161 |
Efeito de tecnicas de envelhecimento acelerado e aplicação de selante sobre a deformação permanente de reembasadores resilientes permanentes / Effect of accelerated aging and surface sealing on permanent deformation of auto-polymerizing soft linersSilva, Joaquim Alberto da 15 August 2018 (has links)
Orientador: Marcelo Ferraz Mesquita / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-15T15:52:10Z (GMT). No. of bitstreams: 1
Silva_JoaquimAlbertoda_D.pdf: 1108935 bytes, checksum: 15a0a956cee4dcf34973383fda778eb8 (MD5)
Previous issue date: 2010 / Resumo: O objetivo neste estudo foi comparar o efeito de dois métodos de envelhecimento acelerado (termociclagem e simulação do intemperismo natural) sobre a propriedade de deformação permanente de dois reembasadores resilientes permanentes usados como forradores de próteses removíveis, um à base de silicone (UP) e outro à base resina acrílica (DF), submetidos ou não à aplicação de selante de superfície. Foram confeccionados 120 corpos-de-prova (12,7 mm de diâmetro, e 19 mm de comprimento), distribuídos aleatoriamente em doze grupos (n=10) e submetidos a envelhecimento acelerado (2.000 ciclos) por meio da termociclagem, ou simulação do intemperismo natural (67 ciclos). Para o ensaio, foi utilizado um aparelho mecânico descrito na especificação no18 da A.D.A., com aplicação de carga compressiva (750 gf) durante 30 segundos. Para comparações do mesmo material com e sem selante e entre os materiais no mesmo intervalo de envelhecimento, foi realizada a análise estatística pelo teste de Mann-Whitney (p=0,05). Os testes de Kruskal-Wallis associado ao método de Dunn foram utilizados para comparação do efeito das técnicas de envelhecimento em cada material (p=0,05). O reembasador à base de silicone apresentou menor deformação permanente que o à base de resina, independente do método de envelhecimento (P<0,05). Foi observado que a aplicação do selante de superfície teve efeito sobre a deformação permanente apenas no grupo do material à base de silicone submetido à termociclagem, e que o envelhecimento acelerado promoveu aumento na deformação permanente apenas para o material à base de resina acrílica. / Abstract: This study was performed in order to compare the effects of two different accelerated aging methods on the property of permanent deformation of two permanent softliners. The softliners selected were an auto-polymerizing acrylic resin based and an auto-polymerizing silicone based. The use of surface sealer was also evaluated on both relining materials. For the permanent deformation test specimens were manufactured with 12.7 mm of diameter and 19 mm length, according to A.D.A. specification number 18. A total of 120 specimens were manufactured, sixty of each relining material. All specimens were randomly distributed into twelve groups (n=10) and later submitted to one of the accelerated aging processes (2000 thermocycling cycles or 67 cycles in an EQUV chamber). The permanent deformation test was performed with a mechanical device described in the specification number 18 of A.D.A. with a compressive load of 750 gf applied during 30 seconds. All data was submitted to statistical analysis. MannWhitney test was performed in order to compare the effect of the surface sealer on each material and to compare the permanent deformation of the materials in the same aging group (p=0.05). Kruskal-Wallis and Dunn tests were performed to compare all aging groups of each material (p=0.05). After analysis of the results it was observed that the silicone based reliner presented lower permanent deformation than the acrylic resin based reliner, regardless of the aging procedure. The surface sealer coating was effective only for the thermocycled silicone group and the accelerated aging processes affected only the permanent deformation of the acrylic resin based material. / Doutorado / Protese Dental / Doutor em Clínica Odontológica
|
162 |
Estudo do deslocamento dental linear em proteses totais processadas em diferentes ciclos de polimerização e tempos pós-prensagem / Study of the tooth movement in complete denturees processed by different polymerazation cyclews and post-pressing timesNegreiros, Wagner Araujo de 18 August 2008 (has links)
Orientador: Rafael Leonardo Xediek Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-11T16:30:52Z (GMT). No. of bitstreams: 1
Negreiros_WagnerAraujode_D.pdf: 1008776 bytes, checksum: c1f49fe9b1212453aa201116e5fe45db (MD5)
Previous issue date: 2008 / Resumo: Este trabalho verificou a movimentação de dentes em próteses totais confeccionadas a partir de diferentes ciclos de polimerização e tempos pós-prensagem. Foram confeccionadas 40 próteses totais superiores com as resinas acrílicas Clássico, QC-20 e Onda-Cryl, as quais foram distribuídas por sorteio em 8 grupos (n=5) de acordo com os ciclos de polimerização (longo em banho de água aquecida (grupo-controle), curto em água em ebulição e por energia de microondas) e tempos pós-prensagem (imediato e 6 horas). A montagem dos dentes foi realizada em articulador semi-ajustável, tendo como referência um modelo inferior dentado. Pinos referenciais metálicos foram posicionados na borda incisal dos incisivos centrais, na cúspide vestibular dos primeiros pré-molares e cúspide mésio-vestibular dos segundos molares. As distâncias transversais PMD-PME (pré-molar direito a pré-molar esquerdo) e MD-ME (molar direito a molar esquerdo) e ântero-posteriores ID-MD (incisivo direito a molar direito) e IE-ME (incisivo esquerdo e molar esquerdo) foram mensuradas