Orientador: Marcelo Coelho Goiato / Abstract: The purpose of this study was to analyse the influence of time exposure to the environmental factors, chemical disinfection with 2% chlorhexidine-based solution and two distincts pigments about dimensional changing and maintenance of details of two silicones for use in maxillofacial prosthesis. Thirty specimens were fabricated for each silicone using a matrix, conformed closely to the specifications for nonaqueous, elastomeric dental impression materials established by the Revised American Dental Association n° 19 and the ISO 4823:1984. Specimens were separated in three groups: control (colourless), pigmented with commercial cosmetic (makeup powders) and pigmented with iron oxid. Specimens were analysed in a comparator microscopic (Carl Zeiss) and stereoscopic loupe. The readings were realized after polymerization of the specimens, and after 30 and 60 days, with and 157 without disinfection. The data were submited to the statistic analysis, by the Tukey's Test. The results indicated that all groups presented contraction; the chemical disinfection only changed the dimensional stability of the Silastic cosmetic pigmented group; the dimensional stability of Silastic was affected after 60 days of exposition in all groups. For the Brascoved silicone, the chemical disinfection only didn't have influence about dimensional stability in initial period; the exposition factor had influence about the dimensional stability of Brascoved in all periods and groups. The details were maintained in all specimens for both silicones, independent of the exposition time, of the pigments or disinfection. / Mestre

Resumo: O dióxido de carbono (CO2) é um importante gás de efeito estufa. No entanto, um aumento gradual ameaça substancialmente o clima. Um dos principais desafios do planejamento ambiental é identificar um modelo que vincule todos os fatores do ciclo de carbono, ou seja, oceano - ecossistema terrestre - emissão antropogênica - atmosfera. Princípios básicos de Termodinâmica podem ser aplicados em uma modelagem estatística com bases em séries históricas para obter concentrações de CO2 na atmosfera, possibilitando a construção de cenários para uma melhor tomada de decisões. Por este motivo, foi desenvolvido no trabalho um modelo que interliga todos os fatores do ciclo de carbono, focalizando em quatro zonas térmicas ou climáticas (Boreal, Temperada, Tropical, Polar), para cálculos de armazenamento de CO2 atmosférico. Os resultados mostram que no ano 2100 se atingirá uma concentração de CO2 quatro vezes maior do que antes do período pré-industrial. A zona temperada emite quase a metade de dióxido de carbono à atmosfera na atualidade; para o ano 2100, essa emissão aumentará a quinze vezes mais que a zona tropical. A China será responsável em uma proporção de vinte quatro a onze com relação aos Estados Unidos. A estabilização das concentrações de CO2 na atmosfera será obtida quando as emissões de dióxido de carbono antropogênico tiverem uma diminuição de mais do que trinta e quatro por cento para o ano 2100 na zona temperada. / Abstract: Carbon dioxide (CO2) is the most important greenhouse gas. A gradual increase on its atmospheric concentration threatens significantly the climate. One of the main challenges of environment planning is to identify a model that connects all factors that determine the carbon cycle, that is, ocean - terrestrial ecosystem - anthropogenic emissions - atmosphere. Basic thermodynamic principles can be applied in a statistical modeling with historic time series to obtain atmospheric CO2 concentration, creating the possibility of construction of scenarios that will help decision making. A model that links all carbon cycle factors was developed in this dissertation work, focusing in four thermal of climatic zones (Boreal, Temperate, Tropical, and Polar) for calculations of atmospheric CO2 storage. Results show that in 2100, the atmospheric CO2 concentration will reach a value four times higher than that of the pre-industrial period. The temperate zone already emits almost half of the carbon dioxide to the atmosphere; by 2100, this emission will increase 15 times more than that corresponding to the tropical zone. China will be responsible for emissions in a proportion of 24 to 11 in comparison to that of the United States. Stabilization of CO2 concentrations in the atmosphere will be obtained when the anthropogenic carbon dioxide emissions attain a decrease of at least 34% in 2100 in the temperate zone. / Orientador: Sérgio João Crnkovic / Coorientador: Humberto Lopes Rodrigues / Banca: Antonio Jorge Abdalla / Banca: Marcelo dos Santos Pereira / Banca: Sandra Giacomin Schneider / Banca: Leonardo Gonçalves Cunha / Doutor

