Made available in DSpace on 2014-06-11T19:24:37Z (GMT). No. of bitstreams: 0 Previous issue date: 2009-07-20Bitstream added on 2014-06-13T20:52:11Z : No. of bitstreams: 1 aivazoglou_mu_me_sjc.pdf: 824575 bytes, checksum: 4e12578b1bcd3f46a9498806051844fd (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo deste trabalho foi avaliar a ação das soluções de armazenamento: água destilada (G1), solução de timol a 0,05%(G2), formalina a 10%(G3), e hipoclorito de sódio a 1%(G4), bem como os métodos de esterilização por autoclave (A) e radiação gama (B), e as associações dos dois fatores, sobre a microdureza da dentina radicular de terceiros molares extraídos. Os dados obtidos foram submetidos aos testes t de Student, ANOVA a 2 e 3 fatores, e teste de Tukey, todos com α=0,05. Quanto ao armazenamento, o G1(nos dois períodos avaliados) foi o único grupo que não alterou significantemente a microdureza, sendo seguido pelos grupos G2 e G3 (7 dias), G2 e G3 (28 dias), e G4 (7 e 28 dias), tendo estes dois últimos subgrupos apresentado as maiores perdas de microdureza. Na análise da esterilização isoladamente, não houve diferença significante para os 2 métodos quando comparadas as microdurezas iniciais e após a esterilização (autoclave: p=0,144; raios gama: p=0,827), apesar da esterilização por autoclave ter induzido diferenças significantes no grupo armazenado por 28 dias em água destilada. Entretanto, estudada a interação de todos os fatores, encontraram-se diferenças significantes quanto à solução empregada, método de esterilização e interações entre eles (p<0,05). Com base nos dados analisados pôde-se concluir que o armazenamento em água destilada não alterou a microdureza dentinária radicular, e sua associação à esterilização por radiação gama foi o melhor método para o armazenamento e esterilização de dentes, no que diz respeito às influências sobre a variável estudada, sendo indicados para dentes extraídos a serem utilizados em pesquisa. / The aim of this study was to evaluate the effect of storage solutions: distilled water (G1), 0.05% thymol solution (G2), 10% formalin (G3), and 1% sodium hypochlorite (G4); sterilization methods- steam autoclaving (A) and gamma irradiation (B)- and the associations between the two factors on the root dentin microhardness of extracted human third molars. Data were subjected to student’s t test for dependent samples, Two and Three-way ANOVA, and Tukey’s test (α = 0.05 for all tests). Regarding storage, only the G1 (in both periods) did not alter the dentin microhardnes significantly. In the analysis of sterilization methods, there were significant differences on the solution employed, storage time and sterilization method (p <0.05). Based on the results, it was concluded that the storage in distilled water did not change the root dentin microhardness, and association of this storage solution with sterilization by Gamma radiation did not produce alterations by means of the studied variable, thus consisting in the best methods regarding storage and sterilization of teeth to be used in research.

