The thesis deals with the high-temperature embrittlement of 14%Cr ODS ferritic steel in liquid lead environment. The 14%Cr ferritic ODS steel ODM401 manufactured by powder metallurgy technology was used as an experimental material. The effect of the long-term annealing, surface corrosion attack in the melt Pb and Pb-Bi on the microstructure and mechanical properties was described. The subsequent microstructural changes were evaluated by means of scanning electron microscopy and transmission electron microscopy The mechanical behaviour of the experimental material was proven by means of microhardness test, impact test and static tensile test. The fractographical evaluation of fracture surfaces were performed on all samples. The surface attack and outstanding microstructural ganges were found after the long-time exposition of the steel in Pb/Pb-Bi melts at temperature 550°C/1000h and 500°C/1000h respectively. The embrittlement of the steel after exposition in Pb/Pb-Bi melts was comparable to the embrittlement after high-temperature annealing of the steel at temperature 650°C/1000h.

No / The shear viscosity of polymethylmethacrylate (PMMA) melt is particularly investigated by using a twin-bore capillary rheometer at four temperatures of 210, 225, 240, and 255 degrees C with different capillary dies. Experimental results show that the geometrical dependence of shear viscosity is significantly dependent on melt pressure as well as melt temperature. The measured shear viscosity increases with the decrease of die diameter at lower temperatures (210 and 225 degrees C) but decreases with the decrease of die diameter at higher temperatures (240 and 255 degrees C). Based on the deviation of shear viscosity curves and Mooney method, negative slip velocity is obtained at low temperatures and positive slip velocity is obtained at high temperatures, respectively. Geometrical dependence and pressure sensitivity of shear viscosity as well as temperature effect are emphasized for this viscosity deviation. Moreover, shear viscosity curve at 210 degrees C deviates from the power law model above a critical pressure and then becomes less thinning. Mechanisms of the negative slip velocity at low temperatures are explored through Doolittle viscosity model and Barus equation, in which the pressure drop is used to obtain the pressure coefficient by curve fitting. Dependence of pressure coefficient on melt temperature suggests that the pressure sensitivity of shear viscosity is significantly affected by temperature. Geometrical dependence of shear viscosity can be somewhat weakened by increasing melt temperature. (c) 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 130: 3384-3394, 2013

No description available.

Trois systèmes ternaires (SAS, BAS et ZAS) ont été étudiés dans le cadre de la thèse. Les principaux objectifs étaient l’élaboration et la caractérisation de verres aluminosilicatés de Sr, Ba et Zn peu étudiés auparavant. Une étude systématique a été réalisée sur des aluminosilicates vitreux et dans certains cas sur des aluminosilicates fondus avec différents rapports MO/Al₂O₃ (M = Sr, Ba, Zn) et SiO₂/Al₂O₃. Les compositions étudiées couvrent une partie significative des diagrammes ternaires (des silicates aux verres peralumineux, des compositions pauvres en silice à celles riches en silice). Cela a permis d'accroître nos connaissances sur les domaines de vitrification de ces systèmes. Afin d’obtenir des informations sur la structure et les propriétés macroscopiques des verres SAS, BAS et ZAS, une approche multi-technique a été mise en place. Une telle approche permet d’avoir une vue d’ensemble sur les systèmes étudiés et de trouver des origines nano- à microscopiques aux propriétés macroscopiques. La spectroscopie de résonance magnétique nucléaire, la diffractométrie de neutrons et la spectroscopie Raman ont été utilisées au cours de la thèse afin de sonder l'échelle à courte et à moyenne distance. Les propriétés macroscopiques mesurées ont été : la densité, la viscosité et la température de transition vitreuse. Les données issues de cette thèse permettent une meilleure compréhension des changements de structures et des propriétés macroscopiques des verres aluminosilicatés produits par les variations de MO/Al₂O₃ ou SiO₂/Al₂O₃, ou par la nature des cations non-formateurs de réseau. / Three ternary systems (SAS, BAS and ZAS) have been investigated within the framework of the PhD thesis. The main goals were the elaboration and characterization of previously poorly studied Sr, Ba and Zn aluminosilicate glasses. A systematic study has been carried out on glasses and in some cases on melts with various MO/Al₂O₃ (M = Sr, Ba, Zn) and SiO₂/Al₂O₃ ratios. The compositions studied cover a significant part of the ternary diagrams (from silicates to peraluminous glasses, from silica-poor to silica-rich compositions). This allowed expanding our knowledge of the vitrification domains in these systems. In order to obtain information on the structure and macroscopic properties of SAS, BAS and ZAS glasses, a multi-technique approach has been implemented. Such approach allows having a broad view on the systems and finding nano- to microscopic origins of macroscopic properties. The techniques used during the thesis probe short- (NMR, ND) to medium-range (Raman) scale and among the properties studied were density, viscosity and glass transition temperature. The data resulting from this thesis provides a better understanding of the changes in the structure and macroscopic properties of the aluminosilicate glasses produced by variations in MO/Al₂O₃ or SiO₂/Al₂O₃, or by the nature of non-network forming cation.

