Made available in DSpace on 2014-10-09T12:44:45Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T13:58:01Z (GMT). No. of bitstreams: 1 06998.pdf: 4836505 bytes, checksum: 8807c39ebe15873ea228aaf490e0ed91 (MD5) / Dissertacao (Mestrado Profissionalizante em Lasers em Odontologia) / IPEN/D-MPLO / Intituto de Pesquisas Energeticas e Nucleares, IPEN/CNEN-SP; Faculdade de Odontologia, Universidade de Sao Paulo

Made available in DSpace on 2014-10-09T12:33:38Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T14:04:04Z (GMT). No. of bitstreams: 0 / Neste trabalho foram avaliadas as propriedades de um adesivo estrutural uretânico que visavam colagens de peças automotivas compostas por combinações de compósitos, termoplásticos e metais, que requerem do adesivo um elevado desempenho e compatibilidade com esses materiais. Para tanto, foram avaliadas as resistências ao cisalhamento de juntas formadas com estes substratos e o adesivo uretânico em diversas condições de exposição, que visam simular os efeitos deletérios que estas juntas estarão expostas durante sua utilização. Estes métodos permitiram caracterizar o adesivo como estrutural para tais aplicações, pois em todos os ensaios a fratura se deu fora da área de colagem, levando a conclusão de que a junta formada é mais resistente do que o substrato isoladamente. Foram desenvolvidos dois inovadores tratamentos de superfície alternativos ao lixamento, que foram o desengraxe com solventes e tratamento com plasma. Estes tratamentos tem contribuído significativamente om a comunidade e a partir deste estudo tem sido utilizados na indústria. A avaliação do comportamento térmico do adesivo e dos substratos permitiu o desenvolvimento de métodos de análise da composição das frações de massa de matriz polimérica, cargas minerais e fibra de vidro de modo prático, rápido e preciso, por uso da termogravimetria. A calorimetria diferencial exploratória possibilitou avaliar as transições vítreas dos substratos e do adesivo, bem como a energia liberada na reação do adesivo uretânico. Os fenômenos de interação química entre o adesivo e os substratos foram investigados pelo uso da técnica de espectroscopia infravermelho por reflectância atenuada, onde pode-se de forma inédita comprovar a existência de reações covalentes e de hidrogênio entre o adesivo e os substratos, que explicam a elevada aderência deste adesivo.Os resultados de todos os ensaios e análises levam à conclusão final que o adesivo uretânico, embora muitas vezes não considerado como estrutural, é um candidato plenamente capacitado ao trabalho de adesão estrutural, especialmente para uso automotivo nas condições descritas neste trabalho. / Tese (Doutoramento) / IPEN/T / Instituto de Pesquisas Energéticas e Nucleares - IPEN-CNEN/SP

Orientador: Marcela Rocha de Oliveira Carrilho / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-09T14:06:10Z (GMT). No. of bitstreams: 1 Bail_Michele_M.pdf: 616698 bytes, checksum: d6737bc67e911ea44d56c9e9884e2c55 (MD5) Previous issue date: 2007 / Resumo: O objetivo deste estudo foi avaliar a eficácia de diferentes métodos empregados na eliminação dos solventes incorporados a sistemas de união com características hidrofílicas diferentes. As hipóteses avaliadas consideraram que a eliminação/retenção dos solventes seria dependente: 1) da característica hidrofílica da resina; 2) da técnica e intervalo de tempo empregados na eliminação desses solventes; 3) do tipo de solvente empregado. Três resinas experimentais, R2, R3 e R5, foram formuladas de modo a exibirem características hidrofílicas distintas, dadas pela seleção e proporcionamento de monômeros, comumente empregados na odontologia. A resina R2 era a menos hidrofílica e R5 a mais hidrofílica. Acetona ou etanol foram adicionados a cada resina numa proporção de 50% (em peso). A eliminação dos solventes foi verificada por método gravimétrico, aplicado antes e após a realização dos seguintes tratamentos: 1) jato de ar à temperatura ambiente (JAAmb) por 15s; 2) JAAmb por 30s; 3) JAAmb por 60s; 4) jato de ar aquecido (JAAq) por 15s; 5) JAAq por 30s ou 6) JAAq por 60s. Os dados foram analisados por análise de variância e teste de Bonferroni (a =0,05). Nenhum tratamento