Estudos têm mostrado que a dentina pode ser modificada pelo laser pulsado de CO2 tornando-a um substrato mais ácido-resistente. Este estudo in vitro se propôs a avaliar o efeito do laser de CO2, associado ou não à aplicação tópica de flúor, na redução da desmineralização de superfícies radiculares humanas, utilizando um laser pulsado de comprimento de onda 10,6 m. Cinquenta superfícies radiculares humanas obtidas de vinte e cinco terceiros molares foram aleatoriamente divididas em 5 grupos (n=10) com os seguintes tratamentos de superfície: G1 Nenhum tratamento (controle negativo), G2 Flúor Fosfato Acidulado (FFA- controle positivo), G3 Laser 4,0 J/cm2, G4 Laser 4,0 J/cm2 + FFA e G5 FFA + Laser 4,0 J/cm2. Após o tratamento da superfície, os espécimes foram submetidos a 7 dias de ciclagem de pH, permanecendo diariamente em soluções desmineralizadora e remineralizadora por 3 h e 21 h, respectivamente. Após o desafio ácido, os espécimes foram avaliados para determinar a perda mineral por meio do QLF. Pode-se concluir que o laser de CO2, associado ou não à aplicação tópica de flúor, é capaz de inibir a desmineralização da superfície radicular, contudo não se observa efeito sinérgico com a associação da irradiação com laser e tratamento com flúor. / Studies have shown that dentine can be modified by pulsed CO2 laser to form a more acid-resistant substrate. This in vitro research aimed to evaluate the effect of CO2 laser, associated or not the topical application of fluoride in reducing demineralization of human root surfaces using a pulsed laser of wavelength 10.6 m. Fifty human root surfaces obtained from twenty-five third molars were randomly divided into 5 groups (n=10) with the following surface treatments: G1 - No treatment (negative control), G2 - acidulated Phosphate Fluoride (FFA-positive control), G3 - Laser 4.0 J/cm2, G4 - Laser 4.0 J/cm2 + FFA and G5 - FFA + Laser 4.0 J/cm2. After surface treatment, specimens were subjected to 7 days of cycling the pH, remaining daily remineralizadora and demineralized in solutions for 21 h and 3 h, respectively. After acid challenge, the specimens were evaluated to determine the mineral loss through QLF. It can be concluded that the CO2 laser, with or without application of topical fluoride is able to inhibit the demineralization of root surface, however do not observed synergistic effect with the combination of laser irradiation and fluoride treatment.

A radioterapia clínica é de fundamental importância para o tratamento de lesões malignas localizadas na região de cabeça e pescoço, contudo, a exposição à irradiação ionizante, pode levar a complicações sistêmicas ou locais durante e após o tratamento radioterápico. Dentre estas complicações locais imediatas, destaca-se na cavidade oral a xerostomia e a consequente mucosite oral. A respeito das complicações tardias produzidas pela radioterapia, salientam-se a cárie de radiação e a osteorradionecrose, lesões dose dependentes, com alto nível de incidência nas últimas décadas e de difícil manejo, embora estas se apresentem após o término do tratamento e sob influência de fatores locais. A metodologia proposta no presente estudo visa analisar o efeito que exerce a radiação gama após a aplicação da radioterapia, utilizando-se a dose empregada em pacientes acometidos com câncer de cabeça e pescoço. As amostras foram obtidas a partir de esmalte dentário e dentina radicular humanos e osso mandibular suíno, as quais foram previamente polidas, e em seguida analisadas quanto à microdureza de superfície inicial de todos os grupos. Posteriormente, as amostras foram irradiadas sob uma taxa de dose de 4 Gy por dia, completando uma dose total de 72 Gy. Finalmente, as amostras foram submetidas a análise da microdureza de superfície após irradiação, a qual apresentou resultados estatisticamente significantes a partir dos testes de t de student, ANOVA e Tukey com respeito à diferença da média dos valores iniciais e finais de cada grupo de estudo com um valor de p = 0,00 (<0.05). Quanto à análise morfológica na microscopia eletrônica de varredura (MEV), o efeito deletério da irradiação gama manifestou-se na forma de trincas, quebras e fraturas superficiais dos tecidos analisados e à análise bioquímica pela técnica de reflexão total atenuada por meio da espectroscopia no infravermelho por transformada de Fourier (ATR - FTIR), a degradação dos componentes inorgânicos e