Caracterização anatômica da matéria-prima e avaliação das propriedades tecnológicas de painéis MDF de madeira de Schizolobium amazonicum Huber ex Ducke e de resíduos de espécies da Amazônia. / Anatomical characterization and evaluation of technological properties MDF manufactured from wood Schizolobium amazonicum Huber ex Ducke and waste native species of the AmazonRibeiro, Victor Cezar Nepomuceno 22 January 2015 (has links)
Estudos sobre a qualidade tecnológica de painéis MDF produzidos a partir de madeiras nativas da Amazônia ainda são escassos. O presente estudo teve como objetivo principal determinar a qualidade de painéis MDF produzidos com a madeira de Schizolobium amazonicum Huber ex Ducke, em forma de resíduos de lâminas e toras (LAM e TOR, respectivamente), e resíduos de espécies nativas da Amazônia (MIX). A partir destas matérias-primas foram produzidos cavacos, fibras e painéis MDF numa unidade industrial de MDF. Na manufatura dos painéis foram adotados 06 tratamentos. Os tratamentos adotados foram analisados por meio de 03 experimentos independentes: Experimento 1 - verificar o efeito da proporção de matéria-prima (25% TOR -75% MIX; 40% LAM - 75% MIX; 40% LAM - 60% MIX) nas propriedades físicas e mecânicas dos painéis; Experimento 2 - para verificar o efeito da espessura (12 e 15 mm) nas propriedades físicas e mecânicas dos painéis; Experimento 3 - também para verificar o efeito da espessura (15 e 18 mm) nas propriedades físicas e mecânicas dos painéis. Os painéis MDF foram colados com 13% de resina a base de ureia-formaldeído e 0,7% de emulsão de parafina. Posteriormente, corpos-de-prova foram obtidos dos painéis MDF para avaliação da massa específica, teor de umidade, absorção de água, inchamento em espessura, módulo de ruptura, módulo de elasticidade, resistência da ligação interna, resistência ao arracamento de parafuso na face e no topo, conduzidos conforme a norma NBR 15316 (ABNT, 2009). Adicionalmente, foi realizada a caracterização das fibras de TOR, LAM e MIX antes e após o desfibramento industrial dos cavacos e determinado o perfil de densidade dos painéis por meio da técnica de atenuação de raios-X. Para verificar o efeito das variáveis sobre as propriedades das chapas MDF foi realizada uma análise de variância e, posteriormente, o teste de Tukey, conduzido ao nível de 5% de probabilidade de erro. Mediante a análise dos resultados dos ensaios, concluiu-se que: No Experimento 1, os painéis MDF manufaturados com a mistura de fibras das madeiras na proporção B apresentaram melhor desempenho nas propriedades de APT e APF, e os painéis na proporção C desempenho superior no MOR. No Experimento 2, os painéis de 12 mm mostraram melhor desempenho nas propriedades de LI e APF, e os painéis de 15 mm melhor desempenho em AA2h, AA24h e IE24H; No Experimento 3, os painéis MDF de 18 mm exibiram melhor desempenho nas propriedades de IE2h, IE24h, MOR e MOE à flexão estática. Os painéis de 15 mm tiveram melhor desempenho nas propriedades de APT e APF. Com exceção dos valores da propriedade de LI, todos os painéis MDF avaliados no presente estudo atenderam aos valores requeridos pela norma NBR 15316-2 (ABNT, 2009), para fabricação de móveis a serem utilizados em condições secas. / Studies about the technological quality of MDF manufactured with wood of native species from Amazon are scare. This study aimed to evaluate the quality of MDF produced with wood Schizolobium amazonicum Huber ex Ducke, waste of veneer and log (LAM and TOR, respectively) and waste of native species from Amazon (MIX). The chips, fibers and MDF, from this material, were produced in an industrial unit MDF. In the manufacture of panels 06 treatments were adopted. The following treatments were analyzed by 03 independent experiments: Experiment 1 - to verify the effect of the proportion of raw material (25% -75% TOR MIX; LAM 40% - 75% MIX; LAM 40% - 60% MIX) on the physical and mechanical properties of the panels; Experiment 2 - to verify the effect of thickness (12 and 15 mm) on the physical and mechanical properties of the panels; Experiment 3 - also, to verify the effect of the thickness (15 and 18 mm) on the physical and mechanical properties of the panels. The MDF panels were bonded with 13% of resin based on urea formaldehyde and 0.7% paraffin emulsion. Posteriorly, samples were obtained to conduct the moisture content, bulk density, water absorption and thickness swelling, modulus of rupture, modulus of elasticity, internal bonding, resistance to face screw-holding and edge screw-holding, tests according to NBR 15316 (ABNT, 2009). Additionally, was characterized the TOR, LAM and MIX fibers, performed before and after industrial refining chip and determined the density profile of the MDF using the technique of X-ray attenuation. To check the effect of variables on the properties of MDF an analysis of variance was performed, and subsequently the Tukey test, conducted at the 5% level of error probability. Through the analysis of tests results it was conclude: In Experiment 1, MDF panels manufactured with a mixture of wood fiber in the ratio B showed better performance in the properties of APT and APF, and the panels in C ratio showed superior performance in MOR. In Experiment 2, the panels of 12 mm showed better performance in the properties of LI and APF, and 15 mm panels perform better in AA2h, AA24h and IE24H; In Experiment 3, the panels of 18 mm panels exhibited better performance on the properties of IE2h, IE24h, MOR and MOE in static bending. 15 mm panels outperformed the properties of APT and APF. With the exception of property values LI, all MDF panels evaluated in this study met the required values by NBR 15316-2 (ABNT, 2009), for the manufacture of furniture to be used in dry conditions.