antes e após o processamento, utilizando microscópio comparador (Olympus Optical Co., Tokyo, Japan), com precisão de 0,0005mm. As resinas acrílicas Clássico e QC-20 foram proporcionadas e manipuladas de acordo com as instruções dos fabricantes e submetidas aos ciclos de polimerização em água a 74ºC por 9 horas e em água em ebulição por 20 minutos, respectivamente. A resina Onda-Cryl foi submetida à polimerização por energia de microondas no ciclo 3 minutos a 35%, 4 minutos a 0% e 3 minutos a 65% da potência máxima do forno de microondas. Os dados coletados foram submetidos à análise de variância e as médias foram comparadas pelo teste de Tukey em nível de 5% de significância. Todas as distâncias mostraram movimentação dental; entretanto, esta não foi estatisticamente significante (5%) antes e após a polimerização para todos os ciclos de polimerização analisados. O ciclo de polimerização por microondas foi comparável estatisticamente ao ciclo convencional em banho de água aquecida (grupo controle) em relação à magnitude da movimentação dental. O tempo pós-prensagem 6 horas não mostrou vantagens em reduzir a magnitude do deslocamento dental em relação à polimerização imediata, na maioria das distâncias avaliadas. Concluiu-se que as alterações não foram similares, mostrando influência das resinas, tempo pós-prensagem e distância entre dentes / Abstract: This study verified the tooth movement in maxillary complete dentures submitted to different polymerization cycles and post-pressing times. Forty maxillary complete dentures fabricated with Classico, QC-20, and Onda-Cryl acrylic resins, were randomly assigned into 8 groups (n=5) according to the polymerization cycles (long cycle in water bath (control-group), fast cycle in boiling water, and microwave cycle) and the post-pressing time (immediate and after 6 hours). The wax pattern was made using a semi-adjustable articulator having a mandibular dentate cast as a reference. Metallic referential pins were placed on the incisal border of the central incisors, vestibular cusp of the first premolars, and the mesio-vestibular cusp of the second molars. The PMD-PME (right premolar to left premolar), MD-ME (right molar to left molar) transversal distances and RI-RM (right incisor to right molar) and LI-LM (left incisor to left molar) anteroposterior distances were measured before and after the complete dentures processing with a linear optical microscope (Olympus Optical Co., Tokyo, Japan) with an accuracy of 0.0005mm. All acrylic resins were proportioned and manipulated following the manufacturer¿s directions. Classico and QC-20 acrylic resins were submitted to the conventional water bath curing at 74ºC for 9 hours or to boiling water curing for 20 minutes respectively. Onda-Cryl acrylic resin was processed by microwave energy cycle for 3 minutes at 35%, 4 minutes at 0%, and 3 minutes at 65% power of the microwave oven. Collected data were submitted to the ANOVA and Tukey test at 5% of significance. All distances showed tooth movement; however, that was not statistically significant (5%) before and after processing for all polymerization cycles analyzed. The microwave polymerization cycle was statisticaly comparable with the conventional one in water bath (control group) considering the magnitude of tooth movement. The 6-hour post-pressing had no advantage in reducing the magnitude of tooth movement in relation to the immediate polymerization for most of the distances evaluated. It was concluded that the changes were not similar being influenced by the polymerization cycles, post-pressing time, and distance among teeth / Doutorado / Protese Dental / Doutor em Clínica Odontológica
|
163 |
Efeito da ciclagem térmica e imersão em clorexidina nas propriedades físicas das resinas de bisacrilato de metila e metacrilato de metila / Effect of thermo cycling and chlorexidine immersion in physicals properties of bis-acryl and methacryl resinsFabiano Martins Malafaia 02 June 2009 (has links)
O uso de resinas acrílicas para confecção de restaurações provisórias é bastante difundido na prática odontológica. Dois tipos de resina encontram-se comercialmente disponíveis, as de bisacrilato de metila e as de metacrilato de metila e, em decorrência das exigências funcionais e estéticas das restaurações provisórias, estes materiais devem apresentar resistência, estabilidade de cor e durabilidade. Objetivo: Verificar a resistência à flexão, a microdureza, a rugosidade superficial e a estabilidade de cor de quatro resinas para restaurações temporárias quando submetidas à termociclagem e à imersão em clorexidina. Metodologia: Foram utilizadas as resinas Luxatemp e Structur 2, a base de bisacrilato de metila, e as resinas Duralay e Alike a base de metacrilato de metila. Os corpos-de-prova (n=220) foram divididos em quatro grupos, de acordo com a marca comercial e o ensaio realizado (resistência à flexão, microdureza, rugosidade superficial e estabilidade de cor), sendo avaliados em três tempos distintos: após 24 horas da confecção, após termociclagem (2000 ciclos) e após termociclagem e imersão em clorexidina a 0,12% por 14 dias. Resultados: Os dados obtidos foram analisados com o teste ANOVA e em seguida com o teste t (p<0,05), evidenciando que a termociclagem alterou as propriedades mecânicas das resinas, diminuindo a resistencia a flexão e a microdureza, aumentando a rugosidade superficial e ocasionando alteração de cor. A clorexidina não afetou as propriedades mecânicas das resinas estudadas, porém alterou a cor das resinas de