21 |
Estudo da corrosão do aço inox AISI 304 em álcool etílico hidratado combustível / Study of corrosion of AISI 304 in hidrated alcohol fuelCosta, Rytney Santos 20 August 2018 (has links)
Orientador: Rodnei Bertazzoli / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-20T09:33:23Z (GMT). No. of bitstreams: 1
Costa_RytneySantos_D.pdf: 3018655 bytes, checksum: 4c710836a20f71e366fa51b7e28fddfe (MD5)
Previous issue date: 2012 / Resumo: O Brasil, em busca de combustíveis alternativos, menos poluentes e com sustentabilidade econômica eficiente, apresentou uma solução para suas necessidades, acrescentando na sua matriz energética o etanol combustível e com isto, submeteu materiais metálicos dos sistemas veiculares e tanques de armazenamento de combustível a processos corrosivos. Aços inoxidáveis têm se mostrado uma alternativa viável, no entanto é necessário estudos para obter dados que permitam averiguar a suscetibilidade desse material a processos corrosivos neste novo meio. O enfoque deste trabalho é analisar os efeitos da corrosão do álcool etílico hidratado combustível (AEHC) sobre o aço inox AISI 304 nas condições de sobtensão e sem tensão, fundamentando-se na possível influência da corrosão nas propriedades mecânicas da liga. Foram realizados ensaios de imersão em longo prazo para avaliação de perda de massa e observação por microscopia eletrônica de varredura (MEV). Paralelamente, amostras na forma de corpos de prova para ensaios de tração e fadiga, foram imersos no meio (AEHC) para avaliação dessas propriedades. Os resultados acusaram, a partir de 3456 horas de imersão, ganho de massa nas condições tensionadas e não tensionadas, sugerindo a ocorrência de passivação do metal. Imagens obtidas por MEV mostraram a formação de pites, cujo tamanho evoluiu em função do tempo de imersão. O ensaio eletroquímico com utilização arranjos de microeletrodos de diâmetros de 10, 20, 30, 100, 200 e 500 ?m acusou baixa corrente de corrosão. As propriedades mecânicas de resistência à tração, limite de escoamento e deformação específica não se mostraram influenciáveis aos efeitos corrosivos do meio sobre a liga. O ensaio de fadiga, usando os parâmetros da distribuição de probabilidade de Weibull e a durabilidade característica (?), mostrou redução da resistência à fadiga da liga quando imersa em AEHC, evidenciando que o meio corrosivo, contendo cloreto, inicializou a nucleação de pites e potencializou a formação de trincas durante os ensaios de fadiga, favorecendo a redução do limite de resistência à fadiga do aço inox AISI 304 / Abstract: The Brazil, in search of alternative fuels, cleaner and with economic efficiency, presented a solution to their needs, adding its energy in the fuel ethanol and with that submitted materials of metal vehicle systems and storage tanks of fuel processes corrosive. Stainless steels have proven a viable alternative; however it is necessary studies to obtain data to determine the susceptibility of this material to corrosive processes in this new medium. The focus of this paper is to analyze the effects of corrosion of hydrous ethanol (AEHC) on AISI 304 stainless steel under conditions of tension and without tension, the ground of the possible influence of corrosion on the mechanical properties of the alloy. Immersion tests were conducted to evaluate long-term weight loss and observation by scanning electron microscopy (SEM). In parallel, samples as specimens for tensile and fatigue, were immersed in the medium (AEHC) for evaluation of these properties. The results showed, as of 3456 hours of immersion, the weight gain of not tensioned and stressed conditions, suggesting the occurrence of passivation of the metal. Images obtained by SEM showed the formation of pits whose size has evolved as a function of immersion time. The electrochemical assay using microelectrode arrays of diameters 10, 20, 30, 100, 200 and 500 ?m charged low-current corrosion. The mechanical properties of tensile strength, yield strength and strain specific were not influenced to the corrosive effects of the medium on the league. The fatigue test, using the parameters of the Weibull probability distribution and durability characteristic (?), showed a reduction in fatigue resistance of the alloy when immersed in AEHC, indicating that the corrosive medium, containing chloride, initiated the nucleation of pits and potentiated the formation of cracks during the fatigue tests, favoring the reduction of the fatigue endurance limit of stainless steel AISI 304 / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica
|
22 |
Propriedades mecânicas e micromecanismos de fratura de corpos-de-prova usinados de rodas ferroviárias fundidas e forjadas / Mechanical properties and fracture micromechanisms of machined specimens from the cast and forged railway wheelsQueiroz, Syme Regina Souza 20 August 2018 (has links)
Orientador: Itamar Ferreira / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-20T17:14:11Z (GMT). No. of bitstreams: 1
Queiroz_SymeReginaSouza_D.pdf: 5101982 bytes, checksum: 1143c4b43c52ed713ed719367ce07ead (MD5)
