Orientador: Marco Antonio Bottino / Banca: Maria Fidela de Lima Navarro / Banca: Marcos Koiti Itinochi / Banca: Luiz Felipe Valandro Soares / Banca: Clóvis Pagani / Resumo: Este estudo analisou o efeito de 2 diferentes tratamentos de superfície na resistência de união de resinas nanoparticuladas antes e após envelhecimento. Blocos (N=128) das resinas Tetric EvoCeram (TE) (Ivoclar) ou Filtek Supreme (FS) (3M ESPE) foram preparados e divididos em 2 grupos: a) controle (sem envelhecimento); b) termociclagem (TC) (x5000, 5-55°C). Os blocos foram novamente divididos em dois grupos, de acordo com o tratamento de superfície: (1) jateamento com óxido de alumínio modificado pro sílica (CoJet, 3M ESPE)+silano (ESPE-Sil)+ Visiobond, (2) adesivo (A). Para o reparo, a mesma resina usada no substrato (FS ou TE) ou resina microhíbrida (Quadrant Anterior Shine, Cavex-QA) foi utilizada. Os espécimes foram submetidos ao teste de cisalhamento ou microtração (1mm/min). Os dados (MPa'mais ou menos'DP) foram analisados com os testes t-Student, ANOVA dois fatores e Tukey. Ensaio de microtração revelou efeito significante no tipo de resina de substrato (p<0.001) e no envelhecimento (p<0.001). Após TC, resina TE (37,6'mais ou menos'12,0) apresentou resistência a microtração significantemente inferior (p<0.05) a FS (45,7'mais ou menos'12,8). TC diminuiu a resistência de união para TE e FS quando comparado com os grupos controle (49,4'mais ou menos'15,6 e 52,2'mais ou menos'17,1, respectivamente). A resina composta usada para o reparo (TE, FS, QA) não afetou significantemente os resultados (p>0,05). Quando o teste de cisalhamento foi aplicado após TC, espécimes tratados com Cojet associado ao silano aumentaram significativamente a resistência de união para FS (21,5) quando comparado com o adesivo (14,8) (p<0,001), mas para TE o adesivo (22,29) foi mais mais efetivo que o Cojet (13,35) (p>0,05). / Abstract: This study evaluated the effect of 2 different surface conditioning methods on the bond strength of nanofilled composites before and after aging conditions. Blocks (N=160) were prepared from composites namely, Tetric EvoCeram (TE) (Ivoclar) or Filtek Supreme (FS) (3M ESPE) and randomly divided into 2 groups: a) control (no aging); b) thermocycling (TC) (x5000, 5-55°C). The specimens were further assigned to two surface-conditioning methods: (1) Silica-coating (CoJet, 3M ESPE)+silane (ESPE-Sil), (2) Adhesive resin (A). As repair composites either the same material was used as the substrate (FS or TE) or a microhybrid one (Quadrant Anterior Shine, Cavex-QA). The specimens were submitted to either microtensile or shear bond test (1mm/min). Data (MPa'mais ou menos'SD) were analyzed using Student t-test, two-way ANOVA and Tukey's test. Microtensile test showed significant effect of the composite type (p<0.001) and the aging condition (p<0.001). After TC aging, TE composite (37.6'mais ou menos'12) showed significantly lower (p<0.05) microtensile bond strength results than FS (45.7'mais ou menos'12.8). TC decreased the bond strength results both for TE and FS when compared to the non-aged control group (49.4'mais ou menos'15.6 and 52.2'mais ou menos'17.1, respectively). The choice of repair composite (TE, FS, QA) did not significantly affect the results (p>0.05). When shear test was employed on TC aged, repaired specimens, silica coating and silanization significantly increased the bond strength for FS (21.5) when compared to adhesive resin application (14.8) (p<0.001) but for TE, adhesive resin (22.29) was more effective than silica coating (13.35) (p>0.05). / Doutor