a desnaturação dos compostos orgânicos foi evidente, pelo qual determinou-se o efeito deletério da irradiação gama sobre os tecidos duros da cavidade bucal com respeito às propriedades mecânicas, composicionais e morfológicas, e da ação contribuinte desta independente dos fatores locais e sistêmicos no paciente irradiado. / Clinical Radiotherapy is extremely important for the treatment of malignant lesions of the head and neck region, however, exposure to ionizing radiation can lead to systemic or local complications during and after radiation treatment. Among these immediate local complications are the oral cavity xerostomia and the consequent oral mucositis. Regarding late complications produced by radiation, tooth decay of radiation and osteoradionecrosis are included, which are considered dose-dependent lesions, with high incidence in recent decades and difficult to manage, although these appear after completion of treatment and under the influence of local factors. The methodology proposed in this study consists in evaluating the effect of gamma radiation after irradiation of the samples, using the dose used in patients suffering with head and neck cancer. The samples were obtained from human enamel and root dentin; and swine mandibular bone, which were previously polished, and then submitted to the analysis of the initial surface microhardness of all groups. Subsequently, the samples were irradiated in a dose rate of 4 Gy per day, completing a total dose of 72 Gy. Finally, the samples were submitted to surface microhardness analysis after irradiation, which presented statistically significant results from the Student t, ANOVA and Tukey statistical tests referred to the difference of the mean of the initial and final values of each study group with a significant value of p = 0.00 (<0.05). Regarding the morphological analysis in scanning electron microscopy (SEM), the deleterious effect of gamma irradiation was evidenced as structural cracks, breaks and superficial fractures of the analyzed tissues and the biochemical analysis by Attenuated Total Reflection technique using Fourier transform infrared spectroscopy (ATR - FTIR) showed degradation of inorganic components and denaturation of organic compounds; whereby, the effect of gamma irradiation on the hard tissues of the oral cavity with respect to mechanical, compositional and morphological properties was deleterious and this study highlighted the isolated action of this ionizing radiation which contributes highly for its appearance, independent of local and systemic factors in the irradiated patients.

A radioterapia clínica é de fundamental importância para o tratamento de lesões malignas localizadas na região de cabeça e pescoço, contudo, a exposição à irradiação ionizante, pode levar a complicações sistêmicas ou locais durante e após o tratamento radioterápico. Dentre estas complicações locais imediatas, destaca-se na cavidade oral a xerostomia e a consequente mucosite oral. A respeito das complicações tardias produzidas pela radioterapia, salientam-se a cárie de radiação e a osteorradionecrose, lesões dose dependentes, com alto nível de incidência nas últimas décadas e de difícil manejo, embora estas se apresentem após o término do tratamento e sob influência de fatores locais. A metodologia proposta no presente estudo visa analisar o efeito que exerce a radiação gama após a aplicação da radioterapia, utilizando-se a dose empregada em pacientes acometidos com câncer de cabeça e pescoço. As amostras foram obtidas a partir de esmalte dentário e dentina radicular humanos e osso mandibular suíno, as quais foram previamente polidas, e em seguida analisadas quanto à microdureza de superfície inicial de todos os grupos. Posteriormente, as amostras foram irradiadas sob uma taxa de dose de 4 Gy por dia, completando uma dose total de 72 Gy. Finalmente, as amostras foram submetidas a análise da microdureza de superfície após irradiação, a qual apresentou resultados estatisticamente significantes a partir dos testes de t de student, ANOVA e Tukey com respeito à diferença da média dos valores iniciais e finais de cada grupo de estudo com um valor de p = 0,00 (<0.05). Quanto à análise morfológica na microscopia eletrônica de varredura (MEV), o efeito deletério da irradiação gama manifestou-se na forma de trincas, quebras e fraturas superficiais dos tecidos analisados e à análise bioquímica