Spelling suggestions: "subject:"histerese."" "subject:"histereses.""
61 |
Determinação da polarização ferroelétrica do PVDF estirado biaxialmente utilizando a técnica de corrente constante. / Determination of the biaxially stretched PVDF ferroelectric polarization using constant current technique.Walterley Araujo Moura 22 July 1998 (has links)
Foi desenvolvido um novo método para a determinação da polarização ferroelétrica de polímeros ferroelétricos, em particular do PVDF estirado biaxialmente. A técnica consiste em manter constante a corrente através da amostra e medir a evolução da tensão (V versus t) entre os eletrodos da mesma. As medidas foram realizadas em ambiente com atmosfera de ar superseco o que permite desprezar a condução elétrica das amostras, simplificando sobremaneira as equações do problema. Considera-se a existência de dois tipos de polarização: a ferroelétrica, com tempo de chavamento desprezível, e uma polarização elétrica foram realizados em duas situações distintas: com chaveamento e sem chaveamento ferroelétrico. O procedimento permite avaliar a dependência da polarização ferroelétrica com o campo, determinada a partir da equação geral da corrente. Para se descrever a resposta da polarização elétrica dependente do tempo, usa-se o princípio da superposição e assume-se que ela está em fase com o campo elétrico aplicado (processo lento). Será mostrado que é possível determinar a polarização ferroelétrica do polímero PVDF estirado biaxialmente sem a necessidade de determinar a formas funcionais da polarização dependente do tempo e de se conhecer o valor da capacitância da amostra. / In this work a novel method was developed for the determination of the ferroelectric polarization of ferroelectric polymers, in particular of biaxially stretched PVDF. The technique consists of maintaining constant the current through the sample and to measure the evolution of the bias voltage (V versus t) on the electrodes. Measurements were performed in super-dry air, which allows one to neglect the electric surface and volumetric conduction of the samples, simplifying the equations of the problem. It is considered the existence of two polarization types: the ferroelectric, with a very short switching time, and a another polarization dependent of the time. The processes for studying the electric polarization were accomplished in two different situations: with switching and without ferroelectric switching. The procedure allows evaluating the dependence of the ferroelectric polarization on the electric field, determined starting from the general equation of the current. To describe the time dependent polarization it is used the principle of superposition and the polarization value assumed to be in phase with the applied electric field (slow process). It will be shown that it is possible to determine the ferroelectric polarization of the material without the need of the functional form of the polarization and the value of the capacitance of the sample.
|
62 |
Exchange Bias em filmes de IrMn/Cu/CoNicolodi, Sabrina January 2007 (has links)
Medidas de magnetização (MAG) e de ressonância ferromagnética (FMR) foram usadas para estudar a interação de troca entre a camada antiferromagnética (AFM) de IrMn e a ferromagnética (FM) de Co no sistema IrMn/Cu/Co em função da espessura do Cu. Parâmetros importantes extraídos destas medidas foram comparados com os respectivos valores obtidos dos ajustes dos dados experimentais através de um modelo fenomenológico. Foi observada uma concordância muito boa entre os dados experimentais e os simulados numericamente. Os valores dos campos de anisotropia e de interação, obtidos pelas duas técnicas, MAG e FMR, foram comparados. Observou-se que, apesar das variações angulares experimentais dos campos de Exchange Bias coincidirem para todas as amostras, a intensidade de acoplamento J e os campos de anisotropia das camadas de Co (obtidos via simulação numérica) HU , são diferentes. Para todas as espessuras de Cu, vimos que J FMR > J MAG e FMR U H < MAG U H . Outro resultado importante é que J diminui exponencialmente com o aumento da espessura do espaçador, resultado de uma interação de curto alcance mediada por pinholes. Todas estas características foram explicadas através de um modelo que considera camadas magnéticas policristalinas com distribuições de eixos fáceis independentes, tomando em conta a anisotropia rodável. Conhecer o papel dos grãos AFM com diferentes tamanhos e diferentes estabilidades magnéticas também é essencial para entender as propriedades deste sistema. Os fatos dos HEB observados serem iguais (diferentemente dos resultados até agora conhecidos) e as interações assim como as anisotropias uniaxiais serem diferentes foram atribuídos ao fato de que as duas técnicas detectam processos diferentes. A medição estática, MAG, prioriza a amostra como um todo, enquanto a FMR (a qual depende da freqüência de oscilação da magnetização) detecta somente os momentos magnéticos cujos tempos de relaxação são menores do que o tempo de excitação da microonda. Quando não existe mais contato entre as camadas de IrMn e Co (e consequentemente, a interação), as diferenças entre as medidas não são mais observadas. / Magnetization (MAG) and ferromagnetic resonance (FMR) measurements were used to study the exchange interaction between the IrMn (antiferromagnetic, AFM) and Co (ferromagnetic, FM) layers in an IrMn/Cu/Co system as a function of the Cu spacer thickness. Important parameters, extracted from these measurements, were compared with the respective values obtained from the experimental data fittings through a phenomenological model, and a very good agreement between experiment and model was observed. The comparison between the anisotropy and interaction fields obtained from both techniques, MAG and FMR, showed that although the experimental angular variations of the exchange-bias fields, FMR eb H and MAG eb H coincide, the coupling strengths, J and the Co layers' anisotropy fields, U H , obtained via numerical simulations, are different. For all Cu thicknesses, it was estimated that J FMR > J MAG e FMR U H < MAG . U H Another important result is that J decreases exponentially with the spacer thickness and is a short-range interaction mediated by pinholes. All these characteristics were explained in the framework of a model considering polycrystalline magnetic layers with independent easy axis distributions and taking into account the rotatable anisotropy. The role of antiferromagnetic grains at the interface with different sizes and different magnetic stability is essential for understanding the behavior of this exchange-biased system. The facts that the observed FMR eb H and MAG eb H are equal (differently from all results known till now) and that the interactions as well as the uniaxial anisotropies are different were attributed to the different processes detected by the techniques. While the static MAG measurement ‘senses’ the sample as a whole, the FMR (which depends on the frequency of the oscillation of the magnetization) detects only the magnetic moments with relaxation times less than the period of the microwave excitation. There are no differences observed between the measurements when there is no contact (and consequently, the interaction) between the IrMn and Co layers.
