness. We selected 44 fragments presenting microhardness data similar to the mean value and these experimental units were randomly divided into groups of four elements that have been adapted in mobile devices to be worn by 11 volunteers. They were instructed to use the device throughout the day, except in meal times, cleaning and whitening sessions. Bleaching procedures were performed in half of the fragments placed on each device (3 applications of 15 minutes) per week for 14 days, totalizing 3 whitening sessions. Unbleached fragments remained on the device without suffering any kind of influence of the bleaching agent. While using the appliance, dental fragments were lead to bacterial colonization; sine a 20% sucrose solution was dripped eight times a day, aiming to increase the cariogenic challenge. After seven days of the end of the treatment, microhardness \analysis was performed. Data were submitted to ANOVA and Fisher's test at 5%. It was observed a decrease in microhardness values for both bleached group (mean: 238.9 to 179.4) and control group (mean: 237.3 to 191.7), besides that, the lowest values were verified in the bleached groups. It was concluded that bleaching using 35%hydrogen peroxide potentiated the reduction in microhardness in teeth submitted to cariogenic challenge

Made available in DSpace on 2014-06-11T19:29:12Z (GMT). No. of bitstreams: 0 Previous issue date: 2009-03-27Bitstream added on 2014-06-13T19:17:33Z : No. of bitstreams: 1 viana_pgs_me_arafo.pdf: 840842 bytes, checksum: 18e582ab40c3b9552459a495ba07430b (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Amostras de esmalte provenientes de dentes extraídos, de origem humana ou bovina, são amplamente utilizadas em estudos realizados in vitro e in situ. Esses dentes são considerados uma fonte em potencial de microorganismos patogênicos e devem ser esterilizados, antes da sua utilização nas pesquisas, para prevenir a ocorrência de infecções cruzadas. No entanto, o processo de esterilização do esmalte não deve alterar a sua integridade estrutural. O presente estudo teve como objetivo avaliar a efetividade da irradiação por microondas na esterilização do esmalte bovino, assim como o efeito deste método sobre a microdureza superficial e resistência à desmineralização do esmalte bovino. Dezoito incisivos bovinos foram utilizados para a obtenção de quarenta amostras de esmalte, divididas em dois grupos (n=20): controle (não-irradiados) e irradiados por microondas (3 minutos a 650 W). As amostras do grupo irradiado foram imersas, individualmente, em 200 mL de água destilada e submetidas à irradiação por microondas por 3 minutos a 650 W. Em seguida, ambos os grupos tiveram suas amostras imersas individualmente em tubos estéreis contendo 10 mL caldo BHI (Brain Heart Infusion), os quais foram incubados por 7 dias a 37°C, sob condições de aerobiose e anaerobiose. Após a incubação, o desenvolvimento de microorganismos foi verificado pela presença de turvação do meio de cultura. Em seguida, foram realizadas diluições seriadas (10-2 a 10-5), plaqueamento em meio ágar sangue e incubação em condições de aerobiose e anaerobiose, durante 48 h e 7 dias, respectivamente. Os valores de unidades formadoras de colônias foram calculados. Para a avaliação das propriedades do esmalte, outras 18 amostras de esmalte (4 x 4 mm) foram preparadas, individualmente embutidas em resina acrílica, seqüencialmente polidas e, então, seccionadas em duas metades, sendo uma das metades... / Enamel samples from bovine or human teeth are routinely used for in vitro and in situ caries research. These enamel samples need to be sterilized before they can be used in intra-oral appliances and the sterilization method must not affect the structural integrity of the tooth. The aim of this study was to evaluate the effectiveness of microwave irradiation