pela técnica de reflexão total atenuada por meio da espectroscopia no infravermelho por transformada de Fourier (ATR - FTIR), a degradação dos componentes inorgânicos e a desnaturação dos compostos orgânicos foi evidente, pelo qual determinou-se o efeito deletério da irradiação gama sobre os tecidos duros da cavidade bucal com respeito às propriedades mecânicas, composicionais e morfológicas, e da ação contribuinte desta independente dos fatores locais e sistêmicos no paciente irradiado. / Clinical Radiotherapy is extremely important for the treatment of malignant lesions of the head and neck region, however, exposure to ionizing radiation can lead to systemic or local complications during and after radiation treatment. Among these immediate local complications are the oral cavity xerostomia and the consequent oral mucositis. Regarding late complications produced by radiation, tooth decay of radiation and osteoradionecrosis are included, which are considered dose-dependent lesions, with high incidence in recent decades and difficult to manage, although these appear after completion of treatment and under the influence of local factors. The methodology proposed in this study consists in evaluating the effect of gamma radiation after irradiation of the samples, using the dose used in patients suffering with head and neck cancer. The samples were obtained from human enamel and root dentin; and swine mandibular bone, which were previously polished, and then submitted to the analysis of the initial surface microhardness of all groups. Subsequently, the samples were irradiated in a dose rate of 4 Gy per day, completing a total dose of 72 Gy. Finally, the samples were submitted to surface microhardness analysis after irradiation, which presented statistically significant results from the Student t, ANOVA and Tukey statistical tests referred to the difference of the mean of the initial and final values of each study group with a significant value of p = 0.00 (<0.05). Regarding the morphological analysis in scanning electron microscopy (SEM), the deleterious effect of gamma irradiation was evidenced as structural cracks, breaks and superficial fractures of the analyzed tissues and the biochemical analysis by Attenuated Total Reflection technique using Fourier transform infrared spectroscopy (ATR - FTIR) showed degradation of inorganic components and denaturation of organic compounds; whereby, the effect of gamma irradiation on the hard tissues of the oral cavity with respect to mechanical, compositional and morphological properties was deleterious and this study highlighted the isolated action of this ionizing radiation which contributes highly for its appearance, independent of local and systemic factors in the irradiated patients.

Orientador: Marco Antonio Bottino / Banca: Luiz Felipe Valandro / Banca: Marcelo Giannini / Banca: Marcela Rocha de Oliveira Carrilho / Banca: Maximiliano Piero Neisser / Resumo: Esse estudo avaliou a performance de dois adesivos com condicionamento ácido prévio (All- Bond 2 e One-step Plus - Bisco) e dois sistemas adesivos autocondicionantes (Clearfil SE Bond- Kuraray e Xeno III- Dentsply) quanto à resistência de união à dentina coronária e do canal radicular, penetração do adesivo na dentina desmineralizada e influência sobre o grau de conversão do cimento resinoso. Também foi determinada, com mecânica da fratura, a tenacidade da interface pino/cimento/dentina formada com o adesivo All-Bond 2. O canal radicular de 80 dentes humanos anteriores superiores foi instrumentado e, em seguida, preparado com brocas do sistema de pinos FRC Postec (Ivoclar). A dentina foi tratada com um dos sistemas adesivos e o pino foi cimentado com cimento Duo-link (Bisco). Oito grupos foram formados de acordo com o sistema adesivo e o tempo de armazenagem em saliva artificial (7 d ou 4 m). Seis secções transversais (~1,0 mm) foram obtidas das regiões compreendidas entre 4 mm acima da JEC até 4mm do ápice radicular, isto é, dentina coronária e do canal radicular. Três destas seis secções foram submetidas ao teste de pushout em máquina de ensaio universal Instron (1 mm/min, 50 Kgf). Nas secções restantes foram avaliados o grau de conversão do cimento e a penetração do adesivo na dentina com μ-Espectroscopia Raman. As amostras de tenacidade consistiram de dois hemi-discos de resina reforçada por fibra (pino) cimentados a duas fatias de dentina da câmara pulpar, formando um sanduíche (espécime Brazil nut). Os resultados do teste Anova 3-fatores de medida repetida (p<0.05) indicam que, apenas, a "região" exerceu efeito significante sobre a resistência de união (MPa). Na porção coronária (4,20 MPa) a resistência foi maior que nas regiões média (3,45 MPa) e apical (3,26 MPa) (Tukey, 5%). A tenacidade de fratura da interface cimento-dentina foi maior... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: This study evaluated the performance of two etch-and-rinse (All-Bond 2 andOne-step Plus- Bisco) and two self-etch adhesive systems (Clearfil SE Bond- Kuraray and XenoIII-Dentsply) concerning their bonding durability to coronal and root canal dentin, infiltration onto dentin and influence on the degree of cure of a dual-cure cement. It was also determined the interfacial fracture toughness of the post/cement/dentin interface forme with All-Bond 2. The root canals of 80 human incisors and canines were instrumented and prepared with burs (FRC Postec System, Ivoclar). Dentin was treated with one of the four adhesives and FRC Postec posts (Ivoclar) were cemented to the root canal with Duo-link dual-cure resin cement (Bisco). Eight groups were formed according to the adhesive system employed and the aging time in water (7 or 4 m). Six transverse sections (~1.0 mm) were cut from 4 mm above the CEJ up to 4 mm short of the root canal apex, comprising coronal and root canal dentin. Three out of the six sections were submitted to push-out testing in an Instron machine (1 mm/min, 50 Kgf). The degree of conversion of the cement and the infiltration of the adhesive were evaluated in the remaining sections through Raman μ-Spectroscopy. The fracture toughness specimens were made out of two half disks of fiber-reinforced composite (post) cemented to dentin pieces, forming the Brazil nut specimen. The analisys obtained with the 3-way Anova of repeated measures test (p<0.05) showed that only the "region" had statistically significant effects on the bond strengths (MPa). Comparison of the means achieved in each region (Tukey, p < 0.05) revealed that the coronal portion (4.20 MPa) was higher than the cervical (3.45 MPa) and middle portions (3.26 MPa) of the root, which were not statistically different. The interfacial fracture toughness was higher for the cement-dentin interface than... (Complete abstract click electronic access below) / Doutor

Orientador: Claudio Antonio Talge Carvalho / Banca: Samira Esteves Afonso Camargo / Banca: Carlos Rocha Gomes Torres / Resumo: O objetivo deste trabalho foi avaliar a ação das soluções de armazenamento: água destilada (G1), solução de timol a 0,05%(G2), formalina a 10%(G3), e hipoclorito de sódio a 1%(G4), bem como os métodos de esterilização por autoclave (A) e radiação gama (B), e as associações dos dois fatores, sobre a microdureza da dentina radicular de terceiros molares extraídos. Os dados obtidos foram submetidos aos testes t de Student, ANOVA a 2 e 3 fatores, e teste de Tukey, todos com α=0,05. Quanto ao armazenamento, o G1(nos dois períodos avaliados) foi o único grupo que não alterou significantemente a microdureza, sendo seguido pelos grupos G2 e G3 (7 dias), G2 e G3 (28 dias), e G4 (7 e 28 dias), tendo estes dois últimos subgrupos apresentado as maiores perdas de microdureza. Na análise da esterilização isoladamente, não houve diferença significante para os 2 métodos quando comparadas as microdurezas iniciais e após a esterilização (autoclave: p=0,144; raios gama: p=0,827), apesar da esterilização por autoclave ter induzido diferenças significantes no grupo armazenado por 28 dias em água destilada. Entretanto, estudada a interação de todos os fatores, encontraram-se diferenças significantes quanto à solução empregada, método de esterilização e interações entre eles (p<0,05). Com base nos dados analisados pôde-se concluir que o armazenamento em água destilada não alterou a microdureza dentinária radicular, e sua associação à esterilização por radiação gama foi o melhor método para o armazenamento e esterilização de dentes, no que diz respeito às influências sobre a variável estudada, sendo indicados para dentes extraídos a serem utilizados em pesquisa. / Abstract: The aim of this study was to evaluate the effect of storage solutions: distilled water (G1), 0.05% thymol solution (G2), 10% formalin (G3), and 1% sodium hypochlorite (G4); sterilization