Made available in DSpace on 2017-07-24T19:22:28Z (GMT). No. of bitstreams: 1 RODRIGO S GRANDE.pdf: 5650250 bytes, checksum: 965396f452f58590edf14d60a01a07f9 (MD5) Previous issue date: 2012-11-30 / The aim of this work were investigate the microtensile bond strength (μTBS), nanoleakage (NL), nano-hardness (NH) and Young’s modulus (YM) of resin-dentin bonding components produced by two simplified etch-and-rinse adhesive with different concentrations of chlorhexidine diacetate (CHX). 99.9% of CHX were added to Ambar (FGM) and XP Bond (Dentsply) in concentrations of 0, 0.01, 0.05, 0.1 and 0.2 wt%. Resin-dentin bonded sticks (0.8 mm2) were prepared for μTBS testing (0.5 mm/min). For NL, some bonded sticks from each tooth were used. Nano-indentations were made on the adhesive interface and NH and YM calculated. The results of μTBS, NL and NH and YM of the hybrid layers of the CHX-free and CHX-containing adhesives were statistically similar (p > 0.05) on immediately time. After 12 months, significant reductions of μTBS were observed for both adhesives in the control group (p< 0.05). In CHX-containing adhesives or CHX-free groups the BS remained stable for both systems. NL was more evident in the control than in the experimental groups (p < 0.05) both in IM and 12 months periods. Conclusions: CHX in concentrations lower than 0.1 wt% incorporated in the two simplified etch-and-rinse adhesives did not impair the immediate resin-dentin bond strength, nanoleakage and mechanical properties of the adhesive and hybrid layers. / O efeito da clorexidina (CHX) como agente para preservar a união tem sido bem estabelecido, mas pouco se sabe sobre a inclusão da CHX nos sistemas adesivos convencionais simplificados. Objetivos: 1) avaliar no tempo imediato o efeito da adição de diferentes concentrações de clorexidina (CHX 0,01%, 0,05%, 0,1% e 0,2%) em dois adesivos simplificados Ambar (AM) e XP Bond (XP) nas propriedades adesivas (resistência de união [RU] e nanoinfiltração [NI]) e físicas (nanoindentação [NP] e módulo de elasticidade [ME]) à dentina (experimento 1); 2) avaliar ao longo de doze meses o efeito da adição da CHX no AM e XP nas propriedades adesivas (resistência de união [RU] e nanoinfiltração [NI]) à dentina (experimento 2); 3) avaliar ao longo de 28 dias a adição de CHX no AM e XP nas características de sorção (SA), solubilidade (SO) e a liberação de clorexidina em água (experimento 3). Metodologia: para o experimento 1 e 2 foram utilizados molares humanos até a exposição da dentina oclusal. Os dentes foram divididos de acordo com as diferentes concentrações de clorexidina e tempo de armazenamento: sem CHX (controle); com 0,01%; 0,05%; 0,1%; e 0,2% de diacetato de CHX, testados imediatamente e ao longo de 12 meses. Após aplicação dos adesivos AM e XP, restaurações de resina composta foram realizadas. Cada dente foi cortado para obtenção de “palitos” que foram divididos de acordo com as propriedades a serem testadas e o tempo de armazenamento. Para RU, os palitos foram testados em tração (0,5mm/min). Para NP e ME foram testados em um nanodurômetro e para o teste de NI, os “palitos” foram corados com nitrato de prata e avaliados através de EDS em MEV. Para cada teste foi aplicada a análise estatística apropriada. Para o experimento 3 foram confeccionados espécimes na forma de discos e posterior verificação da sorção, solubilidade e doação de CHX. As mesmas concentrações de adesivos foram utilizadas. Para SA e SO, os espécimes após fotoativação foram desidratados (m1) e armazenados em água durante28 dias para avaliação gravimétrica úmida (m2) e após nova desidratação (m3) da sorção (m2 m3/volume) e solubilidade (m1-m3/volume). Resultados: A inclusão de diferentes concentrações de CHX não afetou as propriedades adesivas e físicas dos adesivos testados (experimento 1). Nos grupos controles dos dois adesivos testados (AM e XP), ocorreu degradação da resistência de união e aumento da quantidade de nitrato de prata após 12 meses de armazenamento em água, fato este que não ocorreu quando a CHX foi adicionada, independente da concentração (experimento 2). A adição de CHX não afetou a SA e SO, quando comparado com os respectivos grupos controle. Ocorreu liberação de CHX por todo o período do experimento, sendo maior nas primeiras 24 h (experimento 3). Conclusão: a incorporação de CHX ao adesivo não afetou de maneira imediata as propriedades adesivas e físicas de união a dentina, nem a sorção e solubilidade, mas preservou a união ao longo de 12 meses, além de liberar clorexidina por todo o período avaliado.