on bovine enamel sterilization, as well as it's effect on the surface microhardness and resistance to demineralization of bovine enamel. Eighteen bovine incisors were used to produce forty enamel samples, divided in two groups (n = 20): control (nonirradiated) and microwave irradiated (3 minutes at 650 W). Microwaving samples were individually immersed in 200 mL of distilled water and submitted to irradiation at 650 W for 3 minutes. Following the microwaving, specimens from both groups were added individually to 10 mL of Brain Heart Infusion broth in sterile test tubes, which were incubated at 37°C for 7 days under aerobic and anaerobic conditions. After 7 days incubation, those test tubes in which turbidity was observed were considered to contain growing microorganisms. Dilutions of 10-2 to 10-5 were performed on blood agar plates, which were incubated aerobically and anaerobically for growth for up to 48 h and 7 days, respectively. After incubation, the numbers of colonyforming units were calculated. For the properties of enamel analysis, other 18 bovine enamel samples (4 x 4 mm) were prepared, embedded in acrylic resin, serially polished and sliced into two halves: one of the fragments was reserved as control while the other was microwaved in 200 mL of distilled water for 3 minutes at 650 W. Hardness measurements were conducted using a Microhardness tester with a Knoop diamond. Five indentations were performed under a load of 25 gf for 05 seconds. For the resistance to demineralization analysis, the groups were submitted... (Complete abstract click electronic access below)

Este estudo in vitro avaliou o efeito da adição de rodamina B dissolvida em etanol nas concentrações de 0,02mg/mL e 0,10mg/mL, nas propriedades mecânicas dos sistemas adesivos não simplificados considerados padrão-ouro. 96 coroas de terceiros molares humanos hígidos foram seccionadas transversalmente no terço oclusal para remoção do esmalte e exposição da dentina. Os espécimes foram divididos de acordo com os sistemas adesivos Adper Scotchbond Multi-Purpose (MP) - convencional de três passos ou Clearfil SE Bond (SE) - autocondicionante de dois passos: MP-C e SE-C (MP e SE controles); MP-C1 e SE-C1 (MP e SE com rodamina B 0,02mg/mL); MP-C2 e SE-C2: (MP e SE com rodamina B 0,10mg/mL). Para o teste de RU, os espécimes (n=10) foram submetidos ao desgaste com lixas de granulação 320 e 600. A dentina foi tratada de acordo com as instruções de cada fabricante dos sistemas adesivos e restaurada com resina composta FiltekTM Z250. Após o armazenamento em saliva artificial (7dias/37oC), os espécimes foram seccionados para obtenção de palitos com 0,64 mm2 de área média e submetidos ao teste de microtração em máquina de teste universal a 0,5 mm/min, que foram analisados após 7 dias e 6 meses. O modo de fratura dos espécimes foi analisado com estereomicroscópio digital (x200) e classificado em: adesiva, coesiva em dentina, coesiva em resina e mista. Para o teste de MS, as coroas seccionadas (n=6) foram planificadas com lixa de granulação 600. A dentina foi tratada de acordo com as instruções de cada fabricante dos sistemas adesivos e os espécimes foram mantidos secos em estufa a 37oC durante 48 horas. O teste de MS foi realizado utilizando ponta Knoop (Microdurômetro Shimadzu HMV-2), a 10x e carga estática de 25gF por 10 segundos. Os resultados obtidos foram analisados por análise de variância (ANOVA-2 critérios) e teste de Bonferroni para comparações múltiplas (p<0,05). A análise de acordo com o tempo foi realizada com o teste de t-student. Os valores médios de RU e desvio padrão (MPa±dp; 7 dias / 6 meses) foram: MP-C (41,95±2,38 / 22,76±3,66); MP-C1 (28,02±5,12 / 17,93±5,70); MP-C2 (26,28±5,55 / 14,30±5,68); SE-C (46,07±1,43 / 19,07±6,75); SE-C1 (37,49±13,31 / 18,54±6,71); SE-C2 (34,16±7,71 / 17,89±4,87). No tempo