Orientador: João Roberto Gonçalves / Banca: Ary dos Santos-Pinto / Banca: Roberto Henrique Barbeiro / Banca: Darceny Zanetta Barbosa / Banca: Terumi Okada / Resumo: Este estudo avaliou a resposta do tecido mole, do espaço faríngeo e a estabilidade após avanço maxilo-mandibular com rotação anti-horária e reconstrução da ATM com próteses totais articulares do tipo TMJ Concepts system®. As mudanças cirúrgicas e pós-cirúrgicas foram analisadas utilizando-se telerradiografias laterais. Com o movimento cirúrgico, houve redução do ângulo do plano oclusal (14,9 ± 8,0°) e aumento do espaço aéreo faríngeo - PASnar (4,9mm). A região anterior da maxila moveu-se para a frente e para cima enquanto a porção posterior, para a frente e para baixo. A mandíbula avançou, e sofreu rotação no sentido anti-horário. No período pós-cirúrgico, a maxila apresentou alterações mínimas no plano horizontal, enquanto todas as medidas mandibulares permaneceram estáveis. A postura da cabeça (OPT/NS) mostrou flexão imediatamente após a cirurgia e extensão em longo prazo, enquanto a curvatura cervical (OPT/CVT) não apresentou mudanças. Os resultados cirúrgicos mostraram ainda aumento das distâncias entre a terceira vértebra cervical (C3) e o mento e desta com o hióide, permanecendo estáveis durante o período de observação. A distância entre o osso hióide e o plano mandibular reduziu durante e após a cirurgia. Já a resposta do tecido mole evidenciou diferentes razões entre tecido duro/mole nos pacientes com e sem genioplastia. As mudanças horizontais na morfologia do lábio superior após avanço, impacção da maxila, sutura em VY e sutura da base alar mostraram maior movimento do que as mudanças observadas em tecido duro. O avanço maxilo-mandibular com rotação anti-horária do plano oclusal associado a próteses totais de ATM (TMJ Concepts system®) mostrou-se estável durante o período de observação. O espaço aéreo faríngeo aumentou... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: This study evaluated stability, soft tissue response and oropharyngeal airway space changes after maxillo-mandibular advancement and counter-clockwise rotation with TMJ reconstruction using TMJ Concepts system® total joint prostheses. Lateral cephalograms were analyzed to estimate surgical and post surgical changes. During surgery, the occlusal plane angle decreased 14.9 ± 8.0° and the retroglossal airway space (PASnar) increased 4.9mm. The anterior region of maxilla moved forward and upward while the posterior nasal spine moved downward and forward. The mandible changed forward and rotated in a counter-clockwise direction. At long-term follow-up evaluation the maxilla showed minor horizontal changes, while all mandibular measurements remained stable. Head posture (OPT/NS) showed flexure immediately after surgery and extension long-term post surgery, while cervical curvature (OPT/CVT) had no significant changes. Surgery increased the distances between the third cervical vertebrae (C3) and menton, and C3 and hyoid, remaining stable afterwards. The distance from the hyoid to the mandibular plane decreased during surgery and in the longest follow-up. Soft tissue response indicated different hard/soft tissue ratios between patients with or without genioplasties. Horizontal changes in upper lip morphology after maxillary advancement/impaction, VY closure, and alar base cinch sutures showed greater movement, than observed in hard tissue. TMJ Concepts total joint prostheses associated with maxillo-mandibular advancement and counter-clockwise rotation showed to be stable during the follow-up observation period. Immediate increase in oropharyngeal airway dimension, was influenced by post-surgical changes in head posture but remained stable over the follow-up period. Soft tissue changes showed a known predictable response. / Doutor