eliminou completamente o solvente incorporado às resinas. Maior eliminação do solvente foi verificada para a resina menos hidrofílica R2, sendo que, para maioria das condições avaliadas: R2 > R3 e R2 > R5 (p<0,05). Quanto maior tempo de aplicação dos métodos de evaporação, maior a eliminação do solvente, sendo que aos 60s o percentual de massa perdida foi significativamente maior do que aos 15s (p<0,05). Aplicação do JAAq resultou, em geral, na maior eliminação de solvente quando comparado ao JAAmb (p<0,05). Não houve diferença na capacidade de evaporação dos solventes, acetona e etanol (p>0,05). A eliminação de solventes em adesivos mais hidrofílicos pode ser favorecida adotando se períodos de evaporação mais longos do que os indicados pelos fabricantes e aplicando-se jato de ar aquecido / Abstract: The aim of the present study was to evaluate the ability of different methods to eliminate the solvents incorporated into experimental adhesives with different degree of hydrophilicity. The anticipated hypotheses considered that the elimination/retention of the organic solvents would be dependent on: 1) the hydrophilic features of the experimental resins; 2) the method and time employed to eliminate these solvents; 3) the sort of solvent incorporated into the resin. A series of resin comonomers were blended to create three experimental adhesive resins, R2, R3 and R5, with an increasing degree of hydrophilicity. Resin R2 is the most hydrophobic and R5 is the most hydrophilic. The solvents, acetone and ethanol, were added to each experimental resin in a proportion of 50 wt%, generating six different mixtures. The elimination of these solvents was verified by means a gravimetric method applied before and after the following treatments: 1) application of an air-drying at room temperature for 15 s (ART); 2) ART for 30s; 3) ART for 60s; 4) application of heat-air drying (AH - 40 ± 1°C) for 15s; 5) AH for 30s or 6) AH for 60s. Data were analyzed by ANOVA and Bonferroni¿s test (a =0,05). None of the treatments was able to eliminate completely the solvent incorporated into the experimental resins. The highest elimination of solvent was observed for the resin R2, being that for most of conditions: R2 > R3 and R2 > R5 (p<0.05). The percentage of solvent evaporation increased proportionally with the increase of the time of the air-drying application, being significantly higher in the 60s when compared to 15s (p<0.05). In general, the application of the AH resulted in higher elimination of the solvent when compared to that obtained by the application of the ART (p<0.05). The solvent elimination, in general, did not depend on the sort of the solvent incorporated into the resin (p>0.05). The elimination of solvents from hydrophilic resins can be favored by extending the time for solvent evaporation and applying heat-air drying / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários

A tendência atual de simplificação de sistemas adesivos transformou-os em polímeros altamente hidrofílicos e prontamente susceptíveis à permeação de água através de sua estrutura. Estudos recentes têm demonstrado que os sistemas adesivos simplificados se comportam como membranas semipermeáveis, permitindo o movimento de fluidos através da sua estrutura. Soluções a base de oxalato de potássio são efetivos agentes de redução da condutividade hidráulica dentinária. Quando são aplicados na dentina após o condicionamento ácido, podem ser utilizados em associação com os sistemas adesivos sem o comprometimento da adesão. Este trabalho objetivou avaliar os efeitos dos sistemas adesivos AdheSE, One Up Bond F e Single Bond, associados ou não a uma solução a base de oxalato de potássio, na condutividade hidráulica da dentina. Foram realizados preparos de coroas totais em terceiros molares humanos que tiveram suas raízes secionadas e a polpa coronária removida. Os segmentos coronários obtidos foram conectados ao ?Medidor de Fluxo? (Flodec?System, De marco Engineering, Switzerland). A condutividade hidráulica dos espécimes foi mensurada antes e após a aplicação dos sistemas adesivos Single Bond -3M ESPE, One UP Bond F -Tokuyama Inc, AdheSe- Ivoclar- Vivadent. Os adesivos foram aplicados seguindo