Made available in DSpace on 2017-07-24T19:22:34Z (GMT). No. of bitstreams: 1 Fabiana Suelen F Siqueira.pdf: 4912773 bytes, checksum: 2ec106a259c272efabb63a88fac23314 (MD5) Previous issue date: 2014-02-26 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The purpose of this "in vitro" study was to evaluate the effect of the deproteinization of the eroded dentin in bond strength, nanoleakage and morphology of the hybrid layer using three different adhesive systems. The sample consisted of 45 human molars. The teeth had their occlusal surfaces exposed to mid coronal dentin. After the standardization of smear layer and the induction of the dentin erosion, they were randomly divided into 3 groups (n=15), according to the adhesive system used: GS1 - Adper Single Bond™ 2 (3M-ESPE™) - 2 steps simplified adhesive system; GS2- AdheSE® (Ivoclar/Vivadent) - 2 steps self-etch adhesive system; GS3- Single Bond Universal™ (3M-ESPE) - 1 step adhesive system. Previously to the application of the adhesive system, each group was divided into 3 subgroups (n=5), according to the treatment of the dentin: A1– Sound Dentin (control), A2- eroded dentine and A3- eroded dentine + deproteinized with NaOCl ( 5.2% ) for 40 sec. After the application of the adhesive systems according to the manufacturer's instructions, the teeth were restored with composite resin and sectioned to obtain “sticks-like” resin specimens (0.8 mm2). The microtensile bond strength test (TBS) was performed after 24h storage in water at 37 ºC at a rate of 1 mm/min. Before the microtensile test, 4 “sticks” of each experimental condition were randomly assigned for micromorphological analysis (formation of the resin tags and nanoleakage - NI) by SEM. The TBS and NI data were analyzed by 2 way ANOVA complemented by Tukey's test (α=0.05). The group treated with Single Bond Universal and deproteinization showed the highest μ-TBS (41.86 ± 5.80 MPa). The lowest μ-TBS mean was observed for AdheSE® after erosion without deproteinization (14.04 ± 7.28 MPa). The higher NI mean (%) was observed for AdheSE® after erosion without deproteinization (69.40 ± 8.73) and Single Bond Universal had the lowest NI mean (%) for the deproteinized group (14.48 ± 5.47). The photomicrographs of sound dentin and deproteinized dentin for all adhesive systems showed the presence of longer resin tags in the hybrid layer compared to the eroded dentin only The dentin deproteinization resulted in increased TBS in the eroded substrate for the groups in which self-etch adhesive systems were applied.. For the NI, the best conditions were obtained for the Single Bond Universal adhesive system. / O propósito deste estudo foi avaliar “in vitro” o efeito da desproteinização dentinária mediante a aplicação do hipoclorito de sódio 5,2% em dentina erosionada na resistência de união, nanoinfiltração e morfologia da camada híbrida, utilizando três diferentes sistemas adesivos. A amostra consistiu em 45 molares humanos, cujas superfícies oclusais foram expostas até a exposição da dentina média. Após padronização da smear layer e indução da erosão, os dentes foram divididos de forma aleatória em 3 grupos de 15 dentes de acordo com o sistema adesivo utilizado: Grupo GS1 - Adper Single Bond™ 2/3M-ESPE™, sistema adesivo simplificado de 2 passos; Grupo GS2 - AdheSE® Ivoclar/Vivadent, sistema adesivo autocondicionante de 2 passos e Grupo GS3 – Single Bond Universal™/3M-ESPE™, sistema adesivo autocondicionante de 1 passo. Antes da aplicação do sistema adesivo, cada grupo foi dividido em 3 subgrupos com 5 dentes, de acordo com o tratamento ao qual a dentina foi submetida: A1 - Dentina hígida (controle), A2 - Dentina erosionada e A3 – Dentina erosionada + desproteinizada com NaOCl (5,2%) por 40 seg. Após a aplicação e a fotoativação dos sistemas adesivos, de acordo com as especificações do fabricante, os dentes foram restaurados com resina composta e seccionados para obtenção de espécimes em forma de “palitos” (0,8 mm2). O teste de resistência de união (RU) foi realizado após 24h de armazenamento em água a 37 ºC a uma velocidade de 1 mm / mim. Antes do teste de microtração, foram separados aleatoriamente 4 “palitos” de cada condição experimental para análise da formação de tags e nanoinfiltração (NI) em MEV. Os dados de RU e NI foram analisados por ANOVA de 2 fatores complementado pelo teste de Tukey (α = 0,05). O sistema adesivo autocondicionante Single Bond Universal após desproteinização apresentou a maior média de RU (41,86 ± 5,80 MPa). A menor média de RU foi observada para o sistema adesivo autocondicionante AdheSE® após erosão sem desproteinização (14,04 ± 7,28 MPa). A maior média de NI (%) foi observada para o sistema adesivo autocondicionante AdheSE® após erosionado sem desproteinização (69,40 ± 8,73) e o sistema adesivo Single Bond Universal apresentou a menor média de NI (%) para o grupo desproteinizado (14,48 ± 5,47). A observação das fotomicrografias para dentina hígida e desproteinizada em relação a todos os sistemas adesivos notou-se a presença de tags de maior comprimento na camada híbrida. A desproteinização dentinária acarretou um aumento de RU no substrato erosionado para os grupos em que foram aplicados sistemas adesivos autocondicionantes. Em relação à NI, melhores condições foram obtidas para o sistema adesivo simplificado Universal.

Made available in DSpace on 2017-07-24T19:22:35Z (GMT). No. of bitstreams: 1 Andres Felipe M Cardenas.pdf: 5280325 bytes, checksum: 04a1911a6a06b35dcfc2a254330c8113 (MD5) Previous issue date: 2014-02-25 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / This " in vitro " study evaluated the effect of the treatment of eroded dentin with bioglass (Novamin®) and casein phosphopeptides and amorphous calcium phosphate (CPP-ACP) in bond strength, nanoleakage and micromorphology of the hybrid layer, using three different adhesive systems. The sample consisted of 60 extracte human molars. The occlusal surfaces of the teeth were exposed at medial dentin, the smear layer were standardized and the induction of the dentin erosion were accomplished before restoration. The molars were randomly divided into 3 groups (n=20) according to the adhesive system used:G1 - Single Bond 2 ™ / 3M - ESPE ™ system, simplified 2 steps adhesive; G2 - AdheSE Ivoclar/Vivadent, 2 steps self- etch adhesive system and G3 -Universal Single Bond™ /3M-ESPE™, 1-step adhesive system. Previously to application of the adhesive system, each group was divided into 4 subgroups (n=5), according to the treatment which the dentin was submitted: S1 – Sound dentin (control), S2 - eroded dentin, S3 - eroded dentine + toothpaste with fluorine and bioglass and S4 - eroded dentine + toothpaste with CPP-ACP. After the application of the adhesive systems according to manufacturer's specifications, the teeth were restored with composite resin and sectioned