Orientador: Luiz Felipe Mendes de Moura / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-01T19:59:17Z (GMT). No. of bitstreams: 1 Munhoz_AndreLuizJardini_D.pdf: 12745922 bytes, checksum: 60932586deb959236f4b7fbbc4c9dcd3 (MD5) Previous issue date: 2001 / Resumo: Neste trabalho, apresenta-se a aplicação da radiação infravermelha do laser para se obter a cura localizada em resinas termosensíveis usadas para a estereolitografia. Este método permite criar modelos sólidos tridimensionais utilizando a tecnologia do laser para curar (solidificar) regiões localizadas no material através do confinamento da energia na área irradiada. Várias indústrias já empregam o laser na região espectral do ultravioleta (HeCd @0,325 ~m) para construir estruturas tridimensionais. Neste trabalho, o laser de CO2 (10,6 ~) foi focalizado na amostra composta (em peso) de 10 partes de resina epóxi, 1,4 partes de dietileno triamina e 0,7 partes de sílica em pó. Esta resina termo sensível cura, ou solidifica, quando aquecida moderadamente e os resultados mostram que pode-se confinar o aquecimento do material, curando-o em três dimensões. Um modelo físico teórico foi aplicado para descrever o fluxo de calor na cura e para predizer ambas a localização e a taxa de cura em função das condições de irradiação. Usando o calorímetro diferencial de varredura (DSC) pode-se determinar as taxas de cura em função da temperatura e do tempo, a entalpia envolvida na reação e a energia de ativação do processo. de cura. Para simular o fluxo de calor na amostra em função das condições de irradiação foi aplicada a solução da equação geral de condução de calor dependente do tempo em coordenadas cilíndricas utilizando o método de elementos [mitos do programa genérico Ansy' s. Os resultados deste trabalho são de importância nos estudos futuros envolvendo técnicas de prototipagem rápida para a confecção de moldes e modelos tridimensionals via sistemas CAD / Abstract: We present in this work the use of infrared laser radiation to anchieve localized curing in thennosensitive polymers. In stereolithography the objective is to cure a localized region in a material by precisely confining the laser energy to the area that is to be cured. Industry already employs high-power ultraviolet laser radiation (HeCd laser @ 0,352 ~m) to fabricate three dimensional structures. In our experiments, we have focused the beam from a infrared radiation (C02 laser @ 10,6 J.1IIl) onto a sample composed of epoxy resin, diethylene triamine (curing agents) and silica powder (filler). Such resins typically cure, or solidify, when heated to moderately high temperature and our results show that we can confine the heating of the material, and, therefore, its curing, in all three dimensions. U sing a differential scanning calorimetry (DSC) we were able to determine reaction rates as a function of the temperature as well as the enthalpy involved in the phase transition and the activation energy of the curing process. A physical theoretical model is applied to control the parameters which influence the confinement of the curing in the" irradiated bulk. A numerical model is applied too, to model the heat flow in our sample as a result of infrared laser radiation through the resolution of the heat conduction equation dependent on time in cylindrical co-ordinates of the Ansy' s program. The results allow us to predict the curing behavior of the sample as a function of laser irradiation conditions, and we find good agreement with our preliminary experimental observatories. Prototypes has been constructed layer by layer and experimental results of the production of solid layers of thickness 10-1-10-2 mm in two and three dimensions are presented. / Doutorado / Termica e Fluidos / Doutor em Engenharia Mecânica

Orientador: Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T18:18:44Z (GMT). No. of bitstreams: 1 Santos_PauloHenriquedos_D.pdf: 3793254 bytes, checksum: 6011c2ab4379291315d38e0287f59ace (MD5) Previous issue date: 2003 / Doutorado

