This study was aimed at designing a cell carrier from an intelligent polymer to achieve loading of mechanical stress for the purpose of improving the tissue engineering capability in vitro. Ethyleneglycoldimethacrylate (EGDMA) crosslinked poly(Nisopropylacrylamide) (pNIPAM) films were prepared by radical polymerization with ultraviolet light (UV) in the presence of photoinitiator 2,2&#039 / -azoisobutyronitrile (AIBN) in isopropanol/water (1:1). Patterns were formed on the surface of the polymers by using silicon wafers with microridges (2 &amp / #956 / m) and grooves (10 &amp / #956 / m) that were prepared by photolithography technique as the template. The surfaces of the films were also modified by adsorption of ELP-RGD6 polypeptide. Bone marrow stem cells (BMSCs) isolated from 6 week old Sprague-Dawley rats were seeded onto the pNIPAM films with different surface topography and chemistry and cultured under static and dynamic conditions. Dynamic conditions were generated by cyclic temperature changes (15 min at 29&deg / C, 30 min at 37&deg / C) for 10 times a day during 5 days starting on the second day post-cell seeding. ELP-RGD6 on the films enhanced initial cell attachment but had no effect on proliferation in long term culturing. However, for the dynamic culturing, ELP was crucial for both retaining cells attached on the surface when the surface became hydrophilic and resulted in weakened cell attachment, and for better communication between cell and material which enhanced the ability of pNIPAM films to transfer mechanical stress on the cells. Dynamic conditions improved cell proliferation but decreased differentiation. Presence of the patterns also influenced the differentiation but did not affected proliferation.

With the gradual advance of the state-of-the-art VLSI manufacturing technology into the sub-45nm regime, engineering a reliable, high performance VLSI chip with economically attractive yield in accordance with Moore's law of scaling and integration has become extremely difficult. Some of the most serious challenges that make this task difficult are: a) the delay of a transistor is strongly dependent on process induced mechanical stress around it, b) the reliability of devices is affected by several aging mechanisms like Negative Bias Temperature Instability (NBTI), hot carrier injection (HCI), etc and c) the delay and reliability of any device are strongly related to lithographically drawn geometry of various features on wafer. These three challenges are the main focus of this dissertation. High performance fabrication processes routinely use embedded silicon-germanium (eSiGe) technology that imparts compressive mechanical stress to PMOS devices. In this work, cell level timing models considering flexibility to modulate active area to change mechanical stress, were proposed and exploited to perform timing optimization during circuit placement phase. Analysis of key physical synthesis optimization steps such as gate sizing and repeater insertion was done to understand and exploit mechanical stress to significantly improve delay of interconnect and device dominated circuits. Regarding circuit reliability, the proposed work is focused on reducing the clock skew degradation due to NBTI effect specially due to the use of clock gating technique for achieving low power operation. In addition, we also target the detrimental impact of burn-in testing on NBTI. The problem is identified and a runtime technique to reduce clock skew increase was proposed. For designs with predictable clock gating activities, a zero overhead design time technique was proposed to reduce clock skew increase over time. The concept of using minimum degradation input vector during static burn-in testing is proposed to reduce the impact of burn-in testing on parametric yield. Delay and reliability strongly depend on dimension of various features on the wafer such as gate oxide thickness, channel length and contact position. Increased variability of these dimensions can severely restrict ability to analyze or optimize a design considering mechanical stress and circuit reliability. One key technique to control physical variability is to move towards regular fabrics. However, to make implementation on regular fabrics attractive, high quality physical design tools need to be developed. This dissertation proposes a new circuit placement algorithm to place a design on a structured ASIC platform with strict site and clock constraints and excellent overall wirelength. An algorithm for reducing the clock and leakage power dissipation of a structured ASIC by reducing spine usage is then proposed to allow lower power dissipation of designs implemented using structured ASICs. / text