to obtain "sticks-like" (specimens 0.8 mm2). The microtensile bond strength test (TBS) was performed after 24h of storage in water at 37 ºC at a rate of 1mm/min. Before the microtensile test, 4 “sticks-like” for each experimental conditions were randomly assigned for the analysis of the hybrid layer, resin tags and nanoleakage (NI) by SEM. The TBS and NI data were analyzed by 2 away-ANOVA complementary Tukey's test (α=0.05). The Adper Single Bond 2 system after pretreatment with fluorine-based and bioglass and CPP-ACP showed the highest TBS means (53.39 ± 7.88 MPa and 47.72 ± 10.68 MPa, respectively). The lowest TBS mean was observed for the self etch adhesive system (AdheSE) after erosion (14.04 ± 7.28 MPa). The higher NI mean (%)was observed for AdheSE + eroded dentin (69.40 ± 8.73) and Single Bond 2 had the lowest NI mean (%) for treatment with fluoride and bioglass and CPPACP (11.16 ± 1.34 and 15.63 ± 1.47, respectively). The morphological analysis of the micrographs from the subgroups S3 and S4 for adhesives Single Bond 2 and Single Bond Universal showed the presence of more homogeneous resin tags compared to the other tested conditions. The best nanoleakage condition were obtained for Single Bond 2 and Single Bond Universal system. It was concluded that the home or professional application of desensitizing pastes does not interfere with the TBS in eroded dentin, maintaining or improving the TBS for this substrate. / Este estudo avaliou “in vitro” o efeito da aplicação prévia de uma pasta fluoretada com biovidro (Novamin) e uma pasta com fosfopéptideo de caseína-fosfato de cálcio amorfo (CPP-ACP) em dentina erosionada na resistência de união, nanoinfiltração e morfologia da camada híbrida, utilizando três diferentes sistemas adesivos. Sessenta molares humanos extraídos foram utilizados, cujas superfícies oclusais dos dentes foram expostas até a exposição da dentina média. Após padronização da smear layer e indução da erosão, os dentes foram divididos de forma aleatória em 3 grupos de 20 dentes de acordo com o sistema adesivo utilizado: Grupo G1 - Adper Single Bond 2 /3M-ESPE, sistema adesivo simplificado de 2 passos; Grupo G2 - AdheSE Ivoclar/Vivadent, sistema adesivo autocondicionante de 2 passos e Grupo G3 - Single Bond Universal / 3M-ESPE, sistema adesivo autocondicionante de 1 passo. Antes da aplicação do sistema adesivo, cada grupo foi dividido em 4 subgrupos com 5 dentes, de acordo com o tratamento ao qual a dentina foi submetida: S1 - dentina hígida (controle), S2 - dentina erosionada, S3 -dentina erosionada + pasta com flúor e biovidro e S4 – dentina erosionada + pasta com CPP-ACP. Após a aplicação e a fotoativação dos sistemas adesivos e acordo com as especificações do fabricante, os dentes foram restaurados com resina composta e seccionados para obtenção de espécimes em forma de palitos” (0,8 mm2). O teste de resistência de união (RU) foi realizado após 24h de armazenamento em água a 37 ºC a uma velocidade de 1 mm / mim. Antes do teste de microtração, foram separados aleatoriamente 4 “palitos” de cada condição experimental para análise da camada híbrida, formação de tags e nanoinfiltração (NI) em MEV. Os dados de RU e NI foram analisados por ANOVA de 2 fatores complementado pelo teste de Tukey (α = 0,05). O sistema adesivo Adper Single Bond 2 após pré-tratamento à base de flúor e biovidro (53,39 ± 7,88 MPa) e CPP-ACP (47,72 ± 10,68 MPa) apresentaram os maiores valores de RU. A menor média de RU foi observada para o sistema adesivo autocondicionate AdheSE após erosão (14,04 ± 7,28 MPa). A maior média de NI (%) foi observada para o sistema adesivo AdheSE após erosionado (69,40 ± 8,73) e o sistema adesivo Single Bond 2 apresentou a menor média de NI (%) para o tratamento com flúor e biovidro e CPP-ACP respectivamente (11,16 ±1,34) e (15,63 ±1,47). Nas observações das fotomicrografias dos subgrupos S3 e S4 para os adesivos Single Bond 2 e Sigle Bond Universal, abservou-se a presença de tags mais homogêneos. Para esse estudo foi possível concluir que a aplicação de pastas dessensibilizante, seja de uso caseiro ou profissional, não interferiu nos valores de RU em dentina erosionada, mantendo ou melhorando a RU para esse substrato. As melhores condições de nanoinfiltração foram obtidas para o sistema Single Bond 2 e o Single Bond Universal.

Submitted by Eunice Novais (enovais@uepg.br) on 2018-02-05T16:22:24Z No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) Carlos Dávila Sánchez.pdf: 22396898 bytes, checksum: 5122ed06da0d2dc71b9cbf4253c97cda (MD5) / Made available in DSpace on 2018-02-05T16:22:24Z (GMT). No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) Carlos Dávila Sánchez.pdf: 22396898 bytes, checksum: 5122ed06da0d2dc71b9cbf4253c97cda (MD5) Previous issue date: 2017-12-07 / O objetivo deste estudo foi avaliar o efeito da aplicação de primers experimentais à base de flavonoides na resistência de união, nanodureza, módulo de elasticidade e micromorfologia da interface adesiva criada em dentina hígida e dentina afetada por cárie utilizando um adesivo universal aplicado em modo convencional. Superfícies planas de dentina foram expostas em 182 molares permanentes. Noventa e um molares foram armazenados em água, enquanto os outros 91 foram imersos em uma solução de BHI/Sacarose (pH 4.0) e cepas de Streptococcus mutans por 14 dias para induzir lesões artificiais de cárie em dentina. Quarenta e nove dentes foram aleatoriamente alocados em 7 grupos (n=7) de acordo com o primer experimental usado em cada tipo de substrato (hígido ou afetado por cárie): Controle, sem aplicação de primer (CON), Placebo solução hidroalcoólica com tensoativo (PLA), Proantocinidina (PRO), Quercetina (QER), Naringina (NAR), Rutina (RUT), e Hesperidina (HES). Após o condicionamento, lavagem e secagem das superfícies de dentina, os primers foram ativamente aplicados por 1 min para reumedecer a dentina. Após serem restaurados, os espécimes foram seccionados no seu longo eixo até obter palitos retangulares (0,9 mm2) que foram testados em tração com velocidade de 1 mm/min, tanto após 24 h quanto após 25.000 ciclos em uma máquina de ciclagem térmica (5 ºC / 55 ºC). Para os testes de nanodureza e módulo de elasticidade (n=3), os espécimes foram cortados longitudinalmente até obter duas fatias planas (1,2 mm) e foram analisados em um nanoindentador com uma ponta Berkovich tanto após 24 h quanto após 25.000 ciclos térmicos. Para a análise qualitativa de microinfiltração, 21 dentes (n=3) assistida por corantes em Microscópio confocal (CSLM), o adesivo e a resina composta foram misturados com 0,2% de Rhodamina B (massa) antes dos procedimentos restauradores e duas fatias planas foram obtidas para análise após 24 h e 25.000 ciclos térmicos. As fatias foram imersas em uma solução de Fluoresceína (0,1%) por 4 horas. Quatro imagens da interface adesiva de cada dente