|
63 |
Estudo da energia cinética do condensado nos sistemas supercondutores SmBa2Cu3O7−δ , Bi2Sr2CaCu2Ox e Ba(Fe1−xCox)2As2Peña Pacheco, Jully Paola January 2012 (has links)
Nesta dissertação é apresentado um estudo experimental da densidade de energia cinética (Ek), induzida pela aplicação de um campo magnético, em cinco amostras de três sistemas supercondutores do tipo II. As amostras consistem em dois policristais do sistema SmBa2Cu3O7− (Sm123), dois monocristais do sistema Bi2Sr2CaCu2Ox (Bi2212) com concentrações de oxigênio ligeiramente diferentes, e um monocristal do ferro-pnictídeo BaFe1,84Co0,16As2 (BaFeCoAs). Em todos os casos, a densidade de energia cinética é obtida através da expressão proposta por Doria e colaboradores: Ek = −MB, onde M é a magnetização de equilíbrio e B é a indução magnética. A magnetização é obtida a partir de medidas do momento magnético realizadas segundo os procedimentos ZFC (zero field cooled ) e FC (field cooled ). Este estudo limita-se à região reversível da magnetização, nas proximidades da temperatura crítica da transição supercondutora. Para todas as amostras, é feita uma análise qualitativa do comportamento da linha de irreversibilidade e, nas amostras de Bi2212, são observados os efeitos da anisotropia para as situações em que o campo externo é aplicado nas orientações paralela ou perpendicular às camadas atômicas de CuO2. No caso do BaFeCoAs, apenas a configuração em que o campo é aplicado paralelamente ao eixo principal de simetria é investigada. Nas amostras de Sm123 encontraram-se contribuições à energia cinética correspondentes à região de campos intermediários. Nesta região, a magnetização pode ser estudada na aproximação de London para a teoria de vórtices em supercondutores do tipo II. Nas amostras de Bi2212, as contribuições identificadas para Ek originam-se de vórtices do tipo Abrikosov e da granularidade intrínseca. Nestas amostras, quando o campo magnético é aplicado paralelamente aos planos de CuO2, há evidências da ocorrência de uma transição de primeira ordem envolvendo o sistema de vórtices, o qual evolui de um regime 3D para 2D com o aumento da temperatura. Na amostra de BaFeCoAs, a densidade de energia cinética apresenta máximos locais em diferentes valores de temperatura e campo magnético, além de notáveis efeitos de pinning. / This dissertation presents an experimental study about the behavior of the kinetic energy density, Ek, induced by an applied magnetic field on five samples of three different type II superconducting systems. These samples are: two SmBa2Cu3O7− (Sm123) polycrystals, two Bi2Sr2CaCu2Ox (Bi2212) single crystals with slightly different oxygen concentrations, and one BaFe1,84Co0,16As2 (BaFeCoAs) single crystal. The kinetic energy density is obtained through the expression proposed by Doria et al.: Ek = −MB, were M is the equilibrium magnetization and B is the magnetic induction. The magnetization is obtained from magnetic moment measurements carried out following the ZFC and FC procedures. This study is limited to the reversible magnetization region near the critical temperature. For all samples, a qualitative analysis of the irreversibility line is performed. Anisotropy effects are observed in the Bi2212 samples when the external field is applied parallel or perpendicular to the CuO2 atomic planes. For the BaFeCoAs sample, only the configuration where the external field is applied parallel to c-axis is investigated. In the Sm123 samples, the kinetic energy contributions correspond to the intermediate field region, where the magnetization is described by the London approximation for the vortex theory in type II superconductors. In the Bi2212 samples the identified contributions for Ek originate from Abrikosov type vortex and intrinsic granularity. When the magnetic field is applied parallel to the CuO2 planes, evidences are observed for the ocurrence of a first-order transition nearly below Tc, related to decoupling of the vortex lattice from a 3D configuration to a 2D regime upon increasing the temperature. The kinetic energy density in the BaFeCoAs sample presents some local maxima in different temperature and field values. This sample also show strong pinning effects.