Made available in DSpace on 2014-06-11T19:24:08Z (GMT). No. of bitstreams: 0 Previous issue date: 2001-02-22Bitstream added on 2014-06-13T19:10:20Z : No. of bitstreams: 1 campos_lm_me_arafo.pdf: 1694851 bytes, checksum: c552099c9f9895ff873518ab7a91d793 (MD5) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / O objetivo deste estudo foi avaliar in vitro a ocorrência e a largura de fenda na parede cervical através de microscopia eletrônica de varredura, e a microinfiltração marginal em restaurações de classe II com a utilização das resinas compostas Charisma e Solitaire (com a técnica restauradora direta) e o sistema Artglass (com o uso da técnica indireta). Foram utilizados 60 dentes molares permanentes de humanos hígidos e recentemente extraídos nos quais, foram realizados preparos cavitários classe II tipo slot nas faces mesiais cuja a parede cervical localizou-se 1 mm aquém da junção cemento/esmalte (em esmalte), e preparos nas faces distais com a parede cervical ultrapassando em 1mm a junção cemento/esmalte (em cemento). O sistema adesivo Solid bond (Hereaus KULZER) foi padronizado e utilizado com os três materiais restauradores. Os dentes foram divididos em três grupos variando-se Material e Técnica Restauradora, a saber: grupo G1, restaurações com a resina Charisma ;grupo G2, restaurações com a resina Solitaire; e o grupo G3, restaurações com a resina Artglass. As restaurações obtidas foram armazenadas em soro fisiológico por + 370C por 1 semana e posteriormente submetidas ao polimento e ciclagem térmica em água por 200 ciclos em temperaturas de 100 + 20C e 500 + 20C. Os espécimes foram cobertos com Araldite e esmalte de unhas, com margem de 2 mm aquém dos limites das restaurações. Para a análise da microinfiltração os dentes foram imersos em solução de Rodamina B à 0,2% durante 24 horas em estufa à 360C de temperatura. A seguir, os dentes seccionados e analisados em lupa estereoscópica Zeiss por três observadores calibrados através de escores de 0-4. Os resultados foram submetidos às análises não paramétricas de Kruskal-Wallis e Mann-Whitney e demonstraram que nenhum dos materiais e técnicas foram capazes...

Made available in DSpace on 2015-10-24T01:15:12Z (GMT). No. of bitstreams: 1 000475858-Texto+Completo-0.pdf: 569 bytes, checksum: 95c09435c5faf501d607b610fb5734f9 (MD5) Previous issue date: 2015 / The aim of the study was to evaluate the association of different aging methods on bond strength values of composite repair, through the use of shear test. 96 samples of rectangular section were made with the microhybrid composite Point 4 (Kerr) and were divided into 8 groups (n = 12) as follows: (1) immersion in distilled water for 7 days; (2) immersion in distilled water for 30 days; (3) immersion in citric acid for 7 days; (4) immersion in boiling water for 8 hours; (5) immersion in distilled water for 30 days plus immersion in citric acid for 7 days; (6) immersion in distilled water for 30 days plus immersion in boiling water for 8 hours; (7) immersion in citric acid for 7 days plus immersion in boiling water for 8 hours and (8) immersion in distilled water for 30 days plus immersion in citric acid for 7 days plus immersion in boiling water for 8 hours. After going through the designated method of aging the treatment of prerepair was conducted with roughening the surface with sandpaper grain silicon carbide 120 and application of the adhesive system Single Bond 2 (3MESPE) and then made a repair with the same composite resin. The samples were tested in a universal testing machine (EMIC) for the shear bond strength test at a loading speed of 1mm / min. After the failure all samples were evaluated in an increase of 35x stereomicroscope and two samples from each group were evaluated in the SEM as surface after aging and after roughening with sandpaper silicon carbide. The results for evaluation of values in the bond strength test were subjected to statistical test analysis of variance (ANOVA) followed by Tukey test (p <0. 