|
12 |
Produção e avaliação do desempenho de painéis de partículas de Eucalyptus grandis confeccionados com adição de casca de aveia / Production and performance evaluation of particleboard made from Eucalyptus grandis addition of oat hullsVaranda, Luciano Donizeti 10 July 2012 (has links)
Os painéis à base de madeira vêm sendo amplamente utilizados em todo o mundo, em resposta à redução de oferta de madeira maciça em diversos segmentos da indústria madeireira, como em móveis, painéis, estruturas e outros componentes na construção civil. O grande volume de resíduos gerados pela agroindústria viabiliza o desenvolvimento de materiais alternativos e sustentáveis, destacando-se os painéis de partículas. Este trabalho apresenta um estudo da produção e avaliação de painéis de partículas de Eucalyptus grandis e casca de aveia, aderidas sob pressão com dois tipos de resinas (poliuretana à base de mamona e ureia formaldeído). O desempenho físico-mecânico dos painéis produzidos foi avaliado com base na ABNT NBR 14810:2006. Por meio de análise de variância (ANOVA), avaliou-se a influência dos fatores adotados: madeira de Eucalyptus grandis, com proporções mássicas de 70, 85 e 100%; casca de aveia, nas proporções de 15, 30 e 100%; e adesivos, nas proporções de 10, 12 e 14%, bem como a combinação entre ambos, em cada uma das variáveis respostas (propriedades físico-mecânicas) avaliadas. Os resultados apontaram excelentes propriedades físico-mecânicas, em alguns casos muito superiores aos requisitos estipulados pelas normas nacionais e internacionais. Desta maneira, ficou comprovado o bom desempenho dos painéis de partículas produzidos, além de sua compatibilidade para aplicações em indústrias, como de móveis, painéis, embalagens e na construção civil. / Wood-based panels have been widely used around the world, replacing solid wood in various segments of the industry, such as furniture, panels, structures and other building components. The large volume of waste generated by agro industry enables the development of alternative and sustainable materials, highlighting the particleboard. This paper presents a study about production and evaluation of particleboard of Eucalyptus grandis and oat hulls, bonded under pressure with two types of resins (polyurethane based on castor oil and urea formaldehyde). Physical-mechanical performance of the panels produced was evaluated based on ABNT NBR 14810:2006. A variance analysis (ANOVA) evaluated the factors influence: Eucalyptus grandis, with mass ratios of 70, 85 and 100%; oat hulls, in proportions of 15, 30 and 100%; adhesives, in proportions of 10, 12 and 14%, and the combination of both, in each of the response variables (physical and mechanical properties) evaluated. Results showed excellent physical-mechanical properties, in some cases much higher than national and international codes requirements. Thus, panel particles good performance was proved, in addition to its compatibility with applications in wood industries, such as furniture, panels, packaging and in building construction.