metacrilato. Conclusões: As resinas de bisacrilato apresentaram resultados superiores aos das resinas de metacrilato para todas as variáveis estudadas. A termociclagem afetou negativamente todas as resinas, apenas as resinas de bisacrilato não apresentaram alteração de cor após imersão em clorexidina. / The use of acrylic resins is quite spread in dental practice, being accomplished temporary restorations with this material during the prosthetic treatment. Two chemical groups of this material exist, bis-acryl resins and another of methacrylate resins. Aim: This study verified the flexural resistance, micro hardness, superficial roughness and the color variation of four temporary resins submitted to thermo cycling and chlorexidine immersion. Methods: Luxatemp and Structur 2, bis-acryl based resins, and, Duralay and Alike, methacrylate based resins, has been used. The specimens (n=220) were divided in four groups, in agreement with the accomplished rehearsal, being appraised in three different times: after 24 hours, after the thermo cycling (2000 cycles) and after the thermo cycling followed by the immersion in 0.12% chlorexidine solution during 14 days. The tests were accomplished to the flexural, microhardness, superficial roughness and the color variation verification in all of the experimental times. Results: The results were statistically verified with ANOVA test followed by a t-test (p<0.05). Thermo cycling decreased flexural resistance and micro hardness, increased superficial roughness and caused color variation in all studied resins. Chlorexidine immersion did not changes physicals properties of studied resins, but caused color variation in methacrylate resins. Conclusions: The bis-acryl resins obtained results superiors to the checked for the methacrylate resins in all the experimental tests. Thermo cycling manegeament affected negatively all the studied resins. Only bis-acryl resins didnt presented color variation caused by chlorexidine immersion.
|
164 |
Estudo da alteração da dimensão vertical de oclusão (DVO) em dentaduras completas variando-se a fase de inserção da resina acrílica para microondas em mufla e utilizando-se a técnica do propiciador de espaço / Influence of acrylic resin stages and of the space propitiator technique on vertical dimension of occlusion in total denturesAdriana Oshiro 21 September 2007 (has links)
As alterações de dimensão vertical de oclusão em dentaduras completas foram avaliadas através da mudança da fase de inserção (arenosa ou pegajosa) da resina acrílica de microondas Onda-Cryl em muflas próprias com a utilização ou não da técnica do propiciador de espaço. Foram confeccionadas dentaduras superiores em cera, corretamente articuladas com uma dentadura inferior previamente montada em articulador semi-ajustável, sendo realizadas as medidas de dimensão verticais iniciais através de um relógio micrométrico. Estas próteses superiores em cera foram divididas em quatro grupos de 10 elementos cada para acrilização: grupo F (inserção da resina acrílica na fase fibrilar em mufla, sem a utilização da técnica do propiciador de espaço), grupo FP (inserção na fase fibrilar, com utilização da técnica do propiciador de espaço), grupo A (fase arenosa, sem a técnica do propiciador de espaço) e grupo AP (fase arenosa, com a técnica do propiciador de espaço). O ciclo de polimerização em todos os grupos foi de 3 minutos a 30% da potência, 4 minutos com 0 (zero) de potência e 3 minutos a 90% da potência, em forno microondas de 800 Watts, conforme as instruções do fabricante. Após a acrilização, as dentaduras superiores, juntamente com seus respectivos modelos, foram remontadas no articulador semi-ajustável (através da técnica do split-cast com imã), onde novas medidas foram tomadas e comparadas com as iniciais. Os resultados foram submetidos à análise estatística e demonstraram que a técnica do propiciador de espaço foi efetiva na diminuição das alterações de dimensão vertical e que a mudança da fase de inserção da resina, embora não estatisticamente significante, também provoca uma redução dessas alterações. / Changes in vertical dimension of occlusion in maxillary complete dentures were evaluated after modifying Onda Cryl acrylic resin insertion stages (sandy or stringy) in specifics flasks or employing or not a space propitiator technique. Forty maxillary wax total dentures were made and randomly assigned in four groups, each one with 10 elements. They were all mounted in a semi-adjustable articulator and the initial vertical dimension measurements were recorded by the means of a gauging device attached to the articulator\'s guideline. The 4 groups were: Group S (Stringy stage, no use of space propitiator technique), Group SP (Stringy stage associated with the space Propitiator technique), Group Sn (Sandy stage, no use of space propitiator technique) and Group SnP (Sandy stage associated with the space Propitiator technique). All specimens were processed in a domestic microwave oven according to Onda cryl manufacturer\'s instructions. After the curing cycle, the flask was removed from the oven, remaining on the bench until its full cooling and the remounted standardized dentures were replaced in the articulator were reevaluated. The vertical dimensional alterations values were submitted to statistical analysis. Space propitiator technique was effective on reducing the vertical dimension alterations and changing the resin stage (sandy instead stringy stage) results in minor alterations on vertical dimension, although not statiscally significant.