Orientador: Eulália Maria Martins da Silva / Banca: Wirley Gonçalves Assunção / Banca: Paulo Henrique dos Santos / Banca: Osvaldo Luiz Bezzon / Banca: Paulo Martins Ferreira / Resumo: Os protocolos estabelecidos numa técnica de fundição objetivam compensar a contração de solidificação da liga metálica e obter estruturas metálicas fundida com adequada adaptação cervical. A técnica de fundição rápida tem demonstrado ser uma alternativa, mas há dúvidas sobre como os revestimentos se expandem. Este estudo comparou as expansões de presa, térmica e total de três revestimentos odontológicos perante os procedimentos realizados em técnicas de fundição convencional e rápida. Na primeira parte desse estudo, determinaram-se as curvas das expansões resultantes da reação exotérmica de presa (n=5/revestimentoXtécnica), juntamente com as curvas de temperaturas que permitiram determinar o pico da exotermia e o intervalo médio requerido por cada revestimento para atingí-lo e; na segunda parte, aferiu-se a expansão térmica (n=3/revestimento). Para a análise estatística, utilizou-se o ANOVA e o Teste de Tukey (p<0,05). O maior valor médio de temperatura durante a presa foi determinado para o revestimento Micro Fine 1700 (88oC), que não diferiu estatisticamente do Heat Shock (80,3oC) e o menor, para o All Therm (67oC). O Micro Fine 1700 foi o que atingiu seu pico máximo de temperatura mais precocemente (5,8min), seguido pelo Heat Shock (16,4min) e o All Therm (18,8min), sendo todos diferentes entre si (p<0,05). Pôde-se constatar que os três revestimentos avaliados atingiram seus respectivos picos de temperatura num tempo menor ou igual a 20 minutos. Quanto à expansão de presa, para os revestimentos fosfatados foi muito menor no tempo de 20 minutos (tempo de espera para presa na técnica de fundição rápida) em comparação ao que se obteve com 60 minutos; o que não ocorreu, estatisticamente, para o revestimento cerâmico Micro Fine 1700. Só o revestimento cerâmico Micro Fine 1700 apresentou sua expansão de presa estabilizada aos 20 minutos. / Abstract: The protocols established in casting techniques aimed to compensate the solidification contraction of metallic alloy and to get casting metallic structures with accurate marginal fit. The accelerated casting technique has demonstrated to be an alternative, but some doubts regarding investment expansion remains. This study compared the curves of temperatures resultant setting expansion and expansions of setting, thermal and total of three dental investments before the conventional and accelerated casting techniques. In the first part of this study, the curves of the resultant expansion of the setting exothermic reaction (n=5/investment) were determined, together with the curves of temperatures. Based on theses temperatures curves either the maximum exothermic setting reaction temperature, and the mean time interval required for each investment were calculated. In the second part, thermal expansion (n=3/investmentXtechnique) was analyzed. ANOVA and Tukey Test were used as a statistic analysis at 5% level of significance. Micro Fine 1700 investment showed the highest temperature values during the setting (88oC), and did not differ significantly from the Heat Shock (80.3oC) (p>.05). All Therm exhibited lower values (67oC) that differed from the two other investments (p<.05). Micro Fine 1700 reached the maximum exothermic setting reaction temperature first (5.8min), followed by Heat Shock (16.4min) and All Therm (18.8min) (p<.05). It can be evidenced that the three investments had reached their temperature peak until 20 minutes. The setting expansions of the phosphate bonded investments were very lower in the time of 20 minutes (wait time for setting in the accelerated casting technique) in comparison to 60 minutes. However, this difference did not occur to Micro Fine 1700 ceramic investment (p>.05). Analyzing thermal expansion, only Heat Shock showed statistic difference regarding technique factor. / Doutor

Orientador: Ana Lucia Machado / Banca: Ana Cláudia Pavarina / Banca: Luiz Antonio Pessan / Resumo: Este estudo avaliou o efeito de tratamentos da superfície de união e de materiais reembasadores na resistência ao impacto de uma resina para base de prótese. Corpos-de-prova foram confeccionados com a resina Lucitone 550 (60x6x2 mm) e reembasados (2 mm) com o mesmo material (L) ou com as resinas para reembasamento imediato Tokuso Rebase (TR) e Ufi Gel Hard (UH). Para o material L, as superfícies de união permaneceram sem tratamento (L/L/ST) ou foram tratadas com o monômero da resina L (metil metacrilato) for 180 segundos (L/L/M). Quando o reembasamento foi realizado com os reembasadores imediatos, os tratamentos de superfície consistiram de aplicação dos agentes