|
64 |
Análise micromagnética e desenvolvimento computacional aplicados a sistemas que apresentam acoplamento de trocaCichelero, Rafael January 2015 (has links)
O presente estudo aborda a evolução temporal de filmes finos compostos por materiais ferroantiferromagnéticos que apresentam interação de troca, visando a melhor compreensão da origem desse comportamento. Técnicas como a de irradiação iônica e tratamento térmico foram utilizadas para a modificação dos sistemas magnéticos em questão. Após submetidos a essas ferramentas de indução do efeito de exchange bias (viés de troca), as amostras foram expostas a campos magnéticos durante determinado intervalo de tempo `a temperatura ambiente. Após realizada a exposição, a medida de histerese magnética era feita, seus os campos de interesse foram computados, e os resultados são expostos frente ao tempo de exposição há campo magnético. As amostras apresentaram comportamentos distintos dependentes das técnicas de indução. Após irradiação iônica, o estado magnético permanece instável, devido a configuração energética imposta pela irradiação; desse modo efeitos térmicos de baixa amplitude podem fornecer energia para que a camada ferromagnética mude as orientações das magnetizações de grãos interfaciais. Por outro lado, o tratamento térmico promoveu ao sistema de interesse uma configuração energeticamente estável, eliminando ou reduzindo os efeitos térmicos induzidos pós-tratamento. Além disso, o desenvolvimento de uma ferramenta computacional foi necessário na tentativa de obtenção dos resultados obtidos experimentalmente. Este software usa como base a bem conhecida teoria do micromagnetismo a qual, auxiliada pela equação de Landau-Lifshitz-Gilbert, é uma ótima ferramenta tanto para prever como para reproduzir o comportamento de sistemas magnéticos. Todos os procedimentos para o desenvolvimento desse software encontram-se definidos nas seções seguintes, incluindo um método de soma em memória compartilhada, o qual visa melhorar o desempenho computacional para o cálculo dos efeitos provinientes de interações dipolares. Para finalizar, resultados experimentais e computacionais são expostos, mostrando a meta-instabilidade presente nos sistemas magnéticos abordados. / The present study examines the temporal evolution of thin magnetic films composed by ferro and antiferromagnetic materials that present exchange interactions, aiming a better understanding of the origin of their behavior. Techniques such as ion irradiation and magnetic annealing were used for modification of the systems studied. Once used such tools for initialization of the exchange-bias effect, the samples were exposed to magnetic fields during a certain time interval at room temperature. Subsequently, room temperature magnetization hysteresis loops were measured and the corresponding fields of interest were extracted. Depending on the different exchange-bias induction techniques, the samples showed distinct behaviors. After light ion irradiation, the magnetic state remained unstable, most probably due to thermal fluctuations that can alter the magnetic orientation of interface grains. The annealing, from other side, enabled a favorable energy configuration of the system, eliminating or reducing post-treatment thermally-induced effects in our the systems. Moreover, the development of a computational tool turned to be necessary when attempting to reproduce the experimental results. This software built is based on the well-established micromagnetic theory which, by additionally utilizing by the Landau-Lifshitz-Gilbert equation, represents a powerful tool used to predict and/or reproduce the behavior of magnetic systems. All procedures for the development of this software are defined in the following sections, including a shared memory programming, developed in order to increase the computational performance when reproducing dipolar interaction effects. Finally, experimental and simulation results are presented, demonstrating the metastable states of the magnetic systems studied here.