Orientadores: Lourenço Correr Sobrinho, Mario Fernando de Goes / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T18:58:40Z (GMT). No. of bitstreams: 1 Schneider_Rafael_D.pdf: 4169182 bytes, checksum: cafd4b192bbf13608316a7db0fd6c734 (MD5) Previous issue date: 2003 / Doutorado

Orientador: Renata Cunha Matheus Rodrigues Garcia / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T23:50:31Z (GMT). No. of bitstreams: 1 Faot_Fernanda_M.pdf: 6708746 bytes, checksum: 4a7e71f63273a71d6f27c36a33d30baa (MD5) Previous issue date: 2004 / Mestrado / Protese Dental / Mestre em Clínica Odontológica

Made available in DSpace on 2014-06-12T22:59:21Z (GMT). No. of bitstreams: 2 arquivo8475_1.pdf: 1786366 bytes, checksum: 2ad5cbffb66f7f93dbcd127502abfaf9 (MD5) license.txt: 1748 bytes, checksum: 8a4605be74aa9ea9d79846c1fba20a33 (MD5) Previous issue date: 2004 / O objetivo desta pesquisa foi avaliar in vitro a influência da carga mecânica na infiltração marginal de restaurações classe II confeccionadas com o sistema restaurador adesivo Filtek Z-250®. Utilizaram 16 pré-molares humanos hígidos, com raízes completamente formadas, que tiveram o terço apical e superfície oclusal seccionados. Foram confeccionadas cavidades, com término cervical em cemento, sendo os espécimes restaurados, identificados aleatoriamente e divididos em 4 grupos. Todos os espécimes do primeiro foram mantidos em água destilada a 37°C, enquanto os espécimes dos grupos restantes sofreram ciclagem mecânica sob 8Kgf(quilograma força) por 100.000, 250.000 e 500.000 ciclos, respectivamente. Todos os elementos foram levados à termociclagem em temperatura variando entre 5°C (±5°C) e 55°C (±5°C) durante 500 ciclos e submersos em fucsina básica a 0,5%. Os espécimes foram avaliados com auxílio de lupa estereoscópica, com um aumento de 40 vezes, e os resultados, analisados através do teste de Kruskal-Wallis com p>0,05. Estes demonstraram que os espécimes submetidos apenas à termociclagem apresentaram grau 1 de infiltração marginal, enquanto os submetidos a ambas as ciclagens demonstraram maior quantidade de corpos-de-prova infiltrados e maiores escores de infiltração. Concluiu-se que a associação da ciclagem térmica à mecânica provocou efeitos negativos à interface dente/restauração de cavidades classe II restauradas com compósitos, embora os resultados não sejam estatisticamente significativos

Orientador: Monica Campos Serra / Dissertação (mestrado) - Universidade Esatdual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-24T19:47:05Z (GMT). No. of bitstreams: 1 Basting_RobertaTarkany_M.pdf: 5364710 bytes, checksum: fb93ea48edd3f4d2de1426ce80e72d18 (MD5) Previous issue date: 1999 / Resumo: Propriedades dos materiais híbridos de ionômero de vidro/resina composta têm sido extensamente analisadas, podendo-se observar que os testes laboratoriais são os mais utilizados como metodologia de pesquisa. O objetivo deste trabalho foi avaliar a dureza superficial in situ de materiais híbridos de ionômero de vidro/resina composta em função do tempo após a fotopolimerização, através de uma metodologia que possa predizer o desempenho clínico dos materiais. Foram analisados cinco materiais: Fuji II LC / GC Corporation (Fu), Vitremer / 3M (Vi), Freedom / SDI (Fr), Dyract / Dentsply (Dy) e Z 100/ 3M (Zl). Um dispositivo acrílico intra-bucal palatal foi confeccionado para cada um dos 24 voluntários participantes do experimento, no qual foi fixado um corpo de prova de cada material. Os tempos estudados foram: 30 min, 1 h, 2 h, 4 h, 8 h, 24 h, 48 h, 7 dias, 10 dias, 14 dias, 17 dias e 21 dias após a fotopolimerização. A Análise de Variância, seguida do teste de Tukey ao nível de 1%, mostrou diferenças significativas de dureza entre todos os materiais (Fu < Vi < Fr < Dy < ZI) até 48 horas. A partir do sétimo até o décimo quarto dia;, não se verificaram diferenças estatísticas entre os materiais Fr e Dy (Fu < Vi < Fr = Dy < Zl). No décimo sétimo e vigésimo primeiro dias, os materiais Vi, Fr e Dy apresentaram igualdade estatística, diferindo dos demais (Fu < Vi = Fr = Dy < Zl). A