as recomendações do fabricante (grupos SBF, ADF e OBF), de forma experimental (grupos ADE e OBE), e em combinação com uma solução a base de oxalato de potássio (grupos SBO, ADO e OBO). Cada espécime teve seu valor de permeabilidade original ( smear layer) e máxima (após condicionamento ácido) medidos anteriormente, os quais serviram como parâmetros para o cálculo das respectivas alterações frente aos tratamentos, expressas em porcentagem. Após a determinação da condutividade hidráulica, os preparos foram moldados para obtenção de réplicas em resina, as quais foram examinadas em MEV (JEOL 2800, Japão) para qualificar a permeação de fluido através do adesivo. A Análise de variância a 2 critérios mostrou que apesar dos procedimentos adesivos causarem uma redução significante (p< 0.05) na condutividade hidráulica da dentina condicionada, nenhum foi capaz de eliminar completamente a passagem de fluidos através do adesivo polimerizado. Para os três adesivos testados, o tratamento com o oxalato de potássio foi o tratamento mais eficaz na redução da permeabilidade dentinária e esta diferença foi estatisticamente significante quando comparada aos outros tratamentos (p<0,05). Não houve diferença entre os três sistemas adesivos estudados com relação à redução da permeabilidade dentinária (p> 0,05). A análise das réplicas em MEV mostrou que mesmo após a polimerização do adesivo, a transudação de fluidos pôde ser identificada na superfície de todas réplicas examinadas. Nenhum dos sistemas adesivos testados foi capaz de eliminar a permeação de fluidos através da dentina, contudo a associação destes adesivos com uma solução a base de oxalato de potássio reduziu de forma significante a permeabilidade dentinária. / There is an ongoing trend to move away from classical multi-component bonding systems toward simplified adhesives. An immediate consequence of adhesive simplification is the intrinsic permeability to water that result from their increase in hydrophilicity. Current studies have demonstrated that single-step adhesives may act as semi-permeable membranes that allow water diffusion through its structure. Oxalate desensitizers are effective in reducing the hydraulic conductance of dentin. When oxalates are used after acid- etching they do not interfere with subsequent resin bonding. The objective of this study was to test the effects of adhesives systems with or without the application of an oxalate desensitizer on dentin permeability. Crown preparations were made from human extracted teeth. After the roots were sectioned and the coronal pulp removed, the crown segments were connected to an automatic flow-recording device (Flodec-System, De Marco Engineering, Switzerland). Fluid conductance was measured before and after the bonding procedures with the adhesives Single Bond -3M ESPE, One UP Bond F -Tokuyama Inc and AdheSe- Ivoclar Vivadent. Specimens were prepared and tested after the surface had been bonded according to manufacturer?s instructions (SBF,ADF and OBF groups) , in a experimental way (ADE and OBE groups) or integrating with a oxalate desensitizer gel (SBO, ADO and OBO groups). For each specimen, fluid flow across the smear-layer and bonded dentin was expressed as a percentage of acidetched dentin, which was assigned a value of 100% flow rate. After the hydraulic conductance measures, impressions were taken from the crown segments and epoxy resin replicas were produced for SEM examination. Two-Way ANOVA reveled that the adhesive systems reduced dentin permeability significantly (p< 0.05) compared to acid etched dentin, but no bonding system was able to eliminate the fluid flow though dentin. For the three bonding systems tested, treating the acid-etched dentin with potassium oxalate prior to the application of the adhesive was the most effective in reducing the hydraulic conductance of the specimens, and this difference was significant (p< 0.05) when comparing to the other treatments. There were no significant differences among the adhesives in their ability to reduce dentin permeability (p> 0.05). SEM micrographs of resin replicas showed that transudation of dentinal fluid droplets could be identified on the surfaces of all replicas examined.