Nous avons étudié des magmas ferrifères silicatés magnésiens à la pression du manteau terrestre en utilisant la dynamique moléculaire (First Principles Molecular Dynamics). Les résultats de l’équation d’état que nous avons obtenus à partir de nos simulations ont été utilisés pour créer un modèle chimique et minéralogique pour les zones de très basse vitesse sismique (ULVZ, anomalies régionales dans le manteau proche de la limite noyau-manteau). De plus, nous avons étudié le comportement du Ni, du Co et du Fe dans ces magmas et établi la dépendance du spin en fonction de la concentration, de la pression, de la température et du degré de polymérisation du magma silicaté. Nous avons montré qu’une baisse du spin moyen peut être corrélée au changement de pente (kink) observé précédemment pour les coefficients de partage du Ni et du Co. Nous avons analysé la structure du magma pour toutes les compositions étudiées en fonction de la pression. Nos résultats donnent un nouvel aperçu de la coordination des éléments majeurs et traces dans les magmas silicatés de différents degrés de polymérisation. Nous interprétons l’anomalie de coordination Ni-O en fonction de la pression comme un changement d’état de spin. L’effet de la polymérisation du magma silicaté sur les coefficients de partage du Co, du Ni et du W entre le métal et le magma silicaté a été étudié par expériences multi-enclumes en conditions isobares et isothermes. Nous avons réalisé des simulations FPMD de magmas à des degrés de polymérisation similaires aux expériences afin d’expliquer le caractère de plus en plus lithophile du W lorsque le degré de polymérisation du magma silicaté diminue. Nous proposons une explication structurale pour expliquer l’affinité décroissante apparente du W dans les magmas silicatés dépolymérisés. / We explore Fe-bearing Mg-silicate melts through the pressure regime of the Earth’s mantle using First Principles Molecular Dynamics (FPMD). The equation of state results we obtained from our simulations are used to create a chemical and mineralogical model for Ultra-Low Velocity Zones (anomalous region on the mantle side of the core-mantle boundary). Furthermore we study the behaviour of Ni, Co, and Fe in these melts, and asses their spin-crossover dependencies on their concentration, pressure, temperature, and the degree of polymerization of the silicate melts. We show that a decrease in the average spin can be correlated with the previously observed kink in the partitioning coefficient of Ni and Co. We investigate the melt structure of all the compositions studied as a function of pressure. Our results provide new insight into the coordination of major and trace elements in silicate melts with different degrees of polymerization. We interpret the anomalous Ni-O coordination trend with pressure as the result of the spin state change. The effect of silicate melt polymerization on the partitioning of Co, Ni, and W between a metal and silicate melt, is investigated at isobaric and isothermic conditions using multi-anvil experiments. We have performed FPMD simulations of melts with similar degrees of polymerization as the experiments in order to explain the increasing lithophile character of W with the decrease in polymerization of the silicate melt. We propose a structural explanation for tungsten’s apparent increased affinity for depolymerized silicate melts.