05) and no significant differences between the groups tested were found. The evaluation of failure occurred in stereomicroscope were made in a descriptive way, with all samples of all groups presented cohesive failures in the aged resin. Conclusion: The association of different aging methods does not influence the bond strength values of resin repairs made when the roughening method simulating diamond burs coarse-grained is used pre-repair. / O objetivo do estudo foi avaliar a influência da associação de diferentes métodos de envelhecimento nos valores de resistência de união de reparos de resina composta, através da utilização de teste de cisalhamento. Foram confeccionadas 96 amostras com a resina composta microhíbrida Point 4 (Kerr) de secção retangular que foram divididas em 8 grupos (n=12) sendo: (1) imersão em água destilada por 7 dias; (2) imersão em água destilada por 30 dias; (3) imersão em ácido cítrico por 7 dias; (4) imersão em água em ebulição por 8 horas; (5) imersão em água destilada por 30 dias mais imersão em ácido cítrico por 7 dias; (6) imersão em água destilada por 30 dias mais imersão em água em ebulição por 8 horas; (7) imersão em ácido cítrico por 7 dias mais imersão em água em ebulição por 8 horas e (8) imersão em água destilada por 30 dias mais imersão em ácido cítrico por 7 dias mais imersão em água em ebulição por 8 horas. Após passarem pelo método de envelhecimento designado, foi realizado o tratamento de superfície pré-reparo com asperização com lixa de carbeto de silício de granulação 120 e aplicação do sistema adesivo Single Bond 2 (3MESPE) e então, confeccionado um reparo com a mesma resina composta. As amostras foram testadas em uma máquina de ensaio universal (EMIC) para o teste de cisalhamento a uma velocidade de carregamento de 1mm/min. Após a falha todas as amostras foram avaliadas no estereomicroscópio com aumento de 35x e duas amostras de cada grupo foram avaliadas em MEV quanto à superfície após o envelhecimento e após a asperização com lixas de carbeto de silício. Os resultados para avaliação dos valores no teste de resistência de união foram submetidos ao teste estatístico de análise de variância (ANOVA) seguido do teste de Tukey (p<0,05) e não foram encontradas diferenças significativas entre os grupos testados. A avaliação no estereomicroscópio das falhas ocorridas foram feitas de forma descritiva, sendo que todas as amostras de todos os grupos apresentaram falhas coesivas na resina envelhecida. Conclusão: a associação de diferentes métodos de envelhecimento não influencia nos valores de resistência de união em reparos de resina composta, quando o método de asperização simulando pontas diamantadas de granulação grossa é utilizado pré-reparo.

Made available in DSpace on 2016-04-08T03:07:20Z (GMT). No. of bitstreams: 1 000477933-Texto+Parcial-0.pdf: 595 bytes, checksum: 8ccd12258e81b131d7c7c402a8049829 (MD5) Previous issue date: 2016 / Objectives: The aim of this in vitro study was to compare the maximal load resistance of endodontically treated molars restored with: inlays or onlays of Lava Ultimate, composite resin Z350 XT with or without fiberglass post. Methods: Fifty sound extracted third molars were embedded in acrylic resin and divided into 5 groups (n = 10 per group): H = healthy, ON = onlay, IN = inlay, RC = composite resin, PT = fiberglass post + Z350 XT. The MOD preparations and endodontic treatment were performed. Indirect restorations were made through CAD/CAM CEREC system and cemented with SingleBond Universal and RelyX Ultimate under load of 1 kg. Restorations of RC and PT groups were performed by incremental technique and the two posts in the PT group were horizontally transfixed and bonded with flowable resin. Then, mechanical loading in all samples were performed in 500. 000 cycles at 200 N at a frequency of 1 cycle / second and the maximum load test was performed in a universal testing machine at a speed of 1 mm / min. After the mechanical test, the faults were categorized into pulpal floor fracture (irreparable) and cuspal fracture (repairable).Results: Mean values were (means followed by the same letter show no significant difference to ANOVA and Tukey): RC 1680N ± 454 d; PT 2693N ± 372 bc; ON 2922N ± 774 b; IN 2053N ± 313 cd; H 4514N ± 548 a. The predominant failure pattern for teeth restored with onlays, inlays and direct composite resin with or without post was the irreparable type. Conclusion: Endodontically treated molars restored with transfixed fiberglass post and composite resin have similar fracture resistance to those restored with indirect Lava Ultimate inlay and onlay. Horizontally fiber post restoration has the same