Previous issue date: 2012 / Resumo: A tendência mundial das estradas de ferro é utilizar carga elevada por vagão no transporte de produtos e alta velocidade no setor de passageiros. Em ambas as situações, as rodas ferroviárias são muito solicitadas mecanicamente e, em função disso, as propriedades mecânicas dessas rodas devem ser rigorosamente controladas, tendo em vista que as principais causas de acidentes envolvendo trincas nas rodas, ou a retirada da roda antes do final de sua vida, estão direta ou indiretamente associadas a baixos níveis de resistência mecânica, resistência à fadiga e tenacidade à fratura. O conhecimento do comportamento mecânico das rodas ferroviárias com base nas suas propriedades mecânicas é imprescindível para o projeto de rodas ferroviárias e para o aprimoramento de seu processo de fabricação. Este trabalho tem como objetivo caracterizar e analisar a microestrutura, as propriedades mecânicas e os micromecanismos de fratura de cinco rodas ferroviárias, duas fundidas e três forjadas, a partir de corpos-de-prova usinados dos aros e discos dessas rodas. As propriedades mecânicas analisadas são as básicas (limite de escoamento, limite de resistência à tração, alongamento específico até à fratura, redução de área, dureza e energia de impacto Charpy), a resistência à fadiga e a tenacidade à fratura, de corpos-de-prova usinados das rodas ferroviárias. Além das microestruturas e das propriedades mecânicas, foram também caracterizados e analisados os micromecanismos de fratura dos corpos-de-prova dos ensaios de fadiga e impacto, por meio de microscopia eletrônica de varredura. Os resultados dos ensaios indicam, em relação aos limites de escoamento e de resistência à tração, que não houve diferenças significativas entre as rodas fundidas e forjadas analisadas. Quanto à dureza (HRC), ductilidade (alongamento específico e redução de área) e tenacidade à fratura, as rodas forjadas apresentaram valores superiores. Em relação à resistência à fadiga, uma propriedade importante no caso de rodas ferroviárias, os corpos-de-prova usinados das rodas forjadas apresentaram melhores resultados em relação às rodas fundidas. Pode-se também concluir que, tanto para as propriedades mecânicas básicas e nobres como também para os micromecanismos de fratura, os resultados obtidos são compatíveis aos encontrados na literatura especializada, validando e comprovando que a metodologia de análise pode ser utilizada para melhorar os projetos e os processos de fabricação de rodas ferroviárias de aço fundidas e forjadas / Abstract: The word wide tendency of railroads is to use high load per wagon in cargo transport and high-speed in passenger sector. In both situations, the railway wheels are very mechanically requered, and as a result, the mechanical properties of these wheels should be controlled strictly in order that the main causes of accidents involving wheels cracks, or withdrawal of the wheel before end of its life, are directly or indirectly associated with low levels of strength, fatigue resistance and fracture toughness. Knowledge of the mechanical behavior of railway wheels based on their mechanical properties is essential for the design of railway wheels and the improvement of its manufacturing process. This work aims to characterize and analyze the microstructure, mechanical properties and fracture micromechanisms of five railway wheels, two cast and three forged, from the machined specimens of the rim and web of these wheels. The analyzed mechanical properties are the basics (yield strength, tensile strength, elongation, reduction in area, hardness and Charpy impact energy) the fatigue resistance and the fracture toughness, from the specimens machined of railway wheels. In addition to the microstructures and mechanical properties were characterized and analyzed the micromechanisms of fracture of the specimens of fatigue and impact tests, using scanning electron microscopy. The test results indicate, with respect to the yield strength and tensile strength, there were no significant differences between cast and forged wheels analyzed. The hardness (HRC), ductility (elongation and reduction in area) and fracture toughness of the forged wheels showed higher values. Regarding resistance to fatigue, an important property in the case of railway wheels, the forged wheels machined specimens shown better results compared to cast wheels. One can also conclude that, for both the basic and noble mechanical properties as well as for the micromechanisms of fracture, the results are compatible with those found in the literature, validating and verifying that the method of analysis can be used to improve the castings and forgings steel railway wheels and manufacturing processes and projects / Doutorado / Materiais e Processos de Fabricação / Doutora em Engenharia Mecânica
|
23 |
Análise da evolução microestrutural e de propriedades mecânicas de ligas Sn-Ag e Sn-Bi para soldagem e recobrimento de superfícies / Assessment of microstructural evolution and mechanical properties of Sn-Ag and Sn-Bi alloys for soldering and coating applicationsGarcia, Leonardo Richeli 21 August 2018 (has links)
Orientadores: Amauri Garcia, Wislei Riuper Ramos Osório / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-21T02:28:07Z (GMT). No. of bitstreams: 1
Garcia_LeonardoRicheli_D.pdf: 14084477 bytes, checksum: f9b96fac198700cfcafeecf1edca6f9b (MD5)