À l'approche de la transition vitreuse les fondus de polymères montrent une augmentation importante de la viscosité de plusieurs ordres de grandeur. Le but de cette étude est d'acquérir une compréhension plus profonde des propriétés viscoélastiques des fondus de polymères vitrifiables. Les polymères sont modélisés comme des chaînes flexibles en utilisant un modèle de bille-ressort. Les propriétés dynamiques sont analysées dans le cadre de la théorie de couplage de mode idéale. Nous constatons que la température critique de couplage de mode varie avec l'inverse de la longueur de chaîne. En étudiant la fonction de relaxation de cisaillement, nous constatons que les processus de relaxation polymériques, ne sont pas modifiés, mais décalés vers des temps plus importants en approchant la transition vitreuse. / Polymer melts show a remarkable increase of their viscosity by many orders of magnitude on approaching the glass transition. The aim of this study is to gain a deeper insight into the viscoelastic properties of glass forming polymer melts. The polymers are modeled as flexible chains using a bead-spring model. The dynamic properties are analyzed in the framework of the ideal mode-coupling theory. We find that the critical temperature of the ideal mode-coupling theory scales with the reciprocal chain length. By studying the shear relaxation function we find that the polymer relaxation processes are not altered but shifted to later times in the approach of the glass transition.

Die vorliegende Arbeit befasst sich mit dem Fluoreszenzverhalten, speziell der Fluoreszenzlebensdauer, von BODIPY-Farbstoffen in Polymerlösungsmittelgemischen mit unterschiedlicher Polymerkonzentration sowie in Polymerfilmen bei unterschiedlichen Temperaturen. Dazu werden zunächst die Synthesen von vier verschiedenen BODIPY-Fluorophoren mit einem Phenylsubstituent in meso-Position aufgezeigt. Dahingehend wurde eine Synthesestrategie entwickelt, um eine einzelne Polypropylenkette an diese Farbstoffsysteme anzubinden. Dabei soll aufgezeigt werden, dass die Länge des Substituenten am Phenylsubstituenten am chromophoren Kern maßgeblich das Fluoreszenzverhalten der Sonde beeinflusst. BODIPY-Farbstoffe mit makromolekularen Substituenten zeigen im Vergleich zu Derivaten mit kürzeren Substituenten eine deutlich größere Fluoreszenzlebensdauer und eine nicht so stark ausgeprägte Temperaturabhängigkeit. Mehrere Zeitkomponenten der Fluoreszenzlebensdauer der Fluorophore in reinem Polypropylen bzw. deren Mehrkomponentensystemen (Polyethylenpropylen Copolymer oder Kraton) im Vergleich zu reinen Lösungsmitteln (Toluol oder Dodecen) deuten dabei auf lokale Heterogenitäten im Material hin. Außerdem wird der Einfluss der Viskosität auf die Fluoreszenzlebensdauer in Polymer/Lösungsmittelgemischen mit unterschiedlicher Polymerkonzentration untersucht und die Rolle des Wasserstoffbrückennetzwerkes zwischen den Polymer- und Lösungsmittelmolekülen diskutiert.

Alkali metal chloride melts are used to refine refractory metals and as a heat carrier for promising nuclear reactors. The oxygen content is a critical parameter for such systems. It determines technological process and the quality of obtained products. The work is devoted to the development of methods for the determination of oxygen in chloride melts. HORIBA EMGA-620W/C gas analyzer was used. The paper presents information on the choice of methods for determining oxygen in various oxygen-containing compounds of tungsten and molybdenum. An inert chamber has been developed and combined with a gas analyzer. This allowed to determine low oxygen contents in volatile matrices with high affinity for oxygen. / Системы хлоридных расплавов щелочных металлов применяются для рафинирования ряда тугоплавких металлов и в качестве теплоносителя в перспективных реакторах нового типа. Содержание кислорода в таких системах является критическим параметром, обуславливающим правильный ход технологического процесса и качество получаемой продукции. Работа посвящена разработки методики определения кислорода в хлоридных расплавах. Для измерений использовали газоанализатор HORIBA EMGA-620W/C. В работе представлены сведения о выборе способов определения кислорода в различных кислородсодержащих соединениях вольфрама и молибдена. Разработана и совмещена с газоанализатором инертная камера, позволяющая проводить определения низких содержаний кислорода в относительно летучих матрицах, в том числе с макрокомпонентами, имеющими высокое сродство к кислороду. Выбраны оптимальные условия проведения измерений.