Submitted by FERNANDA DE OLIVEIRA ABU-IZZE null (fefeizze@hotmail.com) on 2018-03-12T22:56:56Z No. of bitstreams: 1 12.01.18 biblio correção final.pdf: 10328694 bytes, checksum: 640b2d0c989c903e0216bd6a154400e4 (MD5) / Approved for entry into archive by Silvana Alvarez null (silvana@ict.unesp.br) on 2018-03-20T20:51:39Z (GMT) No. of bitstreams: 1 abu_izze_fo_me_sjc.pdf: 10328694 bytes, checksum: 640b2d0c989c903e0216bd6a154400e4 (MD5) / Made available in DSpace on 2018-03-20T20:51:39Z (GMT). No. of bitstreams: 1 abu_izze_fo_me_sjc.pdf: 10328694 bytes, checksum: 640b2d0c989c903e0216bd6a154400e4 (MD5) Previous issue date: 2017-12-01 / A fim de investigar a vida em fadiga, modos de falha e distribuição de tensões de restaurações ultrafinas parciais, tipo tabletop, em diferentes cerâmicas, sessenta preparos padronizados foram confeccionados em resina epóxi G10 e foram cimentadas adesivamente restaurações cerâmicas de silicato de lítio reforçado com zircônia (ZLS, Vita Suprinity- Vita Zahnfabrik), ou restaurações de cerâmica híbrida (PIC, Vita Enamic- Vita Zahnfabrik), em 0,5 ou 1 mm de espessura. O mesmo protocolo de ciclagem foi aplicado para todos os espécimes, que consistiu em 5.000 ciclos a 200 N, seguidos de 450 N ciclos até a fratura dos espécimes ou a suspensão do teste após 1,5 x 106 ciclos. A carga axial foi realizada com uma freqüência de 4 Hz no equipamento Biocycle V2 (Biopdi, São Carlos, SP), com amostras imersas em água. A presença de falhas e/ou fraturas foi verificada a cada 2,5 x 105 ciclos e a análise de sobrevivência foi realizada com o número de ciclos em que cada espécime falhou. Os espécimes foram avaliados usando estereomicroscópio e microscopia eletrônica de varredura (MEV). Após a tabulação de dados, foram realizados Kaplan-Meier e Mantel-Cox (Teste Log Rank), seguindo de comparação múltipla aos pares, todos com nível de significância de 5% e análise de Weibull. Através da análise tridimensional de elementos finitos, a distribuição de tensões máximas principais (TMP) nas tabletop oclusais posteriores foram avaliados comparando diferentes tipos de substrato (G10, esmalte/dentina, esmalte), espessuras e materiais cerâmicos. As restaurações de silicato de lítio reforçadas com zircônia com 0,5 mm de espessura (ZLS.5) apresentaram menor resistência à fadiga em comparação com restaurações cerâmicas híbridas de 1,0mm (PIC1), e ambas foram similares a outras restaurações (PIC.5 e ZLS1); X2 = 11,2; df = 3; p = 0,0107 <0,05). Os grupos ZLS apresentaram defeitos aleatórios que culminaram com a fratura, ao passo que os grupos PIC apresentaram defeitos que aumentaram com a fadiga mecânica após algum tempo sob ciclagem. As imagens do estereomicroscópio mostram falhas radiais observadas devido à translucidez do material, não houve danos causados pelo aplicador de carga. A distribuição de TMP foi semelhante para os diferentes tipos de substrato, mas o maior módulo de elasticidade mostrou uma concentração de tensão ligeiramente menor. É favorável o uso de PIC em espessura delgada, com resistência à fadiga semelhante à restaurações de ZLS mais espessas. / To investigate the fatigue life, failure modes and stress distribution of partial ultrafine restorations for posterior teeth in different ceramics, sixty standard tabletop preparations in epoxy resin G10 received lithium silicate based zirconia reinforced (ZLS, Vita Suprinity- Vita Zahnfabrik), or hybrid ceramic (PIC, Vita Enamic- Vita Zahnfabrik), restorations in .5 or 1 mm thickness bonded using resin cement. The same cycling protocol was applied for all specimens that consisted of 5.000 cycles at 200 N followed by 450 N cycles until the specimens’ fracture or the suspension of the test after 1.5 x 106 cycles. Axial load was carried out with a 4 Hz frequency in Biocycle V2 equipment (Biopdi, São Carlos, SP), with samples immersed in water. Presence of cracks and/or