Additive manufacturing (AM) processes may introduce large residual stresses in the as-built part, in particular the laser powder bed fusion process (L-PBF). The residual stress state is an inherent consequence of the heterogeneous heating and subsequent cooling during the process. L-PBF has become renowned for its “free complexity” and rapid prototyping capabilities. However, it is vital to ensure shape stability after the component is removed from the build plate, which can be problematic due to the residual stress inducing nature of this manufacturing process. Residual stresses can be analyzed via many different characterization routes (e.g. X-ray and neutron diffraction, hole drilling, etc.), both quantitatively and qualitatively. From an industrial perspective, most of these techniques are either prohibitively expensive, complex or too slow to be implementable during the early prototyping stages of AM manufacturing. In this work a deformation based method employing a specific geometry, a so called “keyhole”-geometry, has been investigated to qualitatively evaluate the effect of different stress relief annealing routes with respect to macroscopic part deformation, mechanical properties and microstructure. Previous published work has focused on structures with open geometry, commonly referred to as bridge-like structures where the deformation required for analysis occurs during removal from the build plate. The proposed keyhole-geometry can be removed from the build plate without releasing the residual stresses required for subsequent measurement, which enables bulk manufacturing on single build plates, prior to removal and stress relief annealing.  Two L-PBF manufactured austenitic stainless steel alloys were studied, 316L and 21-6-9. Tensile specimen blanks were manufactured and the subsequent heat treatments were carried out in pairs of keyhole and tensile blank. Both a contact (micrometer measurement), and a non-contact (optical profilometry) method were employed to measure the residual stress induced deformation in the keyholes. The annealing heat treatment matrix was iteratively expanded with input from the deformation analysis to find the lowest temperature at which approximately zero deformation remained after opening the structure via wire electrical discharge machining. The lowest allowable annealing temperature was sought after to minimize strength loss.  After stress relief annealing at 900 ℃ for 1 hour, the 316L keyhole-geometry was considered shape stable. The lateral micrometer measurement yielded a length change of 1 µm, and a radius of 140 m (over the 22 mm top surface) was assigned from curve fitting the top surface height profiles. The complementary microstructural characterization revealed that this temperature corresponded to where the last remains of the cellular sub-grain structures disappears. Tensile testing showed that the specimen subjected to the 900 ℃ heat treatment had a marked reduction in yield stress (YS) compared to that of the as-built: 540 MPa → 402 MPa, whereas ultimate tensile strength (UTS) only reduced slightly: 595 MPa → 570 MPa. The ductility (4D elongation) was found to be ~13 % higher for the specimen heat treated at 900 ℃ than that of the as-built specimen, 76% and 67% respectively.  For alloy 21-6-9 the residual stress induced deformation minimum (zero measurable deformation) was found after stress relief heat treatment at 850 ℃ for 1 hour. Slight changes in the microstructure were observable through light optical microscopy when comparing the different heat treatment temperatures. The characteristic sub-grain features associated with alloy 316L were not verified for alloy 21-6-9. Similar to the results for 316L, UTS was slightly lower for the tensile specimen subjected to the heat treatment temperature required for shape stability (850 ℃) compared to the as-built specimen: 810 MPa → 775 MPa. The measured ductility (4D elongation) was found to be approximately equal for the as-built (47%), and heat treated (48%) specimen. As-built material exhibited a YS of 640 MPa while the heat treated specimen had a YS of 540 MPa. For alloy 21-6-9, the lateral micrometer deformation measurements were compared with stress relaxation testing performed at 600 ℃, 700℃ and 800 ℃. Stress relaxation results were in good agreement with the results from the lateral deformation measurements.  The study showed that for both steel alloys, the keyhole method could be successfully employed to rapidly find a suitable stress relief heat treatment route when shape stability is vital.

No description available.

No description available.

No description available.

No description available.