adesivos fornecidos pelos fabricantes (L/TR/A - diclorometano e L/UH/A - diclorometano e 2-hidroxietil metacrilato) ou tratamento com o monômero da resina L seguido pelos adesivos (L/TR/MA e L/UH/MA). Corpos-de-prova do material L intacto (60x6x4 mm) também foram confeccionados para se determinar a resistência ao impacto dessa resina. Um total de 140 corpos-de-prova foi confeccionado, sendo 20 para cada condição experimental. Para metade dos corpos-de-prova, os entalhes foram realizados na largura, na superfície correspondente ao material reembasador, com profundidade de 0,8 mm, permanecendo 3,2 mm de material intacto (E1). Para os corpos-de-prova restantes, o entalhe foi realizado na espessura, envolvendo tanto o material reembasador como a resina de base, com profundidade de 1,2 mm (E2), permanecendo 4,8 mm de material intacto. Todos os entalhes, em forma de V, foram realizados na área central do comprimento dos corpos-de-prova. O teste utilizado foi do tipo Charpy, com pêndulo de 0,5 J e distância de 50 mm entre os suportes. Os resultados (kJ/ m2) de cada entalhe foram analisados, separadamente, utilizando-se ANOVA e teste de ...(Resumo completo, clicar acesso eletrônico abaixo) / Abstract: This study evaluated the effect of surface treatments and reline materials on the impact strength of a denture base acrylic resin. Specimens were made using Lucitone 550 resin (60x6x2 mm) and relined (2 mm) with the same material (L) or with the hard chair-side reline resins Tokuso Rebase (TR) and Ufi Gel Hard (UH). For material L, the bond surfaces remained untreated (L/L/ST) or were wetted with resin L monomer (methyl methacrylate) for 180 seconds (L/L/M). When the relining was made with the hard reline materials, the surface treatments consisted of coating with the bonding agents supplied by the manufacturers (L/TR/A - dichloromethane and L/UH/A - dichloromethane and 2-hydroxyethyl methacrylate) or wetting with the resin L monomer followed by bonding agents application (L/TR/MA and L/UH/MA). Material L intact specimens (60x6x4 mm) were also made to determine the impact strength of the bulk resin. A total of 140 specimens were made, 20 for each experimental condition. Half of the specimens were notched across the width to a depth of 0.8 mm, leaving an effective depth under notch of 3.2 mm (E1). For the remaining specimens, the notch was cut across the thickness to a depth of 1.2 mm (E2) leaving an effective depth under notch of 4.8 mm. All the V-notches were machined at the midpoint of the length of the specimens. Impact tests were carried out on a Charpy type pendulum impact tester (0.5 J pendulum; distance between supporting points - 50 mm). Results (kJ/ m2) from each notch depth were analyzed separately using one-way ANOVA and Tukey's HSD tests (a = .05). No significant differences were noted among the mean impact values of L (1.39 kJ/ m2), L/L/ST (1.28 kJ/ m2) and L/L/M (1.20 kJ/ m2) specimens with the E1 notch (P>.05). Similar results were observed (P>.05) for the specimens with the E2 notch (L - 1.00 kJ/ m2; L/L/ST - 0.93 kJ/ m2; ...(Complete abstract, click electronic access below) / Mestre

Orientador: Marcelo Coelho Goiato / Banca: Mitsuru Ogata / Banca: Stefan Fiúza de Carvalho Dekon / Banca: Mário Alexandre Coelho Sinhoreti / Banca: Humberto Gennari Filho / Resumo: O insucesso das próteses faciais é causado pelas limitações das propriedades dos materiais existentes, sendo as mais críticas a flexibilidade e a durabilidade. Uma prótese facial deve ser resistente e ter longa duração, mas se manter suave e flexível para acompanhar os movimentos faciais do paciente. Diante destas considerações, o objetivo desta pesquisa foi o de avaliar a deterioração marginal e a dureza SHORE A de dois silicones para uso em prótese facial - o Silastic 732 R.T.V. e o Silastic MDX4-4210, sob a influência do tempo de armazenagem, da desinfecção diária com clorexidina a 2% e de dois tipos de pigmentação, considerando que sempre houve a necessidade de um material que combinasse a flexibilidade natural da pele humana com durabilidade no seu uso. Foram confeccionados 30 corpos-de-prova para cada material, divididos em 3 grupos: controle (incolor), pigmentados com maquiagem e com óxido de ferro. A análise da deterioração marginal foi realizada em microscópio eletrônico de varredura e o teste de dureza dos materiais foi realizado em durômetro SHORE A, imediatamente, 6 meses e um ano após a confecção