Previous issue date: 2012 / Resumo: A preocupação ambiental sobre a toxicidade do Pb combinada com normas rígidas, estão gradualmente proibindo a aplicação de Pb em ligas de soldas. As ligas alternativas Sn-Ag e Sn-Bi podem estar entre as mais promissoras candidatas à substituição das ligas de solda sem chumbo em função de apresentarem propriedades compatíveis com as da liga Sn-Pb. A fim de adequar os produtos aos novos requisitos, produtores de componentes microeletrônicos necessitam desenvolver novas ligas de solda. Estudos sobre a influência da taxa de resfriamento sobre a microestrutura e as propriedades mecânicas resultantes e as características de recobrimento dessas ligas necessitam ser realizados. Esse trabalho tem exatamente esse objetivo, e no qual é realizado um estudo experimental comparativo das principais características da tradicional liga Sn-Pb e das ligas Sn-Ag e Sn-Bi visando a aplicação dessas ligas como ligas alternativas de solda. As seguintes atividades foram desenvolvidas para atingir tais propósitos: i) solidificação unidirecional das ligas Sn-Ag (hipoeutética Sn-2%Ag e eutética Sn-3,5%Ag) e Sn-Bi (Sn-10, 20 e 40%Bi); ii) ensaios de mergulho de lâminas de cobre nas ligas Sn-Ag e Sn-Bi fundidas e; iii) ensaios de tração de acordo com as especificações da norma ASTM E 8M/04. Foi utilizado um dispositivo de solidificação vertical ascendente para obter os lingotes das ligas e os correspondentes perfis térmicos. Variáveis térmicas de solidificação como: taxa de resfriamento, velocidade de solidificação e tempo local de solidificação foram determinadas para as ligas Sn-Ag e Sn-Bi. Essas variáveis experimentais foram correlacionadas com os espaçamentos dendríticos secundários (l2) e foram propostas equações experimentais de crescimento dendrítico. A espessura da camada solidificada, a área recoberta e as microestruturas resultantes das ligas no substrato de cobre foram avaliadas após o ensaio de mergulho em diferentes temperaturas. Verificou-se que, considerando-se as ligas Sn-Ag e Sn-Bi examinadas, a liga Sn- 40%Bi apresenta maior resistência mecânica e a liga Sn-3,5%Ag apresenta molhabilidade similar quando comparada com a tradicional liga de solda Sn-40%Pb / Abstract: The increasingly environmental concern over the toxicity of Pb combined with strict regulations, are gradually banning the application of Pb-based solders. Sn-Ag and Sn-Bi solder alloys are among the most promising candidates for Pb-free alternatives due to their compatible properties with the Sn-Pb solder alloy. In order to adequate products to such restriction requirements, electronic components manufacturers have to meet such requirements by developing new lead-free solder alloys. Studies focusing on the influence of the cooling rate on the resulting microstructures and on both the mechanical properties and recovery of these alloys need to be carried out. This work has precisely such objective, in which a comparative experimental study of the main features of the traditional Sn-Pb alloy and Sn-Ag and Sn-Bi alloys is carried out with a view to application of the latter alloys as alternative solder materials. The following activities were developed to attain such purpose: i) unidirectional solidification of Sn-Ag alloys (hypoeutectic Sn-2 wt.% Ag, eutectic Sn-3.5 wt.% Ag), and Sn-Bi alloys (Sn-10, 20 and 40 wt.% Bi); ii) copper blades dipped in both molten Sn-Ag and Sn-Bi alloys (hot dipping) and iii) tensile testing according to specifications of ASTM standard E 8M/04. An upward vertical solidification system has been used to obtain the alloys ingots and their correspondent thermal profiles. Solidification thermal variables such as: the cooling rate, tip growth rate and local solidification time have been determined for Sn-Ag and Sn-Bi alloys. Such experimental variables have been correlated with secondary dendrite arm spacings (l2) and experimental equations of dendritic growth have been proposed. The thickness of the coating layers, the spreading areas and the resulting microstructures of these alloys on the copper substrates were evaluated after the hot dipping procedures at different temperatures. It was found that, of the examined Sn-Ag and Sn-Bi alloys, the Sn-40 wt.% Bi alloy has offered the highest mechanical strength and the Sn- 3.5 wt.% Ag alloy has shown similar wettability when compared with the traditional Sn-40 wt.% Pb solder alloy / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica
|
24 |
Solidificação transitoria, microestrutura e propriedades de ligas Al-Ni / Transient solidification, microstruture and properties of Al-Ni alloysCante, Manuel Venceslau 14 August 2018 (has links)
Orientador: Amauri Garcia / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-14T11:35:39Z (GMT). No. of bitstreams: 1
Cante_ManuelVenceslau_D.pdf: 12795296 bytes, checksum: bd8bf91fcf479b66a28e7e3d6b5f7090 (MD5)
Previous issue date: 2009 / Resumo: O desenvolvimento de microestruturas otimizadas durante o processo de solidificação são de fundamental importância nas propriedades e desempenho de produtos acabados baseados em ligas metálicas. Neste estudo é analisada a cinética envolvida no processo de solidificação, seus efeitos nos parâmetros macro e microestruturais e a sua conseqüente influência nas propriedades mecânicas. Com esse intuito, ligas hipoeutéticas do sistema binário são estudadas Al-Ni por meio de experimentos de solidificação vertical ascendente sob regime transitório de condução de calor. Os espaçamentos dendríticos primários (?1) e secundários(?2) foram medidos ao longo de todos os lingotes para cada uma das ligas analisadas e correlacionados com as variáveis térmicas de solidificação. Uma