|
13 |
Avaliação das propriedades mecânicas e reológicas de composições de borracha nitrílica vulcanizadas com resina fenólica / Avaliação das propriedades mecânicas e reológicas de composições de borracha nitrílica vulcanizadas com resina fenólica / Evaluatin of mechanical and rheological properties of vulcanized nitrile rubber compositions with phenolic resin / Evaluatin of mechanical and rheological properties of vulcanized nitrile rubber compositions with phenolic resinJosé Luiz Leite Sanchez 26 June 2008 (has links)
Neste trabalho de Dissertação de Tese, composições do copolímero de butadieno-acrilonitrila (NBR) foram vulcanizadas utilizando como agentes de vulcanização, a resina fenólica e o enxofre, com diferentes proporções de resina fenólica e uma única proporção de enxofre. O sistema ativador foi composto por policloropreno e óxido de zinco para as composições com resina fenólica, enquanto que por ácido esteárico e óxido de zinco para a composição com enxofre. Os materiais foram vulcanizados em uma temperatura de 190C. Foi avaliada a influência da variação dos componentes das composições sobre as propriedades reométricas, físico-mecânicas e reológicas dos materiais. Para auxiliar na interpretação dos resultados obtidos para as propriedades reométricas e físico-mecânicas, foi utilizado um planejamento estatístico de análise de variância para verificar a possibilidade da influência das variáveis e suas possíveis combinações nas propriedades avaliadas. Para as composições vulcanizadas com resina fenólica, os resultados mostraram que a composição de borracha nitrílica se tornou mais rígida com a presença da resina. Também foi observada a ocorrência de pós-cura nas composições vulcanizadas com resina fenólica. Os ensaios reológicos revelaram uma homogeneidade nas amostras submetidas aos testes de varredura de deformação, com desvio de linearidade a partir de 10% de deformação. / In this Thesis Dissertation, acrylonitrile-butadiene rubber (NBR) compositions were vulcanized using phenolic resin and sulfur as vulcanization agents with different proportions of phenolic resin and only one proportion of sulfur. The activator system was composed of polycloroprene and zinc oxide to phenolic resin compositions, while stearic acid and zinc oxide to sulfur composition. The materials were vulcanized in a temperature of 190C. The influence of the components content on rheometric, physico-mechanical and rheological properties of the materials was evaluated. In order to assist in the interpretation of the to physico-mechanical and rheometric properties results, a statistical planning of variant analysis was used to observe a possible influence of the variables and also their possible associations into the evaluated properties. The results showed that the nitrile rubber become more stiffness with the presence of phenolic resin. It was also observed the occurrence of post-vulcanization on the compositions vulcanized with phenolic resin. The rheological results showed homogeneity of the samples submitted to a strain sweep test, with a linear plateau until 10% of strain.
|
14 |
Avaliação das propriedades mecânicas e reológicas de composições de borracha nitrílica vulcanizadas com resina fenólica / Avaliação das propriedades mecânicas e reológicas de composições de borracha nitrílica vulcanizadas com resina fenólica / Evaluatin of mechanical and rheological properties of vulcanized nitrile rubber compositions with phenolic resin / Evaluatin of mechanical and rheological properties of vulcanized nitrile rubber compositions with phenolic resinJosé Luiz Leite Sanchez 26 June 2008 (has links)
Neste trabalho de Dissertação de Tese, composições do copolímero de butadieno-acrilonitrila (NBR) foram vulcanizadas utilizando como agentes de vulcanização, a resina fenólica e o enxofre, com diferentes proporções de resina fenólica e uma única proporção de enxofre. O sistema ativador foi composto por policloropreno e óxido de zinco para as composições com resina fenólica, enquanto que por ácido esteárico e óxido de zinco para a composição com enxofre. Os materiais foram vulcanizados em uma temperatura de 190C. Foi avaliada a influência da variação dos componentes das composições sobre as propriedades reométricas, físico-mecânicas e reológicas dos materiais. Para auxiliar na interpretação dos resultados obtidos para as propriedades reométricas e físico-mecânicas, foi utilizado um planejamento estatístico de análise de variância para verificar a possibilidade da influência das variáveis e suas possíveis combinações nas propriedades avaliadas. Para as composições vulcanizadas com resina fenólica, os resultados mostraram que a composição de borracha nitrílica se tornou mais rígida com a presença da resina. Também foi observada a ocorrência de pós-cura nas composições vulcanizadas com resina fenólica. Os ensaios reológicos revelaram uma homogeneidade nas amostras submetidas aos testes de varredura de deformação, com desvio de linearidade a partir de 10% de deformação. / In this Thesis Dissertation, acrylonitrile-butadiene rubber (NBR) compositions were vulcanized using phenolic resin and sulfur as vulcanization agents with different proportions of phenolic resin and only one proportion of sulfur. The activator system was composed of polycloroprene and zinc oxide to phenolic resin compositions, while stearic acid and zinc oxide to sulfur composition. The materials were vulcanized in a temperature of 190C. The influence of the components content on rheometric, physico-mechanical and rheological properties of the materials was evaluated. In order to assist in the interpretation of the to physico-mechanical and rheometric properties results, a statistical planning of variant analysis was used to observe a possible influence of the variables and also their possible associations into the evaluated properties. The results showed that the nitrile rubber become more stiffness with the presence of phenolic resin. It was also observed the occurrence of post-vulcanization on the compositions vulcanized with phenolic resin. The rheological results showed homogeneity of the samples submitted to a strain sweep test, with a linear plateau until 10% of strain.