regressão polinomial mostrou um aumento de dureza em função do tempo para cada um dos materiais híbridos, exceto para o material Z 1. A metodologia in situ utilizada permitiu concluir que houve um aumento da dureza superficial de todos os híbridos de ionômero de vidro/resina composta testados em função do tempo após fotopolimerização, embora houvesse diferenças de dureza entre esses materiais / Abstract: The properties of glass-ionomer / hybrid composite resin materiaIs have been widely analyzed and laboratory tests are used more as a research methodology. The purpose of this paper was to evaluate the superficial hardness of glass-ionomer / composite resin hybrid materiaIs in situ at different post-iITadiation times, by means of a methodology that can predict the clinical performance of the materiaIs. Four hybrid materiaIs were analyzed: Fuji rI li,C / GC Corporation (Fu), Vitremer / 3M (Vi), Freedom / SDI (Fr) and Dyract / Dentsply (Dy). One composite was used as a control group: Z 100 / 3M (ZI). Palatal intra-oral acrylic appliances were made for each one ofthe 24 volunteers in the experiment. In each appliance, a specimen of each material was fixed. Microhardness testing was performed at 30 min, 1 h, 2 h, 4 h, 8 h, 24 h, 48 h, 7 days, 10 days, 14 days, 17 days and 21 days after initial Iight-curing. The Analysis of Variance, folIowed by the Tukey test, showed significant dift'erences of hardness among alI materiaIs (Fu < Vi < Fr < Dy « ZI) up to 48 hours. From t.he seventh to the fourteenth day, statistical differences were not found between Freedom and Dyract (Fu < Vi < Fr = Dy < ZI). On the seventeenth and twenty-first days, Vitremer, Freedom and4Dyract presented statistical equality, but differed ITom the others (Fu < Vi = Fr = Dy < ZI). The polynomial regression showed an increase of hardness over time for the hybrid materiaIs, but not for the composite. The in situ methodology used allowed the conclusion to be reached that there was an increase in the superficial hardness of alI the glass-ionomer / composite resin hybrid materiaIs tested at each post-irradiation time, although there were differences of hardness among these materiaIs / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientador: Altair Antoninha Del Bel Cury / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-25T09:43:13Z (GMT). No. of bitstreams: 1 Ganzarolli_SolimarMaria_M.pdf: 8627151 bytes, checksum: c3d5f90a3acf2ab8334bd573c19f4a36 (MD5) Previous issue date: 1999 / Resumo: A adaptação das bases de prótese evita a formação de hiperplasias, e mantém uma adequada função mastigatória. A presença de porosidade pode levar à um acúmulo de Cândida albicans, e diminuição da resistência da prótese. Foi propósito deste trabalho avaliar a adaptação e porosidade de 72 bases de prótese, confeccionadas com resina acrílica termopolimerizável convencional Clássico e resinas para polimerização em forno de microondas, Acron-MC e Onda Cryl, quando submetidas ao procedimento de resfriamento brusco, e convencional das mesmas após polimerizadas. A avaliação foi realizada imediatamente após a demuflagem e após um período de armazenagem por 30 dias. Os métodos utilizados para verificação da desadaptação foram: a) Peso de silicona de adição (Express-3M) interposto entre a base de resina e o modelo metálico. b) Medida da desadaptação entre o interior da base de resina e a superfície do modelo de gesso, em 09 pontos diferentes do rebordo. A porosidade foi avaliada pelo peso de cada amostra, em balança de precisão de 0,001g. Os resultados obtidos foram submetidos a ANOV A, e verificou-se com o teste de Tuckey que o resfriamento convencional permitiu a melhor adaptação das bases de prótese e os procedimentos de resfriamento brusco não interferiram na porosidade da resina / Abstract: Good adaptation of denture bases avoids hyperplasic formations and provides an adequate masticatory function. Porosity can lead to microorganisms growing, Cândida albicans, and decrease of denture base strength. The aim of this study was to evaluate