abordagem teórico-experimental é utilizada na determinação quantitativa de tais variáveis térmicas: coeficiente de transferência de calor na interface metal/molde, velocidade de deslocamento da isoterma liquidus, gradientes térmicos, taxa de resfriamento e tempo local de solidificação. Os dados experimentais referentes à solidificação das ligas são confrontados com os principais modelos teóricos de crescimento dendrítico da literatura. Este estudo aborda, também, a influência do teor de soluto nos espaçamentos dendríticos para as ligas estudadas. Do ponto de vista macroestrutural, verifica-se que a transição colunar/equiaxial (TCE) ocorre para ligas hipoeutéticas Al-Ni para uma taxa crítica de resfriamento de 0,16 K/s. Por ensaios de tração as propriedades mecânicas das ligas do sistema Al-Ni são correlacionadas com parâmetros da micro-estrutura dendrítica resultante do processo de solidificação. Verifica-se que os limites de escoamento e de resistência à tração crescem com o aumento da concentração de soluto e decrescem com o aumento dos espaçamentos dendríticos, ?1 e ?2. O alongamento específico, por outro lado, mostra-se independente da composição e do arranjo dendrítico. Para a liga Al-5%Ni foi também realizado um estudo de solidificação rápida por refusão da superfície a laser para análise das variações microestruturais e de dureza entre as áreas não tratadas e tratadas superficialmente. / Abstract: The development of optimized microstructures during the solidification stage of processing is of fundamental importance to the mechanical properties and to the performance of finished products of metallic alloys. In this study the kinetics of solidification and its effects on macro and microstructural parameters, as well as the consequent influence on the final mechanical properties are analyzed. Hypoeutectic Al-Ni alloys are studied by upward unidirectional solidification experiments under transient heat flow conditions. Primary (?1) and secondary (?2) dendrite arm spacings are measured along the castings for all alloys analyzed and correlated with transient solidification thermal variables. A combined theoretical/ experimental approach is used to quantitatively determine such thermal variables, i.e., transient metal/mold heat transfer coefficients, tip growth rates, thermal gradients, tip cooling rates and local solidification time. The experimental data concerning the Al-Ni alloys solidification are compared to the main predictive dendritic models from the literature and the dependence of dendrite arm spacing on the alloy solute content is also analyzed. From the macrostructural point of view, it is found that the CET occurs for a critical value of cooling rate of about 0.16 K/s for hypoeutectic Al-Ni alloys.With a view to correlate mechanical properties to dendrite arm spacings, tensile testings were carried out. It is found that the ultimate tensile strength and the yield strength increase with increasing alloy solute content and with decreasing primary and secondary dendrite arm spacings. In contrast, the elongation is found to be independent of both alloy composition and dendritic arrangement. For the Al 5%Ni alloy a rapid solidification study is carried out by using laser surface remelting in order to permit microstructural and microhardness variations throughout the resulting treated and untreated zones, to be analysed. / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica
|
25 |
Análise de falhas em instrumentais cirúrgicos metálicos / Failure analysis in metallic surgical instrumentsLima, Lonetá Lauro, 1982- 07 July 2009 (has links)
Orientador:Cecilia Amélia de Carvalho Zavaglia / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-17T03:06:41Z (GMT). No. of bitstreams: 1
Lima_LonetaLauro_M.pdf: 24537827 bytes, checksum: 1752c0adc4c679a8527b36c597af320e (MD5)
Previous issue date: 2009 / Resumo: Este trabalho foi desenvolvido juntamente com a equipe de enfermagem do HC da Unicamp. O principal objetivo foi avaliar os modos de falhas presentes em pinças hemostáticas retas e curvas de fabricação nacional, que já haviam sido utilizadas pelo Hospital das Clínicas da Unicamp e que falharam prematuramente durante o uso. Os parâmetros avaliados estão relacionados com a qualidade da matéria-prima, propriedades mecânicas e com o processo de fabricação. As pinças foram avaliadas segundo as normas internacionais da ASTM, entre elas a ASTM F 899-09, a ASTM F 1744-96(2008) e a ASTM F 1026-86(2008). As fraturas ocorridas nas pinças falhadas foram analisadas por microscópio eletrônico de varredura-MEV, sendo possível visualizar que o mecanismo de fratura predominante foi o de corrosão sob tensão. Também foi realizado ensaio em pinças sem uso (nacionais e importadas) e os resultados obtidos foram diferentes para ambas, sendo que a pinça nacional sem uso apresentou itens reprovados pela norma. Os resultados obtidos permitiram concluir que existe diferença no processo de fabricação dos materiais nacionais e importados e isso reflete na durabilidade, qualidade e segurança no uso dos instrumentais nacionais. A inspeção por MEV das pinças nacionais indicou problemas no acabamento de superfície como: pontos de corrosão, trincas e rebarbas, reprovando essas pinças segundo os critérios de aceitação das normas ASTM. Através deste estudo foi possível criar um documento para auxiliar a equipe de enfermagem na avaliação