|
15 |
Produção e avaliação do desempenho de painéis de partículas de Eucalyptus grandis confeccionados com adição de casca de aveia / Production and performance evaluation of particleboard made from Eucalyptus grandis addition of oat hullsLuciano Donizeti Varanda 10 July 2012 (has links)
Os painéis à base de madeira vêm sendo amplamente utilizados em todo o mundo, em resposta à redução de oferta de madeira maciça em diversos segmentos da indústria madeireira, como em móveis, painéis, estruturas e outros componentes na construção civil. O grande volume de resíduos gerados pela agroindústria viabiliza o desenvolvimento de materiais alternativos e sustentáveis, destacando-se os painéis de partículas. Este trabalho apresenta um estudo da produção e avaliação de painéis de partículas de Eucalyptus grandis e casca de aveia, aderidas sob pressão com dois tipos de resinas (poliuretana à base de mamona e ureia formaldeído). O desempenho físico-mecânico dos painéis produzidos foi avaliado com base na ABNT NBR 14810:2006. Por meio de análise de variância (ANOVA), avaliou-se a influência dos fatores adotados: madeira de Eucalyptus grandis, com proporções mássicas de 70, 85 e 100%; casca de aveia, nas proporções de 15, 30 e 100%; e adesivos, nas proporções de 10, 12 e 14%, bem como a combinação entre ambos, em cada uma das variáveis respostas (propriedades físico-mecânicas) avaliadas. Os resultados apontaram excelentes propriedades físico-mecânicas, em alguns casos muito superiores aos requisitos estipulados pelas normas nacionais e internacionais. Desta maneira, ficou comprovado o bom desempenho dos painéis de partículas produzidos, além de sua compatibilidade para aplicações em indústrias, como de móveis, painéis, embalagens e na construção civil. / Wood-based panels have been widely used around the world, replacing solid wood in various segments of the industry, such as furniture, panels, structures and other building components. The large volume of waste generated by agro industry enables the development of alternative and sustainable materials, highlighting the particleboard. This paper presents a study about production and evaluation of particleboard of Eucalyptus grandis and oat hulls, bonded under pressure with two types of resins (polyurethane based on castor oil and urea formaldehyde). Physical-mechanical performance of the panels produced was evaluated based on ABNT NBR 14810:2006. A variance analysis (ANOVA) evaluated the factors influence: Eucalyptus grandis, with mass ratios of 70, 85 and 100%; oat hulls, in proportions of 15, 30 and 100%; adhesives, in proportions of 10, 12 and 14%, and the combination of both, in each of the response variables (physical and mechanical properties) evaluated. Results showed excellent physical-mechanical properties, in some cases much higher than national and international codes requirements. Thus, panel particles good performance was proved, in addition to its compatibility with applications in wood industries, such as furniture, panels, packaging and in building construction.
|
16 |
Aproveitamento de resíduo de soja para produção de painéis MDP (Medium Density Particleboard) / Use of soybean residue for production of MDP panels (Medium Density Particleboard)Guimarães, Íngrid Luz 23 March 2017 (has links)
Submitted by Erika Demachki (erikademachki@gmail.com) on 2017-06-29T22:20:43Z
No. of bitstreams: 2
Dissertação - Ingrid Luz Guimarães - 2017.pdf: 1402447 bytes, checksum: 7d2b3bc12c14d9a3bd34392e4f9d7049 (MD5)
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2017-07-10T10:46:04Z (GMT) No. of bitstreams: 2
Dissertação - Ingrid Luz Guimarães - 2017.pdf: 1402447 bytes, checksum: 7d2b3bc12c14d9a3bd34392e4f9d7049 (MD5)
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2017-07-10T10:46:05Z (GMT). No. of bitstreams: 2
Dissertação - Ingrid Luz Guimarães - 2017.pdf: 1402447 bytes, checksum: 7d2b3bc12c14d9a3bd34392e4f9d7049 (MD5)
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Previous issue date: 2017-03-23 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / Soybean pre-cleaning residue is found in large quantities in the processing and processing
dryers' farms, resulting in serious inconvenience if it is not removed to farther places before the
fermentation process begins. Among the residues generated at the time of harvesting and cleaning
of the grains are soybean pods, which presents as an alternative lignocellulosic material to be used
in the production of Agglomerated panels of the MDP type. The objective of this work was to
verify the effect of the use of soybean pods in the production of eucalyptus MDP panels. The
panels, with a nominal density of 0.70 g / cm³, were composed of three layers, the thin layers of
eucalyptus wood were used in the covers and the core was composed of a mixture of eucalyptus
particles and soybean pods. The proportions used of soybean residue particles in relation to those
of eucalyptus in the kernels were 0, 25, 50, 75 and 100%. For the glueing of the particles the
adhesive urea formaldehyde, in the proportion of 12%, was used for both the covers and the crumb.
The pressing cycle had a temperature of 160 ° C for a period of 15 minutes at a pressure of 4MPa.