foram obtidas em cada momento experimental (24 h ou 25.000 ciclos) a 5 e 10 μm de profundidade. Os resultados foram analisados usando uma análise de variância de medidas repetidas e pós-teste de Bonferroni (= 0,05). Resultados: Os grupos PLA e RUT mostraram os valores mais altos de μTBS em dentina hígida em ambos intervalos (p > 0,05). Na dentina afetada por cárie os grupos RUT e NAR apresentaram os valores mais altos em ambos intervalos. As imagens de CSLM mostraram sinais de infiltração em todos os grupos. PLA, RUT, NAR e PRO mostraram áreas sem infiltração em ambos intervalos e tipo de substrato. As nanopropriedades foram influenciadas pelos grupos experimentais em profundidade dependendo do flavonoide usado. Conclusão: O uso de flavonoides poderia ser uma alternativa terapêutica em dentina hígida e afetada por cárie para melhorar as propriedades e longevidade da interface adesiva. / The aim of this study was to evaluate the effect of experimental flavonoid primers on bond strength, nanohardness, elastic modulus, and micromorphology of bonding interfaces created on sound and caries-affected dentin using one commercially available universal bonding agent applied in the etch-and-rinse mode. Flat midcoronal dentin surfaces were exposed in 182 permanent molars. Ninety-one molars were stored in water while the other 91 molars were kept in a BHI/Sucrose solution (pH 4.0) with Streptococcus mutans strain for 14 days to induce artificial caries-affected dentin. Forty-nine teeth were randomly assigned to 7 groups (n=7) according to the experimental primer applied to each dentin surface condition (sound or caries-affected dentin): Control, in which no primer was applied (CON), Hydroalcoholic solution with surfactant Placebo (PLA), Proanthocianidin (PRO), Quercetin (QER), Naringin (NAR), Rutin (RUT) and Hesperidin (HES). After etching, rinse and drying the dentin surfaces, the primers were actively applied for 1 min to rewet the dentin surface. After bonding and restorative procedures, specimens were sectioned in the long axis to obtain rectangular sticks (0.9 mm2) that were subjected to microtensile tests (μTBS) at a crosshead speed of 1 mm/min, either 24 h or after 25.000 cycles in a thermocycling machine (5ºC / 55ºC). For nanohardness and elastic modulus (n=3), the specimens were longitudinally sectioned to obtain 2 flat silces (1,2 mm) and were analyzed in a nanohardness device with a Berkovich indenter either after 24 h or after 25.000 (5 ºC / 55 ºC) thermal cycles. For the dye assisted microinfiltration qualitative analysis 21 teeth (n=3) was performed with a Confocal Scanning Laser Microscope (CSLM), both adhesive system and resin composite were mixed with 0.2% (weight) Rhodamine B prior to the restorative procedure and two flat slices were obtained for analysis in 24 h and after 25.000 thermal cycles. The bonding interfaces were immersed in a 0,1%. Fluorescein solution for 4 hours. Four images of bonding interface per specimen where obtained in each experimental time (24 h and 25.000 cycles) at 5 and 10 m depth. The data were analyzed using two-way repeated measures ANOVA and Bonferroni post-hoc test ( = 0.05). Results. PLA and RUT showed the highest TBS values in sound teeth at both intervals (24h and ageing) (p>0.05), while RUT and NAR showed the highest TBS values in carious teeth in both stages. CLSM analysis showed signs of microinfiltration for all groups. PLA, RUT, NAR and PRO showed areas of no infiltration in both experiments and intervals. Nanomechanical properties were influenced by experimental groups in deep, dependending on the flavonoid used. Conclusion: The use of flavonoids may be an alternative for therapeutic substances in sound or carious dentin to improve their properties and longevity in the adhesive interphase.

Submitted by Angela Maria de Oliveira (amolivei@uepg.br) on 2018-05-21T18:28:19Z No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) Veridiana Campos.pdf: 1599980 bytes, checksum: dc566e6e595eb2ee2afd4a74f9ee9f2a (MD5) / Made available in DSpace on 2018-05-21T18:28:19Z (GMT). No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) Veridiana Campos.pdf: 1599980 bytes, checksum: dc566e6e595eb2ee2afd4a74f9ee9f2a (MD5) Previous issue date: 2018-02-19 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / O objetivo desse trabalho in vitro foi avaliar a resistência de união ao microcisalhamento (μSBS) de cerâmicas com diferentes graus de translucidez e agentes de cimentação, no tempo imediato e após simulação de 1 ano de envelhecimento em termociclagem, assim como avaliar a composição elementar por espectrometria de energia dispersiva (EDS). Foram selecionadas 4 cerâmicas: Dissilicato de lítio (DL), Prettau Anterior (PA), Prettau (PR) e ICE (IC). Os espécimes cerâmicos foram distribuídos em 16 grupos experimentais (n=5) a depender da combinação de variáveis: cerâmica vs tratamento de superfície (silano- SL ou silano+adesivo- AS) vs tempo de armazenamento (imediato e longevidade) vs cimento resinoso (Variolink II ou Variolink Veneer). As cerâmicas de zircônia foram submetidas ao jateamento com óxido de alumínio e a cerâmica de dissilicato de lítio foi condicionada com ácido fluorídrico à 5% por 20s. Realizado o tratamento de superfície de acordo com cada grupo experimental, tubos de tygon foram posicionados na superfície da cerâmica e preenchidos com cimento resinoso. Após 24 horas em estufa à 37ºC e após 10.000 ciclos térmicos, os espécimes foram submetidos ao teste de microcisalhamento, numa velocidade de 1mm/min até a falha. As falhas foram observadas em microscópio óptico num aumento de 100x, e avaliadas em microscopia eletrônica de varredura (FEG) com uma magnificação de 150x. Adicionalmente, as cerâmicas foram submetidas ao teste de espectrometria de energia dispersiva (EDS) para avaliação da sua composição elementar. Para fins estatísticos, optou-se por dividir os resultados em duas condições experimentais: uma para o cimento Variolink II e outra para o Veneer. Portanto, para cada cimento os dados da μSBS foram submetidos ao teste de μSBS (ANOVA 3-fatores e Tukey, α = 0,05). Para o cimento Variolink II, não foi encontrada interação tripla significativa (p>0,05). A interação dupla tratamento vs tempo (p<0,001) foi significativa, sendo os valores de μSBS imediato estatisticamente superiores à longevidade. Já a interação dupla tratamento vs cerâmica, foi estatisticamente significante (p=0,039), sendo que as cerâmicas à base de zircônia tiveram maiores valores de resistência de união, independente do tratamento de superfície. E a interação dupla tempo vs cerâmica (p<0,001) mostrou uma diminuição da μSBS de todas as cerâmicas após a termociclagem. O cimento Variolink Veneer mostrou uma interação tripla significativa (p<0,001) para todos os grupos. Independente do tratamento de superfície e da cerâmica, estatisticamente