dos corpos-de-prova, seguindo as especificações da ASTM. Os dados da dureza foram submetidos à análise estatística, utilizando-se do teste de Tukey com nível de 99% de confiabilidade. Os dois silicones para uso facial apresentaram um aumento da sua dureza SHORE A com o passar do tempo. Entretanto, a dureza SHORE A manteve-se estável no período de 6 meses a 1 ano. Quando os silicones foram comparados entre si, o Silastic 732 R.T.V. mostrou-se estatisticamente mais flexível que o MDX4-4210. Após a análise visual das fotomicroscopias (aumento de 1000x) foi possível perceber que todos os grupos sofreram deterioração marginal e alteração de sua textura superficial com o passar do tempo...(Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Prosthetic failure can be attributed to the inherent problems of the properties of materials, such as flexibility and durability. The maxillofacial prosthesis must be strong and have durability, but must be soft and flexible enough to respond to the facial motions of the patient. The purpose of this study was to analyse the influence of time’s storage, chemical disinfection with 2% chlorhexidine-based solution and two distincts pigments about marginal deterioration and SHORE A hardness of two silicones for use in maxillofacial prosthesis - the Silastic 732 R.T.V. and the Silastic MDX4-4210. Thirty specimens were fabricated for each silicone using a matrix. Specimens were separated in three groups: control (colourless), pigmented with commercial cosmetic (makeup powders) and pigmented with iron oxid. The marginal deterioration analysis was realized in scanning electron microscope (SEM) and the hardness test was realized in a SHORE A durometer, according to ASTM, designation D 2240. The readings were realized after polymerization of the specimens (initial period), after 6 months and 1 year, with and without disinfection. The data of SHORE A hardness were submited to the statistic analysis, by the Tukey’s Test. Both silicones presented an increase of hardness over time. However, the hardness maintained stable at 6 months and 1 year periods. When both silicones were compared, the Silastic 732 R.T.V. showed statistically softer than MDX4-4210. After visual analysis of photomicrocopies (1000x), was possible note that all groups suffered marginal deterioration over time. The chemical disinfection also contributed to marginal deterioration of silicones, independent of time and pigmentation. Subject to the design, materials and methods used in this research, the following conclusions can be drawn:...(Complete abstract, click electronic address below) / Doutor

Resumo: O objetivo do presente estudo foi avaliar alterações ao redor de implantes inseridos em diferentes níveis em relação à crista óssea, e sob diferentes protocolos de restauração. Trinta e seis implantes foram inseridos nas mandíbulas edêntulas de 6 cães. Três implantes foram instalados por hemi-mandíbula, cada qual representativo de um grupo experimental. Estes foram determinados de acordo com a distância entre a junção implante-conector protético (JIC) e a crista óssea: Ao Nível (ao nível da crista óssea), Menos 1 (1mm apical à crista óssea), ou Menos 2 (2mm apical à crista óssea). Cada hemi-mandíbula foi submetida a um protocolo de restauração: convencional (prótese instalada 120 dias após a implantação) ou imediata (prótese instalada 24 horas após a implantação). Parâmetros clínicos, radiográficos, e histométricos foram avaliados após 90 dias de restauração, e os dados foram analisados estatisticamente (alfa=5%). A posição da margem do tecido mole (PTM) não foi influenciada pelo posicionamento apical da JIC; entretanto, sítios submetidos à restauração imediata tiveram a PTM significantemente mais coronal que os submetidos à restauração convencional (p=0,02, análise clínica). A reabsorção do rebordo não foi estatisticamente diferente entre os grupos (p>0,05, análise radiográfica). Menores quantidades de Perda Óssea Lateral (POL) foram observadas nos sítios restaurados imediatamente em comparação com os restaurados convencionamente (p=0,006, análise histométrica). Os presentes achados sugerem que o posicionamento apical da JIC não põe em risco a altura de tecidos periimplantares moles ou duros. Além disto, a restauração imediata foi benéfica para manter a PTM, e minimizar a POL. / Abstract: The aim of the present study was to evaluate changes that occur around dental implants inserted in