High chromium cast iron (HCCI) is considered as one of the most useful wear resistance materials and their usage are widely spread in industry. The wear resistance and mechanical properties of HCCI mainly depend on type, size, number, morphology of hard carbides and the matrix structure (γ or α). The Hypereutectic HCCI with large volume fractions of hard carbides is preferred to apply in wear applications. However, the coarser and larger primary M7C3 carbides will be precipitated during the solidification of the hypereutectic alloy and these will have a negative influence on the wear resistance. In this thesis, the Ti-added hypereutectic HCCI with a main composition of Fe-17mass%Cr-4mass%C is quantitatively studied based on the type, size distribution, composition and morphology of hard carbides and martensite units. A 11.2μm border size is suggested to classify the primary M7C3 carbides and eutectic M7C3 carbides. Thereafter, the change of the solidification structure and especially the refinement of carbides (M7C3 and TiC) size by changing the cooling rates and Ti addition is determined and discussed. Furthermore, the mechanical properties of hypereutectic HCCI related to the solidification structure are discussed. Mechanical properties of HCCI can normally be improved by a heat treatment process. The size distribution and the volume fraction of carbides (M7C3 and TiC) as well as the matrix structure (martensite) were examined by means of scanning electron microscopy (SEM) and electron backscattered diffraction (EBSD). Especially for the matrix structure, EBSD is a useful tool to classify the fcc (γ) and bcc (α) phases. In conclusion, low holding temperatures close to the eutectic temperature and long holding times are the best heat treatment strategies in order to improve wear resistance and hardness of Ti-alloyed hypereutectic HCCI. / <p>QC 20121130</p>

Electron beam melting (EBM), a metal additive manufacturing (AM) process, has received considerable industrial attention for near net shape manufacture of complex geometries with traditionally difficult-to-machine materials. This has fuelled considerable academic interest in investigating EBM of Alloy 718, a nickel ironbased superalloy possessing an exciting combination of good mechanical behaviour and cost effectiveness. EBM production of Alloy 718 is particularly promising for aerospace and other sectors which value rapid production of components with large scope for design flexibility. The EBM builds are characterized by presence of inevitable defects and, anisotropy within a build is also a concern. Consequently, as-built Alloy 718 has to be subjected to post-build thermal-treatments (post-treatments) to ensure that the parts eventually meet the critical service requirements. Not withstanding the above, limited knowledge is available about optimal post-treatments for EBM-built Alloy 718. Therefore, the main focus of the work presented in this thesis was to systematically investigate the response of EBM-built material to post-treatments, which include hotisostatic pressing (HIPing), solution treatment (ST), and aging. HIPing of EBM-built Alloy 718 led to more than an order of magnitude reduction in defect content, which was reduced from as high as 17% to &lt; 0.2% in samples built with intentionally introduced porosity to investigate limits of defect closure achievable through HIPing. In addition, HIPing also caused complete dissolution of δ and γ" phases present in the as-built condition, with the latter causing dropin hardness of the material. HIPing had no effect on the carbides and inclusions such as TiN, Al2O3 present in the built material. The evolution of microstructure during ST and aging was systematically investigated. Growth of potentially beneficial grain boundary δ phase precipitates was found to cease after a certain duration of ST, with samples subjected to prior-HIPing exhibiting lesser precipitation of the δ phase during ST. While the specimen hardness increased onaging, it was observed to plateau after a duration significantly shorted than the specified ASTM 'standard' aging cycle. Therefore, prima facie there are promising prospects for shortening the overall heat treatment duration. A combination of HIPing, ST, and aging treatments in a single uninterrupted cycle was also explored. Future work involving incorporation of a shortened heat treatment schedule in a combined cycle can have significant industrial implications. / <p>Articles submitted to journals and unpublished manuscripts are not included in this registration</p>

No description available.