To evaluate the quality of the panels produced, their physical and mechanical properties of
apparent density; Compaction ratio; Water absorption and swelling in thickness at 2 and 24 hours
of immersion were determinater; Perpendicular traction; Modulus of elasticity and modulus of
rupture in the static bending. To meet the requirements of Brazilian standard (NBR 14.810 / 2002),
for the properties of swelling in thickness (2h) and modulus of rupture, the maximum amount of
soybean recommended for MDP panels is 20%. / O resíduo da pré-limpeza de soja é encontrado em grande quantidade no pátio das
indústrias de beneficiamento e dos secadores das fazendas, acarretando sérios transtornos
caso não seja removido para locais mais afastados antes que o processo de fermentação se
inicie. Dentre os resíduos gerados no momento da colheita e limpeza dos grãos estão às
vagens de soja, que se apresenta como um material lignocelulósico alternativo para ser
utilizado na produção de painéis aglomerados do tipo MDP. Este trabalho teve como objetivo
verificar o efeito da utilização de vagens de soja na produção de painéis MDP de eucalipto. Os
painéis, com densidade nominal de 0,70 g/cm³, foram constituídos por três camadas, de
modo que nas capas foram utilizadas finas partículas de madeira de eucalipto e o miolo foi composto por uma mistura de partículas de eucalipto e de vagens soja. As proporções
utilizadas de partículas de resíduo de soja em relação às de eucalipto no miolo foram de 0,
25, 50, 75 e 100%. Para o encolamento das partículas foi utilizado o adesivo uréia
formaldeído, na proporção de 12%, tanto para as capas como para o miolo. O ciclo de
prensagem teve temperatura de 160°C, por um período de 15 minutos a uma pressão de
4MPa. Para avaliar a qualidade dos painéis produzidos, foram determinadas suas propriedades
físicas e mecânicas de densidade aparente; razão de compactação; absorção de água e
inchamento em espessura em 2 e 24 horas de imersão; tração perpendicular; módulo de
elasticidade e módulo de ruptura na flexão estática. Para atender as exigências da norma
brasileira (NBR 14.810/2002), para as propriedades de inchamento em espessura (2h) e
módulo de ruptura, a quantidade máxima de vagem de soja recomendada para painéis MDP é
de 20%.
|
17 |
Caracterização anatômica da matéria-prima e avaliação das propriedades tecnológicas de painéis MDF de madeira de Schizolobium amazonicum Huber ex Ducke e de resíduos de espécies da Amazônia. / Anatomical characterization and evaluation of technological properties MDF manufactured from wood Schizolobium amazonicum Huber ex Ducke and waste native species of the AmazonVictor Cezar Nepomuceno Ribeiro 22 January 2015 (has links)
Estudos sobre a qualidade tecnológica de painéis MDF produzidos a partir de madeiras nativas da Amazônia ainda são escassos. O presente estudo teve como objetivo principal determinar a qualidade de painéis MDF produzidos com a madeira de Schizolobium amazonicum Huber ex Ducke, em forma de resíduos de lâminas e toras (LAM e TOR, respectivamente), e resíduos de espécies nativas da Amazônia (MIX). A partir destas matérias-primas foram produzidos cavacos, fibras e painéis MDF numa unidade industrial de MDF. Na manufatura dos painéis foram adotados 06 tratamentos. Os tratamentos adotados foram analisados por meio de 03 experimentos independentes: Experimento 1 - verificar o efeito da proporção de matéria-prima (25% TOR -75% MIX; 40% LAM - 75% MIX; 40% LAM - 60% MIX) nas propriedades físicas e mecânicas dos painéis; Experimento 2 - para verificar o efeito da espessura (12 e 15 mm) nas propriedades físicas e mecânicas dos painéis; Experimento 3 - também para verificar o efeito da espessura (15 e 18 mm) nas propriedades físicas e mecânicas dos painéis. Os painéis MDF foram colados com 13% de resina a base de ureia-formaldeído e 0,7% de emulsão de parafina. Posteriormente, corpos-de-prova foram obtidos dos painéis MDF para avaliação da massa específica, teor de umidade, absorção de água, inchamento em espessura, módulo de ruptura, módulo de elasticidade, resistência da ligação interna, resistência ao arracamento de parafuso na face e no topo, conduzidos conforme a norma NBR 15316 (ABNT, 2009). Adicionalmente, foi realizada a caracterização das fibras de TOR, LAM e MIX antes e após o desfibramento industrial dos cavacos e determinado o perfil de densidade dos painéis por meio da técnica de atenuação de raios-X. Para verificar o efeito das variáveis sobre as propriedades das chapas MDF foi realizada uma análise de variância e, posteriormente, o teste de Tukey, conduzido ao nível de 5% de probabilidade de erro. Mediante a análise dos resultados dos ensaios, concluiu-se que: No Experimento 1, os painéis MDF manufaturados com a mistura de fibras das madeiras na proporção B apresentaram melhor desempenho nas propriedades de APT e APF, e os painéis na proporção C desempenho superior no MOR. No Experimento 2, os painéis de 12 