os maiores valores de resistência de união foram encontrados no tempo imediato, e as cerâmicas à base de zircônia apresentaram valores estatisticamente superiores ao dissilicato de lítio. Pode-se concluir que as cerâmicas de zircônia são mais resistentes ao microcisalhamento, no tempo imediato e após termociclagem; e que a associação AS interfere positivamente nos resultados à longo prazo. / The objective of this in vitro work was to evaluate a micro-shear strength (μSBS) of ceramics with different degrees of translucency and cementing agents,on immediate time and after simulation of 1 year of aging in thermocycling, as well as to evaluate the elemental composition do to the dispersive energy spectrometry (EDS) test. Four ceramics were selected: Lithium Dissilicate (DL), Prettau Anterior (PA), Prettau (PR) and ICE (CI). The ceramic specimens were distributed in 16 experimental groups (n = 5) depending on the combination of variables: ceramic vs. surface treatment (silane-SL or silane + adhesive-AS) vs. storage time (immediate and longevity) vs. resin cement Brochure Variolink II or Variolink). The zirconia ceramics were subjected to blasting with aluminum oxide and the lithium disilicate ceramic with fluoridric acid 5% per 20s. After the surface treatment according to each experimental group, tygon tubes were placed on the ceramic surface and filled with resin cement. After 24 hours in an oven at 37ºC and after 10.000 thermal cycles, the specimens were submitted to the micro-shear test at a speed of 1mm / min until failure. Failures were observed in optical microscope in an increase of 100x, and evaluated in Scanning Electron Microscopy (FEG) with a magnification of 150x. Additionally, ceramics were submitted to the dispersive energy spectrometry (EDS) test to evaluate their elemental composition. For statistical purposes, it was chosen to divide the results into two experimental conditions:: one for Variolink II cement and another for Veneer. Thus, for each cement the μSBS data were subjected to the μSBS test (ANOVA 3-factor and Tukey, α = 0.05). For Variolink II cement, no significant triple interaction was found (p> 0.05). The double treatment vs time interaction (p <0.001) was significant, with immediate μSBS statistically higher values to distance. On the other hand, the double treatment versus ceramic interaction was statistically significant (p = 0.039), and the ceramics based on zirconia had higher values of bond strength, regardless of surface treatment. And the double time vs. ceramic interaction (p <0.001) showed a decrease of μSBS for all ceramics after the thermocycling. Variolink Veneer cement showed a significant triple interaction (p <0.001) for all groups. Regardless the surface treatment and ceramics, statistically, the highest values of resistance were found in the immediate time, and ceramics based on zirconia presented statistically higher values than lithium disilicate. It can be concluded that zirconia ceramics are more resistant to micro-shearing, on immediate time and after thermocycling; and that the AS association interferes positively with long-term results.

Submitted by Fabiano Malheiro (fabianomalheiro22@hotmail.com) on 2017-05-22T15:47:47Z No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Efeito do acréscimo de nanopartículas radiopacas no desempenho de um sistema adesivo experimental autocondicionante livre de Hema.pdf: 1361139 bytes, checksum: 1cfb6b2bb9c9995f2dae4f8712280b04 (MD5) / Made available in DSpace on 2017-05-22T15:47:47Z (GMT). No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Efeito do acréscimo de nanopartículas radiopacas no desempenho de um sistema adesivo experimental autocondicionante livre de Hema.pdf: 1361139 bytes, checksum: 1cfb6b2bb9c9995f2dae4f8712280b04 (MD5) Previous issue date: 2014-11-20 / Sem bolsa / O objetivo deste estudo foi desenvolver um sistema adesivo nanoestruturado, do tipo autocondicionante de dois passos, de alto desempenho e radiopaco. Para isso, primers autocondicionantes foram formulados a partir da mistura de GDMA-P, HEMA ou UDMA PEG 400, etanol e água. Os adesivos de cobertura foram formulados com Bis-GMA, TEGDMA, HEMA ou UDMA PEG 400, CQ e EDAB, além de nanopartículas de trifluoreto de itérbio (YbF3) ou sílica (SiO2). Os adesivos foram avaliados por testes de grau de conversão, radiopacidade, índice de refração, resistência flexural, módulo flexural, sorção e solubilidade em água e resistência de união à dentina após 24h ou 6 meses de imersão em água destilada. Os dados foram analisados estatisticamente com ANOVA e teste complementar de Tukey (α=5%). A concentração mínima de 20% em peso (carga) foi necessária para adesivos contendo UDMA PEG 400 tornarem-se radiopacos, e de 30% em peso (carga) para os adesivos contendo HEMA. De maneira geral, as propriedades físicas avaliadas foram mantidas ou melhoradas a partir da adição das partículas. A adesão à dentina após 6 meses de armazenagem em água foi prejudicada nos grupos contendo sílica, porém o YbF3 protegeu a degradação da adesão no adesivo contendo HEMA, embora no adesivo contendo UDMA PEG 400, ele resultou em redução da adesão. A adição de partículas nanométrica em adesivos odontológicos é uma estratégia viável para aprimorar o desempenho desses materiais. / The aim of this study was to develop a nanostructured adhesive system, two-step self-etch, with high performance and radiopacity property. Selfething-primers were formulated by mixing GDMA-P, HEMA or PEG 400 UDMA, ethanol and water. The resin adhesives were formulated with Bis-GMA, TEGDMA, HEMA or PEG 400 UDMA, CQ and EDAB, besides ytterbium fluoride (YbF3) or silica (SiO2) nanoparticles were added. The adhesives were analyzed using degree of conversion, radiopacity, refractive index, flexural strength, flexural modulus, water sorption and solubility tests. The bond strength to dentin after 24h and 6 months of water storage was also performed. Data were statistically analyzed using ANOVA and Tukey test (α=5%). The minimal concentration in mass of 20% was necessary for the PEG 400 UDMA-based adhesives become radiopaque, and of 30% for the HEMA-containing adhesives. In the overall analysis, the physical properties investigated were maintained or improved by addition of nanoparticles. The adhesion to dentin after 6 months of water storage was negatively affected within the SiO2-based groups, but YbF3 hampered the adhesion degradation within the HEMA-containing adhesive, although within the PEG 400 UDAM-based adhesive it resulted in decrease of microtensile bond strenght. The incorporation of nanofillers into dental adhesives seems to be an interesting way to achieve enhanced properties, although the domain of this technology still needs further further studies to better understand the effect of incorporation of fillers and/or with their surface treatment.