|
165 |
Avaliação do comportamento mecânico de próteses fixas provisórias durante e após ensaio de fadiga - efeito de três tipos de reforços (fibra de vidro, fibra de aramida e fio de aço) e duas extensões de pôntico (12,5 e 22,75mm)Luiz Gustavo Cavalcanti Bastos 27 June 2006 (has links)
A importância das próteses provisórias no tratamento reabilitador oral é inquestionável. Os materiais utilizados para a execução destas restaurações, entretanto, são críticos com relação à resistência e à longevidade, principalmente quando estas são executadas em tratamentos prolongados e/ou em espaços desdentados extensos. A proposta deste trabalho foi determinar através de um ensaio de fadiga e de um teste de resistência à fratura, o efeito do tipo de reforço: fio de aço Ø 0,7 mm, fibra de poli(aramida) (Kevlar®, DuPont - USA) e fibra de vidro (Fibrante®, Ângelus -Brasil) e de duas extensões do pôntico (12,5 e 22,75 mm) sobre o comportamento mecânico de espécimes simulando próteses provisórias. Os grupos foram constituídos de 10 espécimes cada, incluindo um grupo CONTROLE, sem reforço. Os espécimes simulando próteses parciais fixas provisórias foram confeccionados em resina auto-polimerizável com auxílio de uma matriz de aço simulando preparos totais protéticos. As amostras foram submetidas a 10.000 ciclos de fadiga, com carga máxima de 100 N, imersas em água a 37ºC. Através da análise estatística dos resultados observou-se que durante o ensaio de fadiga: 1) quando a extensão do pôntico foi de 22,75 mm, o grupo CONTROLE exibiu uma maior deformação a partir de 500 ciclos. Não foram observadas diferenças quando a extensão do pôntico foi de 12,5 mm. Houve um aumento da deformação em função do número de ciclos para todos os grupos, principalmente para o grupo CONTROLE, de ambas as extensões de pôntico; 2) Somente espécimes do grupo CONTROLE com extensão do pôntico de 22,75 mm demonstraram fraturas à fadiga. E após o ensaio de fadiga, através de um teste de resistência à fratura: 1) Quando a extensão do pôntico foi de 12,5 mm todos os grupos reforçados apresentaram valores médios do limite de elasticidade, em N, significantemente maiores que os demonstrados pelo grupo CONTROLE. Para a extensão do pôntico de 22,75 mm os valores desse parâmetro apresentaram semelhança entre todos os grupos; 2) Em relação à carga máxima (resistência à fratura), quando a extensão do pôntico foi de 12,5 mm o grupo FIBRANTE exibiu o maior valor médio. Quando a extensão do pôntico foi de 22,75 mm, observou-se que o grupo KEVLAR apresentou valores semelhantes neste parâmetro ao grupo FIBRANTE. O grupo CONTROLE sempre apresentou os menores valores médios em ambas as extensões de pôntico. Em relação ao modo de fratura os grupos reforçados apresentaram fraturas mais favoráveis ao reparo, tendo sido do tipo parcial (coesiva da resina sem fratura ou separação do reforço). / Provisional restorations are essential components of oral rehabilitation treatment. The strength and durability features are, however, critical when long-term treatment is needed. This study investigates the mechanical alterations under and after cyclic fatigue in provisional partial fixed denture specimens. Two pontic distances (12.5 mm and 22.75 mm) and three types of reinforcements constituted the experimental groups with ten specimens each: a 0.7 mm of diameter wire; a roving poliaramid fiber Kevlar® and a roving fiberglass Fibrante® (Angelus®). The control group, also with ten samples, included not reinforced specimens. Specimens were fabricated and testing on metal dies. The samples were subjected to 10,000 fatigue cycles with a 100 N maximum load in a MTS 810 Universal Machine and before they were subjected to fracture resistance test in the same machine. Statistical analysis showed that, during the fatigue cycles: 1) All the samples exhibited an increased deflection, in mm, following the fatigue cycles, mainly the CONTROL group; 2) Only specimens of the CONTROL group exhibited fracture due to fatigue cycle. After the fatigue cycle, through the fracture resistance test: 1) All reinforced samples with the pontic distance of 12.5 mm exhibited higher figures in elastic limits than the CONTROL group, and increased the pontic distance to 22.75 mm the results of the elastic limits decreased statistically; 3) the FIBRANTE group with pontic distance of 12.5 mm exhibited the higher results for the resistance fracture. The CONTROL group specimens, with both pontic distances, exhibited the lowest values of this property; 4) It was observed that the reinforced FIBRANTE anda KEVLAR groups specimens fractures were more favorable, occurring, predominantly, in the Partial type.