da qualidade de instrumentais cirúrgicos metálicos / Abstract: This work was developed together with the team of nursing of the HC of the Unicamp. The objective went to evaluate the failure modes in national hemostatic forceps, that already had been used for the Hospital of the Clinics of the Unicamp and that failed prematurely during the use. The evaluated parameters are related with the quality of the raw material, mechanical properties and with the manufacture process. The hemostatic forceps went evaluated according to international norms of the ASTM, between them ASTM F 899-09, ASTM F 1744-96 (2008) and ASTM F 1026-86 (2008). The fracture occurred in the hemostatic forceps went analyzed by scanning electron microscope-SEM, being possible to visualize that the mechanism of predominant failure was stress corrosion crack. Also assay in hemostatic forceps without use (national and imported) and the results had different for both, being that the national forceps without use presented item disaccord to norm. Through the results went possible to conclude there are differences in the process of manufacture of the national and imported forceps, and this reflects in the durability, quality and security in the use of the national instruments. The inspection for SEM of the national fórceps indicated problems in the surface finishing as: points of corrosion, cracks and burrs, disapproving these forceps according to criteria of acceptance of norms ASTM. Through this study went possible to create a document to assist the nursing team to evaluate the quality of the metallic surgical instruments / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica
|
26 |
Tenacidade a fratura em condições elasto-plasticas com corpos de prova não normalisados para aços API 5L : analise numerica e experimental / Elastic-plastic fracture toughness with non standard specimes for API 5L steel : numerical and experimental analysisAguirre Torrico, Ivan Felix 13 February 2006 (has links)
Orientador: Itamar Ferreira / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-06T11:42:58Z (GMT). No. of bitstreams: 1
AguirreTorrico_IvanFelix_D.pdf: 3675970 bytes, checksum: 89da868d1276d05e3f5f216b82efb029 (MD5)
Previous issue date: 2006 / Resumo: O gasoduto Bolívia-Brasil foi fabricado com dutos de aços API 5L X65 e X70. Existem relatos na literatura especializada de que o campo de tensões nas vizinhanças da ponta da trinca e a tenacidade à fratura são similares entre os corpos de prova não normalizados do tipo tração com entalhe lateral [SE(T)] e dutos. Neste trabalho realizou-se um estudo numérico e experimental da tenacidade à fratura em condições elasto-plásticas, com corpos de prova do tipo SE(T), dos aços API 5L X65 e API 5L X70. A determinação dos parâmetros da mecânica da fratura elástica linear foi feita pelos Métodos dos Elementos Finitos (MEF) e dos Elementos de Contorno (MEC) e a determinação do parâmetro elasto-plástico integral J por MEF. O fator eta plástico obtido numericamente, pelo MEF e com dados fornecidos pelo método EPRI, foi de 1,0, para medições do deslocamento de abertura da boca da trinca (CMOD). Com este fator eta plástico, foram realizados ensaios experimentais de tenacidade à fratura com corpos de prova do tipo SE(T), com espessura de 5 mm, e esses valores foram comparados com os resultados de ensaios em corpos de prova de flexão em três pontos [SE(B)], também com espessura de 5 mm. Houve um boa concordância entre os resultados numéricos e experimentais da integral J. Verificou-se que as curvas J-R obtidas com ensaios SE(T) são próximas das obtidas com ensaios SE(B), tendo em vista que a espessura dos corpos de prova utilizada, de 5 mm, não pôde ser modelada no estado plano de tensão ou de deformação / Abstract: The gas pipeline Bolivia-Brazil was manufactured with pipes of API 5L X65 and X70 steels. Specialized literature report that the stress field in the neighborhood of the crack tip and the fracture toughness are similar between not standard single edge notch tensile specimens - SE(T) - and pipes. In this work numerical and experimental study were made of the elastic-plastic fracture toughness using SE(T) specimens for API 5L X65 and X70 steels. The determination of the parameters of the linear elastic fracture mechanics was performed by the methods of the Finite Elements (FEM) and Boundary Elements (BEM). The J-integral parameter was determined by FEM. The plastic eta factor was obtained by FEM and with data supplied by the EPRI method. In both cases for measurements of the crack mouth opening displacement (CMOD) the determined plastic eta factor is 1.0. With this plastic eta factor, experimental tests of fracture toughness were accomplished using SE(T) specimens with thickness of 5 mm, and those values were compared with the test results obtained with standard single edge bend -SE (B)- specimens also with thickness of 5 mm. There was a good agreement between the numeric and experimental results of J-integral. Was verified that the J-R curves obtained with SE(T) specimens are close to the obtained with SE(B) specimens / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica
|
27 |
Microestrutura de solidificação e propriedades mecanicas de ligas Sn-Zn para soldagem e recobrimento de superficies / Solidification microstructure and mechanical properties of Sn-Zn alloys for welding and depositionGarcia, Leonardo Richeli 12 August 2018 (has links)