fractures was checked with every 2,5 x 105 cycles and the survival analysis was performed using the number of cycles in which each specimen failed. All specimens were evaluated using stereomicroscope and scanning electron microscopy (SEM). After data tabulation, Kaplan-Meier and Mantel-Cox (Log Rank test) analysis were performed, followed by multiple pairwise comparison, all with a significance level of 5%, and Weibull analysis. Through tridimensional finite element analysis, stresses distribution and maximum principal stresses in the posterior occlusal veneers were evaluated comparing different types of substrate (G10, enamel/dentin, enamel), thicknesses and ceramic materials. Zirconium-reinforced lithium silicate restorations with 0.5 mm thickness (ZLS.5) showed lower fatigue strength compared to 1.0 mm hybrid ceramic restorations (PIC1), and both were similar to other restorations (PIC.5 and ZLS1) (Log-Rank test, X2 = 11.2; df = 3; p = 0.0107<0.05). ZLS groups presented random defects that culminated with the fracture, whereas PIC groups presented defects that increased with the mechanical fatigue after some time under cycling. Stereomicroscope images show radial cracks observed due to the translucency of the material, there was no damage caused by applicator. TMP distribution was similar for the different substrate types, but the highest modulus of elasticity showed slightly lower stress concentration. PIC is favorable to be used in thin thickness with similar fatigue strength to thicker ZLS restorations.

Orientador: Otávio Rizzi Coelho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Ciências Médicas / Made available in DSpace on 2018-08-17T21:29:46Z (GMT). No. of bitstreams: 1 Tornatore_ThaisFranchini_D.pdf: 5344920 bytes, checksum: 13bb7f4ae7264a0aca117131579c9b8e (MD5) Previous issue date: 2011 / Resumo: Estudamos o gene da FAK (focal adhesion kinase) na mitocondriogênese cardíaca induzida por estresse mecânico. O estresse prolongado (2-12 hs) de miócitos do ventrículo esquerdo de ratos neonatos(NRVM) aumentou a expressão do regulador transcricional mitocondrial PGC-1? (peroxisome proliferator activated receptor coactivator-1), NRF-1 (nuclear respiratory factor) e o Tfam (mitochondrial transcription factor A). A ativação da cascata transcricional mitocondrial em cardiomiócitos estirados foi acompanhada pelo aumento da mitocondriogênese (aumento da densidade mitocondrial e número de cópias do DNA - mtDNA) e hipertrofia(tamanho da célula e transcrição do ANP). Estresse mecânico também aumentou a fosforilação da FAK, a localização nuclear e associação com PGC1-?. FAK C-terminal Recombinante, mas não a N-terminal ou domínio kinase, precipitaram PGC-1? em extratos nucleares de NRVMs. Além disso, a inibição da expressão da FAK por RNA de interferência suprimiu a hiper regulação do PGC-1? e NRF-1, e atenuou o aumento da mitocondriogênese e hipertrofia em cardiomiócitos. Ao mesmo tempo, a inibição da FAK reduziu os níveis de ATP em cardiomiócitos estirados. Estudos complementares em ventrículos esquerdo de camundongos adultos revelaram aumento da expressão de PGC-1?, NRF-1 e mtDNA em resposta à sobrecarga pressórica. In vivo o silenciamento da FAK atenuou a hiper regulação do PGC-1?, NRF-1, mtDNA e a hipertrofia do ventrículo esquerdo induzida por sobrecarga pressórica. A ativação da sinalização da FAK parece ter importante relação no aumento da mitocondriogênese paralelamente à resposta do aumento hipertrófico relacionado ao estresse mecânico dos cardiomiócitos / Abstract: We studied the implication of FAK (focal adhesion kinase) in cardiac mitochondriogenesis induced by mechanical stress. Prolonged stretching (2-12 hs) of neonatal rat ventricular myocytes (NRVM) enhanced the expression of mitochondria transcriptional regulator PGC-1? (peroxisome proliferator activated receptor coactivator-1), NRF-1 (nuclear respiratory factor) and transcripts of Tfam (mitochondrial transcription factor A). The activation of the mitochondria transcriptional cascade in stretched NRVM was accompanied by enhanced mitochondriogenesis (increases in mitochondrial density and DNA copy number - mtDNA) and hypertrophy (cell size and ANP transcripts). Cell stretching also enhanced FAK phosphorylation, nuclear localization and association with PGC1?. Recombinant