|
65 |
Inclusão de efeitos dissipativos em modelos constitutivos hiperelásticos através da modificação da função energia de deformaçãoWrubleski, Eduardo Guilherme Mötke January 2015 (has links)
Este trabalho apresenta uma metodologia para a inclusão de fenômenos dissipativos em relações constitutivas hiperelásticas. Embora seja dada ênfase para o efeito Mullins e histerese, esse procedimento pode ser aplicado a outros fenômenos como, por exemplo, de dano. Para isso, adota-se um modelo fenomenológico que inclui amolecimento em um modelo constitutivo hiperelástico através da pseudo-elasticidade, que permite que diferentes potenciais de energia possam ser utilizados em diferentes etapas do carregamento. Foram utilizados dois modelos hiperelásticos incompressíveis: Ogden e Hoss-Marczak. Para esse estudo, foram selecionados quatro diferentes materiais da literatura, três deles apresentavam apenas dados experimentais para tração uniaxial, enquanto o outro disponibilizou os ensaios de tração uniaxial, tração equibiaxial e cisalhamento puro. Foram selecionados dois parâmetros de amolecimento da literatura (Ogden e Roxburgh, 1999, e Dorfmann e Ogden, 2003) para modelar fenômenos dissipativos e então foram propostos novos parâmetros de amolecimento. Verificação gráfica dos resultados e um coeficiente de correlação (R2) foram utilizados para comparar o desempenho desses parâmetros. Os materiais foram considerados isotrópicos e incompressíveis e o carregamento quasi-estático para obtenção dos resultados. Alguns parâmetros propostos não capturaram o efeito dissipativo, outros superestimaram o amolecimento, enquanto os da literatura capturaram o efeito. Ao final, obteve-se resultados bastante satisfatórios para um dos parâmetros propostos, que se verificou ser uma generalização do modelo de Dorfmann e Ogden, 2003. / This work applies a methodology to include dissipative effects in hyperelastic constitutive relations. The paper focuses on the Mullins effect and hysteresis. However, the methodology can also be applied to other phenomena, like damage. Basically, it is a phenomenological inclusion of the softening behavior in a hyperelastic constitutive model using pseudo-elasticity, in which different energy potentials can be used in different steps of the loading. Two hyperelastic models were employed: Ogden’s and Hoss-Marczak’s models. Four different materials were modeled, three of them subjected to uniaxial tension only, and a fourth subjected to the three classical loadings, namely, uniaxial tension, equibiaxial tension and pure shear. Two softening parameters from the literature were implemented and new softening parameters were proposed. Graphical inspection and R2 correlation coefficient were used to compare the softening parameters. The materials were considered isotropic and incompressible, being subjected to quasi-static loading. Some of the proposed parameters did not captured the dissipative effect, other overestimate the softening, and those from the literature were able to capture the effects. Finally, very satisfying results were obtained with one the proposed softening parameters, which was a generalization of the one proposed by Dorfmann e Ogden, 2003.
|
66 |
Relações entre precipitação, escoamento e sedimentos suspensos na bacia do Rio das Antas, Goiás / Relationships between rainfall, runoff and suspended sediments in the Antas River watershed, GoiásDidonet, Thais Teodoro dos Santos Cordeiro 06 September 2017 (has links)
Submitted by Luciana Ferreira (lucgeral@gmail.com) on 2017-10-16T10:28:49Z
No. of bitstreams: 2
Dissertação - Thais Teodoro dos Santos Cordeiro Didonet - 2017.pdf: 3406839 bytes, checksum: 596f54252c80087a5daf3da4918ebd91 (MD5)
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2017-10-16T10:29:09Z (GMT) No. of bitstreams: 2
Dissertação - Thais Teodoro dos Santos Cordeiro Didonet - 2017.pdf: 3406839 bytes, checksum: 596f54252c80087a5daf3da4918ebd91 (MD5)
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2017-10-16T10:29:09Z (GMT). No. of bitstreams: 2
Dissertação - Thais Teodoro dos Santos Cordeiro Didonet - 2017.pdf: 3406839 bytes, checksum: 596f54252c80087a5daf3da4918ebd91 (MD5)
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Previous issue date: 2017-09-06 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / Sediments transported by surface runoff and by rivers are essential components in the
comprehension of changes in a river basin and the quality of aquatic systems. The high variability
of rainfall events, the SSC and the relation between them produce complex behavioral dynamics
difficult to interpret but the study of these aspects is a useful and frequently used tool in the
quantification of impacts due to erosive and hydrossedimentological processes. The main objective
of this study was to characterize and quantify the hydrological, sedimentological and granulometric
characteristics of the urban watercourse of the Rio das Antas basin, located in Anápolis, Goiás,
wich faces various erosion processes. Continuous monitoring of precipitation, flow rates, sediment
concentrations and turbidity was performed using pluviographs, linigraphs, an automatic sampler
and a laser granulometer during most of a rainy season, where samples were collected and 14
events were analyzed. Descriptive statistical analyzes, identification of hysteresis patterns, Event
Mean Concentration, “first flush” phenomenon effects and grain size distribution and their
relationships with precipitations and flow rates were performed. The peak concentration of total
sediments reached 3,380 mg L -1 , and approximately 83% were suspended sediments. No “first
flush" has been recorded in any event. The highest mean concentration observed for suspended
sediments was 1,714.6 mg/m3 and the mean of the events was 1,001.3 mg/m3, values considered to
be high when compared to river basin flows, where the highest was 15.49 m 3 s -1 . The maximum
flow rates were determinant in the total sediment, however, the same flow range carried very
different amounts of suspended sediments during the floods. This behavior suggests that the
variation also depends on precipitation characteristics and sediment sources. In the hysteresis
analyzes, it can be verified that these sources are located farther from the monitoring point, but are
also the river itself, since the most frequent hysteresis loop was "Figure Eight" followed by the"Counter Clock-wise” type. There were complex hysteretic loops characterized by multiple peaks
of flow and sediments. The size of particles carried by the flow varies throughout the rainy season.