|
166 |
Análise da rugosidade superficial de diferentes marcas comerciais de resina acrílica para coroas provisórias / Surface roughness analysis of acrylic resin for provisional crowns under different commercial brandsCintia Lumi Nishida 30 June 2010 (has links)
As coroas provisórias apresentam algumas características que podem comprometer a estética e facilitar aderência de microorganismos e formação de placa. Estudos prévios demonstraram que a forma de processamento influi na rugosidade e porosidade de uma marca comercial de resina acrílica comumente utilizada para a confecção de provisórias. Como diferentes marcas comerciais apresentam diferenças de qualidade, o presente estudo teve como objetivo principal avaliar a rugosidade superficial de quatro marcas comerciais de resina acrílica utilizadas na confecção de coroas provisórias (Dencor, Vipi, Duralay e Alike) de acordo com quatro técnicas de manipulação, diretas e indiretas. Os processamentos avaliados foram: GRUPO I autopolimerização sob pressão em matriz de silicona; GRUPO II - autopolimerização térmica em mufla; GRUPO III autopolimerização utilizando a técnica do pincel; GRUPO IV autopolimerização pela mistura em pote dappen. Para cada tipo de processamento foram confeccionados 12 corpos-deprova de cada material, totalizando 48 corpos-de-prova para cada grupo e 192 espécimes ao total. Logo após a confecção dos espécimes foi realizado o teste de rugosidade de superfície (Ra) através de um rugosímetro/perfilômetro. Posteriormente, a superfície dos mesmos foi uniformizada e polida com a utilização de politriz, realizando-se novamente os mesmos testes de rugosidade. Antes do acabamento e polimento de superfície, os resultados encontrados apontaram a maior rugosidade para resina Vipi (4,074 ± 0,541) e técnica da mistura em dappen gupo IV (3,538 ± 0,509), enquanto que a menor rugosidade foi encontrada para resina Alike (2,671 ± 0,512) e técnica da prensagem em mufla grupo II (2,733 ± 0,470). Após acabamento e polimento, a maior rugosidade foi encontrada para resina Vipi (0,207 ± 0,032) e técnica da pressão grupo I (0,172 ± 0,037), enquanto que a menor rugosidade para resina Alike (0,113 ± 0,036) e técnica da prensagem em mufla grupo II (0,138 ± 0,027). Com os resultados obtidos, foi possível concluir que a melhor combinação para confecção de coroas provisórias em resina acrílica foi a técnica da prensagem em mufla associada à resina Alike. / Provisional crowns have some features that may compromise aesthetics and favors adherence of microorganisms and dental plaque formation. Previous studies have shown that processing may influence roughness and porosity of acrylic resins commonly used make provisional crowns. Because the several commercial resins available present differences in their quality the aim of this study was to evaluate the surface roughness of four commercial brands of acrylic resins (Dencor, Vipi, Duralay and Alike) according to four manipulation techniques (two direct and two indirect): GROUP I - autopolimerization under pressure in a silicone matrix; GROUP II autppolimerization in flask; GROUP III - autopolimerization using the bead brush technique; GROUP IV - autopolimerization after mixing in dappen dish. For each type of processing 12 specimens were made of each material, being 48 specimens for each group and 192 specimens in total. After specimens preparation, surface roughness tests (Ra) was performed using a rugosimeter / profilometer. Posteriorly, all surfaces were polished for standardization and same roughness tests were performed again. Before finishing and polishing, the results pointed out that Vipi resin presented the highest roughness (4.074 ± 0.541). Mixing the resin in dappen dish group IV (3.538 ± 0.509) also presented the highest roughness values regarding the technique. The lowest roughness values were found with Alike resin (2.671 ± 0.512) and flask technique group II (2.733 ± 0.470). After finishing and polishing techniques, the highest roughness was found with Vipi resin (0.207 ± 0.032) and the autopolimetization under pressure in silicone matrix technique - group I (0.172 ± 0.037). The lowest roughness values were found with Alike resin (0.113 ± 0.036) and flask technique group II (0.138 ± 0.027). With these results, it was possible to conclude that the best combination for making provisional crowns was the flask technique associated with Alike resin.