A irradiação LASER sobre os sistemas adesivos aplicados em dentina, antes de sua fotoativação, tem sido proposta para aumentar a resistência de união de restaurações adesivas. O objetivo foi avaliar o efeito da irradiação com LASER de Diodo (&#x3BB; = 970nm) sobre diferentes sistemas adesivos na resistência de união imediata à dentina. Oitenta molares humanos hígidos foram aleatoriamente distribuídos em 8 grupos (n=10) de acordo com o sistema adesivo: MP (Adper&#x2122; ScotchBond Multi-Purpose Plus - convencional não simplificado), SB (Adper&#x2122; SingleBond 2 - convencional simplificado), CSE (Clearfil&#x2122; SE Bond - autocondicionante não simplificado), EO (Adper&#x2122; EasyOne - autocondicionante simplificado); e respectivos grupos irradiados com LASER de Diodo (SiroLaser, Sirona Dental). Para avaliar a resistência de união foi realizado teste de microtração, obtendo-se valores em MPa, posteriormente analisados através de ANOVA a 2 critérios, seguido de Tukey para comparações individuais e múltiplos testes t (p<0,05) para comparações entre CONTROLE e LASER do mesmo sistema adesivo. Os valores de resistência de união ± desvio padrão para os grupos sem e com irradiação com LASER foram respectivamente: MP (40,10±10,95 / 35,82±7,17), SB (33,49±6,77 / 43,69±8,15), CSE (43,71±15,71 / 37,95±7,66) e EO (19,67±5,86 / 29,87±6,98). A irradiação com LASER de Diodo provocou um aumento da resistência de união obtida pelos sistemas adesivos SB e EO, mostrando-se uma técnica promissora na obtenção de uma adesão mais efetiva de sistemas adesivos simplificados ao substrato dentinário. / LASER irradiation on adhesive systems before it`s activation has been proposed to increase bond strength of composite restorations to dentin. The objective was to evaluate the effect of Diode LASER irradiation (&#x3BB; = 970nm) on different adhesive systems on immediate bond strength to dentin. Eighty healthy human molars were randomly distributed in 8 groups (n=10) according to the adhesive system: MP (Adper&#x2122; ScotchBond Multi-Purpose Plus, non simplified etch and rinse), SB (Adper&#x2122; SingleBond 2 simplified etch and rinse), CSE (Clearfil&#x2122;SE Bond non simplified self-etch), EO (Adper&#x2122; EasyOne simplified self-etch); and respective groups irradiated with Diode LASER (SiroLaser, Sirona Dental). Microtensile test was performed obtaining bond strength values in MPa whice were analyzed by two way ANOVA, followed by Tukey for individual comparisons and multiple t test (p<0.05) for evaluation of CONTROL and LASER groups with the same adhesive systems. Bond strength values ± standard deviation for groups without and with LASER irradiation were respectively: MP (40.10±10.95 / 35.82±7.17), SB (33.49±6.77 / 43.69±8.15), CSE (43.71±15.71 / 37.95±7.66) and EO (19.67±5.86 / 29.87±6.98). Irradiation with Diode LASER resulted in an increase of SB and EO bond strength values, being considered a promising technic to obtain an improved adhesion of simplified adhesive systems to dentin substrate.

O uso do laser previamente à polimerização de sistemas adesivos aplicados sobre a dentina tem sido proposto para melhorar a resistência de união à dentina. O objetivo foi avaliar o efeito da variação da potência (P) e da energia por pulso (Ep) na resistência de união à dentina de um sistema adesivo convencional irradiado com laser previamente à fotoativação. Duzentos terceiros molares foram distribuídos aleatoriamente em 10 grupos (n=20) sendo um grupo sem irradiação (Controle) e nove grupos irradiados com laser de Diodo (970 nm) (SiroLaser - Sirona Dental Systems - Benshein, Alemanha), de acordo com a potência (P) e energia por pulso (Ep) utilizados: 1 - 0,5W/0,05J; 2 - 0,5W/0,08J; 3 - 0,5W/0,1J; 4 - 0,8W/0,05J; 5 - 0,8W/0,08J; 6 - 0,8W/0,1J; 7 - 1W/0,05J; 8 - 1W/0,08J; 9 - 1W/0,1J. Em todos os grupos fez-se o condicionamento com ácido fosfórico, aplicação do sistema adesivo convencional de dois passos AdperTM Single Bond 2 (3M ESPE, St Paul, MN, EUA) e restauração com resina composta Z250 (3M). Para avaliar a resistência de união foi realizado teste de microtração obtendo-se os valores em MPa. Os resultados foram analisados pelo ANOVA a dois critérios, seguido de Dunnett t (p < 0,001) para comparação entre os grupos. Os grupos irradiados foram avaliados pelo ANOVA a um critério, seguido dos testes de comparações múltiplas Bonferroni e Tamhane. Os valores de resistência de união ± desvio padrão de todos os