The suspended sediment particles had dimensions between 0.0019 mm and 0.990 mm being
characterized as sandy silt material. The small and medium particles were more frequent in final
events and larger particles occurred in the middle of the period. Finner particles were more present
during the rise of the hydrograph and in the recession phase the amount of particles with
dimensions between 0.2 mm e 0.6 mm increased in some events. Particles larger than 0.6 mm were
not related to precipitation. It was also observed that the amount of dissolved solids decreases with
increasing particle size and may indicate that larger particles have less capacity to absorb/adsorb
other pollutants. It is observed that the suspended sediments vary between the events and within
the same event and depends on the hydrological behavior, the characteristics of the water body and
the type of monitoring. / Os sedimentos transportados pelo escoamento superficial e pelos rios são componentes essenciais
no entendimento das mudanças ocorridas em uma bacia hidrográfica e da qualidade de sistemas
aquáticos. A alta variabilidade dos eventos chuvosos, da CSS e da relação entre eles produzem
dinâmicas comportamentais complexas de difícil interpretação. Porém o estudo destes aspectos é
uma ferramenta útil e frequentemente usada na quantificação dos impactos decorrentes de
processos erosivos e hidrossedimentológicos. Este estudo teve por objetivo caracterizar e analisar
quanti-qualitativamente as características hidrológicas, sedimentológicas e granulométricas dotrecho urbano da bacia do Rio das Antas, localizado no município de Anápolis, Goiás, o qual
enfrenta vários processos erosivos. Um monitoramento contínuo das precipitações, vazões,
concentrações de sedimentos e turbidez foi realizado utilizando pluvíografos, linígrafos, um
amostrador automático e um granulômetro a laser durante o período chuvoso, onde foram coletadas
amostras e analisados 14 eventos. Análises estatísticas descritivas, identificação dos padrões de
histerese, Concentração Média do Evento, efeitos de “first flush” e a distribuição granulométrica e
suas relações com as precipitações e vazões foram realizados. O pico de concentração de
sedimentos totais foi de 3.380 mg L -1 , sendo que, aproximadamente, 83% eram sedimentos
suspensos. Não foi registrado o fenômeno “first flush” em nenhum evento. A maior Concentração
Média do Evento observada para os sedimentos suspensos foi de 1.714,6 mg/m3 e a média dos
eventos foi de 1.001,3 mg/m3, valores considerados altos quando comparados as vazões de base do
rio, onde o maior pico registrado foi 15,49 m3 s -1 . As vazões máximas foram determinantes no total
de sedimentos, no entanto, uma mesma faixa de vazão transportou quantidades bem diferentes de
sedimentos suspensos durante as cheias. Este comportamento sugere que sua variação também
depende das características das precipitações e das fontes geradoras de sedimentos. Nas análises de
histerese, pode-se verificar que estas fontes estão presentes no próprio rio, mas também em locais
mais distantes do ponto de monitoramento, pois o laço de histerese mais frequente foi “Figura
Oito” seguido do tipo “Anti-horário”. Houveram laços histeréticos complexos caracterizados por
picos múltiplos de vazão e sedimentos. O tamanho das partículas transportadas pelo escoamento
varia em todo o período chuvoso. As partículas de sedimentos suspensos tinham dimensões entre
0,0019 mm e 0,990 mm sendo caracterizadas como material silte arenoso. As partículas pequenas e
médias foram mais frequentes nos eventos finais do período chuvoso e as partículas maiores
ocorreram no meio do período. Partículas mais finas estavam mais presentes durante a ascensão do
hidrograma e, na fase de recessão, a quantidade de partículas com dimensões entre 0,2 mm e 0,6
mm aumentava em alguns eventos. As partículas maiores que 0,6 mm não apresentaram relação
com a precipitação. Foi observado ainda que a quantidade de sólidos dissolvidos diminui com o
aumento do tamanho da partícula, podendo indicar que partículas maiores tem menor capacidade
de absorver/adsorver outros poluentes. Observa-se que os sedimentos suspensos variam entre os
eventos e dentro do mesmo evento e depende do comportamento hidrológico, das características do
corpo hídrico e do tipo de monitoramento.