de 7 dias, os fatores sistema adesivo e concentração de rodamina B foram significantes. Após 6 meses, apenas o fator concentração de rodamina B foi significante. A falha de fratura predominante em todos os grupos foi adesiva. Os valores de MS (KHN) e desvio padrão foram: MP-C (8,97±3,85); MP-C1 (7,33±0,99); MP-C2 (7,17±2,45); SE-C (4,71±4,42); SE-C1 (4,42±0,56); SE-C2 (3,27±0,30). Na comparação entre os sistemas adesivos, eles diferiram entre si na condição controle e de 0,10mg/mL. Para cada adesivo, não houve diferença entre as distintas condições de acordo com a adição de rodamina B. Em função dos resultados apresentados, a adição de rodamina B nos sistemas adesivos não simplificados MP e SE, nas concentrações de 0,02mg/mL e 0,10mg/mL, deve ser incorporada com cautela para que não influencie nas propriedades mecânicas do material. / This in vitro study evaluated the effect of addition of rhodamine B dissolved in ethanol in concentrations of 0.02mg/mL and 0.10mg/mL, the mechanical properties of non-simplified adhesive systems. 96 crowns of human third molars were transversely sectioned on the oclusal third to remove the enamel and exposure the dentin. The specimens were divided according to the adhesive systems Adper Scotchbond Multi-Purpose (MP) 3-step-etch-andrinse or Clearfil SE Bond (SE) 2-step-self-ecthing: MP-C and SE-C (MP and SE controls); MP-C1 and SE-C1 (MP and SE with 0.02mg/mL rhodamine B); MP-C2 and SE-C2: (MP and SE with 0.10mg/mL rhodamine B). For the &#x3BC;TBS test, the specimens (n=10) were ground with 320- to 600-grit silicon carbide paper. The dentin was treated according to the instructions of each manufacturer and restored with composite resin FiltekTM Z250. The specimens were stored in artificial saliva (7 days/37oC), and then sectioned to obtain sticks with an average of 0.64 mm2 area and submitted to &#x3BC;TBS test at a universal testing machine at 0.5 mm/min, which were analyzed immediately after 7 days and 6 months. The mode of fracture of the specimens was analyzed with digital stereomicroscope (x200) and classified as: adhesive, cohesive in dentine, cohesive in resin and mixed. For the SM test, the sectioned crowns (n=6) were flattened with 600-grit silicon carbide paper. The dentin was treated according to the manufacturers instructions for each adhesive system and the specimens were stored in dry condition at 37oC during 48 hours. The SM test was performed with Knoop indenter (Shimadzu HMV-2 hardness tester), at 10x and 25gF of load for 10 seconds. The results were analyzed by two-way analysis of variance tests and the Bonferroni test for multiple comparisons (p<0.05). The analysis regarding time was checked with t-student test. The mean &#x3BC;TBS and standard deviation (MPa±dp; 7 days / 6 months) were: MP-C (41.95±2.38 / 22.76±3.66); MP-C1 (28.02±5.12 / 17.93±5.70); MP-C2 (26.28±5.55 / 14.30±5.68); SE-C (46.07±1.43 / 19.07±6.75); SE-C1 (37.49±13.31 / 18.54±6.71); SE-C2 (34.16±7.71 / 17.89±4.87). In the immediate time, the adhesive system and rhodamine B concentration factors were significant. After 6 months, only the rhodamine B concentration was a significant factor. The predominant failure in all groups was adhesive. The values of SM and standard deviation were: MP-C (8.97±3.85); MP-C1 (7.33±0.99); MP-C2 (7.17±2.45); SE-C (4.71±4.42); SE-C1 (4.42±0.56); SE-C2 (3.27±0.30). In the comparison between the adhesive systems, they were significantly different for the conditions control and 0.10mg/mL. For each adhesive systems, there was no difference between the different conditions according to the addition of rhodamine B. Regarding the shown results, addition of rodhamine B in non-simplified adhesives MP and SE, in the concentrations of 0.02mg/mL e 0.10mg/mL must be carefully added to avoid implications to the mechanical properties of the materials.