grupos foram, respectivamente: 0 - Controle (34,60±10,76); 1 - (19,62±8,65); 2 - (27,56±9,20); 3 - (30,34±7,92); 4 - (23,31±5,96); 5 - (20,93±7,46); 6 - (24,67±8,59); 7 - (23,61±7,04); 8 - (25,94±6,82) e 9 - (21,48±3,59). O laser de Diodo influencia na resistência de união entre os grupos irradiados e não irradiado. A potência de 0,5W e energia por pulso de 0,1J influenciam positivamente nos valores de resistência de união quando o sistema adesivo é irradiado previamente a sua fotoativação. / The use of the laser prior to polymerisation of adhesive systems applied to the dentin has been proposed to improve the bond strength of dentin. The aim of this study was to investigate the effect of the variation of the output power (P) and pulse energy (Ep) on bond strength to dentin irradiated of conventional adhesive system with laser. Two hundred third molars were randomly distributed in 10 groups (n = 20): a group without laser irradiation (group control) and nine groups irradiated with diode laser (970 nm) (SiroLaser Sirona Dental Systems-Benshein, Germany), according to the output power (P) and pulse energy (Ep): 1 - 0,5W/0,05J; 2 - 0,5W/0,08J; 3 - 0,5W/0,1J; 4 - 0,8W/0,05J; 5 - 0,8W/0,08J; 6 - 0,8W/0,1J; 7 - 1W/0,05J; 8 - 1W/0,08J; 9 - 1W/0,1J. It was used in all groups etching with phosphoric acid, application of conventional adhesive system AdperTM Single Bond 2 (3M ESPE, St. Paul, MN, USA) and restoration with composite resin Z250 (3M). Microtensile test was performed obtaining bond strength values in MPa. Results were analyzed by two-ways ANOVA test, followed by Dunnett t (p < 0.001) for comparison between groups. The groups laser irradiated were assessed by one-way ANOVA test and subsequent t test with Bonferroni and Tamhane corrections. Bond strength values ± standard deviation for the groups were, respectively: 0 group control (34.60 ± 10.76); 1 - (19.62 ± 8.65); 2 - (27.56 ± 9.20); 3 - (30.34 ± 7.92); 4 - (23.31 ± 5.96); 5 - (20.93 ± 7.46); 6 - (24.67 ± 8.59); 7 - (7.04 ± 23.61); 8 - (25.94 ± 6.82) and 9 - (3.59 ± 21.48). The Diode laser influences on bond strength between irradiated and without irradiated groups. The output power 0.5W and energy per pulse 0.1J influence positively in the bond strength values when the adhesive system is irradiated prior to their light curing.

Orientadores: Paulo Sollero, Éder Lima de Albuquerque / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-23T11:43:13Z (GMT). No. of bitstreams: 1 Souza_CarlosAlexandreOliveirade_D.pdf: 19059891 bytes, checksum: 202a970a88c1bc18c1c8c3304c5b5e47 (MD5) Previous issue date: 2013 / Resumo: Na indústria aeronáutica é de extrema importância o uso de juntas coladas, rebitadas e parafusadas na união de componentes ou partes estruturais. Com o desenvolvimento de novos materiais e novas técnicas de manufatura, as juntas coladas passaram a ser mais utilizadas devido a algumas vantagens sobre as tradicionais juntas rebitadas e parafusadas, tais como: melhor distribuição das tensões na região de colagem, melhor vedação, melhor acabamento, melhor resistência à fadiga, maior eficiência aerodinâmica e o mais importante em aplicações aeronáuticas, menor peso. O projeto de juntas coladas é baseado em análises para a determinação das tensões normais e cisalhantes no adesivo e do campo de deslocamentos ao longo da junta. E no caso de solicitação cíclica, ou seja, fadiga é necessário ainda desenvolver modelos para prever a vida em fadiga de trincas na camada de adesivo e nos aderentes. O objetivo deste trabalho é estudar o comportamento de juntas coladas em estruturas metálicas de aeronaves solicitadas em fadiga, através de modelos analíticos, numéricos e ensaios experimentais. No decorrer do trabalho foram realizados ensaios estáticos, de fadiga e tenacidade à fratura de corpos de prova com juntas coladas. Também foram projetados e testados subcomponentes que representam de forma aproximada, estruturas aeronáuticas reais. As juntas foram modeladas utilizando o software comercial de elementos finitos ABAQUS Ò . Foi ainda, desenvolvido e implementado um modelo semi-analítico para prever a vida em fadiga de juntas coladas baseado em uma formulação proveniente da teoria de vigas e da lei de Paris. E finalmente, foi desenvolvida uma técnica para medir o crescimento da trinca em fadiga durante um ensaio de forma automática, ou seja, sem precisar parar o ensaio para fazer avaliações subjetivas a partir de inspeções visuais / Abstract: In the aeronautical industry is extremely important the use of bonded, riveted and screwed joints for the union of components or structural parts. Through the development of new materials and new manufacturing techniques, the use of bonded joints has increased considerably over recent years. This growth is mainly due to some advantages over the traditional riveted and bolted joints, such as: better stress distributions, better sealing, smoother surface finishes, enhanced fatigue properties, greater aerodynamic efficiency and lower weight, which is an important issue in aeronautical applications. The design of bonded joints is predominantly based on stress analysis as well as the field of displacement along the joint. In the case of cyclic loading, or fatigue, is also necessary to develop models to predict the fatigue life of cracks in the adhesive layer and adherends. The main objective of this work is to study the behavior of bonded joints in metallic aircraft structures under fatigue loading, through analytical models, numerical models and experimental tests. During this work, was carried out static, fatigue and fracture toughness tests. Also was designed and tested subcomponents that represent real aircraft structures. The joints were modeled using the commercial finite element software ABAQUS. It was also developed and implemented a semi-analytical model to predict the fatigue life of bonded joints based on a formulation derived from the theory of beams and the Paris like-law. Finally, was developed a technique to measure the fatigue crack growth during a test automatically, ie, without stopping the test to make subjective evaluations from visual inspections / Doutorado / Mecanica dos Sólidos e Projeto Mecanico / Doutor em Engenharia Mecânica

Orientador: Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-04T03:47:16Z (GMT). No. of bitstreams: 1 Almeida_JanainaBertoncelode_D.pdf: 3821202 bytes, checksum: 5159fe7fa53555f8e6fcb14be233c2a9 (MD5) Previous issue date: 2005 / Resumo: Os objetivos deste estudo in vitro foram avaliar a resistência da união adesiva à microtração (µT) de 4 sistemas adesivos: Scotchbond MP Plus (SBMP) como controle, Single Bond (SB), OptiBond Solo Plus (OSP), Clearfil SE Bond (CSE), a espessura de suas camadas híbridas (CH) em dentina humana sadia antes e após termociclagem e o tipo de fratura. Setenta e dois terceiros molares recém extraídos armazenados em cloramina 0,5% foram usados. Para µT 48 dentes tiveram o esmalte oclusal removido e as superfícies polidas com lixa d?água granulação 600; 6 dentes foram usados aleatoriamente em cada grupo. Os materiais foram utilizados de acordo com o fabricante e a porção oclusal foi reconstruída com a resina composta Filtek Z250. Após 24 horas de armazenagem à 37°C em água destilada os dentes foram cortados para formar palitos que foram tracionados à velocidade de 0,5 mm/min (5 palitos por dente). Para CH 3 dentes por grupo foram restaurados como descrito e cortados em 4 fatias (cada) para medições em MEV (5 por fatia) em 3300X. Após o armazenamento os grupos termociclados foram submetidos à ciclos entre 5 e 55°C e cortados para µT e CH. O tipo de fratura foi classificado como: coesiva em dentina ou resina, adesiva e mista. Análise de Variância e teste de Tukey-Kramer a 5% de nível de significância mostraram: µT (MPa): SB (37,34) = SBMP (35,98), SBMP = CSE (28,59) > OSP (18,49) e SB (47,85) > SBMP (29,91), SBMP = CSE (34,17) > OSP (17,63); para CH (µm): SBMP (2,81) > SB (2,31) = OSP (2,28) e SBMP (2,89) = SB (2,73) > OSP (2,25), sem e com termociclagem respectivamente. CH não foi detectada para CSE. µT não foi correlacionada com CH. SB teve µT e CH aumentadas após termociclagem. Termociclagem não teve efeito negativo sobre os grupos. Os tipos de fraturas predominantes foram do tipo adesiva e mista / Abstract: The objectives of this in vitro study were to evaluate the microtensile bond strength (µTBS) of 4 adhesive systems: Scotchbond MP Plus (SBMP) as a control, Single Bond (SB), OptiBond Solo Plus (OSP), Clearfil SE Bond (CSE), their hybrid layer width (HL), to sound human dentin, before and after thermocycling and type of failure. 