the adaptation and porosity of 72 denture base made with Clássico conventional heat-cured acrylics resins and microwave-activated resins, Acron-MC and Onda Cryl, when submited to bench cooling. Adaptation assessment was performed immediately after deflasking and after 30 days storage period. The methods used were: a) Weight measured of addition silicon (Express-3M) liner between the denture base and the metallic model; b) microscopic linear measurement between the inner part of the denture base and the plaster cast model, in 9 different points on the residual ridge and palate. Porosity was evaluated by weight of each silicon base acrylic resin using a precision scales with 0,001g accuracy. Data were analyzed with ANOVA and Tuckey's test. Conventional cooling technique presented the best denture base adaptation and the fast cooling procedure did not have influence in resin porosity / Mestrado / Protese / Mestre em Clínica Odontológica

Orientador: Altair Antoninha Del Bel Cury / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-25T11:05:35Z (GMT). No. of bitstreams: 1 Braun_KatiaOlmedo_D.pdf: 4956224 bytes, checksum: 08e169d63e08d6d20fe8eb879fa0237a (MD5) Previous issue date: 1999 / Resumo: Este estudo avaliou o efeito do polimento químico sobre a liberação de monômero residual, dureza superficial, resistência transversa e a textura de superfície de resinas auto e termopolimerizáveis, comparando-o com o polimento mecânico. As amostras foram confeccionadas em resinas termopolimerizável Clássico e autopolimerizável JET -Clássico e divididas em 4 grupos: G1- resina autopolimerizável com polimento mecânico; G2 - resina autopolimerizável com polimento químico; G3 - resina termopolimerizável com polimento mecânico; G4resina termopolimerizável com polimento químico. Após os polimentos recebidos as amostras foram imersas em água destilada à temperatura de 37°C e as avaliações executadas nos períodos de 1, 2, 8 e 32 dias. A liberação do monômero foi realizada em espectrofotômetro BEKMAN OU 65; a dureza Knoop foi medida com microdurômetro SHIMAOZU HMV 2000; a resistência transversa por três pontos em uma máquina de ensaio universal EMIC OL 500, seguindo a especificação n° 12 da AOA. Os resultados foram submetidos a ANOVA (p=5%) sendo as médias do monôn:tero residual e dureza Knoop comparadas com o teste de comparação de médias não paramétrico e as de resistência transversa com o teste t ao nível de significância de 5%. Concluiu-se que: - o polimento químico aumentou a quantidade de monômero residual e reduziu os valores de dureza superficial das duas resinas de maneira significativa em todos os períodos estudados; O polimento químico não interferiu na resistência transversa da resina auto e' termopolimerizável. Na avaliação feita com MEV verificou-se que o polimento químico altera a camada superficial das duas resinas promovendo um aspecto ondulado semelhante / Abstract: Although chemical polishing of dental acrylic resins have became a very used alternative, very litlle is known about tt:1e effect on the properties of acrylic resin. This study evaluated the effect of this polishing on the residual monomer release in the water, microhardness, transverse resistence and surface texture of heat and a could curing resins, comparing the results obtained with mechanical polishing. The specimens were made and divided into 4 groups: G1- Self-curing resins with mechanical polishing; G2- Self-curing resins with chemical polishing; G3- Heat-curing resins with mechanical polishing; G4- Heat-curing resins with chemical polishing. Afier having undergone to polishing the specimens were imerse on destiled water 37°C and the evaluations were made in 1, 2, 8 and 32 days. Monomers released in the water was evaluated with espectrophotometricaly; the Knoop micro-hardness was measured with Shimadzu a micro-hardness teste r ; the transverse resistance was measured by three points in a EMIC DL a universal machine, following ADA specification n° 12 . According to statistical analysis, it was concluded that : - chemical polishing have significantly increased the amount of residual monomers of' both resins in ali periods of time studied and have reduced the superficial hardness of them ali periods; chemical polishing had not interfered on transverse resistance of self-curing and of heat-curing resin. Through evaluation whit SEM it was checked that chemical polishing altered the superficial layer of both resins, promoting a wavy formo / Doutorado / Protese / Doutor em Clínica Odontológica