|
67 |
Análise, por meio da técnica FORC, do efeito da histerese a alta freqüência no fenômeno da GMI / Analysis of the hysteretic effect on the high frequency GMI phenomenon by means of FORC techniqueCosta Arzuza, Luis Carlos, 1983- 19 August 2018 (has links)
Orientador: Kleber Roberto Pirota / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Física Gleb Wataghin / Made available in DSpace on 2018-08-19T11:29:30Z (GMT). No. of bitstreams: 1
CostaArzuza_LuisCarlos_M.pdf: 3383467 bytes, checksum: 8fac04d42ba77c741416d15d643d402a (MD5)
Previous issue date: 2011 / Resumo: Este trabalho visa estudar o comportamento histerético, observado a baixos campos magnéticos, do fenômeno da magnetoimpedância gigante (GMI) em fitas amorfas a base de CoFeSiB com anisotropia magnética transversal. O fenômeno da GMI consiste na variação da impedância elétrica (aproximadamente do 100%) de uma amostra magnética mole quando submetida à aplicação de campo magnético DC externo. Apesar da importância da presença de histerese na GMI, tanto do ponto de vista básico quanto do tecnológico, existem poucos estudos na literatura que visam à explicação da origem desse efeito. Desde o ponto de vista fundamental, o completo entendimento do fenômeno poderia revelar importantes aspectos envolvidos com o processo de magnetização nos materiais considerados. De um ponto de vista prático, a presença da histerese na GMI tanto pode ser desfavorável, quando pensamos na fabricação de sensores, quanto favorável, se levamos em consideração a sua possível aplicação em sistemas de memória magnética. Por outro lado, o método denominado curva de inversão da primeira ordem (first-order reversal curve, FORC, em inglês) mostra-se uma poderosa ferramenta para o estudo e compreensão de fenômenos histeréticos, principalmente da histerese magnética presente em curvas de magnetização de materiais ferromagnéticos. Tal método, fundamentado no modelo clássico de Preisach, dá importantes informações através de medidas de ciclos de histerese secundarias da curva principal. Neste trabalho utilizamos a técnica FORC para estudar o fenômeno da histerese na GMI. Utilizamos fitas amorfas de composição (CoxFe1-x)70Si12B18, com x = 0,040 e 0,045 como sistema de estudo devido a suas propriedades magnéticas moles. Tais fitas possuem 22 µm de espessura, 0,8 mm de largura e constante de anisotropia de 139 J/m3 e 145 J/m3 respetivamente. As medidas de GMI foram realizadas com um analisador de rede vetorial (vector network analizer, VNA, em inglês). Tal equipamento, combinado a um sistema de bobina e fonte de corrente, permitiu-nos fazer medidas de impedância em função da frequência (entre 10 MHz e 1 GHz) e do campo magnético aplicado (até 100 Oe). Consideramos como principal resultado deste trabalho o desenvolvimento de um método eficiente para testar e aprimorar modelos teóricos sobre a origem de tal histerese. Os resultados obtidos do comportamento histeretico no volume e na superficie, foram interpretados levando-se em conta uma estrutura magnética estática volumétrica não uniforme e ao amortecimento das paredes de domínio / Abstract: We studied the hysteretic behavior, observed at low magnetic fields, of the giant magnetoimpedance (GMI) phenomenon in CoFeSiB amorphous ribbons with transversal magnetic anisotropy. The GMI phenomenon consists in the electrical impedance variation (around 100 %) of a soft magnetic sample in the presence of an external DC magnetic field.Despite the importance of hysteresis presence in GMI from technological and basic points of view, it exists only few studies about the description of this effect. From the fundamental outlook, the complete understanding of the phenomenon could reveal important aspects involved in the magnetization process of the concerned materials. For practical applications, the hysteretic GMI can be unfavorable (for example for sensor development) or favorable (for example for magnetic storage memories). On the other side, first-order reversal curve (FORC) method is a powerful tool for the study and understanding of hysteretic phenomena, mainly for the hysteresis present in the magnetization curves of ferromagnetic materials. This method, based on the classical Preisach model, allows to extract important information through minor hysteresis loops inside the major one. In this work, we used the FORC technique to study the GMI hysteretic phenomenon. We investigated amorphous ribbons of (CoxFe1-x)70Si12B18 composition, where x = 0.040 and 0.045. Those ribbons were 2 µm thick and 0.8 mm wide. The GMI measurements were performed with a vector network analyzer (VNA). This equipment, coupled with a system of coil and power supply, allowed impedance measurements versus frequency (between 10 MHz and 1 GHz) and applied magnetic field (until 100 Oe). We consider that the main achievement of this work is the development of an efficient method allowing to test and improve theoretical models about the hysteresis origin. The obtained results were interpreted taking into account a non homogeneous static magnetic structure along the ribbon volume with domain walls damping / Mestrado / Física / Mestre em Física
|
68 |
Comportamento hidráulico de um perfil de solo não saturado de Aparecida de Goiânia-GO / Hydraulic behavior of an unsaturated soil profile of Aparecida de Goiania-GOBORGES, Camilla Rodrigues 30 April 2010 (has links)
Made available in DSpace on 2014-07-29T15:18:19Z (GMT). No. of bitstreams: 1
Camilla Rodrigues 1.pdf: 4672017 bytes, checksum: 12b69633a9d9499c45b4c515dc8a718b (MD5)
Previous issue date: 2010-04-30 / The hydraulic behavior of a tropical and unsaturated soil profile of Aparecida de Goiânia-GO
is presented. The main objective of this research was to contribute to the understanding of
hydraulic properties of a tropical soil, with special emphasis on the soil-water characteristic
curves and its hysteresis. The research work done was divided into two main parts: physical,
chemical and mineralogical characterization; and hydraulic behavior for the unsaturated
condition. The characterization tests indicate that the soil profile studied is formed by two
horizons. The top layer of 1,50 m comprised of transported material and a bottom layer
comprised of young residual soil. The results of particle size analysis have shown that the
various sample preparation conditions (i.e., with or without drying, chemical and physical
disaggregation) produce different grain-size distribution curves. A varying state of
disaggregation can be achieved, that state being dependent on the stability of the soil
aggregates. A fairly good correspondence between conventional hydrometer and laser
diffraction analysis was achieved, considering supposedly equivalent aggregation conditions.