A aplicação de flúor tópico é a principal estratégia de natureza química para a remineralização de lesões incipientes (LI) clinicamente visíveis como manchas brancas (MB) por cárie. Abordagens para aumentar a retenção de F no substrato pode favorecer sua ação e para isso, tratamentos prévios da superfície do esmalte podem ser usados. O objetivo deste trabalho foi comparar a capacidade de remineralização do flúor sem e com pré-tratamento do esmalte com ácido fosfórico e nitrato de alumínio e a sua resistência após novo desafio. Sessenta espécimes de esmalte bovino foram preparados (6mm x 4mm) e selecionados por meio de análise de microdureza de superfície (MS). LI foram produzidas através de ciclagem Desmineralização-Remineralização (DES-RE) e os espécimes divididos aleatoriamente em cinco grupos, de acordo com o tratamento (n=12): V- controle (verniz de fluoreto de sódio 5% por 4 horas), F (sem pré-tratamento); P-F(condicionamento ácido com ácido fosfórico por 30s); Al-F (nitrato de alumínio a 0,05M por 1min); P-Al-F (condicionamento com ácido fosfórico a 37% + nitrato de alumínio a 0,05M). Os tratamentos foram repetidos semanalmente durante quatro semanas. Após o tratamento, os espécimes foram submetidos à nova ciclagem ácida. Após cada etapa, nova MS foi realizada e ao final das análises, um corte transversal dos espécimes foi realizado. Uma das metades foi submetida à análise da microdureza longitudinal (ML) e a outra preparada para realização da microrradiografia transversal (TMR) para a análise de conteúdo mineral perdido. O percentual de perda de dureza de superfície (%PDS) foi analisado por ANOVA a 2 critérios de medidas repetidas e Tukey e o percentual de perda de dureza longitudinal (%PDL) por ANOVA a 3 critérios de medidas repetidas e Tukey (p<0,05). Os dados de TMR no parâmetro LD (profundidade da lesão) foram analisados por ANOVA a dois critérios (p<0,05). Os resultados mostraram que a ciclagem DES-RE resultou em significante %PDS e %PDL em todos os grupos. Grupo F revelou menor perda de MS após tratamento e, F, Al-F e P-Al-F, mostraram menor perda de dureza final, após o novo desafio ácido. Na análise de %PDL, o grupo V apresentou menor perda de dureza final quando comparado com os demais grupos, nas diferentes profundidades. A análise do conteúdo mineral não revelou nenhuma diferença entre os tratamentos e fases. Nenhum dos pré tratamentos propostos foram capazes de otimizar a atuação do gel APF na remineralização de MB. / The topical fluoride is the main chemical strategy to remineralize incipient caries lesions (ICL) visible as carious white spot lesions (WSL). Approaches to increase the fluoride retention may favor its action and therefore, enamel pretreatments can be used for this purpose. The aim of this study was to compare the potential of fluoride remineralization with and without previous enamel pretreatment with aluminum nitrate and phosphoric acid as well as their resistance after a new acid challenge. Sixty bovine enamel specimens were prepared (6mm x 4mm) and selected by the surface hardness (SH) analysis. The ICL were produced using DE-RE cycling and the specimens were randomized in five groups, according to the treatment (n=12): Vcontrol (5% sodium fluoride varnish during 4h), and four groups previously preatreated with topical application of acidulated phosphate fluoride (APF) during 4min: F (without pretreatment), P-F (phosphoric acid etching during 30s), Al-F (0.05M aluminum nitrate during 1min); P-Al-F (phosphoric acid etching + aluminum nitrate). The treatments were performed weekly during four weeks. After the treatment, the specimens were submitted to the new acid challenge. After each step, a new SH analysis was performed followed by the transversal cut of the specimens. A half was submitted to the longitudinal cross-sectional hardness analysis (LH) and the other half was prepared to transverse microradiography assessments (TMR) to determine the loss of mineral content. The percentage of surface mineral loss (%SH) was analyzed using two-way repeated-measures ANOVA and the percentage of crosssectional mineral loss (%LH) by the three-way repeated-measures ANOVA and Tukey (p<0.05). Data of TMR analysis by LD (lesion depth) parameter was analyzed with two-way ANOVA (p<0.05). The results showed significant %SH and %LH after DE-RE cycling for all groups. F group showed the lowest %SH after treatment, with no significant difference to Al-F and P-Al-F after the new acid challenge. V group showed the lowest %LH compared to the other groups, in the different depths, suggesting more resistance. Mineral content assessment did not reveal any difference among treatments and phases. None pretreatments were able to increase the potential of fluoride remineralization.