Orientadores: Amauri Garcia, Wislei Riuper Ramos Osorio / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-12T22:54:52Z (GMT). No. of bitstreams: 1
Garcia_LeonardoRicheli_M.pdf: 15499869 bytes, checksum: 1afa8bd79812971da1e6fac7f4fed383 (MD5)
Previous issue date: 2008 / Resumo: Sabe-se que existem tendências de leis e diretrizes que restringem o uso e aplicação de certas substâncias perigosas utilizadas em processos de fabricação de componentes em geral. Como exemplo, podem-se citar produtos contendo cádmio, mercúrio, cromo hexavalente, bifenilos polibromatos, éteres difenil-polibromato e chumbo. Devido a essas restrições, fabricantes de produtos eletrônicos têm que adequar seus produtos às novas diretrizes e desenvolver novas ligas de solda sem chumbo. Estudos preliminares indicam que ligas Sn-Zn, particularmente a eutética, consistem em alternativas promissoras para a substituição das ligas de solda contendo chumbo. Entretanto, é necessário avaliar influências das taxas de resfriamento do processo sobre a microestrutura formada e as propriedades mecânicas dessas ligas. O presente trabalho tem exatamente esse objetivo, e para cuja consecução foram planejadas as seguintes atividades: i) solidificação unidirecional de ligas Sn-Zn (Sn-4%Zn, Sn-9%Zn e Sn-12%Zn) e da liga eutética Sn-Pb (para comparação), ii) mergulho de lâminas de cobre em banho das ligas Sn-Zn e Sn- Pb por intermédio de imersão à quente e iii) por deposição em substrato de cobre. Para a fase inicial utilizou-se de um dispositivo de solidificação unidirecional vertical ascendente, para obtenção dos lingotes e registro dos respectivos perfis térmicos experimentais. Foram determinadas as variáveis térmicas de solidificação: coeficiente de transferência de calor metal/molde, velocidades de deslocamento da isoterma liquidus e taxa de resfriamento para as ligas do sistema Sn-Zn e para a liga Sn-Pb (Sn-40%Pb). Estas variáveis foram confrontadas com as previsões teóricas de um modelo numérico de solidificação e, em seguida, correlacionadas com os espaçamentos dendríticos secundários (?2) e equações experimentais de crescimento dendrítico foram determinadas. Foram realizados ensaios de mergulho utilizando-se lâminas (substrato) de cobre, a diferentes temperaturas de mergulho, em que foi possível avaliar a espessura da camada depositada sobre o substrato, a porcentagem da área recoberta pelas ligas e verificar as respectivas microestruturas. Foram também realizados ensaios de molhabilidade para avaliação do ângulo de contato
entre cada liga e os respectivos substratos / Abstract: A number of laws and guidelines have been restricted the application of hazardous substances in manufacturing processes of components. This is the case of products containing cadmium, mercury, hexavalent chromium, polibromates biphenyls, polibromate-diphenyl ethers and lead. In order to adequate products to such restriction requirements, electronic components manufacturers have to meet such requirements by developing new lead-free solder alloys. Preliminary studies have indicated that Sn-Zn alloys, in particular the eutectic composition, are promising alternatives to the replacement of solder alloys containing lead. However, studies focusing on the influence of the cooling rate on the resulting microstructures and on the mechanical properties of these alloys need to be carried out. This work has precisely such objective, and the following activities have been planned to attain such purpose: i) unidirectional solidification of Sn-Zn alloys (Sn-4wt%Zn, Sn-9wt%Zn, Sn-12wt%Zn) and of the Sn-Pb eutectic (for comparison purposes), ii) copper blades dipped in molten Sn-Zn and Sn-Pb alloys (hot dipping) and iii) deposition on copper substrate. For the initial experimental step an upward vertical solidification system has been used to obtain the alloys ingots and their correspondent thermal profiles. Solidification thermal variables such as: metal/mold heat transfer coefficient, tip growth rates and cooling rates have been determined for Sn-Zn and the Sn-40wt%Pb alloys. Such experimental variables have been compared with predictions from a solidification numerical model and correlated to secondary dendrite arm spacings (?2) and experimental equations of dendritic growth have been proposed. The thickness of the coating layers, the spreading areas and the resulting microstructures of the alloys on the copper substrates (blades) were evaluated after the hot dipping procedures at different temperatures. Wetting tests have also been carried out in order to evaluate the contact angle between drop and substrate for each alloy / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica
|
28 |
Deformação plástica a frio, transformações de fases e propriedades mecânicas de ligas Ti-Nb-Sn para uso biomédico / Cold deformation, phases transformations and mechanical strength of Ti-Nb-Sn alloys for biomedical usesCremasco, Alessandra, 1983- 21 August 2018 (has links)
Orientador: Rubens Caram Junior / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-21T09:06:40Z (GMT). No. of bitstreams: 1
Cremasco_Alessandra_D.pdf: 50106196 bytes, checksum: 2a7da86acd168979590189fcdb26056f (MD5)