efficiency that onlays restoration. / Objetivos: O objetivo deste estudo foi avaliar e comparar in vitro a resistência máxima ao carregamento de molares tratados endodonticamente e restaurados com: inlays ou onlays de Lava Ultimate, resina composta Z350 XT com ou sem pino de fibra de vidro transfixado. Materiais e métodos: Cinquenta terceiros molares hígidos extraídos foram incluídos em acrílico autopolimerizável e divididos em 5 grupos (n = 10 por grupo): H = hígido, ON = onlay, IN = inlay, RC = resina composta, PT = pino de fibra de vidro + Z350 XT. Em seguida, foram realizados os preparos MOD e o tratamento endodôntico. As restaurações indiretas foram confeccionadas através do sistema CAD/CAM CEREC e cimentadas com SingleBond Universal e RelyX Ultimate sob carga de 1 Kg. As restaurações do grupo RC e PT foram realizadas pela técnica incremental e os dois pinos no grupo PT foram transfixados horizontalmente e colados com resina flowable. Após, os corpos de prova foram submetidos a 500. 000 ciclos de fadiga mecânica sob carga vertical de 200 N na frequência de 1 ciclo/segundo. Na sequência, foi aplicado o teste de carga máxima de carregamento em máquina de ensaio universal a uma velocidade de 1 mm/min. Após o ensaio mecânico, as falhas foram categorizadas em fratura de assoalho pulpar (irreparáveis) e fraturas de cúspides (reparáveis).Resultados: Os valores médios obtidos foram (médias seguidas de mesma letra não apresentam diferença estatística para ANOVA e Tukey): RC 1680N ± 454 d; PT 2693N ± 372 bc; ON 2922N ± 774 b; IN 2053N ± 313 cd; H 4514N ± 548 a. O padrão de falha predominante para dentes restaurados com onlays, inlays e resina composta direta com ou sem pino foi do tipo irreparável. Conclusão: Molares endodonticamente tratados e restaurados com pinos de fibra de vidro transfixado e resina composta Z350 XT direta apresentam resistência à fratura similar às restaurações indiretas tipo inlay e onlay de Lava Ultimate. Restaurações com pino transfixado horizontalmente possuem a mesma eficácia que as restaurações onlays.

Orientador: Francisco Pedro Monteiro da Silva Filho / Resumo: Por muitos anos a profissão odontológica tem procurado um material estético para substituir as ligas de amálgama. Recentemente, têm aparecido no comércio as resinas compostas para dentes posteriores indicadas para restaurações onde não há incidência de forças mastigatórias. Tais resinas têm, porém, apresentado falhas, e, entre elas, a infiltração marginal, que tem enorme importância, pois é responsável pela sensibilidade pós-operatória, manchamento e ocorrência de cáries secundárias com consequentes alterações patológicas da polpa. Este trabalho teve a finalidade de estudar ''in vitro'' a infiltração marginal, a nível cervical, de restaurações classe II com as resinas posteriores quimicamente ativadas P10 e fotoativadas P30, em dois tipos de cavidades: convencional e adesiva. Foi verificado também o efeito do condicionamento ácido nesta região. A pesquisa foi realizada em dentes pré-molares recentemente extraídos por motivo ortodôntico, e para obter cavidades padronizadas os preparos foram feitos com a utilização de um microscópio modificado por GABRIELLI e cols.25 Foi utilizado adesivo dentinário (Scotchbond) em todos grupos experimentais. A infiltração foi evidenciada por meio do corante Rodamina B, após ciclagem térmica entre as temperaturas 10°C e 50°C, e analisada seguindo o critério de HIRSCH e WEINREB37, modificado, com auxílio de uma lupa estereoscópica ZEISS com 10 aumentos. Pelos resultados obtidos, pudemos verificar que: 1- Ocorreu infiltração marginal a nível cervical em 77,5% das restaurações de cavidades convencionais e em 47,5% das cavidades adesivas. 2- A maior percentagem de infiltração, independentemente dos fatores em estudo, ocorreu sempre no nível 3, ou seja, com infiltração até a parede axial. 3- Tanto a resina quimicamente ativada quanto a fotoativada permitiram a mesma infiltração. 