|
167 |
Avaliação da resistência à fratura de próteses fixas provisórias implanto-suportadas variando o comprimento do cantilever e o tipo de fibra: fibras de vidro e fibras de poli(aramida) / Evaluation of the resistance to the fracture of temporary fixed prostheses implant-supported varying the extension of the cantilever and the fiber type: glass fibers and poliaramid fibersPaola del Rosario Colán Guzmán 01 March 2007 (has links)
No tratamento reabilitador oral as restaurações provisórias são de suma importância. A resistência e a longevidade dos materiais utilizados em sua execução são críticas, principalmente em tratamentos prolongados e em espaços desdentados extensos. O objetivo deste trabalho foi avaliar a resistência e o modo de fratura de espécimes que simularam uma prótese fixa de três elementos variando o comprimento do cantilever (7, 14 e 21mm), confeccionadas em resina acrílica poli(metilmetacrilato) (PMMA) autopolimerizável, com e sem reforço em seu interior, construídos sobre componentes para implantes. Os reforços utilizados foram: fibras de vidro (Fibrante® - Ângelus®, Londrina, PR, Brasil) e fibras de poli(aramida) (Kevlar® - Du Pont®, USA). Os grupos foram constituídos de 10 espécimes cada, incluindo um grupo controle, sem reforço. Os espécimes foram submetidos à carga compressiva até a fratura. A análise dos resultados (ANOVA, p < 0,05), para o teste de resistência, mostrou não haver diferença estatística entre os grupos com respeito ao tipo de reforço, sendo que houve diferença estatística significante no que respeita ao comprimento do cantilever. Quando o comprimento do cantilever foi de 7mm todos os grupos apresentaram os valores médios de resistência a fratura, em N, significativamente maiores que os apresentados pelos grupos com 14 e 21mm de comprimento. Em relação ao modo de fratura os grupos reforçados apresentaram fraturas mais favoráveis ao reparo, tendo sido do tipo Parcial. / In the oral rehabilitator treatment, the provisory restorations have extremely importance. The resistance and durability of materials used in the execution are critical, especially in extended treatments and in vast toothless spaces. The goal of this work was to demonstrate the resistance and the types of fracture of specimens that simulate a fixed prosthesis of three elements changing the extension of cantilever (7, 14 e 21mm), made of acrylic resin polymethylmethacrylate (PMMA) autopolymer, with and without reinforcement in its interior, built over implant components. The reinforcements used were: fiberglass (Fibrante® - Angelus®, Londrina, PR, Brazil) and poliaramid fiber (Kevlar® - Du Pont®, USA). The groups have 10 specimens each, including a group of control, without reinforcement. The specimens were submitted to a compressor charge until its fracture. The analysis of results (ANOVA, p < 0,05) for the test of resistance, showed that there is no statistic difference between the groups regarding the type of reinforcement; however, there is a significant statistic difference regarding the cantilever extension. When the extension of cantilever was 7mm, all groups showed medium values of resistance to fractures, in N, significant more than the showed by the groups with 14 and 21mm of extension. In relation with the types of fracture, the reinforcement groups show fractures more favorable to be repaired, even when they were partially fractured.