Submitted by Márcio Ropke (ropke13marcio@gmail.com) on 2017-06-12T14:52:25Z No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Efeito de nanopartículas de sílica funcionalizadas com fosfato na formulação.pdf: 1036117 bytes, checksum: 069d8736b0e612684dd56cc18d7f28f3 (MD5) / Made available in DSpace on 2017-06-12T14:52:25Z (GMT). No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Efeito de nanopartículas de sílica funcionalizadas com fosfato na formulação.pdf: 1036117 bytes, checksum: 069d8736b0e612684dd56cc18d7f28f3 (MD5) Previous issue date: 2015-03-01 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / Este estudo investigou o efeito da incorporação de nanopartículas de sílica funcionalizadas com fosfato (SiO2-POOH) na resistência de união à dentina e propriedades físico-química de um sistema adesivo autocondicionante de um passo (SAA-1). O fosfato foi funcionalizado nas nanopartículas de sílica através da polimerização por radicais livres do monômero ácido fosfatado (metacriloiloxietil dihidrogênio fosfato / bis (metacriloiloxietil) hidrogênio fosfato - HEMA-P), em meio alcoólico. As SiO2-POOH resultantes foram caracterizadas por FTIR, TGA e MET. As SiO2-POOH foram adicionadas aos SAA-1s, os quais foram formulados com três concentrações de HEMA-P (0, 20 e 40 %, em massa), como grupo controle foram formulados SAA-1s sem a adição de SiO2-POOH. Os SAA-1s formulados foram avaliados quanto à resistência de união ao microcisalhamento em dentina e o padrão de fratura foi classificado. Adicionalmente, morfologia da camada híbrida, ângulo de contato, grau de conversão, taxa de polimerização e resistência coesiva foram avaliados. A análise estatística foi realizada considerando o nível de significância de 5%. A reação de funcionalização de SiO2-POOH foi confirmada por FTIR e TGA. Os SAA-1s com SiO2-POOH obtiveram valores de resistência de união significativamente maiores que os SAA-1s sem SiO2-POOH (p = 0,001), exceto para SAA-1s sem HEMA-P que não apresentaram adesão à dentina. Comparando com o correspondente SAA-1 sem SiO2-POOH, a adição de SiO2-POOH melhorou a molhamento da dentina, através da redução do ângulo de contato, e aumentou o grau de conversão e a taxa de polimerização. A resistência coesiva, entretanto, não foi alterada pela adição de SiO2-POOH. Em conclusão, a adição de SiO2-POOH melhora a resistência de união a dentina de SAA-1 sem prejudicar as outras propriedades avaliadas. / This study investigated the effect of the incorporation of phosphate-grafted-silica nanoparticles (SiO2-POOH) on dentin bond strength and the physical-chemical properties of model one-step self-etching adhesive (1-SEA). Phosphate was grafted onto the silica nanoparticles through the free radical polymerization of the acid phosphate monomer (Methacryloyloxyethyl Dihydrogen Phosphate / Bis (methacryloyloxyethyl) Hydrogen Phosphate - HEMA-P), in an alcoholic medium. The resulting SiO2-POOH was characterized by using FTIR spectroscopy, TGA, and a TEM micrograph. The SiO2-POOH were added to 1-SEA with three HEMA-P concentrations (0, 20 and 40% wt.), as the control group an unfilled 1-SEA were formulated. The formulated 1-SEAs were evaluated for microshear bond strength to dentin and classified according to failure mode. Additionally, morphological analysis of bonding interface, contact angle, degree of conversion, rate of polymerization, and the cohesive strength were evaluated. Statistical comparisons were conducted at a 5% significance level. The grafting reaction of SiO2-POOH was confirmed by FTIR and TGA. 1-SEA containing SiO2-POOH had significantly higher shear bond strength values than the non-SiO2-POOH adhesives (p = 0.001), except for 1-SEA with 0% of HEMA-P that did not exhibit bonding to the dentin. Compared with its correspondent unfilled 1-SEA, the addition of SiO2-POOH improved the dentin wettability by decreasing the contact angle and, increasing the degree of conversion and rate of polymerization. The cohesive strength, in contrast, was not affected by SiO2-POOH. In conclusion, the SiO2-POOH addition could be used to produce 1-SEA with enhanced dentin bond strength without harming the other properties that were investigated.