The soil-water characteristic curve (SWCC) was measured for both the natural and the soil
reconstituted by mud consolidation. The role played by the soil fabric on the hydraulic
behavior of the soil was analyzed. The SWCC was obtained for drying, wetting, and mixed
paths, both in terms of total and matric suction. It was determined that the natural and
reconstituted soils have distinct SWCCs. The disaggregation achieved with the reconstituted
soil results in higher air-entry values and a unimodal SWCC, even when the natural soil
presents a bimodal SWCC. Therefore, the pore-size distribution if affected by the different
soil structures. The procedure for wetting and drying soil samples used along with the filter
paper technique resulted in a number of SWCCs showing absence of hysteresis. The study of
the moisture content along the specimen s heights revealed non-homogeneous moisture
content distributions, even after 14 day of equilibrium of water potential. It was concluded
that it is the very existence of SWCC hysteresis, along with a not sufficiently slow wetting
and drying from the specimen surface that results in a non-homogeneous moisture content. / Um estudo do comportamento hidráulico de um perfil de solo tropical e não saturado de
Aparecida de Goiânia-GO é apresentado nesta dissertação. O principal objetivo desta pesquisa
foi contribuir para o entendimento das propriedades hidráulicas do solo, com especial ênfase
na curva característica do solo e na sua histerese. O trabalho teve seu enfoque dividido em
duas partes: caracterização física, química e mineralógica do perfil; e comportamento
hidráulico do solo na condição não saturada. A partir da caracterização do solo, verificou-se
que o perfil estudado se divide em dois extratos, um superior de 1,50 m de material
transportado e um inferior residual jovem. Os resultados dos ensaios de granulometria
mostraram que as várias combinações de preparação (i.e., com ou sem secagem prévia,
desagregação química e desagregação física), produzem curvas granulométricas distintas.
Variados graus de desagregação podem ser atingidos, sendo estes dependentes do grau de
estabilidade das agregações do solo. Obteve-se uma boa correspondência entre a
granulometria convencional e aquela utilizando o granulômetro a laser, para condições de
desagregação supostamente equivalentes. A curva característica foi determinada tanto para o
material natural, quanto para o solo reconstituído por adensamento a partir do estado de lama.
Desta forma, procurou-se verificar o papel da estrutura no comportamento hidráulico do solo.
As curvas características foram obtidas em trajetórias de secagem, molhagem, e mistas, tanto
em termos de sucção matricial, quando de sucção total. Observou-se que o solo natural possui
curvas características distintas do solo reconstituído. A desestruturação do solo reconstituído
resulta em um maior valor de entrada de ar e uma curva característica unimodal, mesmo
quando o material natural apresenta curva bimodal. Pode-se concluir que a distribuição de
poros do material natural é afetada pela estruturação do solo. O procedimento de
umedecimento e secagem utilizado com o método do papel filtro resultou em algumas curvas
características com ausência de histerese. O estudo da distribuição da umidade ao longo da
altura dos corpos de prova revelou que não se obteve umidades homogêneas, mesmo após os
14 dias, adotados como período para equilíbrio do potencial da água do solo. Pôde-se concluir
que é exatamente a existência da histerese, aliada a um umedecimento ou secagem a partir da
face dos corpos de prova que não são suficientemente lentos, que resultam na não
homogeneidade de umidade.
|
69 |
Aplicação do Modelo de Preisach em Ímãs Nanocristalinos / Application of Preisach model in nanocrystalline magnetsCornejo, Daniel Reinaldo 28 May 1998 (has links)
Estudamos propriedades magnéticas de ligas nano cristalinas de Sm-F e-Co. As ligas foram preparadas por mecano-síntese e posterior tratamento térmico. Como resultado, obtivemos ímãs nanocristalinos de Sm18 (Fe,Co)82 , com Sm(Fe,Co)7 como fase principal. As ligas apresentaram excelentes propriedades magnéticas: remanências relativas Mn/ Ms ~ 0.6 e coercividades na faixa 5-20 kOe, dependendo do teor de Fe nos materiais. Interações magnéticas nas ligas foram estudadas com base nos gráficos ele Henkel. Interpretamos, nestes gráficos, de maneira consistente a influência elas interações e dos estados desmagnetizados. / We studied the magnetic properties of nanocrystalline Sm-Fe-Co alloys. These alloys were prepared by mechanical alloying and subsequent annealing. We obtained nanocrystalline rnagnets of composition Sm18 (Fe, Co )82 , for which the main hard magnetic phase is Sm(Fe, Co)82. The alloys showed excellent magnetic properties: relative remanence Mn/ Ms :2; 0.6 and coercive fields ranging from 5 to 20 k0e, depending upon the amount of Fe present. Henkel plots were used in order to study magnetic interactions in these alloys. The influence of the interactions and the demagnetized state on the Henkel plots was also studied.