|
168 |
Influência do número de desinfecção por energia de micro-ondas na dureza, rugosidade e brilho de resinas acrílicas termopolimerizadas / Effectiveness of microwave disinfection of three acrylic resin contaminated by yeast of CadidaSilva, Manoela Capla de Vasconcellos dos Santos da, 1983- 23 August 2018 (has links)
Orientadores: Rafael Leonardo Xediek Consani, Janaína de Cássia Orlandi Sardi / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-23T21:37:58Z (GMT). No. of bitstreams: 1
Silva_ManoelaCapladeVasconcellosdosSantosda_D.pdf: 1387678 bytes, checksum: 17ea18ac10fef54c8580345c3bba0454 (MD5)
Previous issue date: 2013 / Resumo: Este trabalho avaliou o efeito do número de ciclos de desinfecção por energia de micro-ondas na dureza Knoop, rugosidade e brilho de resinas termopolimerizadas para prótese total. Foram confeccionados 20 corpos-de-prova de cada material medindo 20 mm de diâmetro por 2 mm de altura, os quais foram distribuídos em 6 grupos de acordo com as resinas: QC-20, Onda Cryl, Clássico, Vipi Cril, Vipi Wave e Vipi Caracterizada. Todos os corpos-de-prova foram submetidos aos ensaios de rugosidade, dureza e brilho antes (controle, dia 0) e em cada ciclo de desinfecção (7, 14, 21 e 28 dias). Os corpos-de-prova foram polimerizados de acordo com as recomendações dos fabricantes, desincluídos e o acabamento realizado com pedra abrasiva para resina, lixas de carbeto de silício e pastas para polimento. A desinfecção por micro-ondas foi realizada a 650 W por 3 minutos, uma vez por dia durante 28 dias. Entre as desinfecções, as amostras permaneceram imersas em água e armazenadas em estufa a 37°C. Nos ensaios de rugosidade e dureza Knoop foram realizadas três mensurações na superfície de cada corpo-de-prova, sendo registrada a média das leituras. Os valores de brilho foram mensurados com medidor de brilho e para cada corpo-de-prova foram realizadas quatro mensurações, uma em cada quadrante, com feixe de luz incidindo em 60 graus. Os valores obtidos foram submetidos à ANOVA dois fatores para medidas repetidas, e teste de Tukey (5%). Os resultados mostraram que a resina Clássico apresentou o maior e a Vipi Wave o menor valor de rugosidade. Quando se avaliou a dureza, a resina Onda Cryl apresentou os maiores valores nos ciclos de 14 e 21 dias e não houve diferença estatística nos valores de dureza Knoop entre as demais resinas. A resina QC-20 apresentou os maiores valores de brilho, sendo maiores no controle (dia 0) e nos ciclos de 7 e 14 dias, os quais foram diferentes estatisticamente dos ciclos de 21 e 28 dias. Concluiu-se que houve influência da desinfecção por micro-ondas na rugosidade e dureza de todas as resinas, independente do número de ciclos. Com exceção da Clássico, as demais resinas mostraram valores de brilho com diferença estatisticamente significativa entre controle e ciclos de desinfecção / Abstract: This study evaluated the effect of repeated disinfection by microwave irradiation on hardness, surface roughness and gloss of denture base acrylic resins. Twenty samples were prepared for each material measuring 20 mm in diameter and 2 mm in height, which were divided into six groups according to the resins: QC-20, Wave Cryl, Classico, Vipi Cril, Vipi Wave and Vipi Characterized. All samples were tested for roughness, hardness and gloss analysis before and after disinfection cycles. Samples were polymerized according to the manufacturers' recommendations, deflasked and finished with abrasive stones, silicon carbide abrasives and polishing slurry. Disinfection by microwave irradiation was made at 650 W for 3 minutes, one time by day during 28 days. Between disinfection cycles the samples were stored in an incubator at 37°C. Three roughness measurements were made on the polished surface and the average was recorded as the roughness value (Ra, mm) for each sample. Hardness was recorded with three Knoop penetrations with a load of 50 kgf for 10 seconds. Three readings of each sample were used to obtain arithmetic mean for each analysis. The gloss values were measured with glossmeter. Four measurements were performed in each sample, one in each quadrant focusing the light beam at 60 degrees. The readings were recorded as the value of unit gloss (Gloss Unit - GU) and the data were recorded in the software. The values obtained were subjected to two-way ANOVA for repeated measures and Tukey's test (5%). The results showed that Classico had the highest value and Vipi Wave the lowest for surface roughness. Onda Cryl showed the highest values for hardness at 14- and 21-day cycles and there was no statistical difference among other resins. For gloss, QC-20 resin showed the highest values being higher at control and 7- and 14-day cycles, statistically different from 21- and 28-day cycles. It was concluded that there was influence of microwave irradiation in the roughness and hardness for all resins, regardless the number of cycles. Whit exception of Classico, there was statistically significant difference in gloss for all acrylic resins / Doutorado / Protese Dental / Mestre em Clínica Odontológica
|
169 |
Propriedades mecanicas de resinas acrilicas para base de protese antes e apos metodos de reparos / Mechanical properties of denture base acrylic resins before and after repair methodsFaot, Fernanda 11 October 2006 (has links)
Orientadores: Renata Cunha Matheus Rodrigues Garcia, Altair Antoninha Del Bel Cury / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-07T23:27:29Z (GMT). No. of bitstreams: 1
Faot_Fernanda_D.pdf: 1972781 bytes, checksum: b3ce58297c07d4abe90d5b2bf79729e7 (MD5)
Previous issue date: 2006 / Resumo: Fraturas por impacto e flexão ainda são os principais problemas relatados tanto pelos portadores de próteses removíveis como pelos cirurgiões dentistas. Na tentativa de solucionar esse problema, alterações na composição química das resinas acrílicas como a inclusão de co-polímeros, adição de agente de ligação cruzada e a incorporação de partículas de borracha na forma de butadieno estireno têm sido propostas. Entretanto, poucos estudos avaliaram a incorporação destes aditivos modificadores de impacto no processo de fratura, deformação e microestrutura de resinas acrílicas. Além disso, devido à fragilidade dos materiais poliméricos a presença de trincas e fraturas em base de