4- O condicionamento ... / Abstract: For many years the dental profession has sought an esthetic material to replace the amalgam alloys. Recently composite resins for posterior teeth have been introduced into the marketplace. The manufacturers claimed that these materials are indicated for stress-bearing restoration. However. such resins have presented some limitations such as marginal leakage which has great clinical importance because it is responsible for postoperative sensitivity, and occurence of secundary caries followed by pathological changes of the pulp. The purpose of this ''in vitro'' study was to investigate the cervical marginal leakage in class II restorations with chemically cured resin - PlO - and light- cured resin - P30 - in two types of cavities: conventional and adhesive. The effect of acid-etching in this area was also observed. The cavities were prepared in premolar teeth, recently extracted for orthodontic purposes, using a Microscope Modified by GABRIELLI and cols.25, in order to obtain standardized cavities. Dentine adhesive (Scotchbond) was used in all experimental groups Leakage was evidenced by Rodamina B dye penetration after thermocycling procedure between 10°C and 50ºC temperature and analysed according to HIRSCH g WEINREB modified criterion by using ZEISS Stereoscopic Magnifying Glass (10x). According to the results, we should concluded that: 1- Cervical marginal leakage occurred to 77,5% of conventional cavities restorations and 47,5% of adhesives cavities. 2- The major percents of leakage, regardless the factors studied, always occurred at level 3, that is, with leakage up to axial wall. 3- Either chemically cured resin or light - cured resin presented the same leakage. 4- The acid-etching reduced from 70% to 55% the leakage percentage observed. 5- The leakage observed for adhesive or conventional cavities continued when chemically cured resin or light- cured resin was used. 6- Acid-etching... / Doutor

Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2017-10-05T00:11:28Z No. of bitstreams: 1 LeticiaVirginiaDeFreitasChaves_DISSERT.pdf: 624609 bytes, checksum: 00e1748d54f2f6578477eb5c68293890 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2017-10-16T23:12:07Z (GMT) No. of bitstreams: 1 LeticiaVirginiaDeFreitasChaves_DISSERT.pdf: 624609 bytes, checksum: 00e1748d54f2f6578477eb5c68293890 (MD5) / Made available in DSpace on 2017-10-16T23:12:07Z (GMT). No. of bitstreams: 1 LeticiaVirginiaDeFreitasChaves_DISSERT.pdf: 624609 bytes, checksum: 00e1748d54f2f6578477eb5c68293890 (MD5) Previous issue date: 2017-07-07 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior (CAPES) / Objetivos: Avaliar a profundidade de polimeriza??o (PP), tens?o de contra??o (TC), resist?ncia flexural (RF), m?dulo de elasticidade (ME) e a resist?ncia de uni?o (RU) de tr?s comp?sitos Bulk Fill fluidos em compara??o a comp?sitos tradicionais de alta viscosidade. Metodologia: Tr?s comp?sitos Bulk fill fluidos (Filtek BKF, Surefil SDR, X-tra Base) e tr?s tradicionais ( Z250 XT, Grandioso, TPH3) foram utilizados. Para RF/ME, 60 amostras (n=10) em forma de barra (7 mm x 2 mm x 1 mm) foram confeccionadas e avaliadas por meio de uma M?quina de Ensaios Universal (MEU). Para PP e RU, cavidades c?nicas (n=10) preparadas em dentina bovina foram restauradas com os materiais. A PP foi analisada atrav?s da raz?o base/topo de microdureza de superf?cie e a RU pelo teste de push-out numa MEU. A TC foi mensurada em incremento ?nico das Bulk Fill e dois incrementos para as tradicionais em MEU acoplada a um extens?metro (n=5). Os dados foram estatisticamente avaliados por meio dos testes ANOVA 2 fatores e Tukey (p<0,05). Resultados: Para ME, as resinas convencionais apresentaram maiores valores diante de todas as resinas BKF, no entanto para a RF elas foram iguais, com exce??o apenas da BKF da VOCO que foi inferior. Para a PP convencionais e BKF foram estatisticamente semelhantes. Na TC e na RU as BKF apresentaram-se superiores as convencionais, tamb?m com exce??o apenas da Xtra Base Bulk Fill (VOCO) que foi estatisticamente igual as convencionais na RU. Conclus?o: As resinas Bulk Fill flu?das testadas BKF e SDR apresentaram as propriedades mec?nicas testadas