No description available.

In this thesis we design and develop algorithms for predicting the rheological behavior of polymer melts based on the results of detailed atomistic simulations and guided by theories of the Dynamics of Polymers and fundamental Principles of Science of the Non-Equilibrium Thermodynamics. More specifically: 1) We propose a new rheological constitutive model for the time evolution of the tensor conformation tensor C of chains in a polymer melt (and hence the stress tensor τ) using the generalized bracket formalism of Beris and Edwards. The new constitutive model includes terms that describe a whole range of phenomena and are successfully used to describe the rheological properties of commercial polyethylene resins. 2) We developed a new methodology that allows direct connection of the results of atomistic simulations with molecular reptation theory for entangled polymers. The final result of the methodology is the calculation of the function ψ(s,t) which expresses the probability that the segment s along the contour of the primitive path remain in the original tube after time t. 3) We extended the Rouse theory for systems without polymer chain ends, as the polymer rings. While there have been previous theoretical work, a comprehensive analysis of the Rouse model of cyclic polymers was still lacking; here we develop the theory in its entirety. / Στα πλαίσια της παρούσας διατριβής σχεδιάσαμε και αναπτύξαμε αλγορίθμους πρόβλεψης της ρεολογικής συμπεριφοράς πολυμερικών τηγμάτων βασιζόμενοι στα αποτελέσματα λεπτομερών ατομιστικών προσομοιώσεων, καθοδηγούμενοι όμως από Θεωρίες της Δυναμικής των Πολυμερών αλλά και από θεμελιώδεις αρχές της Επιστήμης της Θερμοδυναμικής Εκτός Ισορροπίας. Πιο συγκεκριμένα: 1) Προτείνουμε αρχικά ένα νέο ρεολογικό καταστατικό μοντέλο για τη χρονική εξέλιξη του τανυστή διαμορφώσεων C των αλυσίδων σε ένα πολυμερικό τήγμα (και κατ’ επέκταση για τον τανυστή των τάσεων τ) κάνοντας χρήση του φορμαλισμού των γενικευμένων αγκυλών των Beris και Edwards. Το νέο καταστατικό μοντέλο περιλαμβάνει όρους που περιγράφουν ένα ολόκληρο φάσμα φαινομένων και χρησιμοποιήθηκε με επιτυχία για την περιγραφή των ρεολογικών ιδιοτήτων εμπορικών ρητινών πολυαιθυλενίου. 2) Αναπτύξαμε μια καινούργια μεθοδολογία που επιτρέπει την άμεση σύνδεση των αποτελεσμάτων των ατομιστικών προσομοιώσεων με τη μοριακή θεωρία του ερπυσμού για διαπλεγμένα πολυμερή. Το τελικό αποτέλεσμα της μεθοδολογίας είναι ο υπολογισμός της συνάρτησης ψ(s,t) που εκφράζει την πιθανότητα το σημείο s κατά μήκος του περιγράμματος του πρωτογενούς δρόμου των αλυσίδων να παραμένει στον αρχικό σωλήνα μετά από χρόνο t. Επεκτείναμε τη θεωρία Rouse και για συστήματα πολυμερικών αλυσίδων δίχως άκρα, όπως αυτά των πολυμερικών δακτυλίων. Παρότι στίγματα της θεωρίας είχαν παρουσιαστεί και σε προηγούμενες εργασίες από άλλους ερευνητές, στην παρούσα διατριβή αναπτύξαμε τη θεωρία στην ολότητά της.