Orientador: Luiz Andre Freire Pimenta / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-25T11:04:02Z (GMT). No. of bitstreams: 1 LucaFraga_LuciolaRangelde_D.pdf: 4533837 bytes, checksum: c3aefadacd05d68165389ba5cbcd8b8b (MD5) Previous issue date: 1999 / Resumo: Este trabalho avaliou clinicamente, por um período de 33 meses, dois materiais híbridos de ionômero de vidro/resina composta, quando utilizados como sei antes de fóssulas e fissuras. Os materiais foram aplicados em primeiros molares inferiores de cem crianças da rede pública de ensino da cidade de Piracicaba. Um cimento ionomérico modificado por resina (Vitremer - 3M) foi aplicado em um dos elementos, enquanto uma resina composta modificada por poliácidos (Dyract Dentsply) foi aplicada no dente homólogo. Foi efetuada a análise comparativa dos materiais por meio da avaliação direta de retenção e da capacidade de prevenção de cárie em relação a um grupo controle não selado. Também foram efetuadas avaliações por meio de réplicas em resina epóxica, para a análise do desgaste superficial sofrido por esses materiais no período de tempo em que permaneceram em função na cavidade bucal. Os índices de retenção total foram de 65,9% para o Vitremer e 88,2% para o Dyract, os dados obtidos resultaram em diferença estatística ('X POT. 2¿ = 14,58; p<0,01). Ambos foram capazes de controlar a cárie oclusal quando comparados com o grupo controle (Vitremer 'X POT. 2¿ = 9,27; p<0,01 - Dyract 'X POT. 2¿ = 14,57; p<0,01). O Vitremer e o Dyract não demonstraram diferença estatística entre si ('X POT. 2¿ = 1,06; p>0,05). Quanto ao desgaste superficial, o Dyract demonstrou ser mais resistente em relação ao Vitremer (p<0,01). Ambos os materiais podem ser indicados como selantes de fóssulas e fissuras / Abstract: The aim of this study was to evaluate the clinical performance of two glass ionomer/resin composite hybrid materiais, when applied as pits and fissures sealants, during 33 months. The materiais were applied on mandibular first permanent molars of 100 children registered in public schools at Piracicaba. A resin modified glass ionomer cement (Vitremer -3M) was applied on one side of dental arch, and the same teeth on the other side were sealed with a polyacid modified composite resin (Dyract Dentsply). It was carry out a ,comparative analysis between the materiais by direct evaluation. Examiners documented sealant retention and caries prevention in relation to an unsealed control group. Evaluations were accomplished by examination of epoxi models, to an analysis of the superficial wear of materiais, afier a period of oral function. The rates of complete retention were 65.9% for Vitremer and 88.2% for Dyract. The results, supported by statistical analysis, showed a significant diference between the two materiais ('X POT. 2¿ = 14.58; p<0.01). 80th materiais prevented the oclusal caries (Vitremer 'X POT. 2¿ = 9.27; p<0.01 - Dyract 'X POT. 2¿ = 14.57; p<0.01), do not showed performance estatisticaly diferent ('X POT. 2¿ = 1.06; p>0.05). Dyract showed low superficial wear than Vitremer (p<0.01). The hybrid materiais can be indicate to pit and fissure sealants / Doutorado / Dentística / Doutor em Clínica Odontológica