mm mostraram melhor desempenho nas propriedades de LI e APF, e os painéis de 15 mm melhor desempenho em AA2h, AA24h e IE24H; No Experimento 3, os painéis MDF de 18 mm exibiram melhor desempenho nas propriedades de IE2h, IE24h, MOR e MOE à flexão estática. Os painéis de 15 mm tiveram melhor desempenho nas propriedades de APT e APF. Com exceção dos valores da propriedade de LI, todos os painéis MDF avaliados no presente estudo atenderam aos valores requeridos pela norma NBR 15316-2 (ABNT, 2009), para fabricação de móveis a serem utilizados em condições secas. / Studies about the technological quality of MDF manufactured with wood of native species from Amazon are scare. This study aimed to evaluate the quality of MDF produced with wood Schizolobium amazonicum Huber ex Ducke, waste of veneer and log (LAM and TOR, respectively) and waste of native species from Amazon (MIX). The chips, fibers and MDF, from this material, were produced in an industrial unit MDF. In the manufacture of panels 06 treatments were adopted. The following treatments were analyzed by 03 independent experiments: Experiment 1 - to verify the effect of the proportion of raw material (25% -75% TOR MIX; LAM 40% - 75% MIX; LAM 40% - 60% MIX) on the physical and mechanical properties of the panels; Experiment 2 - to verify the effect of thickness (12 and 15 mm) on the physical and mechanical properties of the panels; Experiment 3 - also, to verify the effect of the thickness (15 and 18 mm) on the physical and mechanical properties of the panels. The MDF panels were bonded with 13% of resin based on urea formaldehyde and 0.7% paraffin emulsion. Posteriorly, samples were obtained to conduct the moisture content, bulk density, water absorption and thickness swelling, modulus of rupture, modulus of elasticity, internal bonding, resistance to face screw-holding and edge screw-holding, tests according to NBR 15316 (ABNT, 2009). Additionally, was characterized the TOR, LAM and MIX fibers, performed before and after industrial refining chip and determined the density profile of the MDF using the technique of X-ray attenuation. To check the effect of variables on the properties of MDF an analysis of variance was performed, and subsequently the Tukey test, conducted at the 5% level of error probability. Through the analysis of tests results it was conclude: In Experiment 1, MDF panels manufactured with a mixture of wood fiber in the ratio B showed better performance in the properties of APT and APF, and the panels in C ratio showed superior performance in MOR. In Experiment 2, the panels of 12 mm showed better performance in the properties of LI and APF, and 15 mm panels perform better in AA2h, AA24h and IE24H; In Experiment 3, the panels of 18 mm panels exhibited better performance on the properties of IE2h, IE24h, MOR and MOE in static bending. 15 mm panels outperformed the properties of APT and APF. With the exception of property values LI, all MDF panels evaluated in this study met the required values by NBR 15316-2 (ABNT, 2009), for the manufacture of furniture to be used in dry conditions.
|
18 |
PROPRIEDADES TECNOLÓGICAS DA MADEIRA DE Tetrorchidium rubrivenium Poeppig & Endlicher / TECHNOLOGICAL PROPERTIES OF Tetrorchidium rubrivenium Poeppig & Endlicher WOODGuma, Rosana Lamana 28 February 2013 (has links)
Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / This work aims to describe the wood anatomy, study the physical characteristics and verify its variation along the tree height, and determine the mechanical properties of Tetrorchidium rubrivenium (Euphorbiaceae) wood, to identify possible uses of this material. Tetrorchidium rubrivenium, of popular name canemaçu, is an arboreal species of Euphorbiaceae botanical family, Crotonoideae subfamily, which is a native species poorly studied. Five trees of this specie were cut in Vale do Sol, Rio Grande do Sul State, Brazil. Environmental license for obtainment of this material was issued according current legislation. Samples of this material were prepared for confection of histologic and quantitative fiber slides, used to describe wood anatomy. Predetermined sized samples were also prepared for the following tests: green and basic specific density, green moisture content, radial and tangential shrinkage, shear, parallel and perpendicular compression, hardness, static and impact bending. The canemaçu wood is composed mostly by fibers and rays, and in lower portion by axial parenchyma and vessels. These anatomic characters agree with expected features for canemaçu family and subfamily. Basic specific density of wood was 0.4062 g/cm3, and presented significant relationship with the position in relation to commercial height of the tree. Similar relationship was found with green specific density, green water content and radial and tangential wood shrinkages. The wood of canemaçu presented low mechanical resistance for parallel compression, hardness and static bending, and median shear resistance. The mechanical properties of canemaçu wood were also related with specific density at 12% moisture and significant relationship was observed with perpendicular compression, radial and tangential hardness, modulus of elasticity, modulus of rupture, work to maximum load in bending and resilience coefficient. Predictive models in function of specific density at 12% moisture were adjusted for these mechanical properties. In according with results of this study, the wood of canemaçu is appropriate to be used on furniture, particleboard, crates and general packaging, and on the manufacture of decorative items, internal finishing and toys. / O presente trabalho tem objetivo de descrever a anatomia da madeira de Tetrorchidium rubrivenium (Euphorbiaceae), estudar as características físicas verificando sua variação ao longo da árvore e determinar suas propriedades mecânicas, a fim de identificar possíveis usos do material. Tetrorchidium rubrivenium, popularmente chamado de canemaçu, é uma espécie arbórea pertencente à família botânica Euphorbiaceae, subfamília Crotonoideae e que ainda é uma espécie nativa pouco estudada. Foram utilizadas cinco árvores coletadas no interior de Vale do Sol, RS. Foi expedida licença ambiental para a obtenção do material, conforme legislação vigente. Amostras do material foram trabalhadas para confeccionar lâminas histológicas e para quantificação de fibras, utilizadas para a descrição anatômica da madeira. Confeccionaram-se também corpos de prova de dimensões pré-estabelecidas para realização dos seguintes testes: massa específica verde e básica, teor de umidade verde, contrações radial e tangencial, cisalhamento, compressão paralela e perpendicular, dureza, flexão estática e resistência ao choque. Constatou-se que o lenho do canemaçu é composto em sua maior parte por fibras e raios e em menor percentual parênquima axial e vasos. As características anatômicas são condizentes com o esperado para a família e subfamília que o canemaçu pertence. A madeira possui massa específica (ME) básica média de 0,4062 g/cm³, esta apresenta relação significativa com a altura comercial da árvore. Relações significativas também foram encontradas entre a ME verde, o teor de umidade verde e as contrações radial e tangencial com a posição em relação à altura comercial da árvore. A madeira apresentou baixa resistência mecânica para compressão paralela, dureza e flexão estática, e resistência mediana para cisalhamento. As propriedades mecânicas foram relacionadas com a ME a 12% de umidade, verificando-se significância com a compressão perpendicular, dureza radial e tangencial, módulo de elasticidade, módulo de ruptura, trabalho absorvido e coeficiente de resiliência. Para estas propriedades, foram ajustados modelos para predição dos respectivos valores a partir da ME. A madeira de canemaçu mostra-se apta para a utilização em móveis, chapas aglomeradas, caixotaria e embalagens em geral, e na confecção de objetos de decoração, acabamento interno e brinquedos.
|
19 |
Análise do desempenho do painel de madeira compensada produzido com lâminas termorretificadas por dois diferentes métodos e coladas com resina poliuretana. /Galdino, Danilo Soares. January 2020 (has links)
Orientador: Cristiane Inácio de Campos / Resumo: Nos últimos anos, o estudo do tratamento térmico na indústria madeireira vem chamando a atenção dos pesquisadores por ser mostrar como uma proposta de preservação sustentável em comparação aos tratamentos químicos tradicionalmente realizados. Com base nisto, este trabalho teve por objetivo avaliar o desempenho do painel compensado produzido com lâminas termorretificadas e coladas com a resina poliuretana à base de óleo de mamona, uma alternativa para substituição do adesivo fenol-formaldeído, que possui a vantagem de ser de origem natural e de não liberar substâncias nocivas ao homem e ao meio ambiente. O processo de termorretificação foi realizado em três diferentes temperaturas (160, 180 e 200°C) e para duas formas de tratamento (prensa e estufa). As alterações ocorridas nas lâminas, após o tratamento, foram avaliadas por meio de testes de rugosidade, utilizando um perfilômetro, e de molhabilidade pelo método de gota, utilizando um goniômetro, os quais mostraram que com o aumento da temperatura as lâminas ficaram menos rugosas e molháveis. O método prensa se mostrou mais efetivo para realizar a termodegradação da madeira na análise do teor de extrativos totais realizado seguindo a norma TAPPI T-257:2012. As alterações verificadas na lâmina impactaram as propriedades físico-mecânicos do painel acabado que foram avaliadas por meio de ensaios recomendados por documentos normativos brasileiros: massa específica aparente (ABNT NBR 9485:2011), inchamento em espessura (ABNT NBR 95... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: In recent years, the study of heat treatment in the wood industry has been attracting the attention of researchers as a proposal for sustainable use compared to the traditionally performed chemical methods. Based on this, this work aimed to evaluate the performance of plywood panel produced with heat-treated veneers and glued with a castor oil-based polyurethane resin, an alternative to replace the phenol-formaldehyde adhesive. The advantage of using polyurethane resin is its natural origin and do not release harmful substances to man and the environment. The heat treatment process was carried out at three different temperatures (160, 180 and 200 ° C) and for two forms of treatment. The changes occurred in the veneers, after treatment, were evaluated by roughness tests and wettability, using a goniometer. As the temperature increased, the veneers became less rough and wettable. The press method proved to be more effective to perform the thermo-degradation of wood in the analysis of the total extractive content carried based a TAPPI T-257: 2012 norm. The changes verified in the veneer impacted the physical-mechanical properties of the finished panel, which were evaluated through tests recommended by Brazilian normative documents: density (ABNT NBR 9485: 2011), thickness swelling (ABNT NBR 9535: 2011), moisture (ABNT NBR 9484: 2011), water absorption (ABNT NBR 9486: 2011 ), static bending test (ABNT NBR 9533: 2013) and glue shear strength (ABNT NBR ISO 12466-1: 2012). It was fo... (Complete abstract click electronic access below) / Mestre
|
20 |
PROPRIEDADES FÍSICO-MECÂNICAS E RESISTÊNCIA A BIODETERIORADORES DE CHAPAS AGLOMERADAS CONSTITUÍDAS POR DIFERENTES PROPORÇÕES DE MADEIRA E CASCA DE ARROZ / PHYSICAL-MECHANICAL PROPERTIES AND DECAY RESISTANCE OF WOOD AND RICE HUSK PARTICLEBOARD IN DIFFERENT PROPORTIONSMelo, Rafael Rodolfo de 06 March 2009 (has links)
Conselho Nacional de Desenvolvimento Científico e Tecnológico / This work aimed at evaluating the quality of particleboards manufactured with different wood proportions (Eucalyptus grandis W. Hill. ex Maiden) and rice husk. The composites were produced in the proportions 0, 20, 40, 60, 80 and 100% of peels of rice with the use of urea-formaldehyde and tannin-formaldehyde adhesives. In order to characterize the quality of the particleboards, physical properties (specific mass; moisture content; water absorption and swelling in thickness after 2 and 24 hours), mechanical resistance (static bending; internal bonding and screw withdrawal) and xylophages resistance (Nasutitermes corniger under alimentary preference assay and decay fungi Gloeophyllum trabeum and Trametes versicolor in laboratory conditions) were evaluated. Results showed that particleboards manufactured with tannin-formaldehyde resins presented a higher quality. The increase of rice husk provided a larger instability and a smaller resistance of the particleboards. Particleboards produced with peels of rice presented a higher resistance to the attack of fungi or xylophages termites. Particleboards glued with tannin-formaldehyde were more resistant to the attack of termites; for the fungi, the difference among adhesives happened when these particleboards were submitted to the attack of Gloeophyllum trabeum, and the particleboards produced with urea-formaldehyde were the most resistant. In the fungi, Trametes versicolor was the fungus that provided the largest mass loss to the particleboards. / Avaliou-se a qualidade de painéis aglomerados produzidos com diferentes proporções de madeira (Eucalyptus grandis W. Hill. ex Maiden) e casca de arroz. Os compósitos foram produzidos nas proporções 0, 20, 40, 60, 80 e 100% de casca de arroz com a utilização dos adesivos ureia-formaldeído e tanino-formaldeído. Para caracterizar a qualidade das chapas, foram avaliadas as propriedades físicas (massa específica; teor de umidade; absorção de água e inchamento em espessura as 2 e 24 horas), a resistência mecânica (flexão estática; ligação interna; e resistência ao arrancamento de parafusos) e a resistência a xilófagos (aos cupins subterrâneos Nasutitermes corniger, em ensaios de preferência alimentar e aos fungos apodrecedores Gloeophyllum trabeum e Trametes versicolor em ensaios de laboratório). Os resultados obtidos indicaram que quando confeccionados utilizando a resina à base de tanino os painéis apresentaram qualidade superior. O acréscimo da casca de arroz proporcionou uma maior instabilidade e uma menor resistência das chapas. Em contrapartida, painéis produzidos com casca de arroz geralmente apresentaram maior resistência ao ataque de fungos apodrecedores ou aos cupins subterrâneos. Painéis colados com tanino-formaldeído foram mais resistentes ao ataque dos térmitas, enquanto que, para os fungos, a diferença entre adesivos ocorreu apenas quando submetidas ao ataque de Gloeophyllum trabeum, sendo as chapas produzidas com ureia-formaldeído as mais resistentes. Dentre os fungos, Trametes versicolor proporcionou uma maior perda de massa aos painéis.
|