methods- steam autoclaving (A) and gamma irradiation (B)- and the associations between the two factors on the root dentin microhardness of extracted human third molars. Data were subjected to student's t test for dependent samples, Two and Three-way ANOVA, and Tukey's test (α = 0.05 for all tests). Regarding storage, only the G1 (in both periods) did not alter the dentin microhardnes significantly. In the analysis of sterilization methods, there were significant differences on the solution employed, storage time and sterilization method (p <0.05). Based on the results, it was concluded that the storage in distilled water did not change the root dentin microhardness, and association of this storage solution with sterilization by Gamma radiation did not produce alterations by means of the studied variable, thus consisting in the best methods regarding storage and sterilization of teeth to be used in research. / Mestre

Made available in DSpace on 2014-06-11T19:35:03Z (GMT). No. of bitstreams: 0 Previous issue date: 2009-05-08Bitstream added on 2014-06-13T20:06:14Z : No. of bitstreams: 1 melo_rm_dr_sjc.pdf: 3484297 bytes, checksum: 204bf95c70038c23b08cc2d82b5974c4 (MD5) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Esse estudo avaliou a performance de dois adesivos com condicionamento ácido prévio (All- Bond 2 e One-step Plus - Bisco) e dois sistemas adesivos autocondicionantes (Clearfil SE Bond- Kuraray e Xeno III- Dentsply) quanto à resistência de união à dentina coronária e do canal radicular, penetração do adesivo na dentina desmineralizada e influência sobre o grau de conversão do cimento resinoso. Também foi determinada, com mecânica da fratura, a tenacidade da interface pino/cimento/dentina formada com o adesivo All-Bond 2. O canal radicular de 80 dentes humanos anteriores superiores foi instrumentado e, em seguida, preparado com brocas do sistema de pinos FRC Postec (Ivoclar). A dentina foi tratada com um dos sistemas adesivos e o pino foi cimentado com cimento Duo-link (Bisco). Oito grupos foram formados de acordo com o sistema adesivo e o tempo de armazenagem em saliva artificial (7 d ou 4 m). Seis secções transversais (~1,0 mm) foram obtidas das regiões compreendidas entre 4 mm acima da JEC até 4mm do ápice radicular, isto é, dentina coronária e do canal radicular. Três destas seis secções foram submetidas ao teste de pushout em máquina de ensaio universal Instron (1 mm/min, 50 Kgf). Nas secções restantes foram avaliados o grau de conversão do cimento e a penetração do adesivo na dentina com μ-Espectroscopia Raman. As amostras de tenacidade consistiram de dois hemi-discos de resina reforçada por fibra (pino) cimentados a duas fatias de dentina da câmara pulpar, formando um sanduíche (espécime Brazil nut). Os resultados do teste Anova 3-fatores de medida repetida (p<0.05) indicam que, apenas, a “região” exerceu efeito significante sobre a resistência de união (MPa). Na porção coronária (4,20 MPa) a resistência foi maior que nas regiões média (3,45 MPa) e apical (3,26 MPa) (Tukey, 5%). A tenacidade de fratura da interface cimento-dentina foi maior... / This study evaluated the performance of two etch-and-rinse (All-Bond 2 andOne-step Plus- Bisco) and two self-etch adhesive systems (Clearfil SE Bond- Kuraray and XenoIII-Dentsply) concerning their bonding durability to coronal and root canal dentin, infiltration onto dentin and influence on the degree of cure of a dual-cure cement. It was also determined the interfacial fracture toughness of the post/cement/dentin interface forme with All-Bond 2. The root canals of 80 human incisors and canines were instrumented and prepared with burs (FRC Postec System, Ivoclar). Dentin was treated with one of the four adhesives and FRC Postec posts (Ivoclar) were cemented to the root canal with Duo-link dual-cure resin cement (Bisco). Eight groups were formed according to the adhesive system employed and the aging time in water (7 or 4 m). Six transverse sections (~1.0 mm) were cut from 4 mm above the CEJ up to 4 mm short of the root canal apex, comprising coronal and root canal dentin. Three out of the six sections were submitted to push-out testing in an Instron machine (1 mm/min, 50 Kgf). The degree of conversion of the cement and the infiltration of the adhesive were evaluated in the remaining sections through Raman μ-Spectroscopy. The fracture toughness specimens were made out of two half disks of fiber–reinforced composite (post) cemented to dentin pieces, forming the Brazil nut specimen. The analisys obtained with the 3-way Anova of repeated measures test (p<0.05) showed that only the “region” had statistically significant effects on the bond strengths (MPa). Comparison of the means achieved in each region (Tukey, p < 0.05) revealed that the coronal portion (4.20 MPa) was higher than the cervical (3.45 MPa) and middle portions (3.26 MPa) of the root, which were not statistically different. The interfacial fracture toughness was higher for the cement-dentin interface than... (Complete abstract click electronic access below)