different levels in relation to crestal bone, under different restoration conditions. Thirty-six implants were inserted in the edentulous mandible of six dogs. Three implants were inserted per hemimandible, each one representing an experimental group according to the distance from the implant-abutment junction (IAJ) to the crestal bone: Bone Level (at crestal bone level), Minus 1 (1mm below crestal bone), or Minus 2 group (2mm below crestal bone). Each hemimandible was submitted to a restoration protocol: conventional (prothesis installed 120 days after implant placement) or immediate (prosthesis installed 24 hours after implant placement). Clinical, radiographic, and histometric parameters were evaluated after 90 days of restoration, and data was analyzed statistically (alpha=5%). The position of soft tissue margin (PSTM) was not influenced by the apical positioning of the IAJ; however, sites submitted to immediate restoration had the PSTM displayed significantly more coronally than those submitted to conventional restoration (p=0.02, clinical analysis). Ridge Loss was not statistically different among groups (p>0.05, radiographic analysis). Greater amounts of Lateral Bone Loss (LBL) were observed for conventionally than for immediately restored sites (p=0.006, histometric analysis). These findings suggest that the apical positioning of IAJ did not jeopardize the height of peri-implantar soft and hard tissues. Moreover, immediate restoration was beneficial to maintain the PSTM, and to minimize LBL. / Orientador: Elcio Marcantonio Junior / Coorientador: Joni Augusto Cirelli / Banca: Roberto Henrique Barbeiro / Banca: Marcio Fernando de Moraes Grisi / Banca: Mário Taba Junior / Banca: Sérgio Luís da Silva Pereira / Doutor

Orientador: Winston Bonetti Yoshida / Banca: Regina Moura / Banca: Carlos Eli Piccinato / Resumo: A migração da endoprótese é uma complicação do tratamento endovascular definida como deslocamento de sua ancoragem inicial. Para avaliação da migração verifica-se a posição da endoprótese em relação à determinada região anatômica. Considerando o aneurisma da aorta abdominal infra-renal, a área proximal de referência consiste na origem da artéria renal mais baixa e, na região distal, situa-se nas artérias ilíacas internas. Os pacientes deverão ser monitorizados por longos períodos a fim de serem identificadas migrações visto que estas ocorrem normalmente após 2 anos de implante. Para se evitarem migrações, forças mecânicas que propiciam fixação e determinadas por características dos dispositivos e a incorporação da endoprótese, devem predominar sobre forças gravitacional e hemodinâmica que tendem a arrastar a prótese no sentido caudal. Angulação, extensão e diâmetro do colo, além da medida transversa do saco aneurismático, são importantes aspectos morfológicos do aneurisma relacionados à migração. Com relação à técnica, o implante de endopróteses com sobredimensionamento excessivo (>30%) não é recomendado por provocar dilatação do colo do aneurisma, além de dobras e vazamentos proximais que também contribuem para migração. Por outro lado, endopróteses com mecanismos adicionais de fixação (ganchos, farpas e fixação supra-renal) parecem estar menos associadas às migrações. O processo de incorporação das endopróteses ocorre parcialmente e parece não ser suficiente para impedir migrações tardias. Neste sentido, estudos experimentais com endopróteses de maior porosidade e uso de substâncias que permitam maior fibroplasia e aderência da prótese à artéria vem sendo realizados e parecem ser promissores. Nesta revisão estes aspectos serão discutidos, em especial o uso da cola de fibrina. / Abstract: Migration of the endoprosthesis is a complication of the endovascular treatment defined as misplacement of its initial fixation. In order to assess such migration, one shall verify the position of the endoprosthesis in relation to the determined anatomic site. Considering the aneurysm of the infra-renal abdominal aorta, the proximal area of reference consists on the origin of the lowest renal artery and, at the distal region, it is located next to the internal iliac arteries. Patients shall be monitored for long periods so that migrations can be spotted; these migrations usually occur 2 years after the implant. To avoid migration mechanical forces that enable fixation and that are determined by features of devices as well as the incorporation of the endoprosthesis have to