superiores ou iguais aos comp?sitos tradicionais, exceto o m?dulo de elasticidade. / Objectives: To evaluate depth of polimerization (DP), contraction strress (SC), flexural strenght (FS), elastic modulus (EM) and bond strength (BS) of three low-viscosity Bulk Fill composites resin compare as of high-viscosity traditional composites. Methods: Three Bulk fill composites (Filtek BKF, Surefil SDR, X-tra Base) and three traditional ( Z250 XT, Grandioso, TPH3) were used. For FS/ME, 60 (n=10) bar specimens (7 mm x 2 mm x 1 mm) were prepared and evaluated with Universal Testing Machine (UTM). For DP e BS, conical cavities (n=10) were prepared in bovine dentine and restored with materials. DP was analyzed trough the ratio base/top with microhardness of surface and BS on the push-out test in UTM. SC was measured for to increment one of Bulk Fill Resins and two increments of traditional resins in UTM attached to a extensometer (n=5). The data were statistically evaluated by ANOVA 2-way/Tukey (p<0,05). Results: For EM the conventional resins show higher values compare to all the BKF resins, however for the FS they were the same, except for only the VOCO Bulk Fill that was inferior. For the PP, conventional and BKF were statistically similar. In TC and in BS the BKF were superior to conventional, also with the exception of Xtra Base Bulk Fill (VOCO), which was statistically the same as the conventional ones in the BS. Conclusion: The Bulk Fill composites resin BKF and SDR present most of property physical and mechanical higher or similar than traditional composites, except the elastic modulus.

Made available in DSpace on 2013-08-07T18:54:15Z (GMT). No. of bitstreams: 1 000423535-Texto+Completo-0.pdf: 597066 bytes, checksum: ce81a6cb6a7764590654a4d5a48d3e79 (MD5) Previous issue date: 2010 / This study aimed to examine the influence of time and intensity of energy, two types of light curing, LED and halogen light, the healing of three dental composite resins with different organic phases, Rok manufacturer of SDI, the organic phase UDMA, Filtek Z250, 3M ESPE, the organic phase Bis-GMA, UDMA, Bis-Ema, TEGDMA, and Ultradent Amelogem Plus, with the organic phase Bis-GMA and TEGDMA. Tests of tensile strength and diametral compressive strength and subsequently determining the modulus of elasticity of these resins. To test diametral tensile strength were prepared specimens with 6 mm in diameter and 3 mm thick for testing compressive strength, specimens with 3 mm in diameter and 6 mm thick. The resins were inserted in the headquarters in increments of 2 mm each and light cured by halogen light (3M Dental Products, Irvine, USA, 450 mW/cm for 18 and 36 s for 2the energy density of 8 and 16 J/cm2, respectively) and LED (High Powered Led Cordless - SDI LTD - Australia, with light intensity of 1200 mW/cm for 7 and 14 s for 2the energy density of 8 and 16 J/cm2). The samples were stored for 14 days at room temperature and distilled water, after this period the samples were tested in a universal testing machine EMIC DL - 2000, with the loading speed of 1 mm/min until the sample fractured. The results were tested using ANOVA and Tukey test with a confidence level of 95%. There was no statistically significant differences between groups of resin when analyzed in relation to the energy density for all items surveyed, compared to light curing units were statistically significant differences in modulus, and the halogen light showed better outcomes in relation to the LED (p=0,0166). With respect to the organic resins were superior in mechanical properties of those containing the UDMA monomer composition. Conclusion: The LED curing device presents itself as a viable alternative for use in dental practices and the implementation of the energy density of 8 J/cm, subject to the mechanical properties 2of the resins studied. / O presente estudo teve por objetivo estudar a influência do tempo e a intensidade de energia, de dois tipos de luz para fotopolimerização, LED e luz halógena, na cura de três resinas odontológicas compostas comerciais com diferentes fases