Submitted by Márcio Ropke (ropke13marcio@gmail.com) on 2017-06-19T14:18:07Z No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) União adesiva à dentina sadia e dentina afetada por cárie.pdf: 2924942 bytes, checksum: 46fc75de5cf29a28244831e9fc608962 (MD5) / Made available in DSpace on 2017-06-19T14:18:07Z (GMT). No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) União adesiva à dentina sadia e dentina afetada por cárie.pdf: 2924942 bytes, checksum: 46fc75de5cf29a28244831e9fc608962 (MD5) Previous issue date: 2016-02-25 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / O objetivo deste trabalho, dividido em três estudos, foi avaliar a resistência de união de sistemas adesivos comerciais e experimentais a diferentes substratos, dando ênfase à dentina afetada por cárie (CAD), por ser um substrato bastante comum na prática clínica e ainda com muitos questionamentos a serem esclarecidos. Materiais e Métodos: No estudo 1, foi comparada a resistência de união entre um Adesivo Universal (Scotchbond Universal, 3 M ESPE) e outros Sistemas adesivos comerciais aplicados a diferentes substratos: esmalte, dentina hígida (SoD), resina composta e porcelana. Espécimes de cada substrato foram confeccionados para o teste de microtração (SoD e resina composta) ou teste de cisalhamento (esmalte e cerâmica). Os dados foram analisados por meio de ANOVA uma via e teste de Tukey (a = 0,05). No estudo 2 foi avaliada, por meio de uma revisão sistemática da literatura, a união de adesivos aplicados à SoD em comparação à CAD. Uma pesquisa no PubMed, Scopus e Web of Science foi realizada por dois revisores independentes. Foram identificados 2.260 artigos únicos e, após avaliação dos títulos/resumos, 65 artigos foram selecionados para leitura completa, dos quais 40 foram incluídos. Os dados foram extraídos e categorizados de acordo com o sistema adesivo utilizado (convencional ou autocondicionante). As médias de resistência de união de ambos substratos foram comparadas utilizando um modelo estatístico de efeitos randômicos (Review Manager Version 5.1). A heterogeneidade estatística foi testada usando teste I2. Uma análise de subgrupo foi realizada considerando métodos de remoção de tecido cariado. O estudo 3 avaliou a resistência de união imediata, e após período de 6 meses, de adesivos experimentais autocondicionantes à SoD e CAD; tais adesivos continham três diferentes concentrações do monômero ácido GDMA-P. Biofilmes de microcosmos originados de saliva humana foram formados sobre discos de dentina e cultivados em anaerobiose por 14 dias. Doze grupos foram definidos com diferentes concentrações de GDMA-P (5%, 20% e 35%), tipo de dentina e período de estocagem. Discos de dentina bovina para cada grupo (n=10) foram incluídos em resina acrílica e o adesivo foi aplicado. Uma matriz de elastômero foi usada para obtenção de dois cilindros (diâmetro 1,5 mm, espessura 0,5 mm) de resina composta na superfície. Os cilindros foram submetidos ao teste de resistência de união após 24h e após 6 meses em uma máquina de Ensaio Universal. Os dados foram analisados por ANOVA e Student-Newman-Keuls (5%). Resultados: No estudo 1, os resultados foram satisfatórios para adesão a cerâmica, resina composta, esmalte e dentina, esta última tanto com a técnica de condicionamento total, como com a autocondicionante. No estudo 2, os sistemas adesivos convencional e autocondicionante aplicados à SoD apresentaram melhores resultados de resistência de união quando comparados aos da CAD. O método 10 utilizado para a remoção de cárie também afetou a resistência de união. No estudo 3, a concentração de GDMA-P e o tipo de substrato interferiram na resistência de união à dentina. Conclusão: Variáveis na formulação dos adesivos interferem no seu desempenho de união a diferentes substratos. Estudos ainda devem ser realizados para se desenvolver uma formulação tida como ideal para substratos mais complexos como CAD. / The main objective of this investigation, divided into three studies, was to assess the bonding strength of commercial and experimental adhesive systems to different substrates, emphasizing caries-affected dentin (CAD), as it is a fairly common substrate in clinical practice and with many doubts to be clarified. Materials and methods: Study 1, to compare the bonding ability of a universal dental adhesive (Scotchbond Universal, 3 M ESPE) to other commercial dental bonding agents applied to different substrates: enamel, sound dentin (SoD), resin composite, and porcelain. Specimens of each substrate were prepared for microtensile bond strength test/µTBS (SoD and composite) or shear bond test/SBS (enamel and porcelain). Data were analyzed using One-Way ANOVA and Tukey’s test (a=0.05). In study 2, the adhesive performance (bonding ability) of dental adhesives applied to sound dentin (SoD) in comparison to caries-affected dentin (CAD) was evaluated through a systematic review of dental literature. A structured search in three international databases (Medline/PubMed, Scopus, and Web of Science) was carried out by two independent reviewers. A total of 2.260 unique articles were found. After excluding articles by title and reading of the abstract, 65 articles were selected for full-text reading, and 40 studies were included in the review. Data were extracted and categorized according to the adhesive system used (etch-and-rinse or self-etch adhesives). The bonding strength mean of the two substrates tested were compared using a randomized effects model (Review Manager Version 5.1). Statistical heterogeneity was tested by using I2 test. A subgroup analysis was carried out to explore the heterogeneity considering the methods used for the removal of caries. Study 3 evaluated immediate and long term shear bonding strength of experimental self-etch adhesives, containing three different concentrations of the acidic monomer GDMA-P, to SoD and CAD. Microcosm biofilms were formed over dentin discs and cultivated under anaerobic conditions for 14 days. Twelve groups were defined by different GDMA-P concentrations (5%, 20%, and 35%), dentin type and storage time. Bovine dentin discs for each group (n=10) were included in acrylic resin and the adhesives were applied. An elastomer mold with cylindrical orifices (1.5 mm diameter) was used to obtain two cylinders of composite resin on the surface. After a period of 24h and 6 months the cylinders were subjected to bond strength test in a mechanical testing machine. Data were analysed by ANOVA and Student-Neuman-Keuls’ test (5%). Results: In Study 1, the results were considered satisfactory for adhesion to ceramic, composite, enamel and dentin, and the latter for both the total etching and self-etching technique. In study 2, the conventional and self-etching adhesive systems applied to SoD showed better bond strength results compared to CAD. The method used for removing carious also affected the bond strength. In 12 study 3, the bond strength to dentin varied with the concentration of GDMA-P and type of substrate. Conclusion: Variables in the formulation of adhesives have impact in their bonding performance to different substrates. Further studies are still necessary to develop an ideal formulation for more complex substrates such as CAD.

