Friction Bit Joining (FBJ) is a method used to join lightweight metals to advanced high-strength steels (AHSS). The automotive industry is experiencing pressure to improve fuel efficiency in their vehicles. The use of AHSS and aluminum will reduce vehicle weight which will assist in reducing fuel consumption. Previous research achieved joint strengths well above that which was required in three out of the four standard joint strength tests using DP980 AHSS and 7075 aluminum. The joints were mechanically tested and passed the lap-shear tension, cross-tension, and fatigue cycling tests. The t-peel test configuration never passed the minimum requirements. The purpose of continuing research was to increase the joint strength using FBJ to join the aluminum and AHSS the automotive industry desires to use specifically in the t-peel test. In this study FBJ was used to join 7085 aluminum and GADP1180 AHSS. The galvanic coating on the AHSS and its increased strength with the different aluminum alloy required that all the tests be re-evaluated and proven to pass the standard tests. FBJ is a two-step process that uses a consumable bit. In the first step the welding machine spins the bit to cut through the aluminum, and the second step applies pressure to the bit as it comes in contact with the AHSS to create a friction weld.

Efforts to reduce vehicle weight and improve crash performance have resulted in increased application of advanced high strength steels (AHSS) and a recent focus on the weldability of these alloys. Resistance spot welding (RSW) is the primary sheet metal welding process in the manufacture of automotive assemblies. Integration of AHSS into the automotive architecture has brought renewed challenges for achieving acceptable welds. The varying alloying content and processing techniques has further complicated this initiative. The current study examines resistance spot welding of high strength and advance high strength steels including high strength low alloy (HSLA), dual phase (DP) and a ferritic-bainitic steel (590R). The mechanical properties and microstructure of these RSW welded steel alloys are detailed. Furthermore a relationship between chemistries and hardness is produced. The effect of strain rate on the joint strength and failure mode is also an important consideration in the design of welded structures. Current literature, however, does not explain the effects of weld microstructure and there are no comprehensive comparisons of steels. This work details the relationship between the joint microstructure and impact performance of spot welded AHSS. Quasi-static and impact tests were conducted using a universal tensile tester and an instrumented drop tower, respectively. Results for elongation, failure load and energy absorption for each material are presented. Failure modes are detailed by observing weld fracture surfaces. In addition, cross-sections of partially fractured weldments were examined to detail fracture paths during static loading. Correlations between the fracture path and mechanical properties are developed using observed microstructures in the fusion zone and heat-affected-zone. Friction stir spot welding (FSSW) has proven to be a potential candidate for spot welding AHSS. A comparative study of RSW and FSSW on spot welding AHSS has also been completed. The objective of this work is to compare the microstructure and mechanical properties of Zn-coated DP600 AHSS (1.2mm thick) spot welds conducted using both processes. This was accomplished by examining the metallurgical cross-sections and local hardnesses of various spot weld regions. High speed data acquisition was also used to monitor process parameters and attain energy outputs for each process.

Efforts to reduce vehicle weight and improve crash performance have resulted in increased application of advanced high strength steels (AHSS) and a recent focus on the weldability of these alloys. Resistance spot welding (RSW) is the primary sheet metal welding process in the manufacture of automotive assemblies. Integration of AHSS into the automotive architecture has brought renewed challenges for achieving acceptable welds. The varying alloying content and processing techniques has further complicated this initiative. The current study examines resistance spot welding of high strength and advance high strength steels including high strength low alloy (HSLA), dual phase (DP) and a ferritic-bainitic steel (590R). The mechanical properties and microstructure of these RSW welded steel alloys are detailed. Furthermore a relationship between chemistries and hardness is produced. The effect of strain rate on the joint strength and failure mode is also an important consideration in the design of welded structures. Current literature, however, does not explain the effects of weld microstructure and there are no comprehensive comparisons of steels. This work details the relationship between the joint microstructure and impact performance of spot welded AHSS. Quasi-static and impact tests were conducted using a universal tensile tester and an instrumented drop tower, respectively. Results for elongation, failure load and energy absorption for each material are presented. Failure modes are detailed by observing weld fracture surfaces. In addition, cross-sections of partially fractured weldments were examined to detail fracture paths during static loading. Correlations between the fracture path and mechanical properties are developed using observed microstructures in the fusion zone and heat-affected-zone. Friction stir spot welding (FSSW) has proven to be a potential candidate for spot welding AHSS. A comparative study of RSW and FSSW on spot welding AHSS has also been completed. The objective of this work is to compare the microstructure and mechanical properties of Zn-coated DP600 AHSS (1.2mm thick) spot welds conducted using both processes. This was accomplished by examining the metallurgical cross-sections and local hardnesses of various spot weld regions. High speed data acquisition was also used to monitor process parameters and attain energy outputs for each process.