Orientador: Mario Alexandre Coelho Sinhoreti / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-04T03:44:27Z (GMT). No. of bitstreams: 1 Segreto_DarioRaimundo_M.pdf: 667315 bytes, checksum: f8321716fe38251826ea9b052af1183b (MD5) Previous issue date: 2005 / Resumo: O objetivo deste estudo foi avaliar o efeito da variação da densidade de energia na resistência da união de compósitos odontológicos à estrutura dental, a partir da interação intensidade de luz versus tempo de exposição, com diferentes fontes de luz. Foram confeccionados 260 preparos cavitários classe V em incisivos bovinos, separados em 26 grupos (n = 10) que, na seqüência, foram restaurados com dois compósitos de marcas comerciais diferentes (Z250 - 3M/ESPE e Esthet-X - Dentsplay). As cavidades foram padronizadas (formato de ¿caixa com expulsividade emergente¿ configurando um troncocônico tridimensional com dimensões de 4 x 4 x 2,4 mm) e obtidas com ponta diamantada tronco-cônica 3131 (KG-Sorensen) com ângulo aproximado de 4o, montada em caneta de alta rotação adaptada a uma mesa de coordenadas. As restaurações foram confeccionadas em incremento único sendo a fotoativação realizada com aparelho de lâmpada halógena ou LED emitindo irradiância inicial de 700mW/cm2 e 600mW/cm2 respectivamente. Após o procedimento restaurador, seccionou-se longitudinalmente a coroa, respeitando-se o plano mésio-distal e, em seguida, realizou-se desgaste cuidadoso, via câmara pulpar, da parede axial da cavidade restaurada, com a finalidade de expor totalmente a base menor da restauração. Os corpos-de-prova foram levados à máquina de ensaio universal Instron (modelo 4411) para realização do teste de push-out. A velocidade do teste foi de 0,5mm/min até a ruptura da união e os dados coletados em Kgf foram transformados em MPa e submetidos a análise de variância e comparados pelo teste de Tukey (5%). Os resultados mostraram que o compósito Z250 apresentou médias de resistência da união estatisticamente superiores (p<0,05) tanto para o aparelho de lâmpada halógena quanto para o LED em todas as simulações clínicas estudadas, quando comparado ao Esthet-X. O aparelho LED, para o compósito Z250, proporcionou valores de resistência da união estatisticamente superiores (p<0,05) quando comparados com à lâmpada halógena e para o Esthet-X isso não foi observado. De modo geral, a densidade de energia disponível durante a fotoativação mostrou ter maior influência na resistência da união que intensidade de luz em restaurações com alto Fator-C / Abstract: The aim of this study was to evaluate the effect of the maintenance of the energy density by the light intensity and exposure time modulation, with different light sources, on the bond strength of dental composites to tooth structure. Two hundred and sixty expulsive box shaped Type V cavities (4 x 4 x 2.4mm) had been prepared in selected bovine incisors, which were divided in 26 groups (n=10) restored immediately with two composites of different brands (Z250 - 3M/ESPE and Esthet-X - Dentsply). Cavities were standardized (trapezoidal 3-D box shaped expulsive cavity with 4x4x2.4mm) and prepared with truncated diamond bur # 3131 (KG-Sorensen) with 4 degrees, mounted in air turbine adapted to a specific device. The restorations were bulk filled and light cured with halogen light or LED emitting irradiance of 700mW/cm2 and 600mW/cm2 respectively. After the restorative procedure, the specimens were longitudinally sectioned, respecting the mesiodistal plan. The axial wall of the cavities was ground via pulp chamber to completely expose the smaller base of the restoration. The samples were submitted to push-out test in a universal tester machine Instron (model 4411) with crosshead speed of 0.5mm/min. The data in Kgf were transformed in MPa, which were submitted to ANOVA and means compared by Tukey's test (5%). The results had shown that the composite Z250 presented higher bond strength means compared to Esthet-X in all tested conditions (p< 0.05), as with the halogen light as with LED. Moreover, for the composite Z250, light-curing with LED resulted in higher bond strength compared to halogen light (p< 0.05), what was not verified for Esthet-X. In general, the energy density supplied during light curing showed to be more important than light intensity in the bond strength of restorations with high C-factor / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários