Made available in DSpace on 2016-06-02T19:19:54Z (GMT). No. of bitstreams: 1 NOSSA_Tamires_2011.pdf: 2727632 bytes, checksum: ba49f3b87c8b3e85ad1b96be146c2896 (MD5) Previous issue date: 2011-02-08 / Financiadora de Estudos e Projetos / Currently, composite materials are being used in several areas in substitution of some metallic alloys regarding to its superior properties and greater project flexibility. Therefore, synthetic fibers reinforced epoxy resin has some mechanical properties limited by its interface due to the interaction between fiber and matrix. The present research studies the interaction between the materials at the interface, considering the resin interaction with the three most employed composites fiber: carbon fiber, Aramida (Kevlar) and glass fiber (E type). The fibers surfaces were analyzed through the AFM (atomic force microscope) and the Contact Angle Method (CAM), becoming possible to determine the surface energy of each material, the superficial interface energy, the matrix-fiber adhesion and the surface profile analysis. The composites were subjected to the single fiber fragmentation test (SFFT) in order to obtain its interfacial share strength to be applied in the Kelly-Tyson equation. Furthermore, through these analysis became possible to evidence the properties differences between the composites, the individual properties of matrix-fiber that can be obtained, the best matrix-fiber interface, classifying them according to the stress transference magnitude and, consequently, greater effectiveness on the matrix-fiber adhesion. / Atualmente, os materiais compósitos são utilizados em diversas áreas em substituição a algumas ligas metálicas em função de suas propriedades superiores e maior flexibilidade de projeto. No entanto, os compósitos de resina epóxi reforçados com fibras sintéticas possuem algumas propriedades limitadas pela resistência da interface resultante da interação entre fibra e matriz. No presente trabalho estuda-se a interação entre os materiais na interface considerando-se a interação da resina com as três fibras mais comumente utilizadas em compósitos, a fibra de carbono, a aramida (Kevlar®) e a fibra de vidro (tipo E). A superfície das fibras foi analisada através do AFM (do inglês Atomic Force Microscope ) e do CAM (do inglês Contact Angle Method ) para determinação da energia de superfície de cada material, da energia de superfície na interface, da adesão fibra-matriz e da análise do perfil superficial. Os compósitos foram submetidos ao ensaio de fragmentação de filamento (SFFT, do inglês Single Fiber Fragmentation Test ), para a obtenção da resistência ao cisalhamento interfacial utilizou-se a equação de Kelly-Tyson. Através das análises foi possível constatar as diferenças de propriedades entre os compósitos, as propriedades individuais de cada fibra-matriz relacionadas, a melhor interface fibra-matriz, classificando-as de acordo com a magnitude da transferência de tensões e, conseqüentemente, maior efetividade na adesão reforço/matriz.

Made available in DSpace on 2015-08-27T02:21:21Z (GMT). No. of bitstreams: 1 000474158-Texto+Completo-0.pdf: 569 bytes, checksum: afa56a15d273f6dd4f85b576eafd26dd (MD5) Previous issue date: 2015 / In this work, it was evaluated the possibility of using bark of black wattle (Acacia mearnsii) as a corrosion inhibitor in environments with presence of CO2 under high pressure. SAE 1010 carbon steel samples were exposed to two corrosive situations (with and without oxygen) under the conditions of 15 MPa and 70 ºC, with distinct tannin concentrations for different exposure times (168, 360 and 2160 hours). In order to characterize the specimens it was used infrared spectroscopy analysis, Xray diffraction, scanning electron microscopy by field emission, energy dispersive spectroscopy, mass loss and potentiodynamic polarization tests, determining the rate of corrosion and the efficiency tannin as of tannin as inhibitor. The results indicated that the tannin in deaerated environmental has no potential for use as an inhibitor once there was no significant reduction in corrosion rates and, also the formation of ferric-tannates film. Was not observed corrosion rates values, due mass loss, and were classified as severe corrosion, according to values of NACE RP-07-75 and was not inhibition efficiency values higher than 21 % obtained. Nevertheless, in aerated environmental, tannin worked as a barrier to diffusion of O2 and/or complexation of Fe2+ and Fe3+, providing favorable conditions to the formation of FeCO3 film with protective features. The corrosion rates were classified as moderate for 2160 hours, while 168 h and 360 h, as severe, also according to the values of NACE-RP-07-75, reaching values of up to 72% inhibition efficiency. / Neste trabalho, avaliou-se a possibilidade de utilização do tanino vegetal da acácia negra (Acacia mearnsii) como inibidor de corrosão em ambientes com a presença de CO2 a alta pressão. Corpos de prova de aço SAE 1010 foram expostos a dois meios corrosivos (sem e com O2) sob condições de 15 MPa e 70°C, com diferentes concentrações de tanino para diferentes tempos de exposição (168, 360 e 2160 h). Para caracterização foram realizadas análises de espectroscopia de infravermelho, difração de raios X, microscopia eletrônica de varredura por emissão de campo, espectroscopia de energia dispersiva, perda de massa e ensaios de polarização potenciodinâmica, determinando-se a taxa de corrosão e a eficiência do tanino como inibidor. Os resultados indicaram que o tanino, em meio desaerado, não apresenta potencial para utilização como inibidor, pois não houve redução significativa nas taxas de corrosão e também não se observou a formação do filme de ferrotanatos. Todos os valores de taxas de corrosão, por perda de massa, foram classificados como corrosão severa, segundo valores da NACE-RP-07-75 e não se obteve valores de eficiência de inibição maiores que 21 %. No entanto, em meio aerado, o tanino atuou como barreira para a difusão de O2 e/ou na complexação dos óxidos de Fe2+ e Fe3+, formando filmes de ferrotanatos, propiciando condições favoráveis para a formação do filme de FeCO3 com características protetoras. As taxas de corrosão foram classificadas como moderada para 2160 h, enquanto que para 168 h e 360 h, como severa, também segundo valores da NACE-RP-07-75, atingindo-se valores de até 72 % de eficiência de inibição.

Made available in DSpace on 2015-10-24T01:15:12Z (GMT). No. of bitstreams: 1 000475858-Texto+Completo-0.pdf: 569 bytes, checksum: 95c09435c5faf501d607b610fb5734f9 (MD5) Previous issue date: 2015 / The aim of the study was to evaluate the association of different aging methods on bond strength values of composite repair, through the use of shear test. 96 samples of rectangular section were made with the microhybrid composite Point 4 (Kerr) and were divided into 8 groups (n = 12) as follows: (1) immersion in distilled water for 7 days; (2) immersion in distilled water for 30 days; (3) immersion in citric acid for 7 days; (4) immersion in boiling water for 8 hours; (5) immersion in distilled water for 30 days plus immersion in citric acid for 7 days; (6) immersion in distilled water for 30 days plus immersion in boiling water for 8 hours; (7) immersion in citric acid for 7 days plus immersion in boiling water for 8 hours and (8) immersion in distilled water for 30 days plus immersion in citric acid for 7 days plus immersion in boiling water for 8 hours. After going through the designated method of aging the treatment of prerepair was conducted with roughening the surface with sandpaper grain silicon carbide 120 and application of the adhesive system Single Bond 2 (3MESPE) and then made a repair with the same composite resin. The samples were tested in a universal testing machine (EMIC) for the shear bond strength test at a loading speed of 1mm / min. After the failure all samples were evaluated in an increase of 35x stereomicroscope and two samples from each group were evaluated in the SEM as surface after aging and after roughening with sandpaper silicon carbide. The results for evaluation of values in the bond strength test were subjected to statistical test analysis of variance (ANOVA) followed by Tukey test (p <0. 05) and no significant differences between the groups tested were found. The evaluation of failure occurred in stereomicroscope were made in a descriptive way, with all samples of all groups presented cohesive failures in the aged resin. Conclusion: The association of different aging methods does not influence the bond strength values of resin repairs made when the roughening method simulating diamond burs coarse-grained is used pre-repair. / O objetivo do estudo foi avaliar a influência da associação de diferentes métodos de envelhecimento nos valores de resistência de união de reparos de resina composta, através da utilização de teste de cisalhamento. Foram confeccionadas 96 amostras com a resina composta microhíbrida Point 4 (Kerr) de secção retangular que foram divididas em 8 grupos (n=12) sendo: (1) imersão em água destilada por 7 dias; (2) imersão em água destilada por 30 dias; (3) imersão em ácido cítrico por 7 dias; (4) imersão em água em ebulição por 8 horas; (5) imersão em água destilada por 30 dias mais imersão em ácido cítrico por 7 dias; (6) imersão em água destilada por 30 dias mais imersão em água em ebulição por 8 horas; (7) imersão em ácido cítrico por 7 dias mais imersão em água em ebulição por 8 horas e (8) imersão em água destilada por 30 dias mais imersão em ácido cítrico por 7 dias mais imersão em água em ebulição por 8 horas. Após passarem pelo método de envelhecimento designado, foi realizado o tratamento de superfície pré-reparo com asperização com lixa de carbeto de silício de granulação 120 e aplicação do sistema adesivo Single Bond 2 (3MESPE) e então, confeccionado um reparo com a mesma resina composta. As amostras foram testadas em uma máquina de ensaio universal (EMIC) para o teste de cisalhamento a uma velocidade de carregamento de 1mm/min. Após a falha todas as amostras foram avaliadas no estereomicroscópio com aumento de 35x e duas amostras de cada grupo foram avaliadas em MEV quanto à superfície após o envelhecimento e após a asperização com lixas de carbeto de silício. Os resultados para avaliação dos valores no teste de resistência de união foram submetidos ao teste estatístico de análise de variância (ANOVA) seguido do teste de Tukey (p<0,05) e não foram encontradas diferenças significativas entre os grupos testados. A avaliação no estereomicroscópio das falhas ocorridas foram feitas de forma descritiva, sendo que todas as amostras de todos os grupos apresentaram falhas coesivas na resina envelhecida. Conclusão: a associação de diferentes métodos de envelhecimento não influencia nos valores de resistência de união em reparos de resina composta, quando o método de asperização simulando pontas diamantadas de granulação grossa é utilizado pré-reparo.

Made available in DSpace on 2016-04-08T03:07:20Z (GMT). No. of bitstreams: 1 000477933-Texto+Parcial-0.pdf: 595 bytes, checksum: 8ccd12258e81b131d7c7c402a8049829 (MD5) Previous issue date: 2016 / Objectives: The aim of this in vitro study was to compare the maximal load resistance of endodontically treated molars restored with: inlays or onlays of Lava Ultimate, composite resin Z350 XT with or without fiberglass post. Methods: Fifty sound extracted third molars were embedded in acrylic resin and divided into 5 groups (n = 10 per group): H = healthy, ON = onlay, IN = inlay, RC = composite resin, PT = fiberglass post + Z350 XT. The MOD preparations and endodontic treatment were performed. Indirect restorations were made through CAD/CAM CEREC system and cemented with SingleBond Universal and RelyX Ultimate under load of 1 kg. Restorations of RC and PT groups were performed by incremental technique and the two posts in the PT group were horizontally transfixed and bonded with flowable resin. Then, mechanical loading in all samples were performed in 500. 000 cycles at 200 N at a frequency of 1 cycle / second and the maximum load test was performed in a universal testing machine at a speed of 1 mm / min. After the mechanical test, the faults were categorized into pulpal floor fracture (irreparable) and cuspal fracture (repairable).Results: Mean values were (means followed by the same letter show no significant difference to ANOVA and Tukey): RC 1680N ± 454 d; PT 2693N ± 372 bc; ON 2922N ± 774 b; IN 2053N ± 313 cd; H 4514N ± 548 a. The predominant failure pattern for teeth restored with onlays, inlays and direct composite resin with or without post was the irreparable type. Conclusion: Endodontically treated molars restored with transfixed fiberglass post and composite resin have similar fracture resistance to those restored with indirect Lava Ultimate inlay and onlay. Horizontally fiber post restoration has the same efficiency that onlays restoration. / Objetivos: O objetivo deste estudo foi avaliar e comparar in vitro a resistência máxima ao carregamento de molares tratados endodonticamente e restaurados com: inlays ou onlays de Lava Ultimate, resina composta Z350 XT com ou sem pino de fibra de vidro transfixado. Materiais e métodos: Cinquenta terceiros molares hígidos extraídos foram incluídos em acrílico autopolimerizável e divididos em 5 grupos (n = 10 por grupo): H = hígido, ON = onlay, IN = inlay, RC = resina composta, PT = pino de fibra de vidro + Z350 XT. Em seguida, foram realizados os preparos MOD e o tratamento endodôntico. As restaurações indiretas foram confeccionadas através do sistema CAD/CAM CEREC e cimentadas com SingleBond Universal e RelyX Ultimate sob carga de 1 Kg. As restaurações do grupo RC e PT foram realizadas pela técnica incremental e os dois pinos no grupo PT foram transfixados horizontalmente e colados com resina flowable. Após, os corpos de prova foram submetidos a 500. 000 ciclos de fadiga mecânica sob carga vertical de 200 N na frequência de 1 ciclo/segundo. Na sequência, foi aplicado o teste de carga máxima de carregamento em máquina de ensaio universal a uma velocidade de 1 mm/min. Após o ensaio mecânico, as falhas foram categorizadas em fratura de assoalho pulpar (irreparáveis) e fraturas de cúspides (reparáveis).Resultados: Os valores médios obtidos foram (médias seguidas de mesma letra não apresentam diferença estatística para ANOVA e Tukey): RC 1680N ± 454 d; PT 2693N ± 372 bc; ON 2922N ± 774 b; IN 2053N ± 313 cd; H 4514N ± 548 a. O padrão de falha predominante para dentes restaurados com onlays, inlays e resina composta direta com ou sem pino foi do tipo irreparável. Conclusão: Molares endodonticamente tratados e restaurados com pinos de fibra de vidro transfixado e resina composta Z350 XT direta apresentam resistência à fratura similar às restaurações indiretas tipo inlay e onlay de Lava Ultimate. Restaurações com pino transfixado horizontalmente possuem a mesma eficácia que as restaurações onlays.

Made available in DSpace on 2014-07-04T02:02:33Z (GMT). No. of bitstreams: 1 000459061-Texto+Completo-0.pdf: 2282963 bytes, checksum: c9b1fec421065d44d34540a0b1217b0a (MD5) Previous issue date: 2014 / The aim of this study was to evaluate the bond strength of Scotchbond Universal to dentin in both total-etch and self-etch applications after storage in water for 24 h and 6 months. The occlusal surface of 24 third molars was removed to obtain flat dentin surfaces, and the teeth were divided into four groups (n=6/grupo): G1 – total-etch application of Scotchbond Universal; G2 – self-etch application of Scotchbond Universal; G3 – Scotchbond Multi Purpose (total-etch application control); G4 – Clearfil SE Bond (self-etch application control). Following the adhesive application, a 6 mm height block of composite resin Z250 was built on the adhesive area. After storage in distilled water at 37ºC for 24 hours, the tooth/resin sets were cut parallel to the long axis of the tooth, in the x and y directions, with a section of about 0. 8 mm2. Forty specimens were obtained for each group; 20 specimens were immediately submitted to microtensile bond strength test, and the others after storage in distilled water at 37o C for 6 months. The microtensile bond strength test was performed in an universal testing machine (EMIC-DL 2000) at 0. 5 mm/min crosshead speed. The failures were observed in scanning electron microscopy (SEM). Additionally, two sets of each group were sectioned mesio-distal in the center of their crown with a diamond blade. The surfaces were polished by wet sanding with 400, 600 and 1200-grit silicon carbide abrasive paper, followed by polishing with 6, 3, 1 and ¼ m diamond paste.The samples were demineralized, deproteinized, dried, metalized and observed on a scanning electron microscope at 1. 500x. The bond strength means (MPa) obtained were the following: 24 h – G1 (39. 37); G2 (31. 02); G3 (35. 09); G4 (35. 84); 6 months – G1 (36. 99); G2 (40. 58); G3 (32. 44); G4 (41. 75). According to two-way ANOVA, there was no significance for adhesive system (p=0,110) and storage time (0,108), but the interaction of adhesive system and storage time was significant (p=0. 015). At 24 h, there was no statistical difference in bond strength between the adhesive systems (p>0,05). At 6 months, there was statistical difference between the adhesive systems (p<0. 05). Clearfil SE Bond obtained the higher bond strength mean, not differing statistically from self-etch application of Scotchbond Universal. Total-etch application of Scotchbond Universal did not differ statistically from Scotchbond Multi Purpose. Most of failures were mixed in both periods of evaluation.The SEM images of the adhesive interface of Scotchbond Universal total-etch application and Scotchbond Multi Purpose showed thicker hybrid layers and more resin tags in comparison with Scotchbond Universal self-etch application and Clearfil SE Bond. It was concluded that the simplification of Scotchbond Universal in one bottle did not decrease the bond strength of this adhesive to dentin during 6 months of storage. / O objetivo do estudo foi avaliar a resistência de união à dentina do sistema adesivo Scotchbond Universal na versão total-etch e self-etch em 24 horas e 6 meses de armazenamento. A superfície oclusal de 24 dentes terceiros molares hígidos foi removida para obter superfície plana em dentina, sendo divididos aleatoriamente em quatro grupos (n=6/grupo): G1 - Scotchbond Universal na versão total-etch; G2 – Scotchbond Universal na versão self-etch; G3 – Scotchbond Multi Purpose (controle da versão total-etch); G4 – Clearfil SE Bond (controle da versão self-etch). Sobre o sistema adesivo foi confeccionado um bloco de 6 mm de altura em resina composta Z250. Após 24 horas de armazenagem em água destilada a 37º C, os conjuntos dente/resina foram cortados paralelamente no longo eixo do dente, nos sentidos x e y, com secção de aproximadamente 0,8 mm2. Quarenta corpos de prova foram obtidos para cada grupo, sendo 20 submetidos imediatamente ao teste de resistência à microtração e, os outros 20, após 6 meses de armazenamento em água destilada a 37º C. O ensaio de microtração foi realizado em uma máquina de ensaio universal EMIC DL-2000, com uma velocidade de 0,5 mm/min. Os tipos de falha foram observados em microscopia eletrônica de varredura (MEV).Adicionalmente, dois conjuntos dente/resina foram preparados e seccionados no sentido mésio-distal, no centro de suas coroas, com um disco diamantado de dupla face. As superfícies foram polidas com lixas de carbeto de silício 400, 600 e 1200, seguido de polimento com pastas diamantadas de granulação 6, 3, 1 e ¼ m. As amostras foram desmineralizadas, desproteinizadas, secadas, metalizadas e observadas em MEV em aumento de 1. 500 vezes. No teste de microtração as médias obtidas (MPa) foram as seguintes: 24 h – G1 (39,37); G2 (31,02); G3 (35,09); G4 (35,84); 6 meses – G1 (36,99); G2 (40,58); G3 (32,44); G4 (41,75). De acordo com o teste ANOVA de duas vias não houve significância para o sistema adesivo (p=0,110) e para o tempo (0,108), mas apenas para a interação entre sistema adesivo e tempo (p=0,015). No período de 24 horas, não houve diferença estatística significativa na resistência à microtração entre os sistemas adesivos (p>0,05). Na avaliação de seis meses de armazenamento, houve diferença estatística entre os sistemas adesivos (p<0,05). O Clearfil SE Bond apresentou o maior valor médio de resistência à microtração, não diferindo estatisticamente do Scotchbond Universal self-etch e total-etch. O Scotchbond Universal total-etch não diferiu estatisticamente do Scotchbond Multi Purpose.Os tipos de falha foram predominantemente mistas para os dois períodos de avaliação. A interface adesiva do Scotchbond Universal na versão total-etch e o Scotchbond Multi Purpose apresentaram camada híbrida mais espessa e mais tags de resina em comparação ao Scotchbond Universal na versão self-etch e Clearfil SE Bond. Concluiu-se que a simplificação em frasco único do Scotchbond Universal não causou diminuição nos valores de resistência de união deste material à dentina em até 6 meses de avaliação.

Made available in DSpace on 2014-08-20T02:02:10Z (GMT). No. of bitstreams: 1 000459626-Texto+Parcial-0.pdf: 120396 bytes, checksum: a65ae75d299912b9f56c5f620ace594e (MD5) Previous issue date: 2014 / This research is related to the investigation of new approaches for noninvasive imaging that allow registering the internal architecture of sedimentary deposits generated in hydraulic simulation tanks. The simulations are conducted to better understand the behavior of turbiditic currents, one of the principal process responsible for the deposition of sediments in deep oceanic waters. For this reason it is purpose of this work the preparation of polymer nanocomposite with inorganic filler for non-destructive testing, with properties and characteristics similar to Coal 205, material currently used in these simulations. As polimeric matrix it was used an orthophthalic polyester resin prepared by mass polymerization, with dyes in different colors and inserting inorganic filler at different concentrations. Barium sulfate was used as the inorganic filler. Using the X-ray tomography tests, it was observed that barium sulfate provides the opacity needed for detection technique and shows potential to be used in non-invasive imaging at the simulations. Through scanning electron microscopy (SEM) it was possible to assess the prepared polymer matrix and classify it as semi-angular and semi-rounded shape. Also was observed at the SEM micrographs that the barium sulfate prepared it was in nanometer dimension. The prepared composites presented specific weight and settling velocity speed values similar to Coal 205 and it was observed that the incorporation of the filler and the different dyes did not affected significantly the desired characteristics. / Este trabalho de pesquisa está relacionado com a investigação de novas abordagens de imageamento não-invasivo que permitam registrar a arquitetura interna de depósitos sedimentares gerados em tanques de simulação hidráulica. Estas simulações são realizadas para melhor compreensão do comportamento das correntes de densidade, que constituem uma das principais responsáveis pela deposição de sedimentos em águas oceânicas profundas. Para isto foi proposta deste trabalho o preparo de nanocompósito polimérico com carga inorgânica para ensaios não destrutivos, com as propriedades e características semelhantes ao Carvão 205, material atualmente utilizado nas simulações. Como matriz polimérica foi utilizada a resina poliéster, preparada por polimerização em massa, com corantes de diferentes cores e inserção de carga inorgânica em diferentes concentrações. Como carga inorgânica foi utilizado o sulfato de bário. Por ensaios de tomografia de raios-X, observou-se que o sulfato de bário disperso na matriz de resina poliéster oferece a opacidade necessária para detecção pela técnica e se mostra potencial para uso nas simulações e imageamento não-invasivo. Por meio de microscopia eletrônica de varredura (MEV) foi possível avaliar a forma da matriz polimérica preparada e classifica-la com forma semi-angular e semi-arredondada. Também foi possível observar nas micrografias obtidas por MEV que a carga de sulfato de bário preparada apresentou dimensões nanométricas. Os compósitos preparados apresentaram valores de peso específico e velocidade de queda comparáveis com os do Carvão 205 e observou-se que a incorporação de corante e carga não influencia significativamente as características desejadas. Desta forma, os compósitos preparados se mostram com potencial para uso nas simulações de correntes de densidade não conservativas.

Made available in DSpace on 2011-12-27T14:14:11Z (GMT). No. of bitstreams: 2 000424760-0.pdf: 9386318 bytes, checksum: 55f075ab7be050ba8f670a49a394022b (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The aim of this in vitro study was to access the strength produced by the nickel titanium closed-coil springs from three different comercial brands (American Orthodontics®, TP orthodontics® and Morelli®) as well as elastomeric chains from two brands available in the market (American Orthodontics® – Memory Chain e Morelli® – conventional) when submitted to 50% and 100% distensions from initial length and then check their strength behavior within time. Both strength values were measured within five intervals of initial 3, 4, 6 and 9 weeks. The sample included 240 nickel titanium closed-coil springs and 80 of the elastomeric chains segments were divided into 16 groups according to the type of material, either nickel titanium closed-coil spring or elastomeric chains, commercial brand and distension submitted. Each group had 20 samples, distended in 50% or 100% from initial length and were kept distended on steel plates immersed in artificial salive solution at the steady temperature of 37ºC. The strength developed by the samples was assessed through a tension test carried out by a mechanic essay machine Emic DL2000® at a 0,5mm/minute speed. The results were submitted to statistical ANOVA and Tukey tests. The NiTi closed coil springs and elastomeric chains distended 50% of the initial length showed initial force between 126. 3 and 267. 5 gf and between 192. 6 and 267. 8 gf, respectively; in the end of nine weeks the average strength was between 131. 7 and 263 gf for the NiTi closed coil springs and between 123. 7 and 141. 3 gf for elastomeric chains. Distension of 100% of initial length of the average initial force produced by the NiTi closed coil springs was between 214. 3 and 451. 5 gf and elastomeric chains between 306. 6 and 380. 5 gf, after nine weeks of average strength remained between 196. 7 and 397. 3 gf for the NiTi closed coil springs and between 179. 4 and 189. 3 gf for elastomeric chains. Such results indicated. / O objetivo do presente estudo foi avaliar, in vitro, as forças produzidas pelas molas fechadas de níquel-titânio de três marcas comerciais diferentes (American Orthodontics®, TP orthodontics® e Morelli®) e cadeias elásticas de duas marcas disponíveis comercialmente (American Orthodontics® – Memory Chain e Morelli® – convencional) quando submetidas a distensões de 50% e 100% do comprimento inicial e verificar o comportamento destas forças ao longo do tempo. As forças foram aferidas em cinco intervalos de tempo: inicial, 3, 4, 6 e 9 semanas. Para tanto 240 molas fechadas de níquel-titânio e 80 segmentos de cadeias elásticas foram divididos em 16 grupos de acordo com o tipo de material, mola fechada de níqueltitânio ou cadeia elástica, marca comercial e distensão submetida. Para cada grupo 20 amostras foram distendidas em 50% ou 100% do comprimento inicial e assim mantidas em placas de aço e imersas em solução de saliva artificial à temperatura constante de 37ºC. As forças desenvolvidas pelas amostras foram aferidas através de um teste de tração realizado por uma máquina de ensaio mecânico Emic DL2000® à velocidade de 0,5mm/minuto. Os resultados foram submetidos a testes estatísticos ANOVA e Tukey. As molas fechadas de NiTi e cadeias elásticas distendidas 50% do comprimento inicial apresentaram força inicial entre 126,3 e 267,5 gf e entre 192,6 e 267,8 gf, respectivamente; ao final de 9 semanas a média de força ficou entre 131,7 e 263 gf para as molas fechadas e entre 123,7 e 141,3 gf para as cadeias elásticas. Na distensão de 100% do comprimento inicial a média de força inicial apresentada pelas molas fechadas de NiTi ficou entre 214,3 e 451,5 gf e para as cadeias elásticas entre 306,6 e 380,5 gf; após 9 semanas a média de força permaneceu entre 196,7 e 397,3 gf para as molas fechadas de NiTi e entre 179,4 e 189,3 gf para as cadeias elásticas. Os resultados indicaram que tanto as molas fechadas de níquel-titânio como as cadeias elásticas desenvolveram forças iniciais maiores e maior taxa de degradação da força ao longo do tempo quando distendidas 100% do comprimento inicial quando comparadas a distensão de 50%. As molas fechadas de NiTi apresentaram menores percentuais de degradação da força do que as cadeias elásticas nas duas distensões avaliadas.

Made available in DSpace on 2011-12-27T14:14:33Z (GMT). No. of bitstreams: 2 000431091-0.pdf: 6484611 bytes, checksum: ee0b40e71498d6a5f8496211522ca10f (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The aim of this study was to evaluate the influence of four resin cements (one conventional and three self-adhesive) on cuspal deflection, fracture load and failure mode of endodontically treated teeth restored with composite resin inlays. Seventy-two maxillary premolars were randomly divided into four groups: G1 - sound teeth (control); G2 - cavities without restoration; G3 - RelyX ARC; G4 - RelyX U100; G5 - Maxcem Elite; G6 - SeT. The teeth from groups 2, 3, 4, 5 and 6 received mesio-occlusal-distal preparations and endodontic treatment. Impressions were made with vinyl polysiloxane and poured using type IV die stone in groups 3, 4, 5 and 6. Inlays with Z350 XT composite resin were built over each cast and luted with the resin cements. After storage in water at 37o C for 72 hours, a 200-N load was applied on the occlusal face using an 8 mm diameter metal sphere, and the cuspal deflection was measured using a micrometer. Following, the specimens were submitted to 500,000 cycles of mechanical fatigue, and the cuspal deflection was measured again. The specimens were then submitted to an axial load until failure. According to Kruskal-Wallis, group 2 (69 μm) had the highest cuspal deflection before mechanical fatigue, and did not differ statistically from group 6 (51 μm). Group 1 (4 μm), group 3 (4 μm) and group 4 (5 μm) obtained the lowest cuspal deflections, and did not differ between them. Intermediate value was obtained for group 5 (21 μm), and this group did not differ statistically from groups 3, 4 and 6. According to Wilcoxon test, there was no statistically difference between the cuspal deflection before and after mechanical fatigue only for group 3 (p=0,015). According to Kruskal- Wallis, group 1 (1902 N) had the highest fracture load, and differed statistically from the other groups. The second highest value was obtained for group 3 (980,8 N), and differed statistically from the other groups. Group 4 (670,6 N), group 5 (533,5 N), group 6 (601,3 N) and group 2 (526,6 N) did not differ between them. There was a predominance of recovery fractures for the restored groups. Composite resin inlays luted with RelyX ARC kept the cuspal deflection stability, obtained higher strength of the teeth, as well as fractures with good prognosis for rehabilitation. / O objetivo desse estudo foi avaliar a influência de quatro cimentos resinosos (um convencional e três autoadesivos) na deflexão de cúspides, carga de fratura e tipos de fratura de pré-molares com acesso endodôntico e restaurados com inlays em resina composta. Setenta e dois primeiros pré-molares foram divididos aleatoriamente em seis grupos (n=12): G1 (controle) - hígidos; G2 – cavidades sem restauração; G3 –RelyX ARC; G4 –RelyX U100; G5- Maxcem Elite; G6 –SeT. Os Grupos 2-6 receberam preparos cavitários MOD e acesso endodôntico. Os grupos 3-6 foram moldados com silicona por adição e vazados com gesso especial para confecção de inlays em resina composta Z350 XT. As restaurações indiretas foram cimentadas nas respectivas cavidades com carga de 1 Kg e fotoativadas. Após armazenagem em água destilada a 37º C por 72 horas, carga de 200 N foi aplicada na região oclusal com uma esfera de 8 mm de diâmetro acoplada na máquina de ensaio universal EMIC DL 2000, sendo medida a deflexão de cúspides com um micrômetro digital. Os corpos de prova foram então submetidos a 500. 000 ciclos de fadiga mecânica, e novo teste de deflexão de cúspides foi realizado. Em seguida, os corpos de prova foram submetidos ao ensaio de compressão até a fratura na máquina de ensaio universal. De acordo com o teste de Kruskal-Wallis, a maior deflexão de cúspides pré-fadiga foi obtida para o grupo 2 (69 μm), não diferindo estatisticamente do grupo 6 (51 μm). As menores deflexões de cúspides foram obtidas para o grupo 1 (4 μm), o grupo 3 (4 μm) e o grupo 4 (5 μm), os quais não diferiram estatisticamente entre si. Valor intermediário foi obtido para o grupo 5 (21 μm), não diferindo estatisticamente dos grupos 3, 4 e 6. De acordo com o teste de Wilcoxon, não houve diferença estatística entre a deflexão de cúspides pré e pós-fadiga apenas para o grupo 3 (p=0,015). De acordo com Kruskal-Wallis, a maior carga de fratura foi obtida para o grupo 1 (1902 N), diferindo estatisticamente dos outros grupos. Segundo maior valor foi obtido para o grupo 3 (980,8 N), diferindo estatisticamente dos outros grupos. Grupo 4 (670,6 N), grupo 5 (533,5 N), grupo 6 (601,3 N) e grupo 2 (526,6 N) não diferiram estatisticamente entre si. Para os grupos restaurados, houve predominância de fraturas recuperáveis. Inlays em resina composta cimentadas com RelyX ARC mantiveram a estabilidade da deflexão de cúspides, proporcionaram maior recuperação da resistência da estrutura dentária, assim como fraturas mais favoráveis para a reabilitação.

Made available in DSpace on 2011-12-27T14:14:19Z (GMT). No. of bitstreams: 2 000415566-0.pdf: 1518608 bytes, checksum: bd39955631082d183040d1bec6aef520 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The aim of this split mouth randomized clinical trial was to evaluate and compare the space closure during the retraction of upper permanent canine with self-ligating"SmartClip" and conventional"Gemini" brackets. Sample complied 13 patients with Class I biprotrusion or Class II 1st division malocclusion, with an average age of 18 years and 4 months, 3 male and 10 female. All were submitted to the therapeutic extraction of two first premolars. The retraction of the upper canines was performed with elastomeric chain with 150g of force. The evaluations were performed at four times (T1 – initial, T2 – 4 weeks, T3 – 8 weeks, T4 – 12 weeks) in stone model casts. The amount of movement and the rotation of the canines as well anchorage loss of upper first molars were evaluated. The space closure measurement was made between canine and second premolar and rotation was assessed by an angle formed by the intersection of the line drawn through the canine’s contact points and the line of the palatal suture. The anchorage loss was measured by a guide adapted at the palatal rugae in stone casts at initial and end. The data obtained were subjected to Student t test considering level of significance of 5%.The results shown that selfligating bracket had an average of 0. 92 mm (+/- 0. 29) of rate movement and 8. 46o (+/- 4. 68) of the rotation of the upper canines and 0. 65 mm (+/- 0. 24) of anchorage loss; the conventional bracket had an average of 0. 84 mm (+/- 0. 22) of rate movement and 11. 77o (+/- 3. 26) of the rotation of and the upper canines and 0. 57 mm (+/- 0. 24) of anchorage loss. There was no difference (p=0. 250) in the rate of movement of the canines between the two types de brackets. The rotational control of the canines was better promoted by self-ligating bracket (p=0. 005). There was anchorage loss for both groups, with no statistical difference between them (p=0. 157). / O objetivo desse trabalho foi avaliar a influência de diferentes cimentos resinosos na deflexão de cúspides e na carga de fratura de dentes com tratamento endodôntico. Quarenta pré-molares superiores foram divididos aleatoriamente em quatro grupos: 1 – hígidos; 2 - RelyX ARC; 3 - RelyX U100; 4 - Maxcem. Os dentes dos grupos 2, 3 e 4 receberam preparos MOD, seguido de moldagem com silicone por adição e vazamento de gesso tipo IV. Sobre cada modelo foi confeccionada uma restauração inlay em resina composta Z250. As restaurações foram cimentadas com os cimentos resinosos, de acordo com cada grupo experimental, seguindo as instruções dos fabricantes. Os corpos-de-prova foram armazenados em água destilada a 37º C por 24 horas. Em máquina de ensaio universal, uma carga de 200 N foi aplicada na região oclusal com esfera de aço de 8 mm de diâmetro e, com o auxílio de um micrômetro posicionado nas faces vestibular e palatina, a deflexão das cúspides foi medida antes e após a carga. Em seguida, os corpos-de-prova foram submetidos à compressão axial com a esfera de aço até ocorrer a fratura. De acordo com ANOVA e teste de Tukey (a = 0,05), o grupo 1 apresentou a menor média de deflexão de cúspide (4μm), não diferindo estatisticamente do grupo 2 (12μm) (p>0,05). O grupo 3 (39μm) e 4 (56μm) apresentaram as maiores médias, diferindo estatisticamente dos grupos 1 e 2 (p<0,05). O grupo 1 teve a maior média de carga de fratura (1982 N), diferindo estatisticamente dos grupos 2 (690 N), 3 (465 N) e 4 (679 N), os quais não diferiram entre si. As inlays fixadas com os cimentos resinosos auto-adesivos RelyX U100 e Maxcem proporcionaram maior deflexão de cúspides. Os valores de carga de fratura para as inlays fixadas com os cimentos resinosos foram semelhantes entre si e não reproduziram a carga de fratura dos dentes hígidos.Houve predominância de falhas consideradas recuperáveis, independente do cimento resinoso empregado.

Made available in DSpace on 2011-12-27T14:14:36Z (GMT). No. of bitstreams: 2 000435512-0.pdf: 973133 bytes, checksum: 14d9f2dc06508d0c9d2ae12d36de90f5 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / Introduction: To determine whether a correlation between water absorption and diametral tensile strength (DTS) exists, two orthodontic adhesives - one of hydrophilic (Transbond Plus Color Change), and other of hydrophobic nature (Transbond XT) - were tested.Methods: Samples were divided into 4 groups (n = 10 each) according to the variables cement type and storage condition (Group I, XT dry; Group II, XT wet; Group III, Plus dry; and Group IV, Plus wet). After measuring and weighting, samples from groups I and III were kept dry, while those from groups II and IV were immersed in distilled water for 72 h. Then, all samples were stored at 37°C for 72 h, re-weighted and re-measured. Statistical analyses assessed significant differences among the groups.Results: Water absorption was significantly higher in group IV when compared to group II (p = 0. 004). As for DTS, group IV values were significantly lower than those obtained from the other groups. A significant correlation between water absorption and diametrical tensile could not be demonstrated. Conclusion: Our results suggest that Transbond Plus Color Change samples, after immersion in distilled water, absorbs more water and has lower DTS values than those obtained from wet and dry Transbond XT samples. / Introdução: Este estudo foi conduzido com o objetivo de avaliar a correlação entre absorção de água e tração diametral de dois cimentos resinosos, um com características hidrofílicas (Transbond Plus Color Change) e outro com características hidrofóbicas (Transbond XT).Métodos: Quarenta amostras divididas em 4 grupos (n=10), de acordo com as variáveis tipo de cimento e meio de armazenagem (seco ou imerso em água destilada). Grupo I (controle): XT seco. Grupo II: XT úmido. Grupo III (controle): Plus seco. Grupo IV: Plus úmido. As amostras dos grupos I e III, medidas e pesadas, foram mantidas secas. Os grupos II e IV imersos em água destilada (100 ml) por 72 horas. Todas armazenadas em estufa (37oC, 72 horas), pesadas e medidas novamente. Para análise estatística foi utilizado o teste t de Student, análise de variância, teste de comparações múltiplas de Tukey e análise de correlação de Pearson. Nível de significância máximo de 5% para todos os testes.Resultados: Para absorção de água o grupo IV apresentou valores significativamente superiores aos do grupo II (p=0,004). Para tração diametral o grupo IV apresenta valores significativamente inferiores aos outros grupos, seguido pelo grupo III. Não houve correlação significativa entre absorção de água e tração diametral. Conclusão: Os resultados indicam que a Transbond Plus Color Change, após imersão em água destilada, absorve mais água e tem menor resistência à tração diametral do que Transbond XT imersa em água destilada ou em ambiente seco.