Os cimentos resinosos têm sido largamente utilizados em odontologia restauradora com a finalidade de reter o pino intra-radicular e dissipar tensões entre este e a raiz. Entretanto, o grau de conversão alcançado pelos mesmos influencia suas propriedades mecânicas, biocompatibilidade e degradação pela água e pelos ácidos bucais. Testes de microdureza podem ser aplicados para estimar o grau de conversão de compósitos, uma vez que apresentam boa correlação com a espectroscopia infravermelha. Este trabalho objetivou analisar a microdureza de quatro cimentos resinosos de polimerização dual utilizados na cimentação de pinos de fibra de vidro, nos períodos inicial, após 24 horas de imersão em etanol a 75% e após 3 meses de armazenamento em água, e testar a hipótese de que não há diferença entre a microdureza dos terços cervical, médio e apical na linha de cimento. Quarenta incisivos bovinos tratados endodonticamente foram distribuídos em quatro grupos para a cimentação de pinos Fibrekor® (Jeneric/Pentron) de 1mm de diâmetro, sendo: Grupo 1 - Panavia F 2.0 (Kuraray Medical Inc.), Grupo 2 - Variolink (Ivoclar), Grupo 3 - Rely X Unicem (3M ESPE) e Grupo 4 - Duolink (Bisco). Após a cimentação, as raízes foram divididas em 2 subgrupos, sendo 5 seccionadas após 7 dias para análise da microdureza inicial e 5 mantidas íntegras em água deionizada por 3 meses, para avaliação da microdureza final no microdurômetro Shimadzu HMV (Japan). Após a mensuração inicial, as raízes seccionadas eram armazenadas a 37º C por 24h em 10mL de solução de etanol a 75%, e reavaliadas. Foram identificadas diferenças estatisticamente significativas entre cimentos, terços e períodos (inicial ou após 24h de imersão em etanol a 75%), bem como interações entre cimento/terços e cimento/períodos de avaliação. O cimento Panavia exibiu os valores de microdureza inicial significativamente superiores, sem diferença estatística entre os demais cimentos. Os valores de microdureza inicial por terços não seguiram um padrão homogêneo; os cimentos Variolink e Duolink exibiram valores de microdureza significativamente superiores no terço cervical, sem diferença significativa entre os terços para os demais cimentos. A imersão em etanol reduziu significativamente a média dos valores de dureza para todos os cimentos; o comportamento por terços variou em função do material. O armazenamento em água por 3 meses não exerceu influência sobre a dureza da maioria dos cimentos, com exceção do Unicem, que exibiu aumento significativo dos valores de dureza após esse período. Portanto, a hipótese proposta neste estudo foi rejeitada. / Resin cements have been largely used in dentistry for retaining intraradicular posts and to minimize tension between them. However, the degree of conversion influences mechanical properties, biocompatibility and susceptibility of water and acid degradation of these polymers. Hardness tests are used to estimate the degree of conversion of composites, as it shows good correlation with infrared spectroscopy. The aim of this study was to evaluate the microhardness of four resin cements used for fiber posts cementation at the nitial period, 24h-immersion in a 75% ethanol solution and after 3-month water storage. Forty bovine incisives were endodontically treated and restored with 1mm diameter Fibrekor® posts (Jeneric/Pentron), being: Group 1 - Panavia F 2.0 (Kuraray Medical Inc.), Group 2 - Variolink (Ivoclar), Group 3 - Rely X Unicem (3M ESPE) and Group 4 - Duolink (Bisco). After cementation, each group was divided in two subgroups: 5 roots were sectioned 7 days after cementation for initial hardness measurement and 5 roots were immersed in deionized water for 3 months for final hardness measurements using Shimadzu Micro Hardness Tester (HMV, Japan). After the initial measurements, the sectioned roots were immersed in 10mL 75% ethanol solution for 24h at 37ºC, and tested again. Differences in hardness values have been detected among resin cements, radicular thirds and periods (initial or 24h-immersion in a 75% ethanol solution). Data also revealed significant interaction to cement/third and cement/period of evaluation. Panavia showed higher hardness values, with no statistical differences among the other cements. It was not verified a homogeneous pattern regarding radicular third; Variolink and Duolink exhibited higher hardness values for the cervical third, without differences among radicular thirds for the other cements. Hardness values decreased after ethanol immersion for all resin cements and the hardness according to radicular thirds varied among the materials. The hardness of tested resin cement showed no influence after 3-month water storage, except for Unicem as it showed an increase in Knoop hardness after this period. Therefore, the null hypotesis proposed was rejected.