Friction bit joining (FBJ) is a new method that enables lightweight metal to be joined to advanced high-strength steels. Weight reduction through the use of advanced high-strength materials is necessary in the automotive industry, as well as other markets, where weight savings are increasingly emphasized in pursuit of fuel efficiency. The purpose of this research is twofold: (1) to understand the influence that process parameters such as bit design, material type and machine commands have on the consistency and strength of friction bit joints in dissimilar metal alloys; and (2) to pioneer machine and bit configurations that would aid commercial, automated application of the system. Rotary broaching was established as an effective bit production method, pointing towards cold heading and other forming methods in commercial production. Bit hardness equal to the base material was found to be highly critical for strong welds. Bit geometry was found to contribute significantly as well, with weld strength increasing with larger bit shaft diameter. Solid bit heads are also desirable from both a metallurgical and industry standpoint. Cutting features are necessary for flat welds and allow multiple material types to be joined to advanced high-strength steel. Parameters for driving the bit were established and relationships identified. Greater surface area of contact between the bit and the driver was shown to aid in weld consistency. Microstructure changes resulting from the weld process were characterized and showed a transition zone between the bit head and the bit shaft where bit hardness was significantly increased. This zone is frequently the location of fracture modes. Fatigue testing showed the ability of FBJ to resist constant stress cycles, with the joined aluminum failing prior to the FBJ fusion bond in all cases. Corrosion testing established the use of adhesive to be an effective method for reducing galvanic corrosion and also for protecting the weld from oxidation reactions.

Recently, Zn-XAl-YMg coatings have emerged as lighter-weight substitutes for traditional Zn-based coatings for the corrosion protection of steels; however, little is currently known concerning the interactions between the oxides present on advanced high strength steel (AHSS) surfaces and the Zn-Al-Mg bath. In the current contri- bution, the selective oxidation and reactive wetting of a series of C-Mn AHSS were determined with the objective of providing a quantitative description of this pro- cess. The process atmosphere pO2 was varied using dew points of −50◦C, −30◦C and −5◦C. The surface oxide chemistry and morphology were analysed by means of SEM and XPS techniques. Reactive wetting of the selectively oxidized surfaces using a Zn-1.6 wt.% Al-1.6 wt.% Mg bath was monitored as a function of annealing time at 60 s, 100 s and 140 s at 800◦C. The resulting bare spot defects in the Zn-1.6 wt.% Al-1.6 wt.% Mg coating were assessed by means of SAM-AES and FIB, while coating adhesion was analysed by 180◦ bend tests. Annealing the steel substrates resulted in the formation of surface MnO, which varied based on pO2 and Mn alloy content, and that this MnO greatly reduced the wettability of the steel by the Zn-1.6 wt.% Al- 1.6 wt.% Mg bath, resulting in bare spot defects. It was determined that the reactive wetting of the steel substrate was dependant on the oxide morphology and oxidation mode, which was a function of both alloying content of Mn in the steel and annealing pO2 process atmosphere (dew point). Finally, it was concluded that the bare spot area percentage on the coated panels was statistically invariant for annealing times of between 60 s and 140 s at 800◦C. / Thesis / Master of Applied Science (MASc) / Metallic coatings are applied to steels that are not naturally corrosion resistant. The aim of this research was to determine how well a coating containing zinc, aluminum and magnesium adhered to high strength automotive steel. It was deter- mined that manganese oxides formed on the steel during heating prior to applying the metallic coating. The manganese oxides prevented good adhesion between the steel and the coating, resulting in bare spot defects in the coating. The bare spot defects are undesirable as they leave the steel exposed and therefore susceptible to corrosion and are unsightly when painted.

No description available.