orgânicas, Rok da fabricante SDI, fase orgânica UDMA; Filtek Z250, 3M ESPE, fase orgânica Bis-GMA, UDMA, Bis-EMA, TEGDMA; e Amelogem Plus da Ultradent, com fase orgânica Bis-GMA e TEGDMA. Foram realizados ensaios de resistência à tração diametral e resistência à compressão e posteriormente a determinação do módulo de elasticidade dessas resinas. Para o teste de resistência à tração diametral foram confeccionados corpos de prova com 6 mm de diâmetro e 3 mm de espessura e para o ensaio de resistência à compressão, corpos de prova com 3 mm de diâmetro e 6 mm de espessura. As resinas foram inseridas nas matrizes em incrementos de 2 mm cada e fotopolimerizadas por lâmpada halógena (3M Dental Products, Irvine, USA, com 450 mW/cm2 por 18 e 36 s para obter densidade de energia de 8 e 16 J/cm2, respectivamente) e por LED (High Powered Led Cordless – SDI LTD – Austrália, com intensidade de luz de 1200 mW/cm2 por 7 e 14 s para obter a densidade de energia de 8 e 16 J/cm2). As amostras foram armazenadas por 14 dias, em temperatura ambiente e água destilada, após esse período as amostras foram ensaiadas em uma máquina de ensaio universal EMIC DL – 2000, com velocidade de carregamento de 1 mm/min até que a amostra sofresse fratura. Os dados obtidos foram submetidos aos testes de variância ANOVA e Tukey com nível de confiança de 95%. Não houve diferenças estatisticamente significativa entre os grupos das resinas quando analisadas em relação à densidade de energia para todos os itens pesquisados (p<0,05).Em relação aos aparelhos fotopolimerizadores houve diferenças estatisticamente significativa para módulo de elasticidade, sendo que a luz halógena apresentou resultados superiores em relação ao LED (p=0,0166). Quanto à fase orgânica das resinas, apresentaram superioridade nas propriedades mecânicas àquelas que contêm o monômero UDMA em sua composição. Conclusão: O aparelho de fotopolimerização LED apresenta-se como uma alternativa viável para ser utilizado em consultórios dentários, bem como a aplicação da densidade de energia de 8 J/cm2, sem prejuízo das propriedades mecânicas das resinas estudadas.

Orientador: Edison Bittencourt / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-08-06T05:15:57Z (GMT). No. of bitstreams: 1 Fregolente_PatriciaBogalhosLucente_M.pdf: 761293 bytes, checksum: da2a8c420bdda1b10fb1d7888911e1b9 (MD5) Previous issue date: 2006 / Resumo: Atualmente, o mercado procura materiais com qualidades ópticas que satisfaçam as exigências dos usuários e que possuam facilidades de processamento. De forma geral, para um polímero apresentar boas propriedades ópticas, este necessita ter boas características como alto índice de refração, alta transmitância da luz, baixo peso específico, resistência ao impacto, estabilidade dimensional pós cura e estabilidade por exposição à luz e ao calor. Industrialmente, utiliza-se para a fabricação de lentes oftálmicas, a técnica de polimerização térmica, ou cura térmica. Dessa maneira, necessita-se de um tempo de cura muito longo (cerca de 20 horas) para evitar defeitos nas lentes. Entretanto, a cura através de irradiação de luz ultra-violeta (UV) permite obter os mesmos tipos de materiais e com características semelhantes com um tempo de processo reduzido em até poucos minutos. No presente trabalho, para confecção das lentes foram estudados os seguintes monômeros e oligômeros: metacrilato de metila (MAM), 1,6-Hexanediol diacrilato (HDODA), diacrilato uretano alifático tetrafuncional (Ebecryl 284) e diacrilato epóxi bisfenol-A (Ebecryl 3700) e para cada formulação o fotoiniciador 2- hidroxi-2-metil-1-fenilpropanona (Darocure 1173). O tempo de fotocura da mistura dura entre 4 a 7 minutos, de acordo com a espessura do molde. As lentes obtidas foram caracterizadas por medidas de dureza Shore D, transmitância nas regiões visível, UVA e UVB, índice de refração, análises térmicas para determinação da temperatura de transição vítrea. As lentes foram recobertas por uma resina multifuncional através do método de deposição por spin-coating e curada por UV. A caracterização dessa camada foi realizada