Orientador: Angela Cristina Cilense Zuanon / Resumo: O cimento de ionômero de vidro (CIV) apresenta características favoráveis como ação antimicrobiana e capacidade de remineralização. A fim de potencializar essas propriedades, sua associação com outros materiais como as nanopartículas (NP) e os vidros bioativos (VB) é estudada e muita atenção deve ser voltada às possíveis alterações que podem ocorrer em suas propriedades físicas, mecânicas e químicas. O objetivo deste estudo foi avaliar propriedades físicas e mecânicas do CIV associado a NP de hidroxiapatita (HPa) a 5% e ao VB 45S5 a 10%, antes e após teste de escovação, em diferentes tempos de armazenamento. Foram avaliadas rugosidade superficial com auxílio de rugosímetro, dureza Vickers por meio de microdurômetro, e variação de massa do material medida por pesagens em balança analítica, além da análise qualitativa de sua superfície, por meio de perfilômetro, nos tempos de 1, 7, 15, 30 e 60 dias, antes e após o teste de escovação. Os dados obtidos foram analisados estatisticamente quanto à normalidade e a homogeneidade. A distribuição foi não normal e os testes não-paramétricos de Wilcoxon, e de Kruskal Wallis seguido pelo de Dunn foram realizados, todos com um nível de significância de 5%. Pode-se observar maiores valores para a perda de massa no primeiro dia de experimento para todos os grupos. A rugosidade superficial foi menor nos grupos Controle e NP aos 30 dias de experimento após o ensaio de escovação. A análise qualitativa por meio do perfil dos materiais confirma a ... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The glass ionomer cement (GIC) has favorable characteristics such as antimicrobial action and remineralization capacity. In order to potentiate these properties, its association with other materials such as nanoparticles (NP) and bioactive glasses (BAG) is studied, and a great deal of attention must be given to the possible changes that may occur in the physical, mechanical and chemical properties. The objective of this study was to evaluate the physical and mechanical properties of GIC associated with 5% of hydroxyapatite NP (NPHPa) and of 10% BAG 45S5 before and after brushing test at different storage times. The surface roughness was evaluated using a rugosimeter, Vickers hardness by microdurometer, and mass variation of the material measured by analytical weighing, as well as the qualitative analysis of its surface by means of a profilometer at the times of 1, 7, 15, 30 and 60 days, before and after the brushing test. The data obtained were statistically analyzed for normality and homogeneity. The distribution was non-normal and the non-parametric Wilcoxon and Kruskal Wallis followed by Dunn's tests were performed, all with a significance level of 5%. It is possible to observe higher values for the loss of mass in the first day of experiment for all the groups. The surface roughness was lower in the control and NP groups at 30 days of experiment after the brushing test. The qualitative analysis through the profile of the materials confirms these findings. Larger values fo... (Complete abstract click electronic access below) / Mestre