predominate over gravitational and hemodynamic forces, which tend to drag the prosthesis toward to caudal direction. Angulation, extension and diameter of the neck, and transversal measure of the aneurysmatic sac, are important morphological aspects related to migration. In relation to technique, the implant of endoprosthesis with excessive oversizing (>30%) is not recommended because it leads to aortic neck dilatation, folds and proximal leaking witch contribute to its migration. On the other hand, endoprosthesis with additional fixation devices (hooks, barbs and supra-renal fixation) seem to be less associated with migration. The process of incorporation of the endoprosthesis occurs partially and does not seem to be enough to prevent later migrations. In this sense, experimental assessment with higher porosity endoprosthesis as well as the use of substances that allow higher fibroplasia and adherence of the prosthesis to the artery have been made and look promising. In this review, such aspects are discussed, specially the use of fibrin glue. / Doutor

Orientador: Marcelo Coelho Goiato / Coorientador: Daniela Micheline dos Santos / Banca: Simone Cecílio Hallak Regalo / Banca: Stefan Fiuza Carvalho Dekon / Resumo: As próteses oculares são responsáveis pela recuperação da estética e auto-estima do usuário. Assim, os materiais utilizados na confecção de prótese ocular devem possuir propriedades específicas para sua indicação e durabilidade. Desse modo, é importante avaliar o comportamento destes materiais quando influenciados por diversas soluções desinfetantes. Este estudo teve como objetivo avaliar a microdureza, rugosidade superficial e alteração de cor de próteses oculares sobre a influência da desinfecção química e armazenagem. Foram confeccionadas 50 amostras simulando próteses oculares contendo duas resinas acrílicas (N1 e incolor), distribuídas em cinco grupos de acordo com o desinfetante utilizado: sabão neutro (I), opti-free (II), efferdent (III), hipoclorito a 1% (IV) e clorexidina a 4% (V). As amostras foram armazenadas por 120 dias, sendo desinfetadas durante este período. As leituras de microdureza, rugosidade e cor das amostras foram realizadas em um período inicial (B) e após 60 (T1) e 120 (T2) dias de armazenagem com desinfecção. A microdureza foi mensurada por meio de um microdurômetro, e a rugosidade determinada por um rugosímetro. A leitura de cor foi realizada por meio da espectrofotometria de reflexão, usando o sistema CIE L*a*b*. A alteração de cor (ΔE) foi calculada para os períodos entre T1 e B (T1B), e T2 e B (T2B). Pelos resultados obtidos a resina N1 para esclera apresentou menor microdureza estatisticamente significante, comparada a resina incolor (P<0,05). A maior alteração dos valores de microdureza e rugosidade foi obtida para os grupos IV e V. Ambos os períodos de desinfecção e armazenagem produziram alterações significativas (P<0,05) nas amostras com diminuição dos valores de... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Ocular prostheses are responsible to restore not only patient's aesthetic but also its self-esteem. The materials used to fabricate the ocular prostheses should present specific properties regarding its indication and durability. Therefore, it is important to investigate the physical behavior of such materials when subjected to different disinfectant solutions. This study evaluated the microhardness, surface roughness and color stability of ocular prostheses under the influence of different chemical disinfectant solutions and storage. A total of 50 samples simulating an ocular prosthesis containing two acrylic resins (N1 and colorless) were fabricated. They were divided into five groups as a function of disinfectant solution: neutral soap (I), opti-free (II), efferdent (III), 1% hypochlorite (IV) and 4% chlorhexidine (V). Samples were storage during 120 days, and they were disinfected throughout the period. Microhardness, roughness and color measurements were performed at baseline (B), after 60 (T1) and 120 (T2) days of storage with disinfection. The microharness and the roughness measurements were evaluated using a microdurometer and a roughness meter, respectively. Samples colors were measured with spectrophotometer using CIE L*a*b* system. Color differences (ΔE*) were calculated for periods between T1 and B (T1B), and T2 and B (T2B). The N1 acrylic resin exhibited statistically lower microhardness when compared to the colorless acrylic resin (P<0.05). The highest microhardness and roughness alterations were observed for groups IV and V. Both disinfection and storage periods statistically reduced the microhadness values and increased the roughness values of the samples (P<0.05). Color alteration was... (Complete abstract click electronic access below) / Mestre