FAK C-terminal, but not the N-terminal or kinase domain, precipitated PGC-1? from NRVM nuclear extracts. Moreover, depletion of FAK by RNA interference suppressed the upregulation of PGC-1? and NRF-1, and markedly attenuated the enhanced mitochondriogenesis and hypertrophy of stretched NRVMs. Concomitantly, FAK depletion induced a marked reduction of ATP levels of stretched NRVM. Complementary studies in adult mice left ventricle revealed enhanced expression of PGC-1?, NRF-1 and mtDNA in response to pressure overload. In vivo FAK silencing attenuated the upregulation of PGC-1?, NRF-1, mtDNA and left ventricular hypertrophy induced by pressure overload. Activation of FAK signaling seems to be important for conferring enhanced mitochondriogenesis coupled to the hypertrophying growth response to mechanical stress in cardiomyocytes / Doutorado / Ciencias Basicas / Doutor em Clínica Médica

Orientador: Francisco Maugeri Filho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia de Alimentos / Made available in DSpace on 2018-08-05T17:05:43Z (GMT). No. of bitstreams: 1 YepezSilva-Santisteban_BernardoOnagar_D.pdf: 1839103 bytes, checksum: 44dfdd6f4dc2a025d2bcdbcf149d2ef1 (MD5) Previous issue date: 2006 / Doutorado / Doutor em Engenharia de Alimentos

A importância das próteses provisórias no tratamento reabilitador oral é inquestionável. Os materiais utilizados para a execução destas restaurações, entretanto, são críticos com relação à resistência e à longevidade, principalmente quando estas são executadas em tratamentos prolongados e/ou em espaços desdentados extensos. A proposta deste trabalho foi determinar através de um ensaio de fadiga e de um teste de resistência à fratura, o efeito do tipo de reforço: fio de aço Ø 0,7 mm, fibra de poli(aramida) (Kevlar®, DuPont - USA) e fibra de vidro (Fibrante®, Ângelus -Brasil) e de duas extensões do pôntico (12,5 e 22,75 mm) sobre o comportamento mecânico de espécimes simulando próteses provisórias. Os grupos foram constituídos de 10 espécimes cada, incluindo um grupo CONTROLE, sem reforço. Os espécimes simulando próteses parciais fixas provisórias foram confeccionados em resina auto-polimerizável com auxílio de uma matriz de aço simulando preparos totais protéticos. As amostras foram submetidas a 10.000 ciclos de fadiga, com carga máxima de 100 N, imersas em água a 37ºC. Através da análise estatística dos resultados observou-se que durante o ensaio de fadiga: 1) quando a extensão do pôntico foi de 22,75 mm, o grupo CONTROLE exibiu uma maior deformação a partir de 500 ciclos. Não foram observadas diferenças quando a extensão do pôntico foi de 12,5 mm. Houve um aumento da deformação em função do número de ciclos para todos os grupos, principalmente para o grupo CONTROLE, de ambas as extensões de pôntico; 2) Somente espécimes do grupo CONTROLE com extensão do pôntico de 22,75 mm demonstraram fraturas à fadiga. E após o ensaio de fadiga, através de um teste de resistência à fratura: 1) Quando a extensão do pôntico foi de 12,5 mm todos os grupos reforçados apresentaram valores médios do limite de elasticidade, em N, significantemente maiores que os demonstrados pelo grupo CONTROLE. Para a extensão do pôntico de 22,75 mm os valores desse parâmetro apresentaram semelhança entre todos os grupos; 2) Em relação à carga máxima (resistência à fratura), quando a extensão do pôntico foi de 12,5 mm o grupo FIBRANTE exibiu o maior valor médio. Quando a extensão do pôntico foi de 22,75 mm, observou-se que o grupo KEVLAR apresentou valores semelhantes neste parâmetro ao grupo FIBRANTE. O grupo CONTROLE sempre apresentou os menores valores médios em ambas as extensões de pôntico. Em relação ao modo de fratura os grupos reforçados apresentaram fraturas mais favoráveis ao reparo, tendo sido do tipo parcial (coesiva da resina sem fratura ou separação do reforço). / Provisional restorations are essential components of oral rehabilitation treatment. The strength and durability features are, however, critical when long-term treatment is needed. This study investigates the mechanical alterations under and after cyclic fatigue in provisional partial fixed denture specimens. Two pontic distances (12.5 mm and 22.75 mm) and three types of reinforcements constituted the experimental groups with ten specimens each: a 0.7 mm