Induction Assisted Single Point Incremental Forming (IASPIF) is a die-less hot sheet metal forming. The IASPIF does not apply characteristic complex tooling like those applied in deep drawing and bending. In this thesis, induction heating was used to heat up the sheet while simultaneously forming with a tool. The research goal is to improve the formability of high strength steels by heating. The IASPIF consists of non-complicated set up that allows induction heating to be utilized through the coil inductor moved under the sheet and synchronized with the forming tool that moves on the upper side of the sheet. The advanced high strength steel alloys, DP980, DP600 and 22MnB5 steels, were investigated. The influence of induction heating on formability was evaluated by the maximum wall angle that can be achieved in a single pass. Additionally, tool diameter and tool feed rate was also varied. The most influencing parameters were tool feed rate, induction power, and the profile depth. A new forming strategy was also developed by control the heating temperature through coupling the formed profile depth with a successively increased tool feed rate. The forming forces of DP980 steel sheet, were reduced from 7 kN to 2.5 kN when forming process was performed at room and elevated temperature, respectively. Stretching stresses were developed during forming process causing a high reduction in the resulting wall part thickness. New findings in this investigation were the reverse relationship between the step-down depth and the thickness reduction percentage. The smaller the tool diameter, the better was the formability. The finite element simulation of the investigated forming process showed that the increase in heating temperature has a direct effect on rising the plastic strain from 0.2 at room temperature to 1.02 at 800 ◦ C. The maximum true strain achieved in the resulting wall part thickness was determined by FEM simulations and validated with experimental trials. The part shape accuracy was measured and the highest deflection was founded when the part was formed by the highest step-down depth. Moreover, the minimum deflection in the part shape was achieved by utilizing a high induction power in the experiments. Finally, the resulting mechanical properties of the 22MnB5 alloy sheet material were tailored during IASPIF. For this purpose, the sheets were locally heated by induction during the forming process and subsequently quenched at different rates. As a result, the produced tailored parts consist of three different regions, which consist of a ductile, transitional and hardened region. The proposed procedure allows forming and quenching at the same time without transfer and thus, process time was reduced. / Die induktionsgestützte, inkrementelle Blechumformung (englisch: Induction Assisted Single-Point Incremental Forming IASPIF) ist Warmumformprozess, bei dem keine komplexen Werkzeuge wie beim Tiefziehen und Biegen benötigt werden. Inhalt dieser Arbeit ist die inkrementelle Umformung eines Bleches mit gleichzeitig ablaufender induktiver Erwärmung. Das Forschungsziel bestand in der Verbesserung der Umformbarkeit von hochfesten Stahlwerkstoffen wie DP600, DP980 und 22MnB5 durch eine gezielte partielle Erwärmung. Der prinzipielle Aufbau des Versuchsstandes besteht aus einem Spuleninduktor, der unterhalb des umzuformenden Blechs platziert ist, und der synchron mit dem Werkzeug – einem Drückdorn – während des Umformvorganges verfährt. Ein wesentlicher Untersuchungsschwerpunkt bestand in der Ermittlung der Einflussgrößen auf den untersuchten IASPIF-Prozess. Für die Bewertung der Umformbarkeit wurden hierbei der maximal erreichbare Teilwandwinkel und die Profiltiefe, die in einem Umformdurchgang herstellbar waren, ermittelt und ausgewertet. Darüber hinaus konnten im Rahmen der Arbeit die Induktionsleistung des Generators, der Werkzeugdurchmesser und die Werkzeugvorschubgeschwindigkeit als relevante Prozessparameter identifiziert werden. Im Ergebnis der durchgeführten Untersuchungen zeigten die Werkzeugvorschubgeschwindigkeit und die Induktionsleistung einen wesentlichen Einfluss auf die erreichbare Profiltiefe. Aufbauend auf den erzielten Ergebnissen konnte eine prozessangepasste Umformstrategie entwickelt werden, bei der eine konstante Erwärmungstemperatur durch das Koppeln der momentanen Profiltiefe mit einer sukzessiv steigenden Werkzeugvorschubgeschwindigkeit erreicht wird. Weiterhin ließen sich die Kräfte bei der Umformung eines Stahlbleches aus DP980 von 7 kN (bei Raumtemperatur) auf 2,5 kN (bei erhöhter Temperatur) reduzieren. Aufgrund des mit einem Streckziehvorgang vergleichbaren Spannungszustandes während des Umformprozesses war eine starke Verringerung der resultierenden Wanddicke zu beobachten. Als neue Erkenntnis in dieser Untersuchung konnte die umgekehrte Beziehung zwischen der Zustelltiefe und dem Dickenreduktionsprozentsatz abgleitet werden. Aus der Finite - Elemente - Simulation des vorgestellten Umformprozesses wurde erkennbar, dass die Erhöhung der Erwärmungstemperatur einen direkten Einfluss auf die plastische Dehnung von 0,2 (bei Raumtemperatur) auf 1,02 (bei 800 °C) hat. Mittels der numerischen Simulation und der nachfolgenden experimentellen Validierung erfolgte darüber hinaus die Bestimmung der maximalen wahren Dehnung, die in der resultierenden Wanddicke erreicht wurde. Bei den Versuchen mit der größten Zustellung ließ sich durch die Bestimmung der Teileformgenauigkeit die höchste Abweichung von der Sollgeometrie CAD Modell feststellen. Abschließend wurde nachgewiesen, dass der IASPIF Prozess auch zur Einstellung maßgeschneiderter Bauteileigenschaften wie der resultierenden mechanischen Eigenschaften des Blechmaterials aus 22MnB5 einsetzbar ist. Zu diesem Zweck wurden die Bleche während des Umformprozesses lokal induktiv erwärmt und anschließend zur Einstellung des gewünschten Gefüges bei unterschiedlichen Abkühlgeschwindigkeiten abgeschreckt.