próteses removíveis ainda é alta e reparos são procedimentos comuns tanto por métodos diretos ou indiretos. Entretanto, as propriedades mecânicas de resinas acrílicas reparadas ainda não estão claramente descritas. Assim, os objetivos do presente trabalho foram: I) avaliar a resistência ao impacto e a flexão, bem como tensão de ruptura, módulo Young e deslocamento de escoamento de resinas acrílicas contendo modificadores de impacto e analisar sua microestrutura; II) determinar a resistência ao impacto e flexão de resinas acrílicas para base de prótese previamente fraturadas e reparadas com resinas fotopolimerizável, autopolimerizável e termopolimerizável. Como resultado, observou-se que a resina contendo borracha considerada de alto impacto, demonstrou alta capacidade de dissipação de energia, absorção de tensão e baixo percentual de deformação; entretanto exibiu processo de fratura frágil. Com relação às resinas utilizadas para reparo, concluiu-se que reparos realizados com a mesma resina usada para confecção dos corpos-de-prova, apresentaram melhores resultados quanto à resistência mecânica / Abstract: Fractures by impact and flexural action are the main problems described by denture users and dentists. Attempting to solve this problem, modifications on the chemical composition of the acrylic resins as co-polymer inclusion, cross linking agents addition and rubber particles incorporation in the form of butadiene styrene have been described as effective and worthwhile means to improve the impact strength and fracture propagation. However, literature lacks information regarding the incorporation of these modifying impact additives in the fracture process, plastic deformation and microstructure of acrylic resins. Furthermore, due to the brittleness of the polymeric materials, the presence of cracks and fractures in the removable prosthesis denture bases still remains high. Thus, frequent repairs are somewhat common procedures in the clinical practice, being by direct or indirect methods. Therefore, the effect of the repairs materials on the mechanical properties of acrylic resins is not clearly described yet. Front of these considerations, the purposes of the present study were: I) evaluate the impact and flexural strength, as well as, stress at yield, Young modulus and displacement at yield of acrylic resins containing impact modifiers and analyze their microstructure; II) determine the impact and flexural strength of denture base acrylic resins previously fractured and repaired with visible-light, auto and heat-polymerized acrylic resins. As results, it could be observed that the acrylic resin containing rubber particles, considered as the high impact, showed high capacity of energy dissipation and stress absorption before the fracture, lower percentage of deformation, however it exhibited brittle fracture process. Regarding to acrylic resins used as repair materials, it was concluded that repairs performed with the same resin used to fabricate the specimens showed the best results for mechanical resistance / Doutorado / Protese Dental / Doutor em Clínica Odontológica
|
170 |
Acrylic resins in wet whiteBallus, Olga, Guix, M., Micó, R., Palop, R. 26 June 2019 (has links)
Content:
The purpose of this paper is to study the influence of acrylic resins on the properties of the hide when added in the pickling-tanning stage of a wet white process.
Among retanning products, acrylic resins are very frequently used because they lend very good properties to the hide on account of their high affinity for chromium. When applied during chrome tanning, these
resins provide the hides with high fullness, due to the strong interaction of the carboxylate groups with chromium.
Extensive bibliography is available on the application of acrylic resins in wet blue, where it is observed that the properties they provide to the hides depend basically on the type of monomers and molecular weight. However, less information is found when these products are applied in wet white tanning.
In this study, 9 resins with different molecular weights and different monomer compositions were selected.
Resins were applied to pelt leathers of Spanish origin split at 3.5 mm. Hides were cut along the backbone. A standard process was applied to the left halves and the same process adding the resin was applied to the right halves. The resin was added after adjusting the salt of the bath and before adding the pickling acids.
The COD was measured before and after adding formic and sulfuric acid, and the shrinkage temperature and the degree of whiteness of the tanned hide were assessed. Hides were retanned and fatliquored with a standard process, and degree of softness, thickness, color intensity and organoleptic properties (fluffiness, compactness and grain tightness) were assessed. Leather shrinkage under temperature was also assessed, and images of leather sections were obtained by scanning electron microscopy (SEM).
While acrylic resins did not increase shrinkage temperature, they did fix and/or deposit themselves in the interfibrillary spaces of the hide; indeed, highly reduced COD values after acidification in the pickling stage were observed. This study shows that homopolymeric acrylic resins provided fuller and fluffier hides, while the rest of resins practically did not improve the physical and organoleptic properties of the hides.
Take-Away:
Homopolymeric acrylic resins provided full er and fluffier hides, while the rest of resins practically did not improve the physical and organoleptic properties of the hides
Wet white tanning improvement
|
Page generated in 0.0565 seconds