72 freshly extracted third molars stored in 0,5% chloramine were used. For the µTBS 48 teeth had their occlusal enamel removed and surface polished with 600 grit SiC paper; 6 teeth were randomly assigned to each group. The adhesive systems were used according to manufacturer instructions and each occlusal was rebuilt with the resin composite Filtek Z250. After 24 hours storage at 37°C in distilled water, teeth were sectioned to form sticks that were tensioned at a crosshead speed of 0,5 mm/min (5 sticks per tooth). For de HL measurements 3 teeth per group were restored as described and sectioned to lend 4 slices to SEM measurements (5 per slice) at 3300X. For the thermocycling groups after the 24 hours storage teeth were submitted to 500 cycles between 5 and 55°C and sectioned to µTBS or HL. Failure was classified as: cohesive in dentin or resin, adhesive and mixed. ANOVA and Tukey-Kramer?s test at 5% significance level showed: µTBS (Mpa): SB (37,34) = SBMP (35,98), SBMP = CSE (28,59) > OSP (18,49) and SB (47,85) > SBMP (29,91), SBMP = CSE (34,17) > OSP (17,63); for HL (µm): SBMP (2,81) > SB (2,31) = OSP (2,28) and SBMP (2,89) = SB (2,73) > OSP (2,25), without and with thermocycling respectively. HL could not be detected for CSE. µTBS could not be correlated to HL width; SB had µTBS and HL increased after thermocycling. Thermocycling had no negative effect on groups. Adhesive and mixed types of failures were predominant / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários

Orientador: Luis Roberto Marcondes Martins / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-04T03:56:33Z (GMT). No. of bitstreams: 1 Casselli_DeniseSaMaia_D.pdf: 2775830 bytes, checksum: 43dd6d3dde0928950dc7944d0226d0be (MD5) Previous issue date: 2005 / Resumo: Este estudo avaliou a sensibilidade pós-operatória de restaurações Classe I de compósito restauradas com sistema de união de condicionamento total ou autocondicionante. Cento e quatro restaurações defeituosas de amálgama foram substituídas em 52 pacientes. Cada paciente substituiu duas restaurações. Após preparo cavitário confeccionado, as restaurações foram confeccionadas, sob isolamento absoluto utilizando-se Single Bond ou Clearfil SE Bond e um compósito odontológico (Filtek Z250). A sensibilidade foi avaliada antes da substituição (baseline), após 7 dias e 6 meses da troca, utilizando-se estímulo frio e escala analógica de dor. Se ocorresse sensibilidade após 7 dias, os pacientes retornavam após 14 e 30 dias. Os escores foram analisados através de testes não paramétricos: Friedman e Wilcoxon. Nenhuma diferença estatística significativa foi encontrada em relação à sensibilidade pós-operatória no baseline, 7 dias e 6 meses. Também não houve diferença entre os adesivos em qualquer tempo. Nenhuma sensibilidade espontânea foi relatada. Os principais motivos de substituição de restaurações de amálgama, neste estudo, foram fratura da restauração e degradação marginal. Os sistemas de união utilizados nesse estudo não mostraram diferenças em relação à sensibilidade pós-operatória e não mostraram sensibilidade espontânea após 6 meses, quando utilizados de acordo com as instruções do fabricante / Abstract: This study evaluated the post-operative sensitivity of posterior Class I composite resin restorations restored with a self-etching primer or a total-etch bonding system. One hundred and four restorations were replaced by one clinician in 52 patients. Each patient received two restorations. After cavity preparations, the restorations were completed under rubber dam isolation and restored using a Clearfil SE Bond or Single Bond and a resin-based restorative material (Filtek Z250). The sensitivity was evaluated at O (baseline) and 7 days and 6 months using cold stimuli, and recorded using a visual-analogue scale. If sensitivity was experienced on day 7, patients were also contacted on days 14 and 30 to assess the degree of sensitivity. The se ores were analyzed as non-parametric data by means of the Friedman and Wilcoxon tests. No statistieally signifieant differences were found in sensitivity between the two adhesives systems at day O, 7 and 6 months. No spontaneous pos-operative sensitivity was reported. The major reasons for failure of amalgam restorations were fraetures restoration and marginal deficiencies. The adhesive systems used in this study showed no differenees in post-operative sensitivity, and did not show spontaneous sensitivity after 6 months if they were used accordance with manufacturer' s instructions / Doutorado / Dentística / Doutor em Clínica Odontológica