Previous issue date: 2012 / Resumo: Ligas de titânio com altos teores de elementos _ estabilizadores, solubilizadas em altas temperaturas e resfriadas rapidamente exibem limitada resistência mecânica e boa ductilidade, o que e resultado da formação de martensita ortorrômbica ou da manutenção da fase _ metaestável. Tal resistência pode ser significativamente aumentada por meio da aplicação de tratamentos térmicos de envelhecimento, que promovem a precipitação de novas fases, combinados com encruamento produzido por deformação plástica a frio. Este trabalho teve como objetivo o desenvolvimento de ligas do sistema Ti-Nb-Sn com propriedades mecânicas otimizadas visando sua utilização como biomaterial. Inicialmente, ligas de titânio com diferentes elementos de liga foram submetidas a ensaios de citocompatibilidade in vitro. Os resultados obtidos sugerem que ligas Ti-Nb-Sn sao biocompativeis. Na sequencia, amostras de ligas Ti-Nb-Sn preparadas em forno de fusao a arco foram tratadas termicamente objetivando homogeneizacao quimica e microestrutural, solubilizadas em alta temperatura, resfriadas rapidamente e deformadas plasticamente a frio. Tais amostras foram tratadas termicamente para promover a recuperacao, a recristalizacao e o envelhecimento da microestrutura. Os resultados obtidos indicam que a aplicacao de deformacao plastica e recozimento produz o refinamento da microestrutura. A aplicacao de tratamentos termicos de envelhecimento a 350 °C resultou na decomposicao da fase martensita ortorrombica e na formacao das fases _, w e a. Constatou-se que o comportamento mecanico das amostras envelhecidas reflete a combinacao das fases e suas respectivas fracoes volumetricas. O refino microestrutural e a precipitação da fase a resultaram em expressivo aumento da dureza, modulo de elasticidade e resistencia mecanica, bem como na queda da ductilidade. Finalmente, a aplicacao de condicoes de processamento otimizadas resultou em amostras com elevada resistencia mecanica e razoavel ductilidade. A liga Ti-35Nb-4Sn apresentou reduzido modulo de elasticidade e alta resistencia a tracao, condicao ideal para aplicacao biomedica / Abstract: Titanium alloys with high _ stabilizing elements content, solution heat treated at high temperatures and rapidly cooled to room temperature, exhibit limited mechanical strength and good ductility as a result of orthorhombic martensite formation or maintenance of the _ metastable phase. However, mechanical strength may be significantly improved by applying aging heat treatment, which leads to precipitation of new phases, combined with hardening provided by cold plastic deformation. The aim of this work is the development of alloys in the Ti-Nb-Sn system with optimized mechanical properties to be applied as biomaterial. Initially, titanium alloys with different alloying elements were tested in terms of cytocompatibility. The results suggest that Ti-Nb-Sn alloys are biocompatible. Following, Ti-Nb-Sn samples were prepared in arc furnace, heat treated aiming chemical and microstructural homogeneity, solution heat treated at high temperature, rapidly cooled to room temperature and cold plastically deformed. These samples were heat treated to promote recovery, recrystallization and aging of the microstructure. The results indicate that application of plastic deformation and annealing produces very refined microstructure. Application of aging heat treatments at 350 ° C resulted in decomposition of orthorhombic martensite phase and formation of _, w and a phases. It was found that mechanical properties of aged samples reflect the combination of such phases and their volume fractions. Microstructural refinement and a phase precipitation resulted in significant increase in hardness, elastic modulus and mechanical strength, as well as a decrease in ductility. Finally, application of optimal processing conditions resulted in samples with high mechanical strength and reasonable ductility. The Ti-35Nb-4Sn alloy showed lower elastic modulus and superior tensile strength. These results consist in ideal conditions for biomedical applications / Doutorado / Materiais e Processos de Fabricação / Doutora em Engenharia Mecânica
|
29 |
Estudo de comportamento mecânico de ligas TiNbSn em função do teor de liga, laminação a frio e envelhecimento / Study of mechanical behavior of TiNbSn alloy in the function of alloy content, cold lamination and agingAzevedo, Thiago Figueiredo 23 August 2017 (has links)
The present study is focused on mechanical properties that result from cold rolling
and aging treatments applied to TiNbSn alloys comprising different Nb (35% and
42%) and Sn (0% and 2.5%) contents. The alloys were arc melted, homogenized,
solubilized, cold rolled and aged at 400 °C for different aging times. A set of
characterization tests performed, included microstructural analysis, X-ray
diffraction, microhardness, tensile tests, toughness (J) and fracture analysis. The
alloys contained all three beta, α” and omega phases after cold rolling, regardless
of the alloying content. The solid solution effect led to changes in the alloys’
mechanical behavior. Furthermore, the alloys presented alpha phase
precipitation, and it led to a peak-aged stage after different aging times due to the
Nb content. The alloys containing 42% and 35% Nb content reached the peakaged
stage within 48 and 72 h, respectively. The α phase precipitation in the
alloys at peak-aged stage increased the hardness, tensile strength and elastic
modulus of the alloys; however, it also caused ductility and toughness decrease.