The present dissertation reports the findings of a study of cracking behavior of a newly developed superalloy, Allvac 718Plus during high power beam welding and post-weld heat treatment. Microstructures of the base alloy, heat affected zone (HAZ) and fusion zone (FZ) of welded and post-weld heat treated (PWHT) coupons were examined by the use of standard metallographic techniques involving optical microscopy, analytical scanning electron microscopy (SEM) and analytical transmission electron microscopy. Moreover, grain boundary segregation behavior of boron atoms during pre-weld heat treatments was evaluated using secondary ion mass spectroscopic system. In the first phase of the research, 718Plus was welded using a low and high heat input CO2 laser to assess its weld cracking response. Detailed examination of the welds by analytical electron microscopic technique revealed the occurrence of cracking in the HAZ of low heat input welds, while their FZ was crack free. However, both the FZ and HAZ of high heat input welds were crack-free. Resolidified constituents were observed along the cracked grain boundaries of the lower heat input welds, which indicated that HAZ cracking in this newly developed superalloy was associated with grain boundary liquation. However, despite a more extensive liquation of grain boundaries and grain interior in the HAZ of high heat input welds, no cracking occurred. This was attributed to the combination of lower welding stresses generated during cooling, and relaxation of these stresses by thick intergranular liquid. Although HAZ cracking was prevented by welding with a high heat input laser, it resulted in a significant damage to the parent microstructure through its extensive liquation. Thus, the use of low heat input welding is desirable. However, this resulted in HAZ cracking which needs to be minimized or eliminated. Therefore, during the second phase of this research, the effects of pre-weld thermal processing on the cracking response of 718Plus were investigated. Results from the quantification of the cracking of the alloy showed that HAZ cracking may be significantly reduced or eliminated through an adequate selection of pre-weld thermal cycle. In the third stage of this research, crack-free welds of 718Plus were post-weld heat treated using standard thermal schedules. A significant solid state cracking of the alloy occurred during the PWHT. The cracking was attributed to the presence of embrittling phases on HAZ grain boundaries, coupled with aging contraction stresses that are generated by a considerable precipitation of gamma prime phase during aging.

The present dissertation reports the findings of a study of cracking behavior of a newly developed superalloy, Allvac 718Plus during high power beam welding and post-weld heat treatment. Microstructures of the base alloy, heat affected zone (HAZ) and fusion zone (FZ) of welded and post-weld heat treated (PWHT) coupons were examined by the use of standard metallographic techniques involving optical microscopy, analytical scanning electron microscopy (SEM) and analytical transmission electron microscopy. Moreover, grain boundary segregation behavior of boron atoms during pre-weld heat treatments was evaluated using secondary ion mass spectroscopic system. In the first phase of the research, 718Plus was welded using a low and high heat input CO2 laser to assess its weld cracking response. Detailed examination of the welds by analytical electron microscopic technique revealed the occurrence of cracking in the HAZ of low heat input welds, while their FZ was crack free. However, both the FZ and HAZ of high heat input welds were crack-free. Resolidified constituents were observed along the cracked grain boundaries of the lower heat input welds, which indicated that HAZ cracking in this newly developed superalloy was associated with grain boundary liquation. However, despite a more extensive liquation of grain boundaries and grain interior in the HAZ of high heat input welds, no cracking occurred. This was attributed to the combination of lower welding stresses generated during cooling, and relaxation of these stresses by thick intergranular liquid. Although HAZ cracking was prevented by welding with a high heat input laser, it resulted in a significant damage to the parent microstructure through its extensive liquation. Thus, the use of low heat input welding is desirable. However, this resulted in HAZ cracking which needs to be minimized or eliminated. Therefore, during the second phase of this research, the effects of pre-weld thermal processing on the cracking response of 718Plus were investigated. Results from the quantification of the cracking of the alloy showed that HAZ cracking may be significantly reduced or eliminated through an adequate selection of pre-weld thermal cycle. In the third stage of this research, crack-free welds of 718Plus were post-weld heat treated using standard thermal schedules. A significant solid state cracking of the alloy occurred during the PWHT. The cracking was attributed to the presence of embrittling phases on HAZ grain boundaries, coupled with aging contraction stresses that are generated by a considerable precipitation of gamma prime phase during aging.