por testes de dureza superficial utilizando graduações de grafites além de um planejamento experimental para observar as variáveis do processo de spin-coating que mais interferem na formação do recobrimento. As lentes produzidas apresentam ótimas qualidades ópticas e mecânicas e esta tecnologia de fotocura apresenta grande potencial para ser aplicada e produzir lentes em escala industrial / Abstract: The materials used for ophthalmic lenses need to present some optical qualities and to satisfy the requirements of the users. Various characteristics are required for the transparent synthetic resins as optical material. A polymer, to have good optical properties, needs to be colorless and tranparent, present good characteristics as high refractive index, high light transmittance, low specific weight, impact resistance, and stability to the exposition to the light and the heat. Industrially, for the manufacture of opthalmic lenses is used the technique of thermal polymerization, or thermal cure. This way, it is needed a long time of cure (about 20 hours) to prevent defects in the lenses. The monomers and monofunctional and multi-functional oligomers that have been studied for production of the lenses are methyl methacrylate (MAM), 1,6-hexanediol diacrylate (HDODA), aliphatic uretane diacrylate and bisphenol A epoxy diacrylate. The photoinitiator 2-hydroxi-2-methyl-1-fenilpropanone was added to each mixture, varying its concentration of 1 to 3%. The cure through ultraviolet irradiation (UV) allows to get the same kind of materials than thermal cure with similar characteristics but with a time of processing of the order of few minutes. In the present work, characteristics as refractive index (n), heat resistance, light transmittance and hardness of the produced lenses were studied from mixtures of acrylates and multi-functional methacrylates through photopolymerization with UV lamp at room temperature. The pencil hardness test was used for characterize the surface coating by spin-coating method, beyond an experimental design to observe the variables of the process that influence the formation of the coating / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química

Determina la diferencia en la resistencia a la flexión entre espigos de fibra de cuarzo y espigo de fibra de vidrio. Se seleccionan 30 espigos de fibra y se dividen en 2 grupos de 15. Grupo A: D.T. Light-Post® Illusion™ X-RO (RTD); Grupo B: Exacto 0.5 (Angelus). Se realiza el ensayo de flexión en tres puntos según norma ISO 14125 para todas las muestras; las cuales se observan hasta que se produzca la fractura de los espigos. Los resultados mecánicos se someten a la prueba estadística t-Student. Donde los espigos de fibra de vidrio (Grupo B) presentan los valores más altos para resistencia a la flexión (2682,6 ± 444,1), mientras que los espigos de fibra de cuarzo (Grupo A) presentaron valores menores (1865,4 ± 153,6). Se encuentra que los espigos de fibra de vidrio presentan mayor resistencia a la flexión (Mpa) que los espigos de fibra de cuarzo; se determina que existe diferencia estadísticamente significativa. / Tesis

Determina cuáles son las variaciones dimensionales en modelos obtenidos a partir de dos técnicas de impresión utilizadas en la práctica clínica, para ello se diseña un modelo maestro del que se reprodujo en yeso 20 impresiones en 2 grupos (doble impresión con recorte y cofias acrílicas). Posteriormente se realizan mediciones en 6 localizaciones de cada modelo a través de una máquina especializada en coordenadas de la marca Zeiss (Duramax 5/5/5, Alemania). Los datos son analizados utilizando el paquete estadístico SPSS 23.0. Se realizan los estadísticos descriptivos y la prueba no paramétrica U de Mann Whitney para comparaciones múltiples. Los resultados muestran que no existen diferencias estadísticamente significativas de ambas técnicas respecto al modelo maestro, pero sí, al comparar ambas técnicas. (P≤0.05). Se concluye que de la técnica de doble impresión con recorte, se obtienen reproducciones que se asemejan más al modelo maestro. / Tesis