of diameter wire; a roving poliaramid fiber Kevlar® and a roving fiberglass Fibrante® (Angelus®). The control group, also with ten samples, included not reinforced specimens. Specimens were fabricated and testing on metal dies. The samples were subjected to 10,000 fatigue cycles with a 100 N maximum load in a MTS 810 Universal Machine and before they were subjected to fracture resistance test in the same machine. Statistical analysis showed that, during the fatigue cycles: 1) All the samples exhibited an increased deflection, in mm, following the fatigue cycles, mainly the CONTROL group; 2) Only specimens of the CONTROL group exhibited fracture due to fatigue cycle. After the fatigue cycle, through the fracture resistance test: 1) All reinforced samples with the pontic distance of 12.5 mm exhibited higher figures in elastic limits than the CONTROL group, and increased the pontic distance to 22.75 mm the results of the elastic limits decreased statistically; 3) the FIBRANTE group with pontic distance of 12.5 mm exhibited the higher results for the resistance fracture. The CONTROL group specimens, with both pontic distances, exhibited the lowest values of this property; 4) It was observed that the reinforced FIBRANTE anda KEVLAR groups specimens fractures were more favorable, occurring, predominantly, in the Partial type.

No tratamento reabilitador oral as restaurações provisórias são de suma importância. A resistência e a longevidade dos materiais utilizados em sua execução são críticas, principalmente em tratamentos prolongados e em espaços desdentados extensos. O objetivo deste trabalho foi avaliar a resistência e o modo de fratura de espécimes que simularam uma prótese fixa de três elementos variando o comprimento do cantilever (7, 14 e 21mm), confeccionadas em resina acrílica poli(metilmetacrilato) (PMMA) autopolimerizável, com e sem reforço em seu interior, construídos sobre componentes para implantes. Os reforços utilizados foram: fibras de vidro (Fibrante® - Ângelus®, Londrina, PR, Brasil) e fibras de poli(aramida) (Kevlar® - Du Pont®, USA). Os grupos foram constituídos de 10 espécimes cada, incluindo um grupo controle, sem reforço. Os espécimes foram submetidos à carga compressiva até a fratura. A análise dos resultados (ANOVA, p < 0,05), para o teste de resistência, mostrou não haver diferença estatística entre os grupos com respeito ao tipo de reforço, sendo que houve diferença estatística significante no que respeita ao comprimento do cantilever. Quando o comprimento do cantilever foi de 7mm todos os grupos apresentaram os valores médios de resistência a fratura, em N, significativamente maiores que os apresentados pelos grupos com 14 e 21mm de comprimento. Em relação ao modo de fratura os grupos reforçados apresentaram fraturas mais favoráveis ao reparo, tendo sido do tipo Parcial. / In the oral rehabilitator treatment, the provisory restorations have extremely importance. The resistance and durability of materials used in the execution are critical, especially in extended treatments and in vast toothless spaces. The goal of this work was to demonstrate the resistance and the types of fracture of specimens that simulate a fixed prosthesis of three elements changing the extension of cantilever (7, 14 e 21mm), made of acrylic resin polymethylmethacrylate (PMMA) autopolymer, with and without reinforcement in its interior, built over implant components. The reinforcements used were: fiberglass (Fibrante® - Angelus®, Londrina, PR, Brazil) and poliaramid fiber (Kevlar® - Du Pont®, USA). The groups have 10 specimens each, including a group of control, without reinforcement. The specimens were submitted to a compressor charge until its fracture. The analysis of results (ANOVA, p < 0,05) for the test of resistance, showed that there is no statistic difference between the groups regarding the type of reinforcement; however, there is a significant statistic difference regarding the cantilever extension. When the extension of cantilever was 7mm, all groups showed medium values of resistance to fractures, in N, significant more than the showed by the groups with 14 and 21mm of extension. In relation with the types of fracture, the reinforcement groups show fractures more favorable to be repaired, even when they were partially fractured.

O comportamento mecânico das próteses parciais fixas implanto-suportadas são foco de vários estudos, onde o entendimento do processo de transmissão de forças mastigatórias e suas reações na estrutura óssea peri-implantar ainda não são totalmente compreendidos. Por isso, o objetivo deste trabalho foi verificar a deformação gerada na região peri-implantar de prótese parcial fixa mandibular. Para isto foi utilizado um modelo de poliuretano em forma de U simulando o osso mandibular com dois implantes hexágono externo de 3,75mm de diâmetro por 13mm de comprimento, nos quais foram fixados intermediários multi-unit. O trabalho apresentou dois grupos divididos de acordo com o tipo de liga das infraestruturas (CoCr ou PdAg) os quais foram submetidos a quatro situações de aplicação de carga. Foram aplicadas forças de 300N, nos pontos de referência pré-determinados na barra entre os implantes e na extremidade livre (5mm, 10mm e 15mm de cantilever). Foram realizadas leituras das deformações geradas na distal, lingual, mesial e vestibular de cada implante, com o uso de extensômetros lineares elétricos, as quais foram correlacionadas com a teoria de remodelação óssea proposta por Frost. Os resultados do estudo demonstraram que a deformação é influenciada pelo ponto de aplicação de carga e pelo módulo de elasticidade da liga da barra. A deformação é diretamente proporcional ao comprimento do cantilever, onde comprimentos maiores do que 10mm provocam tensões que superam a tensão máxima fisiológica proposta pela teoria de Frost. / The mechanical behavior of implant-supported prosthesis is focus of some studies, with the process of bite forces transmissions and its peri-implant bone reactions is not completely understood yet. Therefore, the aim of this study was to verify the deformation in peri-implant region of mandibular fixed partial prosthesis. A U shaped polyurethane model was used to simulated the mandibular bone with two external hexagon implants with 3.75mm of diameter an 13mm of length, provided with multi-unit abutments. Two groups were formed according to the type of alloy of the framework (CoCr or PdAg), which were submitted to four load conditions. Loads of 300N were applied, in the predetermined points on the framework between the implants and the cantilever (5mm, 10mm and 15mm distal to the terminal implant). Readings of the deformations generated on the distal, lingual, mesial and bucal aspects of each implant were obtained with the use of strain gages, which were correlated to the theory proposed by Frost on bone remodeling. The results of the study demonstrated that deformation is influenced by the point of load application and by the elastic modulus of the alloy of the framework. The deformation is directly proportional to the cantilever length. Lengths bigger than 10mm generate tensions that exceed the maximum effective strain proposed by Frost.

A adaptação passiva e estabilidade têm sido descritos como pré-requisitos importantes na escolha dos materiais e técnicas de confecção em prótese implantossuportada. A proposta deste trabalho foi estudar, com auxílio dos strain gauges, a deformação média gerada nos intermediários após a aplicação de carga axial em infraestruturas confeccionadas por três diferentes materiais. Além disso, através da microscopia confocal a laser, avaliar as medidas de comprimento, altura e angulação desses espécimes e mini pilares. Esses dados foram submetidos à análise estatística, a fim de encontrar possível correlação entre a deformação gerada e as medidas internas das infraestruturas com as externas dos intermediários em que foram parafusadas. Para essa investigação foi utilizado um modelo em poliuretano com dois implantes, hexágono externo, posicionados nas áreas dos dentes 43 e 45. A partir deste modelo, 12 infraestruturas de três elementos foram fabricadas e divididas em 3 grupos (n=4) de acordo com a técnica utilizada: (C) fundição convencional em Ni-Cr; (U) usinada em zircônia por CAD/CAM e (S) sinterizada a laser em Co-Cr pelo CAD/CAM. Durante a aplicação de carga axial, as tensões geradas foram registradas por extensômetros unidos aos intermediários, e avaliadas quantitativamente e qualitativamente. De maneira geral, houve um predomínio de áreas de compressão, sendo que as poucas áreas de tração apresentaram baixos valores. O grupo sinterizado a laser foi o único que apresentou forças compressivas para todos os sensores. Os grupos usinado e convencional apresentaram comportamento semelhante, diferindo apenas em uma região. Posteriormente, as infraestruturas e os intermediários foram submetidos à microscopia confocal para avaliação de ângulo, comprimento e altura de suas paredes internas (infraestruturas) e externas (intermediários), nas regiões correspondentes à localização dos strain gauges. Para a angulação, todos os grupos mostraram valores semelhantes entre si e maiores que os dos mini pilares. Quanto ao comprimento e altura, todos valores foram diferentes entre si. Em relação aos mini pilares, os valores foram maiores na altura e menores no comprimento. Estes resultados foram analisados pelo método estatístico de Pearson o que levou à conclusão que, para algumas regiões dos medidores de tensão, há correlação entre deformação e comprimento, e também, deformação e ângulo. Quanto maior o ângulo, e quanto menor for o comprimento, maior a deformação mostrada. / The passive adaptation and stability have been described as important prerequisites in the choice of materials and manufacturing techniques in implant-supported prosthesis. The aim of this work was to study, with the aid of strain gauges, the average deformation generated in the abutment, after application of axial load on frameworks made up of three different materials. Besides, through confocal laser microscopy, assess the length, height, and angle of these specimens, and abutment. These data were statistically analyzed in order to find possible correlation between the deformation generated, and the internal measures of the framework and the external measure of the abutments they were screwed on. For this research, a model made of polyurethane with two external hexagon implants, positioned in the areas of teeth 43 and 45 was used. From this model, 12 three-element frameworks were fabricated and divided into 3 groups (n = 4), according to the technique used: (C) conventional Ni-Cr casting; (U) machined zirconia CAD / CAM and (S) laser sintered Co-Cr by CAD / CAM. During application of axial load, the tensions generated were recorded by strain gauges attached to the abutments, and evaluated quantitatively and qualitatively. In general, there was a predominance of compression areas, and the few areas of traction showed low values. The laser sintered group was the only one with compressive forces for all sensors. The milled and conventional groups behaved similarly, differing only in a region. Subsequently, the framework and the abutment were analyzed by confocal microscopy for evaluation of angle, length and height of the inner (framework) and outer (abutment) walls in regions corresponding to the location of strain gauges. For the variable angle, all groups showed similar values among themselves and greater than the abutments. As for the variables length and height, all values were different. Regarding the abutments, the values were higher in height and smaller in length. These results were analyzed by Pearson statistical method, leading to the conclusion that, for some regions, there was correlation between deformation and length, and also deformation and angle. The higher the angle and the smaller the length, the greater the deformation shown.

Orientadores: Marcelo Ferraz Mesquita, Jessica Mie Ferreira Koyama Takahashi / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-23T00:57:52Z (GMT). No. of bitstreams: 1 Marques_IsabelladaSilvaVieira_M.pdf: 2460672 bytes, checksum: c23d88013ae75d0941f8cc574887e9dc (MD5) Previous issue date: 2013 / Resumo: O objetivo neste estudo foi avaliar a influência da ciclagem mecânica no torque de afrouxamento de parafusos protéticos, no desajuste marginal e na transmissão de tensões ao sistema prótese-implante. Foram confeccionadas 10 infraestruturas metálicas fundidas em titânio comercialmente puro, simulando próteses parciais fixas (PPF) de três elementos retidas por dois implantes e próteses totais fixas (PTF) retidas por cinco implantes. A partir das infraestruturas enceradas e fundidas, foram confeccionados modelos que deram origem aos 3 grupos de avaliação (n = 10): grupo I (pré-fundição), grupo II (adaptado) e grupo III (desajuste simulado), tanto para a PPF quanto para a PTF. Para cada modelo de trabalho (resina) confeccionado, foram avaliados o desajuste marginal e torque de afrouxamento, antes e após a ciclagem mecânica (1 milhão de ciclos mecânicos, 2 Hz, 280 N). Os torques de afrouxamento iniciais dos parafusos protéticos e dos parafusos de mini abutments foram mensurados 24 horas após a aplicação do torque (10 Ncm e 20 Ncm, respectivamente) utilizando um torquímetro digital. O teste do parafuso único foi realizado e o desajuste vertical foi quantificado por meio de microscópio óptico. As tensões geradas aos análogos durante a fixação da infraestrutura foram avaliadas em um modelo de gesso utilizando strain gauges, sendo cada infraestrutura parafusada ao modelo com um torque padronizado de 10 Ncm. Os resultados obtidos foram submetidos à análise exploratória seguida dos testes estatísticos ANOVA e Tukey (? = 0,05) quando obtidos dados paramétricos e Mann Whitney e Wilcoxon quando encontrados dados não paramétricos. Para todos os grupos avaliados, a ciclagem mecânica não apresentou diferença significativa quando analisados torque de afrouxamento dos parafusos protéticos, desajuste e tensão, porém houve um aumento nos valores médios de torque de afrouxamento dos mini abutments nos grupos II e III para a PPF e no grupo III para a PTF. O teste de correlação de Pearson (? = 0,05) indicou correlação positiva entre desajuste e tensão para todas as situações avaliadas e ainda correlação negativa entre torque de afrouxamento e desajuste vertical, para os grupos II e III de ambos os designs protéticos. Dentro das condições avaliadas e resultados obtidos, pode-se concluir que a ciclagem mecânica de infraestruturas de próteses múltiplas parafusadas não exerce influência relevante sobre o torque de afrouxamento, desajuste e tensão. Os parafusos protéticos apresentam maior tendência ao afrouxamento em próteses mal adaptadas. Próteses desadaptadas geram maior tensão ao sistema prótese-implante / Abstract: The aim of this study was to evaluate the influence of cyclic loading on loosening torque, misfit and strain transmitted to prosthesis-implant system. Ten Commercially pure titanium frameworks were casted simulating fixed partial dentures (FPD) of three elements retained by two implants and mandibular full-arch fixed prostheses (FFP) as bars retained by five implants. From the waxed and casted frameworks, models were fabricated, which resulted in three evaluation groups (n = 10): group I (pre-casting), group II (passive fit) and group III (simulated misfit), for both prosthetic designs. For each fabricated acrylic resin cast, the misfit and loosening torque analyses were assessed before and after mechanical loading (106 mechanical cycles, 2 Hz, 280 N). The initial prosthetic and mini abutment screws loosening torque were measured 24 hours after the tightening torque (10 Ncm and 20 Ncm, respectively) using a digital torque meter. The single-screw test was performed and the vertical misfit was quantified using an optical microscope. The strain after fixation was evaluated in a plaster cast using strain gauges analysis with each framework tightened to the cast with 10 Ncm standardized torque. The results were submitted to exploratory analysis followed by statistical tests such as ANOVA and Tukey (? = 0.05) when parametric data were found and Mann-Whitney and Wilcoxon when non-parametric data were obtained. For all groups, the cyclic loading had no significant difference when analyzed the prosthetic screw loosening torque, misfit and strain, but there was an increase of the mini abutment loosening torque mean values for FPD of groups II and III and for FFP of group III. The Pearson correlation test (? = 0.05) indicated a positive correlation between misfit and strain for all evaluated situations and a negative correlation between loosening torque and vertical misfit for both prostheses designs of groups II and III. Within the evaluated conditions and obtained results, it can be concluded that cyclic loading of screw-retained multiple prosthesis does not exert significant influence on loosening torque, misfit and strain. The prosthetic screws have a greater tendency to loosening in ill-fitting prosthesis, which induces higher strain values on prosthesis-implant system / Mestrado / Protese Dental / Mestra em Clínica Odontológica