Estudos têm mostrado que a dentina pode ser modificada pelo laser pulsado de CO2 tornando-a um substrato mais ácido-resistente. Este estudo in vitro se propôs a avaliar o efeito do laser de CO2, associado ou não à aplicação tópica de flúor, na redução da desmineralização de superfícies radiculares humanas, utilizando um laser pulsado de comprimento de onda 10,6 m. Cinquenta superfícies radiculares humanas obtidas de vinte e cinco terceiros molares foram aleatoriamente divididas em 5 grupos (n=10) com os seguintes tratamentos de superfície: G1 Nenhum tratamento (controle negativo), G2 Flúor Fosfato Acidulado (FFA- controle positivo), G3 Laser 4,0 J/cm2, G4 Laser 4,0 J/cm2 + FFA e G5 FFA + Laser 4,0 J/cm2. Após o tratamento da superfície, os espécimes foram submetidos a 7 dias de ciclagem de pH, permanecendo diariamente em soluções desmineralizadora e remineralizadora por 3 h e 21 h, respectivamente. Após o desafio ácido, os espécimes foram avaliados para determinar a perda mineral por meio do QLF. Pode-se concluir que o laser de CO2, associado ou não à aplicação tópica de flúor, é capaz de inibir a desmineralização da superfície radicular, contudo não se observa efeito sinérgico com a associação da irradiação com laser e tratamento com flúor. / Studies have shown that dentine can be modified by pulsed CO2 laser to form a more acid-resistant substrate. This in vitro research aimed to evaluate the effect of CO2 laser, associated or not the topical application of fluoride in reducing demineralization of human root surfaces using a pulsed laser of wavelength 10.6 m. Fifty human root surfaces obtained from twenty-five third molars were randomly divided into 5 groups (n=10) with the following surface treatments: G1 - No treatment (negative control), G2 - acidulated Phosphate Fluoride (FFA-positive control), G3 - Laser 4.0 J/cm2, G4 - Laser 4.0 J/cm2 + FFA and G5 - FFA + Laser 4.0 J/cm2. After surface treatment, specimens were subjected to 7 days of cycling the pH, remaining daily remineralizadora and demineralized in solutions for 21 h and 3 h, respectively. After acid challenge, the specimens were evaluated to determine the mineral loss through QLF. It can be concluded that the CO2 laser, with or without application of topical fluoride is able to inhibit the demineralization of root surface, however do not observed synergistic effect with the combination of laser irradiation and fluoride treatment.

Orientadora: Profa. Dra. Patrícia Aparecida da Ana / Dissertação (mestrado) - Universidade Federal do ABC, Programa de Pós-Graduação em Biotecnociência, 2014.

O objetivo deste estudo foi comparar os ensaios de microtração (MI), ?push-out? (PS), ?push-out? modificado (PSM) e ?pull-out? (PL) na habilidade de mensurar a resistência de união (RU) entre pino de fibra e dentina radicular. Para tanto, além dos resultados de cada ensaio mecânico foram analisados fatores como: sensibilidade quanto às diferentes regiões radiculares, quantidade de falhas prematuras (FP), coeficiente de variação (CV), padrão de fratura (PF) pela microscopia confocal de varredura e distribuição das tensões pela análise de elementos finitos (AEF). Foram utilizados 40 dentes anteriores superiores endodonticamente tratados, divididos em quatro grupos de acordo com o tipo de ensaio realizado. Para os ensaios de PS e MI foi feita a cimentação do pino e posteriormente os cortes para a obtenção dos corpos-de-prova (cps). Para os outros ensaios (PSM e PL), a cimentação antecedeu aos cortes tanto das fatias de dentina como dos pinos. O sistema adesivo Scotbond Multi Uso Plus e o cimento Variolink II foram usados para a cimentação do pino de fibra de vidro FRC Postec Plus em todos os casos. Os cps do ensaio de PS foram obtidos pelos cortes