Resumo: Os implantes dentais têm sido usados extensivamente para a reabilitação de edentulismo total e parcial, com próteses fixas ou removíveis. Em detrimento das suas taxas de sucesso e previsibilidade, falhas ocorrem e são associadas a complicações biomecânicas. Entre os fatores biomecânicos podemos destacar uma proporção adequada entre comprimento do implante e superestrutura. Porém, pouco é encontrado sobre a influência da altura da coroa, o alcance do braço de alavanca e, conseqüentemente, a tensão no osso cortical e no osso trabecular. Apesar do aumento no uso de implantes, muito pacientes que necessitam dessa terapia ficam limitados devido à pouca altura óssea. Sistemas disponibilizam no mercado implantes curtos, onde procedimentos cirúrgicos invasivos poderiam ser evitados; nesses implantes, porém, é muito comum uma relação coroa/área implantada invertida. Desenvolveremos este trabalho em dois capítulos. O primeiro irá avaliar a influência de três alturas de coroas pré-estabelecidas, quando associadas a implantes de hexágono externo em todas as suas estruturas associadas. No segundo, avaliaremos a influência das mesmas alturas de coroas, associadas a implantes de hexágono externo e cone - morse, na distribuição das tensões no tecido ósseo. Para a primeira parte do trabalho, foram confeccionados três modelos tridimensionais, com auxilio dos programas de modelagem gráfica SolidWorks 2006 e Rhinoceros 4.0, além do programa InVesalius (CTI, São Paulo, Brasil), utilizado para gerar o modelo ósseo a partir de uma tomografia computadorizada. Cada modelo foi composto por um bloco ósseo, com um implante de 3,75 x 10,00mm (Conexão Sistemas de Prótese, São Paulo), com o tipo de conexão: hexágono externo, utilizando três alturas de coroas (10 mm; 12.5 mm e 15 mm), colocadas na plataforma oclusal (hexágono externo). Após geração ... (Resumo completo, clicar acesso eletrônco abaixo) / Abstract: The dental implants have been widely used for rehabilitation of partial and complete edentulism using fixed and removable prostheses. Despite the success rate and predictability, failures are reported and commonly associated with biomechanical complications. Among the biomechanical factors, an adequate proportion between the implant and superstructure dimensions should be established. However, there is little information about the influence of crown height and lever arm on stress in cortical and trabecular bone. Although the use of implants has increased, many patients are limited by insufficient bone height. Thus, some implant systems developed short implants to avoid invasive surgical procedures. Nevertheless, such implants present an inverted crown/anchored area ratio. The present study will be divided into two chapters. The first one will evaluate the influence of three pre-established crown heights attached to external hexagon implants on all structures. In the second chapter, it will be evaluated the influence of the same crown heights attached to external hexagon and morse taper implants on the stress distribution in bone tissue. Initially, three 3D models were fabricated using the softwares SolidWorks 2006 and Rhinoceros 4.0. The software InVesalius (CTI, Sao Paulo, Brazil) was also used to generate the bone model through a computed tomography. Each model was composed by a bone block with an external hexagon implant (3.75 X 10.0 mm) (Conexao Sistemas de Protese, Sao Paulo) and a crown with different heights (10 mm, 12.5 mm and 15 mm) attached to the implant platform (external hexagon). After generation of the geometries, the models were imported to the software FEMAP 10.0 (Siemens PLM Software Inc., USA) for pre- and post-processing of finite elements to generate the meshes as well as the loading and boundary conditions. Axial load of 200N and oblique load of 100N were ... (Complete abstract click electronic access below) / Orientador: Eduardo Piza Pellizzer / Coorientador: Jorge Vicente Lopes da Silva / Banca: Fellipo Ramos Verri / Banca: Regina Tamaki / Banca: Estevão Tomomitsu Kimpara / Banca: Cátia Maria Fonseca Guerra / Doutor