Este estudo objetivou investigar a resistência à degradação de restaurações de cimento de ionômero de vidro modificado por resina (CIVMR) e adesivo/resina composta sobre dentina sadia e afetada por cárie de dentes decíduos submetidas a desafio cariogênico e ciclagem mecânica, por meio de teste de microtração e nanoinfiltração. Cavidades oclusais tipo Classe I foram preparadas em 60 molares decíduos esfoliados. Metade dos dentes foi submetida ao processo de indução de cárie artificial, por meio de ciclagem de pH. Os dentes foram aleatoriamente restaurados com um dos dois materiais: um CIVRM (Vitremer®) e um sistema adesivo de condicionamento total (Adper Single Bond 2®) seguido de resina composta (Filtek Z100®). Após 24 horas de armazenagem em água a 37°C, as amostras dos grupos controle seguiram para os procedimentos de teste, enquanto as demais foram re-divididas e submetidas a dois métodos de desafio: desafio cariogênico (ciclagem de pH) e ciclagem mecânica (50.000 ciclos, 90 N, 3 Hz). Para os testes, os dentes foram seccionados em fatias seriadas de aproximadamente 1mm de espessura, das quais uma foi separada para o teste de nanoinfiltração e as demais foram seccionadas no sentido perpendicular de forma a obter espécimes em formato de palito com 1 mm2 de área, que foram fixados a uma máquina de ensaios universal e submetidos ao teste de microtração. Os valores nominais de resistência de união foram registrados em MPa e analisados por meio de ANOVA e testes de comparações múltiplas de Games-Howel (=0,05). As fatias designadas para o teste de nanoinfiltração foram impermeabilizadas com esmalte exceto nas interfaces e imersos em nitrato de prata amoniacal por 24 horas para evidenciação dos espaços nanométricos e sinais de degradação nas interfaces. Após a imersão em solução reveladora, essas fatias foram preparadas e observadas em MEV, utilizando modo de elétrons retroespalhados. A nanoinfiltração nas interfaces foi mensurada com o programa Leica QWin, registradas em m2 e analisadas por meio de ANOVA e teste de comparações múltiplas de Tukey-Kramer. A resistência de união do Vitremer não foi comprometida pela condição da dentina (sadia ou afetada). Contrariamente, o adesivo Single Bond 2® apresentou valores de resistência adesiva significativamente menores quando aderido à dentina afetada por cárie. A ciclagem mecânica não influenciou a resistência de união para ambos os materiais, enquanto o desafio cariogênico resultou em um decréscimo significativo na resistência adesiva do Adper Single Bond 2®, mas não para as restaurações de Vitremer®. O padrão de falha misto foi predominante em todos os grupos. Em relação à nanoinfiltração, o Vitremer® não apresentou diferença no padrão de infiltração em função do substrato sadio ou cariado. Em contrapartida, o adesivo Adper Single Bond 2® apresentou maiores áreas de infiltração de prata nas interfaces com dentina cariada em comparação à dentina sadia. Os desafios cariogênico e mecânico, por sua vez, não influenciaram a infiltração de prata para nenhum dos materiais e substratos. Em conclusão, o substrato cariado e o desafio cariogênico negativamente afetam o comportamento das restaurações de adesivo/resina composta, mas não afetam para as restaurações de CIVRM. / This study aimed to investigate the resistance to degradation of resin modified glass ionomer cement (RMGIC) and adhesive/composite restorations on sound and caries-affected dentin of primary teeth subjected to carious challenge and load-cycling, by means of microtensile test and nanoleakage. Occlusal class I cavities were prepared on sixty sound exfoliated second primary molars. Half teeth were submitted to pH-cycling to induce artificial caries lesion. Teeth were randomly restored with one of the two materials: (1) a RMGIC (Vitremer®) and a (2) a total-etch adhesive system (Adper Single Bond 2®) followed by composite resin (Filtek Z100®). After storage in distilled water 37°C for 24 hours, sample from control groups followed to test procedures while the other ones were re-divided and submitted to two different aging methods: carious challenge (pH-cycling) and load-cycling (50 000 cycles, 90N, 3Hz). For testing, teeth were sectioned into about 1mm slabs, from which, one was separated for nanoleakage testing and the others were perpendicularly sectioned into 1mm2 beams that were tested to failure in tension in a universal testing machine. Data on microtensile bond strengths were registered in MPa and analyzed by ANOVA and Games-Howell multiple-comparisons tests (=0.05). Slabs meant for nanoleakage testing were coated with nail varnish except for the bonded interfaces, and immersed in ammoniacal AgNO3 for 24 hours in order to disclose nanometer-sized spaces and degradation signs within interfaces. After immersion in photodeveloping solution, bonded sections were prepared and observed under SEM using the backscattered electron mode. Nanoleakage patterns at interfaces were measured using Leica QWin, registered in m2 and analyzed by ANOVA and Tukey-Kramers multiple-comparisons tests. Vitremer bond strength was not affected by dentin condition (sound or affected). Conversely, Adper Single Bond 2® showed significantly lower bond strength values when bonded to caries-affected dentin. Load-cycling did not influence bond strength for both materials. While carious challenge resulted in a significant decrease in microtensile bond strengths of Adper Single Bond 2®, but did not for Vitremer restorations. The mixed failure pattern was predominant in all groups. Concerning nanoleakage, Vitremer® did not show difference in leakage pattern between sound and caries-affected dentins. In contrast, the adhesive Adper Single Bond 2®, presented greater leakage areas at affected dentin interfaces than sound ones. The cariogenic and mechanical challenges did not influence silver penetration for none of the materials and substrates. In conclusion, the caries-affected substrate and the cariogenic challenge negatively affected the behavior of the adhesive/composite restorations, but did not affect for RMGIC restorations.

O objetivo da pesquisa foi avaliar a resistência de união entre o titânio fundido e cimentos resinosos, comparada com a de uma liga de níquel-cromo. Os fatores estudados foram: cimentos (Enforce, Cimento de resina 3M, Cement-it); conjugação liga/ revestimento ( titânio obtido com revestimento com a case e sem a case e liga de níquel-cromo, com fosfatado); tratamento superficial ( jateamento com óxido de alumínio e sistema Siloc); desgaste (cimentação antes do desgaste e depois). Para os espécimes foram obtidos discos por fundição, que foram jateados com óxido de alumínio. A metade foi cimentada depois desse tratamento e outra após a aplicação do Siloc. A armazenagem foi por 5 dias fazendo-se termociclagem (1.000 ciclos). Após o rompimento dos espécimes, por ensaio de tração, as superfícies cimentadas foram desgastadas com lixa n o 200 e novamente cimentadas. As conclusões foram: houve grande diferença entre cimentos; o titânio e o níquel-cromo nas devidas condições apresentaram retentividades semelhantes; o Siloc aumentou muito a retenção; o desgaste só influiu um pouco no titânio a case. / The Purpose of the research was to evaluate tensile bond strength of cemented titanium and nickel-chromium alloy cast discs. Factors studied were: Cements (Enforce, Resin cement 3M, Cement-it); Combination alloy/investment ( titanium obtained with a case and without a case investments, and nickel-chromium alloys); surface treatment (sandblasting with Al2O3 and Siloc application): surface abrading (test before and after).Cast discs with fixing stem were sandblasted and half of them were luted in this stage and the other one were luted after Siloc treatment. Specimens were stored for 5 days and thermalcycled (1,000 cycles). After tensile strength test surfaces were abraded and discs were luted again. The conclusions were: cements presented different bond strength; titanium and nickel-chromium alloy, under given condition, presented similar strength; Siloc system presented at least double strength; abrading of a case, titanium enhance only a little bond strength.