seriados da raiz em fatias de 1±0,1mm, para os cps do ensaio de MI estas fatias sofreram ainda a confecção de entalhes laterais diametralmente opostos, que proporcionando um formato final de ampulheta. Para os testes de PL e PSM foram feitos cortes de fatias de dentina de 1±0,1mm e o pino foi dividido em três partes iguais para, então, cada fatia de uma região ser cimentada com o pino correspondente. Os cps do ensaio de PSM tinham 1mm de pino sobressalente para cima e para baixo da fatia de dentina, enquanto que os cps do PL o pino sobressalente estava apenas para cima da dentina. Todos os cps foram submetidos aos testes de RU, à velocidade de 0,5mm/min em máquina de ensaios universais. O PF foi avaliado em um aumento de cem vezes e foi feita uma distribuição de freqüência. Já a AEF obteve modelos tridimensionais de todos os ensaios, e estes foram analisados quanto à tensão de Von Mises. Para os resultados dos testes mecânicos foram feitas análises de variância de cada ensaio variando o fator região, com ou sem as FP, e análise comparando todos os ensaios. O teste Tukey foi feito quando necessário e as FP foram submetidas ao teste estatístico de Fisher. A inclusão ou não destas falhas mostra alteração dos resultados no ensaio de MI, uma vez que possui um maior número delas neste ensaio. O ensaio de PL mostrou as maiores médias de RU, seguido pelo ensaio de PSM, e ambos também tiveram o PF com maior quantidade de fraturas adesivas. O ensaio de PS conseguiu apontar diferença estatística entre as três regiões, mas mostrou a maior freqüência de falhas coesivas, e maior CV. O menor CV foi encontrado para o PSM que também mostrou uma adequada distribuição das tensões. A MI apresentou concentração de tensões nas bordas dos entalhes. Concluiu-se que o tipo de ensaio influencia diretamente nos resultados obtidos. / The aim of this study was to compare microtensile (MI), \"push-out\" (PS), modified \"push-out\" (PSM) and \"pull-out\" (PL) tests in the ability to accurately measure the bond strength of fiber posts luted inside root canals, at different root dentin levels, cervical, middle and apical. The evaluated parameters were: amount of premature failure (PF), coefficient of variation (CV), failure patterns (FP) and the stress distribution by finite elements analysis (FEA). Forty human intact single-rooted and endodontically treated teeth were divided into four groups according to the type test used. For PS and MI specimens, first the post was luted and then the cuts were done, for PSM and PL, first was done the cuts and then fiber post?s pices were luted. Scotbond Multi Use Plus adhesive system and Variolink II cement had been used for luting FRC Postec Plus glass fiber post, in all cases. PS samples were disc shaped of 1±0,1mm. Bond strength between post and dentin was measured in the root slice and the force applied on the center of the specimen. For the Mi test hourglass-shaped samples were obtained by trimming the proximal surfaces of each slice using a diamond bur until it touched the post. For PL and PSM tests cuts of 1±0,1mm of dentine slices were made and the fiber was divided into three parts, and then each slice were luted with a fiber post?s piece. Specimens for PSM had 1mm of post up and down the dentin slice and for PL all of the post was up the dentine slice. All specimens were submitted to a bond strength test at 0.5 mm/minute crosshead speed in a universal testing machine. For FP, each sample was examined under confocal microscopy at 100 times and a frequency distribution was made. For the AEF, three-dimensional models of each tests had been made and analyzed by Von Mises stress. Bond strength data were analyzed by ANOVA and when necessary was used Tukey?s test. For PF data the Fisher test was made. The inclusion of PF, only shows variation on MI, since these test showed the greater number of them. PL provided higher values of bond strength for root dentin and fiber post, followed by PSM. Both of them had also FP with greater amount of adhesive failures. The PS test was able to point statistically differences between root regions, but it showed the highest frequency of cohesive failure, and greater CV. Minor CV was found for the PSM that also showed adequate stress distribution. The MI showed concentration of tensions in the edges of the trimming area. One concluded that the type of test influences directly in the results obtained.