Orientador: Marcelo Giannini / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-04T16:53:21Z (GMT). No. of bitstreams: 1 Reis_AndreFigueiredo_D.pdf: 7439243 bytes, checksum: d418ba9253bb8f6a3265539a4f97ec1c (MD5) Previous issue date: 2005 / Resumo: A efetividade dos procedimentos restauradores adesivos promovida através de diferentes protocolos de aplicação tem sido questionada com relação à durabilidade da união ao substrato dentinário. Os objetivos deste estudo foram avaliar: a resistência de união em diferentes substratos dentais; a importância dos solventes orgânicos na união produzida por adesivos que utilizam o condicionamento ácido prévio; a habilidade de diferentes adesivos em evitar a nanoinfiltração na interface resina-dentina; a sorção de água e solubilidade, a resistência à tração, o módulo de elasticidade e características ultraestruturais dos adesivos. Foram utilizados sistemas que empregam diferentes estratégias para condicionamento e infiltração no substrato dental: adesivos que utilizam condicionamento ácido prévio, adesivos de dois passos que empregam primers autocondicionantes e adesivos autocondicionantes de passo único. Os testes foram realizados após 24 h ou até o período de 12 meses de armazenagem em água e/ou óleo mineral. A resistência de união, foi avaliada através do ensaio de microtração. Para avaliação da nanoinfiltração foi utilizado AgNO3 amoniacal como agente traçador, para evidenciar espaços nanométricos e sinais de degradação nas interfaces. Os espécimes foram preparados para observação em Microsopia Eletrônica de Transmissão e/ou Varredura. Para avaliação da sorção de água e solubilidade, a variação de massa dos espécimes foi aferida. A resistência de união, a resistência máxima à tração e o módulo de elasticidade foram avaliados em máquina de ensaio universal. Os resultados mostraram que nenhum adesivo foi capaz de evitar a nanoinfiltração. A maioria dos materiais mostrou-se eficiente logo após a sua aplicação; no entanto, o comportamento da união ao longo do tempo frente a presença de água variou consideravelmente. Os adesivos autocondicionantes de passo único foram os mais susceptíveis à degradação após armazenagem em água. De acordo com as propriedades estudadas, conclui-se que: dentes bovinos são melhores substitutos para dentes humanos em testes de união; a presença de solventes orgânicos é essencial na adesão à dentina; e, a degradação da união está relacionada à hidrofilia dos materiais testados / Abstract: The effectiveness of adhesive restorative procedures promoted by different application protocols has been questioned with regard to the durability of adhesion to dentin substrate. The aims of this study were to: evaluate the bond strengths to different dental substrates; determine the importance of organic solvents in the adhesion promoted by etch-and-rinse adhesives; evaluate the ability of different adhesive systems to prevent nanoleakage in resin-dentin interfaces; and determine the water sorption and solubility, ultimate tensile strength, elastic modulus and ultrastructural characteristics of the bonding resins. Adhesive systems that use different etching and infiltration strategies were used: etch-and-rinse systems, twostep self-etching primers, and one-step self-etching adhesives. Tests were performed after 24 hours or after a storage period of up to 12 months in water and/or mineral oil. Bond strengths were analyzed by means of the microtensile bond test. Ammoniacal AgNO3 was used as a tracer for the nanoleakage test, in order to disclose nanometer-sized spaces and degradation signs within interfaces. Specimens were prepared for Transmission and/or Scanning Electron Microscopy. For water sorption and solubility analysis, the mass variation of specimens was determined. Microtensile bond strength, ultimate tensile strength and elastic modulus were analyzed in a universal testing machine. Results showed that noadhesive system was able to prevent nanoleakage. Most adhesives proved to be effective right after application; however, the behavior of bonded interfaces after long-term water-storage varied considerably. Single-step self-etching adhesives were the most susceptible to degradation after storage in water. Based on the tests performed and properties analyzed, it can be concluded that: bovine teeth are the best substitutes for human teeth in adhesion tests; organic solvents are essential in dentin adhesion; and, degradation of resin-dentin bonds is related to the hydrophilicity of the materials tested. / Doutorado / Dentística / Doutor em Clínica Odontológica