|
70 |
Projeto e implementação de sistema eletrônico para atenuação de não linearidades dos atuadores piezoelétricos do interferômetro de Fabry-Pérot do espectrômetro astronômico BTFI. / Design and realization of an electronic charge control circuit to attenuate the nonlinearities of the high resolution Fabry-Pérot interferometer\'s amplified piezoelectric actuators.Marchiori, Victor Atilio 23 October 2014 (has links)
Este trabalho apresenta o projeto de pesquisa desenvolvido para a obtenção do título de Mestre em Engenharia Elétrica, na área de concentração de engenharia de sistemas, da Escola Politécnica da Universidade de São Paulo. O principal objetivo deste trabalho foi o desenvolvimento de um sistema de acionamento (driver) para os atuadores piezoelétricos do interferômetro de Fabry-Pérot do espectrômetro BTFI (Brazilian Tunable Filter Imager), um instrumento visitante do telescópio SOAR (Southern Astrophysical Research Telescope), no Chile. O Fabry-Pérot é um instrumento óptico composto de duas superfícies paralelas altamente reflexivas (espelhos), cuja distância é controlada por um sistema de nanoposicionamento composto de três atuadores piezoelétricos (piezos) do tipo APA® (Amplified Piezoelectric Actuators) e um sistema de medida capacitivo. O principal requisito técnico de desempenho do sistema de nanoposicionamento do Fabry-Pérot é tal que o ruído de posicionamento dos espelhos deve ser limitado a 3 . No entanto, os fenômenos não lineares de histerese e escorregamento (creep) dos piezos limitam a precisão de posicionamento do sistema de controle, razão pela qual foi desenvolvido um sistema de acionamento por carga e tensão para os piezos, com o intuito de atenuar suas não linearidades e, consequentemente, melhorar o desempenho do sistema de controle em malha fechada, em termos de ruído de posicionamento. A primeira etapa deste trabalho consistiu da caracterização do modelo e da instrumentação do sistema de nanoposicionamento do Fabry-Pérot, composto de sensores capacitivos, conversores de sinal, atuadores piezoelétricos e sistema de aquisição de dados. Após a caracterização dos componentes do sistema, sua especificação técnica de desempenho de 3 foi traduzida em requisitos de engenharia para o projeto do sistema eletrônico de acionamento dos piezos por carga e tensão, notadamente em termos de ruído, tempo de resposta, banda de resposta em frequência, ganho, corrente e tensão elétricas e dissipação de potência. Uma vez concluído o projeto do driver, um protótipo foi implementado e testado com o sistema real, a fim de se verificar experimentalmente a atenuação dos efeitos não lineares. Finalmente, foram realizados alguns experimentos com o driver e o sistema de nanoposicionamento em malha fechada, controlado por um compensador PI, a fim de se verificar a influência da atenuação das não linearidades dos piezos nesta configuração. Após a análise dos resultados experimentais obtidos, verificou-se que o ruído de posicionamento do sistema, em malha fechada, é significativamente menor quando os fenômenos não linearidades dos piezos são atenuados. / This work represents the research project to obtain the degree of Master of Sciences in Electrical Engineering, specializing in Systems Engineering, at the Escola Politécnica da Universidade de São Paulo, in São Paulo, Brazil. The main objective of this project was to design an electronic power driver for the piezoelectric actuators of the Fabry-Pérot interferometer of the BTFI spectrometer, a visitor instrument of the SOAR telescope, in Chile. Fabry-Pérot is an optical instrument composed by two high reflexive parallel surfaces (mirrors), which distance is controlled by a nanopositioning system composed by three piezoelectric actuators (piezos) of the class APA® (Amplified Piezoelectric Actuators) and a capacitive measurement system. The main performance specification of the Fabry-Pérots nanopositioning system is such that the positioning noise must be limited to 3 . However, the nonlinear behaviors (hysteresis and creep) of the piezos limit the positioning precision of the control system, for which reason a charge and voltage actuation system was developed for the piezos, in order to mitigate its nonlinearities and, consequently, improve the performance of the control system in closed loop, in terms of positioning noise. The first step in this work consisted on the characterization of the Fabry-Pérot nanopositioning systems model and instrumentation, which are composed by capacitive sensors, signal converters, piezoelectric actuators and a data acquisition board. After the characterization of the components of the nanopositioning system, the 3 specification was interpreted to low level engineering requirements for the design of the charge and voltage driver, especially in terms of noise, response time, frequency bandwidth, gain, electrical current, voltage and power dissipation. Once concluded the design of the driver, a prototype was implemented and tested in the real system, in order to verify the attenuation of the nonlinear effects. Finally, some experiments with the driver and the nanopositioning system were performed in closed loop, controlled by a PI compensator, in order to verify the influence of the attenuation of the nonlinearities of the piezos in such configuration. The analysis of the obtained experiment results showed that the nanopositioning systems noise, in closed loop, is significantly reduced when the nonlinear effects of the pizeos are attenuated.
|
Page generated in 0.0889 seconds