The fine dispersed precipitates of the alpha phase generated small and shallow
dimples, which are a characteristic fracture micromechanism of peak-aged alloys. / O presente estudo está focado em propriedades mecânicas resultantes de
tratamentos de laminação a frio e envelhecimento aplicados a ligas de TiNbSn
compreendendo diferentes conteúdos Nb (35% e 42%) e Sn (0% e 2,5%). As
ligas foram fundidas a arco, homogeneizadas, solubilizadas, laminadas a frio e
envelhecidas a 400°C durante diferentes tempos de envelhecimento. Um
conjunto de ensaios de caracterizações, incluindo análise microestrutural, DRX,
ensaios de tração, tenacidade (J) e análise de fraturas. As ligas apresentaram
as mesmas fases beta, α" e ômega após laminação a frio, independentemente
do teor de liga. O efeito da solução sólida levou a mudanças nas propriedades
mecânicas. Além disso, as ligas apresentaram precipitação em fase alfa e
conduziram a um estágio de pico após diferentes tempos de envelhecimento
devido ao teor de Nb. As ligas contendo teor de Nb de 42% e 35% atingiram o
ponto de pico de envelhecimento dentro de 48 e 72 horas, respectivamente. A
precipitação da fase alfa nas ligas no ponto de pico aumentaram a dureza, a
resistência à tração e o módulo de elasticidade das ligas. No entanto, também
causou diminuição da ductilidade e da tenacidade. Os precipitados finos
dispersos da fase alfa geraram microcavidades pequenos e pouco profundos,
que são micromecanismos característicos de fratura de ligas de ponto máximo
de envelhecimento.
|
30 |
Propriedades mecânicas de juntas soldadas com diferença de espessura pelo processo de soldagem por atrito linear com mistura em ligas de Al-Mg para aplicação na construção navalFeistauer, Eduardo Etzberger 21 March 2014 (has links)
The shipbuilding sector, as well as all modern transportation industries, is faced with demands for greater productivity while at the same time ensuring the manufacture of consistently high quality products, reducing levels of re-working, saving energy, and minimizing operational costs. Furthermore, it is imperative that new designs and all the stages of production comply with stringent environmental regulation. Within this context, the application of Friction Stir Welding (FSW) as a manufacturing process to weld Tailor Welded Blanks (TWB) for Al structures can contribute to the development of high speed craft and lightweight ships that are more fuel efficient, based on a high energetic efficient and environmental friendly welding process. In this work, the heterogeneous mechanical behavior of TWB joints welded by FSW was evaluated using quasi-static and cyclic loading, and the observed microstructural features were analyzed. The TWB joints were manufactured using dissimilar alloys and thicknesses (6 and 8mm) of particular interest in the shipbuilding sector (AA5083, AA5059 and AA6082). An evaluation of local constitutive properties in different regions through the TWB joint was performed by digital image correlation linked to the tensile test system. From the DIC data processing were generated stress concentrations diagrams and true stress-strain curves for several TWB subzones. The DIC methodology used as well as the accuracy of the proposed method are described in detail. The joints exhibited excellent mechanical properties approximately the same as those of the base metal for the joints manufactured with work hardened alloys (AA5059/AA5083) and 76% mechanical efficiency to those manufactured with the heat-treatable alloy (AA6082). The fatigue strength of the TWB joints were higher than the IIW references for welded structures in aluminum and the fracture mechanisms were characterized using SEM. / O setor de construção naval, bem como a indústria moderna, é continuamente sobrecarregada por demandas de aumento de produtividade e ao mesmo tempo precisa garantir a fabricação de produtos com alta qualidade, reduzindo os níveis de retrabalhos, economizando energia e diminuindo os custos operacionais. Adicionalmente a este paradoxo, é imperativo que os novos designs de produtos e todos os estágios de produção sejam compatibilizados com as rígidas exigências ambientais. Neste contexto, a concepção de projetos de estruturas leves soldadas por SALM em configurações sob medidas (Tailor Welded Blanks - TWB) em Al podem contribuir para produção de embarcações com eficiente consumo de combustível e redução dos níveis de eliminação de CO2 através da redução do peso de suas estruturas. Além de utilizar um processo de soldagem eficiente energeticamente e amigável ao meio ambiente. Neste trabalho as características heterogêneas de juntas em TWB soldadas por SALM foram avaliadas através de ensaios mecânicos com carregamentos quasi-estáticos e dinâmicos e, foram criadas relações entre as propriedades mecânicas das juntas e alterações microestruturas resultantes do processo de soldagem. As juntas em TWB foram produzidas com três diferentes ligas de alumínio de particular interesse da construção naval, (AA5083, AA5059 e AA6082) em configurações similares e dissimilar, com combinações de espessuras de 6 e 8mm. Acoplado ao ensaio de tração um sistema de correlação digital de imagens (DIC) foi instalado e o perfil de deformação local das juntas foram investigados durante o carregamento. A partir do processamento dos dados obtidos por DIC, diagramas de concentração de tensão e curvas de tensão-deformação locais foram computados para diferentes subzonas das juntas. O procedimento utilizado, bem como os dados obtidos e a precisão da metodologia proposta foram descritos detalhadamente. As juntas apresentaram excelentes propriedades mecânicas, equivalentes às do metal base para a junta dissimilar produzida com as ligas endurecidas por trabalho mecânico (AA5059/AA5083) e 76% de eficiência para as juntas similares produzidas com a liga tratável termicamente (AA6082). A resistência a fadiga das juntas foram superiores às referências do IIW para juntas soldadas em alumínio e os mecanismos de fratura foram caracterizados por MEV.
|